KR100980286B1 - Antimicrobial plastics and antimicrobial oil paint - Google Patents
Antimicrobial plastics and antimicrobial oil paint Download PDFInfo
- Publication number
- KR100980286B1 KR100980286B1 KR1020080051773A KR20080051773A KR100980286B1 KR 100980286 B1 KR100980286 B1 KR 100980286B1 KR 1020080051773 A KR1020080051773 A KR 1020080051773A KR 20080051773 A KR20080051773 A KR 20080051773A KR 100980286 B1 KR100980286 B1 KR 100980286B1
- Authority
- KR
- South Korea
- Prior art keywords
- antimicrobial
- antibacterial
- plastic
- dcoit
- triclosan
- Prior art date
Abstract
본 발명은 합성수지, 4,5-디클로로-2-n-옥틸-4-이소티아졸린-3-원, 그리고 5-클로로-2-(2,4-클로로페녹시)페놀을 포함하는 항균 플라스틱을 제공한다. 상기 4,5-디클로로-2-n-옥틸-4-이소티아졸린-3-원은 항균 플라스틱 전체 중량에 대하여 0.01 내지 5.0 중량%로 포함되고, 상기 5-클로로-2-(2,4-클로로페녹시)페놀은 항균 플라스틱 전체 중량에 대하여 0.01 내지 5.0 중량%로 포함된다.The present invention provides an antimicrobial plastic comprising a synthetic resin, 4,5-dichloro-2-n-octyl-4-isothiazoline-3-one, and 5-chloro-2- (2,4-chlorophenoxy) phenol. to provide. The 4,5-dichloro-2-n-octyl-4-isothiazoline-3-one is included in an amount of 0.01 to 5.0 wt% based on the total weight of the antibacterial plastic, and the 5-chloro-2- (2,4- Chlorophenoxy) phenol is included in an amount of 0.01 to 5.0% by weight based on the total weight of the antibacterial plastic.
상기 항균 플라스틱은 기존 보다 적은 함량의 항균제를 포함하면서도 그램 양성균, 그램 음성균, 및 곰팡이에 모두 뛰어난 항균력을 가지며, 다량의 수분이 존재하는 환경에서도 항균력이 장시간 유지되며, 세균의 변종에 대한 항균력이 우수하고, 인체에 유해성이 적다.The antimicrobial plastics have an excellent antimicrobial activity to gram positive bacteria, gram negative bacteria, and fungi, while containing a smaller amount of antimicrobial agents than before, and the antimicrobial activity is maintained for a long time even in the presence of a large amount of water, and excellent antimicrobial activity against bacterial strains. And less harmful to human body.
항균제품, 항균배수구, 항균에어콘덕트, 항균호스, 항균파이프, 항균쓰레기통, 항균플라스틱, 유성도료, 항균유성도료 Antibacterial product, Antibacterial drainage, Antibacterial air conductor, Antibacterial hose, Antibacterial pipe, Antibacterial waste container, Antibacterial plastic, Oil paint, Antibacterial oil paint
Description
본 발명은 항균 플라스틱 및 항균 유성도료에 대한 것으로서, 보다 상세하게는 기존 보다 적은 함량의 항균제를 포함하면서도 그램 양성균, 그램 음성균, 및 곰팡이에 모두 뛰어난 항균력을 가지며, 다량의 수분이 존재하는 환경에서도 항균력이 장시간 유지되며, 세균의 변종에 대한 항균력이 우수하고, 인체에 유해성이 적은 항균 플라스틱 및 항균 유성도료에 대한 것이다.The present invention relates to an antimicrobial plastic and an antimicrobial oil paint, and more particularly, to include gram-positive bacteria, gram-negative bacteria, and fungi, all of which contain a smaller amount of antimicrobial agents, and have excellent antimicrobial activity even in an environment where a large amount of water is present. This is maintained for a long time, excellent antimicrobial activity against bacterial strains, and less harmful to human body antibacterial plastic and antibacterial oil paint.
일반적으로, 배수구는 물을 빼내거나 물이 빠져나가는 곳을 말하는 것으로, 가정의 싱크대, 욕실, 베란다 건물, 또는 공장 등의 물이 배수되는 각종 시설에 마련되어 각종 작업 후에 발생되는 하수를 외부로 배출하는데 사용된다.In general, the drain is a place where water is drained or drained, and is provided in various facilities where water is drained, such as a sink, a bathroom, a veranda building, or a factory, to discharge sewage generated after various work to the outside. Used.
상기 하수에는 음식 쓰레기나 사람의 피지, 공장, 또는 건물에서 사용되는 각종 부유영양물이 잔존하여, 상기 배수구에 세균이나 곰팡이의 등이 서식하게 하는 영양원이 된다. 상기 세균 또는 곰팡이 등의 대사물에 의해서 배수구 주변에 슬러지가 형성되어 악취가 발생하고, 각종 인체에 유해한 세균과 곰팡이가 증식되고 외부로 전파되어 병의 근원이 되는 문제점이 있다.The sewage remains various food nutrients and various suspended nutrients used in human sebum, factories, or buildings, and becomes a nutrient source for bacteria and fungi to inhabit the drains. Sludge is formed around the drain hole by metabolites such as bacteria or fungi, and odors are generated, and bacteria and molds harmful to various human bodies are multiplied and propagated to the outside, thereby causing a problem.
또한, 배수구는 각종 하수를 처리하는 하수구와 연계되어 있어, 하수구 내부에서 서식하는 각종 세균과 곰팡이로 인하여 배수구에서 악취가 발생하고, 인체에 유해한 세균을 전파하는 파리 및 모기가 하수구에서 배수구 측으로 전파됨으로써 각종 오염의 주범이 되는 문제점이 있다.In addition, drains are associated with sewers that process various sewage, causing various types of bacteria and fungi to live in the sewers, causing odors in the drains, and flies and mosquitoes that propagate harmful bacteria to humans. There is a problem that causes various pollution.
각종 세균과 곰팡이를 제거하기 위하여, 트리클로로 이소시아눌산 분말 또는 차아염소산 나트륨의 수용액 등의 염소계 표백제를 사용하여 세균 또는 곰팡이 등을 화학적 분해함으로써, 살균하는 방법이 사용되어 왔다. 그러나, 트리클로로 이소시아눌린 등의 염소계 표백제는 강력한 산화력이 있어 싱크대나 그 주변의 금속을 부식시키는 위험성이 있으며, 유독성의 염소가스를 발생시킨다. 특히, 식초와 같은 산성 물질과 반응하면 염소가스의 발생이 현저히 증가하며, 이를 사람이 흡입하면 인체에 해로운 영향을 끼치게 된다.In order to remove various bacteria and molds, a sterilization method has been used by chemical decomposition of bacteria or molds using a chlorine bleach such as trichloro isocyanuric acid powder or an aqueous solution of sodium hypochlorite. However, chlorine bleach, such as trichloro isocyanurine, has a strong oxidizing power and there is a risk of corroding the sink and the metal around it, and generates toxic chlorine gas. In particular, the reaction with acidic substances such as vinegar significantly increases the generation of chlorine gas, and if inhaled by humans have a harmful effect on the human body.
또한, 과탄산나트륨 분말이나 과산화수소수 등의 산소계 표백제를 이용하여 살균하는 방법도 사용되어 왔다. 그러나, 상기 산소계 표백제는 용해도가 높아 물과 접촉하면 빠르게 용해되기 때문에 효과의 지속성 면에서 문제점이 있으며, 염소계 표백제에 비해 산화력이 매우 약해 점액질의 원인이 되는 세균이나 곰팡이를 살균할 수 없다는 문제점이 있다.In addition, a method of sterilization using an oxygen-based bleach such as sodium percarbonate powder or hydrogen peroxide solution has also been used. However, the oxygen-based bleach has a high solubility, so that it dissolves quickly when it comes in contact with water, and thus has a problem in terms of persistence.Therefore, the oxygen-based bleach has a problem in that the oxidizing power is very weak compared to the chlorine-based bleach, so that bacteria or molds causing mucus cannot be sterilized. .
한편, 세균과 곰팡이를 살균하기 위하여 배수구 생산 공정에서 살균 물질을 배수구에 포함시키는 방법으로는 살균 물질을 액체 형태 또는 분말 형태로 사출되는 합성수지 재료에 첨가하는 방법이 주로 사용된다. 그러나, 살균 물질은 고농축으로 대개 독성이 있어 취급이 극히 위험하고, 분말 형태로 첨가하는 경우 비산되 어 외부로 전파됨으로써, 작업자와 기계가 오염되며, 밀폐 상태로 취급을 주의하면서 작업을 실시하여야 함에 따라 생산이 어려운 문제점이 있다.On the other hand, as a method of including the sterilizing material in the drain in the drain production process in order to sterilize bacteria and fungi, a method of adding the sterilizing material to the synthetic resin material injected in liquid form or powder form is mainly used. However, sterilization materials are highly concentrated and usually toxic, so handling is extremely dangerous, and when added in powder form, they are scattered and spread to the outside, which contaminates workers and machines. Therefore, the production is difficult.
또한, 액체 형태로 첨가하는 경우 분말 형태와 같이 비산되는 문제는 발생하지 않지만 액상 자체가 독성이 있으므로, 작업자의 눈에 접촉되면 시력을 잃게 할 수 있고, 피부에 접촉되면 발진이 발생하게 된다. 이에 따라, 고무장갑과 보호 안경을 항상 착용한 상태로 작업을 실시하여야 함에 따라 생산효율을 감소하고, 작업자의 안전을 위협하는 문제점이 있다.In addition, when added in a liquid form does not cause the problem of scattering like powder form, but the liquid itself is toxic, it may cause loss of sight when contacting the eyes of the operator, and rash occurs when contacted with the skin. Accordingly, the work must be carried out while wearing rubber gloves and protective glasses at all times, thereby reducing production efficiency and threatening worker safety.
또한, 상기 배수구뿐만 아니라, 그 표면에서 증식하는 세균 또는 곰팡이에 의한 감염을 방지할 수 있다고 광고된 여러 가지의 항균 제품이 출시되어 왔으나, 이들 제품은 세균의 어느 한 종류 또는 곰팡이에만 항균력이 있거나, 항균력이 단시간 내에 사라지는 등의 문제점이 있다. 이에, 다양한 세균과 곰팡이에 광범위하며 효과적인 항균력을 지속적으로 유지하는 항균 제품이 필요한 실정이다.In addition, various antimicrobial products that have been advertised to prevent infection by bacteria or fungi that proliferate on the surface thereof, as well as the drains, have been antimicrobial only to any one type of bacteria or fungi, There is a problem that the antimicrobial activity disappears in a short time. Accordingly, there is a need for an antimicrobial product that continuously maintains a broad and effective antimicrobial activity against various bacteria and fungi.
한편, 습기가 많은 지하실, 장롱이나 물건들이 놓인 벽면, 그리고 아파트 베란다의 벽체 등에는 항상 습기가 많다. 이들 습기로 인하여 곰팡이가 증식하게 되며 증식된 곰팡이는 포자를 공기 중으로 분출시켜 천식을 유발하기도 한다. 또한, 곰팡이는 벽지나 페인트 도장면을 파괴하여 건물의 수명을 단축시키며, 미관상 보기에도 좋지 않다. On the other hand, there is always a lot of moisture in a damp basement, a wall with cabinets or objects, and the walls of an apartment's veranda. This moisture causes the fungus to multiply and the multiplying fungus spores into the air, causing asthma. In addition, mold destroys wallpaper or painted surfaces, shortening the lifespan of buildings, which is not good for aesthetics.
목재로 지어진 건물의 경우 장마철에는 목재가 다량의 수분을 함유하게 된다. 이에 따라, 목재에 방부처리를 하였다 하더라도 곰팡이와 조류 및 목재성분인 셀룰로즈를 발효시키는 세균들이 증식하게 되어 목재건물의 수명을 단축시킨다. 따라서, 곰팡이와 조류 및 세균의 증식을 억제하여 건물의 수명을 늘리고 건물의 외관을 깨끗하게 유지할 필요가 있다. In the case of buildings made of wood, during the rainy season the wood contains a lot of moisture. Accordingly, even if the wood is preservative treatment, bacteria and fungi fermenting fungi, algae and cellulose, which is a wood component, are multiplied, which shortens the life of the wood building. Therefore, it is necessary to increase the life of the building and keep the exterior of the building clean by suppressing the growth of mold, algae and bacteria.
또한, 공업적인 측면에서 제지공장, 가죽제조공장 등의 제조 시설물 등에 발생하는 슬러지는 제품의 품질을 떨어뜨리고, 생산성을 감소시키는 중요한 요인이다. 따라서, 제조 시설물에 슬러지의 발생을 억제함으로써 품질을 향상하고 생산성을 증대시키고자 하는 요구가 증대되고 있다.In addition, in the industrial aspect, sludge generated in manufacturing facilities such as paper mills, leather manufacturing plants, etc. is an important factor for reducing product quality and reducing productivity. Therefore, the demand for improving the quality and increasing the productivity by suppressing the generation of sludge in the manufacturing facility is increasing.
본 발명의 목적은 기존 보다 적은 함량의 항균제를 포함하면서도 그램 양성균, 그램 음성균, 및 곰팡이에 모두 뛰어난 항균력을 가지며, 다량의 수분이 존재하는 환경에서도 항균력이 장시간 유지되며, 세균의 변종에 대한 항균력이 우수하고, 인체에 유해성이 적은 항균 플라스틱 및 항균 유성도료를 제공하는 것이다.The purpose of the present invention is to include an antimicrobial agent of less than the existing content while having excellent antimicrobial activity to all gram positive bacteria, gram negative bacteria, and fungi, the antimicrobial activity is maintained for a long time even in the presence of a large amount of water, It is to provide an excellent antimicrobial plastics and antimicrobial oil paints less harmful to the human body.
상기 목적을 달성하기 위하여, 본 발명의 일 구체예에 따르면, 합성수지, 4,5-디클로로-2-n-옥틸-4-이소티아졸린-3-원(4,5-dichloro-2-n-octyl-4-isothiazoline-3-one, DCOIT), 그리고 5-클로로-2-(2,4-클로로페녹시)페놀(5-chloro-2-(2,4-dichlorophenoxy)phenol, 트리클로산)을 포함하는 항균 플라스틱을 제공한다. 상기 4,5-디클로로-2-n-옥틸-4-이소티아졸린-3-원은 항균 플라스틱 전체 중량에 대하여 0.01 내지 5.0 중량%로 포함되고, 상기 5-클로로-2-(2,4-클로로페녹시)페놀은 항균 플라스틱 전체 중량에 대하여 0.01 내지 5.0 중량%로 포함된다.In order to achieve the above object, according to one embodiment of the present invention, a synthetic resin, 4,5-dichloro-2-n-octyl-4-isothiazoline-3-one (4,5-dichloro-2-n- octyl-4-isothiazoline-3-one, DCOIT), and 5-chloro-2- (2,4-chlorophenoxy) phenol (5-chloro-2- (2,4-dichlorophenoxy) phenol, triclosan) To provide antibacterial plastic. The 4,5-dichloro-2-n-octyl-4-isothiazoline-3-one is included in an amount of 0.01 to 5.0 wt% based on the total weight of the antibacterial plastic, and the 5-chloro-2- (2,4- Chlorophenoxy) phenol is included in an amount of 0.01 to 5.0% by weight based on the total weight of the antibacterial plastic.
상기 항균 플라스틱은 4,5-디클로로-2-n-옥틸-4-이소티아졸린-3-원, 5-클로로-2-(2,4-클로로페녹시)페놀, 및 합성수지를 포함하는 항균 마스터배치(master batch)를 포함할 수 있다. 이때, 상기 4,5-디클로로-2-n-옥틸-4-이소티아졸린-3-원은 항균 플라스틱 전체 중량에 대하여 0.01 내지 5.0 중량%로 포함되고, 상기 5-클로로-2-(2,4-클로로페녹시)페놀은 항균 플라스틱 전체 중량에 대하여 0.01 내지 5.0 중량%로 포함된다.The antimicrobial plastic is an antimicrobial master comprising 4,5-dichloro-2-n-octyl-4-isothiazoline-3-one, 5-chloro-2- (2,4-chlorophenoxy) phenol, and synthetic resin May contain a master batch. In this case, the 4,5-dichloro-2-n-octyl-4-isothiazoline-3-one is contained in 0.01 to 5.0% by weight based on the total weight of the antibacterial plastic, the 5-chloro-2- (2, 4-chlorophenoxy) phenol is included at 0.01 to 5.0% by weight based on the total weight of the antibacterial plastic.
본 발명의 다른 일 구체예에 따르면, 유성도료, 4,5-디클로로-2-n-옥틸-4-이소티아졸린-3-원, 그리고 5-클로로-2-(2,4-클로로페녹시)페놀을 포함하는 항균 유성도료를 제공한다. 상기 4,5-디클로로-2-n-옥틸-4-이소티아졸린-3-원은 항균 유성도료 전체 중량에 대하여 0.01 내지 5.0 중량%로 포함되고, 상기 5-클로로-2-(2,4-클로로페녹시)페놀은 항균 유성도료 전체 중량에 대하여 0.01 내지 5.0 중량%로 포함된다.According to another embodiment of the present invention, an oil paint, 4,5-dichloro-2-n-octyl-4-isothiazoline-3-one, and 5-chloro-2- (2,4-chlorophenoxy ) Provides an antibacterial oil paint containing phenol. The 4,5-dichloro-2-n-octyl-4-isothiazoline-3-one is included in an amount of 0.01 to 5.0 wt% based on the total weight of the antibacterial oil paint, and the 5-chloro-2- (2,4 -Chlorophenoxy) phenol is contained in an amount of 0.01 to 5.0% by weight based on the total weight of the antibacterial oil paint.
본 발명의 항균 플라스틱 및 항균 유성도료는 기존 보다 적은 함량의 항균제를 포함하면서도 그램 양성균, 그램 음성균, 및 곰팡이에 모두 뛰어난 항균력을 가지며, 다량의 수분이 존재하는 환경에서도 항균력이 장시간 유지되며, 세균의 변종에 대한 항균력이 우수하고, 인체에 유해성이 적다.Antimicrobial plastics and antimicrobial oil paints of the present invention have an excellent antimicrobial activity to gram positive bacteria, gram negative bacteria, and molds, while containing a smaller amount of antimicrobial agents than before, and the antimicrobial activity is maintained for a long time even in the presence of a large amount of water. Excellent antibacterial activity against strains, less harmful to human body.
또한, 본 발명의 일 구체예에 따른 항균 플라스틱의 제조 방법에 따르면, 항균제의 취급 및 합성수지와의 혼합이 용이하며, 먼지의 비산 문제가 없어 생산성을 향상시킨다.In addition, according to the manufacturing method of the antimicrobial plastics according to an embodiment of the present invention, it is easy to handle the antimicrobial agent and mixing with the synthetic resin, there is no problem of scattering dust to improve the productivity.
이하, 본 발명을 보다 상세하게 설명한다.Hereinafter, the present invention will be described in more detail.
본 발명의 일 구체예에 따른 항균 플라스틱은 합성수지, 4,5-디클로로-2-n-옥틸-4-이소티아졸린-3-원(4,5-dichloro-2-n-octyl-4-isothiazoline-3-one, DCOIT), 그리고, 5-클로로-2-(2,4-클로로페녹시)페놀(5-chloro-2-(2,4- dichlorophenoxy)phenol, 트리클로산)을 포함한다. Antibacterial plastic according to an embodiment of the present invention is a synthetic resin, 4,5-dichloro-2-n-octyl-4-isothiazoline-3-one (4,5-dichloro-2-n-octyl-4-isothiazoline -3-one, DCOIT), and 5-chloro-2- (2,4-chlorophenoxy) phenol (5-chloro-2- (2,4-dichlorophenoxy) phenol, triclosan).
상기 항균 플라스틱은 합성수지, 그리고 DCOIT, 트리클로산 및 합성수지를 포함하는 항균 마스터배치(master batch)를 포함하며, 상기 DCOIT를 전체 중량에 대하여 0.01 내지 5.0 중량%로 포함하고, 상기 트리클로산을 전체 중량에 대하여 0.01 내지 5.0 중량%로 포함할 수 있다.The antimicrobial plastic includes a synthetic resin and an antibacterial master batch including DCOIT, triclosan and synthetic resin, wherein the DCOIT is contained in an amount of 0.01 to 5.0% by weight based on the total weight, and the triclosan is 0.01% by weight. To 5.0 wt%.
본 발명의 다른 일 구체예에 따른 항균 유성도료는 유성도료, DCOIT, 그리고 트리클로산을 포함한다. 상기 항균 유성도료는 DCOIT를 전체 중량에 대하여 0.01 내지 5.0 중량%로 포함하고, 트리클로산을 전체 중량에 대하여 0.01 내지 5.0 중량%로 포함한다.Antibacterial oil paint according to another embodiment of the present invention includes an oil paint, DCOIT, and triclosan. The antimicrobial oil paint includes DCOIT in an amount of 0.01 to 5.0 wt% based on the total weight, and triclosan in an amount of 0.01 to 5.0 wt% based on the total weight.
상기 DCOIT와 트리클로산은 화학적인 구조 특성상 무극성을 띄는 소수성 성질을 가지므로 같은 소수성 계열인 플라스틱과 소수성 유기용제를 사용하는 유성도료에 쉽게 혼합되며, 균일하게 분산되어 플라스틱이나 유성도료 표면에 균일한 항균력을 나타낼 수 있도록 한다. 또한, 상기 DCOIT와 트리클로산은 수분 등에 의해 쉽게 용출되지 않아 플라스틱과 유성도료에 혼입되는 경우에도 지속적인 항균력을 유지한다.The DCOIT and triclosan have non-polar hydrophobic properties due to their chemical structural properties, so they are easily mixed with oil-based paints using the same hydrophobic plastic and hydrophobic organic solvents, and are uniformly dispersed to provide uniform antimicrobial activity on the surface of plastics or oil paints. To show. In addition, the DCOIT and triclosan are not easily eluted by moisture, etc., even when incorporated into plastics and oil paints to maintain a continuous antibacterial activity.
상기 항균 플라스틱 및 항균 유성도료는 상기 DCOIT를 전체 중량에 대하여 0.01 내지 5.0 중량%로 포함하고, 상기 트리클로산을 전체 중량에 대하여 0.01 내지 5.0 중량%로 포함하여, 항균력이 광범위하고 효과적이며 지속적으로 발현된다.The antimicrobial plastic and the antimicrobial oil paint include the DCOIT in an amount of 0.01 to 5.0% by weight based on the total weight, and the triclosan in an amount of 0.01 to 5.0% by weight based on the total weight. .
기존에 많은 항균 제품들 출시되어 소비자들의 관심을 끌었으나, 소비자들이 느낄 만큼의 실제적인 항균력을 나타내지 않았다. 항균 제품은 곰팡이, 그램 양성 균(gram-positive bacteria), 그램 음성균(gram-negative bacteria) 모두를 사멸시키고 지속적인 항균력을 나타내야 한다. 그러나, 대부분의 항균 제품은 특정 균류에 특이적으로 작용하고 모든 미생물에 광범위한 항균력을 나타내지는 못한다. 미생물은 각각 고유의 특이성 있는 대사과정을 거쳐 생존하게 되는데 한가지의 항균제가 모든 미생물에 작용하기는 기대하기 어렵다. Many antimicrobial products have been released in the past to attract the attention of consumers, but did not show the actual antimicrobial power as consumers feel. Antimicrobial products should kill all fungi, gram-positive bacteria, and gram-negative bacteria and exhibit sustained antimicrobial activity. However, most antimicrobial products act specifically on certain fungi and do not exhibit extensive antimicrobial activity on all microorganisms. Each microorganism survives through its own specific metabolic process, and one antimicrobial agent is unlikely to work on all microorganisms.
또한, 대부분의 항균제들은 거의 모두 수용성이어서 항균 성분이 물기가 있는 곳에서는 곧 물에 용해되어 사출물 외부로 용출되므로 비교적 짧은 시간 내에 항균력을 상실하게 된다.In addition, most of the antimicrobial agents are almost all water-soluble, so that the antimicrobial component is dissolved in water and eluted out of the injection molding where it is wet, and thus the antimicrobial activity is lost within a relatively short time.
그러나, 상기 항균 플라스틱 및 항균 유성도료는 곰팡이와 그램 양성균에 뛰어난 항균력을 갖는 DCOIT와 그램 양성균과 그램 음성균에 뛰어난 항균력을 갖는 트리클로산을 병행 사용하여 광범위한 항균력을 가진다. 또한, 상기 DCOIT와 트리클로산은 물에 잘 용해되지 않는 물질이기 때문에, 상기 항균 플라스틱 및 항균 유성도료는 다량의 수분이 존재하는 환경에서 사용시 특히 유용하며, 항균력이 장시간 동안 유지된다. However, the antimicrobial plastic and the antimicrobial oil paint have broad antimicrobial activity by using DCOIT having excellent antimicrobial activity against mold and gram positive bacteria and triclosan having excellent antimicrobial activity against gram positive bacteria and gram negative bacteria. In addition, since the DCOIT and triclosan are insoluble in water, the antimicrobial plastic and the antimicrobial oil paint are particularly useful when used in an environment in which a large amount of water is present, and the antimicrobial activity is maintained for a long time.
상기 DCOIT(CAS No.: 64359-81-5)는 분자량이 282.2274g/mol이고, 분자식은 C11H17Cl2NOS이다. 세균 또는 곰팡이의 세포벽은 상기 DCOIT를 흡수할 때 아데노신 트리포스페이트(adenosine triphosphate, ATP) 에너지를 사용하는 능동수송을 하기 때문에, DCOIT는 신속하게 흡수되어 빠른 항균활성을 나타낸다.The DCOIT (CAS No .: 64359-81-5) is the molecular weight 282.2274g / mol, molecular formula is C 11 H 17 C l2 NOS. Since the cell walls of bacteria or fungi carry active transport using adenosine triphosphate (ATP) energy when absorbing the DCOIT, DCOIT is rapidly absorbed and exhibits rapid antimicrobial activity.
도 1은 DCOIT가 맥주효모균(Saccharomyces cerevisiae)의 세포벽에 흡수되는 양을 시간에 따라 나타낸 그래프이다. 도 1을 참조하면, DCOIT는 세포벽으로 신속하게 흡수되어 짧은 시간 내에 미생물의 세포 내부에 다량이 존재하게 되며, 미생물의 증식을 억제하여 항균 플라스틱 또는 항균 유성도료가 갖추어야 할 항균력을 신속하게 나타내게 됨을 알 수 있다. 1 shows that DCOIT is brewer's yeast ( Saccharomyces) cerevisiae ) is a graph showing the amount absorbed by the cell wall over time. Referring to Figure 1, DCOIT is quickly absorbed into the cell wall is present in a large amount inside the cells of the microorganisms within a short time, and inhibits the growth of the microorganisms to quickly exhibit the antibacterial power that the antimicrobial plastic or antimicrobial oil paint should have. Can be.
세포벽을 통하여 흡수된 DCOIT는 미생물의 산소 호흡을 억제시켜 미생물의 증식을 억제하고, ATP 생산을 억제하며, 각종 효소를 불활성화시켜 미생물을 사멸시킨다. 도 2는 DCOIT 투입 후 대장균(Escherichia coli)의 산소 호흡이 억제되는 정도를 나타내는 그래프이다. 도 2를 참조하면, DCOIT 투여 후 수분 내에 대장균의 산소 호흡이 급격하게 감소하여 대장균이 신속하게 사멸하게 되는 것을 알 수 있다.DCOIT absorbed through the cell wall inhibits microbial oxygen respiration, inhibits microbial growth, inhibits ATP production, and inactivates various enzymes to kill microorganisms. Figure 2 is Escherichia coli after the addition of DCOIT coli ) is a graph showing the extent to which oxygen respiration is suppressed. Referring to FIG. 2, it can be seen that the oxygen breathing of E. coli rapidly decreases within a few minutes after administration of DCOIT, thereby rapidly killing E. coli.
또한, DCOIT는 탈수소효소(dehydrogenase)들의 티올(thiol)기와 반응하여 탈수소효소를 파괴하고 불활성화시킨다. 탈수소효소들은 미생물이 영양분을 섭취한 후 에너지 대사를 하는 과정에 필수적인 효소들이다. 따라서, 탈수소효소의 불활성화는 미생물의 에너지 대사(metabolism)를 불가능하게 하여 세포 내의 ATP 에너지 생성을 억제한다. 이에 따라, 세포 내 에너지가 고갈되어 미생물은 사멸하게 된다. 도 3은 알코올 탈수소효소에 DCOIT를 투입한 후 그 활성의 변화를 나타내는 그래프이다. 도 3을 참조하면, 알코올 탈수소효소의 활성이 DCOIT 투입 후 신속하게 감소하는 것을 알 수 있다.In addition, DCOIT reacts with thiol groups of dehydrogenases to destroy and inactivate dehydrogenases. Dehydrogenases are essential enzymes for the metabolism of microorganisms after nutrients. Thus, inactivation of dehydrogenase inhibits the energy metabolism of microorganisms and thus inhibits ATP energy production in cells. As a result, the energy in the cells is depleted and the microorganisms are killed. Figure 3 is a graph showing the change in activity after the addition of DCOIT to alcohol dehydrogenase. Referring to Figure 3, it can be seen that the activity of the alcohol dehydrogenase is rapidly reduced after the addition of DCOIT.
또한, DCOIT는 세포 내 자유 라디칼(free radical)을 증가시켜 세포의 구성 성분을 파괴하고, 세포의 자체 조절능력을 상실시켜 미생물을 사멸시킨다.In addition, DCOIT increases the free radicals in the cell, destroying the cell's components, and killing microorganisms by losing the cell's self-regulation ability.
상기 트리클로산(CAS No.: 3380-34-5)은 분자량이 289.53g/mol이고, 분자식은 C12H7Cl3O2이다. 상기 트리클로산은 에노일-아실캐리어프로테인리덕테이즈(Enoyl-acyl carrier protein reductase)를 불활성화시킨다. 상기 에노일-아실캐리어프로테인리덕테이즈는 미생물 세포의 지방산을 생산하는 핵심 효소로 지방산은 세포막의 주성분이다. 상기 트리클로산은 에노일-아실캐리어프로테인리덕테이즈와 1:1로 결합하여 에노일-아실캐리어프로테인리덕테이즈를 영구히 불활성화시킴으로써, 지방산의 생성을 억제한다. 이에 따라, 세포막 형성이 불가능해져 세포는 사멸하게 된다. 상기 에노일-아실 캐리어프로테인리덕테이즈는 모든 미생물에 존재하기 때문에 상기 트리클로산은 광범위한 세균 종류에 대하여 항균력을 나타낸다.The triclosan (CAS No .: 3380-34-5) has a molecular weight of 289.53 g / mol, and a molecular formula is C 12 H 7 Cl 3 O 2 . The triclosan inactivates Enoyl-acyl carrier protein reductase. The enoyl-acyl carrier protein reductase is a key enzyme for producing fatty acids of microbial cells and fatty acids are the main components of cell membranes. The triclosan binds 1: 1 with the anoyl-acyl carrier protein reductase to permanently inactivate the anoyl-acyl carrier protein reductase, thereby inhibiting the production of fatty acids. As a result, cell membrane formation becomes impossible and the cells die. Since the enoyl-acyl carrier protein reductase is present in all microorganisms, the triclosan shows antimicrobial activity against a wide range of bacterial species.
상기 항균 플라스틱이 포함하는 합성수지는 사출성형할 수 있는 것이면 어느 것이나 사용 가능하고, 폴리에틸렌(PE), 폴리프로필렌(PP), 폴리스티렌(PS), 스티렌/아크릴로니트릴/부타디엔(ABS), 폴리아미드(PA), 폴리옥시메틸렌(POM), 폴리에틸렌테레프탈레이트(PET), 폴리부틸렌테레프탈레이트(PBT), 폴리메틸메타크릴레이트(PMMA), 폴리카보네이트(PC), 피씨 알로이(PC Alloy) 등을 사용할 수 있으나, 본 발명이 이에 한정되는 것은 아니다. Synthetic resin included in the antimicrobial plastics can be used as long as it can be injection molded, polyethylene (PE), polypropylene (PP), polystyrene (PS), styrene / acrylonitrile / butadiene (ABS), polyamide ( PA), polyoxymethylene (POM), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polymethyl methacrylate (PMMA), polycarbonate (PC), PC alloy, etc. can be used. However, the present invention is not limited thereto.
또한, 상기 항균 마스터배치가 포함하는 합성수지는 폴리에틸렌(PE), 폴리프로필렌(PP), 폴리스티렌(PS), 스티렌/아크릴로니트릴/부타디엔(ABS), 폴리아미드(PA), 폴리옥시메틸렌(POM), 폴리에틸렌테레프탈레이트(PET), 폴리부틸렌테레프탈레이트(PBT), 폴리메틸메타크릴레이트(PMMA), 폴리카보네이트(PC), 피씨 알로 이(PC Alloy) 등일 수 있으나, 본 발명이 이에 한정되는 것은 아니다. In addition, the synthetic resin included in the antimicrobial masterbatch polyethylene (PE), polypropylene (PP), polystyrene (PS), styrene / acrylonitrile / butadiene (ABS), polyamide (PA), polyoxymethylene (POM) , Polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polymethyl methacrylate (PMMA), polycarbonate (PC), PC alloy (PC Alloy) and the like, but the present invention is not limited thereto. no.
상기 항균 플라스틱이 포함하는 합성수지와 항균 마스터배치가 포함하는 합성수지는 같은 합성수지를 사용할 수 있다. 이 경우, 항균 마스터배치와 합성수지가 같은 물성을 갖게 되어 혼합이 용이해진다.Synthetic resin included in the antimicrobial plastic and synthetic resin included in the antimicrobial masterbatch may use the same synthetic resin. In this case, the antimicrobial masterbatch and the synthetic resin have the same physical properties, thereby facilitating mixing.
상기 항균 유성도료가 포함하는 유성도료로는 유성페인트, 유성에나멜, 알키드수지도료, 아미노알키드수지도료, 아크릴수지도료, 페놀수지도료, 에폭시수지도료, 불포화폴리에스테르수지도료, 폴리우레탄수지도료 등을 사용할 수 있으나, 본 발명이 이에 한정되는 것은 아니다.The oil paints included in the antimicrobial oil paints include oil paints, oil enamels, alkyd resins, amino alkyd resins, acrylic resins, phenol resins, epoxy resins, unsaturated polyester resins, polyurethane resins, and the like. Although it may be used, the present invention is not limited thereto.
상기 항균 플라스틱 및 항균 유성도료는 DCOIT가 미생물 세포 내의 탈수소효소를 파괴하는 작용과 트리클로산이 에노일-아실캐리어프로테인리덕테이즈의 활성을 저해하여 지방산 생성을 억제하는 작용을 통하여 높은 항균력을 가질 뿐만 아니라, 상기 DCOIT을 항균 플라스틱 전체 중량에 대하여 0.01 내지 5.0 중량%로 포함하고, 상기 트리클로산을 항균 플라스틱 전체 중량에 대하여 0.01 내지 5.0 중량%로 포함함으로써, DCOIT와 트리클로산이 상승 작용하여 기존 보다 적은 농도에서도 충분한 항균력을 나타낸다.The antimicrobial plastic and the antimicrobial oil paint have high antimicrobial activity through the action of DCOIT destroying dehydrogenase in microbial cells and the action of triclosan inhibiting the activity of the anoyl-acyl carrier protein reductase to inhibit fatty acid production. Including DCOIT in an amount of 0.01 to 5.0% by weight based on the total weight of the antimicrobial plastics, and incorporating the triclosan in an amount of 0.01 to 5.0% by weight, based on the total weight of the antimicrobial plastics, the DCOIT and triclosan are synergistic to be sufficient even at a lower concentration than before. It shows antibacterial activity.
모든 미생물은 적어도 한 가지 항균제에 내성을 나타내는 경우가 많다. 또한, 한 가지 항균제가 장시간 사용되면 반드시 내성을 갖는 변종이 나타나고, 이럴 경우 항균력은 급격히 감소되기 시작한다. 그러나, 상기 항균 플라스틱 및 항균 유성도료는 DCOIT와 트리클로산을 상기 함량 범위로 사용함으로써 이러한 문제점을 해결할 수 있다. 즉, 동시에 두 가지 항균제에 저항하는 변종의 발생은 극히 힘들 기 때문에, 상기 항균 플라스틱을 장기적으로 사용하는 경우에도 내성 발현의 염려가 매우 적다.All microorganisms are often resistant to at least one antimicrobial agent. In addition, when one antimicrobial agent is used for a long time, a strain with resistance necessarily appears, and in this case, the antimicrobial activity begins to decrease rapidly. However, the antimicrobial plastic and antimicrobial oil paint can solve this problem by using DCOIT and triclosan in the content range. That is, since the occurrence of strains that are resistant to two antimicrobial agents at the same time is extremely difficult, there is little concern about resistance expression even when using the antimicrobial plastic for a long time.
또한, 광범위한 항균성 확보는 항균 제품의 필수 요건이다. 상기 DCOIT는 주로 곰팡이와 조류에 강력한 항균력을 나타내며, 트리클로산은 주로 그램 양성균과 그램 음성균에 강력한 항균력을 나타낸다. 그러나, 특이한 곰팡이와 조류는 DCOIT보다 트리클로산에 의해 쉽게 사멸될 수 있고, 특이한 그램 양성균과 그램 음성균은 트리클로산 보다 DCOIT에 쉽게 사멸될 수 있다. 따라서, 상기 항균 플라스틱 및 항균 유성도료는 DCOIT와 트리클로산을 상기 함량 범위로 사용함으로써 보다 넓은 범위의 미생물을 사멸시키는 효과를 확보할 수 있다.In addition, securing a wide range of antimicrobial properties is an essential requirement for antimicrobial products. The DCOIT shows a strong antimicrobial activity mainly on fungi and algae, triclosan mainly shows a strong antimicrobial activity against gram positive and gram negative bacteria. However, unusual fungi and algae are more easily killed by triclosan than DCOIT, and unusual gram positive and gram negative bacteria are more easily killed by DCOIT than triclosan. Therefore, the antimicrobial plastic and the antimicrobial oil paint can secure the effect of killing a wider range of microorganisms by using DCOIT and triclosan in the content range.
항균 제품은 장기적인 항균력을 유지하여야 한다. 특히, 수분이 많이 존재하는 환경에서 장기적인 항균력을 유지하기 위해서는 항균 제품에 함유된 항균제의 용출이 극히 미약해야 가능하다. 수분이 많이 존재하는 환경에서 수용성의 항균제를 사용하면 항균제는 곧 용출되어 사라지게 된다. 그러나, DCOIT는 물에 대한 용해도가 상온에서 약 2ppm이며 트리클로산도 약 5 내지 10ppm으로 물에 잘 용해되지 않는다. 상기 항균 플라스틱 및 항균 유성도료는 상기 DCOIT와 트리클로산을 상기 함량으로 포함함으로써, 물기가 많은 환경에 사용되어도 오랜 시간 동안 항균력을 유지한다. Antimicrobial products should maintain long-term antimicrobial activity. In particular, in order to maintain the long-term antimicrobial activity in the environment where there is a lot of moisture, it is possible that the leaching of the antimicrobial agent contained in the antimicrobial product is extremely weak. If a water-soluble antimicrobial agent is used in an environment where there is a lot of water, the antimicrobial agent will soon elute and disappear. However, DCOIT has a solubility in water of about 2 ppm at room temperature and triclosan of about 5 to 10 ppm, so that it is insoluble in water. The antimicrobial plastic and the antimicrobial oil paint contain the DCOIT and triclosan in the above contents, thereby maintaining the antimicrobial activity for a long time even when used in a wet environment.
또한, 상기 항균 플라스틱 및 항균 유성도료는 DCOIT와 트리클로산을 상기 함량으로 포함함으로써, 지속적인 항균력과 더불어 뛰어난 안전성을 갖는다. 상기 DCOIT와 트리클로산 자체가 안전한 물질일 뿐만 아니라, 상기 함량 범위로 사용하 는 경우 인체에 유해성이 적다. 상기 DCOIT는 식품 포장에 사용될 수 있도록 미국 식품의약청(FDA)의 승인을 받은 항균제이고, 트리클로산은 일반적으로 치약, 화장품, 또는 피부 연고 등에 사용되는 의약부외품으로 인체에 비교적 안전한 항균제다.In addition, the antimicrobial plastics and the antimicrobial oil paint includes DCOIT and triclosan in the above contents, thereby having excellent antimicrobial activity and excellent safety. The DCOIT and triclosan itself are not only safe substances, but also less harmful to the human body when used in the content range. The DCOIT is an antimicrobial agent approved by the US Food and Drug Administration (FDA) for use in food packaging, and triclosan is a quasi-drug that is generally used in toothpaste, cosmetics, or skin ointment, and is a relatively safe antibacterial agent to the human body.
상기 항균 플라스틱은 다양한 형태로 성형되어, 항균 배수구, 항균 쓰레기통, 항균 에어콘 덕트, 항균 호스, 또는 항균 파이프 등으로 사용될 수 있으나, 본 발명이 이에 한정되는 것은 아니다.The antimicrobial plastic may be molded in various forms, and may be used as an antimicrobial drain, an antibacterial bin, an antibacterial air duct, an antibacterial hose, or an antibacterial pipe, but the present invention is not limited thereto.
상기 항균 플라스틱은 합성수지 원료와 DCOIT 및 트리클로산을 혼합한 후, 중합시켜 제조할 수 있고, 상기 항균 유성도료는 유성도료에 DCOIT 및 트리클로산을 첨가한 후 혼합시켜 제조할 수 있다. The antimicrobial plastics may be prepared by mixing synthetic resin raw materials with DCOIT and triclosan, followed by polymerization, and the antimicrobial oil paint may be prepared by adding DCOIT and triclosan to an oil paint.
또한, 상기 항균 플라스틱은 분쇄한 합성수지와 DCOIT 및 트리클로산을 반응용기에 넣고 60 내지 80℃에서 교반한 후, 펠렛 형상으로 항균 마스터배치를 제조하고, 상기 제조된 항균 마스터배치를 합성수지에 첨가한 후, 이를 성형하여 제조할 수 있다. 상기 성형 방법으로는 종래에 플라스틱의 성형 방법이면 어떤 것도 이용 가능하며, 압축 성형, 사출 성형, 압출 성형, 공기 취입 성형, 열 성형, 열 용융 성형, 발포 성형, 롤 성형, 또는 강화 플라스틱 성형 등을 이용할 수 있으나, 본 발명이 이에 한정되는 것은 아니다.In addition, the antimicrobial plastic is put into the reaction vessel and pulverized synthetic resin and DCOIT and triclosan and stirred at 60 to 80 ℃, to prepare an antimicrobial masterbatch in the form of pellets, after adding the prepared antimicrobial masterbatch to the synthetic resin, It can be produced by molding. As the molding method, any plastic molding method can be used, and compression molding, injection molding, extrusion molding, air blow molding, thermoforming, hot melt molding, foam molding, roll molding, or reinforced plastic molding may be used. Although it may be used, the present invention is not limited thereto.
상기 항균 마스터배치 제조시 DCOIT와 트리클로산의 함량 및 상기 합성수지에 항균 마스터배치를 첨가할 때 항균 마스터배치의 함량은 제조된 최종 항균 플라스틱에서의 DCOIT와 트리클로산의 함량이 각각 0.01 내지 5.0 중량%가 되도록 조절 할 수 있다.The content of DCOIT and triclosan in the preparation of the antimicrobial masterbatch and the content of the antimicrobial masterbatch when the antimicrobial masterbatch is added to the synthetic resin are controlled so that the content of DCOIT and triclosan in the final antimicrobial plastic is 0.01 to 5.0% by weight, respectively. can do.
상기 항균 플라스틱의 제조 방법에 따르면, 항균제를 마스터배치로 제조하여 혼합함으로써, 합성수지와의 혼합 및 취급이 용이하고, 먼지의 비산 문제가 없어 생산성을 향상시킨다. According to the manufacturing method of the antimicrobial plastics, by preparing and mixing the antimicrobial agent in a master batch, it is easy to mix and handle with the synthetic resin, there is no problem of scattering dust to improve the productivity.
이하 본 발명의 바람직한 실시예 및 비교예를 기재한다. 그러나 하기 실시예는 본 발명의 바람직한 일 실시예일 뿐 본 발명이 하기한 실시예에 의해 한정되는 것은 아니다.Hereinafter, preferred examples and comparative examples of the present invention are described. However, the following examples are only preferred embodiments of the present invention and the present invention is not limited to the following examples.
(항균 유성도료의 제조)(Production of antibacterial oil paint)
DCOIT, 트리클로산, 및 DCOIT와 트리클로산을 함께 사용한 항균도료의 항균력을 페이퍼 디스크(paper disk)법을 통하여 측정하였다. 이때, 균주는 그램 음성균인 대장균(Escherichia coli)을 사용하였다.The antimicrobial activity of DCOIT, Triclosan, and antimicrobial paints using DCOIT and Triclosan were measured by the paper disk method. At this time, the strain is Escherichia coli which is a gram negative bacteria coli ) was used.
(( 참고예Reference Example 1) One)
유성아크릴바인더 30 중량%, 자일렌 35 중량%, 톨루엔 34.5 중량%, 아크릴분산제 0.2 중량%, 점도조절제 0.1 중량%, 및 DCOIT 0.2 중량%를 혼합한 후 30분간 교반하여 항균 유성도료를 제조하였다. 상기 제조된 항균 유성도료를 페이퍼 디스크에 흡착시켰다. 한편, 영양 한천(nutrient agar, NA) 배지에 세균 배양액(100배 희석)을 첨가한 후, 2ml씩 배지에 접종하였다. 페이퍼 디스크를 영양 한천 배지에 올려놓은 후, 30℃ 배양기에서 3일 동안 배양하였다. 30 wt% of an oily acrylic binder, 35 wt% of xylene, 34.5 wt% of toluene, 0.2 wt% of an acrylic dispersant, 0.1 wt% of a viscosity modifier, and 0.2 wt% of DCOIT were mixed and stirred for 30 minutes to prepare an antimicrobial oil paint. The antimicrobial oil paint prepared above was adsorbed on a paper disk. Meanwhile, after adding a bacterial culture solution (100-fold dilution) to nutrient agar (NA) medium, 2ml each was inoculated into the medium. The paper disks were placed on nutrient agar medium and incubated in a 30 ° C. incubator for 3 days.
(( 참고예Reference Example 2) 2)
상기 참고예 1에서 DCOIT 대신에 트리클로산을 항균제 총 함량이 0.2 중량% 가 되도록 한 것을 제외하고는 참고예 1과 동일하게 실시하였다.Triclosan was replaced with DCOIT in Reference Example 1, except that the total content of the antimicrobial agent was 0.2% by weight.
(( 실시예Example 1) One)
상기 참고예 1에서 DCOIT를 0.1 중량%로 사용하고, 트리클로산을 0.1 중량%로 사용하여, 항균제의 총 함량이 0.2 중량%가 되도록 한 것을 제외하고는 참고예 1과 동일하게 실시하였다.In Reference Example 1, DCOIT was used at 0.1 wt%, and triclosan was used at 0.1 wt%, except that the total content of the antimicrobial agent was 0.2 wt%.
(항균 유성도료의 항균력 실험 결과)(Antimicrobial Activity Test Result of Antibacterial Oil Paint)
참고예 1, 참고예 2, 및 실시예 1에서 배양한 미생물의 성장 결과를 도 4 내지 6에 나타내었다. 도 4 내지 6을 참조하면, 실시예 1의 경우 참고예 1 및 2에 비하여 더 넓은 저지대가 형성되었음을 알 수 있다. 또한, 실시예 1의 경우 항균제의 총 함량이 0.2 중량%로 참고예 1 및 2의 항균제의 총 함량과 같으나, 참고예 1 및 2의 저지대 보다 더 넓은 저지대가 형성되었음을 알 수 있다. 즉, DCOIT와 트리클로산을 함께 사용하여 항균력이 증진되었음을 알 수 있다.The growth results of the microorganisms cultured in Reference Example 1, Reference Example 2, and Example 1 are shown in FIGS. 4 to 6. 4 to 6, it can be seen that in the case of Example 1, a wider low band was formed than in Reference Examples 1 and 2. In addition, in the case of Example 1, the total content of the antimicrobial agent is 0.2% by weight, which is the same as the total content of the antimicrobial agents of Reference Examples 1 and 2, but it can be seen that a lower zone is formed wider than that of Reference Examples 1 and 2. That is, it can be seen that the antimicrobial activity was enhanced by using DCOIT and triclosan together.
(항균 플라스틱의 제조)(Manufacture of antibacterial plastic)
(( 참고예Reference Example 3) 3)
분쇄한 ABS 수지, 및 DCOIT를 반응용기에 넣고 60℃의 온도로 혼합한 후, 펠렛 타입으로 성형하여 항균 마스터배치를 제조하였다. 상기 제조된 항균 마스터배치를 분쇄한 ABS 수지에 첨가하고, 상기 항균 마스터배치를 포함하는 ABS 수지를 사출성형하여 항균 플라스틱을 제조하였다. 이때, 상기 DCOIT의 함량은 항균 플라스틱 전체 중량에 대하여 0.3 중량%가 되도록 조절하였다.The crushed ABS resin and DCOIT were put in a reaction vessel and mixed at a temperature of 60 ° C., and then molded into pellets to prepare an antibacterial masterbatch. The prepared antimicrobial masterbatch was added to the crushed ABS resin, and the ABS resin including the antimicrobial masterbatch was injection molded to prepare an antimicrobial plastic. At this time, the content of the DCOIT was adjusted to 0.3% by weight relative to the total weight of the antibacterial plastic.
(( 참고예Reference Example 4) 4)
상기 참고예 3에서 항균제로 DCOIT 대신에 트리클로산을 사용한 것을 제외하고는 참고예 3과 동일하게 실시하여 항균 플라스틱을 제조하였다. 이때, 상기 트리클로산의 함량은 항균 플라스틱 전체 중량에 대하여 0.3 중량%가 되도록 조절하였다.An antimicrobial plastic was prepared in the same manner as in Reference Example 3 except that triclosan was used instead of DCOIT as the antimicrobial agent in Reference Example 3. At this time, the content of the triclosan was adjusted to 0.3% by weight relative to the total weight of the antibacterial plastic.
(( 실시예Example 2) 2)
상기 참고예 3에서 항균제로 DCOIT 및 트리클로산을 사용한 것을 제외하고는 참고예 3과 동일하게 실시하여 항균 플라스틱을 제조하였다. 이때, 상기 DCOIT의 함량은 항균 플라스틱 전체 중량에 대하여 0.1 중량%가 되도록 조절하였고, 상기 트리클로산의 함량은 항균 플라스틱 전체 중량에 대하여 0.1 중량%가 되도록 조절하였다.An antimicrobial plastic was prepared in the same manner as in Reference Example 3 except that DCOIT and triclosan were used as the antimicrobial agents in Reference Example 3. At this time, the content of the DCOIT was adjusted to 0.1% by weight relative to the total weight of the antimicrobial plastic, the content of the triclosan was adjusted to 0.1% by weight relative to the total weight of the antimicrobial plastic.
(항균 플라스틱의 항균력 실험 결과)(Antibacterial activity test result of antibacterial plastic)
상기 참고예 3, 참고예 4, 및 실시예 2에서 제조된 항균 플라스틱의 포도상구균(S. aureus), 대장균, 및 곰팡이(Asp . niger) 각각에 대한 항균력을 세균 저지대 형성 실험을 통하여 측정하였다.Reference Example 3, Reference Example 4, and Example 2 Staphylococcus aureus of the prepared antimicrobial plastic (S. aureus), Escherichia coli, and fungi (Asp. Niger) were measured through a low-lying areas to form the antimicrobial activity of each test bacteria in.
영양 한천 배지에 포도상구균 또는 대장균 배양액(100배 희석)을 첨가한 후, 2ml씩 배지에 접종하였다. 제조된 항균 플라스틱을 영양 한천 배지에 올려놓은 후, 30℃ 배양기에서 3일 동안 배양하였다. 곰팡이의 경우, 영양 한천 배지 대신에 감자 포도당 한천(potato dextrose agar, PDA) 배지를 사용한 것을 제외하고는 포도상구균 또는 대장균의 경우와 동일하게 실시하였다.Staphylococcus aureus or Escherichia coli culture (100-fold dilution) was added to the nutrient agar medium, and then 2 ml each was inoculated into the medium. The prepared antimicrobial plastics were placed on nutrient agar medium, and then cultured in a 30 ° C. incubator for 3 days. In the case of mold, the same procedure was performed as in the case of Staphylococcus aureus or Escherichia coli, except that potato agar (potato dextrose agar, PDA) medium was used instead of nutrient agar medium.
참고예 3의 세균 저지대 형성 실험 결과를 도 7 내지 9에 나타내었고, 참고 예 4의 세균 저지대 형성 실험 결과를 도 10 내지 12에 나타내었고, 실시예 2의 세균 저지대 형성 실험 결과를 도 13 내지 15에 나타내었다. The bacterial low zone formation test results of Reference Example 3 are shown in FIGS. 7 to 9, the bacterial low zone formation test results of Reference Example 4 are shown in FIGS. 10 to 12, and the bacterial low zone formation test results of Example 2 are shown in FIGS. 13 to 15. Shown in
도 7 내지 9를 참조하면, 참고예 3의 항균 플라스틱은 포도상구균과 곰팡이에 대하여는 항균력을 보이나 대장균에 대해서는 항균력을 전혀 나타내지 못함을 알 수 있다.7 to 9, the antimicrobial plastics of Reference Example 3 showed antibacterial activity against Staphylococcus aureus and mold, but did not show antibacterial activity against Escherichia coli.
도 10 내지 12를 참조하면, 참고예 4의 항균 플라스틱은 포도상구균과 대장균에 대하여는 항균력을 보이나 곰팡이에 대해서는 항균력을 전혀 나타내지 못함을 알 수 있다.10 to 12, it can be seen that the antimicrobial plastic of Reference Example 4 showed antibacterial activity against Staphylococcus aureus and Escherichia coli but no antibacterial activity against mold.
도 13 내지 15를 참조하면, 실시예 2의 항균 플라스틱은 전체 항균제의 함량이 참고예 3 및 참고예 4 보다 적었음에도 불구하고, 모든 세균과 곰팡이에 고른 항균력을 보였음을 알 수 있다. 즉, DCOIT와 트리클로산을 혼합 사용함으로써, 보다 적은 양의 항균제로 보다 넓은 범위의 미생물에 대한 강력한 항균력을 확보할 수 있었다.13 to 15, the antimicrobial plastics of Example 2 showed even antibacterial activity against all bacteria and molds, although the total antimicrobial content was less than Reference Examples 3 and 4. That is, by using a mixture of DCOIT and triclosan, it was possible to secure a strong antimicrobial activity against a wide range of microorganisms with a smaller amount of antimicrobial agent.
본 발명의 단순한 변형 또는 변경은 모두 이 분야의 통상의 지식을 가진 자에 의하여 용이하게 실시될 수 있으며 이러한 변형이나 변경은 모두 본 발명의 영역에 포함되는 것으로 볼 수 있다.All simple modifications or changes of the present invention can be easily carried out by those skilled in the art, and all such modifications or changes can be seen to be included in the scope of the present invention.
도 1은 DCOIT가 맥주효모균의 세포벽에 흡수되는 양을 시간에 따라 나타낸 그래프.1 is a graph showing the amount of DCOIT absorbed to the cell wall of brewer's yeast over time.
도 2는 DCOIT 투입 후 대장균의 산소 호흡이 억제되는 정도를 나타내는 그래프.Figure 2 is a graph showing the extent to which oxygen breathing of E. coli is suppressed after DCOIT.
도 3은 알코올 탈수소효소에 DCOIT를 투입한 후 그 활성의 변화를 나타내는 그래프.Figure 3 is a graph showing the change in activity after injecting DCOIT to alcohol dehydrogenase.
도 4는 참고예 1에서 배양한 미생물의 성장 결과를 나타내는 사진.Figure 4 is a photograph showing the growth results of the microorganisms cultured in Reference Example 1.
도 5는 참고예 2에서 배양한 미생물의 성장 결과를 나타내는 사진.5 is a photograph showing growth results of microorganisms cultured in Reference Example 2. FIG.
도 6은 실시예 1에서 배양한 미생물의 성장 결과를 나타내는 사진.Figure 6 is a photograph showing the growth results of the microorganisms cultured in Example 1.
도 7 내지 9는 참고예 3에서 제조된 항균 플라스틱의 포도상구균, 대장균, 및 곰팡이에 대한 세균 저지대 형성 실험 결과를 나타내는 사진.7 to 9 are photographs showing the bacterial low zone formation test results for Staphylococcus aureus, Escherichia coli, and mold of the antibacterial plastic prepared in Reference Example 3.
도 10 내지 12는 참고예 4에서 제조된 항균 플라스틱의 포도상구균, 대장균, 및 곰팡이에 대한 세균 저지대 형성 실험 결과를 나타내는 사진.10 to 12 are photographs showing the bacterial low zone formation test results for Staphylococcus aureus, Escherichia coli, and mold of the antibacterial plastic prepared in Reference Example 4.
도 13 내지 15는 실시예 2에서 제조된 항균 플라스틱의 포도상구균, 대장균, 및 곰팡이에 대한 세균 저지대 형성 실험 결과를 나타내는 사진.Figures 13 to 15 are photographs showing the bacterial low zone formation test results for Staphylococcus aureus, Escherichia coli, and mold of the antibacterial plastic prepared in Example 2.
Claims (3)