KR100973915B1 - Method for cooling of rolled plate - Google Patents

Method for cooling of rolled plate Download PDF

Info

Publication number
KR100973915B1
KR100973915B1 KR1020080029817A KR20080029817A KR100973915B1 KR 100973915 B1 KR100973915 B1 KR 100973915B1 KR 1020080029817 A KR1020080029817 A KR 1020080029817A KR 20080029817 A KR20080029817 A KR 20080029817A KR 100973915 B1 KR100973915 B1 KR 100973915B1
Authority
KR
South Korea
Prior art keywords
cooling
rolled sheet
water
unit
rolled
Prior art date
Application number
KR1020080029817A
Other languages
Korean (ko)
Other versions
KR20090104407A (en
Inventor
김기호
박충재
김대현
김민철
Original Assignee
주식회사 포스코
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 포스코 filed Critical 주식회사 포스코
Priority to KR1020080029817A priority Critical patent/KR100973915B1/en
Publication of KR20090104407A publication Critical patent/KR20090104407A/en
Application granted granted Critical
Publication of KR100973915B1 publication Critical patent/KR100973915B1/en

Abstract

압연 판재 냉각방법을 제공한다. Provided is a rolled sheet cooling method.

본 발명은 압연된 압연 판재(1)의 두께 또는 종류에 따라 냉각수 분사구간을 조정할 수 있는 냉각설비(10)를 이용하여 압연 판재(1)를 냉각하는 압연 판재 냉각방법에 있어서, 압연 판재(1)에 분사된 냉각수의 일부가 압연 판재(1)에 체류하는 체류수의 체류구간과 체류시간을 최소화하도록 압연 판재(1) 입측으로부터 출측까지 순차로 배치되는 1번에서 N번의 N개의 단위 냉각유닛(20)을 포함하는 상기 냉각설비(10)의 압연 판재 출측에 위치하는 N번 냉각유닛(20)을 기준으로 압연 판재(1)의 두께 또는 종류에 따라 입측방향으로 순차적으로 각 단위별 냉각유닛(20)의 냉각수 분사를 조정하여 냉각수 분사구간을 설정하며, 상기 냉각유닛(20) 단위별 또는 상기 냉각유닛(20)에 포함되는 냉각수 노즐헤드(21) 단위별로 냉각수 분사량과 분사속도를 조정하는 것을 특징으로 한다.The present invention provides a rolled sheet cooling method for cooling a rolled sheet member 1 by using a cooling facility 10 capable of adjusting a coolant spray section according to the thickness or type of the rolled rolled sheet member 1. 1 to N N unit cooling units sequentially arranged from the inlet side to the outlet side of the rolled sheet member 1 so as to minimize the retention period and the residence time of the retained water in the part of the cooling water sprayed on the rolled sheet member 1). Cooling unit for each unit sequentially in the entry direction according to the thickness or type of the rolled sheet material 1 on the basis of the N number cooling unit 20 located on the rolled sheet material exit side of the cooling installation 10 including the (20) Adjusting the coolant injection of the (20) to set the coolant injection section, and adjusts the cooling water injection amount and injection speed for each of the cooling unit 20 unit or the cooling water nozzle head 21 unit included in the cooling unit 20 Characteristic It shall be.

본 발명에 의하면, 냉각설비의 압연 판재 출측을 기준으로 압연 판재의 두께나 종류에 따라 냉각설비에서의 냉각수 분사구간을 설정하고 조정하여 냉각수 분사구간 통과 후 압연 판재에 존재하는 체류수의 체류구간과 체류시간을 최소화할 수 있고, 이에 따라 체류수의 존재에 의해서 발생하는 압연 판재의 표면 변형을 최소화할 수 있으며, 압연 판재의 표면 변형이 최소화되기 때문에 압연 판재의 평탄도가 좋아져서, 냉각설비 다음에 위치하는 교정기를 사용하여 압연 판재를 평탄화시키는 압연 판재의 교정율이 감소 된다. According to the present invention, according to the rolled sheet material exit side of the cooling equipment, the cooling water spraying section in the cooling equipment is set and adjusted according to the thickness or type of the rolled sheet, and the retention period of the remaining water present in the rolled sheet after passing through the cooling water spraying section. It is possible to minimize the residence time, thereby minimizing the surface deformation of the rolled sheet produced by the presence of the retained water, and because the surface deformation of the rolled sheet is minimized, the flatness of the rolled sheet is improved, so The correction rate of the rolled sheet to flatten the rolled sheet using a straightener located at is reduced.

압연, 판재, 냉각설비, 체류수 Rolling, plate, cooling equipment, water retention

Description

압연 판재 냉각방법{Method for cooling of rolled plate} Method for cooling of rolled plate

본 발명은 압연 판재 냉각방법에 관한 것으로, 보다 상세하게는 압연된 압연 판재의 열처리를 위해서 압연 판재의 두께 또는 종류에 따라 냉각설비에서의 냉각수 분사구간을 달리하여 압연 판재를 냉각시, 냉각수 분사구간을 냉각설비의 압연 판재 출측을 기준으로 설정하여 냉각수 분사구간 통과 후 압연 판재에 존재하는 체류수의 체류시간을 최소화할 수 있는 압연 판재 냉각방법에 관한 것이다. The present invention relates to a method for cooling a rolled sheet, and more particularly, to cool a rolled sheet by cooling the rolled sheet by varying a coolant spray section in a cooling facility according to the thickness or type of the rolled sheet for heat treatment of the rolled sheet. The present invention relates to a method for cooling a rolled sheet that can minimize the residence time of the residual water present in the rolled sheet after passing through the coolant jetting section by setting the rolled sheet on the rolled sheet exit side of the cooling facility.

먼저, 도 1에서는 알려진 열간소재 압연공정 특히, 후판재(날판)의 열간 공정을 도시하고 있다.First, FIG. 1 shows a known hot material rolling process, in particular, a hot process of a thick plate material (blade).

즉, 도 1의 (a) 에서 도시한 바와 같이, 연속주조 공정에 의해서 제조된 슬래브(Slab)는 가열로(2)에서 강종에 따른 목표 온도까지 가열되고, 가열로(2)를 통과한 압연 소재(6)는, 거칠기 압연기(roughing Mill, RM)와 마무리 압연(finishing Mill, FM)기(3) 등의 압연단계를 거쳐 일정한 두께 예컨대, 최종 제품의 지시 두께까지 소재를 압연하여 후판재와 같은 압연 판재(1)를 생산한다.That is, as shown in Figure 1 (a), slab (Slab) produced by the continuous casting process is heated to the target temperature according to the steel grade in the heating furnace 2, the rolling passed through the heating furnace (2) The raw material 6 is rolled up to a predetermined thickness, for example, the thickness of the final product through a rolling step such as a roughing mill (RM) and a finishing mill (FM) machine 3, and the The same rolled plate 1 is produced.

다음, 마무리 압연에 의해 소정의 판 두께로 압연된 후판재와 같은 압연 판재(1)는 결정립 미세화나 변태조직의 제어와 같은 열처리를 위한 가속냉각을 위해 서 냉각설비(10)를 거치게 된다. Next, the rolled sheet material 1, such as a thick plate rolled to a predetermined plate thickness by finish rolling, is subjected to the cooling facility 10 for accelerated cooling for heat treatment such as grain refinement or control of the transformation structure.

그리고, 압연제품(후판 제품)의 질을 높이기 위하여 교정기(4)를 통한 교정단계 즉, 평탄화 단계를 거치고, 최종적으로 냉각대(5)에서 제품으로 완성된다. Then, in order to increase the quality of the rolled product (thick plate product), the calibration step through the calibrator 4, that is, the flattening step, and finally finished in the product in the cooling table (5).

전술된 냉각설비(10)에서는 압연 판재(1)의 두께나 종류에 따라 냉각수 분사구간을 조정할 수 있도록 되어 있다. In the cooling device 10 described above, the cooling water jetting section can be adjusted according to the thickness and type of the rolled sheet material 1.

예컨대, 비교적 그 두께가 얇은 압연 판재(1)의 경우에는 냉각량이 비교적 작기 때문에 냉각설비(10)에서의 냉각수 분사구간이 상대적으로 작게 되고, 비교적 두께가 두꺼운 압연 판재(1)의 경우에는 냉각량이 비교적 크기 때문에 냉각설비(10)에서의 냉각수 분사구간이 상대적으로 크게 된다. For example, since the cooling amount is relatively small in the case of the rolled sheet 1 having a relatively thin thickness, the cooling water injection section in the cooling installation 10 is relatively small, and in the case of the rolled sheet 1 having a relatively thick thickness, the cooling amount is relatively small. Because of the relatively large size, the cooling water injection section in the cooling system 10 becomes relatively large.

종래에 이러한 냉각수 분사구간의 설정과 조정은 냉각설비(10)의 압연 판재(1) 입측으로부터, 즉 입측을 기준으로 설정되고 조정되었다. In the related art, the setting and adjustment of such a cooling water injection section have been set and adjusted from the entrance side of the rolled sheet 1 of the cooling installation 10, that is, on the basis of the entrance side.

즉, 압연 판재(1)의 두께 또는 종류에 따라 냉각설비(10)에서의 냉각수 분사구간이 냉각설비(10)의 압연 판재(1) 입측을 기준으로 출측 방향으로 커지도록 되어 있었다.That is, according to the thickness or kind of the rolled sheet material 1, the cooling water injection section in the cooling installation 10 became large in the exit direction based on the rolled sheet material 1 entrance side of the cooling installation 10. As shown in FIG.

이와 같이 설정되고 조정된 냉각설비(10)의 냉각수 분사구간을 압연 판재(1)가 지나게 되면 분사된 냉각수의 일부가 압연 판재(1)에 체류하여 체류수가 발행하게 된다. When the rolled sheet material 1 passes through the cooling water injection section of the cooling facility 10 set and adjusted as described above, a part of the injected coolant stays in the rolled sheet material 1, and the water stays.

이러한 체류수는 압연 판재(1)에 비교적 균일하게 존재하도록 분사되는 냉각수와는 달리 압연 판재(1)에 불균일하게 존재하기 때문에 이에 의해서 압연 판재(1)가 국부적으로 냉각되어 압연 판재(1)의 표면이 불균일하게 된다. Unlike the cooling water sprayed to exist relatively uniformly in the rolled sheet 1, such a retention water is non-uniformly present in the rolled sheet 1, whereby the rolled sheet 1 is locally cooled, The surface becomes uneven.

즉, 압연 판재(1)의 표면이 변형된다. That is, the surface of the rolled sheet material 1 is deformed.

이를 교정하기 위해서 전술된 교정기(4)를 냉각설비(10) 다음에 위치시켜서 불균일한 압연 판재(1)의 표면을 균일하게 교정하게 된다. In order to correct this, the above-described calibrator 4 is placed next to the cooling installation 10 to uniformly correct the surface of the uneven rolled sheet 1.

그러나, 체류수가 압연 판재(1) 표면에 과다하게 존재하는 경우에는 압연 판재(1) 표면의 변형이 심하게 이루어지기 때문에, 압연 판재(1) 표면의 평탄도가 좋지 않다는 문제점이 있었다. However, when the number of retained waters is excessively present on the surface of the rolled sheet 1, since the deformation of the surface of the rolled sheet 1 is severely performed, there is a problem that the flatness of the surface of the rolled sheet 1 is not good.

따라서, 압연 판재(1) 표면의 평탄도를 교정하기 위해서 냉각설비(10) 다음에 위치하는 교정기(4)를 사용하여 압연 판재(1) 표면의 평탄도를 교정하는 교정율이 커지게 된다는 문제점이 있었다. Therefore, in order to correct the flatness of the surface of the rolled sheet 1, the problem that the correction rate for correcting the flatness of the surface of the rolled sheet 1 is increased by using the calibrator 4 positioned next to the cooling installation 10. There was this.

본 발명은 상기한 문제점을 해결하기 위해서 창출된 것으로, 본 발명의 목적은 압연 판재의 두께나 종류에 따라 냉각수 분사구간을 조정할 수 있는 냉각설비를 사용하여 압연 판재를 냉각하는 경우 냉각설비의 압연 판재 출측을 기준으로 냉각수 분사구간을 설정하고 조정하여 압연 판재에 존재하는 체류수의 체류구간과 체류시간을 최소화하여서 체류수의 존재에 의하여 발생하는 압연 판재의 표면 변형을 최소화할 수 있는 압연 판재 냉각방법을 제공하는 것이다. The present invention was created in order to solve the above problems, an object of the present invention is to use a cooling equipment that can adjust the cooling water injection section according to the thickness or type of the rolling plate to cool the rolled sheet material of the rolling plate of the cooling equipment Rolled plate cooling method that minimizes surface deformation of rolled plate caused by the presence of retained water by minimizing the retention period and retention time of the retained water in the rolled sheet by setting and adjusting the coolant spray section based on the exit side. To provide.

상기한 목적을 달성하기 위해서 본 발명은 The present invention to achieve the above object

압연된 압연 판재의 두께 또는 종류에 따라 냉각수 분사구간을 조정할 수 있는 냉각설비를 이용하여 압연 판재를 냉각하는 압연 판재 냉각방법에 있어서, In the rolled sheet cooling method for cooling the rolled sheet using a cooling facility that can adjust the coolant spray section according to the thickness or type of the rolled rolled sheet,

압연 판재에 분사된 냉각수의 일부가 압연 판재에 체류하는 체류수의 체류구간과 체류시간을 최소화하도록 압연 판재 입측으로부터 출측까지 순차로 배치되는 1번에서 N번의 N개의 단위 냉각유닛을 포함하는 상기 냉각설비의 압연 판재 출측에 위치하는 N번 냉각유닛을 기준으로 압연 판재의 두께 또는 종류에 따라 입측방향으로 순차적으로 각 단위별 냉각유닛의 냉각수 분사를 조정하여 냉각수 분사구간을 설정하며,
상기 냉각유닛 단위별 또는 상기 냉각유닛에 포함되는 냉각수 노즐헤드 단위별로 냉각수 분사량과 분사속도를 조정하는 것을 특징으로 하는 압연 판재 냉각방법을 제공한다.Said cooling comprising one to N N unit cooling units sequentially arranged from the entrance to the exit of the rolled sheet so that a part of the cooling water sprayed on the rolled sheet is minimized in the retention period and the residence time of the retained water in the rolled sheet. Based on the cooling unit No. N located on the rolled sheet exit side of the equipment, the cooling water injection section is set by adjusting the coolant injection of the cooling unit for each unit sequentially in the entry direction according to the thickness or type of the rolled sheet.
It provides a rolled sheet cooling method characterized in that for adjusting the cooling water injection amount and the injection speed for each cooling unit unit or cooling water nozzle head unit included in the cooling unit.

삭제delete

더 바람직하게, 상기 냉각설비의 압연 판재 입측과 출측 및 그 사이에 배치된 하나 이상의 체류수발생 방지유닛을 통해서 압연 판재의 체류수 발생을 방지한다.  More preferably, the generation of the residual water of the rolled sheet is prevented through at least one residual water generation preventing unit disposed between the entry and exit sides of the cold plate and the exit side of the cooling installation.

더 바람직하게, 상기 체류수발생 방지유닛은 고압수를 압연 판재에 분사하여 체류수 발생을 방지하되, 그 분사방향을 압연 판재 진행방향 또는 진행방향의 역방향으로 구별하여 분사한다. More preferably, the retentive water generation prevention unit sprays the high-pressure water to the rolled sheet to prevent the generation of the retentive water, the jetting direction is divided by the rolling direction or the reverse direction of the rolling direction.

더 바람직하게, 상기 냉각설비의 압연 판재 입측에 배치된 체류수발생 방지유닛은 압연 판재 진행방향으로 고압수를 분사하고, 상기 냉각설비의 압연 판재 출측에 배치된 체류수발생 방지유닛과 상기 냉각설비의 압연 판재 입측과 출측 사이에 배치된 체류수발생 방지유닛은 압연 판재 진행방향의 역방향으로 고압수를 분사한다. More preferably, the residing water generation preventing unit disposed at the inlet side of the rolled sheet of the cooling equipment sprays high pressure water in a rolling plate traveling direction, and the residing water preventing unit and the cooling system arranged at the outlet of the rolled sheet of the cooling equipment. The retentive water generation prevention unit disposed between the rolled sheet material entry and exit sides of the sprayed high-pressure water is injected in the reverse direction of the rolling plate advance direction.

더 바람직하게, 상기 냉각설비의 압연 판재 입측과 출측 사이에 배치되되 압연 판재 진행방향으로 고압수를 분사하는 하나 이상의 체류수발생 방지유닛을 더 포함하여 체류수 발생을 방지한다. More preferably, the cooling apparatus further comprises at least one retentive water generation unit disposed between the entry and exit side of the rolled sheet and spraying the high pressure water in the rolling plate advancing direction to prevent the retention of water.

삭제delete

본 발명에 의하면, 냉각설비의 압연 판재 출측을 기준으로 압연 판재의 두께나 종류에 따라 냉각설비의 냉각수 분사구간을 설정하고 조정하여 냉각수 분사구간 통과 후 압연 판재에 존재하는 체류수의 체류구간과 체류시간을 최소화할 수 있다 는 효과가 있다. According to the present invention, based on the rolled sheet outgoing side of the cooling equipment, the cooling water spraying section of the cooling equipment is set and adjusted according to the thickness or type of the rolled sheet, and after the passage of the cooling water spraying section, the retention section and the retention period of the retained water present in the rolled sheet material. This can minimize the time.

따라서, 체류수의 존재에 의해서 발생하는 압연 판재의 표면 변형을 최소화할 수 있다는 효과가 있다. Therefore, there is an effect that the surface deformation of the rolled sheet material generated by the presence of the retention water can be minimized.

또한, 압연 판재의 표면 변형을 최소화할 수 있기 때문에 압연 판재의 평탄도가 좋아진다는 효과가 있다. In addition, since the surface deformation of the rolled sheet can be minimized, the flatness of the rolled sheet is improved.

그리고, 압연 판재의 평탄도가 좋아지기 때문에 냉각설비 다음에 위치하는 교정기를 사용하여 압연 판재를 평탄화시키는 압연 판재의 교정율이 감소된다는 효과가 있다. And since the flatness of a rolled board material improves, there exists an effect that the correction rate of the rolled board material which flattens a rolled board material using the straightener next to a cooling installation is reduced.

이하, 첨부도면을 참조로 하여 본 발명을 상세하게 설명한다. Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.

도2는 본 발명에 따른 압연 판재 냉각방법의 일실시예에 사용되는 냉각설비를 나타내는 개략도이다. Figure 2 is a schematic diagram showing a cooling facility used in one embodiment of a rolled sheet cooling method according to the present invention.

도시된 바와 같이 냉각설비(10)는 냉각설비(10)의 압연 판재(1) 입측으로부터 출측까지 1번부터 7번까지 7개의 냉각유닛(20)을 포함한다. As shown, the cooling system 10 includes seven cooling units 20 from 1 to 7 from the inlet side to the outlet side of the rolled sheet 1 of the cooling unit 10.

각 냉각유닛(20)은 냉각설비(10)의 입측으로부터 출측까지 진행하는 압연 판재(1)에 냉각수를 분사하여 압연 판재(1)를 냉각할 수 있도록 압연 판재(1)의 상하에 각각 4개씩 배치된 냉각수 노즐헤드(21)를 구비한다. Each cooling unit 20 has four each above and below the rolled plate 1 so as to cool the rolled plate 1 by spraying cooling water onto the rolled plate 1 traveling from the entry side to the exit side of the cooling installation 10. The cooling water nozzle head 21 is provided.

냉각수 노즐헤드(21)는 이에 냉각수를 공급하는 냉각수 공급관(22)과 연결되어 있고 냉각수 공급관(22)은 도시되지는 않았지만 냉각수 공급원에 연결되어 냉각 수를 공급받도록 되어 있다. The coolant nozzle head 21 is connected to a coolant supply pipe 22 for supplying coolant thereto, and the coolant supply pipe 22 is connected to a coolant supply source to supply coolant although not shown.

냉각수 공급관(22)에는 냉각수 제어밸브(23)가 구비되어 있어서 냉각수 노즐헤드(21)에서 냉각수가 분사 또는 차단되게 하고 냉각수 노즐헤드(21)로부터 분사되는 냉각수의 유량이나 분사속도를 조절할 수 있도록 되어 있다. The coolant supply pipe 22 is provided with a coolant control valve 23 to allow the coolant to be injected or blocked by the coolant nozzle head 21 and to adjust the flow rate or the spray rate of the coolant injected from the coolant nozzle head 21. have.

따라서, 압연 판재(1)는 냉각설비(10)의 입측에서 냉각설비(10)의 출측으로 이동하면서 냉각수 노즐헤드(21)로부터 분사되는 냉각수에 의해서 냉각되게 된다. Therefore, the rolled sheet material 1 is cooled by the cooling water sprayed from the cooling water nozzle head 21 while moving from the entrance side of the cooling installation 10 to the exit side of the cooling installation 10.

이러한 냉각설비(10)에서는 각 냉각유닛(20)에 구비된 냉각수 제어밸브(23)를 사용하여, 즉 냉각수 제어밸브(23)를 열거나 닫아서 냉각수가 분사되는 냉각유닛(20)의 개수를 조정함으로써 냉각수 분사구간을 조정할 수 있다. The cooling system 10 adjusts the number of cooling units 20 to which coolant is injected by using the cooling water control valve 23 provided in each cooling unit 20, that is, opening or closing the cooling water control valve 23. As a result, the cooling water injection section can be adjusted.

이에 따라 압연 판재(1)의 두께나 종류에 따라 달라지는 냉각량에 따라 냉각설비(10)에서의 냉각수 분사구간을 조정할 수 있다. Thereby, the cooling water injection section in the cooling installation 10 can be adjusted according to the cooling amount which changes with the thickness and kind of the rolled sheet material 1. As shown in FIG.

본 실시예의 냉각설비(10)에서 냉각유닛(20)은 7개를 사용하였으나 이에 한정되지 않으며 냉각설비(10)를 통과하는 압연 판재(1)의 두께나 종류에 따라 냉각수 분사구간을 조정하여 압연 판재(1)를 냉각할 수 있는 것이라면 어떠한 개수라도 가능하다. Although seven cooling units 20 are used in the cooling installation 10 of the present embodiment, the cooling unit 20 is not limited thereto, and the cooling water injection section is adjusted according to the thickness or type of the rolling plate 1 passing through the cooling installation 10. Any number can be used as long as the plate 1 can be cooled.

분사되는 냉각수의 분사량과 분사속도는 1번과 2번의 냉각유닛(20)과 같이 냉각수 노즐헤드(21) 단위별로 조정될 수도 있고 3번 내지 7번의 냉각유닛(20)과 같이 냉각유닛(20) 단위별로 조정될 수도 있다. The injection amount and the injection speed of the sprayed coolant may be adjusted for each coolant nozzle head 21 unit, such as the cooling unit 20 of the first and second units, or the cooling unit 20 unit, such as the cooling unit 20 of the third to seventh units. It may be adjusted very much.

냉각설비(10)에는 도2에 도시된 바와 같이 압연 판재(1)의 입측과 출측 및 그 사이에 각각 체류수발생 방지유닛(30)이 배치되어 있다. As shown in FIG. 2, the cooling installation 10 is provided with a retentive water generation preventing unit 30 between the entry and exit sides of the rolled sheet 1 and therebetween.

본 실시예의 냉각설비(10)에는 냉각설비(10) 입측에 3개의 체류수발생 방지유닛(30)이 배치되어 있고 냉각설비(10) 출측에 2개의 체류수발생 방지유닛(30)이 배치되어 있다. In the cooling system 10 of the present embodiment, three residual water generation preventing units 30 are disposed at the inlet side of the cooling facility 10, and two residual water generation preventing units 30 are disposed at the exit side of the cooling facility 10. have.

또한, 2번과 3번의 냉각유닛(20) 사이에 1개의 체류수발생 방지유닛(30)이 배치되어 있고, 4번과 5번의 냉각유닛(20) 사이에 2개의 체류수발생 방지유닛(30)이 배치되어 있으며, 6번과 7번의 냉각유닛(20) 사이에 1개의 체류수발생 방지유닛(30)이 배치되어 있다. In addition, one residence water generation prevention unit 30 is disposed between the second and third cooling units 20, and two residence water generation prevention units 30 are disposed between the fourth and fifth cooling units 20. ) Is disposed, and one residence water generation prevention unit 30 is disposed between the sixth and seventh cooling units 20.

각 체류수발생 방지유닛(30)에서는 고압수가 분사되며, 도3과 도4에 도시된 바와 같이 냉각수 분사구간 양쪽에 위치된 체류수발생 방지유닛(30)에서 고압수를 분사시켜서, 분사된 냉각수가 냉각수 분사구간을 통과하는 압연 판재(1) 부분 이외의 다른 부분으로 이동하지 않고 압연 판재(1) 아래로 모두 떨어지도록 흐르게 하여, 압연 판재(1) 표면에 분사된 냉각수의 일부가 압연 판재(1) 표면에 남게 되어 발생하는 체류수가 압연 판재(1) 표면에 발생하는 것을 방지한다. High pressure water is injected from each of the residual water generation preventing units 30, and the high temperature water is injected from the residual water generation preventing unit 30 located at both sides of the cooling water injection section, as shown in FIGS. Flows so as to fall under the rolled sheet material 1 without moving to other portions than the rolled sheet material 1 portion passing through the coolant spray section, so that a part of the coolant sprayed on the surface of the rolled sheet material 1 is rolled sheet material ( 1) Residual water generated by remaining on the surface is prevented from occurring on the surface of the rolled sheet 1.

각 체류수발생 방지유닛(30)은 고압수를 분사하는 고압수 노즐헤드(31)와 고압수 노즐헤드(31)에 고압수를 공급하는 고압수관(도시되지 않음), 고압수관에 연결되어 고압수관에 고압수를 공급하는 고압수원(도시되지 않음) 및, 고압수관에 구비된 고압수 제어밸브(도시되지 않음)를 포함하여 구성된다. Each residence water generation prevention unit 30 is connected to a high pressure water pipe (not shown) and a high pressure water pipe for supplying high pressure water to the high pressure water nozzle head 31 for spraying the high pressure water and a high pressure water pipe. It comprises a high pressure water source (not shown) for supplying high pressure water to the water pipe, and a high pressure water control valve (not shown) provided in the high pressure water pipe.

여기에서 체류수발생 방지유닛(30)의 고압수원과 냉각유닛(20)의 냉각수 공급원은 같을 수도 있고 다를 수도 있다. Here, the high pressure water source of the retentive water generation preventing unit 30 and the cooling water supply source of the cooling unit 20 may be the same or different.

각 체류수발생 방지유닛(30)에서 고압수가 분사되는 방향은 압연 판재(1)의 진행방향 또는 진행방향의 역방향일 수 있다. The direction in which the high pressure water is sprayed from each of the retentive water generation preventing units 30 may be a traveling direction or a reverse direction of the traveling direction of the rolled sheet material 1.

본 실시예의 냉각설비(10)에서 냉각설비(10) 입측에 배치된 3개의 체류수발생 방지유닛(30)과, 4번과 5번의 냉각유닛(20) 사이에 배치된 2개의 체류수발생 방지유닛(30) 중 하나는 고압수를 압연 판재(1) 진행방향으로 분사하도록 되어 있고, 나머지 체류수발생 방지유닛(30)은 압연 판재(1) 진행방향의 역방향으로 분사하도록 되어 있다. In the cooling system 10 of the present embodiment, three residual water generation preventing units 30 disposed at the inlet side of the cooling system 10 and two residual water generation units disposed between the fourth and fifth cooling units 20 are prevented. One of the units 30 is configured to spray the high pressure water in the rolling direction of the rolled sheet 1, and the remaining residence water generation preventing unit 30 is sprayed in the reverse direction of the rolling direction of the rolled sheet 1.

따라서, 전술된 바와 같이 압연 판재(1) 진행방향으로 고압수를 분사하는 체류수발생 방지유닛(30)과 압연 판재(1) 진행방향의 역방향으로 고압수를 분사하는 체류수발생 방지유닛(30)을 동시에 사용하여 압연 판재(1) 표면에서 냉각수가 모아져서 흐르게 하여 압연 판재(1) 아래로 떨어지게 함으로써 압연 판재(1)에 체류수가 발생하는 것을 방지하게 된다. Therefore, as described above, the retentive water generation preventing unit 30 for spraying the high pressure water in the rolling direction of the rolled plate 1 and the retentive water generation preventing unit 30 for spraying the high pressure water in the reverse direction of the rolling plate 1 traveling direction Cooling water is collected and flows on the surface of the rolled sheet 1 at the same time so as to fall below the rolled sheet 1 to prevent the retention of water in the rolled sheet 1.

이때, 냉각설비(10)의 입측에 배치되어 고압수를 압연 판재(1)의 진행방향으로 분사시키는 3개의 체류수발생 방지유닛(30)은, 후술할 바와 같이 7번 냉각유닛(20)을 기준으로 사용되는 냉각유닛(20)의 개수가 4개 이상인 경우 사용하면, 압연 판재(1)의 체류수 발생방지에 바람직하고, 4번과 5번의 냉각유닛(20) 사이에 위치하여 압연 판재(1)의 진행방향으로 고압수를 분사시키는 1개의 체류수발생 방지유닛(30)은 7번 냉각유닛(20)을 기준으로 사용되는 냉각유닛(20)의 개수가 4개 미만인 경우 사용하면 압연 판재(1)의 체류수 발생방지에 바람직하다.At this time, the three residual water generation prevention unit 30 which is disposed at the inlet side of the cooling facility 10 and sprays the high-pressure water in the advancing direction of the rolled sheet material 1, uses the seventh cooling unit 20 as described later. When the number of the cooling unit 20 used as a reference is 4 or more, it is preferable to prevent the retention of water in the rolled sheet 1, and is located between the 4 and 5 cooling units 20 and the rolled sheet ( 1) The one residence water generation prevention unit 30 for spraying the high pressure water in the traveling direction of 1) is used when the number of cooling units 20 used for the cooling unit 20 based on the number 7 is less than four. It is preferable to prevent the generation of residual water in (1).

체류수발생 방지유닛(30)의 위치나 개수는 본 실시예에 한정되지 않고 냉각 설비(10)의 압연 판재(1) 입측과 출측 및 그 사이 중 어느 하나에 배치되어 압연 판재(1)에 발생하는 체류수를 방지할 수 있는 것이라면 어떠한 위치나 개수라도 가능하다. The position or number of the retentive water generation preventing unit 30 is not limited to the present embodiment, but is disposed in the rolled sheet 1 at the entry and exit sides of the rolled sheet 1 of the cooling installation 10, and is generated in the rolled sheet 1. Any position or number can be used as long as the number of stays can be prevented.

전술된 바와 같은 냉각설비(10)를 사용하는 본 발명에 따른 압연 판재 냉각방법은 압연 판재(1)가 냉각수 분사구간을 통과한 후 분사된 냉각수의 일부가 압연 판재(1)에 체류하는 체류수의 체류구간과 체류시간이 최소화될 수 있도록 냉각설비(10)의 압연 판재(1) 출측을 기준으로 냉각수 분사구간을 설정하고 조정하게 된다. In the method for cooling a rolled sheet according to the present invention using the cooling system 10 as described above, a portion of the cooling water sprayed after the rolled sheet 1 passes through the coolant jetting section remains in the rolled sheet 1. The cooling water injection section is set and adjusted based on the exit of the rolled sheet material 1 of the cooling installation 10 so that the residence time and the residence time of the cooling machine 10 can be minimized.

본 실시예에서 사용되는 냉각설비(10)의 경우에는 7번 냉각유닛(20)을 기준으로 냉각수 분사구간을 설정하고 조정하게 된다. In the case of the cooling system 10 used in the present embodiment, the cooling water injection section is set and adjusted based on the cooling unit 20.

즉, 예컨대 압연 판재(1)의 두께나 종류에 따라 냉각량이 많지 않은 경우에는 7번 냉각유닛(20)만을 사용하고, 압연 판재(1)의 두께가 증가하거나 냉각량이 많은 종류의 압연 판재(1)를 냉각하는 경우에는 사용되는 냉각유닛(20)을 7번 냉각유닛(20)으로부터 역순으로 증가시키면서 냉각설비(10)에서 진행하는 압연 판재(1)를 냉각하게 된다. That is, for example, when the amount of cooling is not large depending on the thickness or type of the rolled sheet 1, only the seventh cooling unit 20 is used, and the thickness of the rolled sheet 1 increases or the type of rolled sheet having a large amount of cooling 1 In the case of cooling), the rolled sheet material 1 advancing in the cooling installation 10 is cooled while increasing the cooling unit 20 used in the reverse order from the seventh cooling unit 20.

따라서, 압연 판재(1)의 두께가 증가하거나 냉각량이 많이 필요해짐에 따라 냉각설비(10)의 냉각수 분사구간이 냉각설비(10)의 압연 판재(1) 출측인 7번 냉각유닛(20)을 기준으로 냉각설비(10)의 압연 판재(1) 입측으로 점진적으로 증가하게 된다. Therefore, as the thickness of the rolled sheet 1 increases or the amount of cooling is required, the cooling water spraying section of the cooling apparatus 10 changes the number 7 cooling unit 20 which is the rolled sheet 1 of the cooling apparatus 10. As a reference, it gradually increases toward the inlet side of the rolled sheet 1 of the cooling installation 10.

이와 같이, 압연 판재(1)의 출측을 기준으로 냉각수 분사구간을 설정하고 조정하게 되므로, 압연 판재(1)가 냉각수 분사구간을 통과한 후 분사된 냉각수의 일부가 압연 판재(1)에 체류하는 체류수가 7번 냉각유닛(20) 이후에 발생하게 된다. As described above, since the coolant spray section is set and adjusted based on the exit side of the rolled sheet material 1, a part of the coolant sprayed after the rolled sheet material 1 passes through the coolant spray section remains in the rolled plate 1. Residual water is generated after the cooling unit 20.

이에 따라, 체류수의 체류구간과 체류시간이 최소화될 수 있으므로, 체류수의 존재에 의해서 발생하는 압연 판재(1)의 불균일 냉각에 의한 압연 판재(1) 표면의 변형을 최소화할 수 있게 된다. Accordingly, since the retention period and the residence time of the retained water can be minimized, it is possible to minimize the deformation of the surface of the rolled plate 1 due to non-uniform cooling of the rolled sheet 1 caused by the presence of the retained water.

도3은 압연 판재의 두께에 따라 도2에 도시된 냉각설비를 사용하여 본 발명에 따른 압연 판재 냉각방법으로 압연 판재를 냉각하는 경우의 냉각수 분사구간과 체류수 체류구간을 나타내는 도면이고, 도4는 압연 판재의 두께에 따라 도2에 도시된 냉각설비를 사용하여 종래의 압연 판재 냉각방법으로 압연 판재를 냉각하는 경우의 냉각수 분사구간과 체류수 체류구간을 나타내는 도면이다. 3 is a view showing a coolant spray section and a retention water retention section in the case of cooling a rolled sheet by the rolling sheet cooling method according to the present invention using the cooling apparatus shown in FIG. 2 according to the thickness of the rolled sheet. 2 is a view showing a coolant jetting section and a retention water retention section in the case of cooling a rolled sheet by a conventional rolled sheet cooling method using a cooling apparatus shown in FIG. 2 according to the thickness of the rolled sheet.

종래 압연 판재 냉각방법으로 압연 판재(1)를 냉각하는 경우에는 본 발명에 따른 압연 판재 냉각방법과 달리 냉각설비(10)의 4번 냉각유닛(20)과 5번 냉각유닛(20) 사이에 배치되며 압연 판재(1)의 진행방향으로 고압수를 분사하는 체류수발생 방지유닛(30)이 불필요하다. In the case of cooling the rolled sheet 1 by the conventional rolled sheet cooling method, it is arranged between the 4th cooling unit 20 and the 5th cooling unit 20 of the cooling installation 10, unlike the rolling sheet cooling method according to the present invention. And there is no need for the retention water generation unit 30 for spraying high pressure water in the traveling direction of the rolled plate (1).

왜냐하면, 냉각수 분사구간이 냉각설비(10)의 압연 판재(1) 입측을 기준으로 설정되고 조정되기 때문에 압연 판재(1) 진행방향으로 고압수를 분사하는 체류수발생 방지유닛(30)은 압연 판재(1) 입측에 배치된 체류수발생 방지유닛(30)으로 충분하기 때문이다. Because the cooling water spraying section is set and adjusted on the basis of the rolled sheet 1 entrance of the cooling system 10, the retentive water generation preventing unit 30 for spraying the high pressure water in the rolling plate 1 traveling direction is a rolled sheet material. (1) This is because the residual water generation preventing unit 30 disposed at the entrance side is sufficient.

따라서, 도4에 도시된 바와 같이 종래 압연 판재 냉각방법으로 압연 판재(1)를 냉각하는 경우에는 본 발명에 따른 압연 판재 냉각방법으로 압연 판재(1)를 냉각하는 경우와 달리 냉각설비(10)의 4번 냉각유닛(20)과 5번 냉각유닛(20) 사이에 배치되고 압연 판재(1)의 진행방향으로 고압수를 분사하는 체류수발생 방지유닛(30)은 냉각설비(10)에서 없게 된다. Therefore, as shown in FIG. 4, in the case of cooling the rolled sheet material 1 by the conventional rolled sheet cooling method, unlike the case of cooling the rolled sheet material 1 by the rolled sheet cooling method according to the present invention, the cooling facility 10 is used. The cooling water 10 is not disposed between the cooling unit 10 and the cooling water generation unit 30 disposed between the cooling unit 20 and the cooling unit 20 in which the high pressure water is sprayed in the traveling direction of the rolled sheet 1. do.

도시된 바와 같이 도3의 (a)와 도4의 (a)의 경우에는, 압연 판재(1)의 두께가 18mm 내지 21mm인 경우에, 본 발명에 따른 압연 판재 냉각방법으로 압연 판재(1)를 냉각설비(10)에서 냉각하는 경우와, 종래의 압연 판재 냉각방법으로 압연 판재(1)를 냉각설비(10)에서 냉각하는 경우를 나타낸다. As shown in FIGS. 3A and 4A, when the thickness of the rolled sheet 1 is between 18 mm and 21 mm, the rolled sheet member 1 is subjected to the rolling sheet cooling method according to the present invention. The case where it cools in the cooling installation 10 and the case where the rolling board | plate material 1 is cooled in the cooling installation 10 by the conventional rolling plate cooling method is shown.

또한, 도3의 (b)와 도4의 (b)의 경우에는, 압연 판재(1)의 두께가 21mm 내지 25mm인 경우에, 본 발명에 따른 압연 판재 냉각방법으로 압연 판재(1)를 냉각설비(10)에서 냉각하는 경우와, 종래의 압연 판재 냉각방법으로 압연 판재(1)를 냉각설비(10)에서 냉각하는 경우를 나타낸다. 3 (b) and 4 (b), when the thickness of the rolled sheet 1 is 21 mm to 25 mm, the rolled sheet material 1 is cooled by the rolling sheet cooling method according to the present invention. The case where it cools in the installation 10 and the case where the rolled sheet material 1 is cooled by the cooling installation 10 by the conventional rolling plate cooling method is shown.

그리고, 도3의 (c)와 도4의 (c)의 경우에는, 압연 판재(1)의 두께가 25mm 내지 30mm인 경우에, 본 발명에 따른 압연 판재 냉각방법으로 압연 판재(1)를 냉각설비(10)에서 냉각하는 경우와, 종래의 압연 판재 냉각방법으로 압연 판재(1)를 냉각설비(10)에서 냉각하는 경우를 나타낸다. 3 (c) and 4 (c), when the thickness of the rolled sheet 1 is 25 mm to 30 mm, the rolled sheet member 1 is cooled by the rolling sheet cooling method according to the present invention. The case where it cools in the installation 10 and the case where the rolled sheet material 1 is cooled by the cooling installation 10 by the conventional rolling plate cooling method is shown.

도3의 (a)와 (b) 및 (c) 그리고 도4의 (a)와 (b) 및 (c) 각각의 하단에 도시된 실선은 냉각수 분사구간을 나타내고 점선은 체류수 체류구간을 나타낸다. Solid lines shown at the lower ends of FIGS. 3A, 3B, and 3C, and FIGS. 4A, 4B, and 4C respectively indicate coolant injection sections and dotted lines represent retention water retention sections. .

도3과 도4에 도시된 바와 같이 압연 판재(1)의 두께가 증가함에 따라 냉각수를 분사하는 냉각유닛(20)의 개수도 증가하게 된다. 3 and 4, as the thickness of the rolled sheet 1 increases, the number of cooling units 20 for spraying the cooling water also increases.

도4에 도시된 바와 같이 종래의 압연 판재 냉각방법으로 압연 판재(1)를 냉각하는 경우에는 냉각수를 분사하는 냉각유닛(20)이 도4의 (a)의 경우에는 1번 냉각유닛(20)과 2번 냉각유닛(20) 2개이었으나, 압연 판재(1)의 두께가 증가함에 따라 도4의 (b)의 경우에는 1번 냉각유닛(20)에서 3번 냉각유닛(20)까지 냉각수를 분사하고, 도4의 (c)의 경우에는 1번 냉각유닛(20)에서 4번 냉각유닛(20)까지 냉각수를 분사하게 된다. As shown in FIG. 4, in the case of cooling the rolled sheet 1 by the conventional rolled sheet cooling method, the cooling unit 20 for spraying the cooling water is the first cooling unit 20 in the case of FIG. And two cooling units 20, but as the thickness of the rolled sheet 1 increases, in the case of FIG. 4 (b), cooling water is cooled from cooling unit 20 to cooling unit 20 from cooling unit 20. In the case of FIG. 4 (c), the cooling water is sprayed from the first cooling unit 20 to the fourth cooling unit 20.

이때, 도4의 (a)의 경우에는 냉각설비(10)의 압연 판재(1) 입측에 배치된 체류수발생 방지유닛(30)과, 2번 냉각유닛(20)과 3번 냉각유닛(20) 사이에 배치된 체류수발생 방지유닛(30)을 사용하여 압연 판재(1) 표면의 체류수 발생을 방지하고, 도4의 (b)와 (c)의 경우에는 냉각설비(10)의 압연 판재(1) 입측에 배치된 체류수발생 방지유닛(30)과, 4번 냉각유닛(20)과 5번 냉각유닛(20) 사이에 배치된 체류수발생 방지유닛(30)을 사용하여 압연 판재(1) 표면의 체류수 발생을 방지한다. At this time, in the case of Fig. 4 (a), the retentive water generation prevention unit 30, the second cooling unit 20 and the third cooling unit 20 arranged on the inlet side of the rolled sheet 1 of the cooling installation 10 ) To prevent the generation of residual water on the surface of the rolled sheet 1 using the residual water generation preventing unit 30 disposed therebetween, and in the case of FIGS. 4B and 4C, the cooling facility 10 is rolled. Rolled sheet material using the residual water generation prevention unit 30 arrange | positioned at the board | plate material 1 entrance side, and the residual water generation prevention unit 30 arrange | positioned between the 4th cooling unit 20 and the 5th cooling unit 20. (1) To prevent the generation of residual water on the surface.

반면에, 본 발명에 따른 압연 판재 냉각방법으로 압연 판재(1)를 냉각하는 경우에는 냉각수를 분사하는 냉각유닛(20)이 도3의 (a)의 경우에는 7번 냉각유닛(20) 하나이었으나, 압연 판재(1)의 두께가 증가함에 따라 도시된 바와 같이 도3의 (b)의 경우에는 7번 냉각유닛(20)과 6번 냉각유닛(20)에서 냉각수를 분사하고, 도3의 (c)의 경우에는 7번 냉각유닛(20)과 6번 냉각유닛(20) 및 5번 냉각유닛(20)에서 냉각수를 분사하게 된다. On the other hand, in the case of cooling the rolled sheet 1 by the method for cooling the rolled sheet according to the present invention, the cooling unit 20 for spraying the cooling water was one of the seventh cooling units 20 in FIG. As the thickness of the rolled sheet 1 increases, in the case of FIG. 3 (b), cooling water is injected from the cooling unit 20 and the cooling unit 20, and the cooling unit 20 of FIG. In the case of c), the cooling water is sprayed from the cooling unit 20, the cooling unit 20, and the cooling unit 20.

이때, 도3의 (a)와 (b) 및 (c)의 경우에는 냉각설비(10)의 압연 판재(1) 출측에 배치된 체류수발생 방지유닛(30)과, 4번 냉각유닛(20)과 5번 냉각유닛(20) 사이에 배치된 체류수발생 방지유닛(30)을 사용하여 압연 판재(1) 표면의 체류수 발생을 방지한다. At this time, in the case of Fig. 3 (a), (b) and (c), the residual water generation prevention unit 30 arranged on the exit side of the rolled sheet material 1 of the cooling installation 10 and the fourth cooling unit 20 ) And the retention water generation prevention unit 30 disposed between the cooling unit 20 and the number 5 is used to prevent the generation of retention water on the surface of the rolled sheet 1.

전술된 바와 같이, 종래의 압연 판재 냉각방법으로 압연 판재(1)를 냉각하는 경우에는 도4에 도시된 바와 같이 냉각설비(10)의 입측을 기준으로 냉각수 분사구간을 설정하고 조정하게 된다. As described above, in the case of cooling the rolled sheet 1 by the conventional rolled sheet cooling method, as shown in FIG. 4, the coolant spray section is set and adjusted based on the entrance side of the cooling facility 10.

즉, 1번 냉각유닛(20)을 기준으로 순차적으로, 냉각설비(10)의 압연 판재(1) 출측 방향으로, 냉각수가 분사되는 냉각유닛(20)을 압연 판재(1)의 두께가 증가함에 따라 증가시키게 된다. That is, the thickness of the rolling plate 1 increases the cooling unit 20 to which the coolant is injected, in the direction of exiting the rolling plate 1 of the cooling installation 10 sequentially based on the first cooling unit 20. Increase accordingly.

따라서, 도4의 (a)와 (b) 및 (c)의 하단에 도시된 바와 같이 냉각수 분사구간은 압연 판재(1)의 두께가 증가함에 따라 1번 냉각유닛(20)을 기준으로 순차적으로 증가하게 된다. Therefore, as shown in the lower end of Figure 4 (a) and (b) and (c) the cooling water jet section is sequentially based on the number 1 cooling unit 20 as the thickness of the rolled sheet (1) increases Will increase.

또한, 냉각수 분사구간이 끝난 후 분사된 냉각수의 일부가 압연 판재(1)에 체류하는 체류수 체류구간은 냉각수 분사구간을 이루는 냉각유닛(20) 중 출측 방향에 가장 가까운 냉각유닛(20)의 다음 냉각유닛(20)에서 시작하여 교정기(4)까지가 된다. In addition, the residence water retention section in which a part of the cooling water injected after the cooling water injection section stays in the rolled sheet 1 is next to the cooling unit 20 closest to the discharge direction among the cooling units 20 constituting the cooling water injection section. It starts with the cooling unit 20 and becomes the calibrator 4.

즉, 도4의 (a)의 경우에는 3번 냉각유닛(20)에서 교정기(4)까지의 구간이 되고, 도4의 (b)의 경우에는 4번 냉각유닛(20)에서 교정기(4)까지의 구간이 되며, 도 4의 (c)의 경우에는 5번 냉각유닛(20)에서 교정기(4)까지의 구간이 된다. That is, in the case of FIG. 4A, the section is from the third cooling unit 20 to the calibrator 4, and in the case of FIG. 4B, the calibrator 4 in the fourth cooling unit 20. In the case of Figure 4 (c) is a section from the fifth cooling unit 20 to the calibrator (4).

이와는 반대로, 본 발명에 따른 압연 판재 냉각방법으로 압연 판재(1)를 냉각하는 경우에는 냉각설비(10)의 압연 판재(1) 출측을 기준으로 냉각수 분사구간을 설정하고 조정하게 된다. On the contrary, in the case of cooling the rolled sheet 1 by the rolling sheet cooling method according to the present invention, the cooling water injection section is set and adjusted based on the exit of the rolled sheet 1 of the cooling installation 10.

즉, 7번 냉각유닛(20)을 기준으로 역순으로, 냉각설비(10)의 입측 방향으로, 압연 판재(1)의 두께가 증가함에 따라 냉각수가 분사되는 냉각유닛(20)을 증가시키게 된다. That is, in the reverse order with respect to the seventh cooling unit 20, in the inlet direction of the cooling facility 10, as the thickness of the rolled sheet material 1 increases, the cooling unit 20 to which the cooling water is injected is increased.

따라서, 도3의 (a)와 (b) 및 (c)의 하단에 각각 도시된 바와 같이 냉각수 분사구간은 압연 판재(1)의 두께가 증가함에 따라 7번 냉각유닛(20)을 기준으로 역순으로 증가하게 된다. Therefore, as shown in the lower portions of (a), (b) and (c) of Fig. 3, the coolant jetting section is reversed based on the seventh cooling unit 20 as the thickness of the rolled sheet 1 increases. To increase.

또한, 체류수 체류구간은 도시된 바와 같이 압연 판재(1)의 두께 증가에 관계없이 항상 7번 냉각유닛(20)에서 시작하게 되기 때문에 체류수 체류구간은 7번 냉각유닛(20)에서 교정기(4) 사이의 구간이 된다. In addition, since the retention water retention section always starts in the cooling unit 20, regardless of the increase in the thickness of the rolled plate (1) as shown, the retention water retention section is a calibrator (7) in the cooling unit 20 4) section.

물론, 도4에 도시된 바와 같이 종래 압연 판재 냉각방법으로 냉각설비(10)에서 압연 판재(1)를 냉각하는 경우에는, 사용되는 냉각유닛(20) 즉, 냉각수를 분사하는 냉각유닛(20)이 증가함에 따라 체류수 체류구간이 감소되지만, 전술되고 도3에 도시된 바와 같이 본 발명에 따른 압연 판재 냉각방법으로 압연 판재(1)를 냉각하는 경우보다 상대적으로 그 길이가 길게 된다. Of course, in the case of cooling the rolled sheet material 1 in the cooling installation 10 by the conventional rolled sheet cooling method as shown in Figure 4, the cooling unit 20 that is used, that is, the cooling unit 20 for spraying the cooling water As this increases, the retention water retention period is reduced, but the length thereof is relatively longer than when the rolled sheet material 1 is cooled by the rolled sheet cooling method according to the present invention as described above and shown in FIG.

따라서, 종래 압연 판재 냉각방법으로, 즉 냉각설비(10)의 압연 판재(1) 입측을 기준으로 냉각수 분사구간을 설정하고 조정하는 경우보다, 본 발명에 따른 압연 판재 냉각방법으로, 즉 냉각설비(10)의 압연 판재(1) 출측을 기준으로 냉각수 분사구간을 설정하고 조정하는 경우가 체류수의 체류구간과 체류시간이 상대적으로 더 짧게 되어 체류수의 영향을 덜 받게 된다. Therefore, rather than setting and adjusting the cooling water spraying section based on the conventional rolled sheet cooling method, that is, on the basis of the entrance of the rolled sheet 1 of the cooling installation 10, that is, the cooling equipment ( In the case of setting and adjusting the coolant jetting section based on the exit of the rolled sheet 1 of 10), the retention section and the residence time of the retained water are relatively shorter, which is less affected by the retained water.

즉, 압연 판재(1)에 체류수가 존재하여 나타나는 압연 판재(1)의 불균일 냉각에 의하여 발생하는 압연 판재(1) 표면의 변형이 종래 압연 판재 냉각방법으로 압연 판재(1)를 냉각하는 경우보다 더 적게 이루어지게 된다. That is, the deformation of the surface of the rolled sheet material 1 caused by the uneven cooling of the rolled sheet material 1 due to the presence of the residual water in the rolled sheet material 1 is less than that of the case where the rolled sheet material 1 is cooled by the conventional rolled sheet cooling method. Less is done.

따라서, 교정기(4)로 들어가는 압연 판재(1)의 평탄도가 좋아지기 때문에, 교정기(4)에 의해서 압연 판재(1)를 평탄화해야할, 즉 교정기(4)의 교정율이 작아지게 되어서 바람직하다.Therefore, since the flatness of the rolled sheet material 1 entering the straightener 4 improves, it is preferable that the straightened sheet 4 should be flattened by the straightener 4, that is, the correction rate of the straightener 4 becomes small. .

도3과 도4에 도시된 바와 같이 본 발명에 따른 압연 판재 냉각방법으로 냉각설비(10)에서 압연 판재(1)를 냉각하는 경우에는, 종래 압연 판재 냉각방법으로 냉각하는 경우와 비교해서, 같은 두께의 압연 판재(1)의 경우라도 사용하는 냉각유닛(20)의 개수가 하나 더 적게 된다. 3 and 4, in the case of cooling the rolled sheet material 1 in the cooling apparatus 10 by the rolled sheet cooling method according to the present invention, the same as compared with the case of cooling by the conventional rolled sheet cooling method. Even in the case of the thick rolled sheet 1, the number of the cooling units 20 to be used is one less.

이는 본 발명에 따른 압연 판재 냉각방법으로 냉각설비(10)를 이용하여 압연 판재(1)를 냉각하는 경우에는, 냉각수에 의한 압연 판재(1)의 냉각 이전에, 즉 수냉각 이전에 공기에 의한 냉각인 공냉이 이루어지기 때문에, 공냉에 의한 압연 판재(1)의 영향을 최소화하기 위해서, 종래 압연 판재 냉각방법보다 급속냉각이 이루 어져야 하기 때문이다. This is a method of cooling the rolled sheet material 1 using the cooling apparatus 10 by the rolling sheet cooling method according to the present invention, before cooling the rolled sheet material 1 by cooling water, that is, before water cooling by air. This is because rapid cooling is achieved because air cooling, which is cooling, is to be performed in order to minimize the effect of the rolling plate 1 due to air cooling.

아래의 표 1은 종래 압연 판재 냉각방법과 본 발명의 압연 판재 냉각방법으로 두께가 25mm 내지 30mm인 압연 판재(1)를 냉각하는 경우 압연 판재(1)의 시험 데이터를 나타내는 표이다. Table 1 below is a table showing the test data of the rolled sheet material 1 when the rolled sheet material 1 having a thickness of 25 mm to 30 mm by the conventional rolled sheet cooling method and the rolled sheet cooling method of the present invention.

표에서 알 수 있는 바와 같이, 본 발명의 압연 판재 냉각방법으로 압연 판재(1)를 냉각하는 경우가 종래의 압연 판재 냉각방법으로 압연 판재(1)를 냉각하는 경우보다, 압연 판재(1)의 평탄도가 좋아지고 냉간교정율이 낮아짐을 알 수 있다. As can be seen from the table, the case where the rolled sheet material 1 is cooled by the rolled sheet material cooling method of the present invention is higher than that when the rolled sheet material 1 is cooled by the conventional rolled plate cooling method. The flatness is improved and the cold correction rate is lowered.

구분division 종래 압연 판재 냉각방법Conventional Rolled Sheet Cooling Method 본 발명의 압연 판재 냉각방법Rolled sheet cooling method of the present invention 사용된 냉각유닛Cooling Unit Used 4개Four 3개Three 제품매수(매)Number of products 1919 2222 표면파고(mm)Surface Crest (mm) 22.222.2 14.814.8 냉간교정율(%)Cold correction rate (%) 8989 6060 항복응력(MPa)Yield Stress (MPa) 479479 476476 인장응력(MPa)Tensile Stress (MPa) 558558 549549

이상과 같이 본 발명은 비록 한정된 실시예와 도면에 의해 설명되었으나, 본 발명은 이것에 의해 한정되지 않으며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 본 발명의 기술사상과 아래에 기재될 특허청구범위의 균등범위 내에서 다양한 수정 및 변형이 가능함은 물론이다. As described above, although the present invention has been described by way of limited embodiments and drawings, the present invention is not limited thereto, and the technical concept of the present invention will be described by those skilled in the art to which the present invention pertains. Of course, various modifications and variations are possible within the scope of equivalents of the claims to be described.

도 1의 (a)는 알려진 후판제품 생산(압연)공정을 도시한 공정도이다. Figure 1 (a) is a process diagram showing a known thick plate product production (rolling) process.

도 1의 (b)는 도1의 (a)의 냉각설비에 의한 가속 냉각 공정을 도시한 공정도이다. FIG. 1B is a process diagram showing an accelerated cooling process by the cooling apparatus of FIG. 1A.

도2는 본 발명에 따른 압연 판재 냉각방법의 일실시예에 사용되는 냉각설비를 나타내는 개략도이다. Figure 2 is a schematic diagram showing a cooling facility used in one embodiment of a rolled sheet cooling method according to the present invention.

도3은 압연 판재의 두께에 따라 도2에 도시된 냉각설비를 사용하여 본 발명에 따른 압연 판재 냉각방법으로 압연 판재를 냉각하는 경우의 냉각수 분사구간과 체류수 체류구간을 나타내는 도면이다. 3 is a view showing a coolant spray section and a retention water retention section in the case of cooling a rolled sheet by the rolling sheet cooling method according to the present invention using the cooling apparatus shown in FIG. 2 according to the thickness of the rolled sheet.

도4는 압연 판재의 두께에 따라 도2에 도시된 냉각설비를 사용하여 종래의 압연 판재 냉각방법으로 압연 판재를 냉각하는 경우의 냉각수 분사구간과 체류수 체류구간을 나타내는 도면이다. 4 is a view showing a coolant jetting section and a retention water retention section in the case of cooling a rolled sheet by a conventional rolled sheet cooling method using a cooling apparatus shown in FIG. 2 according to the thickness of the rolled sheet.

* 도면의 주요부분에 대한 부호의 설명 *         Explanation of symbols on the main parts of the drawings

1 : 압연 판재 2 : 가열로1: rolled sheet 2: heating furnace

3 : 압연기 4 : 교정기3: rolling mill 4: straightener

5 : 냉각대 6 : 압연 소재5: cooling stand 6: rolled material

10 : 냉각설비 20 : 냉각유닛10: cooling facility 20: cooling unit

21 : 냉각수 노즐헤드 22 : 냉각수 공급관21: cooling water nozzle head 22: cooling water supply pipe

23 : 냉각수 제어밸브 30 : 체류수발생 방지유닛23: Cooling water control valve 30: Residual water generation prevention unit

31 : 고압수 노즐헤드 31: high pressure nozzle head

Claims (7)

압연된 압연 판재의 두께 또는 종류에 따라 냉각수 분사구간을 조정할 수 있는 냉각설비를 이용하여 압연 판재를 냉각하는 압연 판재 냉각방법에 있어서, In the rolled sheet cooling method for cooling the rolled sheet using a cooling facility that can adjust the coolant spray section according to the thickness or type of the rolled rolled sheet, 압연 판재에 분사된 냉각수의 일부가 압연 판재에 체류하는 체류수의 체류구간과 체류시간을 최소화하도록 압연 판재 입측으로부터 출측까지 순차로 배치되는 1번에서 N번의 N개의 단위 냉각유닛을 포함하는 상기 냉각설비의 압연 판재 출측에 위치하는 N번 냉각유닛을 기준으로 압연 판재의 두께 또는 종류에 따라 입측방향으로 순차적으로 각 단위별 냉각유닛의 냉각수 분사를 조정하여 냉각수 분사구간을 설정하며,Said cooling comprising one to N N unit cooling units sequentially arranged from the entrance to the exit of the rolled sheet so that a part of the cooling water sprayed on the rolled sheet is minimized in the retention period and the residence time of the retained water in the rolled sheet. Based on the cooling unit No. N located on the rolled sheet exit side of the equipment, the cooling water injection section is set by adjusting the coolant injection of the cooling unit for each unit sequentially in the entry direction according to the thickness or type of the rolled sheet. 상기 냉각유닛 단위별 또는 상기 냉각유닛에 포함되는 냉각수 노즐헤드 단위별로 냉각수 분사량과 분사속도를 조정하는 것을 특징으로 하는 압연 판재 냉각방법.Rolling sheet cooling method characterized in that for adjusting the cooling water injection amount and the injection speed for each of the cooling unit unit or cooling water nozzle head unit included in the cooling unit. 삭제delete 제1항에 있어서, 상기 냉각설비의 압연 판재 입측과 출측 및 그 사이 중 어느 하나에 배치된 하나 이상의 체류수발생 방지유닛을 통해서 압연 판재의 체류수 발생을 방지하는 것을 특징으로 하는 압연 판재 냉각방법. The method for cooling a rolled sheet according to claim 1, wherein the rolled sheet is prevented from generating a residual water through at least one residual water generation preventing unit disposed at any one of the entrance and exit of the rolled sheet of the cooling installation and an exit side therebetween. . 제3항에 있어서, 상기 체류수발생 방지유닛은 고압수를 압연 판재에 분사하여 체류수 발생을 방지하되, 그 분사방향을 압연 판재 진행방향 또는 진행방향의 역방향으로 구별하여 분사하는 것을 특징으로 하는 압연 판재 냉각방법. [4] The method of claim 3, wherein the water retention prevention unit sprays the high pressure water onto the rolled plate to prevent the generation of the retention water, and the spraying direction is divided into the rolling direction or the reverse direction of the rolling direction. Rolled plate cooling method. 제4항에 있어서, 상기 냉각설비의 압연 판재 입측에 배치된 체류수발생 방지유닛은 압연 판재 진행방향으로 고압수를 분사하고, 상기 냉각설비의 압연 판재 출측에 배치된 체류수발생 방지유닛과 상기 냉각설비의 압연 판재 입측과 출측 사이에 배치된 체류수발생 방지유닛은 압연 판재 진행방향의 역방향으로 고압수를 분사하는 것을 특징으로 하는 압연 판재 냉각방법. 5. The retentive water generation preventing unit of claim 4, wherein the residing water generation preventing unit disposed at the inlet side of the rolled sheet of the cooling system injects high pressure water in a rolling plate traveling direction, and the residing water generation preventing unit disposed at the side of the rolled plate of the cooling system. And a retentive water generation preventing unit disposed between the entry and exit sides of the rolled sheet of the cooling installation, injects high-pressure water in the reverse direction of the rolled sheet moving direction. 제5항에 있어서, 상기 냉각설비의 압연 판재 입측과 출측 사이에 배치되되 압연 판재 진행방향으로 고압수를 분사하는 하나 이상의 체류수발생 방지유닛을 더 포함하여 체류수 발생을 방지하는 것을 특징으로 하는 압연 판재 냉각방법. 6. The method of claim 5, further comprising at least one residing water preventing unit disposed between the entry and exit side of the rolled sheet of the cooling equipment and spraying the high-pressure water in the rolling plate advancing direction to prevent the residing water generation. Rolled sheet cooling method. 삭제delete
KR1020080029817A 2008-03-31 2008-03-31 Method for cooling of rolled plate KR100973915B1 (en)