KR100890783B1 - Manfacturing method of a ceramic ball used in neutralizating a poisonous material - Google Patents
Manfacturing method of a ceramic ball used in neutralizating a poisonous material Download PDFInfo
- Publication number
- KR100890783B1 KR100890783B1 KR1020070010021A KR20070010021A KR100890783B1 KR 100890783 B1 KR100890783 B1 KR 100890783B1 KR 1020070010021 A KR1020070010021 A KR 1020070010021A KR 20070010021 A KR20070010021 A KR 20070010021A KR 100890783 B1 KR100890783 B1 KR 100890783B1
- Authority
- KR
- South Korea
- Prior art keywords
- ball
- toxic substances
- ceramic
- neutralizing
- food waste
- Prior art date
Abstract
본 발명은 음식물 쓰레기 처리시 발생하는 독성물을 중화하는 세라믹볼 제조방법에 관한 것으로, 음식물 쓰레기처리의 배출공정에서 발생하는 독성산화물 또는 휘발성 독성물과 이에 함유된 악취가스를 세라믹 볼 형태의 중화재를 건식 또는 습식방식의 음식물 쓰레기 처리장치 내에서 사용하여 효율적으로 중화하기 위한 독성물 중화용 세라믹볼 제조방법을 제공하는 것을 목적으로 한다. 본 발명은 음식물 쓰레기 배출공정에서 발생하는 인체에 유해한 독성물과 악취를 중화하기 위한 독성물 중화용 세라믹볼 제조방법에 있어서, (a)주로 운모와 고령토로 구성되며 소량의 구리를 함유한 광물질 85~90 Wt%과, 주로 쑥과 활성탄으로 구성되며 소량의 허브를 함유한 섬유성 물질 3~8 Wt%과, 다시마와 우뭇가사리를 함유한 해조류 3~8 Wt%를 주요성분으로 포함하는 혼합물을 3~4 시간 동안 혼합하고 졸(sol)상태로 숙성하는 공정, (b)상기 숙성된 혼합물을 3~5일간 교반조에서 교반하고 혼합물을 볼형상으로 정제하는 정제장치를 사용하여 5 ~ 15mm 크기의 다공성 개방형의 볼을 형성하는 공정, 및 (c)상기 다공성 개방형 볼을 4~5일간 건조한 후, 고온로에서 300 ~ 1500 ℃까지의 범위에서 열처리하여 상온에서 냉각시키는 공정을 포함한다. The present invention relates to a ceramic ball manufacturing method for neutralizing toxic substances generated during the treatment of food waste, wherein the toxic oxides or volatile toxic substances generated in the discharge process of the food waste treatment and the odorous gas contained therein are neutralized in the form of ceramic balls. It is an object of the present invention to provide a method for producing a ceramic ball for neutralizing toxic substances for efficiently neutralizing using a dry or wet food waste treatment apparatus. The present invention provides a ceramic ball manufacturing method for neutralizing toxic substances harmful to humans and odors generated in a food waste discharge process, comprising: (a) mainly mica and kaolin, and containing a small amount of copper 85 3 mixtures containing ~ 90 Wt%, 3-8 Wt% fibrous material consisting mainly of wormwood and activated carbon and containing a small amount of herbs, and 3-8 Wt% seaweeds containing kelp and fern Mixing for 4 hours and aging in a sol state, (b) stirring the matured mixture in a stirring vessel for 3 to 5 days and purifying the mixture into a ball shape with a size of 5 to 15 mm. Forming a porous open ball, and (c) drying the porous open ball for 4 to 5 days, and heat-treated in a range from 300 to 1500 ℃ in a high temperature furnace to cool at room temperature.
광물질, 섬유성 물질, 해조류,세라믹 볼 Minerals, fibrous materials, algae, ceramic balls
Description
도 1은 본 발명에 따른 일 실시예의 독성물 중화용 세라믹볼 제조방법을 나타낸 공정도이다. 1 is a process chart showing a method for manufacturing a ceramic ball for toxic neutralization according to an embodiment of the present invention.
도 2는 본 발명에 따른 제조방법에 의해 제조된 세라믹 볼을 이용하여 악취농도에 대한 세라믹볼 투입 경과시간에 따른 중화농도를 측정한 시험예 1 내지 시험예 5를 설명하기 위한 그래프이다.FIG. 2 is a graph illustrating Test Examples 1 to 5 in which neutralization concentrations were measured according to the elapsed time of ceramic ball input to odor concentration using the ceramic balls manufactured by the manufacturing method according to the present invention.
본 발명은 음식물 쓰레기 처리시 발생하는 독성물을 중화하는 세라믹볼 제조방법에 관한 것으로, 더욱 상세하게는 음식물 쓰레기처리의 배출공정에서 발생하는 독성산화물 또는 휘발성 독성물과 이에 함유된 악취가스를 세라믹 볼 형태의 중화재를 건식 또는 습식방식의 음식물 쓰레기 처리장치내에서 사용하여 효율적으로 중화하기 위한 독성물 중화용 세라믹볼 제조방법에 관한 것이다. The present invention relates to a ceramic ball manufacturing method for neutralizing toxic substances generated during food waste treatment, and more particularly, to toxic oxides or volatile toxic substances generated in the discharge process of food waste treatment and odor gas contained therein. The present invention relates to a method for producing a ceramic ball for neutralizing toxic substances for efficiently neutralizing the neutralizing material in a dry or wet food waste disposal apparatus.
인간 실생활에서 음식물 쓰레기 등 환경유해물질로 인하여 일어나는 심각한 환경오염문제에 대처하기 위해 환경 관련 기업들은 친환경 제품이면서 유해물질을 함유하지 않은 물질을 제조하기 위하여 환경유해물질에서 유해한 독성성분을 제거하는 독성흡수재를 찾는 데 많은 연구 개발을 하고 있다. To deal with the serious environmental pollution problem caused by environmentally harmful substances such as food waste in human life, environmental companies are eco-friendly products that remove harmful toxic substances from environmentally harmful substances in order to manufacture environmentally friendly products that do not contain harmful substances. He is doing a lot of research and development.
그 연구 개발의 하나로서 일반적으로 사용되고 있는 독성 흡수방법을 예로 들면 독성가스와 물과,산성 또는 염기성 산화물들을 혼합하고 이때 생성된 환경유해물질을 제거하기 위해 음식물 쓰레기 처리시 쓰레기처리장치에 생성되는 음식물쓰레기의 앙금 또는 찌거기 때 등 더러운 슬래그(slag)를 수시로 청소하는 한편, 상기 독성가스와 산성 또는 염기성 산화물들을 포함한 환경유해물질을 교반조로 공급하고, 상기 공급된 환경유해물질과 물을 직접접촉시켜 교반조의 하부에 체류시켜 독성물은 분리하여 친환경 제품이 독성물로 되지 않도록 하는 독성흡수재를 사용한 독성흡수방법이 있다. As one of the research and development, for example, a toxic absorption method that is commonly used includes, for example, toxic gas, water, acidic or basic oxides mixed, and food generated in a garbage disposal device in order to remove environmentally harmful substances produced at this time. While dirty slag such as sediment or scum of garbage is frequently cleaned, the environmentally harmful substances including toxic gases and acidic or basic oxides are supplied to a stirring tank, and the environmentally harmful substances are directly contacted with water to stir. There is a toxic absorption method using a toxic absorbent which stays in the bottom of the tank to separate the toxic substances and prevent the eco-friendly products from becoming toxic.
이 독성흡수방법에 의해서 처리시 환경유해물질에 부수적으로 발생되는 환경에 유해한 독성물로는 아황산가스, 이산화 탄소, 일산화 탄소, 질소산화물 등의 독성가스와, 포름알데히드 및 기타 유기화합물이 있다.Toxic substances harmful to the environment which are incidental to environmentally harmful substances when treated by this toxic absorption method include toxic gases such as sulfurous acid gas, carbon dioxide, carbon monoxide and nitrogen oxides, formaldehyde and other organic compounds.
하지만 이 독성제거방법은 고가의 음식물 쓰레기 처리장치를 사용하여 음식물쓰레기의 슬래그 및 환경유해물질을 여전히 배출하고 있고 환경유해물질에서 일부 독성을 제거한다 하여도 계속해서 환경유해물질 자체 내에서 발생하는 독성가스를 충분히 제거하지 못하고 더구나 야외에 장기간 방치됨으로 인해 독성 가스를 발생하는 것을 막지 못하는 문제점이 있다.However, this method of detoxification still uses the expensive food waste treatment device, which still emits slag and environmentally harmful substances from food waste and removes some of the toxicity from environmentally harmful substances. There is a problem that can not prevent the generation of toxic gas due to not sufficiently remove the gas and further left for a long time in the outdoors.
상기와 같은 종래기술의 문제점을 해결하고자, 본 발명자는 수많은 연구와 실험을 거듭하고 그 결과에 근거하여, 음식물 쓰레기처리의 배출공정에서 발생하는 독성산화물 또는 휘발성 독성물과 이에 함유된 악취가스를 세라믹 볼 형태의 중화재를 건식 또는 습식방식의 음식물 쓰레기 처리장치내에서 사용하여 효율적으로 중화하기 위한 독성물 중화용 세라믹볼 제조방법을 제공하는 것을 목적으로 한다.In order to solve the problems of the prior art as described above, the inventors have repeated numerous studies and experiments, and based on the results, the toxic oxide or volatile toxic substances generated in the discharge process of food waste treatment and the odor gas contained therein are ceramics. It is an object of the present invention to provide a method for producing a ceramic ball for neutralizing toxic substances for efficiently neutralizing a ball-type neutralizing material in a dry or wet food waste disposal apparatus.
이에 본 발명은 음식물 쓰레기 배출공정에서 발생하는 인체에 유해한 독성물과 악취를 중화하기 위한 독성물 중화용 세라믹볼 제조방법에 있어서, In the present invention, in the method of manufacturing a ceramic ball for neutralizing toxic substances for neutralizing toxic substances and odors harmful to human body generated in the food waste discharge process,
(a)주로 운모와 고령토로 구성되며 소량의 구리를 함유한 광물질 85~90 Wt%과, 주로 쑥과 활성탄으로 구성되며 소량의 허브를 함유한 섬유성 물질 3~8 Wt%과, 다시마와 우뭇가사리를 함유한 해조류 3~8 Wt%를 주요성분으로 포함하는 혼합물을 3~4 시간 동안 혼합하고 졸(sol)상태로 숙성하는 공정, (b)상기 숙성된 혼합물을 3~5일간 교반조에서 교반하고 혼합물을 볼형상으로 정제하는 정제장치를 사용하여 5 ~ 15mm 크기의 다공성 개방형의 볼을 형성하는 공정, 및 (c)상기 다공성 개방형 볼을 4~5일간 건조한 후, 고온로에서 300 ~ 1500 ℃까지의 범위에서 열처리하여 상온에서 냉각시키는 공정을 포함한다. (a) 85 to 90 Wt% of minerals, mainly consisting of mica and kaolin, and 3 to 8 Wt% of fibrous material, mainly consisting of mugwort and activated carbon, containing small amounts of copper, and kelp and woodworm Mixing a mixture containing 3 ~ 8 Wt% of seaweed containing as a main component for 3 to 4 hours and aged in a sol state, (b) stirring the aged mixture in a stirring tank for 3-5 days And forming a porous open ball having a size of 5 to 15 mm using a refining apparatus for purifying the mixture into a ball shape, and (c) drying the porous open ball for 4 to 5 days, and then at 300 to 1500 ° C. in a high temperature furnace. It includes a step of cooling at room temperature by heat treatment in the range up to.
이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예를 제시하나, 하기 실시예는 본 발명을 예시하는 것일 뿐 본 발명의 범위가 하기 실시예에 한정되는 것은 아니다.Hereinafter, preferred examples are provided to help understanding of the present invention, but the following examples are merely to illustrate the present invention, and the scope of the present invention is not limited to the following examples.
도 1은 본 발명에 따른 일 실시예의 독성물 중화용 세라믹볼 제조방법을 나타낸 공정도이다. 도 2는 본 발명에 따른 제조방법에 의해 제조된 세라믹 볼을 이용하여 악취농도에 대한 세라믹볼 투입 경과시간에 따른 중화농도를 측정한 시험예 1 내지 시험예 5를 설명하기 위한 그래프이다.1 is a process chart showing a method for manufacturing a ceramic ball for toxic neutralization according to an embodiment of the present invention. FIG. 2 is a graph illustrating Test Examples 1 to 5 in which neutralization concentrations were measured according to elapsed time of ceramic ball input to malodor concentration using ceramic balls manufactured by the manufacturing method according to the present invention.
본 발명에 따른 독성물 중화용 세라믹볼 제조방법은 음식물 쓰레기 처리시 발생하는 환경유해물질과 이 환경유해물질에 함유된 독성가스를 중화하는 다공성 개방형의 세라믹 볼을 형성하기 위하여 광물질 85~90 Wt%를 주요성분으로 포함하고, 그 나머지는 섬유성 물질 3~8 Wt%과 해조류 3~8 Wt% 성분으로 하여 혼합한 혼합액을 혼합 내지 숙성하고, 개방형 볼을 형성하고, 열처리후 냉각시키는 공정을 포함한다.Ceramic ball manufacturing method for neutralizing toxic substances according to the present invention is 85 ~ 90 Wt% minerals to form a porous open ceramic ball to neutralize the environmentally harmful substances generated during the treatment of food waste and toxic gases contained in the environmentally harmful substances The main component, and the rest includes mixing and ripening the mixed solution mixed with 3 to 8 Wt% of the fibrous material and 3 to 8 Wt% of the algae, forming an open ball, and cooling after heat treatment. do.
본 발명의 세라믹 볼을 제조할 경우 우선 광물질 85~90 Wt%를 주요성분으로 포함하고, 그 나머지는 섬유성 물질 3~8 Wt%과 해조류 3~8 Wt% 성분으로 한다. 그러나 상기 광물질, 섬유성 물질 및 해조류의 주요성분이 80:5:5 (중량%)의 조성범위로 한정되는 것이 아니다.In the manufacture of the ceramic ball of the present invention, first, the minerals include 85 to 90 Wt% as a main component, and the rest are composed of 3 to 8 Wt% of fibrous material and 3 to 8 Wt% of algae. However, the main components of the mineral, fibrous material and seaweed are not limited to the composition range of 80: 5: 5 (% by weight).
본 발명의 단위 세라믹 볼은 환경유해물질을 마치 블랙홀(Blackhall)처럼 흡수하는 흡수하기위한 중화재로서 상기 세라믹 볼이 차지하는 광물질 85~90 Wt% 내에서, 상기 광물질로는 고령토를 83~88 Wt% 로 하고, 그 나머지를 견운모, 백운모, 흑운모를 갖는 운모3~8 Wt%와, 구리3~8 Wt%와 자수정 씨앗, 황토, 사장석, 맥반석, 티탄(Ti), 게르마늄(Ge) 및 제올라이트(Zeolite)로 선택하여 배합하지만 이에 한정되는 것이 아니다.The unit ceramic ball of the present invention is a neutralizing material for absorbing environmentally harmful substances as if it were a black hole, and within 85 to 90 Wt% of minerals occupied by the ceramic balls, 83 to 88 Wt% of kaolin is used as the mineral. The remainder is composed of mica, dolomite, biotite with mica 3-8 Wt%, copper 3-8 Wt% and amethyst seeds, ocher, plagioclase, elvan, titanium (Ti), germanium (Ge) and zeolite (Zeolite). ), But is not limited thereto.
구리는 악취 및 독성물에 함유된 곰팡이,세균, 미생물 등 각종 유기물로 인한 악취를 탈취한다. 또 티탄(Ti)은 세라믹 볼 형성시 숙성하는 공정중에 노출되는 주변의 자외선 조사, 또는 자외선 조사램프의 조사에 의하여 각종 유기물을 광분해하는 살균작용을 한다. 제올라이트(Zeolite)는 악취 및 독성물에 함유된 중금속 이온을 흡착하여 정화하는 작용을 한다. Copper deodorizes odors caused by various organic substances such as molds, bacteria and microorganisms contained in odors and toxic substances. In addition, titanium (Ti) has a sterilizing effect of photodegrading various organic substances by irradiation of surrounding ultraviolet rays or ultraviolet irradiation lamps exposed during the process of aging during the formation of ceramic balls. Zeolites act to adsorb and purify heavy metal ions contained in odors and toxic substances.
상기 섬유성 물질로는 본 발명의 단위 세라믹 볼에서 차지하는 섬유성 물질 3~8 Wt% 내에서, 허브를 대부분의 구성성분으로 포함하고 기타 쑥, 인정쑥, 오렌지 껍질, 헛개비 나무, 자작나무,국화, 허브, 향나무, 박하, 계피, 코코아, 커피, 녹차를 미량으로 배합하지만 이에 한정되는 것이 아니다.As the fibrous material, within 3 to 8 Wt% of the fibrous material occupied in the unit ceramic ball of the present invention, the herb is included as the most constituent, and other mugwort, mugwort, orange peel, barberry, birch, Chrysanthemum, herbs, juniper, peppermint, cinnamon, cocoa, coffee, green tea in a small amount, but is not limited thereto.
상기 해조류로는 다시마50중량%, 우뭇가사리50중량% 기타 곰피로 배합하지만 이에 한정되는 것이 아니다.As the seaweed, but not limited to 50% by weight kelp seaweed, 50% by weight butts and other gompi.
또한, 본 발명의 독성물 중화용 세라믹볼 제조방법은, 도 1에 예시된 바와 같이 상기 혼합 내지 숙성하는 공정(a)에서 혼합물은, 사전에 상기 광물질은 325 nm 크기의 입자로 분쇄되도록 분쇄하고, 섬유성 물질은 소나무, 자작나무 및 야자수를 활성탄으로 하여 고온에서 농축시켜 액체를 만들고, 해조류 물질은 압축하여 액체를 배출하도록 준비한다. 다시 말하면, 광물질은 325 nm 크기의 입자로 분쇄된 것을 준비하고, 섬유성 물질은 농축시켜 액체로 된 것을 준비하며, 해조류 물질은 압축하여 액체를 배출시킨 것을 준비한다.In addition, in the method of manufacturing a ceramic ball for neutralizing a toxic substance of the present invention, as illustrated in FIG. 1, in the mixing (aging) process (a), the mixture is pulverized so that the mineral is pulverized into particles having a size of 325 nm in advance. The fibrous material is made of pine, birch and palm trees as activated charcoal, concentrated at high temperature to make a liquid, and the algae material is compressed to prepare a liquid. In other words, the mineral material is prepared by pulverizing into particles of 325 nm size, the fibrous material is prepared by concentrating the liquid, and the algae material is prepared by compressing the liquid to be discharged.
또 상기 혼합 내지 숙성하는 공정(a)에서 형성된 혼합물은 3 ~ 5 일간 교반조에서 교반하여 그 크기에 따라 독성물을 흡수하는 속도의 차이가 있으므로, 혼합물을 볼형상으로 정제하는 정제장치를 사용하여 5 ~ 15 mm 크기의 다공성 개방형 볼을 형성(볼 형성 공정(b))하는 데, 이때 혼합물을 볼 형상으로 정제하는 정제장치의 하부에 다공성 개방형 볼을 적재한다. In addition, the mixture formed in the mixing (aging) step (a) is stirred in a stirring tank for 3 to 5 days, there is a difference in the rate of absorption of toxic substances depending on the size, using a purification apparatus for purifying the mixture into a ball shape A porous open ball having a size of 5 to 15 mm is formed (ball forming step (b)), wherein the porous open ball is loaded at the bottom of the refining apparatus for purifying the mixture into a ball shape.
또한 이 결과 교반조에 의해 교반되고 혼합물을 볼형상으로 정제하는 정제장치를 통해 정제된 상기 다공성 개방형 볼은 상기 열처리공정(c)을 통하여 상기 다공성 개방형 볼을 4~5일간 건조한 후, 고온로에서 300 ~ 1500 ℃ 까지의 범위에서 열처리하여 상온에서 냉각시킨다. As a result, the porous open ball, which was stirred by a stirring tank and purified through a refining apparatus for purifying the mixture into a ball shape, dried the porous open ball for 4 to 5 days through the heat treatment step (c), and then dried in a high temperature furnace. Heat treatment in the range of ~ 1500 ℃ to cool at room temperature.
이에 따라, 본 발명은 도 1에 예시된 바와 같이 상기 혼합 내지 숙성하는 공정(a), 상기 개방형 볼을 형성하는 공정(b) 및 상기 열처리공정(c)을 거쳐 다공성 개방형 볼이 세라믹 볼로서 완성된다. Accordingly, the present invention is a porous open ball is completed as a ceramic ball through the step of mixing or maturing (a), the step of forming the open ball (b) and the heat treatment step (c) as illustrated in FIG. do.
이와 같이 완성된 세라믹 볼은 가정용의 건식 방법을 사용하거나 또는 산업용의 습식방법을 사용하는 어떤 방식의 음식물 쓰레기 배출장치도 적용되어서 독성물에 함유된 독성분과 강한 악취를 현저하게 중화시킬 수 있다. The finished ceramic ball can be applied to any type of food waste discharging device using a dry method for home use or an industrial wet method, which can significantly neutralize toxic substances and strong odor contained in the toxic material.
또한 본 발명의 독성물 중화용 세라믹볼 제조방법은 다공성 개방형의 세라믹 볼에 의하여 독성분과 강한 악취를 중화하기 때문에 최종적으로 잔류하는 독성물과 악취 가스는 세라믹 볼과 반응하여 제거되며 이는 다음 시험예로 확인된다.In addition, the method of manufacturing the ceramic ball for neutralizing toxic substances of the present invention neutralizes toxic components and strong odors by the porous open ceramic ball, and finally, the remaining toxic substances and odor gases are removed by reacting with the ceramic balls. It is confirmed.
<시험예><Test Example>
이하 본 발명의 시험예를 상세하게 설명한다.Hereinafter, the test example of the present invention will be described in detail.
본 발명의 시험예는, 다공성 개방형으로 형성하는 세라믹 볼을 제조하기 위해 광물질 85~90 Wt%를 주요성분으로 포함하고, 그 나머지는 섬유성 물질 3~8 Wt%과 해조류 3~8 Wt% 를 각각 부분성분으로 하고, 상기 혼합 내지 숙성하는 공정(a), 상기 다공성 개방형의 볼을 형성하는 공정(b) 및 상기 열처리공정(c)을 사용하여 아래 표 1에 나타낸 바와 같이 실험결과를 얻었다. In the test example of the present invention, in order to produce a ceramic ball formed in a porous open type, it contains 85 to 90 Wt% of minerals as main components, and the rest is 3 to 8 Wt% of fibrous materials and 3 to 8 Wt% of seaweeds. Experimental results were obtained as shown in Table 1 below by using the respective components as a partial component, the step of mixing or maturing (a), the step of forming the porous open ball (b) and the heat treatment step (c).
표 1은 반응용기내의 온도를 20 ℃ 로 일정하게 유지한 경우에 악취 및 및 독성물의 원인이 되는 물질에서 배출되는 가스 가운데 악취가 발생하는 황화수소(HS)를 함유한 표준시료 1000 g 을 반응용기에 주입하고 세라믹 볼 100 g 을 혼합하고, 상기 악취와 세라믹볼을 반응시킨 가스를 반응시간 10 ~ 150분(min) 후 악취 분석기를 이용하여 악취 농도에 따른 세라믹 볼의 중화율을 측정하고, 일정시간 경과한 후 황화수소를 중화하는 중화효율을 농도(ppm)으로 나타낸 결과이다. Table 1 shows 1000 g of a standard sample containing hydrogen sulfide (HS) that emits odor among gases emitted from substances causing odors and toxic substances when the temperature in the reaction vessel is kept constant at 20 ° C. Inject and mix 100 g of ceramic balls, and after the
도 2는 본 발명에 따른 제조방법에 의해 제조된 세라믹 볼을 이용한 악취농도에 대한 세라믹볼 투입 경과시간에 따른 중화농도를 측정한 시험예 1 내지 시험예 5를 설명하기 위한 그래프이다.FIG. 2 is a graph illustrating Test Examples 1 to 5, in which neutralization concentrations were measured according to elapsed time of ceramic ball input to odor concentration using ceramic balls manufactured by the manufacturing method according to the present invention.
도 2에 나타낸 바와 같이, 100 g의 세라믹 볼을 투입하고 반응용기내의 온도를 20 ℃ 로 일정하게 유지한 경우에는 본 발명에 따라 시험예 1은 악취 및 및 독성물의 원인이 되는 물질에서 배출되는 가스 가운데 황화수소(HS)와 세라믹 볼100 g이 반응 후 10분이 경과한 후 황화수소 80.2 ppm 를 제거하는 중화효율을 나타냈으며, 시험예 2는 반응 후 30분이 경과한 후 세라믹 볼에 의해 중화된 농도가 390.3 ppm, 시험예 3은 반응 후 60분이 경과한 후 세라믹 볼에 의해 중화된 농도가 694.6 ppm, 시험예 4는 반응 후 120분이 경과한 후 세라믹 볼에 의해 중화된 농도가 1097.3 ppm, 시험예 5는 반응 후 150분이 경과한 후 세라믹 볼에 의해 중화된 농도가 1098.4 ppm의 황화수소의 중화효율을 나타내었다.As shown in FIG. 2, when 100 g of ceramic balls were added and the temperature in the reaction vessel was kept constant at 20 ° C., according to the present invention, Test Example 1 was a gas discharged from a substance causing odor and toxic substances. In the middle, hydrogen sulfide (HS) and 100 g of ceramic balls showed a neutralizing efficiency of removing 80.2 ppm of hydrogen sulfide after 10 minutes after the reaction.In Test Example 2, the concentration neutralized by the ceramic balls after 30 minutes after the reaction was 390.3. ppm, Test Example 3 was 694.6 ppm neutralized by ceramic balls after 60 minutes after the reaction, Test Example 4 was 1097.3 ppm neutralized by the ceramic balls after 120 minutes after the reaction, Test Example 5 After 150 minutes after the reaction, the concentration neutralized by the ceramic ball showed a neutralization efficiency of hydrogen sulfide of 1098.4 ppm.
여기에서 본 발명에 따라 광물질 85~90 Wt%: 섬유성 물질 3~8 Wt%: 해조류 3~8 Wt% 의 성분비로 가하여 혼합한 반응시킨 시험예 1 내지 3의 경우 표준시료 100g 에 대해 세라믹 볼 100g 을 단독으로 투입하여 사용한 경우 중화된 농도가 지속적으로 중화됨을 확인할 수 있었다. 또한 도 2에서의 시험예 1~5로부터 시험예 1 내지 3보다 시험예 4 내지 5에서의 세라믹 볼의 투입시간의 증가에 의한 황화수소의 중화효율이 더욱 우수하게 나타나고, 악취 및 독성물이 현저하게 중화되어 감소하는 경향을 나타냄을 알 수 있다.According to the present invention, in the case of Test Examples 1 to 3, which were mixed and added in a component ratio of minerals 85 to 90 Wt%: fibrous materials 3 to 8 Wt%: seaweeds 3 to 8 Wt%, ceramic balls were used for 100 g of standard sample. When 100g was used alone, it was confirmed that the neutralized concentration was continuously neutralized. In addition, the neutralization efficiency of hydrogen sulfide due to the increase in the ceramic ball input time in Test Examples 4 to 5 from Test Examples 1 to 3 in Test Examples 1 to 5 is more excellent, and odors and toxic substances are remarkable. It can be seen that it tends to be neutralized and decrease.
즉 본 발명의 시험예 1~5 의 독성물 중화용 세라믹볼 제조방법은 음식물 쓰레기 처리시 다공성 개방형의 세라믹 볼에 의하여 악취 및 독성물을 중화시키는 중화 효율이 우수하게 나타남을 확인할 수 있었다.That is, the ceramic ball manufacturing method for neutralizing toxic substances in Test Examples 1 to 5 of the present invention showed that the neutralizing efficiency of neutralizing odors and toxic substances by the porous open ceramic ball during food waste treatment was excellent.
나아가 이와 같이 완성된 세라믹 볼은 가정용의 건식 방법을 사용하거나 또는 산업용의 습식방법을 사용하는 어떤 방식의 음식물 쓰레기 배출장치도 적용되어서 독성물에 함유된 독성분과 강한 악취를 현저하게 중화시킬 수 있다. Furthermore, the finished ceramic ball may be applied to any food waste discharging device using a dry method for home use or a wet method for industrial use to significantly neutralize toxic substances and odors contained in toxic substances.
이상에서 본 발명의 기재된 실시예에 대해서만 상세히 설명되었지만, 본 발명의 기술사상 범위 내에서 다양한 변형 및 수정이 가능함은 당업자에게 있어서 명백한 것이며, 이러한 변형 및 수정이 첨부된 특허청구범위에 속함은 당연한 것이다. Although only described in detail with respect to the described embodiments of the present invention, it will be apparent to those skilled in the art that various modifications and variations are possible within the technical spirit of the present invention, it is natural that such variations and modifications belong to the appended claims. .
본 발명의 독성물 중화용 세라믹볼 제조방법에 따르면 환경유해물질의 처리의 배출공정에서 발생하는 독성산화물 또는 휘발성 독성물과 이에 함유된 악취가스를 세라믹 볼 형태의 중화재를 건식 또는 습식방식의 음식물 쓰레기 처리장치내에서 사용하여 효율적으로 중화함으로써 독성물과 악취의 배출을 방지하고, 더욱이 작업자들의 작업환경을 개선할 수 있는 효과가 있다.According to the method of manufacturing a ceramic ball for neutralizing toxic substances according to the present invention, the toxic oxides or volatile toxic substances generated in the process of discharging environmentally harmful substances and the odorous gas contained therein are used in a dry or wet type food or beverage of the neutralizer in the form of ceramic balls. By effectively neutralizing by using in the waste disposal apparatus, it is possible to prevent the emission of toxic substances and odors, and further improve the working environment of workers.
Claims (1)