KR100966136B1 - High luminance multifunctional sheet - Google Patents

High luminance multifunctional sheet Download PDF

Info

Publication number
KR100966136B1
KR100966136B1 KR1020080080412A KR20080080412A KR100966136B1 KR 100966136 B1 KR100966136 B1 KR 100966136B1 KR 1020080080412 A KR1020080080412 A KR 1020080080412A KR 20080080412 A KR20080080412 A KR 20080080412A KR 100966136 B1 KR100966136 B1 KR 100966136B1
Authority
KR
South Korea
Prior art keywords
lens
composite sheet
light
high brightness
sheet according
Prior art date
Application number
KR1020080080412A
Other languages
Korean (ko)
Other versions
KR20100021800A (en
Inventor
정돈호
Original Assignee
도레이첨단소재 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 도레이첨단소재 주식회사 filed Critical 도레이첨단소재 주식회사
Priority to KR1020080080412A priority Critical patent/KR100966136B1/en
Publication of KR20100021800A publication Critical patent/KR20100021800A/en
Application granted granted Critical
Publication of KR100966136B1 publication Critical patent/KR100966136B1/en

Abstract

본 발명은 일체형 고휘도 복합시트 및 그를 포함한 액정표시장치에 관한 것이다.The present invention relates to an integrated high brightness composite sheet and a liquid crystal display device including the same.

본 발명의 복합시트는 투명기재, 상기 투명기재의 제1면상에 상호 인접하여 배열된 복수개의 렌즈로 이루어진 출광부; 및 상기 투명기재의 제2면상에 상기 렌즈가 서로 맞닿는 접점영역과 대향(對向)하는 위치에 돌출부가 형성되고 상기 돌출부 상에 형성된 반사층으로 이루어진 입광부;로 이루어지되, 상기 렌즈가 하단부에 삼각형 단면의 프리즘 형상을 가지고, 상기 렌즈의 하단부를 제외한 렌즈의 중앙부에 원형 또는 타원형의 단면 형상 구조를 동시에 구비한 것이다. 상기 복합시트가 유효각도에서 입사되는 입사광뿐만 아니라, 유효하지 않은 각도에서 입사되는 입사광의 집광효율을 극대화하도록 제조함으로써, 액정표시장치 모듈의 고휘도화를 구현하고, 확산시트 및 프리즘시트의 기능을 일체화하여 제조공정을 단순화함으로써, 제조단가를 낮출 수 있다.The composite sheet of the present invention comprises a light-emitting unit made of a transparent substrate, a plurality of lenses arranged adjacent to each other on the first surface of the transparent substrate; And a light incident portion formed on a second surface of the transparent substrate so as to face a contact area where the lens abuts each other, and a light incident portion formed of a reflective layer formed on the protrusion. It has a prism shape of a cross section, and has a circular or elliptical cross-sectional structure at the center of the lens except for the lower end of the lens. The composite sheet is manufactured to maximize the light condensing efficiency of incident light incident at an invalid angle as well as incident light incident at an effective angle, thereby realizing high luminance of the liquid crystal display module and integrating the functions of a diffusion sheet and a prism sheet. By simplifying the manufacturing process, the manufacturing cost can be lowered.

복합시트, 렌티큘러, 프리즘, 집광효율 Composite Sheet, Lenticular, Prism, Condensing Efficiency

Description

일체형 고휘도 복합시트{HIGH LUMINANCE MULTIFUNCTIONAL SHEET}Integrated high brightness composite sheet {HIGH LUMINANCE MULTIFUNCTIONAL SHEET}

본 발명은 일체형 고휘도 복합시트 및 그를 포함한 액정표시장치에 관한 것으로서, 더욱 상세하게는 종래 일정 곡률의 구형 또는 타원 형상의 렌티큘러 렌즈가 아닌, 렌즈의 하단부에 삼각형 단면의 프리즘 형상을 가지고, 상기 렌즈의 하단부를 제외한 렌즈의 중앙부에 원형 또는 타원형의 단면 형상 구조를 동시에 구비하여, 개구부로부터 입사된 광의 집광을 최적화시킬 뿐만 아니라 비유효각으로 입사된 빛은 반사층에 의한 재귀반사를 통하여 개구부로 다시 입사시켜 집광효율을 극대화한 고휘도 복합시트의 구조에 관한 것이다. The present invention relates to an integrated high brightness composite sheet and a liquid crystal display device including the same, and more particularly, has a prism shape of a triangular cross section at the lower end of the lens, rather than a spherical or elliptic lenticular lens having a constant curvature. A circular or oval cross-sectional structure is simultaneously provided at the center of the lens except for the lower end, thereby optimizing the condensing of the light incident from the opening, and incident light at an ineffective angle is incident again into the opening through retroreflection by the reflective layer. The present invention relates to a structure of a high brightness composite sheet that maximizes light collection efficiency.

액정표시장치(이하,“LCD”라 함)는 초박형으로 제작이 가능한 저소비전력, 저발열 및 고선명의 화상출력 장치로서, 최근 산업 각 분야의 화상표시 장치로 각광 받고 있으며, 특히 LCD-TV 시장은 2004년 7%에서 2007년 22%로 그 비중이 지속적으로 성장하고 있다. 이러한 액정표시장치는 다른 평판 디스플레이 방식과는 달리 액정 자체가 비발광 소재이며, 편광된 광을 이용하므로 광원이 필요함과 동시에 광효율을 높이는 장치가 필요하며 이를 백라이트 유닛(이하, "BLU"라 한다)이 담당하고 있다.Liquid crystal display (hereinafter referred to as "LCD") is a low power consumption, low heat generation and high definition image output device that can be manufactured in an ultra-thin, and has recently been spotlighted as an image display device in various fields of the industry, especially the LCD-TV market The proportion has continued to grow from 7% in 2004 to 22% in 2007. Unlike other flat panel display systems, the liquid crystal itself is a non-light-emitting material, and since polarized light is used, a light source is required and a device for enhancing the light efficiency is required, which is referred to as a backlight unit (hereinafter referred to as "BLU"). This is in charge.

BLU는 측면 라이트 방식 및 배면 라이트 방식 등이 있는데, 측면 라이트 방식은 디스플레이 소자의 측면에 부착된 광원으로부터 발생되는 빛을 도광판을 통하여 반대편에까지 이르게 하는 도중에 도광판의 밑면, 상세하게는 광원쪽 면에 광학적으로 설계된 패턴에서 산란 반사하게 되어 액정 패널방향으로 광을 균일화하고 도광판 상면에 확산 필름, 프리즘 등을 통하여 광을 좀 더 균일화함과 동시에 집광시킴으로써, 디스플레이 화면의 밝기를 향상시키는 간접 조명방식이다. 이러한 측면 라이트 방식의 BLU는 상대적으로 낮은 휘도와 박막을 요구하는 노트북이나 모니터 등에 사용된다. 이와 달리 높은 휘도를 요구하는 TV의 경우 배면에 많은 수의 램프를 수납하는 형식의 배면 라이트 방식의 BLU가 사용된다.The BLU includes a side light method and a back light method, and the side light method is an optical method on the bottom surface of the light guide plate, in detail, on the light source side, while the light generated from the light source attached to the side of the display element is led to the opposite side through the light guide plate. It is an indirect illumination method that improves the brightness of the display screen by scattering and reflecting light in a pattern designed to uniformize light in the direction of the liquid crystal panel and condensing light at the same time through a diffusion film, a prism, and the like on the upper surface of the light guide plate. This side light BLU is used in notebooks and monitors that require relatively low brightness and thin film. On the other hand, in the case of a TV requiring high brightness, a BLU of a back light type in which a large number of lamps are stored on the back is used.

BLU 내부 구조를 상세히 살펴보면, 반사시트; 램프; 도광판(측면 라이트 BLU의 경우) 또는 확산판(배면 라이트 BLU의 경우); 확산시트; 프리즘 시트; 보호시트; 및 액정 패널;로 이루어지며, 상기 반사시트가 램프에서의 빛을 위로 반사시켜 가능한 한 많은 빛을 도광판 또는 확산판에 도달하게 하고, 상기 도광판 또는 확산판 위에 위치한 확산시트가 빛을 골고루 확산 및 일차 집광시키고, 이어 확산시트 상에 적층된 프리즘 시트가 집광하도록 하여 2차 휘도를 상승시킨다. 이러한 백라이트 방식에서는 최소의 소비전력으로 최대의 화상 밝기를 구현할 수 있도록 설계되어 있다.Looking at the internal structure of the BLU in detail, the reflection sheet; lamp; Light guide plate (for side light BLU) or diffuser plate (for back light BLU); Diffusion sheet; Prism sheet; Protective sheet; And a liquid crystal panel, wherein the reflective sheet reflects the light from the lamp upwards to reach as much light as possible to the light guide plate or the diffuser plate, and the diffuser sheet located on the light guide plate or the diffuser plate evenly diffuses and primary light. The light is condensed, and then the prism sheet laminated on the diffusion sheet is condensed to raise the secondary luminance. In the backlight method, the maximum image brightness is designed with the minimum power consumption.

상기 BLU 중에서 휘도향상 목적으로 사용되는 확산시트는 보통 유기입자의 돌기에 의한 렌즈모양이 광을 집광시키는 역할을 하고 반면, 프리즘 시트는 특정 범위의 유효각으로 입사된 광은 집광시키는 반면 일부는 재귀 반사에 의해 회 수(recycling)된 광이 그 특정범위의 각으로 재입사되어 또 다시 집광되도록 하여 집광효과가 반복적으로 일어나 휘도를 증가시킨다. 프리즘시트는 이러한 구조의 광학적 원리로 휘도 향상에서는 뛰어난 효과가 있으나, 완전하지는 못하여 일부의 광은 유효각으로 입사되지 못하고 소실되는 단점이 있다.Among the BLUs, the diffusion sheet used for the purpose of improving luminance usually collects the light by the lens shape due to the projections of the organic particles, whereas the prism sheet collects the light incident at a certain range of effective angles, while some recursively. The light recycled by the reflection is reincident at an angle within a specific range and focused again so that the light collecting effect is repeatedly generated to increase luminance. Prism sheet is an optical principle of such a structure has an excellent effect in improving the brightness, but it is not perfect, there is a disadvantage that some light is not incident at the effective angle is lost.

상기 기술한 바와 같이, 전형적인 BLU의 광학부품의 조합은 도광판이나 확산판을 제외하고 전형적으로 확산시트, 프리즘 시트, 보호시트로 이루어져 있어 BLU의 부품 소재비가 높고, 여러 장의 광학 필름을 조립하는 공정비용 또한 높아 이를 개선하려는 노력이 최근 몇 년 이래 이루어지고 있다.As described above, a typical BLU optical component combination is composed of a diffusion sheet, a prism sheet, and a protective sheet, except for a light guide plate or a diffusion plate, so that the BLU component material cost is high, and the process cost of assembling several optical films It is also high and efforts to improve it have been made in recent years.

이러한 노력의 일환으로 렌티큘러(Lenticular) 렌즈 구조의 집광 시트가 개발되어 왔으나 이의 경우, 입사되는 광은 렌즈 중앙부를 통과하면 집광효율이 우수하나[도 3a], 입사되는 광의 방향이 수직 또는 비스듬히 입사되면, 렌티큘러 렌즈에 의해 부딪혀 리사이클 되거나 측면으로 입사되어 전체적인 집광효율이 저하된다[도 3b]. As part of this effort, a light collecting sheet having a lenticular lens structure has been developed, but in this case, the incident light has excellent light collecting efficiency when passing through the center of the lens [ FIG. 3A ]. It is hit by the lenticular lens, recycled or incident to the side, the overall light collection efficiency is lowered [ Fig. 3b ].

또한, 프리즘 시트는 기재시트층 상에 삼각형 단면을 가지는 선형 프리즘 렌즈 구조로 형성되어, 집광시트로서 사용된다. 그러나, 상기 삼각형 단면형상을 갖는 프리즘시트는 시야각의 조정이 어렵고, 입사광 중 유효하지 않은 방향에서 입사된 입사광은 사이드 로브(Side Lobe)를 발생시킴에 따라 집광효율 및 콘스라스트 등 광학성능을 향상시키는데 한계가 있다. 또한 프리즘 시트는 삼각형의 그 끝이 매우 날카롭기 때문에 제조공정상, 유통 및 관리상의 스크랫치가 다양하게 발생하는 단점이 있어 그 제조원가 및 기타 비용이 매우 높다. 그 외에도 슬림형 LCD TV가 절대적으로 요구하는 램프 은폐성은 종래의 표준적인 광학시트 구성으로는 불가능한 측면이 있다.Further, the prism sheet is formed in a linear prism lens structure having a triangular cross section on the base sheet layer, and is used as the light collecting sheet. However, the prism sheet having the triangular cross-sectional shape is difficult to adjust the viewing angle, and incident light incident from an invalid direction among the incident light generates side lobes, thereby improving light condensing efficiency and contrast performance. There is a limit. In addition, the prism sheet is very sharp at the end of the triangle has the disadvantage of a variety of scratches in the manufacturing process, distribution and management, the manufacturing cost and other costs are very high. In addition, the lamp concealment absolutely required by a slim LCD TV is impossible with a conventional standard optical sheet configuration.

이러한 문제를 해소하기 위해서는 많은 입사광량이 제공되어야 한다는 전제하에, BLU 제조비용을 절감하는 방법으로 확산시트 2장을 적층시키는 방법, 슬림형 LCD TV의 은폐성을 강화하기 위하여 패턴확산판 상에 확산시트 및 프리즘 시트를 적층한 후, 상기 확산시트 및 프리즘시트를 재적층하고 보호필름을 적층하는 방법 또는 패턴확산판 상에 패턴압출시트, 프리즘 시트 및 보호시트를 적층하는 방법이 시도되어 왔다. 그러나, 이러한 경우 많은 수의 광학 시트를 사용하여 BLU의 단가를 올리는 단점이 있다.In order to solve such a problem, a large amount of incident light must be provided. A method of stacking two diffusion sheets in a way to reduce the BLU manufacturing cost, and a diffusion sheet on a pattern diffusion plate to enhance the concealment of a slim LCD TV. And a method of laminating the diffusion sheet and the prism sheet and laminating the protective film after laminating the prism sheet, or laminating the pattern extrusion sheet, the prism sheet, and the protective sheet on the pattern diffusion plate. However, in this case, there is a disadvantage in that the cost of the BLU is increased by using a large number of optical sheets.

이에 최근에는 LCD 대형화 및 박막화 추세와 더불어 제조단가를 낮추고자 하는 시장요구에 따라, 종래의 프리즘시트 및 확산시트의 기능을 일체화시킨 복합시트가 등장하고 있다. Recently, in accordance with the trend of larger LCDs and thinner LCDs and lower market costs, composite sheets having integrated functions of conventional prism sheets and diffusion sheets have been introduced.

이러한 복합시트는 투명기재, 상기 투명기재의 제1면상에 상호 인접하여 배열된 복수개의 렌즈로 이루어진 출광부 및 상기 투명기재의 제2면상에 상기 렌즈가 서로 맞닿는 접점영역과 대향(對向)하는 위치에 돌출부가 형성되고 상기 돌출부 상에 형성된 반사층으로 이루어진 입광부로 이루어지고 있다.The composite sheet opposes a light emitting portion made up of a transparent substrate, a plurality of lenses arranged adjacent to each other on a first surface of the transparent substrate, and a contact area in which the lenses contact each other on a second surface of the transparent substrate. The protrusion is formed at the position and consists of a light incidence portion formed of a reflective layer formed on the protrusion.

그러나, 상기 복합시트의 출광부는 일정 곡률의 구형 또는 타원의 렌티큘러 형상의 렌즈를 가지고 있으므로, 렌즈의 중앙부로 입사되는 빛만이 효율적으로 집광되기 때문에 입광부의 개구부를 좁게 할 수 밖에 없으며 이에 따라 반사층에 사용되는 무기입자의 광흡수 및 여러 차례의 재귀반사로 매질의 통과 길이(Path Length)가 길어지게 되어 매질에 의한 광흡수 또한 매우 높아 광효율을 저하시키는 요인이 되 고 있다. 또한, 종래 렌티큘러 형상의 렌즈를 가지는 복합시트는 상면(출광부)의 렌즈와 하면의 반사층(입광부)의 정교한 일치를 위한 복잡한 제조공정으로, 낮은 수율 및 높은 제품가격 등이 문제점으로 지적되고 있다. However, since the light exit portion of the composite sheet has a spherical or elliptical lenticular lens of a certain curvature, only the light incident on the center portion of the lens is efficiently focused, so that the opening of the light incident portion can be narrowed. The light absorption of the inorganic particles used in and the multiple reflex reflections cause the path length of the medium to be long, so that the light absorption by the medium is also very high, which is a factor that lowers the light efficiency. In addition, the conventional composite sheet having a lenticular lens is a complicated manufacturing process for precise matching of the lens on the upper surface (light emitting portion) and the reflective layer (light receiving portion) on the lower surface, and low yields and high product prices have been pointed out as problems. .

이에, 본 발명자들은 종래 문제점을 개선하고자 노력한 결과, 렌즈 하단부에 직선의 프리즘 구조를 도입하여 렌티큘러 또는 구형 렌즈 구조를 개량하고 반사층을 도입하여 넓은 개구부에도 불구하고 렌즈에 의한 집광효율을 최적화하고 광흡수를 최소화함으로써, 본 발명을 완성하였다. Accordingly, the present inventors have tried to improve the conventional problems, and as a result, by introducing a straight prism structure at the lower end of the lens to improve the lenticular or spherical lens structure and the reflection layer to optimize the light collection efficiency and absorption of light despite the wide openings By minimizing the present invention, the present invention has been completed.

본 발명의 목적은 개구부로부터 입사된 광의 매질에 의한 흡수를 최소화함과 동시에 집광을 최적화시킨 일체형 고휘도 복합시트를 제공하는 것이다.It is an object of the present invention to provide an integrated high brightness composite sheet which minimizes absorption by a medium of light incident from an opening and at the same time optimizes light collection.

이를 위하여 렌즈의 하단부에 삼각형 단면의 프리즘 형상을 가지고, 렌즈의 중앙부에 원형 또는 타원형의 단면 형상 구조를 구비한 일체형 고휘도 복합시트를 제공하는 것이다.To this end, it is to provide an integrated high brightness composite sheet having a prism shape having a triangular cross section at the lower end of the lens, and having a circular or oval cross-sectional structure at the center of the lens.

상기 목적을 달성하기 위하여, 본 발명은 투명기재(1); 상기 투명기재의 제1면상에 상호 인접하여 배열된 복수개의 렌즈로 이루어진 출광부(2); 및 상기 투명기재의 제2면상에 상기 렌즈가 서로 맞닿는 접점영역과 대향(對向)하는 위치에 돌출부(5)가 형성되고, 상기 돌출부(5) 상에 형성된 반사층(6)으로 형성된 입광부(3);로 이루어진 일체형 고휘도 복합시트(10)를 제공하며, 상기 출광부(2)가 유효하지 않은 각도에서 입사되는 입사광까지 효율적으로 집광할 수 있도록 설계된 복수개의 렌즈를 구비한다. 더욱 상세하게는 본 발명의 일체형 고휘도 복합시트(10)의 구조가 렌즈의 하단부(2b)에 삼각형 단면을 가지는 프리즘 형상과, 상기 렌즈의 하단부를 제외한 렌즈의 중앙부(2a)에 원형 또는 타원형의 단면 형상을 가진 구조로서, 종래의 렌티큘러 렌즈구조를 개량하여 광효율을 향상한다. 상기 광효율 향상의 메커니즘은 렌즈의 중앙부(2a)로 입사된 광은 일정 곡률의 원형 또는 타원형의 형상에 의해 집광되고 이외의 부분 즉, 프리즘 형상으로 입사되는 광은 개구부의 넓이를 최적화하여 유효 입사광의 비율을 극대화하여 또다시 집광되도록 하는 것이다. 즉, 개구부로부터 수직에 가깝게 입사되는 광은 대부분 곡률을 가지는 렌즈중앙부로 몰리게 되어 곧바로 집광되며 프리즘의 유효각으로 비스듬히 입사되는 광은 프리즘에 의해 재귀반사없이 곧바로 집광된다. 중앙부의 구형 또는 렌티큘라 렌즈와 하단의 프리즘의 크기비율을 자유자재로 조절하여 두 렌즈의 기능을 용이하게 최적화시킬 수 있다. 종래 프리즘의 경우 중앙부로 입사되는 광은 대부분 집광이 되는 것이 아니라 재귀 반사되어 집광되는데, 이러한 경우 유기 필름을 통과하는 길이가 길어져 필름에 의한 광 흡수가 일어나 광효율이 떨어지는 단점이 있다.In order to achieve the above object, the present invention is a transparent substrate (1); A light-out part 2 comprising a plurality of lenses arranged adjacent to each other on a first surface of the transparent substrate; And a light incident portion formed on a second surface of the transparent substrate, the protrusion 5 being formed at a position facing the contact area where the lens abuts, and formed of a reflective layer 6 formed on the protrusion 5. 3); provides an integrated high brightness composite sheet 10 consisting of a plurality of lenses designed to efficiently collect the incident light incident on the light exiting part 2 from an invalid angle. More specifically, the structure of the integrated high brightness composite sheet 10 of the present invention has a prism shape having a triangular cross section at the lower end portion 2b of the lens, and a circular or elliptical cross section at the center portion 2a of the lens except for the lower end portion of the lens. As a structure having a shape, the conventional lenticular lens structure is improved to improve light efficiency. The mechanism for improving the light efficiency is that light incident on the center portion 2a of the lens is focused by a circular or elliptical shape having a certain curvature, and light incident on other portions, that is, prismatic shapes, optimizes the width of the opening to provide effective incident light. Maximizing the ratio so that it is concentrated again. That is, the light incident close to the vertical from the opening portion is mostly focused on the lens center portion having the curvature and condensed immediately, and the light obliquely incident on the effective angle of the prism is immediately condensed by the prism without retroreflection. The size ratio of the spherical or lenticular lens at the center and the prism at the bottom can be freely adjusted to easily optimize the functions of the two lenses. In the case of the conventional prism, the light incident to the center portion is collected mostly by being retroreflected instead of being focused. In this case, the length of the light passing through the organic film is increased and light absorption by the film occurs, resulting in a low light efficiency.

본 발명의 복수개의 렌즈로 이루어진 출광부(2)에 있어서, 상기 단위렌즈의 폭(width, w)이 50 내지 250㎛이고, 단위렌즈의 높이(height, h)는 상기 폭 길이에 대하여, 25 내지 200% 범위가 되도록 고안된다.In the light exiting part 2 composed of a plurality of lenses of the present invention, the unit lens has a width ( w ) of 50 to 250 μm, and the height of the unit lens (height, h ) is 25 with respect to the width length. To 200%.

또한, 상기 렌즈 하단부(2b)가 상기 단위렌즈의 높이(h) 길이에 대하여, 바람직하게는 50 내지 80% 이내로 형성되지만 제한은 없다.Further, the lens lower end portion 2b is preferably formed within 50 to 80% of the height h of the unit lens, but there is no limitation.

본 발명의 입광부(3)의 구성으로서, 돌출부(5)는 그의 높이가 5 내지 50㎛이며, 상기 돌출부(5) 상에 형성된 반사층(6)의 두께는 5 내지 50㎛이다.As the configuration of the light incidence part 3 of the present invention, the protrusion part 5 has a height of 5 to 50 μm, and the thickness of the reflective layer 6 formed on the protrusion part 5 is 5 to 50 μm.

또한, 상기 돌출부와 바로 이웃하는 돌출부간에 형성된 공간을 개구부라 하며, 상기 개구부가 상기 렌즈의 단위 폭 길이에 대하여, 30 내지 90%를 만족한다.In addition, a space formed between the protrusion and the immediately adjacent protrusion is called an opening, and the opening satisfies 30 to 90% of the unit width of the lens.

상기 반사층(6)은 반사물질이 첨가된 수지로 형성되거나, 착색안료 또는 염료에서 선택되는 1종 이상과 반사물질이 첨가된 수지로 형성된다. The reflective layer 6 is formed of a resin to which a reflective material is added, or at least one selected from a coloring pigment or a dye and a resin to which a reflective material is added.

수지로는 자외선 경화형수지, 전자선 경화형수지 및 열경화형 수지로 이루어진 군 에서 선택되는 어느 하나가 사용될 수 있으며, 상기 반사물질로서 바람직하게는 TiO2, BaSO4, Al(OH)3, Al2O3, CaCO3, ZnO, ZnS 등의 무기 입자나 다양한 형태의 유기입자로 이루어진 군에서 선택되는 1종 이상을 사용하는 것이다.As the resin, any one selected from the group consisting of an ultraviolet curable resin, an electron beam curable resin, and a thermosetting resin may be used. Preferably, the reflective material is TiO 2 , BaSO 4 , Al (OH) 3 , Al 2 O 3. , At least one selected from the group consisting of inorganic particles such as CaCO 3 , ZnO, ZnS, and organic particles in various forms.

이에, 본 발명은 상기 일체형 고휘도 복합시트 및 상기 복합시트를 향해 빛을 조사하는 광원부로 이루어진 백라이트 어셈블리를 제공한다.Accordingly, the present invention provides a backlight assembly comprising the integrated high brightness composite sheet and a light source unit for irradiating light toward the composite sheet.

나아가, 상기 백라이트 어셈블리를 포함하는 액정표시장치를 제공한다.Furthermore, a liquid crystal display device including the backlight assembly is provided.

본 발명에 따라, 단위렌즈의 하단부에 삼각형 단면을 가지는 프리즘 형상과 상기 렌즈의 중앙부에 원형 또는 타원형의 단면 형상 구조를 동시에 가진 렌즈를 도입한 일체형 고휘도 복합시트를 제공함으로써, 유효각도에서 입사되는 입사광뿐만 아니라, 유효하지 않은 각도에서 입사되는 입사광의 집광효율을 극대화한다. 또한, 입광부 하면에 위치한 반사층은 확산기능을 가지고 있어 확산시트의 효과를 나타낸다.According to the present invention, an incident light incident at an effective angle is provided by providing an integrated high brightness composite sheet having a prism shape having a triangular cross section at a lower end of a unit lens and a lens having a circular or oval cross-sectional structure at the center of the lens. In addition, it maximizes the light collection efficiency of incident light incident from an invalid angle. In addition, the reflective layer located on the lower surface of the light incident portion has a diffusion function, which shows the effect of the diffusion sheet.

또한, 본 발명의 일체형 고휘도 복합시트의 구조적 특징에 따라, 유효각도에서 입사되는 입사광뿐만 아니라, 유효하지 않은 각도에서 입사되는 입사광의 집광효율을 극대화하여, 액정표시장치 모듈의 고휘도화를 구현한다. 또한, 본 발명의 일체형 고휘도 복합시트는 확산시트 및 프리즘시트의 기능을 일체화시켜, 제조공정을 단순화함으로써, 제조단가를 낮출 수 있다.In addition, according to the structural features of the integrated high-brightness composite sheet of the present invention, not only the incident light incident at an effective angle but also the incident light incident at an invalid angle may be maximized to realize high luminance of the LCD module. In addition, the integrated high-brightness composite sheet of the present invention integrates the functions of the diffusion sheet and the prism sheet to simplify the manufacturing process, thereby lowering the manufacturing cost.

이하, 본 발명을 더욱 상세히 설명하고자 한다. Hereinafter, the present invention will be described in more detail.

본 발명은 도 1에서 도시한 바와 같이, 본 발명은 투명기재(1); 상기 투명기재의 제1면상에 상호 인접하여 배열된 복수개의 렌즈로 이루어진 출광부(2); 및 상기 투명기재의 제2면상에 상기 렌즈가 서로 맞닿는 접점영역과 대향(對向)하는 위치에 돌출부(5)가 형성되고, 상기 돌출부(5) 상에 반사층(6)이 형성된 입광부(3);로 이루어진 일체형 고휘도 복합시트(10)를 제공한다.As the present invention is shown in Figure 1 , the present invention is a transparent substrate (1); A light-out part 2 comprising a plurality of lenses arranged adjacent to each other on a first surface of the transparent substrate; And a light incident portion 3 having a protrusion 5 formed on a second surface of the transparent substrate facing a contact area where the lens abuts each other, and a reflective layer 6 formed on the protrusion 5. Provides an integrated high brightness composite sheet (10) consisting of.

본 발명의 일체형 고휘도 복합시트(10)는 유효하지 않은 각도에서 입사되는 입사광까지 효율적으로 집광할 수 있도록 투명기재의 제1면상에 상호 인접하여 배열된 복수개의 렌즈를 구비한 출광부(2); 및 반사층(6) 형성에 의해 반사율 및 은폐력을 향상시켜 광효율을 극대화할 수 있는 입광부(3);로 이루어진 구조를 특징으로 한다.The integrated high brightness composite sheet 10 of the present invention includes: a light emitting part 2 having a plurality of lenses arranged adjacent to each other on a first surface of a transparent substrate so as to efficiently collect incident light incident at an invalid angle; And a light incident part 3 capable of maximizing light efficiency by improving reflectance and hiding power by forming a reflective layer 6.

본 발명의 일체형 고휘도 복합시트(10) 중, 출광부(2)는 상기 렌즈의 하단부(2b)가 삼각형 단면을 가지는 프리즘 형상이고, 상기 렌즈의 하단부를 제외한 렌즈의 중앙부(2a)가 원형 또는 타원형의 단면 형상을 가진 구조로서, 개구부로부터 입사된 광의 집광을 최적화시킨다. 특히, 상기 프리즘 형상을 통해 사각으로 입사된 광을 집광하고, 구면 또는 타원 형상을 통해 수직각에 가깝게 입사된 광의 집광을 최적화한다.In the integrated high brightness composite sheet 10 of the present invention, the light exit portion 2 has a prism shape in which the lower end portion 2b of the lens has a triangular cross section, and the center portion 2a of the lens except for the lower end portion of the lens has a circular or elliptical shape. As a structure having a cross-sectional shape of, the light condensing of light incident from the opening is optimized. In particular, the light condensed into the square through the prism shape, and optimizes the condensing of the light incident close to the vertical angle through the spherical or elliptical shape.

본 발명의 복수개의 렌즈로 이루어진 출광부(2)는 단위렌즈의 폭(w)이 50 내지 250㎛이 바람직하며, 더욱 바람직하게는 50 내지 200㎛, 더욱 더 바람직하게는 150㎛이하인 것이다. 이때, 250㎛를 초과하면, 모아레 현상이 발생하기 쉽고, 화상에 패턴이 보이게 되어 바람직하지 않고, 폭이 50㎛미만이면, 반사층(6) 패턴 구현이 어렵다. The light output part 2 composed of a plurality of lenses of the present invention preferably has a width w of a unit lens of 50 to 250 μm, more preferably 50 to 200 μm, even more preferably 150 μm or less. At this time, if it exceeds 250㎛, the moire phenomenon is likely to occur, the pattern is visible in the image is not preferable, if the width is less than 50㎛, it is difficult to implement the reflective layer (6) pattern.

또한, 상기 단위렌즈의 높이(h)가 상기 폭 길이에 대하여, 25 내지 200%인 것을 특징으로 한다. 이때, 25% 미만이면, 광의 집광성이 저하되고, 200%를 초과하면, 광의 전반사량 증가로 오히려 휘도가 감소하여 바람직하지 않다. In addition, the height h of the unit lens is characterized in that 25 to 200% with respect to the width length. At this time, if it is less than 25%, the light condensing property is lowered, and if it exceeds 200%, the luminance is rather decreased due to the increase in total reflection amount of light, which is not preferable.

렌즈 하단부(2b)는 상기 렌즈의 높이(h)의 길이에 대하여, 20 내지 80%로 형성되며, 더욱 바람직하게는 50 내지 80%로 형성된다. 이때, 렌즈의 하단부 20% 미만으로 프리즘 형상이 형성되면, 프리즘 형상에 의한 효율이 떨어지므로, 종래 렌티큘러 렌즈가 유효하지 않은 각도에서 입사되는 입사광에 대하여 낮은 집광효율을 보이는 문제점이 여전히 해소되지 않으며, 80%를 초과하면, 수직광에 대한 집광효율이 저하된다.The lower end portion 2b of the lens is formed from 20 to 80% with respect to the length of the height h of the lens, more preferably from 50 to 80%. At this time, if the prism shape is formed less than 20% of the lower end of the lens, the efficiency due to the prism shape is lowered, the problem that the conventional lenticular lens shows a low condensing efficiency with respect to the incident light incident from an invalid angle is still not solved, When it exceeds 80%, the light condensing efficiency for vertical light is lowered.

본 발명의 출광부(2)에서 상기 삼각형 단면의 프리즘 형상으로 이루어진 렌즈 하단부(2b)를 제외한 부분을 렌즈 중앙부(2a)라 하며, 그 단면이 종래 렌티큘라 렌즈 형상의 원형 또는 타원형의 형상으로 이루어진다. 따라서, 렌즈 중앙부(2a)의 구조를 통해, 유효각도에서 입사되는 입사광 내지 수직각에 가깝게 입사된 광의 집광을 최적화한다.A part of the light exiting part 2 of the present invention except for the lens lower end part 2b having the prism shape of the triangular cross section is called the lens center part 2a, and its cross section is formed in a circular or elliptical shape of a conventional lenticular lens shape. . Therefore, through the structure of the lens center portion 2a, the light condensing of the incident light incident at the effective angle or close to the vertical angle is optimized.

본 발명의 일체형 고휘도 복합시트(10) 중, 입광부(3)는 상기 투명기재의 제2면상에 상기 렌즈가 서로 맞닿는 접점영역과 대향(對向)하는 위치에 돌출부(5)가 형성되고, 상기 돌출부(5) 상에 형성된 반사층(6)으로 이루어진 구조로서, 돌출부(5)와 바로 이웃하는 돌출부(5)간에 형성된 홈 형상의 개구부(4)가 연속적으로 교대 배열된다.In the unitary high brightness composite sheet 10 of the present invention, the light incidence part 3 is provided with a protrusion 5 at a position facing the contact area where the lens abuts on the second surface of the transparent substrate, As the structure consisting of the reflective layer 6 formed on the protrusion part 5, the groove-shaped opening part 4 formed between the protrusion part 5 and the immediately adjacent protrusion part 5 is alternately arranged.

이때, 상기 개구부의 길이는 렌즈의 단위 폭 길이에 대하여, 30 내지 90% 를 만족한다.In this case, the length of the opening satisfies 30 to 90% of the unit width of the lens.

이때, 돌출부(5)의 높이는 5 내지 50㎛이며, 5㎛ 미만이면, 반사층의 코팅이 어렵고 50㎛를 초과하면, 반사층을 코팅하기 위한 사각기둥의 투명한 측면으로의 광투과가 일어나 전체적인 광학적 기능을 저해하여 바람직하지 않다.At this time, the height of the protruding portion 5 is 5 to 50㎛, less than 5㎛, if the coating of the reflective layer is difficult and exceeds 50㎛, light transmission to the transparent side of the square pillar for coating the reflective layer occurs to the overall optical function Inhibiting is undesirable.

또한, 상기 돌출부(5)와 이웃하는 돌출부간의 간격 즉, 입광부에 해당하는 개구부(4)의 길이는 이 단위렌즈의 폭의 길이에 대하여, 30 내지 90% 범위 이내로 배열되도록 설치된다. 이때, 30% 미만으로 좁은 간격으로 배열하면, 유효 입사광이 지나치게 작아 휘도 향상에 바람직하지 않고, 90% 초과하는 범위로 넓게 배열되면, 돌출부(5) 상의 반사층(6)의 면적이 좁아 반사광에 의한 리사이클링 효과가 저하된다.In addition, the distance between the protrusion 5 and the adjacent protrusion, that is, the length of the opening 4 corresponding to the light incident portion, is provided so as to be arranged within the range of 30 to 90% with respect to the length of the width of the unit lens. At this time, if the array is arranged at a narrow interval of less than 30%, the effective incident light is too small, which is not preferable for improving the brightness, and when the array is wider in the range exceeding 90%, the area of the reflective layer 6 on the protrusion 5 is narrowed, which causes Recycling effect is reduced.

본 발명의 반사층(6)은 빛의 유효각도에서 벗어나 입사되는 즉 비유효각에서 입사되는 입사광을 얼마나 효율적으로 반사시키는가에 따라 집광시트 광효율의 대부분이 결정된다.Most of the light collecting sheet light efficiency is determined by the reflecting layer 6 of the present invention depending on how efficiently the incident light incident from the effective angle of light is incident, i.e., incident at an ineffective angle.

상기 돌출부(5)에 상기 반사층(6)을 형성할 때, 그라비아 인쇄법, 옵셋 인쇄법, 실크스크린 인쇄법 및 잉크젯 인쇄법으로 이루어진 군에서 선택되는 어느 하나의 방법으로 수행하여 광 성능을 최적화할 수 있는 두께로 조절할 수 있다. 이때, 반사층(6)의 바람직한 두께는 5 내지 50㎛ 범위일 때, 광 성능의 향상효과가 있고, 상기 범위를 벗어나면, 반사효율 및 작업성이 저하된다.When the reflective layer 6 is formed on the protrusion 5, the optical performance may be optimized by any one method selected from the group consisting of gravure printing, offset printing, silkscreen printing, and inkjet printing. You can adjust the thickness. At this time, when the preferable thickness of the reflective layer 6 is in the range of 5 to 50 μm, there is an effect of improving the light performance, and if it is out of the above range, the reflection efficiency and workability are reduced.

따라서, 본 발명은 반사층(6)의 도입으로 유효하지 않는 각으로 입사되는 광을 재귀반사시켜 유효입사각의 광으로 전환하여 렌즈에 집광을 최적화되도록 하며, 반사층(6)의 두께가 5㎛미만이면, 반사층의 두께가 얇기 때문에, 유효각에서 벗어난 각 도에서 입사되는 입사광이 반사층에 의해 리사이클링되지 않고 투과 진행하므로, 집광효율이 떨어지고 상대적으로 투과하는 빛이 커짐에 따라 은폐력이 작아지게 된다. 따라서, 유효각도로 전환되어 재사용될 수 있는 광량이 적고, 반사층(6)을 투과하여 유효각도 이외의 각도로 투과되는 광이 생기므로, 유효한 시야각 외로 광의 손실이 발생한다. 반면에, 50㎛를 초과하면, 코팅이 어려운 문제가 있다.Therefore, according to the present invention, the reflection layer 6 is retroreflected to light having an ineffective angle to be converted into light having an effective incidence angle so as to optimize condensing on the lens, and if the thickness of the reflection layer 6 is less than 5 μm, Since the thickness of the reflective layer is thin, incident light incident at an angle deviating from the effective angle is transmitted without being recycled by the reflective layer, so that the condensing power decreases and the hiding power decreases as the light relatively transmitted increases. Accordingly, the amount of light that can be converted to the effective angle and reused is small, and light is transmitted through the reflective layer 6 to be transmitted at an angle other than the effective angle, so that light loss occurs outside the effective viewing angle. On the other hand, if it exceeds 50 μm, the coating is difficult.

도 2는 본 발명의 일체형 고휘도 복합시트(10)에 의한 집광효율을 모식화한 것으로서, 돌출부 상에 형성된 반사층에 의하여, 유효각에서 벗어난 각도에서 입사되는 입사광까지 리사이클되게 함으로써, 광손실을 최소화하고 반사체의 반사율 및 은폐력을 향상시켜 입광부의 광효율을 극대화할 수 있다. FIG. 2 illustrates the light condensing efficiency of the integrated high brightness composite sheet 10 of the present invention, and the light loss is minimized by recycling the incident light incident at an angle outside the effective angle by the reflective layer formed on the protrusion. It is possible to maximize the light efficiency of the light incident part by improving the reflectance and hiding power of the reflector.

본 발명의 반사층(6)는 반사물질이 자외선 경화형 수지, 전자선 경화형 수지 및 열 경화형 수지 중 선택된 수지에 첨가되어 형성된다. The reflective layer 6 of the present invention is formed by adding a reflective material to a resin selected from an ultraviolet curable resin, an electron beam curable resin, and a thermosetting resin.

상기 반사물질은 당 기술분야에 알려진 물질이 제한되지 않고 사용될 수 있으나 바람직하게는, TiO2, BaSO4, Al(OH)3, Al2O3, CaCO3, ZnO 및 ZnS로 이루어진 군에서 선택되는 1종 이상의 반사용 안료를 사용하는 것이다. 더욱 바람직하게는 백색의 반사용 안료를 사용하는 것으로, 가장 바람직하게는 TiO2를 사용한다. 상기 반사물질로는 은(silver)입자 및 알루미늄 입자를 사용할 수 있다.The reflective material may be used without limitation to materials known in the art, but is preferably selected from the group consisting of TiO 2 , BaSO 4 , Al (OH) 3 , Al 2 O 3 , CaCO 3 , ZnO and ZnS. One or more kinds of reflection pigments are used. More preferably, a white reflecting pigment is used, and most preferably TiO 2 is used. As the reflective material, silver particles and aluminum particles may be used.

이때, 반사물질은 10 내지 80중량%가 수지에 첨가되는 것으로서, 10중량% 미만이면, 반사효율이 미비하고, 반사물질로서 사용되는 반사용 안료가 80중량%를 초과하여 과량 사용되면, 잘 분산되지 않아 안료의 뭉침현상 등으로 균일한 인쇄가 어렵 다.At this time, the reflecting material is 10 to 80% by weight is added to the resin, if less than 10% by weight, the reflection efficiency is inadequate, if the amount of the reflecting pigment used as a reflection material exceeds 80% by weight, it is well dispersed Uniform printing is difficult due to pigment aggregation.

또한, 본 발명의 반사층(6)은 콘트라스트 등 광학특성을 향상하기 위해 착색 안료와 염료 중 선택된 1종 이상을 반사물질이 혼합된 수지에 더 첨가할 수 있다. 이때, 추가로 첨가될 수 있는 착색 안료로는 적색, 황색, 녹색, 청색, 자색, 및 흑색 등의 유색 안료를 사용하는 것이며, 상기 안료와 염료로 인하여, 반사 또는 여러 가지의 원하는 색상을 구현할 수 있으며, 염료는 물에 녹는 성질이 있는 것이 안료와 다른 특징이다.In addition, the reflective layer 6 of the present invention may further add one or more selected from color pigments and dyes to the resin mixed with the reflective material in order to improve the optical characteristics such as contrast. In this case, as a color pigment that may be added, color pigments such as red, yellow, green, blue, purple, and black may be used, and due to the pigment and the dye, reflection or various desired colors may be realized. The dyes are water soluble and different from pigments.

반사물질이 첨가된 수지, 또는 반사물질 및 상기 추가의 첨가물질이 첨가된 수지의 점도는 1,000∼6,000cps가 바람직하다.The viscosity of the resin to which the reflective material is added or the resin to which the reflective material and the additional additive material are added is preferably 1,000 to 6,000 cps.

본 발명의 투명기재(1)는 광학용으로 사용 가능한 투명 필름에 특별히 제한되지 않고 사용할 수 있으나, 바람직하게는 폴리에틸렌테레프탈레이트(PET)를 사용하는 것이다.The transparent base material 1 of the present invention can be used without particular limitation on the transparent film usable for optics, but preferably, polyethylene terephthalate (PET) is used.

본 발명의 제조방법에 의해 제조된 일체형 복합시트는 광원부(미도시)에서 출사된 빛 중 유효각도에서 입사되는 입사광은 개구부(4)로 입사되어 출광부(2)의 렌즈를 통해 출사되고, 광원부(미도시)에서 출사된 빛 중 유효하지 않은 각도에서 입사되는 입사광은 반사층(6)에 의해 반사되어 광원부로 되돌아 가게 된다.In the integrated composite sheet manufactured by the manufacturing method of the present invention, incident light incident at an effective angle among light emitted from a light source unit (not shown) is incident through the opening 4 and is emitted through the lens of the light exit unit 2, and the light source unit Incident light incident at an invalid angle among the light emitted from (not shown) is reflected by the reflective layer 6 to be returned to the light source unit.

이하, 실시예를 통하여 본 발명을 보다 상세히 설명하고자 한다. Hereinafter, the present invention will be described in more detail with reference to Examples.

본 실시예는 본 발명을 보다 구체적으로 설명하기 위한 것이며, 본 발명의 범위가 이들 실시예에 한정되는 것은 아니다.This embodiment is intended to illustrate the present invention in more detail, and the scope of the present invention is not limited to these examples.

< 실시예 1∼2> < Examples 1 and 2>

고투명한 폴리에스테르필름(도레이새한 주식회사 XG533-100㎛)의 한 면에 하기 표 1에 기재된 바와 같이 양면에 패턴을 설정한 후, 압출성형방법으로 제조하여 도 1과 같은 확산패턴이 형성된 일체형 복합시트를 제조하였다. 이때, 단위렌즈의 폭(width, w)은 200㎛이다.After setting a pattern on both sides of one of the highly transparent polyester film (Toray Saen Co., Ltd. XG533-100㎛) as shown in Table 1 below , an integral composite sheet having a diffusion pattern as shown in FIG. Was prepared. In this case, the width w of the unit lens is 200 μm.

Figure 112008058597196-pat00001
Figure 112008058597196-pat00001

<< 실험예Experimental Example 1> 광학특성 측정 1> Optical property measurement

1. 휘도 측정1. Measurement of luminance

상기에서 제조된 일체형 복합시트의 휘도를 측정하기 위하여 하기와 같이 수행하였다.In order to measure the luminance of the integrated composite sheet prepared above was performed as follows.

32" 직하형 백라이트 유니트를 이용하여 휘도를 측정하였으며, 일체형 복합 시트를 재단, 광확산판(투과율 70%) 위에 장착하여 탑콘사의 BM-7 측정기를 이용하여 측정각도 5도, BM-7과 백라이트 유니트와의 간격을 25cm로 하여 가로 세로 등간격 4분할 하여 그 교차점인 9개 지점의 휘도를 9회 반복 측정하여 휘도 평균값으로 휘도 로 대표하였다. Luminance was measured using a 32 "direct backlight unit, and an integrated composite sheet was cut and mounted on a light diffusion plate (70% transmittance), using Topcon's BM-7 measuring device, measuring angles of 5 degrees, BM-7 and The distance from the backlight unit was 25 cm, and the screen was divided into four equal intervals. The luminance of the nine points, the intersections thereof, was measured 9 times and represented as the luminance average value.

비교를 위하여 레퍼런스로 현재 광학 시트의 표준 구성으로 동일한 광확산판, 확산시트, 프리즘, 보호시트를 차례로 적층하여 동일한 방법으로 휘도를 측정하였다.For comparison, the same light diffusing plate, diffusion sheet, prism, and protective sheet were sequentially stacked in the standard configuration of the current optical sheet, and the luminance was measured by the same method.

그 결과, 본 발명의 일체형 복합시트의 휘도가 레퍼런스의 휘도가 100일 때, 실시예 1의 경우 105, 실시예 2의 경우 110의 휘도를 나타낸 반면, 비교예 1의 휘도는 95, 비교예 2의 경우 85, 비교예 3의 경우 70을 확인하였다. 상기 실시예 1의 휘도 결과는 렌티큘라 렌즈로만 이루어진 비교예 1에 대비하여 높게 나타났으며, 개구부(4)가 실시예 1 보다 넓은 실시예 2가 실시예 1의 경우보다 휘도가 높게 측정되었다. 또한 실시예 1 및 2의 모든 경우 개구부가 매우 좁은 비교예 2와 반사층이 없는 렌티큘러 렌즈로만 이루어진 비교예 3보다 매우 높은 휘도를 보여 주고 있다. 따라서, 종래 렌티큘러 렌즈를 출광부로 이루어진 복합시트 대비하여 본 발명의 일체형 복합시트는 고휘도를 구현할 뿐만 아니라 종래의 3매로 이루어진 표준 광학 시트 대비, 일체형 복합시트 1매로도 그에 상응하는 휘도를 보였다. As a result, when the luminance of the integrated composite sheet of the present invention was 100 for the reference, the luminance was 105 for Example 1 and 110 for Example 2, whereas the luminance of Comparative Example 1 was 95 and Comparative Example 2 In the case of 85 and Comparative Example 3, 70 was confirmed. The luminance result of Example 1 was higher than that of Comparative Example 1 consisting of only a lenticular lens, and Example 2, in which the opening 4 was wider than Example 1, was measured to have higher luminance than that of Example 1. In addition, all of Examples 1 and 2 showed much higher luminance than Comparative Example 2 having a very narrow opening and Comparative Example 3 consisting of only a lenticular lens without a reflective layer. Therefore, the integrated composite sheet of the present invention compared with the conventional lenticular lens composite sheet consisting of the light emitting unit not only implements high brightness, but also shows the corresponding luminance even with one integrated composite sheet compared to the standard optical sheet consisting of three sheets.

2. 2. 은폐력Hiding power 측정 Measure

상기에서 제조된 일체형 복합시트에 대한 은폐력은 육안으로 램프선이 얼마나 보이는가를 측정하였다.The hiding power of the integrated composite sheet prepared above was measured how visible the lamp line is to the naked eye.

그 결과, 램프 은폐성은 실시예 1 > 비교예 1 > 실시예 2의 순서로 측정되었다. 비교예 2와 3은 휘도에서 많은 차이가 나서 은폐력 측정에는 제외하였다. 상기 실시예 2의 경우 반사 면적이 좁아짐에 따라 그 확산성이 낮아 일어난 당연한 결과로 보인다. 이로써 종래의 3매의 광학 시트 구성 대비 일체형 복합시트가 은폐력에 있어서도 동등한 성능을 나타내고 있으며 복합시트의 광학적 설계를 최적함으로써 종래보다 우수한 결과도 보여 줄 것이다.As a result, lamp hiding was measured in the order of Example 1> Comparative Example 1> Example 2. Comparative Examples 2 and 3 have a large difference in luminance, and thus were excluded from the hiding power measurement. In the case of Example 2, as the reflecting area is narrowed, it seems to be a natural result that its diffusion property is low. As a result, the integrated composite sheet exhibits the same performance in hiding power as compared to the conventional three optical sheet configurations, and the optical design of the composite sheet is optimized to show better results than before.

상기에서 살펴본 바와 같이, 본 발명은 단위렌즈가 종래의 렌티큘라 렌즈구조가 아닌, 렌즈의 하단부에 삼각형 단면을 가지는 프리즘 형상과, 렌즈의 중앙부에 그 단면이 원형 또는 타원형의 형상을 동시에 구비함으로써, 유효각도에서 입사되는 입사광뿐만 아니라, 유효하지 않은 각도에서 입사되는 입사광의 집광효율을 극대화한 일체형 고휘도 복합시트를 제공하였다.As described above, the present invention provides a prism shape having a triangular cross section at the lower end of the lens and a circular or oval shape at the center of the lens, instead of the conventional lenticular lens structure. In addition to providing incident light incident at an effective angle, an integrated high-brightness composite sheet maximizing condensing efficiency of incident light incident at an invalid angle was provided.

또한, 본 발명의 일체형 고휘도 복합시트는 확산시트 및 프리즘시트의 기능을 일체화시켜, 제조공정을 단순화함으로써, 제조단가를 낮출 수 있다.In addition, the integrated high-brightness composite sheet of the present invention integrates the functions of the diffusion sheet and the prism sheet to simplify the manufacturing process, thereby lowering the manufacturing cost.

이상에서 본 발명은 기재된 실시예에 대해서만 상세히 기술되었지만, 본 발명의 기술사상 범위 내에서 다양한 변형 및 수정이 가능함은 당업자에게 명백한 것이며, 이러한 변형 및 수정이 첨부된 특허청구범위에 속함은 당연한 것이다. Although the present invention has been described in detail only with respect to the embodiments described, it will be apparent to those skilled in the art that various modifications and variations are possible within the technical scope of the present invention, and such modifications and modifications belong to the appended claims.

도 1은 본 발명의 일체형 고휘도 복합시트의 구조를 도시한 것이고, Figure 1 illustrates the structure of the integrated high brightness composite sheet of the present invention,

도 2는 본 발명의 일체형 고휘도 복합시트에 의한 집광효율을 모식화한 것이고, 2 schematically illustrates the light condensing efficiency of the integrated high-brightness composite sheet of the present invention.

도 3a는 종래 렌티큘러 구조의 렌즈로 이루어진 확산시트에 입사되는 광의 진행경로를 도시한 것이고, FIG. 3A illustrates a traveling path of light incident on a diffusion sheet having a lens having a conventional lenticular structure.

도 3b는 종래 렌티큘러 구조의 렌즈로 이루어진 확산시트에 입사되는 광의 다른 진행경로를 도시한 것이다. 3B illustrates another path of propagation of light incident on a diffusion sheet having a lens having a conventional lenticular structure.

<도면 부호에 대한 간단한 설명><Short description of drawing symbols>

10: 본 발명의 일체형 복합시트10: integrated composite sheet of the present invention

1: 투명기재 2: 출광부 1: transparent material 2: light emitting part

3: 입광부 2a: 렌즈의 중앙부3: light incident part 2a: center part of lens

2b: 렌즈의 하단부 4: 개구부2b: lower portion 4: opening of lens

5: 돌출부 6: 반사층 5: protrusion 6: reflective layer

Claims (13)

투명기재;Transparent substrate; 상기 투명기재의 제1면상에 상호 인접하여 배열된 복수개의 렌즈로 이루어진 출광부; 및 A light emitting unit including a plurality of lenses arranged adjacent to each other on the first surface of the transparent substrate; And 상기 투명기재의 제2면상에 상기 렌즈가 서로 맞닿는 접점영역과 대향(對向)하는 위치에 돌출부가 형성되고, 상기 돌출부 상에 형성된 반사층으로 이루어진 입광부;로 이루어지되, 상기 복수개의 렌즈 하단부가 삼각형 단면을 가지는 프리즘 형상이고, 상기 렌즈의 하단부를 제외한 렌즈 중앙부가 원형 또는 타원형의 단면 형상 구조를 가지는 것을 특징으로 하는 일체형 고휘도 복합시트. And a light incident portion formed on a second surface of the transparent substrate so as to face a contact area in which the lens abuts each other, and a light incident portion formed of a reflective layer formed on the protrusion. A prism shape having a triangular cross section, wherein the central portion of the lens except for the lower end of the lens has a circular or oval cross-sectional structure. 제1항에 있어서, 상기 렌즈의 단위 폭(width) 길이가 50 내지 250㎛인 것을 특징으로 하는 일체형 고휘도 복합시트. The unitary high brightness composite sheet according to claim 1, wherein a unit width of the lens is 50 to 250 µm. 제1항에 있어서, 상기 렌즈의 단위 높이(height)가 상기 렌즈의 단위 폭 길이에 대하여, 25 내지 200%인 것을 특징으로 하는 일체형 고휘도 복합시트. The unitary high brightness composite sheet according to claim 1, wherein the unit height of the lens is 25 to 200% with respect to the unit width length of the lens. 제1항에 있어서, 상기 렌즈 하단부가 상기 렌즈의 높이(height)의 길이에 대하여, 20 내지 80%로 형성된 것을 특징으로 하는 일체형 고휘도 복합시트. The integrated high brightness composite sheet according to claim 1, wherein the lower end of the lens is formed at 20 to 80% with respect to the length of the lens. 제1항에 있어서, 상기 돌출부의 높이가 5 내지 50㎛인 것을 특징으로 하는 일체형 고휘도 복합시트. The integrated high brightness composite sheet according to claim 1, wherein the protrusion has a height of 5 to 50 µm. 제1항에 있어서, 상기 반사층의 두께가 5 내지 50㎛인 것을 특징으로 하는 일체형 고휘도 복합시트. The integrated high brightness composite sheet according to claim 1, wherein the reflective layer has a thickness of 5 to 50 µm. 제1항에 있어서, 상기 돌출부와 바로 이웃하는 돌출부간에 형성된 개구부가 상기 렌즈의 단위 폭 길이에 대하여, 30 내지 90% 인 것을 특징으로 하는 일체형 고휘도 복합시트.The integrated high brightness composite sheet according to claim 1, wherein an opening formed between the protrusion and the immediately adjacent protrusion is 30 to 90% of the unit width of the lens. 제1항에 있어서, 상기 반사층이 반사물질이 첨가된 수지로 형성된 것을 특징으로 하는 일체형 고휘도 복합시트.The integrated high brightness composite sheet according to claim 1, wherein the reflective layer is formed of a resin to which a reflective material is added. 제8항에 있어서, 상기 반사층이 착색안료 또는 염료에서 선택되는 1종 이상과 반사물질이 첨가된 수지로 형성된 것을 특징으로 하는 일체형 고휘도 복합시트.The integrated high brightness composite sheet according to claim 8, wherein the reflective layer is formed of at least one selected from a coloring pigment or a dye and a resin to which a reflective material is added. 제8항에 있어서, 상기 수지가 자외선 경화형수지, 전자선 경화형수지 및 열경화형 수지로 이루어진 군에서 선택되는 어느 하나인 것을 특징으로 하는 일체형 고휘도 복합시트.The integrated high brightness composite sheet according to claim 8, wherein the resin is any one selected from the group consisting of an ultraviolet curable resin, an electron beam curable resin, and a thermosetting resin. 제8항에 있어서, 상기 반사물질이 TiO2, BaSO4, Al(OH)3, Al2O3, CaCO3, ZnO 및 ZnS로 이루어진 군에서 선택되는 1종 이상인 것을 특징으로 하는 일체형 고휘도 복합시트.The integrated high brightness composite sheet according to claim 8, wherein the reflective material is at least one member selected from the group consisting of TiO 2 , BaSO 4 , Al (OH) 3 , Al 2 O 3 , CaCO 3 , ZnO, and ZnS. . 제1항의 일체형 고휘도 복합시트 및 Integrated high brightness composite sheet of claim 1 and 상기 복합시트를 향해 빛을 조사하는 광원부를 포함하는 것을 특징으로 하는 백라이트 어셈블리.And a light source unit irradiating light toward the composite sheet. 제12항의 백라이트 어셈블리를 포함하는 것을 특징으로 하는 액정표시장치.A liquid crystal display device comprising the backlight assembly of claim 12.
KR1020080080412A 2008-08-18 2008-08-18 High luminance multifunctional sheet KR100966136B1 (en)