KR100972657B1 - Filtering media for smoking containing the montmorillonite and cigarette filter comprising the same - Google Patents
Filtering media for smoking containing the montmorillonite and cigarette filter comprising the same Download PDFInfo
- Publication number
- KR100972657B1 KR100972657B1 KR1020070138345A KR20070138345A KR100972657B1 KR 100972657 B1 KR100972657 B1 KR 100972657B1 KR 1020070138345 A KR1020070138345 A KR 1020070138345A KR 20070138345 A KR20070138345 A KR 20070138345A KR 100972657 B1 KR100972657 B1 KR 100972657B1
- Authority
- KR
- South Korea
- Prior art keywords
- tobacco
- montmorillonite
- filtration
- smoking
- cigarette
- Prior art date
Abstract
본 발명은 몬모릴로나이트를 함유하는 흡연 여과용 여과물질 및 이를 포함하는 담배에 관한 것으로, 좀 더 구체적으로는 몬모릴로나이트를 물에 용해시켜 침전되는 불순물을 제거한 다음, 40∼60℃로 유지되는 기포발생기가 부착된 수조에서 2∼4일간 동안 숙성 및 교반 작업을 거쳐 호기성 미생물인 생균을 배양시킨 다음, 상기 배양물을 40∼60℃의 온도에서 건조시킨 후, 이를 -40∼-45℃에서 멸균시킨 1000∼1200 메쉬의 몬모릴로나이트 분말 94∼99.9중량%와 1000∼1200 메쉬의 티탄옥사이드 0.1∼6중량%로 구성된 몬모릴로나이트를 함유하는 흡연 여과용 여과물질 및 이를 포함하는 담배에 관한 것이다.The present invention relates to a filtration material for smoking filtration containing montmorillonite and a cigarette comprising the same, and more specifically, to remove the impurities precipitated by dissolving montmorillonite in water, and then attached to the bubble generator maintained at 40 ~ 60 ℃ After aging and stirring for 2 to 4 days in a water tank, the aerobic microorganisms were cultured, and the culture was dried at a temperature of 40 to 60 ° C, and then sterilized at -40 to -45 ° C. The present invention relates to a filtration material for smoking filtration comprising montmorillonite composed of 94 to 99.9 wt% of 1200 mesh montmorillonite powder and 0.1 to 6 wt% of titanium oxide of 1000 to 1200 mesh, and a cigarette comprising the same.
본 발명은 기존에 담배흡입시 인체로 들어오는 니코틴, 타르 등 각종 유해물질을 현저하게 줄여 주면서도 담배 맛을 순하고 부드러우며 신선하게 제공할 수 있을 뿐만 아니라 흡연시 오존(O3)이 방출되는 것을 막을 수 있어 소비자에게 좀더 순하고 부드러운 담배 맛을 안전하게 제공할 수 있는 효과가 있다.The present invention can significantly reduce the harmful substances such as nicotine, tar, etc. that enters the human body when inhaling a cigarette while providing a mild, soft and fresh taste of tobacco as well as preventing ozone (O 3 ) from being released during smoking. There is an effect that can provide a more mild and soft tobacco taste to consumers safely.
몬모릴로나이트, 티탄옥사이드, 담배, 흡연, 여과 Montmorillonite, Titanium Oxide, Tobacco, Smoking, Filtration
Description
본 발명은 몬모릴로나이트를 함유하는 흡연 여과용 여과물질 및 이를 포함하는 담배에 관한 것으로, 좀 더 구체적으로는 원적외선 및 음이온을 발산하고, 향균력, 탈취력, 다량의 미네랄을 함유하는 천연광물질인 몬모릴로나이트와 티탄옥사이드 분말로 구성된 흡연 여과용 여과물질 및 이를 포함하는 담배에 관한 것이다.The present invention relates to a filtration material for smoking filtration containing montmorillonite and a cigarette comprising the same. More specifically, montmorillonite and titanium oxide, which emits far-infrared rays and anions, contain antibacterial activity, deodorizing power, and a large amount of minerals. It relates to a filter material for smoking filtration composed of a powder and a cigarette comprising the same.
일반적으로, 담배 연기에는 다양한 종류의 독성 물질이 들어있는 바, 특히 니코틴, 일산화탄소, 타르 등이 대표적인 독성물질이며, 이러한 독성물질은 폐암 등과 같은 질병을 유발하게 된다. 이에 따라 담배에는 담배 연기를 여과하는 필터가 구비되어 있으며, 상기 필터는 담배 입자를 내장한 외피의 단부에 내장 배치되고, 통과하는 담배 연기를 여과하게 된다.In general, cigarette smoke contains various types of toxic substances, in particular nicotine, carbon monoxide, tar and the like are typical toxic substances, and these toxic substances cause diseases such as lung cancer. Accordingly, the cigarette is provided with a filter for filtering the tobacco smoke, the filter is embedded in the end of the outer shell containing the tobacco particles, it is to filter the tobacco smoke passing through.
통상의 담배필터는 타르 및 니코틴 등 인체 유해물질을 걸러주는 기능으로 사용하는 흡착제로 쓰이는 다공질 고체입자 활성탄(charcoal)과 제올라이트(zeolite) 또는 활성탄과 제올라이트를 한 개의 과립으로 결합시켜 여과 및 탈취기능을 부여한 것과, 다공질 고체로서 실리카, 알루미나, 탄소, 금속산화물 등 무기계의 것과, 합성수지 등 유기계의 것이 있다. 흡착제가 선택적으로 흡착할 수 있는 물질은 다공질 고체 세공 표면의 성질과 세공크기에 따라 결정되며, 세공표면이 친수성인 흡착제로 실리카겔, 활성알루미나, 합성 또는 천연제올라이트 등이 있으며, 이것들은 물처럼 극성인 물질을 잘 흡착한다. 이러한 다공성 막이 설치된 장치를 여과기(filter)라 한다. 여과기를 용도별로 구분하면 청징용 여과기와 케이크용 여과기로 나룰 수 있는데, 담배필터는 청징용 여과기에 속한다.Conventional cigarette filter combines porous solid particle charcoal and zeolite or zeolite or activated carbon and zeolite into one granule, which is used as an adsorbent to filter out harmful substances such as tar and nicotine into one granule for filtration and deodorization. As the porous solids, there are inorganic ones such as silica, alumina, carbon and metal oxides, and organic ones such as synthetic resins. The material that the adsorbent can adsorb selectively is determined by the nature and pore size of the porous solid pore surface.The hydrophilic adsorbent is silica gel, activated alumina, synthetic or natural zeolite. Adsorb the material well. A device equipped with such a porous membrane is called a filter. The filters can be divided into clarifier filters and cake filters. Tobacco filters belong to clarifier filters.
기존의 담배필터에 관한 특허문헌을 살펴보면, 특허문헌 1에서는 독성물질이 인체에 흡수되는 것을 감소시키기 위하여 차의 특이한 향취와 맥반석의 효능을 활용하도록 하는 차와 맥반석 분말을 이용한 담배필터를 제공하고 있다. 특허문헌 2에서는 활성탄과 제올라이트를 혼합한 흡착제를 주성분으로 하는 담배필터의 조성물의 제조방법을 개시하고 있다. 특허문헌 3에서는 벤토나이트 계열의 광물을 주재로 하는 흡연 여과용 여과물질과 이를 포함하는 담배필터, 담배 및 끽연용구를 개시하고 있고, 특허문헌 4에서는 대나무 활성탄을 이용한 담배필터를, 특허문헌 5에서는 담배 첨가향을 흡착시킨 황토의 소성 분말과 과립상의 황토 소성 입자를 각각 담배의 연초와 필터에 포함시켜 구성되는 황토-함유 담배를 개시하고 있다.Looking at the existing patent literature on cigarette filters, Patent Document 1 provides a cigarette filter using tea and ganban stone powder to utilize the unique flavor of tea and the efficacy of ganban stone to reduce the absorption of toxic substances into the human body. .
그러나, 종래에 개시된 기술들은 담배 연기 등을 여과하나, 니코틴, 타르, 일산화탄소 등과 같은 독성 물질과 특히 흡연시 발생되는 오존을 충분히 여과하는 데에 미흡하다는 단점이 있다.However, the techniques disclosed in the prior art have the disadvantage of filtering cigarette smoke and the like, but insufficient filtering of toxic substances such as nicotine, tar, carbon monoxide and the like, especially ozone generated when smoking.
특허문헌 1: 한국 실용신안출원 제2006-0021237호Patent Document 1: Korean Utility Model Application No. 2006-0021237
특허문헌 2: 한국 특허출원 제2005-0012583호Patent Document 2: Korean Patent Application No. 2005-0012583
특허문헌 3: 한국 특허출원 제2005-0054770호Patent Document 3: Korean Patent Application No. 2005-0054770
특허문헌 4: 한국 특허출원 제2006-0032569호Patent Document 4: Korean Patent Application No. 2006-0032569
특허문헌 5: 한국 특허출원 제2002-0011701호Patent Document 5: Korean Patent Application No. 2002-0011701
이에 본 발명에서는 천연광물질인 몬모릴로나이트를 숙성시켜 원적외선, 음이온, 향균력, 탈취력, 및 다량의 미네랄을 활성화시키고, 여기에 오존의 산화능을 가지고 있는 티탄옥사이드를 혼합시켜 제조된 필터입자를 이용하여 담배의 독성물질과 비린 맛을 제공하는 오존을 흡착 및 산화시킬 수 있었다.In the present invention, montmorillonite, a natural mineral, is aged to activate far-infrared rays, anions, antibacterial activity, deodorizing power, and a large amount of minerals. It was able to adsorb and oxidize ozone which gives the substance and fishy taste.
따라서, 본 발명의 목적은 탈취력과 흡수력이 우수한 몬모릴로나이트를 이용하여 기존에 담배흡입시 인체로 들어오는 니코틴, 타르 등 각종 유해물질을 현저하게 줄여 주면서도 담배 맛을 순하고 부드럽고 신선하게 제공할 수 있을 뿐만 아니라 티탄옥사이드 분말(TiO2)을 첨가함으로써 흡연시 오존(O3)이 방출되는 것을 막을 수 있는 몬모릴로나이트를 함유하는 흡연 여과용 여과물질을 제공하는 데 있다.Accordingly, an object of the present invention is to use montmorillonite excellent in deodorizing and absorbing power, while not only significantly reducing various harmful substances such as nicotine and tar coming into the human body when inhaling cigarettes, but also providing a mild, soft and fresh tobacco taste as well as titanium. The present invention provides a filtration material for smoking filtration containing montmorillonite that can prevent the release of ozone (O 3 ) during smoking by adding an oxide powder (TiO 2 ).
본 발명의 다른 목적은 상기 몬모릴로나이트를 함유하는 흡연 여과용 여과물질을 필터, 연초를 수용하는 종이, 및/또는 담배 포장지 등에 포함하여 특유의 비린내도 없게 만들어 소비자에게 좀더 순하고 부드러운 담배 맛을 안전하게 제공할 수 있는 흡연 여과용 여과물질을 포함하는 담배를 제공하는 데 있다.Another object of the present invention is to include a filtration material for montmorillonite containing montmorillonite filter, tobacco containing paper, and / or cigarette wrapping paper without the unique fishy to provide a more gentle and soft tobacco taste to consumers safely To provide a cigarette comprising a filter material for smoking filtration.
상기 목적을 달성하기 위한 본 발명의 몬모릴로나이트를 함유하는 흡연 여과용 여과물질은;Filtration material for smoking filtration containing montmorillonite of the present invention for achieving the above object;
몬모릴로나이트를 물에 용해시켜 침전되는 불순물을 제거한 다음, 40∼60℃로 유지되는 기포발생기가 부착된 수조에서 2∼4일간 동안 숙성 및 교반 작업을 거쳐 호기성 미생물인 생균을 배양시킨 다음, 상기 배양물을 40∼60℃의 온도에서 건조시킨 후, 이를 -40∼-45℃에서 멸균시킨 1000∼1200 메쉬의 몬모릴로나이트 분말 94∼99.9중량%와 1000∼1200 메쉬의 티탄옥사이드 0.1∼6중량%로 구성된 것을 특징으로 한다.After dissolving montmorillonite in water to remove impurities, and then aging and stirring for 2 to 4 days in a bubble bath equipped with a bubble generator maintained at 40 to 60 ℃ to incubate the aerobic microorganisms, and then the culture After drying at a temperature of 40 to 60 ℃, it was composed of 94 to 99.9% by weight of 1000 to 1200 mesh montmorillonite powder sterilized at -40 to -45 ℃ and 0.1 to 6% by weight of 1000 to 1200 mesh titanium oxide It features.
본 발명의 흡연 여과용 여과물질에 있어서, 상기 분말은 기류식 분쇄방법으로 분말화되는 것을 특징으로 한다.In the filter material for smoking filtration of the present invention, the powder is characterized in that powdered by air flow grinding method.
본 발명의 다른 목적을 달성하기 위한 몬모릴로나이트를 함유하는 흡연 여과용 여과물질을 포함하는 담배는;Tobacco comprising a filtration material for smoking filtration containing montmorillonite for achieving another object of the present invention;
종이에 의해 감싸여 연초가 수용되는 연초부와, 상기 연초가 타면서 생성되는 연기 속에 포함된 유해물질을 걸러주는 필터입자를 포함하는 필터부로 구성된 담배에 있어서,In the cigarette comprising a tobacco part wrapped by paper and the tobacco containing accommodating tobacco, and the filter unit including filter particles for filtering the harmful substances contained in the smoke generated by burning the tobacco,
상기 필터입자가 상기 흡연 여과용 여과물질로 입자화된 것을 특징으로 한다.The filter particles are characterized in that the granulated with the filter material for smoking filtration.
본 발명의 흡연 여과용 여과물질을 포함하는 담배에 있어서,In the cigarette comprising the filtration material for smoking filtration of the present invention,
상기 종이는 상기 흡연 여과용 여과물질이 첨가되어 제조된 것을 특징으로 한다.The paper is characterized in that the smoking filtration material is prepared by addition.
본 발명은 기존에 담배흡입시 인체로 들어오는 니코틴, 타르 등 각종 유해물질을 현저하게 줄여 주면서도 담배 맛을 순하고 부드럽고 신선하게 제공할 수 있을 뿐만 아니라 흡연시 오존(O3)이 방출되는 것을 막을 수 있어 소비자에게 좀더 순하고 부드러운 담배 맛을 안전하게 제공할 수 있는 효과가 있다.The present invention can significantly reduce the harmful substances such as nicotine, tar, etc. coming into the human body when inhaling the cigarette while providing a pure, smooth and fresh taste of the cigarette as well as preventing the release of ozone (O 3 ) during smoking. There is an effect that can provide consumers with a milder, softer tobacco taste.
이하 본 발명을 좀 더 구체적으로 살펴보면 다음과 같다.Looking at the present invention in more detail as follows.
몬모릴로나이트는 약 1,200 만년 전, 백악기 시대의 화산활동에 의하여 생긴 규소성 광물질로서 녹니석, 각섬석, 티탄옥사이드, 칼륨, 나트륨과 같은 인체에 유익한 미네랄, 아미노산과 일반 광물질에서 발견되지 않는 인체에 유익한 호기성 미생물(생균)과 티탄옥사이드는 피부조직 재생과 자외선차단 및 미백효과가 뛰어난 것으로 확인되었다.Montmorillonite is a silicon mineral produced by volcanic activity in the Cretaceous Period, about 12 million years ago. Live bacteria) and titanium oxide were found to have excellent skin tissue regeneration, UV protection and whitening effects.
몬모릴로나이트에서 방사되는 원적외선은 고온에서만 방사되는 황토와는 달리 인체 온도 37∼37.5℃에서도 방사되는 특징이 있으며, 탁월한 탈취작용과 세포를 활성화시켜 주는 음이온과 함께 인체에 흡수, 신진대사 촉진 및 혈액순환을 활성화시켜 주며 인체의 노화 방지와 인체 내에 축적된 노폐물과 유해물질을 흡착하는 효과가 크다.Far-infrared rays emitted from montmorillonite are characterized by radiation at human body temperature of 37 ~ 37.5 ℃, unlike loess which is emitted only at high temperature, and absorbs into the human body, promotes metabolism, and promotes blood circulation with anion that activates cells. It activates and prevents the aging of the human body and absorbs the waste and harmful substances accumulated in the human body.
몬모릴로나이트는 음이온에 의한 모세혈관 확장과 혈액순환을 촉진시켜 세포 활성화를 돕고 신경 안정적 작용과 면역력 강화 작용에 도움을 주는 "공기 비타민 작용"으로 공기의 정화작용을 한다. 담배의 연기보다 신선한 공기를 먼저 제공함으로써 시원하고 부드러운 맛을 더해줄 수 있다.Montmorillonite promotes capillary expansion and blood circulation by negative ions, which helps cell activation and stabilizes the air with "air vitamin action", which helps to stabilize nerves and strengthen immune system. By providing fresh air before cigarette smoke, it can add a cool and soft taste.
몬모릴로나이트의 원적외선 방사는 5∼20㎛의 파장을 지닌 원적외선의 방사로 혈액순환을 촉진시키며, 탈취력과 흡수력이 우수하여 종전 담배흡입시 인체로 들어오는 니코틴, 타르 등 각종 유해물질을 현저하게 줄여 주면서도 담배 맛을 순하고 부드러우며 신선하게 제공할 수 있다. 또한, 몬모릴로나이트는 원적외선 방사 분포가 어느 한쪽에 기울임 없이 골고루 분포되고, 열전도율도 높다. 따라서, 담배 맛을 더욱더 신선하게 골고루 느낄 수 있다.The far-infrared radiation of montmorillonite promotes blood circulation by the radiation of far-infrared rays with a wavelength of 5-20㎛, and it has excellent deodorizing and absorbing power, and it significantly reduces various harmful substances such as nicotine and tar, which enters the human body when inhaling cigarettes. It can be served mildly, softly and freshly. In addition, montmorillonite has a far-infrared radiation distribution evenly distributed on either side, and high thermal conductivity. Therefore, the taste of tobacco can be felt even more freshly.
몬모릴로나이트는 수분조절 능력이 다른 지구상에 어떠한 광물질보다 뛰어나다. 기존의 황토나 광물질은 수분흡착률이 1 : 1의 비율이지만, 몬모릴로나이트는 약 1 : 3의 비율로 일반 분말에 대하여 수분흡착률은 3배가 높다. 강력한 흡착력과 미세한 다공성 입자로 되어있어 모세관현상을 일으켜 피부층의 오염물질과 각종 공해물질 및 잡균, 중금속 등을 흡착, 분해, 제거시키는 효과가 크다.Montmorillonite is better than any other mineral on earth with its ability to control moisture. Existing loess or minerals have a moisture absorption ratio of 1: 1, but montmorillonite has a ratio of about 1: 3, which is three times higher than that of ordinary powder. It has strong adsorption power and fine porous particles, which causes capillary phenomenon, which is very effective in adsorbing, decomposing and removing contaminants in the skin layer, various pollutants, various bacteria and heavy metals.
본 발명에 있어서, 몬모릴로나이트 분말을 얻는 과정을 살펴보면, 먼저, 몬모릴로나이트를 통상의 물에 용해시켜 침전물을 제거하는 소정의 정제 과정을 거친다. 이렇게 정제된 몬모릴로나이트는 40∼60℃로 유지되는 기포발생기가 부착된 수조에서 약 2∼4일 동안 숙성 및 교반(약 500∼1000rpm) 작업을 거쳐 호기성 미생물인 생균을 배양시킨다. 배양을 마친 다음, 상기 배양물을 40∼60℃의 온도에서 건조시켜 수분을 완전히 제거한 후, 분쇄하여 1000∼1200 메쉬의 입도를 가진 분말을 만든다. 이때의 분쇄방법은 철과 같은 불순물이 첨가되지 않도록 공기에 의한 분쇄방법인 기류식 분쇄방법이 바람직하고, 분쇄 입도를 1000∼1200 메쉬로 한정하는 것이 바람직하다. 이는 기존에 분쇄방법인 파쇄 분쇄방법의 단점을 보완하기 위함이다. 파쇄분쇄의 단점은 분쇄과정에서 봉과 봉사이의 접촉(마찰) 과정에서 (철)가루나 다른 이물질이 생길 수 있는 위험한 요소가 있다. 그래서 봉과 봉이 서로 마찰이나 접촉방법이 아닌 공기의 압을 이용한 기류식 분쇄방식을 이용하면서 철과 이물질이 발생하는 것을 방지할 수 있었고, 1000∼1200 메쉬로 미세하게 분세함으로써 더욱더 적정 점성을 가져서 입자화시키는데 바람직하다. 한편, 상기 숙성 온도가 40℃ 미만일 때는 미생물 증식이 느려지고, 60℃를 초과하면 미생물 증식이 아주 없어짐으로 40∼60℃를 유지해야 호기성 미생물을 얻을 수 있다. 이렇게 분쇄된 분말은 제품의 안정성을 위하여 멸균처리 과정을 거치는데, -40∼-45℃에서 멸균처리 과정을 거치는 것이 생성된 효소를 파괴하지 않아 바람직하다.In the present invention, looking at the process of obtaining montmorillonite powder, first, the montmorillonite is dissolved in ordinary water to undergo a predetermined purification process to remove the precipitate. The montmorillonite thus purified is cultured in aerobic microorganisms through aging and stirring (about 500 to 1000 rpm) for about 2 to 4 days in a bubble bath equipped with a bubble generator maintained at 40 to 60 ° C. After the incubation, the culture is dried at a temperature of 40 ~ 60 ℃ to completely remove the moisture, and then ground to form a powder having a particle size of 1000 ~ 1200 mesh. The grinding method at this time is preferably an airflow grinding method, which is a grinding method by air so that impurities such as iron are not added, and the grinding particle size is preferably limited to 1000 to 1200 mesh. This is to compensate for the shortcomings of the conventional crushing grinding method. The disadvantage of crushing is that there is a risk that (iron) powder or other foreign matter may be generated during contact (friction) of the rod and the service member during the grinding process. Therefore, it was possible to prevent the occurrence of iron and foreign matters by using airflow pulverization method using air pressure instead of friction or contact method with each other. It is preferable to. On the other hand, when the aging temperature is less than 40 ℃ microbial growth is slow, if it exceeds 60 ℃ microbial growth is very disappeared to maintain a 40 to 60 ℃ to obtain aerobic microorganisms. This pulverized powder is subjected to a sterilization process for the stability of the product, it is preferable that the sterilization process at -40 ~ -45 ℃ does not destroy the produced enzyme.
이렇게 전 처리된 몬모릴로나이트 분말에는 황토나 다른 어떠한 광물질에서 발견되지 않는 인체에 유익한 1g당 약 80만 마리의 호기성 미생물(생균)이 증식하며, 이들이 생산하는 효소로는 카탈라이제, 디페놀옥사다이제, 사카라제, 프로테아제 등의 효소가 존재하며, 이중 카탈라이제 효소는 노화의 원인인 과산화수소와 과산화 지질분해 및 해독능력이 더욱 탁월한 것으로 알려져 있다.In this pretreated montmorillonite powder, about 800,000 aerobic microorganisms (probiotics) per 1g, which are beneficial to the human body, not found in ocher or any other minerals, are multiplied, and the enzymes they produce include catalase and diphenoloxadiase. Enzymes such as saccharase and protease exist, and the catalase enzyme is known to be more excellent in hydrogen peroxide and lipid peroxidation and detoxification which are causes of aging.
본 발명은 이렇게 얻은 몬모릴로나이트 분말 94∼99.9중량%와 티탄옥사이드 분말 0.1∼6중량%를 혼합한 흡연 여과용 여과물질을 담배 필터를 제조하거나, 공지된 기능성 담배 제조방법이나 기능성 포장지 제조방법에 상기 여과물질을 첨가하여 기능성 담배나 기능성 포장지를 제조할 수 있다.The present invention provides a filter for smoking filtration material containing 94 to 99.9 wt% of the montmorillonite powder thus obtained and 0.1 to 6 wt% of titanium oxide powder to produce a tobacco filter, or the filtration to a known functional tobacco production method or functional packaging paper manufacturing method. Substances can be added to produce functional tobacco or functional packaging.
도 1 및 도 2를 참조하면, 일반적으로 담배(10)는 종이에 의해 감싸여 연초가 수용되는 연초부(1)와, 상기 연초가 타면서 생성되는 연기 속에 포함된 유해물질을 걸러주는 필터입자를 포함하는 필터부(3)로 구성되며, 상기 필터부(3)는 셀룰로오스아세테이트 섬유재(2), 필터입자(4) 및 천공(5)으로 구성된다.1 and 2, in general, the
따라서, 본 발명에서는 몬모릴로나이트 분말과 티탄옥사이드 분말을 혼합한 여과물질 그 자체, 또는 통상의 담배 필터 크기로 입자화하여 도 1 및 2와 같은 형태로 담배에 충진시킬 수 있다. 또한, 연초부(1)의 외부를 감싸는 연초지, 또는 담배를 담고 있는 담배각 포장지에 충진 또는 제조시 충진 물질로 함침(통상의 제조과정에서 종이에 첨가되는 통상의 충진제 등과 함께 약 1중량% 정도를 첨가함)시켜 담배의 흡입으로 발생하는 니코틴, 타르, 일산화탄소, 과산화수소, 과산화지질 등 인체 유해 물질을 분해하고 해독할 수 있다.Therefore, in the present invention, the montmorillonite powder and the titanium oxide powder are mixed with the filtration material itself, or granulated to a normal tobacco filter size, so that the cigarette can be filled in the form as shown in FIGS. 1 and 2. In addition, it is impregnated with a filler material during filling or manufacturing the tobacco paper wrapping the outside of the tobacco leaf portion 1, or tobacco packaging each containing tobacco (about 1% by weight with a conventional filler added to the paper in the normal manufacturing process, etc.) To decompose and detoxify harmful substances such as nicotine, tar, carbon monoxide, hydrogen peroxide and lipid peroxide.
한편, 기존 황토나 천연광물질에서 발산하는 음이온과 함께 방출되는 O3(오존)은 인체에 좋을 수만은 없다. 음이온은 공기를 정화시켜 주는 아주 유익한 이온이지만 이때 함께 발생하는 O3(비린내)을 장시간 흡입하면 두통, 구토, 천식, 피부 따가움, 후두염, 피부암 등을 일으킬 수 있다. 그래서 광촉매 작용을 하는 물질인 티탄옥사이드 분말(TiO2)을 상기 몬모릴로나이트 분말에 첨가함으로써 오존(O3)이 방출되는 것을 막을 수 있고, 특유의 비린내도 없게 만들어 소비자에게 좀더 순하고 부드러운 담배 맛을 안전하게 제공할 수 있다.On the other hand, O 3 (ozone) released together with the anion emanating from the existing loess or natural minerals can not be good for the human body. Negative ions are very beneficial ions that purify the air, but prolonged inhalation of O 3 (smelling) that occurs together can cause headaches, vomiting, asthma, skin itching, laryngitis and skin cancer. Therefore, by adding titanium oxide powder (TiO 2 ), which is a photocatalytic material, to the montmorillonite powder, ozone (O 3 ) can be prevented from being released, and it does not have a unique fishy smell, thus providing a safer and softer tobacco taste to consumers. can do.
기존의 담배 필터는 탄소알갱이 방식과 여과기인 필터의 흡습솜과 내부의 흡 습재의 흡습에 한계가 있어 장시간 흡연을 계속하면 구토,두통 증세가 심했다. 또 기존의 흡습재의 분말입자는 파쇄 분쇄 방식이어서 200∼500 메쉬 밖에 얻을 수 없어 흡습 능력에 한계가 있었지만, 기류식 미쇄 분쇄방식을 이용하면서 몬모릴로나이트 분말 1000∼1200메쉬 입도를 가진 분말을 만들어 담배필터와 담배를 싸고 있는 권련지 그리고 담배각에 가공첨가 합침하므로 담배의 유해성분을 더욱 줄일 수 있고 내용물은 일정습도를 유지할 수 있어 더욱더 신선한 담배 맛을 제공할 수 있다.Existing cigarette filter has a limit on the moisture absorption of the carbon granular filter and the hygroscopic cotton of the filter which is a filter and the internal hygroscopic material, and the symptoms of vomiting and headache were severe after prolonged smoking. In addition, the powder particles of the existing hygroscopic materials were crushed and pulverized, so that only 200 to 500 mesh could be obtained. Therefore, the moisture absorbing ability was limited. Processing additives are added to the cigarette paper wrapped around the cigarette and the tobacco angle to further reduce the harmful components of the cigarette, and the contents can be maintained at a constant humidity, thereby providing a fresher tobacco taste.
본 발명에 따르면, 몬모릴로나이트에는 인체의 유익한 미네랄 성분이 풍부하며 여기에 티탄옥사이드(TiO2)를 첨가함으로써 식물의 광합성과 같은 원리의 빛(열)을 받으면 촉매반응을 일으켜 각종 유해물질을 무해한 물질로 산화, 환원시키는 광촉매 역할을 한다. 총 중량에 티탄옥사이드 분말 0.1∼6중량%를 유지한다 이때, 티탄옥사이드 분말 중량이 0.1중량% 미만이면 첨가 효과가 거의 없고, 6중량%를 초과하면 비등현상이 불안정해서 담배 고유의 맛을 얻을 수 없으며, 티탄옥사이드 분말 중량이 0.5∼2중량%일 때 가장 안정적인 담배 맛을 얻을 수 있어 바람직하다.According to the present invention, montmorillonite is rich in beneficial minerals of the human body and by adding titanium oxide (TiO 2 ) to it, when it receives light (heat) on the same principle as the photosynthesis of plants, it causes a catalytic reaction to produce various harmful substances as harmless substances. It acts as a photocatalyst to oxidize and reduce. Maintain 0.1-6% by weight of titanium oxide powder in total weight. At this time, if the weight of titanium oxide powder is less than 0.1% by weight, there is little effect of addition. If it exceeds 6% by weight, the boiling phenomenon is unstable and the inherent taste of tobacco can be obtained. It is preferable to obtain the most stable tobacco taste when the weight of the titanium oxide powder is 0.5 to 2% by weight.
이하 실시 예를 통하여 본 발명을 좀 더 구체적으로 살펴보지만, 하기 예에 본 발명의 범주가 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to the following examples, but the scope of the present invention is not limited to the following examples.
실시 예 1Example 1
물 1ℓ와 몬모릴로나이트 1㎏을 혼합하고, 침전되는 불순물을 제거한 다음, 약 50℃로 유지되는 기포발생기가 부착된 수조에서 3일간 동안 약 700rpm으로 교반 하면서 숙성시켜 호기성 미생물을 배양시켰다. 검체 10g에 대하여 멸균 생리식염수 90㎖을 화장품 미생물 한도 시험법으로 측정하였고, 그 결과 7.9×105 CFU/g의 세균수를 확인하였다. 상기 배양물을 약 50℃에서 건조시킨 후, 기류식 분쇄법으로 1000∼1200 메쉬로 분말화시킨 다음, -40∼-45℃에서 멸균시켰다.1 L of water and 1 kg of montmorillonite were mixed, and impurities precipitated were removed, and aged in a water tank equipped with a bubble generator maintained at about 50 ° C. while stirring at about 700 rpm for 3 days to incubate aerobic microorganisms. 90 g of sterile physiological saline was measured with 10 g of the sample by the cosmetic microbial limit test method. As a result, the bacterial count of 7.9 × 10 5 CFU / g was confirmed. The culture was dried at about 50 ° C., then powdered to 1000-1200 mesh by air flow grinding, and then sterilized at −40 to 45 ° C.
상기 분말 10g을 전하 입자 측정장치를 이용하여 실내온도 24℃, 습도 51%, 대기중 음이온 수 108/㏄ 조건에서 KFIA-FI-1042 법으로 음이온 농도를 시험하였으며, 측정대상물에서 방출되는 음이온을 측정하여 단위 체적당 ION수로 표시한 결과, 약 226ION/㏄이었다. 또한, 상기 분말의 탈취율을 측정하여 하기 표 1에 나타내었다.10g of the powder was tested by using KFIA-FI-1042 method at room temperature 24 ℃, 51% humidity, and 108 / 수 of anions in the air using a charged particle measuring device. As a result, it was expressed as the number of IONs per unit volume, which was about 226 ION / cc. In addition, the deodorization rate of the powder was measured and shown in Table 1 below.
탈취시험
Deodorization test
1) 대조구는 시료를 넣지 않은 상태에서 측정한 것임.1) Control was measured with no sample.
시험방법: KFIA-FI-1004Test Method: KFIA-FI-1004
시험가스: 암모니아Test gas: Ammonia
가스농도측정: 가스검지관Gas concentration measurement: gas detector
한편, 염분을 제거한 심층수를 약 8℃에서 3일 동안 숙성시킨 다음, 상기 분말과 상기 심층수를 3 : 1의 무게비로 혼합시켜 본 발명의 미용 마사지 팩을 제조하였다.Meanwhile, the deep water after removing the salt was aged at about 8 ° C. for 3 days, and the powder and the deep water were mixed at a weight ratio of 3: 1 to prepare a cosmetic massage pack of the present invention.
실시 예 2Example 2
상기 실시 예 1에 따른 몬모릴로나이트 980g과 TiO2 20g을 혼합하고, 직경이 0.2∼1.3㎜의 크기로 입자화하여 필터를 제조하고, 도 1 또는 도 2와 같은 구조를 갖는 담배에 필터입자로 제공하였다.980 g of montmorillonite according to Example 1 and 20 g of TiO 2 were mixed and granulated to a size of 0.2 to 1.3 mm to prepare a filter, and provided as filter particles in a cigarette having a structure as illustrated in FIG. 1 or 2. .
이렇게 제조된 실시 예 2에 따른 담배를 흡연자 30명의 패널요원에게 각각의 흡연량으로 1개월간 흡연시켰다.The cigarette according to Example 2 thus prepared was smoked by the panelists of thirty smokers for one month in each smoking amount.
그 결과, 패널 요원 30명에서 담배 맛이 순하고 부드러우며 신선하다는 답을 얻을 수 있었다. 특히, 인체 온도에서 원적외선과 음이온의 효과인 "시원하다, 신선하다, 입안이 깔끔하다"는 답을 얻을 수 있었다. 또한, 흡연을 하면서 생기는 구토, 두통 증세도 생기지 않는다는 것도 알 수 있었고, 흡연자의 입안 특유의 냄새도 줄일 수 있었으며, 담배의 연기성분이 입안으로 들어오는 과정에서 부드럽고 담배연기 냄새가 비리지 않았다는 답을 얻을 수 있었다. 더더욱 혈액 순한 촉진과 심신의 안정을 얻을 수 있었다.As a result, 30 panelists found that the taste of tobacco was mild, smooth and fresh. In particular, the answer to the effect of far infrared rays and negative ions on the human body temperature is "cool, fresh, clean mouth." In addition, it was found that there was no vomiting or headache symptoms caused by smoking, and it was possible to reduce the peculiar smell of the smoker's mouth, and the answer was that the smoke component of the cigarette was soft and the smell of cigarette smoke was not emptied as it entered the mouth. there was. In addition, blood gentle palpation and mental and physical stability were obtained.
전술한 바와 같이, 본 발명은 니코틴, 타르 등 각종 유해물질을 현저하게 줄여 주면서도 담배 맛을 순하고 부드러우며 신선하게 제공할 수 있어 기능성 담배, 및/또는 기능성 담배 종이 등의 제조에 유용하다.As described above, the present invention can reduce the number of harmful substances such as nicotine and tar while providing a mild, soft and fresh taste of tobacco, which is useful for producing functional tobacco, and / or functional tobacco paper.
도 1은 본 발명에 따른 담배필터의 일 실시 예를 나타낸 것이다.1 shows an embodiment of a cigarette filter according to the present invention.
도 2는 본 발명에 따른 담배필터의 다른 실시 예를 나타낸 것이다.Figure 2 shows another embodiment of a cigarette filter according to the present invention.
- 도면의 주요 부분에 대한 부호의 설명 --Explanation of symbols for the main parts of the drawing-
1: 연초부 2: 셀룰로오스아세테이트 섬유재1: Tobacco Part 2: Cellulose Acetate Fiber
3: 필터부 4: 필터입자3: filter part 4: filter particles
5: 천공 10: 담배5: perforation 10: tobacco
Claims (4)