KR100978296B1 - Cover for protecting pile in water and method for mounting it on the pile - Google Patents
Cover for protecting pile in water and method for mounting it on the pile Download PDFInfo
- Publication number
- KR100978296B1 KR100978296B1 KR1020100025110A KR20100025110A KR100978296B1 KR 100978296 B1 KR100978296 B1 KR 100978296B1 KR 1020100025110 A KR1020100025110 A KR 1020100025110A KR 20100025110 A KR20100025110 A KR 20100025110A KR 100978296 B1 KR100978296 B1 KR 100978296B1
- Authority
- KR
- South Korea
- Prior art keywords
- protective cover
- underwater
- layer
- pile
- cover
- Prior art date
Abstract
Description
본 발명은 하천 또는 해상 구조물을 지지하는 수중파일의 둘레에 설치되어 수중파일의 부식 등을 방지하는 보호커버에 관한 것이다.The present invention relates to a protective cover installed around the underwater pile supporting the river or offshore structure to prevent corrosion of the underwater pile.
일반적으로 하천 또는 해상에 설치된 구조물을 지지하기 위하여 구조물 하부에는 강관 파일 또는 콘크리트 말뚝으로 이루어진 기둥 등(이하 '수중파일'로 통칭하여 기술함)이 설치된다.In general, in order to support a structure installed on a river or at sea, a lower portion of the structure is provided with a steel pipe pile or a pillar made of concrete piles (hereinafter referred to as 'underwater pile').
수중파일은 물에 항상 잠겨 있거나 반복적으로 물에 접촉되면서 어느 정도 시간이 지나면 부식 또는 열화되어 강도가 약해지게 되는데, 이를 방지하거나 보강하기 위해 수중파일에 보호 구조물을 설치하게 된다.Underwater piles are always immersed in water or repeatedly contacted with water, which, after a certain time, deteriorates in strength due to corrosion or deterioration. To prevent or reinforce, a protective structure is installed in the pile.
또한 수중파일을 바다에 설치한 경우에, 수상 부분 또는 썰물 최저점에서 수중1m까지 부분에 부식이 심하게 발생하게 되므로, 수중파일 시공 초기부터 파일 둘레에 보호 구조물을 설치하여 반영구적인 보호하기도 한다.In addition, when the underwater pile is installed in the sea, corrosion is severely generated in the water part or the bottom of the low tide to 1m in the water, so the protection structure is installed around the pile from the beginning of the underwater pile construction to protect it permanently.
이러한 보호 구조물 중에는 수중파일 둘레에 감싸듯이 설치되는 수중파일 보호커버가 있다.Among these protective structures is an underwater pile protective cover installed as if wrapped around the underwater pile.
종래 수중파일 보호커버 설치 방법은, 수중파일 둘레에 페트로레이텀 테이프를 감고, 그 위에 PVC테이프를 감은 다음, 섬유복합체 등으로 이루어진 보호커버를 씌우는 공정으로 진행된다.Conventional underwater file protective cover installation method, the petrolatum tape wrapped around the underwater file, PVC tape is wound thereon, and then proceeds to the process of covering the protective cover made of a fiber composite or the like.
그러나, 상기한 바와 같은 종래 수중파일 보호커버 및 이를 이용한 시공 방법은, 테이프를 감은 후에 보호커버를 설치하기 때문에 공정이 복잡하여, 시공성이 떨어짐은 물론 시공비용이 많이 들어 경제성도 떨어지는 문제점이 발생되고 있다.However, the conventional underwater pile protective cover as described above and the construction method using the same, because the protective cover is installed after winding the tape, the process is complicated, the construction is poor, as well as the construction cost is high, there is a problem that the economic efficiency is also lowered have.
또한, 종래에는 수중파일 둘레에 페트로레이텀 테이프, PVC 테이프 등을 감은 다음, 그 위에 보호커버를 씌우기 때문에 테이프층과 보호커버 간의 공극으로 인해 보호커버 내부로 수분(특히 해수)이 유입되면 페트로레이텀 컴파운드가 손실되어 수중파일 보호 유지 기능이 현저히 떨어지는 문제점도 있다.In addition, conventionally, by wrapping a petrolatum tape, PVC tape, etc. around the underwater pile, and then put a protective cover thereon, when water (especially seawater) flows into the protective cover due to the gap between the tape layer and the protective cover, petroleum There is also a problem that the loss of the term compound, which greatly reduces the underwater file protection function.
또한, 종래에는 단순히 섬유복합체로 이루어진 보호커버를 씌우는 방식으로 이루어지기 때문에 전체적으로 보호커버가 수중파일에 밀착되는 밀착력이 떨어지고, 또 이물질에 의해 보호커버에 충격이 가해질 경우에 쉽게 파손되는 등의 문제가 발생되어, 전체적으로 수중파일 보호 기능이 떨어질 뿐만 아니라 설치 공사비 외에 부수적인 유지 보수비의 증가 및 지속적인 관리의 어려움이 따르는 문제점이 발생되고 있다.
In addition, conventionally, since the protective cover made of a fiber composite is simply covered, the overall adhesion of the protective cover to the underwater pile is inferior, and a problem such as being easily broken when an impact is applied to the protective cover by foreign matters. As a result, there is a problem that not only the protection function of the underwater file as a whole decreases, but also the additional maintenance cost and the difficulty of continuous management in addition to the installation construction cost.
이상 설명한 배경기술의 내용은 이 건 출원의 발명자가 본 발명의 도출을 위해 보유하고 있었거나, 본 발명의 도출 과정에서 습득한 기술 정보로서, 반드시 본 발명의 출원 전에 일반 공중에게 공개된 공지기술이라 할 수는 없다.The contents of the background art described above are technical information possessed by the inventor of the present application for the derivation of the present invention or acquired in the derivation process of the present invention, and are known technologies disclosed to the general public before the application of the present invention. You can't.
본 발명은 상기한 문제점을 해결하기 위하여 안출된 것으로서, 보호커버에 페트로레이텀컴파운드층을 일체로 구성함과 아울러 EPDM발포고무시트층과 같은 탄성층을 구비함으로써 보호커버 설치 시공이 용이하고, 수중파일에 밀착된 상태를 안정적으로 장시간 유지할 수 있도록 하여, 시공성, 신뢰성, 경제성 향상에 기여할 수 있는 수중파일 보호커버 및 이를 이용한 수중파일 보호 시공방법을 제공하는 데 목적이 있다.The present invention has been made to solve the above problems, the protective cover is integrally formed with a petrolatum compound layer and provided with an elastic layer, such as EPDM foam rubber sheet layer is easy to install the protective cover, underwater It is an object of the present invention to provide an underwater file protective cover and a method of protecting the underwater file using the same, which can contribute to improving workability, reliability, and economic efficiency by maintaining a state in close contact with the file for a long time stably.
또한 본 발명은, 보호커버 내에 탄성층을 일체로 구비함으로써 외력에 의해 파손되지 않도록 하여 전체적으로 강성을 증대시킬 수 있고, 또한 페트로레이텀컴파운드층이 수중파일의 표면에 완전히 밀착되도록 하여, 수중파일 부식 방식 효과를 높이는 동시에 수분 유입을 최소화함으로써 보호커버의 기능성 및 신뢰성 향상에 기여할 수 있는 수중파일 보호커버 및 이를 이용한 수중파일 보호 시공방법을 제공하는 데 목적이 있다.In addition, according to the present invention, by providing the protective cover integrally with the elastic layer, the rigidity of the protective cover can be prevented from being damaged by external force, thereby increasing the overall rigidity. The purpose of the present invention is to provide an underwater file protective cover and a method of protecting the underwater file using the same, which can contribute to improving the functionality and reliability of the protective cover by minimizing moisture influx while minimizing moisture influx.
또한 본 발명은, 보호커버의 상단부와 하단부에 수분배출겸 수분유입방지부를 구성하여, 보호커버 내로 수분이 유입되지 않도록 하고, 특히 보호커버 설치 시공시, 보호커버 내의 탄성층 압착시킬 때 보호커버의 가운데 부분으로부터 양쪽(상하) 방향으로 점차적으로 수분을 밀어내듯이 배출시키는 방법으로 시공함으로써, 별도의 수분 배출 장비를 사용하지 않고도 간편하게 수분을 배출하면서 보호커버를 신뢰성 있게 설치할 수 있는 수중파일 보호커버 및 이를 이용한 수중파일 보호 시공방법을 제공하는 데 목적이 있다.
In addition, the present invention comprises a moisture discharge and moisture inflow prevention portion at the upper and lower ends of the protective cover, so that moisture does not flow into the protective cover, especially when the protective cover is installed, the compression of the elastic layer in the protective cover of the protective cover Underwater pile protective cover that can be installed reliably while discharging moisture without using a separate moisture discharging equipment by constructing it by discharging it gradually like pushing water in both (up and down) directions from the center part. The purpose is to provide a construction method for protecting underwater files.
상기한 과제를 실현하기 위한 본 발명에 따른 수중파일 보호커버는, 수중파일 둘레에 밀착되는 커버 본체부와, 상기 커버 본체부의 양단부에 구비되어 체결 부재에 의해 상호 연결되는 양측 플랜지부와, 상기 커버 본체부의 상단부와 하단부에 구비되어 수분을 배출하면서 수분이 유입되는 것은 차단하는 수분배출겸 수분유입방지부를 포함하고; 상기 커버 본체부는, 바깥쪽으로부터 외피층을 구성하는 유리섬유강화플라스틱층, 압착 탄성력을 제공하는 EPDM발포고무시트층, 수중파일의 표면에 밀착되는 페트로레이텀컴파운드층 순으로 일체로 구성된 것을 특징으로 한다.Underwater pile protection cover according to the present invention for realizing the above object is, the cover body portion in close contact with the underwater pile, the both side flange portions provided on both ends of the cover body portion and interconnected by a fastening member, the cover It is provided in the upper end and the lower end of the main body portion while the moisture is discharged to include a water discharge and moisture inflow prevention block to block; The cover body portion is composed of a glass fiber-reinforced plastic layer constituting the outer skin layer from the outside, an EPDM foam rubber sheet layer providing a compression elastic force, a petrolatum compound layer in close contact with the surface of the underwater pile. .
상기 커버 본체부는 페트로레이텀컴파운드층을 보호하면서도 용이하게 벗겨낼 수 있는 보호시트를 더 포함되어 구성될 수 있다.The cover body portion may further include a protective sheet that can be easily peeled off while protecting the petrolatum compound layer.
상기 보호커버는, 보호커버를 성형하는 몰드에 유리섬유크로스를 펴고, 여기에 경화제와 촉진제가 혼합된 수지를 기포가 발생되지 않도록 일정 두께로 적층하여 유리섬유강화플라스틱층을 형성하고,The protective cover is formed by spreading the glass fiber cross on a mold for forming the protective cover, and laminating a resin mixed with a curing agent and an accelerator to a predetermined thickness so as not to generate bubbles to form a glass fiber reinforced plastic layer,
상기 유리섬유강화플라스틱층 위에 접착제를 도포한 후에, 별도로 제작된 EPDM발포고무시트를 적층하여 EPDM발포고무시트층을 형성하고,After applying the adhesive on the glass fiber reinforced plastic layer, the EPDM foam rubber sheet produced separately is laminated to form an EPDM foam rubber sheet layer,
상기 EPDM발포고무시트층 위에 부직포를 적층한 다음, 페트로레이텀컴파운드를 함침시켜 페트로레이텀컴파운드층을 형성하는 과정으로, 유리섬유강화플라스틱층, EPDM발포고무시트층, 페트로레이텀컴파운드층을 일체화시켜 제작한 것이 바람직하다.Laminating the nonwoven fabric on the EPDM foam rubber sheet layer, and then impregnating the petrolatum compound to form a petrolatum compound layer, the glass fiber reinforced plastic layer, EPDM foam sheet, petrolatum compound layer is integrated It is preferable to make it.
상기한 과제를 실현하기 위한 본 발명에 따른 수중파일 보호커버를 이용한 수중파일 보호 시공방법은, 상기한 보호커버를 이용하여 수중파일 보호 시공방법으로서, 수중파일의 둘레에 상기 보호커버를 감듯이 밀착시키고, 양쪽 플랜지부를 상호 맞댄 상태에서, 클램프를 이용하여 양쪽 플랜지부를 밀착시키는 제1단계와; 제1단계 후에, 체결 부재를 양쪽 플랜지부의 가운데 부분부터 상측 방향과 하측 방향으로 차례로 체결하여, 보호커버와 수중파일 사이에 남아있는 수분을 가운데 부분으로부터 상측과 하측으로 점차적으로 밀어내면서 보호커버 바깥쪽으로 배출시키는 제2단계를 포함한 것을 특징으로 한다.Underwater file protection construction method using the underwater file protection cover according to the present invention for realizing the above problems, as the underwater file protection construction method using the above-mentioned protection cover, close to the protective cover around the underwater file A first step of bringing the two flange parts into close contact with each other by using the clamps; After the first step, the fastening member is fastened sequentially from the center of both flange portions in an upward direction and a downward direction, and gradually pushes moisture remaining between the protective cover and the underwater pile from the middle portion to the upper side and the lower side, and then outside the protective cover. It characterized in that it comprises a second step to discharge toward.
상기 제1단계에서 이용되는 클램프는, 상기 양쪽 플랜지부를 압착시키는 압착판에 구비된 압착면이 상호 마주하는 방향으로 만곡된 형상으로 돌출되게 형성되어, 클램프 작동시에 양쪽 플랜지부의 가운데 부분을 먼저 밀착시키고, 이후 가운데 부분을 중심으로 상측 부분과 하측 부분 방향으로 다른 부분들을 점차적으로 밀착시킬 수 있도록 구성되는 것이 바람직하다.The clamp used in the first step is formed so as to protrude in a curved shape in the direction in which the pressing surfaces provided on the pressing plate for pressing the two flange parts in a mutually opposite direction, the center portion of both flanges during the clamp operation It is preferably configured to be in close contact with each other, and then gradually close to other parts in the direction of the upper part and the lower part about the center part.
상기 제2단계에서, 양쪽 플랜지부에 체결 부재를 체결할 때, 체결 부재의 조임 강도는 상기 보호커버의 EPDM발포고무시트층의 수축률이 60~70% 정도가 되도록 하는 것이 바람직하다.
In the second step, when fastening the fastening member on both flanges, the tightening strength of the fastening member is preferably such that the shrinkage of the EPDM foam rubber sheet layer of the protective cover is about 60 ~ 70%.
상기한 바와 같은 본 발명의 주요한 과제 해결 수단들은, 아래에서 설명될 '발명의 실시를 위한 구체적인 내용', 또는 첨부된 '도면' 등의 예시를 통해 보다 구체적이고 명확하게 설명될 것이며, 이때 상기한 바와 같은 주요한 과제 해결 수단 외에도, 본 발명에 따른 다양한 과제 해결 수단들이 추가로 제시되어 설명될 것이다.The main problem solving means of the present invention as described above, will be described in more detail and clearly through examples such as 'details for the implementation of the invention', or the accompanying 'drawings' to be described below, wherein In addition to the main problem solving means as described above, various problem solving means according to the present invention will be further presented and described.
본 발명에 따른 수중파일 보호커버 및 이를 이용한 수중파일 보호 시공방법은 다음과 같은 효과를 갖는다.Underwater file protection cover according to the present invention and a method for constructing the underwater file protection using the same has the following effects.
본 발명은, 커버 본체부가 외피층, 탄성층, 부식방지층, 보호시트의 4층 구조로 구성됨에 따라, 수중파일에 보호커버를 두른 상태에서 클램프로 양쪽 플랜지부를 압착한 다음, 체결부재로 체결하는 작업으로 수중파일 보호커버 설치 작업을 완료할 수 있으므로, 시공이 간편하고 공사단가를 줄여, 작업성 및 경제성을 향상시킬 수 있는 효과가 있다.According to the present invention, the cover body is composed of a four-layer structure of an outer layer, an elastic layer, an anti-corrosion layer, and a protective sheet, so that both flange portions are crimped with a clamp in a state in which a protective cover is attached to an underwater pile, and then fastened with a fastening member. Since the installation of the underwater file protective cover can be completed by the work, the construction is simple and the construction cost is reduced, thereby improving the workability and economic efficiency.
또한, 본 발명은 단일 보호커버로 일체로 구성되므로, 외피층과 페트로레이텀테이프층 사이의 공극이 존재하지 않아, 종래 시공의 문제점이었던 보호커버층과 방식테이프층 사이의 공극으로 인해 수분이 유입되어 페트로레이텀컴파운드 물질이 수중에서 씻겨 나가는 문제를 해결하여, 장시간 수중파일을 안정적으로 보호할 수 있으며, 또한 종래 시행되었던 PVC테이프 감기 공정을 생략하여 PVC테이프 공정으로 인하여 발생하였던 재료비 및 공사비를 절감함은 물론 작업성 향상을 도모하는 효과도 있다.In addition, since the present invention is integrally formed with a single protective cover, there is no gap between the outer cover layer and the petrolatum tape layer, and moisture is introduced due to the gap between the protective cover layer and the anticorrosive tape layer, which was a problem of the conventional construction. It solves the problem that petrolatum compound material is washed out in the water, and can protect the underwater pile for a long time stably, and also saves the material cost and construction cost caused by the PVC tape process by omitting the conventional PVC tape winding process. Of course, it also has the effect of improving workability.
또한, 본 발명은 보호커버의 중간층(탄성층)인 EPDM발포고무층이 130~250% 정도 발포되어 연성 및 탄성을 가짐에 따라 보호커버를 수중파일에 밀착시켜 장착할 때, EPDM발포고무층이 60~70% 정도 수축하여 표면이 고르지 못한 수중파일도 공차 없이 보호커버를 설치할 수 있게 되어 보호커버 설치 효율성을 높일 수 있는 효과가 있다.In addition, according to the present invention, when the EPDM foam rubber layer, which is an intermediate layer (elastic layer) of the protective cover, is foamed about 130 to 250% and has ductility and elasticity, when the protective cover is attached to the underwater pile, the EPDM foam rubber layer is 60 to 60%. By shrinking about 70%, even the uneven surface of the pile can be installed protective cover without tolerance, thereby increasing the efficiency of the protective cover installation.
또한, 종래에는 보호커버가 강성만을 가져 큰 충격이 가해질 경우에 보호커버가 깨지는 등 손상되어 수분이 유입되는 문제가 있었으나, 본 발명은, 중간에 EPDM발포고무로 이루어진 탄성층을 구비함으로써, 태풍이나 파도에 의해 밀려온 이물질 등이 보호커버에 충격을 주더라도 EPDM발포고무층이 이를 흡수하여 보호 커버 설치 후 오랜 시간 안정적으로 보호커버 기능을 수행할 수 있는 효과가 있다.In addition, in the related art, the protective cover has only a rigidity, and the protective cover is damaged when a large impact is applied, such that the protective cover is broken and water is introduced therein. Even if foreign matters pushed by the waves impact the protective cover, the EPDM foam rubber layer absorbs it, so that the protective cover function can be stably performed for a long time after the protective cover is installed.
또한, 본 발명은, 수중파일 둘레에 보호커버를 설치할 때, EPDM발포고무시트층이 60~70% 정도 수축하면서 수중파일에 압착하게 됨에 따라 부착강도가 현저히 높아지고, 이에 따라 보호커버가 아래로 흘러내릴 우려가 없이 초기 장착 상태를 장시간 그대로 유지할 수 있는 효과가 있다. 이로 인하여 종래 스토퍼 설치로 인해 그 스토퍼가 부식되어 박리되었을 때, 보호커버가 아래로 흘러내리는 문제점을 해결함과 아울러 스토퍼 설치 공정을 생략으로 재료비 및 공사비용 등을 절감할 수 있는 효과가 있다.In addition, the present invention, when the protective cover is installed around the underwater pile, as the EPDM foam rubber sheet layer shrinks about 60-70% and compresses to the underwater pile, the adhesion strength is significantly increased, and thus the protective cover flows downward. There is an effect that can maintain the initial mounting state for a long time without fear of falling. Therefore, when the stopper is corroded and peeled off due to the installation of the conventional stopper, the protection cover flows down and the material stops the construction cost by eliminating the stopper installation process.
또한, 본 발명은, 외피층을 특수 수지와 부직포로 이루어진 유리섬유강화플라스틱층으로 구성함으로써 외력에 의해 쉽게 깨지지 않게 되어 전체적으로 보호커버의 강성을 증대시킬 수 있는 효과가 있다.In addition, the present invention, the outer layer is composed of a glass fiber reinforced plastic layer made of a special resin and non-woven fabric is not easily broken by the external force has the effect of increasing the overall rigidity of the protective cover.
또한, 본 발명은, 보호커버의 상단부와 하단부에 수분배출겸 수분유입방지부를 구비함으로써, 수분이 보호커버와 수중파일 사이로 유입되지 않도록 하여 보호커버의 기능성을 향상시킬 수 있는 효과가 있다.In addition, the present invention, by providing a water discharge and moisture inflow prevention portion at the upper end and the lower end of the protective cover, there is an effect that can prevent moisture from flowing between the protective cover and the underwater pile to improve the functionality of the protective cover.
또한, 본 발명은, 보호커버의 플랜지부를 연결할 때, 클램프를 이용하여 양쪽 플랜지부를 가운데 부분에서부터 강하게 밀착시키면서 점점 상측과 하측 방향으로 밀착시킨 상태에서 볼트를 체결함으로써 수중 공사시에도 보호커버와 수중파일 사이에 남아있는 수분을 보다 확실하게 제거하여, 잔량의 수분에 의해 수중파일이 부식되는 등의 문제점을 해결할 수 있고, 이에 따라 수중파일 설치 작업의 편의성 및 신뢰성을 높일 수 있는 효과가 있다.
In addition, the present invention, when connecting the flange portion of the protective cover, by tightening the bolt in a state in which the both sides of the flange portion in close contact with the upper and lower directions while using a clamp to strongly adhere from the center portion and the protective cover even during underwater construction By removing the water remaining between the underwater piles more reliably, it is possible to solve problems such as corrosion of the underwater pile by the residual amount of water, thereby improving the convenience and reliability of the underwater pile installation work.
도 1은 본 발명의 일 실시예에 따른 수중파일 보호커버가 도시된 사시도,
도 2는 도 1의 종방향 단면도,
도 3은 도 1의 횡방향 단면도,
도 4는 본 발명에 따른 수중파일 보호커버를 이용한 수중파일 보호 시공방법에 사용되는 클램프가 도시된 사시도,
도 5는 본 발명의 일 실시예에 따른 수중파일 보호커버가 수중파일에 설치되어 있는 상태를 보인 개략적인 사시도,
도 6은 본 발명의 일 실시예에 따른 수중파일 보호커버가 수중파일에 설치되어 있는 상태를 보인 단면도이다.1 is a perspective view of the underwater file protective cover according to an embodiment of the present invention,
2 is a longitudinal cross-sectional view of FIG. 1;
3 is a cross sectional view of FIG. 1;
Figure 4 is a perspective view of the clamp used in the underwater file protection construction method using the underwater file protective cover according to the present invention,
Figure 5 is a schematic perspective view showing a state in which the underwater file protection cover is installed in the underwater file according to an embodiment of the present invention,
6 is a cross-sectional view showing a state that the underwater file protective cover is installed in the underwater file according to an embodiment of the present invention.
첨부된 도면을 참조하여 본 발명의 바람직한 실시 예를 설명하면 다음과 같다.Hereinafter, exemplary embodiments of the present invention will be described with reference to the accompanying drawings.
도 1 내지 도 3은 본 발명의 일 실시예에 따른 수중파일 보호커버가 도시된 사시도, 종단면도, 횡단면도이다.1 to 3 is a perspective view, a longitudinal cross-sectional view, a cross-sectional view showing an underwater pile protective cover according to an embodiment of the present invention.
이들 도면을 참고하면, 본 발명의 일 실시예에 따른 수중파일 보호커버(10)는, 도 5에 도시된 바와 같이 수중파일(100)의 둘레에 밀착된 상태로 설치되는데, 이를 위해 크게 수중파일(100) 둘레에 밀착되는 커버 본체부(11)와, 이 커버 본체부(11)의 양단부에 구비되어 체결 부재(21, 22)에 의해 상호 연결되는 양측 플랜지부(17)와, 커버 본체부(11)의 상단부와 하단부에 구비되는 수분배출겸 수분유입방지부(19)로 이루어진다.Referring to these drawings, the underwater file
이렇게 구성되는 수중파일 보호커버(10)(이하 '보호커버'라고도 함)에 대하여, 각 구성을 중심으로 상세히 설명한다.The underwater file protective cover 10 (hereinafter also referred to as "protective cover") configured as described above will be described in detail with a focus on each component.
먼저, 커버 본체부(11)는, 도 2와 도 3을 참조하면, 바깥쪽 면으로부터 외피층(12 참조), 탄성층(13 참조), 부식방지층(14 참조), 보호시트(15) 등 총 4개의 층으로 구성될 수 있는데, 여기서 외피층은 유리섬유강화플라스틱층(12)으로, 탄성층은 EPDM발포고무시트층(13)으로, 부식방지층은 페트로레이텀컴파운드층(14)으로 이루어지는 것이 바람직하다. 여기서 커버 본체부(11)를 구성하는 층들은 반드시 상기 재질로 이루어진 층으로만 한정되는 것은 아니고 동일한 기능을 수행하는 다른 재질로 하나 이상의 층을 대체하여 구성하는 것이 가능함은 물론이다.First, referring to FIGS. 2 and 3, the cover
이하 외피층, 탄성층, 부식방지층을 유리섬유강화플라스틱층(12), EPDM발포고무시트층(13), 페트로레이텀컴파운드층(14)으로 구성된 것을 중심으로 설명한다. Hereinafter, the outer skin layer, the elastic layer, and the anti-corrosion layer will be described based on the glass fiber reinforced
상기 유리섬유강화플라스틱층(12)은 보호커버(10)의 가장 바깥쪽에 위치된 것으로서, 경량성, 내식성, 내충격성 높아지도록 유리섬유 부직포와 특수수지를 이용하여 제작되는 것이 바람직하며, 전체적인 두께는 2~4mm 정도로 구성하는 것이 바람직하다.The glass fiber reinforced
상기 EPDM발포고무시트층(13)은 상기 유리섬유강화플라스틱층(12) 안쪽면에 구성된 것으로서, EPDM(ethylene propylene diene M-class)고무를 130~250% 정도, 바람직하게는 130~180% 정도 발포시켜 구성하는 것이 가능하다.The
이러한 EPDM발포고무시트층(13)은 보호커버(10)를 수중파일(100)의 둘레에 감을 때, 두께가 60~70% 정도 수축되면서 그 내측의 페트로레이텀컴파운드층(14)이 수중파일(100) 둘레에 완전히 밀착될 수 있도록 탄성을 제공하는 기능을 하게 된다. 즉, 보호커버(10)가 수중파일(100)의 둘레에 설치될 때, EPDM발포고무시트층(13)이 압축되면서 페트로레이텀컴파운드층(14)을 압박함으로써 수중파일(100)의 표면과 페트로레이텀컴파운드층(14) 사이의 공간을 최소화 할 수 있게 된다. 따라서 EPDM발포고무시트층(13)에 의해 수중파일(100)의 불균일한 면까지도 압착하게 됨에 따라, 전체적으로 보호커버(10)가 수중파일(100)의 둘레에 안정적이면서도 완전히 밀착된 상태를 유지할 수 있게 되고, 또한 외력에 의해 보호커버(10)에 충격이 가해지더라도 EPDM발포고무시트층(13)이 완충작용을 하여 보호커버(10)의 손상을 방지하는 기능을 하게 된다.When the EPDM foam
상기 페트로레이텀컴파운드층(14)은, 상기 EPDM발포고무시트층(13) 안쪽면에 구성된 것으로서, 흡수률이 50% 이상인 부직포에 페트로레이텀컴파운드를 함침하여 구성하는 것이 바람직하다. The
이러한 페트로레이텀컴파운드층(14)은 부직포에 페트로레이텀컴파운드를 함침하여 구성함으로써 장시간 내구성이 유지됨과 아울러, 페트로레이텀컴파운드에 부식억제제, 수분박리제, 미생물서식억제제 등이 첨가되어 있으므로 수중파일(100)의 부식 등 손상을 방지할 수 있게 된다.The
상기 보호시트(15)는 상기 페트로레이텀컴파운드층(14)의 안쪽면에 부착된 것으로서, 보호커버(10)를 수중파일(100)에 설치하기 전에 페트로레이텀컴파운드 성분이 손실되는 것을 방지하는 기능을 하게 된다.The
이러한 보호시트(15)는 페트로레이텀컴파운드층(14)을 보호하면서도 간편하게 벗겨낼 수 있도록 필름 또는 이형지로 구성되는 것이 바람직하다.The
다음, 상기 양쪽 플랜지부(17)는, 상기 커버 본체부(11)의 양쪽에 일체로 각각 구비되어 커버 본체부(11)가 수중파일(100)의 둘레에 감싸도록 설치된 상태에서 커버 본체부(11)를 통형 구조로 상호 연결하여 고정하는 부분으로서, 볼트(21) 등 체결 부재(21, 22)에 의해 상호 밀착되어 연결될 수 있도록 구성된다.Next, the both
이러한 양쪽 플랜지부(17)는 커버 본체부(11)의 유리섬유강화플라스틱층(12)의 1.5배 정도의 두께로 구성되는 것이 바람직하며, 커버 본체부(11)의 접선에 대하여 밀착면의 각도(θ)가 대략 80~89ㅀ정도가 되도록 형성하는 것이 바람직하다(도 3 참조).Both
여기서, 플랜지부(17)를 형성할 때, 유리섬유강화플라스틱층(12)의 1.5배 정도의 두께로 형성하는 이유는, 양쪽 플랜지부(17)를 상호 고정할 때, 플랜지부(17)의 진직도 및 80~89ㅀ의 형성 각도 등을 그대로 유지함으로 양쪽 플랜지부가 정밀하게 밀착되고, 아울러, 볼트(21) 체결 과정 또는 체결 후에 찢어지는 등의 문제를 방지하기 위해서이다.Here, when forming the
또한, 양쪽 플랜지부(17)의 각도를 80~89ㅀ가 되도록 형성하는 이유는, 플랜지부의 각도를 90ㅀ 이상(둔각)으로 형성하게 되면, 볼팅 체결시에 양쪽 플랜지부가 90ㅀ이상으로 휘어져서 완전히 밀착되지 않을 수 있고, 이로 인하여 볼트 체결의 어려움이 발생할 수 있으며, 또한 정밀시공이 되지 않아 하자요인이 되는 문제 등을 방지하기 위해서이다. 이와 함께 양쪽 플랜지부(17)가 보호커버의 바깥쪽 방향으로 벌어지도록 형성함으로써 볼트 체결시에 벌어져 있던 양쪽 플랜지가 서로 밀착되면서 보호 커버의 내측 방향으로 압착력을 제공할 수 있도록 하기 위한 것이다.Further, the reason for forming the angle of both
이와 같은 양쪽 플랜지부(17)는 상기 커버 본체부(11)의 유리섬유강화플라스틱층(12)을 형성할 때, 유리섬유강화플라스틱층과 동일한 소재로 일체로 성형하는 것이 바람직하다.When both of the
다음, 수분배출겸 수분유입방지부(19)는, 커버 본체부(11)에 고정된 상태에서 내측 방향 즉, 보호커버(10) 설치시에 수중파일(100)에 밀착되는 방향으로 돌출되어, 보호커버(10) 설치시에는 수분(이하 '해수'라고도 함)을 배출하고, 보호커버(10)를 설치한 다음에는 보호커버 안쪽으로 해수가 유입되는 것을 방지하는 기능을 한다. Next, the water discharge and moisture
이러한 수분배출겸 수분유입방지부(19)는, 탄성을 갖는 고무재질로 구성되는 것이 바람직하며, 수중파일(100)의 둘레에 밀착되어 실링(sealing) 기능이 향상될 수 있도록 커버 본체부(11)에 고정된 부분으로부터 끝단으로 갈수록 그 두께가 점차 얇아지는 구조로 형성되는 것이 바람직하다.The water discharge and moisture
한편, 수분배출겸 수분유입방지부(19)는 도 2를 참조하면 4~6mm 정도의 두께(t1)가 커버 본체부(11)에 고정되고, 4~5mm 정도의 두께(t2)가 보호커버(10)의 내측 방향으로 돌출된 상태가 되도록 구성될 수 있다.
On the other hand, the moisture discharge and moisture
이제, 상기한 바와 같이 구성되는 보호커버(10)의 제조 방법에 대하여 설명한다.Now, the manufacturing method of the
먼저, 보호커버(10)를 성형하는 몰드에 이형용 왁스를 도포한 다음, 상기 몰드에 1차 유리섬유크로스를 펴고, 여기에 경화제와 촉진제가 혼합된 수지를 적층용 롤러 등을 이용하여 기포가 발생되지 않도록 2~6mm정도의 두께로 적층하여 유리섬유강화플라스틱층(12)을 형성한다.First, the release wax is applied to the mold for forming the
이때, 플랜지부(17)도 함께 형성하는 바람직한데, 몰드에서 유리섬유강화플라스틱층(12)을 성형하는 부분의 양쪽에 플랜지부(17)를 성형하는 부분도 함께 형성하여 플랜지부(17)를 일체로 형성한다. 플랜지부(17)는 위에서 설명한 바와 같이 유리섬유강화플라스틱층(12)의 1.5배 정도 더 두껍게 형성하는 것이 바람직하다.At this time, the
다음, 상기 유리섬유강화플라스틱층(12) 위에 접착제, 예를 들면 에폭시를 도포한 후에, 별도로 제작된 EPDM발포고무시트를 적층하여 EPDM발포고무시트층(13)을 형성한다.Next, after the adhesive, for example epoxy, is applied on the glass fiber reinforced
여기서, 유리섬유강화플라스틱층(12)에 EPDM발포고무시트층(13)을 형성할 때, 상단부와 하단부에 수분배출겸 수분유입방지부(19)도 함께 적층하여 부착 등의 방법으로 설치하는 것이 바람직하다. 즉, 도 2에서와 같이 유리섬유강화플라스틱층(12)의 양단부에 수분배출겸 수분유입방지부(19)가 끼워지는 홈부(11a)를 각각 형성하고, 각 홈부(11a)에 수분배출겸 수분유입방지부(19)의 돌기(19a)를 각각 끼운 상태에서, EPDM발포고무시트층(13)을 적층하여 고정하는 방법으로 설치하는 것이 바람직하다. 물론, EPDM발포고무시트층(13)을 먼저 적층하고 유리섬유강화플라스틱층(12)에 수분배출겸 수분유입방지부(19)를 부착 등의 방법으로 고정하는 것도 가능하다.Here, when the EPDM foam
다음, 상기 EPDM발포고무시트층(13) 위에 흡수률이 50% 이상인 부직포를 적층한 다음, 페트로레이텀컴파운드를 함침시켜 페트로레이텀컴파운드층(14)을 형성한다.Next, a nonwoven fabric having a water absorption of 50% or more is laminated on the EPDM foam
다음, 상기 페트로레이텀컴파운드층(14) 위에 보호시트(15)를 적층하여 구성함으로써 본 발명에 따른 보호커버(10)를 제작할 수 있게 된다.
Next, the
상기한 바와 같이 구성되고 제조되는 본 발명에 따른 수중파일 보호커버(10)를 이용한 수중파일(100) 보호 시공방법에 대하여 설명한다.The construction method for protecting the
수중파일(100)을 고압 세척 방법, 그라인더 등으로 수중파일(100)의 표면에 붙어 있는 이물질, 녹 등을 제거하고, 상기한 바와 같은 본 발명에 따른 수중파일 보호커버(10)를 설치하게 된다.
수중파일 보호커버(10) 시공시에 본 발명에 따른 보호커버 설치용 클램프(30)(이하 '클램프'라고도 함)를 이용하게 되는데, 도 4를 참조하여 클램프(30)에 대하여 간단히 먼저 설명하고, 그 다음에 수중파일 보호커버를 시공하는 방법에 대하여 설명한다.When the underwater file
보호커버 설치용 클램프(30)는, 보호커버(10)의 양쪽 플랜지부(17)를 (길이 방향으로) 가운데 부분으로부터 밀착시키면서 점차 상측과 하측 부분으로 밀착시킬 수 있도록 구성된 장비이다.The protective cover mounting clamp 30 is a device configured to be able to closely adhere to the upper and lower portions while keeping both
도 4는 보호커버 설치용 클램프(30)의 일례를 보여주는 도면으로서, 크게 양쪽 플랜지부(17)를 압착시키는 한 쌍의 압착판(31)과, 이 압착판(31)의 뒤쪽으로 집게 모양으로 길게 연결된 가압 제공부(35)로 이루어진다.4 is a view showing an example of the protective cover mounting clamp 30, a pair of pressing
한 쌍의 압착판(31)은 양쪽 플랜지부(17)를 압착하는 면(31)(이하 '압착면'이라함)이 상호 마주하는 방향으로 곡면으로 돌출되게 형성되는데, 이때 곡면 돌출 모양은 전체 길이 대비에서 1/100 ~ 1.5/100 정도로 만곡되게 형성되는 것이 바람직하다.The pair of
또한 상기 양쪽 플랜지부(17)가 볼트(21) 및 너트(22) 등의 체결 부재에 의해 상호 고정되는 바, 양쪽 압착판(31)에는 양쪽 플랜지부(17)를 밀착시킨 상태에서 볼트(21) 및 너트(22)를 체결할 수 있도록 길이 방향으로 일정 간격마다 체결 홀(33)들이 형성되는 것이 바람직하다.In addition, the two
이때 체결 홀(33)들은 시공 오차 등을 고려하여 상하로 길게 슬롯(slot) 형상으로 형성되는 것이 바람직하다.At this time, the fastening holes 33 are preferably formed in a slot shape up and down in consideration of construction errors and the like.
상기 가압 제공부(35)는 상기 한 쌍의 압착판(31)에 집게 모양으로 연결된 부분으로서, 한 쌍의 압착판(31)을 상호 압착시킬 수 있는 구조이면 공지의 집게 구조 또는 클램프 구조를 이용하여 다양하게 구성할 수 있다. 다만, 양쪽 플랜지부(17)를 압착시킨 상태에서 볼팅 체결 작업을 진행해야 하므로, 가압 제공부(35)에는 한 쌍의 압착판(31)의 압착 상태를 유지시키는 압착유지기구(37)가 설치되는 것이 바람직하다. 압착유지기구는 집게 구조를 가진 가압 제공부(35)의 좁힌 상태 또는 벌린 상태가 그대로 유지되도록 하는 구조로서, 도면에 예시된 구조 외에 공지의 구조를 이용하여 다양하게 구성할 수 있다.The
또한 가압 제공부(35)는 단순히 집게 형태의 수동식 뿐만 아니라, 기계식 구조 즉, 유압 제공 방식 등에 의해 양쪽 압착판(31)이 양쪽 플랜지부(17)를 압착시키도록 구성하는 것도 가능하다.
In addition, the
이제, 상기와 같은 보호커버 설치용 클램프(30)를 이용하여, 보호커버(10)를 수중파일에 설치하는 본 발명에 따른 수중파일 보호 시공 방법에 대하여 설명한다.Now, a method for protecting the underwater file construction according to the present invention for installing the
먼저, 보호커버(10)의 안쪽에 부착되어 있는 이형지 또는 필름으로 이루어진 보호시트(15)를 제거하고, 이물질의 제거된 수중파일(100)의 둘레에 보호커버(10)를 감듯이 밀착시키고, 양쪽 플랜지부(17)를 상호 맞댄 상태에서 상기 보호커버 설치용 클램프(30)를 이용하여 양쪽 플랜지부(17)를 밀착시킨다.First, remove the
이때, 보호커버 설치용 클램프(30)의 양쪽 압착판(31)이 양쪽 플랜지부(17)를 밀착시키게 되는데, 압착판(31)의 압착면(32)이 상호 마주하는 방향으로 만곡된 형상으로 돌출되게 형성됨에 따라, 클램프(30)의 가압 제공부(35)를 압착하는 방향으로 작동시키게 되면, 도 6을 참조하면, 양쪽 플랜지부(17)의 가운데 부분(C)을 먼저 밀착시키고, 이후 가운데 부분(C)을 중심으로 상측 부분(U)과 하측 부분(D) 방향으로 다른 부분들을 점차적으로 밀착시키게 된다.At this time, both pressing
이와 같은 상태에서, 보호커버 설치용 클램프(30)의 가압 제공부(35)를 고정하고, 양쪽 플랜지부(17)의 가운데 부분부터 상측과 하측으로 볼트(21) 및 너트(22)를 차례로 체결한다. 이때, 볼트(21)의 조임 강도는 EPDM발포고무시트층(13)의 수축률이 60~70%정도가 되도록 체결하는 것이 바람직하다. 따라서, EPDM발포고무시트층(13)이 60~70% 정도까지 수축되면서 압착됨에 따라 수중파일(100)의 고른 표면은 물론 표면이 불균일한 손상 부위까지도 보호커버(10)의 페트로레이텀컴파운드층(14)이 밀착되어 수중파일 보호 효과를 높일 수 있게 된다.In such a state, the
이와 같은 방법으로 양쪽 플랜지부(17)에 체결 부재(21, 22)를 설치하는 작업이 완료되면, 양쪽 플랜지부(17) 사이 또는 양쪽 플랜지부(17)의 상단부와 하단부 등을 실링재를 이용하여 실링 처리 작업을 실시하여, 수중파일(100)에 보호커버(10)를 설치하는 작업을 완료한다.After the installation of the
한편, 상기와 같이 보호커버 설치용 클램프(30)를 이용하여 양쪽 플랜지부(17)의 가운데 부분부터 상측과 하측 방향으로 밀착시키고, 이후 체결 부재(21, 22)도 양쪽 플랜지부(17)의 가운데 부분(C)부터 상측 방향(U)과 하측 방향(D)으로 차례로 체결함에 따라, 체결 부재(21, 22)의 체결력에 의해 EPDM발포고무시트층(13)이 압착되면서 전체적으로 보호커버(10)가 수중파일(100) 둘레에 가운데 부분으로부터 상측과 하측 방향으로 점진적으로 밀착된다. 따라서, 보호커버(10)와 수중파일(100) 사이에 남아있는 해수가 가운데 부분으로부터 상측과 하측으로 점차 밀리면서 최종적으로는 보호커버(10)의 수분배출겸 수분유입방지부(19)의 바깥쪽으로 밀려나가게 된다. On the other hand, using the protective cover mounting clamp 30 as described above from the center portion of the two
그리고 보호커버(10) 밖으로 밀려 나간 해수는 보호커버(10)를 수중파일(100)에 설치할 때, 수분배출겸 수분유입방지부(19)가 수중파일(100)의 둘레에 밀착됨에 따라 보호커버(10) 밖에서는 보호커버(10) 안쪽으로 유입되지 않게 된다.And the seawater pushed out of the
결국, 상기한 바와 같은 본 발명에 따른 보호커버(10)에 의해 완전히 감싸진 상태에서 EPDM발포고무시트층(13)에서 제공하는 탄성력에 의해 페트로레이텀컴파운드층(14)이 수중파일(10)의 표면에 전체적으로 고르게 밀착되어 부식 발생 등을 방지되고, 유리섬유강화플라스틱층(12) 및 EPDM발포고무시트층(13)에 의해 외력에도 쉽게 손상되지 않은 강성 및 탄성을 갖으며, 상단부와 하단부에 구비된 수분배출겸 수분유입방지부(19)에 의해 보호커버 내부로 수분이 유입되는 것을 방지하여, 수중파일을 보다 경제적이면서 신뢰성 있게 보호할 수 있게 된다.
As a result, the
이하, 본 발명의 따른 수중파일 보호 시공방법과 종래 시공방법으로 시공한실험 결과를 소개하면 다음과 같다.
Hereinafter, the experimental results of the construction of the underwater file protection construction method and the conventional construction method according to the present invention are as follows.
1. 실험방법
1. Experimental method
① 실시예1Example 1
수중파일에 본 발명에 따른 보호커버(10)를 감듯이 밀착시키고, 양쪽 플랜지부(17)를 상호 맞댄 상태에서, 클램프(30)를 이용하여 양쪽 플랜지부를 밀착시킨후, 체결 부재(21, 22)를 양쪽 플랜지부(17)의 가운데 부분부터 상측 방향과 하측 방향으로 차례로 체결하여, 보호커버(10)와 수중파일(100) 사이에 남아있는 수분을 가운데 부분으로부터 상측과 하측으로 점차적으로 밀어내면서 보호커버(10) 바깥쪽으로 배출시킨 후에, 양쪽 플랜지부(17)의 가운데 부분으로부터 상측과 하측으로 차례로 볼트와 너트를 체결하였다. 이때 EPDM발포고무시트층(13)의 수축률을 65% 정도가 되도록 하였다.
After the
②실시예2② Example 2
본 발명에 따른 보호커버(10)에서 유리섬유강화플라스틱층(12)에 크랙과 깨짐을 준 뒤, 위 [실시예1]과 같은 시공방법으로 시공하였다.
After giving a crack and crack to the glass fiber reinforced
③비교예1③ Comparative Example 1
1. 수중파일에 페트로레이텀테이프를 감는다.1. Wrap the petrolatum tape on the underwater file.
2. 상기 페트로레이텀테이프 위에 PVC시트를 감는다.2. Wind the PVC sheet on the petrolatum tape.
3. 상기 PVC시트 위에 섬유복합체로 이루어진 보호커버를 감고 볼트와 너트를 플랜지부에 체결한다.3. Wrap the protective cover made of fiber composite on the PVC sheet and fasten the bolt and nut to the flange part.
4. 상기 보호커버가 흘러내리지 않도록 수중파일에 스토퍼를 설치한다.
4. Install the stopper on the underwater pile so that the protective cover does not flow down.
④비교예2④ Comparative Example 2
1. 수중파일을 고압세척 방법으로 세척한다.1. Clean the underwater pile by autoclaving.
2. 세척된 수중파일에 에폭시수지 주제와 경화제를 섞어 수중파일 표면에 도포하여 수중파일 겉면에 에폭시 층을 만든다.
2. Mix the epoxy resin main material with the curing agent in the washed underwater pile and apply it to the surface of the underwater pile to make an epoxy layer on the surface of the underwater pile.
2. 실험결과2. Experimental Results
상기의 실시예1, 실시예2, 비교예1, 비교예2의 방법으로 각각 시공한 후, 6개월이 지난 시점에 확인하여 본 결과는 다음과 같다.
After the construction by the method of Example 1, Example 2, Comparative Example 1, Comparative Example 2, respectively, six months later, the results were as follows.
① 실시예1Example 1
실시예1에서의 보호커버(10)는 보호커버의 크랙 또는 깨짐이 없었으며, 보호커버(10)를 벗겨 냈을 때 그 안에 페트로레이텀 물질이 그대로 남아있어 수중파일의 부식을 억제하는 역할을 지속하고 있음을 확인할 수 있었다.
The
②실시예2② Example 2
실시예2에서의 보호커버(10)는 유리섬유강화플라스틱층(12)에 크랙과 깨짐을 주었음에도 불구하고, 보호커버(10)를 벗겨 냈을 때, 그 안에 페트로레이텀 물질이 그대로 남아있어, 이와 같은 경우에도 수중파일의 부식을 억제하는 역할을 지속하고 있음을 확인할 수 있었다
Although the
③비교예1③ Comparative Example 1
비교예1에서는, 보호커버에 크랙이 발생하였고, 이로 인하여 보호커버 안쪽으로 바닷물이 침투한 상태였으며, 보호커버를 벗겨 냈을 때, 페터르레이텀 물질이 대부분 씻겨 내려가 수중파일의 부식억제 역할이 떨어지고 있음을 확인할 수 있었다.
In Comparative Example 1, a crack occurred in the protective cover, which caused seawater to penetrate into the protective cover, and when the protective cover was peeled off, most of the PETTERRATERM material was washed away, thereby reducing the corrosion inhibitor role of the underwater pile. It could be confirmed.
④비교예2④ Comparative Example 2
비교예2에서는, 에폭시층의 접착력이 약해 도장부위에 균열이 일어났으며 50%이상의 에폭시 도장부위가 떨어져 나가고 있음을 확인할 수 있었다.
In Comparative Example 2, it was confirmed that the adhesive strength of the epoxy layer was weak, so that a crack occurred at the coated portion and 50% or more of the epoxy coated portion was falling off.
3. 상기 실시예 및 비교예의 실험 결과 정리3. Summary of Experimental Results of the Examples and Comparative Examples
상기 실시예1에서, 보호커버(10)가 크랙이나 깨짐이 없던 이유는 EPDM발포고무시트층(13)의 충격흡수 영향으로 판단되며, 보호커버를 벗겨 냈을 때, 페트로레이텀 물질이 계속 잔존한 이유는 수분배출겸 수분유입방지부(19)로 인해 보호커버 안쪽으로 해수유입을 차단되었고, 이와 함께 EPDM발포고무시트층(13)을 65% 정도 압착시켜 볼트를 체결함으로써, 수중파일과 보호커버 간에 공극이 발생하지 않았기 때문으로 판단된다.In Example 1, the reason why the
또한 상기 실시예2에서 보호커버(10)의 유리섬유강화플라스틱층(12)에 크랙과 깨짐을 주었음에도 불구하고, EPDM발포고무시트층(13)이 수중파일을 감싸고 있고 EPDM발포고무시트층(13)이 수중파일 표면으로 해수침투 방지역할도 수행하고 있었으며, 수중파일과 보호커버 간의 공극이 발생하지 않아 페트로레이텀 물질이 그대로 잔존하고 있었다.In addition, despite the cracks and cracks in the glass fiber reinforced
결국, 본 발명에 따른 보호커버로 수중 파일을 보호할 경우에, 보호커버 안쪽으로 해수가 유입되는 것을 확실하게 차단할 수 있었고, 또한 페트로레이텀 물질이 장시간 유실되지 않고 잔존하여 수중파일이 부식되는 것을 방지함으로써, 수중파일 보호 효과가 장기간 지속되어, 보다 우수한 수중파일 보호 성능을 확보할 수 있고, 이에 따라 수중파일 보호 공법의 신뢰성을 높일 수 있다는 것을 확인할 수 있었다.
As a result, when protecting the underwater file with the protective cover according to the present invention, it was possible to reliably block the inflow of seawater into the protective cover, and also that the petroleum material remains without being lost for a long time and the underwater file is corroded. By preventing the damage, the underwater file protection effect lasted for a long time, and it was confirmed that a superior underwater file protection performance could be ensured, thereby increasing the reliability of the underwater file protection method.
상기한 바와 같은, 본 발명의 실시예에서 설명한 기술적 사상들은 각각 독립적으로 실시될 수 있으며, 서로 조합되어 실시될 수 있다. 또한, 본 발명은 도면 및 발명의 상세한 설명에 기재된 실시예를 통하여 설명되었으나 이는 예시적인 것에 불과하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능하다. 따라서, 본 발명의 기술적 보호범위는 첨부된 특허청구범위에 의해 정해져야 할 것이다.As described above, the technical ideas described in the embodiments of the present invention may be implemented independently, or may be implemented in combination with each other. While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is evident that many alternatives, modifications, and variations will be apparent to those skilled in the art. It is possible. Accordingly, the technical scope of the present invention should be determined by the appended claims.
Claims (6)
상기 커버 본체부는, 바깥쪽으로부터 외피층을 구성하는 유리섬유강화플라스틱층, 압착 탄성력을 제공하는 EPDM발포고무시트층, 수중파일의 표면에 밀착되는 페트로레이텀컴파운드층 순으로 일체로 구성되며,
상기 커버 본체부는 페트로레이텀컴파운드층을 보호하면서도 용이하게 벗겨낼 수 있는 보호시트가 더 포함된 것을 특징으로 하는 수중파일 보호커버.
The cover body part which is in close contact with the circumference of the underwater pile, the two flange parts provided on both ends of the cover body part and interconnected by a fastening member, and the upper and lower ends of the cover body part are provided with water while discharging moisture Water blocking and water inlet prevention unit to block,
The cover body is integrally formed in the order of the glass fiber reinforced plastic layer constituting the outer skin layer from the outside, the EPDM foam rubber sheet layer providing a compression elastic force, the petrolatum compound layer in close contact with the surface of the underwater pile,
The cover body portion is a protective cover for underwater files further comprising a protective sheet that can be easily peeled off while protecting the petrolatum compound layer.
상기 보호커버는, 보호커버를 성형하는 몰드에 유리섬유크로스를 펴고, 여기에 경화제와 촉진제가 혼합된 수지를 기포가 발생되지 않도록 일정 두께로 적층하여 유리섬유강화플라스틱층을 형성하고,
상기 유리섬유강화플라스틱층 위에 접착제를 도포한 후에, 별도로 제작된 EPDM발포고무시트를 적층하여 EPDM발포고무시트층을 형성하고,
상기 EPDM발포고무시트층 위에 부직포를 적층한 다음, 페트로레이텀컴파운드를 함침시켜 페트로레이텀컴파운드층을 형성하는 과정으로, 유리섬유강화플라스틱층, EPDM발포고무시트층, 페트로레이텀컴파운드층을 일체화시켜 제작한 것을 특징으로 하는 수중파일 보호커버.
The method according to claim 1,
The protective cover is formed by spreading the glass fiber cross on a mold for forming the protective cover, and laminating a resin mixed with a curing agent and an accelerator to a predetermined thickness so as not to generate bubbles to form a glass fiber reinforced plastic layer,
After applying the adhesive on the glass fiber reinforced plastic layer, the EPDM foam rubber sheet produced separately is laminated to form an EPDM foam rubber sheet layer,
After laminating the nonwoven fabric on the EPDM foam rubber sheet layer, impregnating the petrolatum compound to form a petrolatum compound layer, the glass fiber reinforced plastic layer, EPDM foam sheet, petrolatum compound layer is integrated Underwater file protective cover characterized in that the production.
수중파일의 둘레에 상기 보호커버를 감듯이 밀착시키고, 양쪽 플랜지부를 상호 맞댄 상태에서, 클램프를 이용하여 양쪽 플랜지부를 밀착시키는 제1단계와;
제1단계 후에, 체결 부재를 양쪽 플랜지부의 가운데 부분부터 상측 방향과 하측 방향으로 차례로 체결하여, 보호커버와 수중파일 사이에 남아있는 수분을 가운데 부분으로부터 상측과 하측으로 점차적으로 밀어내면서 보호커버 바깥쪽으로 배출시키는 제2단계를 포함한 것을 특징으로 하는 수중파일 보호커버를 이용한 수중파일 보호 시공방법.
A construction method of protecting an underwater file using the protective cover according to claim 1 or 3,
A first step of bringing the protective cover close to the periphery of the underwater pile, and the two flange parts being brought into close contact with each other by using a clamp;
After the first step, the fastening member is fastened sequentially from the center of both flange portions in an upward direction and a downward direction, and gradually pushes moisture remaining between the protective cover and the underwater pile from the middle portion to the upper side and the lower side, and then outside the protective cover. Underwater file protection construction method using the underwater file protective cover, characterized in that it comprises a second step to discharge toward.
상기 제1단계에서 이용되는 클램프는, 상기 양쪽 플랜지부를 압착시키는 압착판에 구비된 압착면이 상호 마주하는 방향으로 만곡된 형상으로 돌출되게 형성되어, 클램프 작동시에 양쪽 플랜지부의 가운데 부분을 먼저 밀착시키고, 이후 가운데 부분을 중심으로 상측 부분과 하측 부분 방향으로 다른 부분들을 점차적으로 밀착시킬 수 있도록 구성된 것을 특징으로 하는 수중파일 보호커버를 이용한 수중파일 보호 시공방법.
The method of claim 4,
The clamp used in the first step is formed so as to protrude in a curved shape in the direction in which the pressing surfaces provided on the pressing plate for pressing the two flange parts in a mutually opposite direction, the center portion of both flanges during the clamp operation Underwater file protection construction method using the underwater file protective cover, characterized in that the first contact, and then configured to be in close contact with the other parts in the upper part and the lower part direction centered around the center portion.
상기 제2단계에서, 양쪽 플랜지부에 체결 부재를 체결할 때, 체결 부재의 조임 강도는 상기 보호커버의 EPDM발포고무시트층의 수축률이 60~70% 정도가 되도록 하는 것을 특징으로 하는 수중파일 보호커버를 이용한 수중파일 보호 시공방법.The method of claim 4,
In the second step, when fastening the fastening member on both flanges, the tightening strength of the fastening member is such that the shrinkage of the EPDM foam rubber sheet layer of the protective cover is 60 to 70%, characterized in that the pile pile protection Underwater file protection construction method using cover.