KR100881680B1 - Heat insulation material for agricultural and horticultural facility - Google Patents
Heat insulation material for agricultural and horticultural facility Download PDFInfo
- Publication number
- KR100881680B1 KR100881680B1 KR20057002783A KR20057002783A KR100881680B1 KR 100881680 B1 KR100881680 B1 KR 100881680B1 KR 20057002783 A KR20057002783 A KR 20057002783A KR 20057002783 A KR20057002783 A KR 20057002783A KR 100881680 B1 KR100881680 B1 KR 100881680B1
- Authority
- KR
- South Korea
- Prior art keywords
- heat insulation
- resin
- wavelength
- filler
- transmittance
- Prior art date
Abstract
본 발명의 농원예 시설용 단열 자재는, 미립자형상의 단열 필러가 분산된 수지기재로 이루어지는 단열층을 구비한 단열 자재이며, 단열 필러가 6붕화 란탄 및 안티몬 첨가 산화 주석에서 선택된 적어도 1종이다. 이 농원예 시설용 단열 자재는, 단열성의 지표로서의 일사투과율이 10∼80%이며, 가시광 투과율은 30∼90%로서, 자외선 영역에서의 광투과율은 파장 320㎚에서 5∼80% 및 파장 290㎚에서 0∼70%이다.
농원예 시설, 단열 자재, 미립자형상, 단열 필러, 란탄, 안티몬, 산화주석.
The heat insulating material for agricultural and horticultural facilities of this invention is a heat insulating material provided with the heat insulation layer which consists of a resin base material in which particulate heat insulation filler was disperse | distributed, and a heat insulation filler is at least 1 sort (s) chosen from lanthanum hexaboride and antimony addition tin oxide. The heat-transmitting material for agricultural and horticultural facilities has a solar radiation transmittance of 10 to 80%, a visible light transmittance of 30 to 90%, and a light transmittance in the ultraviolet region of 5 to 80% at a wavelength of 320 nm and a wavelength of 290 nm. 0 to 70%.
Agricultural horticulture facilities, thermal insulation materials, particulate form, thermal insulation filler, lanthanum, antimony, tin oxide.
Description
본 발명은, 농원예용 하우스의 지붕이나 외벽재 등에 이용되는 필름형상 또는 보드형상의 자재에 관한 것으로, 특히, 단열 효과를 가지는 농원예 시설용 단열 자재에 관한 것이다.BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a film-like or board-shaped material used for a roof or an outer wall material of a farm horticultural house, and more particularly, to a heat insulating material for agrohorticultural facilities having a heat insulating effect.
종래, 농업용이나 원예용의 하우스를 비롯한 농원예 시설에는, 지붕이나 외벽재 등으로서 일반적으로 수지 필름이나 수지판이 사용되고 있다. 그 대표적인 재질로서는, 염화비닐수지, 폴리에틸렌수지, 폴리에스테르수지, 불소수지 등이 일반적으로 사용되고, 최근에는 내후성이나 자외선 영역의 광투과성 등이 우수한 불소수지도 주목받고 있다.Background Art Conventionally, a resin film or a resin plate is generally used for a farming and gardening facility including a house for farming and horticulture as a roof or an exterior wall material. As the representative material, vinyl chloride resin, polyethylene resin, polyester resin, fluorine resin, and the like are generally used, and recently, fluorine resin having excellent weather resistance and light transmittance in the ultraviolet region is also attracting attention.
이들 농원예 시설의 지붕이나 외벽재 등에 이용되는 자재는, 그 대부분이 보온을 목적으로 해서 설계된 것이다. 그러나, 보온의 목적은 외기의 차단에 의해 거의 달성되는 한편, 동계 이외에 있어서는 시설 내의 온도가 지나치게 높아지는 것을 피하기 위해서, 지붕이나 외벽재의 일부를 개폐해서 온도조절을 행할 필요가 있었다.Most of the materials used for roofing or exterior wall materials of these farming and gardening facilities are designed for thermal insulation purposes. However, while the purpose of thermal insulation was almost achieved by blocking the outside air, it was necessary to open and close a part of the roof and the exterior wall material to control the temperature in order to avoid excessively high temperatures in the facility except in winter.
그 때문에, 농원예 시설의 지붕이나 외벽재 등에 사용되는 자재로서, 농원예 종사자로부터는 단열성을 구비한 자재의 요구가 높아지고 있지만, 이것을 고려한 필름형상 또는 보드형상의 자재는 거의 제공되고 있지 않은 현재 상태이다.Therefore, as a material used for a roof or an outer wall material of a farm gardening facility, the demand of the material with heat insulation is increasing from the farmer or horticultural worker, but the film- or board-like material which considered this is the present state which is hardly provided. .
그런데, 일본국 특개평9-330612호 공보에는, 0A기기용의 부재로서, 근적외선 흡수 능력을 가지는 색소를 수지에 첨가해서 단열 특성을 주는 제안이 되고 있다. 또, 일본국 특개평6-118228호 공보에는, 광학필터로서, 동이온을 함유시킨 단열 수지가 제안되고 있다.By the way, Japanese Unexamined Patent Application Publication No. 9-330612 proposes to provide a heat insulating property by adding a pigment having near infrared absorption capability to a resin as a member for 0A devices. In addition, Japanese Patent Laid-Open No. 6-118228 discloses a heat insulating resin containing copper ions as an optical filter.
그러나, 상기 공보에 제안된 색소나 동은 내후성이 낮고 자외선이나 열 등에 의한 열화가 일어나기 쉽기 때문에, 수지에 포함시켜 단열용 자재로서 사용했을 경우, 옥외에 장기간 폭로되면 빠른 시기에 단열 효과가 열화한다는 결점이 있다. 또, 색소의 경우는 블리딩이 발생하기 쉽기 때문에, 수지표면이 백화하여 광투과성이 극단적으로 저하한다는 결점도 있다. 따라서, 색소나 동이온을 포함하는 수지 필름 등은, 특히 농원예 시설용 자재로서 장기간의 사용은 곤란하였다.However, since the pigments and copper proposed in the above publications have low weather resistance and are susceptible to deterioration due to ultraviolet rays or heat, when used as a heat insulating material in a resin, the thermal insulation effect deteriorates quickly when exposed to the outdoors for a long time. There is a flaw. Moreover, in the case of a pigment | dye, since bleeding is easy to generate | occur | produce, there exists also a fault that the resin surface whitens and the light transmittance extremely falls. Therefore, the resin film containing a pigment | dye and a copper ion etc. was difficult especially long-term use as a material for agricultural horticultural facilities.
본 발명은, 이러한 종래의 사정을 감안하여, 농원예용 하우스의 지붕이나 외벽재 등에 이용되는 필름형상 또는 보드형상의 자재로서, 내후성이 우수한 동시에, 가시광을 투과해서 필요한 밝기를 유지하면서, 근적외광을 효율적으로 차폐함으로써 단열성을 구비한 농원예 시설용 단열 자재를 제공하는 것을 목적으로 한다.In view of such a conventional situation, the present invention is a film- or board-shaped material used for a roof or an outer wall material of a farm horticultural house, which is excellent in weatherability, and transmits near-infrared light efficiently while maintaining visible brightness by transmitting visible light. It aims at providing the heat insulating material for agricultural and horticultural facilities provided with heat insulation by shielding by the shielding.
즉, 본 발명에 관한 농원예 시설용 단열 자재는, 미립자형상의 단열 필러가 분산된 수지기재로 이루어지는 단열층을 구비하고, 이 단열 필러가 6붕화 란탄 및 안티몬 첨가 산화 주석으로부터 선택된 적어도 1종인 것을 특징으로 한다.That is, the heat insulating material for agricultural and horticultural facilities which concerns on this invention is equipped with the heat insulation layer which consists of a resin base material in which the particulate heat insulation filler was disperse | distributed, and this heat insulation filler is at least 1 sort (s) chosen from lanthanum hexafluoride and antimony addition tin oxide, It is characterized by the above-mentioned. do.
그리고, 본 발명에 관한 농원예 시설용 단열 자재는, 가시광 투과율이 30∼90%로서, 일사투과율이 10∼80%인 것이 바람직하고, 또한, 자외선 영역에 있어서의 파장 320㎚의 광투과율이 5∼80%, 및 파장 290㎚의 광투과율이 0∼70%인 것이 바람직하다.And the heat insulating material for agricultural and horticultural facilities which concerns on this invention is 30 to 90% of visible light transmittance, and it is preferable that the solar radiation transmittance is 10 to 80%, and the light transmittance of wavelength 320nm in an ultraviolet region is 5--5. It is preferable that the light transmittance of 80% and wavelength 290nm is 0 to 70%.
또, 본 발명에 관한 농원예 시설용 단열 자재에 있어서는, 상기 단열층에 있어서의 단열 필러의 함유량이, 6붕화 란탄에서는 0.01∼1g/㎡, 안티몬 첨가 산화 주석에서는 1.0∼50g/㎡인 것이 바람직하다. 또, 상기 단열층의 수지기재는 불소계 수지 또는 폴리에틸렌테레프탈레이트수지인 것이 바람직하다.Moreover, in the heat insulating material for agricultural / horticultural facilities which concerns on this invention, it is preferable that content of the heat insulation filler in the said heat insulation layer is 0.01-1 g / m <2> in lanthanum hexaboride, and 1.0-50 g / m <2> in antimony addition tin oxide. Moreover, it is preferable that the resin base material of the said heat insulation layer is a fluororesin or polyethylene terephthalate resin.
또한, 본 발명에 관한 농원예 시설용 단열 자재의 구체적 형태로서는, 상기 단열층만으로 이루어지는 단일의 필름형상 또는 보드형상이든지, 혹은 상기 단열층이 필름형상 또는 보드형상의 모재표면상에 적층되고 또는 2장의 모재간에 협지되어 있는 형태를 들 수 있다.Moreover, as a specific form of the heat insulation material for agricultural and horticultural facilities which concerns on this invention, it is a single film form or board shape which consists only of the said heat insulation layer, or the said heat insulation layer is laminated | stacked on the film form or board-shaped base material surface, or between two base materials. It may be in the form of a pinch.
여기에서, 본 발명에 있어서 상기한 각 광투과율의 값은, 건축창 글래스용 필름에 관한 JIS A 5759(1998)(광원:A광)에 의거하여 측정하고, 산출한 것이다. 다만, 측정용 시료는 글래스에 첨부하지 않고, 필름형상 또는 보드형상의 것을 그대로 사용하였다. 또, 일사투과율은 350∼2100㎚의 파장역의 빛에 대한 투과율이며, 본 발명에 있어서 농원예 시설용 단열 자재의 태양광선에 대한 단열성을 평가하는 지표로서 사용하였다. 또한, 가시광 투과율은 380∼780㎚의 파장역의 빛에 대한 투과율이며, 인간의 눈에 대한 밝기를 평가하는 지표로서 사용하였다.Here, in the present invention, the value of each light transmittance described above is measured and calculated based on JIS A 5759 (1998) (light source: A light) relating to the film for building window glass. In addition, the sample for a measurement did not adhere to glass, and the film form or board form was used as it is. In addition, the solar radiation transmittance is a transmittance | permeability with respect to the light of the wavelength range of 350-2100 nm, and was used as an index which evaluates the heat insulation with respect to the sunlight of the heat insulating material for agricultural and horticultural facilities in this invention. In addition, visible light transmittance is the transmittance | permeability with respect to the light of the wavelength range of 380-780 nm, and was used as an index which evaluates the brightness with respect to a human eye.
도 1은, LaB6 미립자 분산막의 투과 스펙트럼(1㎡당 미립자 중량이 상이한 2종류의 분산막이 도시되어 있고 상측의 프로필이 미립자 중량이 적은 투과 스펙트럼이다)을 도시한 그래프도이다.1 is a graph showing the transmission spectrum of two LaB 6 fine particle dispersion films (two types of dispersion films having different particle weights per m 2 are shown, and the upper profile is a transmission spectrum having a small particle weight).
도 2는, ATO 미립자 분산막의 투과 스펙트럼(1㎡당 미립자 중량이 상이한 2종류의 분산막이 도시되어 있고 상측의 프로필이 미립자 중량이 적은 투과 스펙트럼이다)을 도시한 그래프도이다.FIG. 2 is a graph showing the transmission spectrum of the ATO fine particle dispersion film (two types of dispersion films having different particle weights per m 2 are shown, and the upper profile is a transmission spectrum having a small particle weight).
(발명을 실시하기 위한 최선의 형태)(The best mode for carrying out the invention)
이하, 본 발명을 더욱 구체적으로 설명한다.Hereinafter, the present invention will be described in more detail.
우선, 본 발명에 관한 농원예 시설용 단열 자재는, 농원예용 하우스의 지붕이나 외벽재 등으로서 사용되는 필름형상이나 보드형상(판자형상)으로서, 미립자형상의 단열 필러를 분산시킨 수지기재로 이루어지는 단열층을 구비하고 있다. 특히, 단열 필러로서, 근적외광을 효율적으로 흡수하고, 우수한 단열성을 부여할 수 있는 6붕화 란탄(LaB6) 또는 안티몬 첨가 산화 주석(SnO2+Sb2O5=이하, ATO로 약기한다) 중 어느 1종을 이용하든지 또는 2종을 병용한다.First, the heat insulating material for agricultural horticultural facilities which concerns on this invention is a film shape or board shape (plate shape) used as a roof, exterior wall material, etc. of a farm horticultural house, and is equipped with the heat insulation layer which consists of a resin base material which disperse | distributed the fine thermal insulation filler. Doing. In particular, as a heat insulation filler, in lanthanum hexaboride (LaB 6 ) or antimony-added tin oxide (SnO 2 + Sb 2 O 5 = hereinafter abbreviated as ATO) which can absorb near infrared light efficiently and impart excellent heat insulation. Either one or two are used in combination.
농원예 시설용 단열 자재에 있어서는, 단열의 대상은 태양광선의 열 에너지이다. 지표에 도달하는 태양광선은 일반적으로 약 290∼2100㎚의 파장역이라고 말해지고, 이 중 약 380∼780㎚의 가시광 파장영역의 빛은 시설 내의 밝기를 유지하고, 식물의 육성에 필요한 빛이다. 따라서, 태양광선의 단열에 있어서는, 약 780 ∼2100㎚의 근적외광을 선택적으로 효율적으로 흡수함으로써, 단열성에 기여하는 재료를 선택하는 것이 바람직하다.In the heat insulating material for agricultural horticultural facilities, the object of heat insulation is heat energy of sunlight. The sunlight reaching the earth is generally said to be in the wavelength range of about 290 to 2100 nm, of which light in the visible wavelength range of about 380 to 780 nm is the light necessary for maintaining the brightness in the facility and for plant growth. Therefore, in heat insulation of sunlight, it is preferable to select the material which contributes to heat insulation by selectively and efficiently absorbing near-infrared light of about 780-2100 nm.
또, 자외선 영역의 빛에 대해서는, 재배하는 식물에 의해 또는 수분(受粉)에 이용하는 곤충의 종류 등에 의해 최적인 조건이 있지만, 일반적으로 290∼320㎚의 파장역을 제어하는 것이 요구된다. 즉, 이 파장역의 적당량의 자외선을 차폐함으로써 해충이나 병에 의한 해를 억제하는 효과가 있기 때문이다. 종래 사용되고 있는 농업용 필름은 자외선을 어느 정도 차폐하는 것이 많고, 그 조건에서 품종개량된 식물은 자외선을 많이 필요로 하지 않는다. 다만, 대부분의 자외선을 차폐해 버리면, 꿀벌 등에 의한 곤충을 이용한 수분이 활발하게 행하여지지 않거나, 식물의 육성에 악영향을 주거나 하는 경우가 있어 바람직하지 못하다.Moreover, about the light of an ultraviolet-ray region, although there exist optimal conditions by the plant to grow or the kind of insect used for water, etc., it is generally required to control the wavelength range of 290-320 nm. That is, it is because there exists an effect which suppresses the damage by a pest or a disease by shielding the ultraviolet-ray of the appropriate amount of this wavelength range. Agricultural films that are conventionally used to a certain extent to shield the ultraviolet rays, plants that are improved varieties under the conditions do not require much ultraviolet rays. However, if most of the ultraviolet rays are shielded, it is not preferable because moisture using insects by bees or the like may not be actively performed or adversely affect the growth of plants.
LaB6 미립자 분산막의 투과 스펙트럼은, 도 1에 도시한 바와 같이, 가시광역의 빛의 투과가 크고, 파장 550㎚부근에 투과의 피크를 가진다. 이 투과 피크는 사람의 눈의 감도가 가장 큰 파장과 일치하기 때문에, 시설 내의 밝기를 유지하는데에 유리하다. 또한, 파장 1000㎚부근에 큰 흡수가 있기 때문에, 근적외광을 효율적으로 흡수하고, 태양광선의 열 에너지를 효율적으로 단열할 수 있다. 또, LaB6에 의한 자외선흡수는 적고, 따라서 곤충에 의한 수분 활동이나 식물의 생육에 악영향을 주는 경우는 없다. 또한, 파장 290∼320㎚의 자외선의 투과성은, 수지기재 중으로의 LaB6 미립자의 첨가량을 조정함으로써 제어하는 것이 가능하다.As shown in FIG. 1, the transmission spectrum of the LaB 6 fine particle dispersion film has a large transmission of visible light and a peak of transmission near the wavelength of 550 nm. This transmission peak is advantageous for maintaining the brightness in the facility because the sensitivity of the human eye matches the wavelength of the largest. In addition, since there is a large absorption near the wavelength of 1000 nm, near-infrared light can be efficiently absorbed and heat energy of sunlight can be efficiently insulated. In addition, UV absorption by LaB 6 is small, and therefore, does not adversely affect the water activity and the growth of plants by insects. In addition, the transmittance of ultraviolet rays having a wavelength of 290 to 320 nm can be controlled by adjusting the amount of LaB 6 fine particles added to the resin substrate.
또한 자외선 영역의 투과율에 대해서 제어가 필요할 경우에는, 자외선 차폐 용의 무기재료, 유기재료, 유기무기 복합재료, 예를 들면, 산화세륨, 산화티탄, 산화지르코늄, 산화아연, 벤조페논계 자외선 흡수제 등을 목적에 맞춰 첨가하면 된다. 또, 상기 무기재료계 자외선 흡수재는, 자외선을 흡수했을 때 표면에 전자와 홀이 발생하고, 이것이 원인으로 수지기재를 열화시킬 가능성이 있기 때문에, 그 표면이 피막 처리되어 있는 것이 바람직하다. 표면 피막 처리로서는, 각종 커플링제, 표면개질제, 졸겔 실리케이트 등이 대표적이지만, 수지의 열화를 방지하는 효과를 얻을 수 있으면 방법은 상관없다.When control is required for the transmittance in the ultraviolet region, inorganic materials for ultraviolet shielding, organic materials, organic inorganic composite materials, such as cerium oxide, titanium oxide, zirconium oxide, zinc oxide, benzophenone ultraviolet absorbers, etc. It may be added according to the purpose. In addition, the inorganic material ultraviolet absorber may have electrons and holes on its surface when it absorbs ultraviolet rays, which may cause deterioration of the resin base material. Therefore, the surface of the inorganic material ultraviolet absorber is preferably coated. As the surface coating treatment, various coupling agents, surface modifiers, sol-gel silicates and the like are typical, but the method may be used as long as the effect of preventing the deterioration of the resin can be obtained.
이렇게, LaB6 미립자를 단열 필러로 하는 본 발명의 단열 자재는, 태양광선의 근적외선 영역을 효율적으로 흡수함으로써 단열 특성이 있고, 동시에 파장 550㎚부근을 중심으로 가시광 영역의 투과 특성이 양호하기 때문에, 시설 내의 밝기를 충분히 유지할 수 있다. 더군다나, 바람직하게 파장 320㎚이하의 자외선을 투과하는 특징이 있고, 이것에 의해 수분에 기여하는 꿀벌 등이 활발하게 활동할 수 있고, 안정된 수확을 기대할 수 있다.In this way, the heat insulating material of the present invention in which the LaB 6 fine particles as heat-insulating filler, since by absorbing the near infrared range of the solar rays efficiently to good transmission characteristics in the visible region and the heat insulating properties, at the same time around the wavelength of 550㎚, Sufficient brightness can be maintained in the facility. Furthermore, preferably, ultraviolet rays having a wavelength of 320 nm or less are transmitted, whereby bees and the like contributing to moisture can be actively active, and stable harvesting can be expected.
또, ATO 미립자 분산막의 투과 스펙트럼을 도 2에 도시한다. 도 2로부터 알 수있듯이, 파장 380∼780㎚의 가시광역에 있어서 크고 또한 평탄한 투과 프로필을 나타내고, 가시광역의 흡수가 거의 없기 때문에 시설 내를 밝게 유지할 수 있는데다, 동시에 파장 800㎚이상의 근적외 영역에 흡수를 가지기 때문에 높은 단열 효과를 얻을 수 있다. 또, 파장 290∼320㎚의 자외선 영역에 있어서의 투과도 얻을 수 있기 때문에, 꿀벌 등의 수분에도 악영향이 거의 없다.The transmission spectrum of the ATO fine particle dispersion film is shown in FIG. 2. As can be seen from Fig. 2, it exhibits a large and flat transmission profile in the visible region having a wavelength of 380 to 780 nm, and can keep the inside of the facility bright because there is little absorption of the visible region. Since it has an absorption, a high thermal insulation effect can be obtained. In addition, since transmission in the ultraviolet region having a wavelength of 290 to 320 nm can be obtained, there is almost no adverse effect on moisture such as honey bees.
또한, 이 ATO에 있어서도, 자외선 영역의 투과율을 제어하기 위해서, 자외선 차폐용의 무기재료, 유기재료, 유기무기 복합재료를 첨가할 수 있는 것, 및 무기재료계 자외선 흡수재에 관해서는 수지기재의 열화 방지를 위한 표면 피막 처리가 바람직한 것은, 상기 LaB6의 경우와 동일하다.Also in this ATO, in order to control the transmittance in the ultraviolet region, an inorganic material, an organic material, an organic inorganic composite material for ultraviolet shielding can be added, and an inorganic material ultraviolet absorber deteriorates the resin base material. It has a surface coating treatment for prevention is desired, the same as that of the LaB 6.
이렇게, ATO 미립자를 단열 필러로 하는 본 발명의 단열 자재는, 가시광 영역이며 무색 투명하기 때문에 시설 내의 밝기를 충분히 유지할 수 있고, 근적외선 영역의 흡수 또는 흡수에 의해 높은 단열 효과를 가지는 동시에, 자외선 영역의 투과도 겸비하고 있다.Thus, since the heat insulating material of this invention which uses ATO microparticles as a heat insulation filler is visible light region and colorless and transparent, the brightness | luminance in a facility can fully be maintained, and it has a high heat insulation effect by absorption or absorption of a near-infrared region, It also has a transmission.
또, 단열 필러로서 LaB6과 ATO를 병용하는 것도 가능하며, 이 때 더욱 유효한 단열 특성을 가지는 단열 자재를 얻을 수 있다. 즉, 도 1 및 도 2에 도시한 대로, LaB6은 파장 1000㎚부근에 큰 흡수를 가지고, 한편 ATO는 800㎚이상의 파장에서 서서히 흡수가 증가한다. 따라서, 양방의 미립자를 수지기재 중에 분산시킴으로써, 어느 편방만을 이용할 경우와 비교해서 근적외역의 흡수 또는 흡수가 한층 크게 또한 효율적으로 되어, 더욱 높은 단열 특성을 얻을 수 있다.In addition, it is also possible to combined use of LaB 6 and ATO as an insulating filler and, at this time, it is possible to obtain a heat insulating material having a more effective heat insulating properties. That is, as shown in Figs. 1 and 2, LaB 6 has a large absorption near the wavelength of 1000 nm, while ATO gradually increases the absorption at a wavelength of 800 nm or more. Therefore, by dispersing both fine particles in the resin base material, the absorption or absorption of the near-infrared region is much more and more efficient as compared with the case of using only one side, and higher heat insulating properties can be obtained.
따라서, LaB6 및/또는 ATO미립자를 단열 필러로 하는 본 발명의 농원예 시설용 단열 자재는, 바람직한 밝기를 유지하기 위한 가시광역의 투과성, 높은 단열 효과를 주는 근적외역의 흡수성, 및 자외역의 투과성의 3특성을 동시에 겸비하고, 하우스 등의 농원예 시설의 지붕이나 외벽재 등으로서 지극히 유용하다. 더군다나, 이들 단열 필러는 무기재료이기 때문에, 유기계 재료와 비교해서 높은 내후성을 얻 을 수 있고, 보통 옥외에서 사용되는 농원예 시설용 단열 자재로서 특히 우수하다.Therefore, LaB 6 and / or ATO plantations eg facilities heat insulating material of the present invention that the particulate heat-insulating filler, the permeability of the visible light region to maintain the desired brightness of the near-infrared range absorbent giving a high heat insulating effect, and the ultraviolet region permeability It combines three characteristics at the same time, and is extremely useful as a roof or exterior wall material of agricultural and horticultural facilities such as houses. Moreover, since these insulating fillers are inorganic materials, they can achieve high weather resistance compared to organic materials, and are particularly excellent as insulating materials for agricultural horticultural facilities which are usually used outdoors.
이러한 본 발명의 농원예 시설용 단열 자재에서는, 광학적으로 가시광역의 투과성과 근적외역의 흡수성의 밸런스가 좋은 것이 중요하다. 즉, 가시광 투과율은 30∼90%인 것이 바람직하고, 60∼90%인 것이 더욱 바람직하다. 동시에, 일사투과율은 10∼80%인 것이 바람직하고, 10∼70%인 것이 더욱 바람직하다. 또, 자외선 영역의 광투과율에 대해서는, 파장 320㎚의 광투과율이 5∼80%인 것이 바람직하고, 파장 290㎚의 광투과율이 0∼70%인 것이 바람직하다.In the heat insulating material for agricultural and horticultural facilities of this invention, it is important that optically the balance of the transmittance | permeability of visible region and the absorbance of near-infrared region is important. That is, it is preferable that visible light transmittance is 30 to 90%, and it is more preferable that it is 60 to 90%. At the same time, the solar radiation transmittance is preferably 10 to 80%, more preferably 10 to 70%. Moreover, about the light transmittance of an ultraviolet-ray region, it is preferable that the light transmittance of wavelength 320nm is 5 to 80%, and it is preferable that the light transmittance of wavelength 290nm is 0 to 70%.
상기한 미립자형상의 단열 필러의 입자지름(응집 입자도 포함한다)은, 산란 효과를 이용할 것인가 아닌가에 의해 적당하게 선택할 수 있다. 예를 들면, 단열층의 수지기재 중에 분산시킨 단열 필러의 입자지름이 200㎚이하, 특히 100㎚이하의 경우는, 태양광선의 산란이 극히 작아지고, 태양광선은 식물이나 지면에 직접 도달하게 된다. 또한, 가시광 영역의 빛도 거의 산란되지 않기 때문에, 하우스 등의 시설 내의 상황을 외부에서 관찰하는 것이 용이하고, 시설내에서 외부상황을 확인할 수도 있다.The particle diameter (including agglomerated particles) of the above-described particulate particulate insulating filler can be appropriately selected depending on whether or not a scattering effect is used. For example, when the particle diameter of the heat insulation filler dispersed in the resin base material of a heat insulation layer is 200 nm or less, especially 100 nm or less, scattering of sunlight becomes extremely small, and the sunlight reaches a plant or the ground directly. In addition, since light in the visible region is hardly scattered, it is easy to observe the situation in the facility such as a house from the outside, and the external situation can be confirmed in the facility.
한편, 단열층 중에 분산된 미립자의 입자지름이 200㎚을 넘으면, 태양광선의 산란이 크고, 시설내의 식물 및 지면에 도달하는 빛은 균일해지고, 하우스의 골조 등의 그림자가 식물에 주는 영향이 적어진다. 그러나, 동시에 가시광 영역의 빛도 산란되기 때문에, 시설 내를 필요한 밝기로 유지할 수 있어도, 시설 내의 상황을 외부에서 선명하게 관찰하는 것은 어렵게 된다.On the other hand, when the particle diameter of the fine particles dispersed in the heat insulation layer exceeds 200 nm, the scattering of sunlight is large, the light reaching the plants and the ground in the facility becomes uniform, and the influence of shadows such as the framing of the house on the plants is reduced. . However, since light in the visible region is also scattered at the same time, it is difficult to clearly observe the situation in the facility from the outside even if the inside of the facility can be maintained at the required brightness.
LaB6 및 ATO의 입자지름을 제어하는 방법은 각종 있지만, 입자지름을 작게 할 경우에는, 매체 교반밀, 초음파처리, 충돌 분쇄, pH 제어 등의 방법이 있고, 이들의 방법을 습식법 또는 건식법 등 용도에 맞춰서 선택할 수 있다. 특히, 입자지름 200㎚이하의 미립자의 분산을 행할 경우에는, 각종 커플링제, 분산제, 계면활성제를 사용하면 안정된 상태로 분산시킬 수 있고, 처리 후의 분산입자도 안정되게 유지할 수 있다.There are various methods for controlling the particle diameter of LaB 6 and ATO. However, when the particle diameter is reduced, there are methods such as medium stirring mill, sonication, impingement pulverization, pH control, etc., and these methods are used in wet or dry methods. You can choose according to. In particular, in the case of dispersing fine particles having a particle diameter of 200 nm or less, various coupling agents, dispersants, and surfactants can be used to disperse in a stable state, and the dispersed particles after treatment can also be stably maintained.
LaB6 및/또는 ATO의 미립자를 분산시킨 수지기재의 단열층을 포함하는 본 발명의 농원예 시설용 단열 자재는, 종래부터 농업용 하우스 등에 지붕이나 외벽재로서 사용되고 있는 형태, 즉 필름형상 또는 보드형상(판자 형상)이다. 일반적으로는 단열층만으로 이루어지는 단일의 필름형상 또는 보드형상이지만, 별도제작된 수지나 글래스 등으로 이루어지는 투명한 필름형상 또는 보드형상의 모재표면상 또는 2장의 모재간에, 적어도 1층의 단열층을 적층 또는 협지한 구조의 것이라도 좋다.LaB 6 and / or farm of the invention comprising a thermal insulation layer of the resin base material obtained by dispersing fine particles of ATO facilities heat insulating material is, the form which is used as a roof or oebyeokjae like agricultural house conventionally, that is, film-shaped or board-shaped (plank-like )to be. Generally, it is a single film or board shape composed of only a heat insulating layer, but at least one heat insulating layer is laminated or sandwiched on a transparent film or board-like base material surface made of a resin, glass, or the like produced separately or between two substrates. It may be of structure.
이러한 각종 형태를 가지는 농원예 시설용 단열 자재에 있어서, 그 단열층의 형성은, 단열 필러인 LaB6 및/또는 ATO미립자를 수지에 혼련하여 넣고, 이것을 성형함으로써 행할 수 있다. 수지에 혼련하여 넣을 경우, 필요에 따라 상기 방법으로 미립자의 입자지름을 제어하는 것이 가능하다. 또, LaB6 및 ATO의 미립자는 열적으로도 안정적이기 때문에, 수지의 융점부근의 온도(200∼300℃전후)에서 혼련하는 것이 가능하다.In the example farm facilities heat insulating materials having such various forms, the formation of the heat insulating layer is placed by mixing the insulating filler of LaB 6 and / or ATO fine particles in the resin, molding can be carried out by this. When kneaded in the resin, it is possible to control the particle diameter of the fine particles by the above method as necessary. Moreover, since the fine particles of LaB 6 and ATO are thermally stable, they can be kneaded at a temperature near the melting point of the resin (around 200 to 300 ° C).
LaB6 및/또는 ATO미립자를 혼련한 수지는, 펠렛화한 후, 예를 들면, 압출성형법, 임프레션 성형법, 용액 유연(流延)법 등에 의해, 필름형상 또는 보드형상으로 성형한다. 또한, 이 때의 필름 또는 보드의 두께는, 사용 목적에 따라 적당하게 설정할 수 있지만, 일반적으로 필름의 경우는 10∼1000㎛, 바람직하게는 20∼500㎛의 범위, 보드의 경우에는 2∼15㎜의 범위로 하는 것이 바람직하다. 또, 수지 중에 혼련하는 LaB6 및/또는 ATO 미립자의 양은, 혼련 및 성형 시의 조작성 등을 고려하면 일반적으로 수지에 대하여 50중량％이하가 바람직하다.The resin kneaded with LaB 6 and / or ATO fine particles is pelletized and then molded into a film or board shape by, for example, extrusion molding, impression molding, solution casting, or the like. In addition, although the thickness of the film or board at this time can be set suitably according to a use purpose, generally, in the case of a film, it is 10-1000 micrometers, Preferably it is the range of 20-500 micrometers, and in the case of board, 2-15 It is preferable to set it as the range of mm. The amount of LaB 6 and / or ATO fine particles to be kneaded in the resin is generally preferably 50% by weight or less with respect to the resin in consideration of the operability during kneading and molding.
단열층 중에 균일하게 분산된 단열 필러의 함유량은, 목적으로 하는 광학 특성 및 단열 특성에 따라 임의로 바꿀 수 있다. 예를 들면, LaB6은 단위 중량에 있어서의 단열 효율이 높기 때문에, 단열층 1㎡당의 함유량이 0.01g이상에서 유효한 단열 효과를 얻을 수 있다. 또, 1g/㎡에서는 약 90%의 태양광선의 열 에너지를 흡수하는 것이 가능해서, 여름 철의 단열에는 충분한 효과를 얻을 수 있고, 동계의 보온 효과를 고려하면 이 이상의 첨가는 바람직하지 않다. 따라서, LaB6의 함유량은 0.01∼1g/㎡의 범위로 하는 것이 바람직하다.Content of the heat insulation filler uniformly disperse | distributed in a heat insulation layer can be changed arbitrarily according to the optical characteristic and heat insulation characteristic made into the objective. For example, LaB 6 is due to the high heat insulating efficiency of the unit weight and a sugar content 1㎡ heat insulating layer to obtain a valid insulation from above 0.01g. Moreover, at 1 g / m <2>, it is possible to absorb about 90% of the thermal energy of sunlight, and sufficient effect can be acquired for heat insulation of summer season, and considering this heat insulation effect, this addition is not preferable. Therefore, the content of LaB 6 is preferably in a range of 0.01~1g / ㎡.
또, 단열 필러가 ATO의 경우에는, 단열층의 1㎡당 약 3g의 함유량에서, 30%정도의 태양광선의 열 에너지를 흡수하는 것이 가능하다. 일반적으로는, 1.0ｇ/㎡미만에서는 단열 효과가 충분하지 않고, 또 50g/㎡를 넘으면 코스트가 높아지고, 또한 단열용 자재로의 가공이 곤란해지기 때문에 바람직하지 못하다. 따라서, ATO의 함유량은 1.0∼50g/㎡의 범위인 것이 바람직하다.Moreover, when a heat insulation filler is ATO, it is possible to absorb about 30% of the heat energy of the sunlight with content of about 3 g per 1 m <2> of a heat insulation layer. Generally, less than 1.0 g / m <2> is not preferable because a heat insulation effect is not enough, and when it exceeds 50 g / m <2>, cost will become high and processing into a heat insulating material will become difficult. Therefore, it is preferable that content of ATO is the range of 1.0-50 g / m <2>.
또한, 상기 단열 필러의 함유량에 대해서는, 단열층 내에 포함되는 모든 단열 필러가 단열층에 입사하는 광선에 대하여 대략 동등하게 작용하기 때문에, 단열층의 두께를 고려하지 않고 단열층 1㎡당의 필러 함유량으로 평가할 수 있다.In addition, about content of the said heat insulation filler, since all the heat insulation fillers contained in a heat insulation layer act | work substantially equally to the light ray which injects into a heat insulation layer, it can evaluate by the filler content per 1 m <2> of heat insulation layers, without considering the thickness of a heat insulation layer.
단열층의 매트릭스가 되는 수지는, 특별히 한정되는 것은 아니고, 용도에 맞춰서 선택가능하다. 예를 들면, 종래부터 하우스 등에 사용되고 있는 폴리에틸렌수지, 폴리에스테르수지, 연질 염화비닐수지 이외, 저코스트이며, 투명성이 높고, 범용성이 넓은 수지로서, 폴리에틸렌테레프탈레이트(PET)수지, 아크릴수지, 폴리아미드수지, 염화비닐수지, 폴리카보네이트수지, 올레핀수지, 에폭시수지, 폴리이미드수지 등을 들 수 있다. 특히 PET수지는 자외선 영역의 투과성에 특징이 있고, 파장 320㎚부근은 투과하지만, 파장 290㎚부근은 거의 투과하지 않으므로, 자외선 영역의 투과율을 제어하는데에 바람직한 수지재료이다.Resin used as a matrix of a heat insulation layer is not specifically limited, It can select according to a use. For example, in addition to polyethylene resins, polyester resins, and soft vinyl chloride resins conventionally used for houses, low cost, high transparency, and wide versatility, polyethylene terephthalate (PET) resins, acrylic resins, polyamides, etc. Resins, vinyl chloride resins, polycarbonate resins, olefin resins, epoxy resins, polyimide resins, and the like. In particular, PET resin is characterized by transmittance in the ultraviolet region, and transmits near the wavelength of 320 nm, but hardly transmits near the wavelength of 290 nm, which is a preferable resin material for controlling the transmittance in the ultraviolet region.
또, 내후성이나 자외선 투과성 등을 고려하면, 불소계 수지가 유효하다. 여기에서 불소계 수지란, 분자구조 중에 불소를 함유하는 수지면 좋고, 예를 들면, 4불화에틸렌수지, 3불화에틸렌수지, 2불화에틸렌수지, 1불화에틸렌수지 등을 들 수 있고, 이들의 혼합물이라도 상관없다.In addition, in consideration of weather resistance, ultraviolet ray permeability and the like, a fluorine resin is effective. Here, the fluorine-based resin may be a resin containing fluorine in its molecular structure, and examples thereof include tetrafluoroethylene resin, trifluoroethylene resin, difluoroethylene resin, monofluoroethylene resin, and the like. none.
더욱 구체적으로는, 폴리테트라플루오르에틸렌(PTFE), 테트라플루오르에틸렌-퍼-플루오르알킬비닐에테르공중합체(PFA), 테트라플루오르에틸렌-헥사플루오르프로필렌공중합체(FEP), 테트라플루오르에틸렌-헥사플루오르프로필렌-퍼-플루오르알킬비닐에테르공중합체(EPE), 테트라플루오르에틸렌-에틸렌공중합체(ETEF), 폴리클로로트리플루오르에틸렌(CPTFE), 클로로트리플루오르에틸렌-에틸렌공중합체 (ECTFE), 폴리비닐리덴플루오라이드(PVDF), 폴리비닐플루오라이드(PVF) 등을 들 수 있다. 이들의 불소계수지, 및 그 각종 변성품 또는 복합품 등은 각종 시판되고 있고, 필요로 하는 특성에 따라 선택 사용하는 것이 가능하다.More specifically, polytetrafluoroethylene (PTFE), tetrafluoroethylene-per-fluoroalkyl vinyl ether copolymer (PFA), tetrafluoroethylene-hexafluoropropylene copolymer (FEP), tetrafluoroethylene-hexafluoropropylene- Per-fluoroalkyl vinyl ether copolymer (EPE), tetrafluoroethylene-ethylene copolymer (ETEF), polychlorotrifluoroethylene (CPTFE), chlorotrifluoroethylene-ethylene copolymer (ECTFE), polyvinylidene fluoride ( PVDF), polyvinyl fluoride (PVF), etc. are mentioned. These fluorine resins and various modified products or composite products thereof are commercially available and can be selectively used depending on the required properties.
또, 상기한 적층구조의 농원예 시설용 단열 자재의 경우, 예를 들면 LaB6 및/또는 ATO 미립자를 포함하는 단열층을, 기존의 수지제 필름이나 보드 또는 글래스판 등으로 이루어지는 모재의 편방 또는 양방의 표면상에, 코팅해서 제조할 수 있다. 코팅 방법은, 모재표면에 균일한 도막을 형성할 수 있으면 되고, 예를 들면 바 코트법, 그라비아 코트법, 스프레이 코트법, 딥 코트법 등을 이용할 수 있다.In the case of farms of the above-described laminated structure example facilities heat insulating material, for a example LaB 6 and / or pyeonbang or both of the base metal the heat insulating layer, made of a conventional resin-made film or board or a glass plate or the like containing the ATO fine particles On the surface, it can manufacture by coating. The coating method only needs to be able to form a uniform coating film on the surface of the base material, and for example, a bar coating method, a gravure coating method, a spray coating method, a dip coating method or the like can be used.
상기 코팅법에 의해 단열층을 형성할 경우, 미립자를 유지하는 수지 또는 바인더로서 자외선 경화 수지를 이용하는 것이 바람직하다. 즉, 자외선 경화 수지와 적당한 입자지름의 단열 필러를 혼합해서 액상 내지 페이스트 형상으로 하고, 모재 표면에 코팅하고, 용제를 증발시킨 후, 자외선을 조사해서 경화시키는 것이 가능하다. 또한, 자외선 경화 수지로서 하드 코트성의 수지를 사용하면, 표면 내마모 강도가 높은 단열층을 얻을 수 있고, 모래 먼지 등이 충돌해도 상처가 생기기 어려운 표면 특성을 부여할 수 있다. 이 때, SiO2 등을 주성분으로 하는 무기 결합제나, SiO2 미립자 등을 첨가함으로써, 또한, 마모 강도를 향상시킬 수 있다.When forming a heat insulation layer by the said coating method, it is preferable to use an ultraviolet curable resin as a resin or binder which hold | maintains microparticles | fine-particles. That is, it is possible to mix an ultraviolet curable resin and a heat insulating filler having an appropriate particle diameter to form a liquid or paste shape, to coat the surface of the base material, to evaporate the solvent, and to irradiate and cure ultraviolet rays. Moreover, when hard-coat resin is used as an ultraviolet curable resin, the heat insulation layer with high surface abrasion resistance can be obtained, and even if sand dust etc. collide, the surface property which is hard to produce a wound can be provided. At this time, by adding an inorganic binding agent or, SiO 2 fine particles consisting primarily of SiO 2, etc., Further, it is possible to improve the abrasion resistance.
또, 상기와 같이 단열층을 코팅할 경우에는, 미리 모재 표면을 처리해서 단열층과의 밀착력을 향상시키는 것이 바람직하다. 이 표면처리에 의해, 동시에 모재 표면의 젖음성이 개선되어서 코팅 시의 튀김을 방지하고, 균일한 코팅을 얻는 것이 용이하게 된다. 특히 불소계수지로 이루어지는 모재에는 표면처리를 실시하는 것이 바람직하다. 표면처리 방법으로서는, 코로나 처리, 스퍼터 처리, 프라이머 코팅 처리 등이 잘 알려져 있다.Moreover, when coating a heat insulation layer as mentioned above, it is preferable to process a base material surface beforehand, and to improve adhesive force with a heat insulation layer. By this surface treatment, the wettability of the surface of the base material is simultaneously improved to prevent splashing during coating and to obtain a uniform coating easily. It is preferable to surface-treat especially the base material which consists of fluororesins. As the surface treatment method, corona treatment, sputter treatment, primer coating treatment and the like are well known.
또한, 단열층이 코트된 모재의 상기 단열층 위에 다른 모재를 임의의 수법으로 적층해서 단열층을 협지하거나, 필름형상 또는 보드형상으로 미리 형성된 단열층을 임의의 수법으로 2장의 모재에 의해 협지시켜서 농원예 시설용 단열 자재를 형성할 수 있다. 이 경우, 단열 필러의 미립자를 유지하는 수지 또는 바인더로서 수지 필름 라미네이트용 수지, 예를 들면 염화비닐코폴리머 등을 이용할 수도 있다.In addition, another base material is laminated on the heat insulating layer of the base material coated with the heat insulating layer by any technique to sandwich the heat insulating layer, or the heat insulating layer previously formed in a film or board shape is sandwiched by two base materials by any method to insulate agrohorticultural facilities. Can form materials. In this case, resin for resin film lamination, for example, vinyl chloride copolymer, etc. can also be used as resin or binder which hold | maintains microparticles | fine-particles of a heat insulation filler.
또한, 단열 필러의 미립자를 상온 경화성의 수지와 혼합함으로써 기존의 농원예용 시설의 지붕이나 외벽재의 표면에 코팅하고, 후에 단열 특성을 부여하는 것도 가능하다.Moreover, it is also possible to mix the microparticles | fine-particles of a heat insulation filler with the resin of normal temperature hardening, and to coat the surface of the roof or exterior wall material of an existing agricultural and horticultural facility, and to provide heat insulation characteristic later.
이렇게, 목적 및 용도에 따라 수지기재를 선정함으로써, 단열 특성을 모재에 부여하는 것이 가능하다.Thus, by selecting the resin base material according to the purpose and use, it is possible to give heat insulation characteristics to a base material.
이하, 본 발명의 실시예에 대해서 구체적으로 설명한다.EMBODIMENT OF THE INVENTION Hereinafter, the Example of this invention is described concretely.
[실시예1]Example 1
LaB6 미립자(비표면적 30㎡/g) 20중량부, 톨루엔 75중량부, 분산제 5중량부를 혼합하고, 분산 처리를 해서 평균 분산입자 지름 80㎚의 분산액(A)을 얻었다. 이 분산액(A)으로 진공건조기를 이용하여 50℃로 용제성분을 제거하고, 분산 처리 한 LaB6의 분말(A)이라고 하였다. 또한, 평균 분산입자 지름은, 동적 광산란법을 이용한 측정 장치(오츠카덴시 가부시키가이샤(제):ELS-800)에 의해 측정하고, 그 평균치로 하였다.20 parts by weight of LaB 6 fine particles (specific surface area 30 m 2 / g), 75 parts by weight of toluene, and 5 parts by weight of a dispersant were mixed and dispersed to obtain a dispersion (A) having an average dispersed particle diameter of 80 nm. Using a vacuum drier with a dispersion (A) removing a solvent component in 50 ℃, which was that the powder (A) of a distributed processing LaB 6. In addition, the average dispersed particle diameter was measured with the measuring apparatus (Otsuka Denshi Co., Ltd. make: ELS-800) using the dynamic light scattering method, and made it the average value.
이 LaB6의 분말(A) 0.01㎏과, ETFE(테트라플루오르에틸렌-에틸렌공중합체)수지 8.7㎏을, V 블렌더로 건식 혼합하였다. 그 후, ETFE수지의 용융 온도 부근인 320℃에서 충분히 밀폐 혼합하고, 그 혼합물을 320℃로 압출성형하고, 두께 약 50㎛의 필름을 형성하였다. 이 필름 중의 LaB6 미립자의 함유량은 0.13g/㎡에 상당한다.0.01 kg of the powder (A) of LaB 6 and 8.7 kg of ETFE (tetrafluoroethylene-ethylene copolymer) resin were dry mixed in a V blender. Thereafter, the mixture was hermetically sealed at 320 ° C. near the melting temperature of the ETFE resin, and the mixture was extruded at 320 ° C. to form a film having a thickness of about 50 μm. The content of LaB 6 fine particles in this film corresponds to 0.13 g / m 2.
얻어진 필름형상의 단열 자재에 대해서, JIS A 5759(1998)(광원:A광)에 준거해서 광학측정을 행하고, 가시광 투과율, 일사투과율, 및 자외선 영역에서의 광투과율을 구하였다. 다만, 측정용 시료는 글래스에 첨부하지 않고, 필름 그대로를 사용하였다. 또, 투명성을 평가하기 위해서, JIS K 7105에 근거하여 헤이즈 값을 측정하였다. 헤이즈 값이 낮을수록, 투명도가 높다.About the obtained film-form heat insulating material, optical measurement was performed based on JISA 5759 (1998) (light source: A light), and the visible light transmittance, the solar radiation transmittance, and the light transmittance in an ultraviolet range were calculated | required. However, the sample for a measurement did not adhere to glass and used the film as it was. Moreover, in order to evaluate transparency, haze value was measured based on JISK7105. The lower the haze value, the higher the transparency.
그 결과, 상기 필름형상 단열 자재의 가시광 투과율은 70% 및 일사투과율은 50%이며, 가시광 영역의 빛을 충분히 투과하는 동시에, 태양광선의 직접 입사광을 50% 차폐할 수 있어, 높은 단열 효과를 가지는 것을 알 수 있었다. 또, 자외선 영역의 투과율은, 파장 290㎚에서 18% 및 320㎚에서 26%이며, 꿀벌 등이 충분히 활발하게 수분을 행할 수 있는 범위였다. 또한, 헤이즈 값은 4.2%로, 내부의 상황을 외부에서도 충분히 확인할 수 있는 높은 투명성을 가지고 있다.As a result, the visible light transmittance of the film-shaped heat insulating material is 70% and the solar radiation transmittance is 50%, while sufficiently transmitting the light in the visible light region, and can shield 50% of the direct incident light of the sunlight, has a high thermal insulation effect I could see that. Moreover, the transmittance | permeability of the ultraviolet-ray area | region was 18% at wavelength 290 nm, and 26% at 320 nm, and was a range in which honeybees etc. can fully actively moisturize. Moreover, haze value is 4.2% and has high transparency which can fully confirm the internal situation from the outside.
[비교예1]Comparative Example 1
실시예1에 있어서, 단열 필러의 LaB6 미립자를 첨가하지 않고, ETFE수지를 압출성형하고, 두께 약 50㎛의 필름을 형성하였다. 얻어진 필름의 가시광 투과율은 89%로 가시광 영역의 빛을 충분히 투과하고 있지만, 일사투과율도 89%이며, 태양광선의 직접 입사광을 약 11%밖에 차폐할 수 없어, 단열 효과가 낮은 것을 알 수 있었다. 또한, 자외선 영역의 투과율은 파장 290㎚에서 82% 및 320㎚에서 88%이며, 또 헤이즈 값은 4.0%이었다.In Example 1, ETFE resin was extruded without the addition of LaB 6 fine particles of the thermal insulation filler to form a film having a thickness of about 50 μm. Although the visible light transmittance of the obtained film was 89% and fully permeate | transmitted the light of visible region, it was 89% of solar radiation transmittance, and it was understood that only about 11% of the direct incident light of sunlight can be shielded, and the heat insulation effect is low. Moreover, the transmittance | permeability of the ultraviolet range was 82% at wavelength 290 nm, and 88% at 320 nm, and haze value was 4.0%.
[실시예2]Example 2
실시예1에 있어서의 LaB6의 분말(A) 0.005㎏과, ETFE수지 8.7㎏을, V 블렌더로 건식 혼합하였다. 그 후, 실시예1과 마찬가지로, ETFE수지의 용융 온도 부근인 320℃에서 충분하게 밀폐 혼합을 행하고, 그 혼합물을 320℃로 압출성형하고, 두께 약 50㎛의 필름을 형성하였다. 이 필름 중의 LaB6 미립자의 함유량은 0.05g/㎡에 상당한다.0.005 kg of the powder (A) of LaB 6 in Example 1 and 8.7 kg of the ETFE resin were dry mixed with a V blender. Thereafter, similarly to Example 1, airtight mixing was sufficiently performed at 320 ° C near the melting temperature of the ETFE resin, and the mixture was extruded at 320 ° C to form a film having a thickness of about 50 µm. The content of the LaB 6 fine particles in the film are equivalent to 0.05g / ㎡.
얻어진 필름형상의 단열 자재를 실시예1과 마찬가지로 평가한 바, 가시광 투과율은 80% 및 일사투과율은 65%이며, 가시광 영역의 빛을 충분히 투과하는 동시에, 태양광선의 직접 입사광을 약 35% 차폐할 수 있어, 높은 단열 효과를 가지는 것을 알 수 있었다. 자외선 영역의 투과율은, 파장 290㎚에서 34% 및 320㎚에서 43%이며, 꿀벌 등이 충분히 활발하게 수분을 행할 수 있는 범위였다. 또한, 헤이즈 값은 4.1%이며, 투명성이 높고, 내부의 상황을 외부에서도 충분히 확인할 수 있 다.The obtained film-shaped heat insulating material was evaluated in the same manner as in Example 1, and the visible light transmittance was 80% and the solar transmittance was 65%, while sufficiently transmitting light in the visible region and shielding about 35% of the direct incident light of the sunlight. It was able to know that it had a high heat insulation effect. The transmittance | permeability of an ultraviolet-ray area | region was 34% at wavelength 290 nm, and 43% at 320 nm, and it was a range in which honeybees etc. can carry out water actively enough. In addition, the haze value is 4.1%, high transparency, the internal situation can be sufficiently confirmed from the outside.
[실시예3]Example 3
실시예2에 있어서, ETFE수지 대신에 PET(폴리에틸렌테레프탈레이트)수지를 이용하고, 가열온도를 PET수지가 충분히 연화되는 온도(약 300℃)로 한 것 이외는, 실시예2와 같은 방법으로 필름을 제작하였다. 이 필름 중의 LaB6 미립자의 함유량은 실시예2와 같이 0.05g/㎡에 상당하다.In Example 2, a film was prepared in the same manner as in Example 2 except that PET (polyethylene terephthalate) resin was used in place of ETFE resin and the heating temperature was set to a temperature at which the PET resin was sufficiently softened (about 300 ° C). Was produced. The content of the LaB 6 fine particles in the film are equivalent to 0.05g / ㎡ as in Example 2.
얻어진 필름형상의 단열 자재를 실시예1과 마찬가지로 평가한 바, 가시광 투과율은 79% 및 일사투과율은 65%이며, 가시광 영역의 빛을 충분히 투과하는 동시에, 태양광선의 직접 입사광을 약 35% 차폐하고 있어, 높은 단열 효과를 가지는 것을 알 수 있었다. 또, 자외선 영역의 투과율은, 파장 290㎚에서 0% 및 320㎚에서 35%이며, 290㎚에서의 투과율이 0%인 것은 수지기재인 PET수지의 영향이다. 또한, 헤이즈 값은 2.5%이며, 투명성이 매우 높은 것을 알 수 있다.The obtained film-shaped heat insulating material was evaluated in the same manner as in Example 1, and the visible light transmittance was 79% and the solar transmittance was 65%, while sufficiently transmitting the light in the visible light region and shielding about 35% of the direct incident light of the sunlight. It turned out that it has a high heat insulation effect. The transmittance in the ultraviolet region is 0% at wavelength 290 nm and 35% at 320 nm, and 0% transmittance at 290 nm is influenced by PET resin, which is a resin substrate. In addition, the haze value is 2.5% and it turns out that transparency is very high.
[비교예2]Comparative Example 2
실시예3에 있어서, 단열 필러의 LaB6 미립자를 첨가하지 않고, PET수지를 압출성형하고, 두께 약 50㎛의 필름을 형성하였다. 얻어진 필름의 가시광 투과율은 88%로 가시광 영역의 빛을 충분히 투과하고 있지만, 일사투과율도 88%이며, 태양광선의 직접 입사광을 약 12%밖에 차폐할 수 없어, 단열 효과가 낮은 것을 알 수 있다. 또, 자외선 영역의 투과율은, 파장 290㎚에서 0% 및 320㎚에서 52%이며, 헤이즈 값은 1.0%이었다.In Example 3, without the addition of LaB 6 fine particles of a heat-insulating filler, and extrusion molding the PET resin to form a film having a thickness of about 50㎛. Although the visible light transmittance of the obtained film is 88% and fully permeate | transmits the light of a visible light region, it is 88% of solar radiation transmittance, and it can be seen that only about 12% of the direct incident light of sunlight can be shielded, and a heat insulation effect is low. Moreover, the transmittance | permeability of the ultraviolet-ray area | region was 0% at wavelength 290 nm, and 52% at 320 nm, and haze value was 1.0%.
[실시예4]Example 4
ATO 미립자(비표면적 50㎡/g) 20중량부, 톨루엔 75중량부, 분산제 5중량부를 혼합하고, 분산 처리를 해서 평균 분산입자 지름 75㎚의 분산액(B)을 얻었다. 이 분산액(B)으로 진공건조기를 이용하여 50℃에서 용제성분을 제거하고, 분산 처리한 ATO의 분말(B)이라고 하였다.20 weight part of ATO microparticles | fine-particles (specific surface area 50m <2> / g), 75 weight part of toluene, and 5 weight part of dispersing agents were mixed, and the dispersion process was performed and the dispersion liquid (B) of 75 nm of average particle diameters was obtained. This dispersion liquid (B) was used as a vacuum (dryer) to remove the solvent component at 50 ° C, and was referred to as ATO powder (B).
이 ATO의 분말(B) 0.4㎏과, ETFE수지 8.65㎏을 V 블렌더로 건식 혼합한 후, ETFE수지의 용융 온도인 320℃에서 충분히 밀폐 혼합을 행하고, 이 혼합물을 320℃로 압출성형하여, 두께 약 50㎛의 필름을 형성하였다. 이 필름 중의 ATO미립자의 함유량은 4.5g/㎡에 상당하다.0.4 kg of the powder (B) of this ATO and 8.65 kg of the ETFE resin were dry mixed with a V blender, and then hermetically mixed at 320 ° C., which is the melting temperature of the ETFE resin, sufficiently mixed, and the mixture was extruded at 320 ° C. to have a thickness. A film of about 50 μm was formed. The content of ATO fine particles in this film is equivalent to 4.5 g / m 2.
얻어진 필름형상의 단열 자재를 실시예1과 마찬가지로 평가한 바, 가시광 투과율은 79% 및 일사투과율은 63%이며, 가시광 영역의 빛을 충분히 투과하고 있는 동시에, 태양광선의 직접 입사광을 약 37% 차폐할 수 있어, 높은 단열 효과를 가지고 있는 것을 알 수 있다. 또, 자외선 영역의 투과율은, 파장 290㎚에서 3.4% 및 320㎚에서 30.0%이며, 꿀벌 등의 수분이 충분히 활발하게 행할 수 있는 것을 알 수 있다. 또한, 헤이즈 값은 4.5%이며, 내부의 상황을 외부에서도 충분히 확인할 수 있는 투명성을 가지고 있다.The obtained film-shaped heat insulating material was evaluated in the same manner as in Example 1, and the visible light transmittance was 79% and the solar transmittance was 63%, while sufficiently transmitting the light in the visible light region and shielding about 37% of the direct incident light of the sunlight. It can be seen that it has a high thermal insulation effect. Moreover, the transmittance | permeability of an ultraviolet-ray region is 3.4% at wavelength 290 nm, and 30.0% at 320 nm, and it turns out that moisture, such as a bee, can fully actively carry out. Moreover, haze value is 4.5% and it has transparency which can fully confirm the situation inside.
[실시예5]Example 5
실시예4의 ATO의 분말(B) 0.2㎏과, ETFE수지 8.65㎏을 V블렌더로 건식 혼합하였다. 그 후, EFTE수지의 용융 온도인 320℃부근에서 충분하게 밀폐 혼합을 행하고, 그 혼합물을 320℃로 압출성형해서 두께 약 50㎛의 필름으로 형성하였다. 이 필름의 ATO 미립자의 함유량은 2.0ｇ/㎡에 상당하다.0.2 kg of powder (B) of ATO of Example 4 and 8.65 kg of ETFE resin were dry mixed with a V blender. Thereafter, airtight mixing was sufficiently performed at around 320 ° C., which is the melting temperature of the EFTE resin, and the mixture was extruded at 320 ° C. to form a film having a thickness of about 50 μm. Content of the ATO microparticles | fine-particles of this film is equivalent to 2.0 g / m <2>.
얻어진 필름형상의 단열 자재를 실시예1과 마찬가지로 평가한 바, 가시광 투과율은 84% 및 일사투과율은 73%이며, 가시광 영역의 빛을 충분히 투과하고 있는 동시에, 태양광선의 직접 입사광을 약 27% 차폐하고 있어, 높은 단열 효과를 가지는 것을 알 수 있다. 또, 자외선 영역의 투과율은, 파장 290㎚에서 15% 및 320㎚에서 49%이며, 꿀벌 등이 충분히 활발하게 수분을 행하는 것이 가능한 범위이다. 또한, 헤이즈 값은 4.2%이며, 투명성이 높고, 내부의 상황을 외부에서도 충분히 확인할 수 있다.The obtained film-shaped heat insulating material was evaluated in the same manner as in Example 1, and the visible light transmittance was 84% and the solar transmittance was 73%, while sufficiently transmitting the light in the visible light region and shielding about 27% of the direct incident light of the sunlight. It turns out that it has a high heat insulation effect. Moreover, the transmittance | permeability of an ultraviolet-ray area | region is 15% at wavelength 290 nm, and 49% at 320 nm, and it is a range in which a bee etc. can sufficiently actively moisture. Moreover, haze value is 4.2%, transparency is high, and the internal situation can fully be confirmed externally.
[실시예6]Example 6
실시예1에 있어서의 LaB6 미립자의 분산액(A) 10중량부를, 하드 코트용 자외선 경화수지(고형분 100%) 100중량부와 혼합하였다. 얻어진 액을 미리 표면 코로나 처리한 두께 50㎛의 PET수지 필름 위에 바 코터를 이용하여 성막하고, 이것을 100℃에서 30초 건조해서 용제를 증발시킨 후, 고압 수은램프로 경화시켜서 PET수지 필름 위에 단열층을 형성하였다.Example 1 10 parts by weight, the ultraviolet curable resin for hard coat (100% solids) dispersion (A) of LaB 6 fine particles in 100 parts by weight was mixed with. The obtained liquid was previously formed on a 50 μm-thick PET resin film having a surface corona treatment using a bar coater, dried at 100 ° C. for 30 seconds to evaporate the solvent, and then cured with a high pressure mercury lamp to form a heat insulating layer on the PET resin film. Formed.
얻어진 필름형상의 단열 자재는, LaB6 미립자가 하드 코트용 자외선 경화수지 중에 분산된 단열층과, 이 단열층이 코트된 모재인 PET수지 필름으로 구성된 적층구조를 가지고 있다. 또, 이 필름의 단열층은, 두께가 약 2㎛이며, LaB6 미립자의 함유량은 0.08g/㎡에 상당한다.Heat insulating material of the obtained film-shaped, LaB 6 fine particles may have a multilayer structure composed of the hard coat and the heat insulating layer, a PET resin film, a heat insulating layer of the coat the base metal dispersed in a radiation-curing resin. Further, a heat insulating layer of the film, from about 2㎛ the thickness, the content of the LaB 6 fine particles is equivalent to 0.08g / ㎡.
얻어진 필름형상의 단열 자재를 실시예1과 마찬가지로 평가한 바, 가시광 투 과율은 75% 및 일사투과율은 57%이며, 가시광 영역의 빛을 충분히 투과하고 있는 동시에, 태양광선의 직접 입사광을 약 43% 차폐하고 있어, 높은 단열 효과를 가지는 것을 알 수 있다. 또, 자외선 영역의 투과율은, 파장 290㎚에서 0% 및 320㎚에서 22%이며, 290㎚에서의 투과율이 0%인 것은 PET수지기재의 영향이다. 또한, 헤이즈 값은 1.0%이며, 투명성이 지극히 높고, 내부의 상황을 외부에서도 분명히 확인할 수 있다.The obtained film-shaped heat insulating material was evaluated in the same manner as in Example 1, and the visible light transmittance was 75% and the solar transmittance was 57%, while sufficiently transmitting the light in the visible light region, and about 43% of the direct incident light of the sunlight. It is shielded and it turns out that it has a high heat insulation effect. The transmittance in the ultraviolet region is 0% at wavelength 290 nm and 22% at 320 nm, and the transmittance at 290 nm is 0%. In addition, the haze value is 1.0%, the transparency is extremely high, and the internal situation can be clearly confirmed from the outside.
이상과 같이, 본 발명에 관한 농원예 시설용 단열 자재는 내후성이 우수하고, 또한 내부에서의 작업이나 식물의 육성에 필요한 가시광역의 빛을 충분히 투과하는 동시에, 근적외광을 효율적으로 흡수 또는 차단해서 높은 단열성을 구비하고, 더군다나, 자외선을 적절하게 투과하고 또는 그 투과를 제어할 수 있으므로 병해충의 발생을 억제하는 동시에 수분에 필요한 꿀벌 등의 곤충을 충분히 활발하게 활동시킬 수 있다. 따라서, 농업용이나 원예용 하우스의 지붕이나 외벽재 등에 이용하는데에 적합하다.As described above, the heat insulating material for agricultural horticultural facilities according to the present invention is excellent in weather resistance, and sufficiently transmits visible light required for internal work or plant growth, and efficiently absorbs or blocks near infrared light, thereby increasing Insulation is provided, and furthermore, ultraviolet rays can be appropriately transmitted or controlled so as to suppress the occurrence of pests and to actively activate insects such as bees necessary for pollination. Therefore, it is suitable to use for the roof of an agricultural and horticultural house, an exterior wall material, etc.
Claims (6)