KR100950503B1 - Polarizing plate with improved dichroic ratio and liquid crystal display having the same - Google Patents

Polarizing plate with improved dichroic ratio and liquid crystal display having the same Download PDF

Info

Publication number
KR100950503B1
KR100950503B1 KR1020080006231A KR20080006231A KR100950503B1 KR 100950503 B1 KR100950503 B1 KR 100950503B1 KR 1020080006231 A KR1020080006231 A KR 1020080006231A KR 20080006231 A KR20080006231 A KR 20080006231A KR 100950503 B1 KR100950503 B1 KR 100950503B1
Authority
KR
South Korea
Prior art keywords
liquid crystal
polarizing plate
dye
film
dichroic dye
Prior art date
Application number
KR1020080006231A
Other languages
Korean (ko)
Other versions
KR20090080332A (en
Inventor
김근영
최우석
윤호철
김성태
Original Assignee
삼성정밀화학 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 삼성정밀화학 주식회사 filed Critical 삼성정밀화학 주식회사
Priority to KR1020080006231A priority Critical patent/KR100950503B1/en
Publication of KR20090080332A publication Critical patent/KR20090080332A/en
Application granted granted Critical
Publication of KR100950503B1 publication Critical patent/KR100950503B1/en

Abstract

이색성비가 향상된 편광판 및 이를 구비하는 액정표시장치가 개시된다. 개시된 편광판은, 배향된 액정 및 상기 액정 사이에 분산되어 상기 액정과 같은 방향으로 배향된 적어도 1종의 이색성 염료를 포함하는 편광막을 구비하고, 상기 편광막의 이색성비는 40 이상인 것을 특징으로 한다.Disclosed are a polarizing plate having an improved dichroic ratio and a liquid crystal display device having the same. The disclosed polarizing plate comprises a polarizing film comprising an oriented liquid crystal and at least one dichroic dye dispersed between the liquid crystals and oriented in the same direction as the liquid crystal, wherein the dichroic ratio of the polarizing film is 40 or more.

따라서, 개시된 편광판 및 이를 구비하는 액정표시장치는 이색성비가 향상되어 높은 편광도를 나타내고 자외선 저항성이 향상될 수 있다. Accordingly, the disclosed polarizing plate and the liquid crystal display device having the same may have a high dichroic ratio, thereby exhibiting a high degree of polarization and improving UV resistance.

Description

이색성비가 향상된 편광판 및 이를 구비하는 액정표시장치{Polarizing plate with improved dichroic ratio and liquid crystal display having the same}Polarizing plate with improved dichroic ratio and liquid crystal display having the same}

본 발명은 편광판 및 이를 채용한 액정표시장치에 관한 것으로서, 더욱 상세하게는 이색성비가 향상된 편광판 및 이를 구비하는 액정표시장치에 관한 것이다.The present invention relates to a polarizing plate and a liquid crystal display device employing the same, and more particularly, to a polarizing plate having an improved dichroic ratio and a liquid crystal display device having the same.

디스플레이 패널은 전자계산기, 전자시계, 자동차 네비게이션, 사무자동화기기, 휴대전화, 노트북 컴퓨터, 및 정보통신 단말기 등의 표시장치에 널리 사용되고 있다. 이러한 표시장치 중 액정표시장치는 내부에 투명전극과 배향막을 형성하여 서로 대향되게 배치한 상부패널과 하부패널, 및 상기 상부패널과 하부패널 사이에 주입된 액정을 포함한다. 현재 사용되고 있는 액정표시장치는 선편광을 이용하고 있으므로, 광흡수형 편광막을 구비한 편광판이 패널의 상하에 배치되어 사용되고 있다.Display panels are widely used in display devices such as electronic calculators, electronic clocks, car navigation systems, office automation equipment, cellular phones, notebook computers, and information communication terminals. Among such display devices, the liquid crystal display device includes an upper panel and a lower panel formed to face each other by forming a transparent electrode and an alignment layer therein, and liquid crystal injected between the upper panel and the lower panel. Since the liquid crystal display currently used uses linear polarization, the polarizing plate provided with the light absorption type polarizing film is arrange | positioned above and below the panel, and is used.

최근 편광판에 요구되는 특성은 광투과율, 편광도, 및 색상과 같은 우수한 광학특성과, 박형화 및 경량화, 그리고 편광판에 사용되는 광흡수 물질의 광학적 성질이 사용기간에 따라 변화되지 않는 성질, 즉 광학적 내구성을 포함한다.Recently, the characteristics required for the polarizing plate are excellent optical properties such as light transmittance, polarization degree, and color, and thinness and weight, and the optical properties of the light absorbing material used in the polarizing plate do not change with the service life, that is, optical durability. It includes.

현재 가장 보편적으로 사용되는 폴리비닐알코올(PVA) 연신 편광 필름의 경우 우수한 광학특성의 구현이 가능하나, 박형화 및 경량화 등이 어려운 문제가 있다. 이러한 문제를 해결하기 위하여 PVA 대신 액정을 사용하여 이를 한 방향으로 배향시키고, 액정의 배향된 방향으로 이색성을 가지는 염료를 배향시켜 사용하는 액정 및 염료 편광 필름의 개발이 시도되고 있다.In the case of polyvinyl alcohol (PVA) stretched polarizing film which is most commonly used at present, it is possible to implement excellent optical properties, but it is difficult to reduce thickness and weight. In order to solve this problem, it has been attempted to develop a liquid crystal and a dye polarizing film using a liquid crystal instead of PVA to align it in one direction and aligning a dye having dichroism in the oriented direction of the liquid crystal.

미국특허출원 제1999-171299호 및 제1997-836635호 등은 용매변성 액정(Lyotropic Liquid Crystal)과 염료 등을 기재 필름 위에 코팅하여 액정 및 염료 편광 필름을 제조하는 기술을 개시하고 있으며, 대한민국특허출원 제2006-7008569호는 열변성 액정(Thermotropic Liquid crystal)과 염료 등을 기판 위에 코팅하여 액정 및 염료 편광 필름을 제조하는 기술을 개시하고 있다.U.S. Patent Application Nos. 1999-171299 and 1997-836635 disclose a technique for manufacturing a liquid crystal and a dye polarizing film by coating a solvent-modified liquid crystal (Lyotropic Liquid Crystal) and dyes on a base film, and the Republic of Korea Patent Application No. 2006-7008569 discloses a technique of manufacturing a liquid crystal and a dye polarizing film by coating a thermotropic liquid crystal and a dye or the like on a substrate.

그러나, 이러한 종래기술로 제조되는 액정 및 염료 편광 필름의 경우, 박형화와 경량화는 가능하지만, 광학 특성, 특히 편광도 성능이 기존의 폴리비닐알코올계 편광 필름에 비해 낮은 단점이 있다.However, in the case of the liquid crystal and the dye polarizing film manufactured by the prior art, it is possible to reduce the thickness and weight, but there is a disadvantage that the optical properties, in particular the polarization degree performance is lower than the conventional polyvinyl alcohol-based polarizing film.

상기 편광도는 이색성비(dichroic ratio)의 크기로 정의되는데, 종래의 액정 및 염료 편광판은 이색성비가 최대 15 정도에 불과하여 만족할만한 편광도를 나타내지 못하였다. The polarization degree is defined as the size of the dichroic ratio, the conventional liquid crystal and the dye polarizing plate did not exhibit satisfactory polarization degree because the dichroic ratio is only about 15 maximum.

또한, 종래의 편광판에 사용되는 광흡수 물질은 사용기간이 경과함에 따라 자외선에 지속적으로 노출됨으로써 그 물성이 변화하여 이색성비가 점진적으로 악화되는 문제점이 있다.In addition, the light absorbing material used in the conventional polarizing plate has a problem that the dichroic ratio is gradually worsened by changing its physical properties by continuously being exposed to ultraviolet light as the use period elapses.

본 발명은 이색성비가 향상되어 높은 편광도를 나타낼 수 있는 편광판 및 이를 채용한 액정표시장치를 제공하는 것을 목적으로 한다.SUMMARY OF THE INVENTION An object of the present invention is to provide a polarizing plate capable of improving dichroic ratio and exhibiting a high degree of polarization and a liquid crystal display device employing the same.

본 발명의 다른 목적은 자외선 저항성이 향상된 편광판 및 이를 채용한 액정표시장치를 제공하는 것이다.Another object of the present invention is to provide a polarizing plate having improved UV resistance and a liquid crystal display device employing the same.

상기와 같은 과제를 해결하기 위하여, 본 발명은,In order to solve the above problems, the present invention,

배향된 액정 및 상기 액정 사이에 분산되어 상기 액정과 같은 방향으로 배향된 적어도 1종의 이색성 염료를 포함하는 편광막을 구비하고,A polarizing film comprising at least one dichroic dye dispersed between the oriented liquid crystal and the liquid crystal and oriented in the same direction as the liquid crystal,

상기 편광막의 이색성비가 40이상인 편광판을 제공한다.Provided is a polarizing plate having a dichroic ratio of the polarizing film of 40 or more.

본 발명의 한 구현예에 따르면, 상기 액정에 대한 상기 이색성 염료의 용해도가 이방성 액정상에서 등방성 액정상으로의 액정의 전이온도보다 10℃ 높은 온도에서 15% 이상이다. According to one embodiment of the invention, the solubility of the dichroic dye in the liquid crystal is at least 15% at a temperature 10 ° C. higher than the transition temperature of the liquid crystal from the anisotropic liquid crystal phase to the isotropic liquid crystal phase.

본 발명의 다른 구현예에 따르면, 상기 편광막의 자외선 저항성은 황색도를 기준으로 측정될 때 ASTM D1925에 따라 자외선 조사전에 측정된 황색도(Yellow index)(YI0)와 누적 조사량이 50J이 되는 시점에서 측정된 자외선 조사후의 황색도(YI)의 차이가 하기 조건을 만족한다: YI-YI0 < 5.According to another embodiment of the present invention, when the ultraviolet resistance of the polarizing film is measured based on the yellowness, the yellowness index (Yellow) (YI0) and the cumulative irradiation amount measured before the ultraviolet irradiation according to ASTM D1925 are 50J. The difference in yellowness (YI) after the ultraviolet irradiation measured satisfies the following condition: YI-YI0 <5.

삭제delete

본 발명의 또 다른 구현예에 따르면, 상기 이색성 염료의 함량은 상기 액정 100중량부 대비 6 내지 15중량부이다. According to another embodiment of the present invention, the content of the dichroic dye is 6 to 15 parts by weight based on 100 parts by weight of the liquid crystal.

본 발명의 또 다른 구현예에 따르면, 상기 이색성 염료는, 최대 흡수파장이 300 내지 500㎚인 제1염료, 최대 흡수파장이 500 내지 600㎚인 제2염료, 최대 흡수파장이 600 내지 700㎚인 제3염료를 포함한다.According to another embodiment of the present invention, the dichroic dye is a first dye having a maximum absorption wavelength of 300 to 500 nm, a second dye having a maximum absorption wavelength of 500 to 600 nm, and a maximum absorption wavelength of 600 to 700 nm. Phosphorus third dye.

본 발명의 또 다른 구현예에 따르면, 상기 액정은 스메틱 액정이다.According to another embodiment of the present invention, the liquid crystal is a smect liquid crystal.

본 발명의 또 다른 구현예에 따르면, 상기 이색성 염료는 요오드계, 안트라퀴논계, 및 아조계로 이루어진 군으로부터 선택된 적어도 1종, 더욱 바람직하게는 적어도 2종, 가장 바람직하게는 적어도 3종이다. According to another embodiment of the present invention, the dichroic dye is at least one selected from the group consisting of iodine-based, anthraquinone-based, and azo-based, more preferably at least two, most preferably at least three. .

본 발명의 또 다른 구현예에 따르면, 상기 액정은 그 사이에 이색성 염료가 분산되어 있는 액정 경화체의 필름 형태이다.According to another embodiment of the present invention, the liquid crystal is in the form of a film of a liquid crystal cured body in which a dichroic dye is dispersed therebetween.

본 발명의 또 다른 구현예에 따르면, 상기 편광판은, 상기 편광막의 일면에 적층된 기능층을 더 구비한다. According to another embodiment of the present invention, the polarizing plate further includes a functional layer laminated on one surface of the polarizing film.

본 발명의 또 다른 구현예에 따르면, 상기 기능층은 하드코팅 기능, 안티글래어 기능, 반사방지 기능, 위상차 보상 기능, 및 오염방지 기능 중 적어도 하나의 기능을 갖는 단일층, 또는 상기 기능들 중 적어도 하나의 기능을 갖는 층이 둘 이상 적층된 다층 구조를 가진다.According to another embodiment of the present invention, the functional layer is a single layer having at least one of a hard coating function, an antiglare function, an antireflection function, a phase difference compensation function, and an antifouling function, or any of the above functions. At least one function has a multilayer structure in which two or more layers are laminated.

또한 상기와 같은 과제를 해결하기 위하여, 본 발명은In addition, in order to solve the above problems, the present invention

상기 구현예들 중 어느 한 구현예에 따른 편광판을 구비하는 액정표시장치를 제공한다.Provided is a liquid crystal display device including a polarizing plate according to any one of the above embodiments.

본 발명에 의하면, 이색성비가 향상되어 높은 편광도를 나타낼 수 있는 편광판 및 이를 채용한 액정표시장치가 제공될 수 있다.According to the present invention, a polarizing plate capable of improving dichroic ratio and exhibiting high polarization degree and a liquid crystal display device employing the same can be provided.

또한 본 발명에 의하면, 자외선 저항성이 향상된 편광판 및 이를 채용한 액정표시장치가 제공될 수 있다.In addition, according to the present invention, a polarizing plate having improved UV resistance and a liquid crystal display device employing the same may be provided.

이하에서는 첨부 도면을 참조하여 본 발명의 바람직한 구현예에 관하여 상세히 설명한다.Hereinafter, with reference to the accompanying drawings will be described in detail a preferred embodiment of the present invention.

도 1은 본 발명의 한 구현예에 따른 편광판을 도시한 단면도이다.1 is a cross-sectional view showing a polarizing plate according to an embodiment of the present invention.

도 1을 참조하면, 본 구현예에 따른 편광판(20)은 베이스필름(21), 배향막(22), 편광막(23), 점착제층(24), 및 기능층(25)을 포함한다.Referring to FIG. 1, the polarizing plate 20 according to the present exemplary embodiment includes a base film 21, an alignment layer 22, a polarizing layer 23, an adhesive layer 24, and a functional layer 25.

베이스필름(21)은 폴리에테르술폰(PES, polyethersulphone), 폴리아크릴레이트(PAR, polyacrylate), 폴리에테르 이미드(PEI, polyetherimide), 폴리에틸렌 나프탈레이트(PEN, polyethyelene naphthalate), 폴리에틸렌 테레프탈레이트(PET, polyethyleneterephthalate), 폴리페닐렌 설파이드(polyphenylene sulfide: PPS), 폴리아릴레이트(polyallylate), 폴리이미드(polyimide), 폴리카보네이트(PC), 셀룰로오스 트리 아세테이트(TAC), 셀룰로오스 아세테이트 프로피오네이트(cellulose acetate propionate: CAP)로 이루어진 그룹으로부터 선택되는 1종 이상의 물질로 형성될 수 있다. 바람직하게는, 폴리카보네이트(PC), 폴리에틸렌 테레프탈레이트(PET, polyethyeleneterephthalate), 트리아세틸 셀룰로오스(TAC), 또는 폴리에틸렌 나프탈레이트(PEN, polyethyelene naphthalate)일 수 있다. 베이스필름(21)은 25 내지 200㎛의 두께로 형성되는 것이 바람직하나, 본 발명이 이에 한정되는 것은 아니다.The base film 21 is made of polyethersulphone (PES), polyacrylate (PAR, polyacrylate), polyetherimide (PEI, polyetherimide), polyethylene naphthalate (PEN, polyethyelene naphthalate), polyethylene terephthalate (PET, polyethyleneterephthalate, polyphenylene sulfide (PPS), polyallylate, polyimide, polycarbonate (PC), cellulose tri acetate (TAC), cellulose acetate propionate: CAP) and one or more materials selected from the group consisting of: Preferably, it may be polycarbonate (PC), polyethylene terephthalate (PET, polyethyeleneterephthalate), triacetyl cellulose (TAC), or polyethylene naphthalate (PEN, polyethyelene naphthalate). Base film 21 is preferably formed to a thickness of 25 to 200㎛, but the present invention is not limited thereto.

배향막(22)은 후술하는 편광막(23)에 포함된 액정을 일정한 방향으로 배향시키기 위한 것으로, 이를 위해 일정한 방향으로 배향처리된다. 상기 배향방법으로는 여러가지 방법이 알려져 있지만, 현재 가장 많이 사용되는 방법은 러빙(rubbing)처리에 의한 배향방법이다. 상기 러빙처리에 의한 배향방법은 베이스필름(21)에 배향막(22)을 형성한 후 이를 러빙포를 이용하여 러빙함으로써 배향막 표면을 일정한 방향으로 배향시키는 방법이다. 이와 같이 함으로써, 도 2에 도시된 바와 같이, 러빙에 의해 배향처리된 배향막(22) 표면에서 후술하는 편광막(23)에 포함된 액정분자(23a)가 상호작용하여 액정에 배향규제력 또는 표면고정력(즉, 프리틸트각과 배향방향)을 제공하고, 이로 인해 배향막(22) 전표면에 걸쳐서 상기 표면에 인접한 액정분자(23a)를 일정한 방향으로 배향시키게 된다. 이와 같이 액정분자(23a)가 일방향으로 배향됨으로써, 액정분자(23a) 사이에 분산되어 있는 이색성 염료(23b)도 액정분자(23a)와 같은 방향으로 배향되게 된다.The alignment layer 22 is used to orient the liquid crystal included in the polarizing layer 23 described later in a predetermined direction, and for this purpose, the alignment layer 22 is aligned in a predetermined direction. Although various methods are known as the orientation method, the most commonly used method is an orientation method by rubbing treatment. The orientation method by the rubbing treatment is a method of orienting the surface of the alignment film in a predetermined direction by forming the alignment film 22 on the base film 21 and then rubbing it with a rubbing cloth. By doing so, as shown in FIG. 2, the liquid crystal molecules 23a included in the polarizing film 23 described later interact with each other on the surface of the alignment film 22 subjected to rubbing to form an alignment control force or surface fixing force on the liquid crystal. (I.e., pretilt angle and orientation direction), thereby aligning the liquid crystal molecules 23a adjacent to the surface in a constant direction over the entire surface of the alignment film 22. As the liquid crystal molecules 23a are oriented in one direction as described above, the dichroic dye 23b dispersed between the liquid crystal molecules 23a is also aligned in the same direction as the liquid crystal molecules 23a.

배향막(22)은 일반적으로 폴리이미드나 폴리아미드 등의 수지에 경화제를 첨가한 배향막 조성물을 용매에 녹여 베이스필름(21) 상에 도포한 후, 건조 및 경화시킴으로써 형성된다. 도포법은 주로 나이프, 콤마, 다이, 그라비아, 닙 등의 코팅헤드를 이용하는 코팅방식에 의한다. 배향막(22)은 0.5 내지 20㎛의 두께로 형성되는 것이 바람직하나, 본 발명이 이에 한정되는 것은 아니다. The alignment film 22 is generally formed by dissolving an alignment film composition in which a curing agent is added to a resin such as polyimide or polyamide in a solvent and applying it onto the base film 21, followed by drying and curing. The coating method is mainly based on a coating method using a coating head such as a knife, comma, die, gravure, nip, and the like. The alignment layer 22 is preferably formed to a thickness of 0.5 to 20㎛, but the present invention is not limited thereto.

한편, 이러한 배향막(22)은 생략될 수도 있는데, 이 경우에는 베이스필름(21)의 표면을 러빙처리함으로써 러빙처리된 베이스필름(21)의 표면이 배향막의 역할을 수행하도록 하게 된다.Meanwhile, the alignment layer 22 may be omitted. In this case, the surface of the rubbed base film 21 serves as an alignment layer by rubbing the surface of the base film 21.

편광막(23)은 배향막(22) 상에 적층되는 것으로 전술한 바와 같이 배향막(22)에 의해 일방향으로 배향된 액정 사이에 분산되어 상기 액정과 같은 방향으로 배향된 적어도 1종, 더욱 바람직하게는 적어도 2종, 가장 바람직하게는 적어도 3종의 이색성 염료를 포함하고, 이러한 편광막(23)의 이색성비는 40 이상이다. 여기서, 이색성비는 액정 및 염료 경화체로 이루어진 필름의 축에 평행한 방향의 평면 편광 흡수도를 상기 축에 직각인 방향의 광흡수도로 나눈 값으로 정의된다. 상기 광흡수도(A)는 하기 수학식 1에 의해 정의된다.The polarizing film 23 is laminated on the alignment film 22 and is dispersed between the liquid crystals oriented in one direction by the alignment film 22 as described above, and is at least one kind, more preferably, aligned in the same direction as the liquid crystal. At least 2 types, most preferably at least 3 types of dichroic dyes are included, and the dichroic ratio of such a polarizing film 23 is 40 or more. Here, dichroic ratio is defined as the value obtained by dividing the planar polarization absorbance in the direction parallel to the axis of the film composed of the liquid crystal and the dye cured product by the light absorption in the direction perpendicular to the axis. The light absorption degree (A) is defined by Equation 1 below.

A = -log10TA = -log 10 T

상기 식에서, A는 광흡수도이고, T는 광투과도이다.Wherein A is light absorption and T is light transmission.

상기 액정은, 도 3에 도시되어 있는 바와 같이, 그 사이에 후술하는 이색성 염료가 분산되어 있는 액정 경화체의 필름 형태로 존재할 수 있다. As shown in FIG. 3, the liquid crystal may exist in the form of a film of a liquid crystal cured body in which a dichroic dye described later is dispersed therebetween.

상기 액정으로는 스메틱(smetic) 액정이 사용되는 것이 바람직하나, 본 발명이 이에 한정되는 것은 아니며, 광학적 이방성을 갖는 것으로 3종 이상의 이색성 염료와 조합하여 40 이상의 이색성비를 제공할 수 있는 한 다른 임의의 액정이 사용되어도 무방하다. 여기서, 스메틱 액정이란 액정분자들이 층층이 정렬된 액정을 의미한다. 구체적으로, 스메틱 액정에서 액정분자는 서로 평행하게 배열되어 있으며, 막대모양의 액정분자가 층 모양의 구조를 형성하고 있다. 또한, 상기 층의 면 에서는 분자의 위치에 규칙성이 없지만 면에 직각인 방향에는 분자 위치에 규칙성을 유지하며, 분자축은 전체로서 한 방향을 향한 질서를 갖는다.As the liquid crystal, a smetic liquid crystal is preferably used, but the present invention is not limited thereto. As long as the liquid crystal has optical anisotropy and a combination of three or more dichroic dyes to provide a dichroic ratio of 40 or more, Any other liquid crystal may be used. Here, the smectic liquid crystal refers to a liquid crystal in which liquid crystal molecules are aligned in layer layers. Specifically, the liquid crystal molecules are arranged in parallel with each other in the smectic liquid crystal, and the rod-shaped liquid crystal molecules form a layered structure. In addition, in the plane of the layer, there is no regularity in the position of the molecule, but in the direction perpendicular to the plane, the regularity is maintained in the molecular position, and the molecular axis has an order toward one direction as a whole.

상기 이색성 염료(dichroic dye)는 결정된 파장 영역에 대하여, 두개의 편광직교 성분들 중 하나의 광을 흡수하고 다른 하나의 편광 직교 성분을 투과시키는 염료를 의미한다. 즉, 이색성 염료는 광을 선형으로 편광시키는 특성을 갖는다. The dichroic dye refers to a dye that absorbs light of one of two polarization orthogonal components and transmits another polarization orthogonal component with respect to the determined wavelength region. In other words, the dichroic dye has a property of linearly polarizing light.

상기 액정에 대한 이색성 염료의 용해도는 이방성 액정상에서 등방성 액정상으로의 액정의 전이온도보다 10℃ 높은 온도에서 15% 이상이다. 액정 물질은 최초의 고체상태에서 가열하게 되면 이방성을 가지는 액정상(Nematic 또는 Smectic)을 구현하다가 더 가열하면 액체상태(Isotropic Phase)로 바뀌게 된다. 즉, 상기 액정의 전이온도란 액정이 이방성 액정상에서 완전한 등방성 액체상으로 바뀌는 온도를 의미한다. 즉, 등방성 액체 상태에서 액정 물질에 대한 염료의 용해도는 15% 이상이어야 한다는 것이다. 상기 용해도가 15% 이상인 영역에서는 그 값이 높을수록 더욱 바람직한데, 이는 염료의 용해도가 높아야만 액정내에서 염료가 균일하게 분포될 수 있기 때문이다.The solubility of the dichroic dye in the liquid crystal is at least 15% at a temperature 10 占 폚 higher than the transition temperature of the liquid crystal from the anisotropic liquid crystal phase to the isotropic liquid crystal phase. When the liquid crystal material is heated in the first solid state, an anisotropic liquid crystal phase (Nematic or Smectic) is realized, and when further heated, the liquid crystal material is changed into an isotropic phase. In other words, the transition temperature of the liquid crystal means the temperature at which the liquid crystal changes from an anisotropic liquid crystal phase to a completely isotropic liquid phase. That is, the solubility of the dye in the liquid crystal material in the isotropic liquid state should be at least 15%. In the region where the solubility is 15% or more, the higher the value, the more preferable, since the dye may be uniformly distributed in the liquid crystal only when the solubility of the dye is high.

이 후 상기 액정을 냉각할 경우, 등방성 액체는 다시 이방성 액정상을 가지게 된다. 상기 액정이 이방성 액정상이 되면서 용해되었던 염료가 액정방향으로 배향되면서 석출되게 된다. 이때 염료는 액정에 균일하게 분산된 상태에서 응집없이 석출된다.After cooling the liquid crystal afterwards, the isotropic liquid again has an anisotropic liquid crystal phase. The dye dissolved as the liquid crystal becomes an anisotropic liquid crystal phase is precipitated while being oriented in the liquid crystal direction. At this time, the dye is precipitated without aggregation in the state uniformly dispersed in the liquid crystal.

상기 용해도가 15% 미만이면 상기 이색성 염료의 배향 방향이 상기 액정의 배향 방향과 일치하지 않아 그 편차가 커져서 완성된 편광막(23)의 이색성비가 작아 지므로 바람직하지 않다.If the solubility is less than 15%, the orientation direction of the dichroic dye does not coincide with the orientation direction of the liquid crystal, and the deviation becomes large, which is not preferable because the dichroic ratio of the completed polarizing film 23 becomes small.

또한, 상기 이색성 염료를 사용한 편광 필름은 자외선 조사 이 후의 색상 변화가 적은 것을 특징으로 한다. In addition, the polarizing film using the dichroic dye is characterized by little color change after ultraviolet irradiation.

또한, 상기 이색성 염료의 함량은 상기 액정 100중량부 대비 6 내지 15중량부이다. 상기 함량이 6중량부 미만이면 광흡수율이 낮아져서 편광도가 지나치게 낮아지기 때문에 바람직하지 않고, 15중량부를 초과하게 되면 상기 이색성 염료가 액정에 완전히 용해되지 않아서 이색성비 또는 광투과율이 지나치게 낮아지기 때문에 바람직하지 않다. In addition, the content of the dichroic dye is 6 to 15 parts by weight based on 100 parts by weight of the liquid crystal. If the content is less than 6 parts by weight, the light absorption rate is lowered and the polarization degree is too low. .

또한 상기 이색성 염료는 최대 흡수파장이 300 내지 500㎚인 제1염료, 최대 흡수파장이 500 내지 600㎚인 제2염료, 최대 흡수파장이 600 내지 700㎚인 제3염료를 포함한다. 이와 같이 최대 흡수파장의 범위가 서로 다른 3종 이상의 이색성 염료를 사용함으로써 400 내지 700㎚의 가시광 영역 전부에 걸쳐 광을 선형으로 편광시킬 수 있다.In addition, the dichroic dye includes a first dye having a maximum absorption wavelength of 300 to 500 nm, a second dye having a maximum absorption wavelength of 500 to 600 nm, and a third dye having a maximum absorption wavelength of 600 to 700 nm. As such, by using three or more dichroic dyes having different maximum absorption wavelengths, light can be linearly polarized over the entire visible light region of 400 to 700 nm.

또한, 상기 이색성 염료는 액정 100중량부 대비 2 내지 5중량부의 제1염료, 2 내지 5중량부의 제2염료, 및 2 내지 5중량부의 제3염료를 포함한다. In addition, the dichroic dye includes 2 to 5 parts by weight of the first dye, 2 to 5 parts by weight of the second dye, and 2 to 5 parts by weight of the third dye relative to 100 parts by weight of the liquid crystal.

이러한 이색성 염료로는 안트라퀴논(anthraquinone)계, 프탈로시아닌(phthalocyanine)계, 프로피린아조 염료, 비아조 염료, 및 트리아조 염료가 사용될 수 있다. 특히, 이색성 아조(azo) 염료가 적합하다. 적합한 이색성 아조염료의 예는 미국등록특허 제 6,133,973호에 개시된 것을 포함한다. 구체적으로, 상기 이색성 염료는 요오드계, 안트라퀴논계, 및 아조계로 이루어진 군으로부터 선택된 적 어도 1종, 더욱 바람직하게는 적어도 2종, 가장 바람직하게는 적어도 3종인 것이 바람직하다. As such dichroic dyes, anthraquinone-based, phthalocyanine-based, propyrinazo-dyes, viazo-dyes, and triazo-dyes may be used. In particular, dichroic azo dyes are suitable. Examples of suitable dichroic azo dyes include those disclosed in US Pat. No. 6,133,973. Specifically, the dichroic dye is preferably at least one, more preferably at least two, and most preferably at least three selected from the group consisting of iodine, anthraquinone, and azo.

상기 액정 편광막(23)의 제조방법은 필름(즉, 배향막(22))상에 액정을 직접 코팅 및 경화시켜 박막을 만드는 방법과 한쌍의 유리기판 사이에 액정을 주입한 후 경화시켜 박막을 만드는 두가지 방법이 이용될 수 있다. 먼저 필름상에 직접 코팅 하는 방법은, 광학적 이방성을 갖는 액정물질에 이색성 염료와, 중합개시제, 레벨링제, 대전방지제 등의 첨가제를 배합하여 액정 편광막 조성물을 제조한 다음, 이 액정 편광막 조성물을 배향막(22) 상에 코팅하고, 건조 및 경화시킴으로써 액정 편광막(23)을 형성하는 것이다. 상기 중합개시제로는 카르보닐 화합물, 유황 화합물, 아조 화합물 또는 유기과산화물 등의 광중합개시제가 사용되는 것이 바람직하지만, 본 발명이 이에 한정되는 것은 아니다. 또한, 상기 경화제로는 알파-히드록시-케톤계, 페닐글리옥실레이트(phenylglyoxylate)계, 벤질 디메틸-케톤, 및/또는 아실 포스핀(acyl phosphine) 등이 사용될 수 있으나 본 발명이 이에 한정되는 것은 아니다. 또한, 상기 레벨링제로는 Ciba-Geigy사의 Tego-Rad 등이 사용될 수 있다. 또한, 상기 대전방지제의 종류도 특별히 한정되지 않는다. The manufacturing method of the liquid crystal polarizing film 23 is a method of making a thin film by directly coating and curing the liquid crystal on the film (ie, the alignment layer 22) and injecting the liquid crystal between a pair of glass substrates to make a thin film Two methods can be used. First, a method of directly coating on a film is to prepare a liquid crystal polarizing film composition by blending a dichroic dye and an additive such as a polymerization initiator, a leveling agent, an antistatic agent to a liquid crystal material having optical anisotropy, and then the liquid crystal polarizing film composition Is coated on the alignment film 22, dried and cured to form the liquid crystal polarizing film 23. As the polymerization initiator, a photopolymerization initiator such as a carbonyl compound, a sulfur compound, an azo compound or an organic peroxide is preferably used, but the present invention is not limited thereto. In addition, the curing agent may be alpha-hydroxy ketone-based, phenylglyoxylate-based, benzyl dimethyl- ketone, and / or acyl phosphine (acyl phosphine), but the present invention is not limited thereto. no. In addition, the leveling agent may be used, such as Tego-Rad of Ciba-Geigy. Moreover, the kind of said antistatic agent is not specifically limited, either.

이와는 달리, 한쌍의 유리기판 사이에 액정을 주입하여 액정 편광막(23)을 제조하는 방법은, 배향막이 한면 또는 양면에 코팅되어 있는 한쌍의 유리기판 사이에 액정물질과 이색성 염료, 중합개시제 등의 첨가물이 배합된 배합물을 주입시킨후 경화시킴으로써 액정 편광막(23)을 형성하는 것이다. 이 경우 용도에 따라 유리기판을 제거하여 사용하는 것도 가능하다.In contrast, a method of manufacturing a liquid crystal polarizing film 23 by injecting a liquid crystal between a pair of glass substrates includes a liquid crystal material, a dichroic dye, a polymerization initiator, or the like, between a pair of glass substrates on which an alignment layer is coated on one or both surfaces. The liquid crystal polarizing film 23 is formed by hardening | curing after inject | pouring the compound | mixture which the additive of which was mix | blended. In this case, it is also possible to remove and use the glass substrate depending on the application.

이와 같이 형성된 액정 편광막(23)은 40 이상의 이색성비를 가짐으로써 높은 편광도를 나타낼 뿐만 아니라, 높은 자외선 저항성을 가짐으로써 장기간 사용시에도 상기 이색성비를 일정하게 유지하여 높은 편광도를 지속적으로 나타낼 수 있다. 구체적으로, 상기 편광막의 자외선 저항성은 황색도를 기준으로 측정될 때 ASTM D1925에 따라 자외선 조사전에 측정된 황색도(Yellow index)(YI0)와 누적 조사량이 50J이 되는 시점에서 측정된 자외선 조사후의 황색도(YI)의 차이(YI-YI0)가 5 이하일 수 있다.
또한, 이러한 액정 편광막(23)은 우수한 기계적 강도를 갖고, 열 및/또는 습도에 의해 변형되지 않으므로 광흡수형 편광막으로서 연신 필름을 사용하는 경우에서와 같이 편광막 보호필름을 구비하지 않아도 된다. 아울러, 연신 필름을 사용할 경우에 요구되는, 편광막과 편광막 보호필름 사이에 배치되는 점착제층도 불필요하게 된다. 또한, 액정 편광막(23)은 0.5 내지 20㎛의 두께로 형성되는 것이 바람직하나, 본 발명이 이에 한정되는 것은 아니다.The liquid crystal polarizing film 23 formed as described above not only exhibits a high degree of polarization by having a dichroic ratio of 40 or more, but also has a high UV resistance to maintain a constant degree of dichroic ratio even when used for a long period of time, thereby continuously displaying a high degree of polarization. Specifically, the ultraviolet resistance of the polarizing film when measured based on the yellowness, yellow after ultraviolet irradiation measured at the time of the yellow index (YI0) and cumulative irradiation amount measured before the ultraviolet irradiation according to ASTM D1925 50J The difference YI-YI0 of the degree YI may be 5 or less.
In addition, since the liquid crystal polarizing film 23 has excellent mechanical strength and is not deformed by heat and / or humidity, it is not necessary to provide a polarizing film protective film as in the case of using a stretched film as a light absorption type polarizing film. . In addition, the adhesive layer arrange | positioned between a polarizing film and a polarizing film protective film required when using a stretched film also becomes unnecessary. In addition, the liquid crystal polarizing film 23 is preferably formed to a thickness of 0.5 to 20㎛, but the present invention is not limited thereto.

본 구현예에 따른 편광판(20)은 편광막(23)의 일면, 즉 배향막(22)과 반대쪽 면에 적층된 기능층(25)을 더 구비할 수 있다. 이러한 기능층(25)은 하드코팅 기능, 안티글래어 기능, 반사방지 기능, 위상차 보상 기능, 및 오염방지 기능 중 적어도 하나의 기능을 갖는 단일층, 또는 상기 기능들 중 적어도 하나의 기능을 갖는 층이 둘 이상 적층된 다층 구조를 가진다. 또한, 이러한 기능층(25)은 점착제층(24)에 의해 편광막(23)에 부착된다. 점착제층(24)의 재질은 특별히 한정되지는 않으나 감압성 점착제(pressure sensitive adhesive: PSA)인 것이 바람직하다. 점착제층(24)은 바람직하게는 0.01 내지 5㎛, 더욱 바람직하게는 0.05 내지 5㎛의 건조 두께(dry thickness)로 도포된다.The polarizing plate 20 according to the present exemplary embodiment may further include a functional layer 25 stacked on one surface of the polarizing film 23, that is, the surface opposite to the alignment layer 22. The functional layer 25 is a single layer having at least one of a hard coating function, an antiglare function, an antireflection function, a phase difference compensation function, and an antifouling function, or a layer having at least one of the above functions. It has a multilayer structure in which two or more are stacked. In addition, this functional layer 25 is attached to the polarizing film 23 by the adhesive layer 24. Although the material of the adhesive layer 24 is not specifically limited, It is preferable that it is a pressure sensitive adhesive (PSA). The pressure-sensitive adhesive layer 24 is preferably applied at a dry thickness of 0.01 to 5 mu m, more preferably 0.05 to 5 mu m.

또한 본 발명에 의하면 상기와 같은 구성을 갖는 편광판(20)을 구비한 액정표시장치가 제공될 수 있다.In addition, according to the present invention can be provided with a liquid crystal display device having a polarizing plate 20 having the above configuration.

이하 실시예를 들어 본 발명을 상세히 설명한다. 그러나 본 발명이 하기 실시예로만 한정되는 것은 아니다.The present invention will be described in detail with reference to the following Examples. However, the present invention is not limited only to the following examples.

실시예Example

도 1의 구조와 유사한 구조를 갖는 편광판을 제조하였다. 다만, 도 1의 구성요소 중 배향막(22), 점착제층(24), 및 기능층(25)은 생략되었다. 베이스필름(21)으로는 러빙 처리된 두께 50㎛의 폴리에틸렌 테레프탈레이트 필름을 사용하였다.A polarizing plate having a structure similar to that of FIG. 1 was prepared. However, among the components of FIG. 1, the alignment layer 22, the pressure-sensitive adhesive layer 24, and the functional layer 25 are omitted. As the base film 21, a polyethylene terephthalate film having a thickness of 50 µm subjected to a rubbing treatment was used.

(액정의 선택)(Selection of liquid crystal)

스위스 Ciba사 제조 ABPAC6 100중량부(10g)를 사용하였다.100 parts by weight (10 g) of ABPAC6 manufactured by Ciba, Switzerland was used.

(이색성 염료의 선택)(Choice of dichroic dye)

제조예 1: 이색성 염료(1)의 선택Preparation Example 1 Selection of Dichroic Dye (1)

최대 흡수 파장이 420㎚인 Ciba사 제조 GSID 2184를 액정 100중량부 대비 5중량부(0.5g)를 사용하였다.5 parts by weight (0.5 g) of GSID 2184, manufactured by Ciba, Inc., having a maximum absorption wavelength of 420 nm, was used.

제조예 2: 이색성 염료(2)의 선택Preparation Example 2 Selection of Dichroic Dye (2)

최대 흡수 파장이 510㎚인 Ciba사 제조 GSID 2219를 액정 100중량부 대비 5중량부(0.5g)를 사용하였다.5 parts by weight (0.5 g) of GSID 2219 manufactured by Ciba, Inc., having a maximum absorption wavelength of 510 nm, was used.

제조예 3: 이색성 염료(3)의 선택Preparation Example 3 Selection of Dichroic Dye (3)

최대 흡수 파장이 630㎚인 Ciba사 제조 CISG 449를 액정 100중량부 대비 5중량부(0.5g)를 사용하였다.5 parts by weight (0.5 g) of CISG 449 manufactured by Ciba, Inc., having a maximum absorption wavelength of 630 nm, was used.

(편광필름의 제조)(Manufacture of Polarizing Film)

상기 액정 및 이색성 염료(1),(2),(3)을 디클로로메탄과 혼합하여 전체 고형 분의 농도가 40 중량%인 혼합 용액을 제조하였다. 상기 혼합 용액 전체의 100중량부 대비 5중량부(1.44g)의 광개시제(Ciba사, IG-184)와 0.2중량부(0.06g)의 레벨링 첨가제(Ciba사, Tego-Rad)를 상기 용액에 더 첨가하였다. 상기 제조된 용액을 폴리에틸렌 테레프탈레이트 필름 위에 롤 코팅 방법에 의해 박막 도포하였다. 도포 후 건조기에서 용제를 건조시키며 액정을 배향시킨 후 자외선 조사를 통해 필름을 제조하였다. 이 때 건조 조건은 90℃이었고, 자외선 광조사는 300W(중심 파장 360nm)램프를 사용하였다. 상기와 같이 제조된 도막 두께는 4.5㎛이었다.The liquid crystal and the dichroic dyes (1), (2) and (3) were mixed with dichloromethane to prepare a mixed solution having a total solid content of 40 wt%. 5 parts by weight (1.44 g) of photoinitiator (Ciba, IG-184) and 0.2 parts by weight (0.06 g) of leveling additive (Ciba, Tego-Rad) were added to the solution. Added. The prepared solution was thin-film coated on a polyethylene terephthalate film by a roll coating method. After coating, the solvent was dried in a drier and the liquid crystals were oriented to prepare a film through ultraviolet irradiation. At this time, the drying conditions were 90 ℃, UV light irradiation used a 300W (center wavelength 360nm) lamp. The coating film thickness prepared as above was 4.5 micrometers.

비교예Comparative example

실시예에서 3종의 이색성 염료 대신에 아조 염료 NKX2029C를 액정 100중량부 대비 3중량부(0.3g)사용한 것을 제외하고는 실시예 1과 동일한 방법으로 도막 두께 4.0~4.2㎛의 필름을 얻었다.A film having a coating thickness of 4.0 to 4.2 µm was obtained in the same manner as in Example 1, except that 3 parts by weight (0.3 g) of azo dye NKX2029C was used instead of three parts of dichroic dye in Examples.

평가예Evaluation example

(파장대별 광흡수도 그래프)(Light Absorption Graph by Wavelength)

실시예 및 비교예에서 제조한 편광필름의 광흡수축 및 광투과축 각각에 대한 파장대별 광흡수도 그래프를 도 4 및 도 5에 나타내었다. 파장대별 광흡수도 측정을 위해 광원상에 편광필터가 배치된 자외선-가시광선 스펙트럼 측정기인 V-550(일본 자스코(JASCO)사 제품)을 사용하였다. 4 and 5 show graphs of light absorption for each wavelength band of the light absorption axis and the light transmission axis of the polarizing films prepared in Examples and Comparative Examples. In order to measure the light absorption of each wavelength band, V-550 (produced by JASCO, Japan), which is an ultraviolet-visible spectrum analyzer having a polarizing filter disposed on a light source, was used.

도 4 및 도 5를 참조하면, 3종의 염료를 사용하는 실시예의 경우가 1종의 염료를 사용하는 비교예의 경우에 비해 가시광선 커버 영역이 넓고, 최대 광흡수도도 크다는 사실을 확인할 수 있다.4 and 5, it can be seen that the embodiment using three dyes has a wider visible light cover area and a larger maximum light absorption than that of the comparative example using one dye. .

(이색성비 계산)(Dichroism Ratio Calculation)

도 4와 도 5로부터 실시예와 비교예에서 제조한 편광필름의 이색성비를 계산한 결과, 실시예의 경우 그 값이 52이었고, 비교예의 경우에는 그 값이 12이었다. 여기서, 이색성비는 도 4 및 도 5의 그래프에서 각 스펙트럼과 파장축(가로축)으로 이루어진 면적을 각각 구한 다음, 광흡수축 스펙트럼의 면적을 광투과축 스펙트럼의 면적으로 나누어 계산하였다. 따라서, 본 실시예의 경우가 비교예의 경우에 비해 이색성비의 값이 훨씬 커졌음을 확인할 수 있다. As a result of calculating the dichroic ratios of the polarizing films prepared in Examples and Comparative Examples from FIGS. 4 and 5, the value was 52 in Examples, and 12 in the Comparative Examples. Here, the dichroic ratio was calculated by dividing the area of each spectrum and the wavelength axis (horizontal axis) in the graphs of FIGS. 4 and 5, and then dividing the area of the light absorption axis spectrum by the area of the light transmission spectrum. Therefore, it can be confirmed that the value of the dichroic ratio is much larger in the case of the present example than in the case of the comparative example.

(자외선 저항성 평가)UV resistance evaluation

실시예와 비교예에서 제조한 편광필름에 대하여 ASTM D1925에 따라 황색도(YI: Yellow Index)를 측정하였다.Yellow index (YI) was measured according to ASTM D1925 for the polarizing films prepared in Examples and Comparative Examples.

구체적으로, 세명 백트론사의 MTL 4kw 가이드부 경화기를 상기 편광필름을 자외선에 노출시켜 변색을 촉진시킨 후 누적 조사량이 50J이 되는 시점에서 ASTM D1925에 따라 YI(Yellow Index)를 측정하였다. 이 때 테스트 전후의 YI차이가 5초과이면 불량, 5이하이면 양호로 판정하였는데, 실시예의 경우 YI차이가 3.2로 양호하였으나 비교예의 경우에는 6.1로 불량하였다.Specifically, the YTL (Yellow Index) was measured according to ASTM D1925 at the time when the cumulative irradiation amount was 50J after the polarizing film was exposed to ultraviolet rays to promote discoloration by exposing the polarizing film to ultraviolet rays. At this time, if the YI difference before and after the test was more than 5, it was determined to be poor, and if it was 5 or less, the YI difference was good as 3.2, but in the comparative example, it was poor as 6.1.

이상에서 도면을 참조하여 본 발명에 따른 바람직한 구현예가 설명되었으나, 이는 예시적인 것에 불과하며, 당해 기술분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 구현예가 가능하다는 점을 이해할 수 있을 것이다. 따라서, 본 발명의 보호범위는 첨부된 특허청구범위에 의해서 정해져야 할 것이다. Although the preferred embodiment according to the present invention has been described above with reference to the drawings, this is merely exemplary, and those skilled in the art can understand that various modifications and equivalent other embodiments are possible therefrom. There will be. Therefore, the protection scope of the present invention should be defined by the appended claims.

도 1은 본 발명의 한 구현예에 따른 편광판을 도시한 단면도이다.1 is a cross-sectional view showing a polarizing plate according to an embodiment of the present invention.

도 2는 배향막의 러빙공정과 러빙각도에 따른 액정의 배향을 개략적으로 설명하기 위한 도면이다.2 is a view for schematically explaining the alignment of the liquid crystal according to the rubbing process and the rubbing angle of the alignment layer.

도 3은 이색성 염료가 분산되어 있는 액정이 자외선 경화되어 액정 경화체를 형성하는 원리를 설명하기 위한 도면이다.It is a figure for demonstrating the principle in which the liquid crystal in which dichroic dye is disperse | distributed is ultraviolet-cured, and forms a liquid crystal hardened body.

도 4는 실시예에서 제조한 편광막의 파장대별 광흡수도를 나타낸 그래프이다.4 is a graph showing light absorption by wavelength band of the polarizing film prepared in Example.

도 5는 비교예에서 제조한 편광막의 파장대별 광흡수도를 나타낸 그래프이 다.5 is a graph showing light absorption by wavelength band of a polarizing film prepared in Comparative Example.

<도면의 주요 부분에 대한 부호의 설명><Explanation of symbols for the main parts of the drawings>

20: 편광판 23: 편광막20: polarizing plate 23: polarizing film

24: 점착제층 25: 기능층24: pressure-sensitive adhesive layer 25: functional layer

22: 배향막 22: alignment layer

Claims (11)

배향된 액정 및 상기 액정 사이에 분산되어 상기 액정과 같은 방향으로 배향된 적어도 1종의 이색성 염료를 포함하는 편광막을 구비하고,A polarizing film comprising at least one dichroic dye dispersed between the oriented liquid crystal and the liquid crystal and oriented in the same direction as the liquid crystal, 상기 편광막의 자외선 저항성은 황색도를 기준으로 측정될 때 ASTM D1925에 따라 자외선 조사전에 측정된 황색도(Yellow index)(YI0)와 누적 조사량이 50J이 되는 시점에서 측정된 자외선 조사후의 황색도(YI)의 차이가 하기 조건을 만족하는 편광판:The UV resistance of the polarizing film, when measured based on the yellowness, is measured according to ASTM D1925 (Yellow index (YI0) and the yellowness after UV irradiation measured at the time when the cumulative irradiation amount is 50J (YI). A polarizer whose difference satisfies the following conditions: YI-YI0 < 5.YI-YI0 <5. 제1항에 있어서,The method of claim 1, 상기 액정에 대한 상기 이색성 염료의 용해도가 이방성 액정상에서 등방성 액정상으로의 액정의 전이온도보다 10℃ 높은 온도에서 15% 이상인 것을 특징으로 하는 편광판.And a solubility of the dichroic dye in the liquid crystal is 15% or more at a temperature of 10 ° C. higher than the transition temperature of the liquid crystal from the anisotropic liquid crystal phase to the isotropic liquid crystal phase. 삭제delete 제1항에 있어서,The method of claim 1, 상기 이색성 염료의 함량은 상기 액정 100중량부 대비 6 내지 15중량부인 것 을 특징으로 하는 편광판. The dichroic dye content is 6 to 15 parts by weight based on 100 parts by weight of the liquid crystal. 제1항에 있어서,The method of claim 1, 상기 이색성 염료가 최대 흡수파장이 300 내지 500㎚인 제1염료, 최대 흡수파장이 500 내지 600㎚인 제2염료, 최대 흡수파장이 600 내지 700㎚인 제3염료를 포함하는 것을 특징으로 하는 편광판. The dichroic dye comprises a first dye having a maximum absorption wavelength of 300 to 500 nm, a second dye having a maximum absorption wavelength of 500 to 600 nm, and a third dye having a maximum absorption wavelength of 600 to 700 nm. Polarizer. 제1항에 있어서, The method of claim 1, 상기 액정은 스메틱 액정인 것을 특징으로 하는 편광판.Said liquid crystal is a smect liquid crystal, The polarizing plate characterized by the above-mentioned. 제1항에 있어서, The method of claim 1, 상기 이색성 염료는 요오드계, 안트라퀴논계, 및 아조계로 이루어진 군으로부터 선택된 적어도 3종인 것을 특징으로 하는 편광판. The dichroic dye is at least three selected from the group consisting of iodine-based, anthraquinone-based, and azo-based polarizing plate. 제1항에 있어서,The method of claim 1, 상기 액정은 그 사이에 이색성 염료가 분산되어 있는 액정 경화체의 필름 형태로 존재하는 것을 특징으로 하는 편광판.The liquid crystal is present in the form of a film of a liquid crystal cured body in which a dichroic dye is dispersed therebetween. 제1항에 있어서,The method of claim 1, 상기 편광막의 일면에 적층된 기능층을 더 구비하는 것을 특징으로 하는 편광 판. The polarizing plate further comprises a functional layer laminated on one surface of the polarizing film. 제9항에 있어서,10. The method of claim 9, 상기 기능층은 하드코팅 기능, 안티글래어 기능, 반사방지 기능, 위상차 보상 기능, 및 오염방지 기능 중 적어도 하나의 기능을 갖는 단일층, 또는 상기 기능들 중 적어도 하나의 기능을 갖는 층이 둘 이상 적층된 다층 구조를 가진 것을 특징으로 하는 편광판.The functional layer may be a single layer having at least one of a hard coating function, an antiglare function, an antireflection function, a phase difference compensation function, and an antifouling function, or two or more layers having at least one of the above functions. A polarizing plate having a laminated multilayer structure. 제1항, 제2항 및 제4항 내지 제10항 중 어느 한 항에 따른 편광판을 구비하는 액정표시장치.A liquid crystal display device comprising the polarizing plate according to any one of claims 1, 2, and 4 to 10.
KR1020080006231A 2008-01-21 2008-01-21 Polarizing plate with improved dichroic ratio and liquid crystal display having the same KR100950503B1 (en)