KR100825270B1 - The water wiping intaglio ink composition with magnetic and infrared absorption characteristics - Google Patents

The water wiping intaglio ink composition with magnetic and infrared absorption characteristics Download PDF

Info

Publication number
KR100825270B1
KR100825270B1 KR1020060059819A KR20060059819A KR100825270B1 KR 100825270 B1 KR100825270 B1 KR 100825270B1 KR 1020060059819 A KR1020060059819 A KR 1020060059819A KR 20060059819 A KR20060059819 A KR 20060059819A KR 100825270 B1 KR100825270 B1 KR 100825270B1
Authority
KR
South Korea
Prior art keywords
magnetic
infrared absorption
water
weight
ink
Prior art date
Application number
KR1020060059819A
Other languages
Korean (ko)
Other versions
KR20080001392A (en
Inventor
손규복
윤준희
고병옥
서범준
Original Assignee
한국조폐공사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한국조폐공사 filed Critical 한국조폐공사
Priority to KR1020060059819A priority Critical patent/KR100825270B1/en
Publication of KR20080001392A publication Critical patent/KR20080001392A/en
Application granted granted Critical
Publication of KR100825270B1 publication Critical patent/KR100825270B1/en

Abstract

본 발명은 화폐나 각종 유가증권 등의 위변조 방지와 진위식별의 구분이 용이하며, 금융자동화기기의 기능성 유지를 위하여 특수한 인쇄기계를 활용하여 약 50㎛ 이상의 잉크 도막을 형성하도록 인쇄하는 데 사용하는 잉크로서 자성 특성과 적외선 흡수 특성을 동시에 갖는 수불식 요판잉크에 관한 것으로, 구체적으로는 은행권이나 각종 유가증권 등의 위변조 방지 및 진위감별을 위하여 특수한 인쇄방법인 수불식 요판 인쇄방식에 사용할 수 있는 잉크로서 자성안료와 적외선 흡수 안료를 포함하는 수불식 요판잉크에 관한 것이다. The present invention can be easily distinguished from forgery and forgery identification of money or various securities, and used to print an ink film of about 50 μm or more by using a special printing machine to maintain the functionality of the automatic teller machine. The present invention relates to a water immersion intaglio ink having both magnetic properties and infrared absorption characteristics. Specifically, it is an ink that can be used in a water printing gravure printing method, which is a special printing method for preventing forgery and discrimination of banknotes and various securities. The present invention relates to a hydrophobic intaglio ink containing a magnetic pigment and an infrared absorbing pigment.

본 발명에 따른 자성 특성과 적외선 흡수 특성을 동시에 갖는 수불식 요판잉크는 80~85℃로 가열된 인쇄판에 전달되고, 약 50톤 정도의 인쇄압(선압)을 받아 직접 피인쇄체에 인쇄하는 최근의 요판인쇄기(Super Orlof Intaglio)에 적용할 수 있으며, 인쇄제품에 대한 물리화학적 내구성이 우수하여 오랜기간 사용하여도 자성특성이나 적외선 흡수 기능이 저하되지 않고, 타사 제품의 잉크로 인쇄한 경우와 비교하여 적외선 흡수파장이 완전히 다르게 나타나므로 진위식별이 용이한 장점을 가지고 있다.The water-insoluble intaglio inks having both magnetic properties and infrared absorption characteristics according to the present invention are transferred to a printing plate heated at 80 to 85 ° C., and have a printing pressure (linear pressure) of about 50 tons to print directly onto the printed object. It can be applied to Super Orlof Intaglio, and it has excellent physicochemical durability of printed products, so it does not deteriorate magnetic properties or infrared absorption function even after long-term use. Since infrared absorption wavelength appears completely different, it is easy to identify the authenticity.

적외선 흡수, 자성, 금융자동화기기, 아쿠아세이브 Ⅱ, 불식용액, 화선부, 비화선부, 와이핑시린더, 수불식 요판잉크  Infrared absorption, magnetic, automatic teller machine, aqua save Ⅱ, insoluble solution, wire line, non-fire line, wiping cylinder, water intaglio intaglio ink

Description

자성 특성과 적외선 흡수 특성을 동시에 갖는 수불식 요판잉크 조성물{The water wiping intaglio ink composition with magnetic and infrared absorption characteristics}The water wiping intaglio ink composition with magnetic and infrared absorption characteristics

도 1 - 자성안료별 IR spectrum (MIOB : 새한미디어 제품 Magnetic Iron Oxide Brown EP-060, BASF 025 : BASF사 Magnetic Pigment 025, Zmag 1105 : ISK Magnetics사 Zmag 1105)Figure 1-IR spectrum for magnetic pigments (MIOB: Magnetic Iron Oxide Brown EP-060, BASF 025: BASF's Magnetic Pigment 025, Zmag 1105: ISK Magnetics' Zmag 1105)

도 2 - 자성안료별 IR viewer 특성 (MIOB : 새한미디어 제품 Magnetic Iron Oxide Brown EP-060, BASF 025 : BASF사 Magnetic Pigment 025, Zmag 1105 : ISK Magnetics사 Zmag 1105)Figure 2-IR viewer characteristics of magnetic pigments (MIOB: Magnetic Iron Oxide Brown EP-060, BASF 025: BASF Magnetic Pigment 025, Zmag 1105: ISK Magnetics Zmag 1105)

도 3 - Magnetic iron oxide brown 에 적외선 흡수 안료를 투입한 잉크의 IR spectrumFIG. 3-IR spectrum of ink injecting infrared absorption pigment into Magnetic iron oxide brown

도 4 - Magnetic iron oxide brown 에 적외선 흡수 안료를 투입한 잉크의 IR viewer 특성Fig. 4-IR viewer characteristic of ink injecting infrared absorption pigment into magnetic iron oxide brown

도 5 - Magnetic pigment 025 에 적외선 흡수 안료를 투입한 잉크의 IR spectrum5-IR spectrum of the ink in which the infrared absorption pigment is added to the magnetic pigment 025

도 6 - Magnetic pigment 025 에 적외선 흡수 안료를 투입한 잉크의 IR viewer 특성Fig. 6-IR viewer characteristics of ink injecting infrared absorption pigment into Magnetic pigment 025

도 7 - 실시예 1 및 비교예 1의 잉크의 IR spectrum7-IR spectrum of the ink of Example 1 and Comparative Example 1

도 8 - 실시예 1 및 비교예 1의 잉크의 IR viewer 특성8-IR viewer characteristics of the ink of Example 1 and Comparative Example 1

도 9 - 실시예 2 및 비교예 2의 잉크의 IR spectrum9-IR spectrum of the ink of Example 2 and Comparative Example 2

도 10 - 실시예 2 및 비교예 2의 잉크의 IR viewer 특성10-IR viewer properties of the ink of Example 2 and Comparative Example 2

도 11 - 실시예 3 및 비교예 3의 잉크의 IR spectrum11-IR spectrum of the ink of Example 3 and Comparative Example 3

도 12 - 실시예 3 및 비교예 3의 잉크의 IR viewer 특성12-IR viewer characteristics of the ink of Example 3 and Comparative Example 3

도 13 - 실시예 4 및 비교예 4의 잉크의 IR spectrumFigure 13-IR spectrum of the ink of Example 4 and Comparative Example 4

도 14 - 실시예 4 및 비교예 4의 잉크의 IR viewer 특성14-IR viewer properties of the ink of Example 4 and Comparative Example 4

도 15 - 실시예 5 및 비교예 5의 잉크의 IR spectrum15-IR spectrum of the ink of Example 5 and Comparative Example 5

도 16 - 실시예 5 및 비교예 5의 잉크의 IR viewer 특성16-IR viewer properties of the ink of Example 5 and Comparative Example 5

도 17 - 실시예 6 및 비교예 6의 잉크의 IR spectrum17-IR spectrum of the ink of Example 6 and Comparative Example 6

도 18 - 실시예 6 및 비교예 6의 잉크의 IR viewer 특성18-IR viewer characteristics of the ink of Example 6 and Comparative Example 6

도 19 - 미국은행권((a) 10$, (b) 50$, (c) 100$)의 자성잉크 IR spectrumFigure 19-Magnetic ink IR spectrum for US bank notes ((a) 10 $, (b) 50 $, (c) 100 $)

도 20 - 일본은행권((a) 1000, 2000￥, (b) 5000￥, (c) 10000￥)의 자성잉크 IR spectrumFigure 20-Magnetic ink IR spectrum of Bank of Japan ((a) 1000, 2000yen, (b) 5000yen, (c) 10000yen)

도 21 - 유로화((a) 50€, (b) 100€, (c) 200€, (d) 500€)의 자성잉크 IR spectrumFigure 21-Magnetic ink IR spectrum in Euros ((a) 50 €, (b) 100 €, (c) 200 €, (d) 500 €)

본 발명은 화폐나 유가증권의 위변조 방지와 진위식별, 금융자동화기기 감응성 기능을 부여하고 타사 제품과의 차별화를 위하여, 자성 특성을 잉크에 적외선 흡수 특성을 부가하므로서 자성 특성과 적외선 흡수 특성을 동시에 갖는 수불식 요판잉크에 관한 것이다. 구체적으로는 은행권이나 각종 유가증권 등의 위변조 방지 및 진위감별을 위하여 특수한 인쇄방법인 수불식 요판 인쇄방식에 사용할 수 있는 잉크로서 자성안료와 적외선 흡수 안료를 포함하는 수불식 요판잉크에 관한 것이다. The present invention provides magnetic properties and infrared absorption characteristics simultaneously by adding infrared absorption characteristics to magnetic inks for imparting anti-counterfeiting and authenticity of money or securities, and sensitivity of financial automation equipment and differentiating them from other products. It relates to a waterless intaglio ink. Specifically, the present invention relates to a inkless intaglio ink containing a magnetic pigment and an infrared absorbing pigment as an ink which can be used in a water-based intaglio printing method, which is a special printing method for preventing forgery and forgery of banknotes and various securities.

세계 각국의 화폐나 유가증권은 위변조 방지, 진위식별, 금융자동화기기 감응성에 대응하기 위하여 자성, 적외선 흡수, 적외선 반사, 형광 등의 특성을 갖는 여러 가지 물질을 비공개적으로 용지나 잉크에 첨가하여 제품을 생산하고 있으며, 제품은 수명이 끝날 때까지 모든 기능성이 유지되어야 한다. 화폐 제조는 여러단계의 복잡한 공정을 거쳐 이루어지며, 각종의 기능성 요소를 적용하기 위해서는 인쇄방법, 잉크도막의 두께, 인쇄면적, 디자인 원도 등이 고려되어야 하며, 대부분의 화폐를 살펴보면 요판잉크는 인쇄 도막이 두껍고 색상이 어둡기 때문에 기능성 요소를 부가해도 측정기기나 특수한 도구를 사용하지 않고는 육안으로 식별하는 것이 곤란하고, 칼라복사기에 의한 복사물이나, 잉크젯 프린터에 의한 출력물에서는 기능성이 나타나지 않는다. 따라서 대부분 요판잉크에 기능성을 부가하고 있으며, 요판인쇄기계는 엄격하게 보안관리를 유지하는 조폐국에만 보유하고 있기 때문에 민간이 운영하는 인쇄소에서는 요판인쇄물의 제조가 불가능하다.Money and securities from around the world are manufactured by adding various materials that have characteristics such as magnetic, infrared absorption, infrared reflection, and fluorescence to paper or ink in order to prevent counterfeiting, authenticity identification, and sensitivity of financial automation equipment. And all functionality must be maintained until the end of its life. The manufacture of money takes place through a complex process of several stages, and in order to apply various functional elements, the printing method, thickness of ink coating, printing area, design originality, etc. should be taken into consideration. Since the coating is thick and the color is dark, it is difficult to visually identify even adding a functional element without using a measuring device or a special tool, and the functionality does not appear in a copy by a color copier or an output by an inkjet printer. Therefore, most of them add functionality to intaglio ink, and since intaglio printing machines are reserved only in the Mint, which maintains strict security management, it is impossible to manufacture intaglio printing at privately operated printing shops.

종래의 요판잉크는 한 종류의 잉크에 한가지 기능만 갖도록 설계되어 있고, 각국의 화폐를 전문가가 특정한 도구를 이용하여 분석하면 알 수 있으며, 또한 이는 위변조 방지 차원에서 기술을 공개하지 않는 것이 일반적인 관례이다.Conventional intaglio ink is designed to have only one function in one kind of ink, and it is common practice to analyze the currency of each country with a special tool, and it is a common practice not to disclose the technology in order to prevent forgery and alteration. .

또한 종래의 자성잉크를 적용한 은행권, 수표, 카드류, 고속도로 통행 티켓, 전화카드, 통장 등의 자성부분은 대부분 흑색 안료를 사용하였기 때문에 흑색이나 짙은 갈색으로 인쇄되어 다양한 색상을 나타낼 수 없었다.In addition, since magnetic parts such as banknotes, checks, cards, highway tickets, phone cards, and bankbooks to which conventional magnetic ink is applied, most of them used black pigment, they could not be printed in black or dark brown to show various colors.

수불식 요판인쇄는 인쇄판의 화선부인 오목한 부분(요판; 凹版)에 잉크를 채우고 비화선부분에 묻은 잉크를 플라스틱 재질의 와이핑시린더로 닦아낸 후 제거된 잉크는 불식용액(wiping solution)에 쉽게 분산되어야 하는 특성을 갖아야 하는 반면, 화선부에 채워진 잉크는 인쇄용지에 전이되어 건조된 후의 잉크 도막은 내약품성이나 내알카리성이 강해야 제품을 장기적으로 사용할 수 있다. 또한 종래 요판 인쇄기계의 불식시스템(아쿠아세이브)은 폐수처리 시스템으로 이루어져 있기 때문에 기계 1대당 약 750ℓ/hr 정도 발생하는 불식용액을 처리하여야 하는 문제점을 갖고 있었으나 최근에 개발된 불식시스템(아쿠아세이브 Ⅱ)은 불식용액을 전량 회수하여 재활용하는 방식이므로 잉크중의 바니시 성분이 쉽게 검화되어야 필터에 막힘이 발생하지 않는다.Water-based intaglio printing fills in the recessed portion of the printing plate, and wipes the ink on the non-heated portion with a wiping cylinder made of plastic, and then removes the ink easily with a wiping solution. On the other hand, the ink filled in the wire part has to be dispersed, and the ink coating film after being transferred to the printing paper and dried has a strong chemical resistance or alkali resistance so that the product can be used for a long time. In addition, the conventional intaglio printing machine's erosion system (aqua save) consists of a wastewater treatment system, which has had a problem of treating the erosion solution generated about 750 l / hr per machine, but the recently developed erosion system (aqua save Ⅱ) ) Is a method of recovering and recycling all of the insoluble solution, so that the varnish component in the ink should be easily saponified to prevent clogging of the filter.

은행권이나 유가증권 등의 인쇄에 사용되는 최근에 개발된 요판인쇄기(Super Orlof Intaglio)는 4개의 잉크 유니트가 있으며, 각각의 잉크 유니트에서 공급되는 잉크는 조각로라(chablon roller)를 거쳐 1개의 집합통(collecting drum)에 합쳐진 다음, 집합통에 합쳐진 잉크가 80 내지 84℃의 온도를 유지하는 인쇄판에 전달 되고, 인쇄판에 전달된 잉크는 약 50톤의 선압을 받아 피인쇄체(종이)에 잉크가 전달되는 간접 잉킹방식으로서 잉크의 전이성이 좋아야 하며, 불식시스템은 종전과 같으나 불식용액(물 98.8 내지 99.0중량%, 가성소다 0.8중량%, 황산화피마자유 0.2 내지 0.4중량%)은 응집처리와 여과과정을 거쳐 전량 재활용되기 때문에 요판잉크의 성분 중 바니시의 검화가 완전히 이루어져야 한다.The recently developed Super Orlof Intaglio, which is used for printing banknotes and securities, has four ink units, and the ink supplied from each ink unit is collected through a chablon roller. The ink, which is combined with the collecting drum, is then transferred to a printing plate maintaining a temperature of 80 to 84 ° C, and the ink delivered to the printing plate receives about 50 tons of linear pressure, and the ink is delivered to the printed object (paper). As the indirect inking method, the transferability of ink should be good, and the erosion system is the same as before, but the erosion solution (98.8 to 99.0 wt% of water, 0.8 wt% of caustic soda, 0.2 to 0.4 wt% of sulfated castor oil) is coagulated and filtered. Since the whole is recycled through, the varnish of the intaglio ink must be completely saponified.

한편 종전의 은행권이나 유가증권 등의 요판인쇄에 사용하는 요판잉크는 자성과 적외선 흡수 기능을 다른 색상에서 나타날 수 있도록 하여 인쇄도수의 제한을 받게 되어있다. 이는 여러나라의 화폐를 분석하면 확실하게 구분된다.On the other hand, intaglio ink, which is used for intaglio printing of conventional banknotes and securities, is limited in the printing frequency by allowing magnetic and infrared absorption functions to appear in different colors. This is clearly distinguished by analyzing various currencies.

대한민국 공개특허 제2002-0058117호에는 근적외선 흡수제, 이의 제조방법 및 이를 포함하는 잉크가 공지되어 있으며, 대한민국 공개특허 제1999-0037835호에는 적외선 기기 감지 요소가 적용된 은행권 및 수표가 공지되어 있고, 대한민국 공개특허 제1985-0000712호에는 지폐감별방법 및 그 장치가 공지되어 있으나, 상기 특허들은 적외선 흡수나 자성 특성 중 한가지 기능을 이용하였으며, 불식용액에 분산이 되지 않으므로 수불식 요판인쇄 방식에 적용할 수 없는 문제점을 가지고 있다.In Korean Laid-Open Patent Publication No. 2002-0058117, a near-infrared absorber, a manufacturing method thereof, and an ink including the same are known. In Korean Laid-Open Patent Publication No. 1999-0037835, a banknote and a check to which an infrared device sensing element is applied are known. In Patent No. 1985-0000712, a banknote discrimination method and a device thereof are known, but the above patents use one of infrared absorption and magnetic properties, and are not applicable to water-based intaglio printing methods because they are not dispersed in an insoluble solution. I have a problem.

이에 본 발명자는 최근에 개발된 요판인쇄기계 시스템에 적용상 문제점이 없고, 인쇄적성이나 인쇄효과가 우수하며, 오랜기간이 경과하여도 기능성이 소실되지 않는 자성 특성과 적외선 흡수 특성의 두가지 기능을 동시에 갖는 수불식 요판잉크 조성물를 개발하고자 연구노력한 결과, 자성안료와 적외선 흡수 안료를 동시에 채용함으로서 자성과 적외선 흡수의 복합 기능을 갖으면서 수불식 요판잉크의 무간지적성, 불식적성, 잉크 전이성, 미스팅 방지적성이 우수하고, 인쇄물의 내약품성, 내알카리성 등의 특성이 우수한 수불식 요판잉크의 조성물을 제조하였다. Therefore, the present inventors have no problem in application to the recently developed intaglio printing machine system, have excellent printing aptitude or printing effect, and simultaneously perform two functions of magnetic characteristics and infrared absorption characteristics, which are not lost even after a long time. As a result of research efforts to develop water-insoluble intaglio inks, the magnetic pigments and infrared absorbing pigments are adopted simultaneously, so that it has the combined function of magnetic and infrared absorption, and it is possible to prevent the incoherence, incoherence, ink transfer, and mist of inks. A composition of a water-insoluble intaglio ink having excellent aptitude and excellent properties such as chemical resistance of a printed matter and alkali resistance was prepared.

따라서, 본 발명의 목적은 상기한 바와 같이 자성안료와 적외선 흡수 안료를 동시에 함유하여 은행권이나 각종 유가증권 등의 위변조를 식별하기 위해 자성특성과 적외선 흡수 특성을 동시에 가지는 수불식 요판잉크 조성물을 제공하는 것이며, 또한 요판잉크의 물성에 변화를 주지않고 인쇄적성이나 불식적성에 영향을 미치지 않으며 인쇄한 후의 인쇄물은 내약품성, 내알카리성 등이 우수하고, 영구적으로 자성특성과 적외선 흡수 특성을 갖는 수불식 요판잉크 조성물을 제공하는 것을 목적으로 한다.Accordingly, it is an object of the present invention to provide a water-insoluble intaglio ink composition having both magnetic properties and infrared absorption properties simultaneously to contain a magnetic pigment and an infrared absorbing pigment at the same time to identify forgery and alteration of banknotes and various securities. Also, it does not affect the printability or incorruption without changing the physical properties of the intaglio ink, and the printed product after printing is excellent in chemical resistance, alkali resistance, etc. and has permanent magnetic properties and infrared absorption characteristics. It is an object to provide an ink composition.

본 발명의 다른 목적은 최근에 개발된 요판인쇄기계(Super Orlof Intaglio)에 적용하는데 문제점이 없는 수불식 요판잉크 조성물을 제공하는 데 있다.Another object of the present invention is to provide a water-insoluble intaglio ink composition having no problem in application to recently developed intaglio printing machines (Super Orlof Intaglio).

본 발명의 또 다른 목적은 화폐의 위변조방지, 진위식별, 금융자동화기기 취급시 문제점이 없는 수불식 요판잉크 조성물을 제공하는 데 있다.Still another object of the present invention is to provide a water-infiltrating intaglio ink composition which has no problems in preventing forgery and alteration of money, authenticity identification, and handling of automated teller machines.

본 발명의 또 다른 목적은 자성 특성을 갖는 다양한 색상의 잉크 제조가 가능하므로 인쇄물 색상의 다양화를 기할 수 있으며, 육안 식별이 되지 않고 특정한 도구나 광학기기에 의해서만 판독이 가능하므로 보안인쇄 제품의 비공개 요소로 적 용할 수 있는 특성을 가진 수불식 요판잉크 조성물을 제공하는데 있다.Another object of the present invention is to produce a variety of colors of the ink having a magnetic property, it is possible to diversify the color of the printed matter, it is not visible to the naked eye can be read only by a specific tool or optics, so the security of printed products To provide a hydrophobic intaglio ink composition having a property that can be applied as a urea.

본 발명의 또 다른 목적은 상기 자성특성 및 적외선 흡수 특성을 동시에 가지는 수불식 요판잉크 조성물을 이용하여 인쇄된 은행권 및 각종 유가증권을 제공하는 것이다.It is still another object of the present invention to provide a banknote and various securities printed using a water-insoluble intaglio ink composition having both magnetic properties and infrared absorption properties.

상기한 목적을 달성하기 위하여, 본 발명은 자성안료와 적외선 흡수 안료를 동시에 함유하는 자성특성과 적외선 흡수 특성을 동시에 가지는 수불식 요판잉크 조성물에 관한 것으로, 본 발명에 다른 자성특성과 적외선 흡수 특성을 동시에 가지는 수불식 요판잉크 조성물은 자성안료; 적외선 흡수 안료; 및 요판잉크의 인쇄적성과 불식적성을 향상시키기 위한 전색제를 함유하는 것을 특징으로 한다. 또한 본 발명에 따른 자성특성과 적외선 흡수 특성을 동시에 가지는 수불식 요판잉크 조성물을 은행권 및 각종 유가증권에 사용하는 것을 특징으로 하며, 적외선 최대 흡수 파장을 이용하여 위변조 은행권 및 유가증권을 식별하는 방법을 특징으로 한다.In order to achieve the above object, the present invention relates to a water-insoluble intaglio ink composition having both a magnetic pigment and an infrared absorbing pigment at the same time having a magnetic characteristic and an infrared absorbing characteristic, the magnetic properties and infrared absorption characteristics different from the present invention At the same time, the water-insoluble intaglio ink composition comprises a magnetic pigment; Infrared absorbing pigments; And a colorant for improving the printability and the indelibility of the intaglio ink. In addition, a water-insoluble intaglio ink composition having both magnetic properties and infrared absorption characteristics according to the present invention is used for banknotes and various securities, and a method for identifying counterfeit bank notes and securities using an infrared maximum absorption wavelength. It features.

이하, 본 발명을 보다 상세히 설명하면 다음과 같다.Hereinafter, the present invention will be described in more detail.

상술한 바와 같이, 본 발명에 따른 자성특성과 적외선 흡수 특성을 가지는 수불식 요판잉크 조성물은 적외선 흡수 안료와 자성안료를 모두 포함하는 것을 주요 특징으로 한다. As described above, the water-insoluble intaglio ink composition having magnetic properties and infrared absorption properties according to the present invention is characterized by including both an infrared absorption pigment and a magnetic pigment.

적외선 흡수 안료는 내구성과 내약품성이 강하고, 잉크제조 적성이 양호하 며, 인쇄후에도 잉크도막이 각종 용제에 불용해되는 성질을 가지고 있는 것으로 폴리가교형 프탈로시아닌계 화합물을 사용하며, 사용되는 폴리가교형 프탈로시아닌계 화합물은 대한민국 등록특허 제0528155호에 공개된 방법에 의하여 제조된 것으로 적외선 흡수파장 범위(λmax) 800 내지 900㎚ 이고, pH; 5.5±1.5, 평균입자; 0.4～4㎛, 강열잔분; 8.9%의 특성을 갖는 화합물로, 하기의 구조로 표시되며, 시판되는 대표적 제품으로 상품명 CMS Blue 2A-905(CMS 테크놀로지(주))가 있다.Infrared absorbing pigments have strong durability and chemical resistance, have good ink manufacturing aptitude, and have a property that the ink coating is insoluble in various solvents even after printing. The system compound is prepared by the method disclosed in Korean Patent No. 0528155 and has an infrared absorption wavelength range (λ max ) of 800 to 900 nm, pH; 5.5 ± 1.5, average particle; 0.4-4 micrometers, ignition residue; A compound having a property of 8.9% is represented by the following structure, and a representative commercial product is a trade name CMS Blue 2A-905 (CMS Technology Co., Ltd.).

Figure 112006046886473-pat00001
Figure 112006046886473-pat00001

[상기 식에서 M1과 M2는 각각 무금속, 금속, 금속 산화물 또는 금속 할라이드에서 선택된 것으로서 서로 같거나 다른 것일 수 있으며, R1 내지 R16은 각각 수소원자, 할로겐원자, 수산기, 아미노기, 히드록시술포닐기, 아미노술포닐기, 알킬기, 탄소수 1∼20의 치환기를 갖는 알킬기이고, SR17, SR18, OR19, NHR20 또는 NHR21이며, 선택된 것으로 각각 동일하거나 다른 것일 수 있으며, 여기서, R17은 치환기를 가진 페닐기, 알킬기 또는 탄소수 1∼20의 알킬기이고, R18은 탄소수 1∼20의 알콕시기를 가진 페닐기이며, R19, R20은 각각 치환기를 가진 페닐기, 아릴알킬기 또는 탄소수 1∼20의 알킬기이고, R21은 치환기를 가진 탄소수 1∼20의 알킬기이며, n은 1∼20의 정수이다.][Wherein M 1 and M 2 are each selected from a metal free, metal, metal oxide or metal halide, and may be the same or different from each other, and R 1 to R 16 are each a hydrogen atom, a halogen atom, a hydroxyl group, an amino group, or a hydroxyl group; And a sulfonyl group, an aminosulfonyl group, an alkyl group, an alkyl group having 1 to 20 carbon atoms, SR 17 , SR 18 , OR 19 , NHR 20, or NHR 21 , and each selected may be the same or different, wherein R is 17 is a phenyl group having an substituent, an alkyl group or an alkyl group having 1 to 20 carbon atoms, R 18 is a phenyl group having an alkoxy group having 1 to 20 carbon atoms, and R 19 and R 20 are each a phenyl group having an substituent, an arylalkyl group or 1 to 20 carbon atoms Is an alkyl group, R 21 is an alkyl group having 1 to 20 carbon atoms having a substituent, and n is an integer of 1 to 20.]

상기 적외선 흡수 안료의 첨가량은 수불식 요판잉크 전체 조성물에 대하여 1 내지 3 중량%가 바람직하며, 상기 첨가량이 1 중량% 미만이면 유통 중 인쇄물에 약간의 오염 내지는 훼손 발생시 적외선 흡수능이 떨어져 기기감지가 곤란하게 되고, 3 중량%를 초과하면 적외선 흡수 안료가 고가이므로 잉크 가격이 상승하여 실용화에 문제점이 있다.The addition amount of the infrared absorbing pigment is preferably 1 to 3% by weight based on the total composition of the water-insoluble intaglio ink, and when the addition amount is less than 1% by weight, the infrared absorbing ability is difficult to detect the device when there is slight contamination or damage to the printed material during distribution, making it difficult to detect the device. If it exceeds 3% by weight, the infrared absorbing pigment is expensive, so the ink price increases, which causes problems in practical use.

상기 적외선 흡수 안료 이외에 본 발명의 자성특성과 적외선 흡수 특성을 동시에 가지는 수불식 요판잉크 조성물을 구성하는 주요성분인 자성안료는 적외선을 완전히 흡수하는 흑색계열 또는 백색계열의 안료를 제외한 자성안료를 사용하는 것이 바람직한데, 상기 흑색계열의 자성안료로는 밝은 색상의 잉크 제조가 불가능하고 전파장의 적외선 영역에서 흡수 특성을 나타내므로 은행권이나 유가증원의 진위감별의 요소로 활용할 수 없기 때문이다. 적외선 반사특성을 가지는 황색계열 자성안료, 적외선 흡수와 반사의 중간특성을 가지는 회색계열 자성안료 또는 황색계열 자성안료와 회색계열 자성안료의 혼합 자성안료를 사용하는 것이 바람직하다.In addition to the infrared absorbing pigment, the magnetic pigment, which constitutes the water-insoluble intaglio ink composition having both the magnetic properties and infrared absorption properties of the present invention, uses a magnetic pigment except for a black or white pigment that completely absorbs infrared rays. It is preferable to use the black pigment as a light pigment because it is impossible to manufacture a bright color ink and exhibits absorption characteristics in the infrared region of the electric field, and thus cannot be used as an element of authenticity of banknotes or oil price increase. It is preferable to use a yellow magnetic pigment having infrared reflecting properties, a gray magnetic pigment having an intermediate characteristic of infrared absorption and reflection, or a mixed magnetic pigment of yellow based magnetic pigment and gray magnetic pigment.

상기 자성안료의 첨가량은 수불식 요판잉크 전체 조성물에 대하여 8 내지 12 중량%가 바람직하며, 상기 첨가량이 8 중량% 미만이면 자성강도가 낮아져 금융자동 화기기에 설정된 하한값에 미치지 못하여 인식율이 낮아지므로 진위식별이 명확하지 않고, 12 중량%를 초과하면 자성강도는 높아지나 금융자동화기기에 설정된 상한값을 벗어나게 되고, 무기안료이기 때문에 잉크의 물성이 나빠지고, 크롬으로 도금된 인쇄판과 스프링강으로 이루어진 독타브레이드, PVC로 구성된 와이핑 시린더의 마모가 쉽게되어 인쇄상에 여러 가지 문제점이 발생되므로 생산성이 떨어지게 된다.The addition amount of the magnetic pigment is preferably 8 to 12% by weight based on the total composition of the water-insoluble intaglio ink, and if the addition amount is less than 8% by weight, the magnetic strength is lowered, so that the recognition rate is lowered since the recognition rate is lowered. If it is not clear and exceeds 12% by weight, the magnetic strength is increased, but it is out of the upper limit set in the automatic teller machine. Because it is an inorganic pigment, the physical properties of the ink are deteriorated. The wearability of the wiping cylinder made of PVC is easy, resulting in various problems in printing, thereby reducing productivity.

상기 황색계열 자성안료는 보자력(Hc); 385±10(Oe), 포화자속밀도(σs); 71~73(emu/g), pH; 2.7~3.6, 흡유량(OA); 6.5~8.0(㎖/20g), 표면적(BET); 24.5±1.5(㎡/g)의 특성을 갖는 것이 바람직하고, 시판되는 대표적 제품으로 새한미디어 제품인 Magnetic Iron Oxide Brown EP-060가 있고, 회색계열 자성안료는 표면적 (BET); 0.4(㎡/g), 평균입자; 4~6(㎛), 비중; 7.7(g/㎤), 흡유량; 7.5(g oil/100g pigment), 최대잔류자속밀도(δm); 200(A ㎡/kg), 철분; Fe>97%(순도)의 특성을 갖는 것이 바람직하며, 시판되는 대표적 제품으로 BASF사 제품인 Magnetic Pigment 025 BASF이 있다.The yellow magnetic pigment has a coercive force (Hc); 385 ± 10 (Oe), saturation magnetic flux density (σs); 71-73 (emu / g), pH; 2.7 to 3.6, oil absorption (OA); 6.5-8.0 (ml / 20g), surface area (BET); It is desirable to have a characteristic of 24.5 ± 1.5 (m2 / g), and representative commercially available products include Magnetic Iron Oxide Brown EP-060, a Saehan Media product, and a gray-based magnetic pigment has a surface area (BET); 0.4 (m 2 / g), average particle; 4 to 6 µm, specific gravity; 7.7 (g / cm 3), oil absorption; 7.5 g oil / 100 g pigment, maximum residual magnetic flux density (? M); 200 (A m 2 / kg), iron powder; It is desirable to have a characteristic of Fe> 97% (purity), and a representative commercial product is Magnetic Pigment 025 BASF manufactured by BASF.

본 발명에 따른 자성 특성과 적외선 흡수 특성을 동시에 가지는 수불식 요판잉크 조성물은 상기 적외선 흡수 안료 및 자성안료 이외에 요판잉크의 인쇄적성과 불식적성을 향상시키기 위한 전색제를 포함한다.The water-insoluble intaglio ink composition having both magnetic properties and infrared absorption properties according to the present invention includes a colorant for improving the printability and incorrosiveness of the intaglio ink in addition to the infrared absorbing pigment and the magnetic pigment.

본 발명에 사용하는 전색제는 우레탄변성 알키드바니시, 에폭시변성 알키드바니시, 폴리에스텔변성 알키드바니시, 로진변성 알키드바니시, 멜라민변성 알키드 바니시, 아마이드변성 알키드바니시, 아크릴변성 알키드바니시로 이루어진 군으로부터 선택된 1종 이상;과 알키드수지 바니시, 페놀수지 바니시, 요소수지 바니시, 멜라민수지 바니시, 폴리우레탄수지 바니시로 이루어진 군에서 선택된 1 종 이상;의 혼합물이 바람직하며, 특히 인쇄시 사용하는 불식용액에 대한 분산성과 인쇄적성, 잉크도막적성, 내구성, 내약품성, 건조성 등을 고려하면, 산가 30 내지 35, 점도 300 내지 400poise(25℃), 중량평균 분자량 20,000 내지 25,000인 우레탄변성 알키드바니시 및 산가 65 내지 70, 점도 400 내지 700poise(25℃), 중량평균 분자량 8,000 내지 12,000인 알키드수지 바니시가 가장 바람직하며, 혼합비는 인쇄적성과 불식적성, 건조적성, 전이성, 미스팅, 인쇄물의 피막강인성, 접착성, 내알카리성 등의 특성 면에서 우레탄변성 알키드바니시와 알키드수지 바니시를 1:1 내지 1.5 중량비가 바람직하며, 수불식 요판잉크 전체 조성물에 대하여 우레탄변성 알키드바니시 15 내지 25중량％ 및 알키드수지 바니시 15내지 25중량%를 사용한다. 상기 각각의 바니시 사용량이 15 중량% 미만이면 불식적성과 내마모성 및 내약품성이 불량하게 되고, 25 중량% 초과 사용하면 잉크의 불식적성 등은 향상되나 택크, 점도, 유동성 등 제반 잉크물성의 조정이 곤란하여 인쇄적성이 미흡한 문제점이 발생한다.The colorant used in the present invention is at least one selected from the group consisting of urethane modified alkyd varnishes, epoxy modified alkyd varnishes, polyester modified alkyd varnishes, rosin modified alkyd varnishes, melamine modified alkyd varnishes, amide modified alkyd varnishes, and acrylic modified alkyd varnishes. And at least one selected from the group consisting of alkyd resin varnishes, phenolic resin varnishes, urea resin varnishes, melamine resin varnishes, polyurethane resin varnishes, and in particular, dispersibility and printability for insoluble solutions used in printing. In consideration of ink coating suitability, durability, chemical resistance, dryness, and the like, an acid value of 30 to 35, a viscosity of 300 to 400 poise (25 ° C), a urethane-modified alkyd varnish having a weight average molecular weight of 20,000 to 25,000, and an acid value of 65 to 70, a viscosity of 400 Alkyd resin varnish having a weight average molecular weight of 8,000 to 12,000 Most preferably, the mixing ratio is 1: 1 to 1.5 weight ratio of urethane-modified alkyd varnish and alkyd resin varnish in terms of printability, incorrosiveness, dryness, transferability, misting, film toughness, adhesiveness and alkali resistance of printed materials. Preferably, 15-25 weight% of urethane-modified alkyd varnishes and 15-25 weight% of alkyd resin varnishes are used with respect to the total number of water-insoluble intaglio inks. If the amount of each varnish is less than 15% by weight, incorrosion, abrasion resistance, and chemical resistance are poor, and when used in excess of 25% by weight, it is difficult to adjust ink properties such as ink, viscosity, fluidity, etc. As a result, printability is insufficient.

또한 본 발명에 따른 자성특성과 적외선 흡수 특성을 동시에 가지는 수불식 요판잉크 조성물은 상기 적외선 흡수 안료, 자성안료 및 전색제 이외에 수불식 요판 인쇄에 적합하도록 잉크의 물성 조성과 인쇄적성, 건조성, 내구성, 기상안정성, 마모성 등의 특성을 유지하기 위하여 지방족탄화수소계 용제와 글리콜에테르계 용제, 분산제, 왁스, 건조제 등이 포함되며, 착색안료, 체질안료 및 탈수피마자유지방산 등 종래의 잉크제조에 사용되는 것을 더 포함할 수 있다.In addition, the water-insoluble intaglio ink composition having both magnetic properties and infrared absorption properties according to the present invention is suitable for printing ink-intaglio printing in addition to the infrared absorbing pigments, magnetic pigments and colorants, and the physical properties of the ink, printability, dryness, durability, Aliphatic hydrocarbon solvents, glycol ether solvents, dispersants, waxes, desiccants, etc. are included to maintain the properties of gas phase stability and abrasion, and those used in conventional ink manufacturing such as coloring pigments, extender pigments, and dehydrated castor oil fatty acids. It may further include.

한편, 본 발명에 따른 자성특성과 적외선 흡수 특성을 동시에 가지는 수불식 요판잉크 조성물에는 잉크 물성 조정을 위하여 지방족 탄화수소계 용제와 글리콜에테르계 용제를 혼합하여 사용하는 것이 바람직하며, 상기 글리콜에테르계 용제는 디에틸렌글리콜 모노부틸에테르, 디에틸렌글리콜 모노에틸에테르, 디에틸렌글리콜 모노메틸에테르로 이루어진 군으로부터 선택된 하나 또는 그 이상을 혼합하여 사용할 수 있으며, 지방족탄화수소계 용제는 기상안정성과 무간지적성을 향상시킬 수 있도록 비점범위 290 내지 340℃의 고비점 지방족석유계 용제를 혼합하여 사용하는 것이 바람직하다. 상기 지방족탄화수소계 용제와 글리콜에테르계 용제의 사용량은 수불식 요판잉크 전체 조성물에 대하여 각각 3 내지 7 중량% 및 2 내지 5 중량% 사용한다.On the other hand, it is preferable to use an aliphatic hydrocarbon solvent and a glycol ether solvent in the water-insoluble intaglio ink composition having both magnetic properties and infrared absorption properties according to the present invention for adjusting ink properties, the glycol ether solvent One or more selected from the group consisting of diethylene glycol monobutyl ether, diethylene glycol monoethyl ether, and diethylene glycol monomethyl ether may be used, and aliphatic hydrocarbon solvents may improve gas phase stability and tackiness. It is preferable to use a mixture of high boiling point aliphatic petroleum solvents having a boiling point range of 290 to 340 ° C. The aliphatic hydrocarbon solvent and the glycol ether solvent may be used in an amount of 3 to 7 wt% and 2 to 5 wt% based on the total amount of the insoluble intaglio ink.

또한 본 발명에 따른 자성특성과 적외선 흡수 특성을 동시에 가지는 수불식 요판잉크 조성물은 뒷묻음 방지 효과를 향상시키기 위해 왁스를 포함하며, 본 발명의 잉크 조성물에 포함되는 왁스는 몬탄에스테르 석검왁스 단독 사용보다 파라핀왁스를 혼용함이 바람직하며, 특히 상기 왁스는 내마모성, 뒤묻음적성, 전이성, 불식용액에 의한 분산적성 등의 향상을 위하여 융점 68 내지 71℃의 파라핀왁스와 융점 98 내지 105℃, 산값 10 내지 15, 비누화값 120 내지 150 의 몬탄에스테르 석검왁스를 1: 3.5 내지 4.5 중량비의 혼합한 것이 가장 바람직하며, 상기 혼합비로 혼합 된 혼합왁스는 수불식 요판잉크 전체 조성물에 대하여 5 내지 6 중량%로 사용하는것이 바람직하다.In addition, the water-insoluble intaglio ink composition having both magnetic properties and infrared absorption properties according to the present invention includes a wax to improve the anti-backing effect, and the wax contained in the ink composition of the present invention is better than using montan ester stone gum wax alone. It is preferable to use paraffin wax, and in particular, the wax has a melting point of 68 to 71 ° C. and a melting point of 98 to 105 ° C. and an acid value of 10 to 10 to improve abrasion resistance, burial resistance, transferability, dispersibility by insoluble solution, and the like. 15, it is most preferable to mix the montan ester stone gum wax having a saponification value of 120 to 150 in a ratio of 1: 3.5 to 4.5, and the mixed wax mixed at the above mixing ratio is used in an amount of 5 to 6% by weight based on the total composition of the water insoluble intaglio ink. It is desirable to.

착색안료는 잉크제조 분야에 있어서, 통상적으로 사용되는 청색, 적색, 황색 등의 안료를 포함하며, 상기 착색안료의 사용량은 7 내지 12 중량%가 바람직하며, 사용량이 7 중량% 미만이면 잉크의 농도가 낮아 색상효과가 미흡하게 되고, 12 중량% 초과하면 불식적성이 미흡한 문제점이 있다. 또한 체질안료는 보통 충진제로 알려져 있으며, 바람직하게는 탄산칼슘, 황산바륨, 탈크 또는 이산화규소 중에서 선택된 어느 하나를 사용하며, 상기 체질안료의 사용량은 20 내지 25 중량%가 바람직하고, 20 중량%미만이면 불식적성이 미흡하고 잉크의 물성조정이 곤란하여 인쇄적성에 문제점이 있으며, 25 중량%초과하면 잉크의 내마모성 불량, 인쇄판 마모 등의 문제점이 발생한다.The coloring pigments include pigments such as blue, red, yellow, and the like, which are commonly used in the field of ink manufacturing, and the amount of the coloring pigment is preferably 7 to 12% by weight, and the amount of the ink is less than 7% by weight. Lower color effect is insufficient, if more than 12% by weight there is a problem inadequate inadequate. In addition, the extender pigment is commonly known as a filler, preferably any one selected from calcium carbonate, barium sulfate, talc or silicon dioxide, the amount of the extender pigment is preferably 20 to 25% by weight, less than 20% by weight There is a problem in printability due to insufficient incorrosiveness and difficult to adjust the physical properties of the ink. If it exceeds 25% by weight, problems such as poor wear resistance of the ink and wear of the printing plate occur.

또한 분산제 4 내지 7 중량%, 건조제 0.5 내지 1.5 중량% 및 탈수피마자유지방산 1 내지 3 중량%를 더 포함할 수 있다.In addition, the dispersant may further comprise 4 to 7% by weight, desiccant 0.5 to 1.5% by weight and dehydrated castor oil fatty acid 1 to 3% by weight.

본 발명에 따른 자성특성과 적외선 흡수 특성을 동시에 가지는 수불식 요판잉크 조성물은 적외선 흡수 안료 1 내지 3중량％; 자성안료 8 내지 12중량%; 우레탄변성 알키드바니시 15 내지 25중량％; 알키드수지 바니시 15내지 25중량%; 지방족탄화수소계 용제 3 내지 7중량％; 글리콜에테르계 용제 2 내지 5중량％; 왁스 5 내지 6중량％; 분산제 4 내지 7중량％; 착색안료 7 내지 12중량%; 체질안료 20 내지 25중량%; 건조제 0.5 내지 1.5중량％; 및 탈수피마자유지방산 1 내지 3 중량%; 로 이루어진다.The water-insoluble intaglio ink composition having both magnetic properties and infrared absorption properties according to the present invention comprises 1 to 3% by weight of an infrared absorbing pigment; Magnetic pigment 8 to 12% by weight; 15-25 weight% of urethane-modified alkyd varnishes; Alkyd resin varnishes 15 to 25% by weight; 3 to 7% by weight of an aliphatic hydrocarbon solvent; 2 to 5% by weight of a glycol ether solvent; 5 to 6 weight percent wax; 4 to 7% dispersant; Coloring pigments 7 to 12% by weight; Sieving pigment 20 to 25% by weight; 0.5 to 1.5 weight percent of a desiccant; And 1-3% by weight of dehydrated castor oil fatty acid; Is made of.

한편, 본 발명에 따른 자성특성과 적외선 흡수 특성을 동시에 가지는 수불식 요판잉크 조성물로 은행권 및 각종 유가증권의 적어도 일면의 일부분을 인쇄하여 인쇄된 은행권이나 유가증권은 내용제성이 우수하고 인쇄물 고유의 색상을 유지하고 800 내지 900 nm의 파장범위에서 최대 흡광도(λmax)를 나타내는 것으로부터 위변조 은행권 및 유가증권을 식별할 수 있다.On the other hand, the banknote or securities printed by printing at least a portion of the banknotes and various securities as a water-insoluble intaglio ink composition having both magnetic properties and infrared absorption characteristics according to the present invention has excellent solvent resistance and intrinsic color of printed matter. Forgery banknotes and securities can be discerned from maintaining and showing the maximum absorbance (λ max ) in the wavelength range from 800 to 900 nm.

이하, 실시예 및 비교예를 통하여 발명의 구성 및 작용효과를 보다 구체적으로 설명한다. 그러나, 본 발명이 이들 실시예 및 비교예에만 한정되는 것이 아님은 당업자에게 있어서 자명한 사실이다.Hereinafter, the constitution and effects of the invention will be described in more detail with reference to Examples and Comparative Examples. However, it is apparent to those skilled in the art that the present invention is not limited only to these examples and comparative examples.

실시예 및 비교예는 인쇄적성과 적외선 흡수 및 자성 특성의 실험 목적으로 특정한 색상을 지정하지 않았고, 잉크 조성은 요구되는 색상에 따라 다양하게 변경할 수 있으며, 비교예는 적외선 흡수 안료를 사용하지 않은 잉크로서 종전의 자성잉크에 해당한다.Examples and Comparative Examples did not specify a specific color for the purpose of experimentation of printability and infrared absorption and magnetic properties, the ink composition can be varied in accordance with the required color, Comparative Example is an ink that does not use an infrared absorbing pigment This corresponds to the previous magnetic ink.

자성안료로서 황색계열은 새한미디어 제품으로서 보자력(Hc); 385±10(Oe), 포화자속밀도(σs); 71~73(emu/g), pH; 2.7~3.6, 흡유량(OA); 6.5~8.0(㎖/20g), 표면적(BET); 24.5±1.5(㎡/g)의 특성을 갖는 Magnetic Iron Oxide Brown EP-060을 사용하였으며, 회색계열은 BASF사 제품으로 표면적 (BET); 0.4(㎡/g), 평균입자; 4~6(㎛), 비중; 7.7(g/㎤), 흡유량; 7.5(g oil/100g pigment), 최대잔류자속밀도(δm); 200(A ㎡/kg), 철분; Fe>97%(순도)인 Magnetic Pigment 025 BASF를 사용하였다. 또한 적외선 흡수 안료로는 대한민국 특허 등록번호 10-0528155로 등록된 폴리가교형 프탈로시아닌계 화합물로 λmax; 880㎚, pH; 5.5±1.5, 평균입자; 0.4~4㎛, 강열잔분; 8.9%의 특성을 갖는 씨엠에스테크놀로지(주)의 CMS Blue 2A-905를 사용하였다.Yellow pigment as magnetic pigment is coercive force (Hc) as Saehan media product; 385 ± 10 (Oe), saturation magnetic flux density (σs); 71-73 (emu / g), pH; 2.7 to 3.6, oil absorption (OA); 6.5-8.0 (ml / 20g), surface area (BET); Magnetic Iron Oxide Brown EP-060 having a characteristic of 24.5 ± 1.5 (m2 / g) was used, and the gray series is BASF Co. 0.4 (m 2 / g), average particle; 4 to 6 µm, specific gravity; 7.7 (g / cm 3), oil absorption; 7.5 g oil / 100 g pigment, maximum residual magnetic flux density (? M); 200 (A m 2 / kg), iron powder; Magnetic Pigment 025 BASF with Fe> 97% (purity) was used. In addition, the infrared absorbing pigment is a poly-crosslinked phthalocyanine-based compound registered in Korea Patent Registration No. 10-0528155 λ max ; 880 nm, pH; 5.5 ± 1.5, average particle; 0.4 ~ 4㎛, ignition residue; CMS Blue 2A-905 of CMS Technology Co., Ltd. having a characteristic of 8.9% was used.

또한 인쇄적성을 충족시키기 위하여, 전색제로서 수불식적성이 우수한 우레탄변성알키드바니시와 알키드바니시를 사용하고, 잉크의 물성 조정과 인쇄적성, 건조성, 내구성, 기상안정성, 마모성 등의 특성을 유지하기 위하여 지방족탄화수소계 용제와 글리콜에테르계 용제, 분산제, 건조제, 왁스 등의 원료를 사용하였으며, 잉크 색상은 은행권 인쇄에 사용하는 색상중 일부를 선정하여 실험을 실시하였다.In addition, in order to satisfy printability, urethane-modified alkyd varnish and alkyd varnish with excellent water-information properties are used as a colorant, and in order to maintain properties such as adjusting ink properties, printability, dryness, durability, weather stability, and wearability, etc. Raw materials such as aliphatic hydrocarbon solvents, glycol ether solvents, dispersants, desiccants, and waxes were used. The ink color was tested by selecting some of the colors used for banknote printing.

[실시예 1 및 비교예 1] Magnetic iron oxide brown을 이용한 황색잉크Example 1 and Comparative Example 1 Yellow ink using a magnetic iron oxide brown

하기 표 1에 기재된 성분들을 기재된 양만큼씩 혼합한 후 연육기에서 4~5회 연육하여 요판 인쇄적성에 적합한 황색잉크 조성물을 제조하였다.To the yellow ink composition suitable for intaglio printing suitability was prepared by mixing the ingredients shown in Table 1 by the amount described, followed by four to five times in a meat grinder.

[표 1]TABLE 1

Figure 112006046886473-pat00002
Figure 112006046886473-pat00002

[실시예 2 및 비교예 2] Magnetic iron oxide brown을 이용한 적색잉크[Example 2 and Comparative Example 2] Red ink using Magnetic iron oxide brown

하기 표 2에 기재된 성분들을 기재된 양만큼씩 혼합한 후 연육기에서 4~5회 연육하여 요판 인쇄적성에 적합한 적색잉크 조성물을 제조하였다.The ingredients shown in Table 2 were mixed by the amount described, followed by four to five times meat preparation in a meat grinder to prepare a red ink composition suitable for intaglio printing suitability.

[표 2]TABLE 2

Figure 112006046886473-pat00003
Figure 112006046886473-pat00003

[실시예 3 및 비교예 3] Magnetic iron oxide brown을 이용한 청색잉크Example 3 and Comparative Example 3 Blue Ink Using Magnetic Iron Oxide Brown

하기 표 3에 기재된 성분들을 기재된 양만큼씩 혼합한 후 연육기에서 4~5회 연육하여 요판 인쇄적성에 적합한 청색잉크 조성물을 제조하였다.After mixing the ingredients described in Table 3 by the amount described, and then four to five times in a meat grinder to prepare a blue ink composition suitable for intaglio printability.

[표 3]TABLE 3

Figure 112006046886473-pat00004
Figure 112006046886473-pat00004

[실시예 4 및 비교예 4] Magnetic pigment 025를 이용한 황색잉크Example 4 and Comparative Example 4 Yellow ink using a magnetic pigment 025

하기 표 4에 기재된 성분들을 기재된 양만큼씩 혼합한 후 연육기에서 4~5회 연육하여 요판 인쇄적성에 적합한 황색잉크 조성물을 제조하였다.To the yellow ink composition suitable for intaglio printing suitability was prepared by mixing the ingredients shown in Table 4 by the amount described, and then four to five times in a meat grinder.

[표 4]TABLE 4

Figure 112006046886473-pat00005
Figure 112006046886473-pat00005

[실시예 5 및 비교예 5] Magnetic pigment 025를 이용한 적색잉크Example 5 and Comparative Example 5 Red ink using Magnetic pigment 025

하기 표 5에 기재된 성분들을 기재된 양만큼씩 혼합한 후 연육기에서 4~5회 연육하여 요판 인쇄적성에 적합한 적색잉크 조성물을 제조하였다.After mixing the ingredients described in Table 5 by the amount described, and then four to five times in a meat grinder to prepare a red ink composition suitable for intaglio printability.

[표 5]TABLE 5

Figure 112006046886473-pat00006
Figure 112006046886473-pat00006

[실시예 6 및 비교예 6] Magnetic pigment 025를 이용한 청색잉크Example 6 and Comparative Example 6 Blue Ink Using Magnetic Pigment 025

하기 표 6에 기재된 성분들을 기재된 양만큼씩 혼합한 후 연육기에서 4~5회 연육하여 요판 인쇄적성에 적합한 청색잉크 조성물을 제조하였다.To the blue ink composition suitable for intaglio printing suitability was prepared by mixing the ingredients shown in Table 6 by the amount described, followed by 4 to 5 times in the meat grinder.

[표 6]TABLE 6

Figure 112006046886473-pat00007
Figure 112006046886473-pat00007

상기 실시예 및 비교예에서 사용되는 자성안료에 적외선 흡수 안료의 첨가량에 따른 IR 스펙트럼을 도 3 및 도 5에 나타내었고, IR wiewer 특성을 도 4 및 도 6에 나타내었다. 상기 도 3 및 도 5로부터 자성안료에 적외선 흡수 안료의 첨가함으로써 800 내지 900 nm에서 최대 흡광도를 나타내는 것을 알 수 있었으며, 도 4 및 도 6으로부터 자성안료에 적외선 흡수 안료를 첨가사용함으로써 색상을 조절할 수 있음을 알 수 있었다. 이는 상기 실시예 1 내지 6 및 비교예 1 내지 6에서 제조된 잉크 조성물의 IR 스펙트럼(도 7, 9, 11, 13, 15 및 17) 및 IR viewer 특성(도 8, 10, 12, 14, 16 및 18)에서도 확인할 수 있었다.IR spectra of the magnetic pigments used in Examples and Comparative Examples according to the addition amount of the infrared absorbing pigment are shown in FIGS. 3 and 5, and IR wiewer characteristics are shown in FIGS. 4 and 6. It can be seen from FIG. 3 and FIG. 5 that the maximum absorbance is shown at 800 to 900 nm by adding the infrared absorbing pigment to the magnetic pigment, and the color can be adjusted by using the infrared absorbing pigment to the magnetic pigment from FIGS. 4 and 6. I could see that. The IR spectra (Figs. 7, 9, 11, 13, 15 and 17) and IR viewer properties (Figs. 8, 10, 12, 14, 16) of the ink compositions prepared in Examples 1 to 6 and Comparative Examples 1 to 6 were used. And 18).

또한 본 발명에 따라 자성안료와 적외선 흡수 안료를 함유하는 실시예 1 내지 6의 잉크는 최신의 요판인쇄기에서 인쇄한 결과 잉크전이성, 불식적성, 인쇄물 선예성, 무간지적성 등 제반 인쇄적성과 내약품성, 내구성 등이 양호하였으며, 각각의 잉크는 상기 도 7, 9, 11, 13, 15 및 17에 나타낸 바와 같이 차별화되는 적외선 흡수 특성을 갖고 있으며, 동시에 자성특성을 가지고 있는 복합 기능을 갖음이 입증되었다.In addition, according to the present invention, the inks of Examples 1 to 6 containing the magnetic pigment and the infrared absorbing pigment were printed on the latest intaglio printing presses, and the printability and chemical resistance, such as ink transferability, incorruption, print sharpness, and paperlessness, etc. , Durability, etc., each ink has a different infrared absorption characteristics as shown in Figure 7, 9, 11, 13, 15 and 17, and at the same time proved to have a complex function having magnetic properties .

이상에서 살펴본 바와 같이, 본 발명의 적외선 흡수 특성과 자성 특성의 복합기능을 갖는 수불식 요판잉크 조성물로 인쇄된 은행권이나 유가 증권은 위변조방지 기능과 진위감별 요소로서의 특징을 가질 수 있다.As described above, banknotes or securities printed with a water-insoluble intaglio ink composition having a complex function of infrared absorption characteristics and magnetic properties of the present invention may have features as anti-counterfeiting function and authenticity discrimination element.

또한, 칼라복사기와 컴퓨터 주변기기의 발달로 인하여 화폐의 위변조 수법도 고급화 및 다양화되는 현 시점에서 복합기능의 특성을 갖는 잉크나 물질은 인쇄하는 과정에서 적용하는 것이 가장 이상적인 방법이다.In addition, since the development of color copiers and computer peripherals is also advanced and diversified, the most suitable method is to apply ink or materials having complex characteristics in the printing process.

또한 자성잉크의 특성은 화폐의 기능 중 현급지급기, 자동판매기, 계수기 등의 금융자동화기기에서 반드시 요구되므로 모든 국가의 화폐에 적용하고 있으며, 복합기능을 갖는 잉크 제조 기술은 선진기술에 해당된다.In addition, the characteristics of magnetic ink are required in financial automation equipment such as cash dispensers, vending machines, and counters among the functions of money, so they are applied to all countries' currencies. Ink manufacturing technology with multiple functions is an advanced technology.

한편, 상기에서는 본 발명의 바람직한 실시예들을 참조하여 설명하였지만, 해당 기술분야에서 통상의 지식을 가진 자라면 하기의 청구의 범위에 기재된 본 발 명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다.On the other hand, while the above has been described with reference to the preferred embodiments of the present invention, those skilled in the art to which the present invention pertains without departing from the spirit and scope of the present invention described in the claims below It will be understood that modifications and changes can be made.

Claims (25)

수불식 요판잉크 전체 조성물에 대하여 최대 흡수 파장(λmax)이 800 내지 900nm의 범위의 적외선 흡수 안료로 pH; 5.5±1.5, 평균입자; 0.4~4(㎛), 강열잔분; 8.9%의 특성을 갖는 하기 구조로 표시되는 폴리가교형 프탈로시아닌계 화합물 1 내지 3 중량%; 보자력(Hc); 385±10(Oe), 포화자속밀도(σs); 71~73(emu/g), pH; 2.7~3.6, 흡유량(OA); 6.5~8.0(㎖/20g), 표면적(BET); 24.5±1.5(㎡/g)의 특성을 갖는 황색계열의 자성안료, 표면적 (BET); 0.4(㎡/g), 평균입자; 4~6(㎛), 비중; 7.7(g/㎤), 흡유량; 7.5(g oil/100g pigment), 최대잔류자속밀도(δm); 200(A ㎡/kg), 철분; Fe>97%(순도)의 특성을 갖는 회색계열의 자성안료 또는 황색계열 자성안료와 회색계열 자성안료의 혼합 자성안료 8 내지 12 중량%; 우레탄변성 알키드바니시, 에폭시변성 알키드바니시, 폴리에스텔변성 알키드바니시, 로진변성 알키드바니시, 멜라민변성 알키드바니시, 아마이드변성 알키드바니시, 아크릴변성 알키드바니시로 이루어진 군으로부터 선택된 1종 이상 15 내지 25 중량%; 및 알키드수지 바니시, 페놀수지 바니시, 요소수지 바니시, 멜라민수지 바니시, 폴리우레탄수지 바니시로 이루어진 군에서 선택된 1종 이상 15 내지 25 중량%;를 함유하는 것을 특징으로 하는 자성 특성과 적외선 흡수 특성을 동시에 갖는 수불식 요판잉크 조성물.The total absorption wavelength (λ max ) for the entire water-insoluble intaglio ink composition is an infrared absorbing pigment in the range of 800 to 900 nm; 5.5 ± 1.5, average particle; 0.4-4 (micrometer), ignition residue; 1-3 wt% of a polycrosslinked phthalocyanine compound represented by the following structure having a property of 8.9%; Coercive force (Hc); 385 ± 10 (Oe), saturation magnetic flux density (σs); 71-73 (emu / g), pH; 2.7 to 3.6, oil absorption (OA); 6.5-8.0 (ml / 20g), surface area (BET); Yellowish magnetic pigment with a characteristic of 24.5 ± 1.5 (m 2 / g), surface area (BET); 0.4 (m 2 / g), average particle; 4 to 6 µm, specific gravity; 7.7 (g / cm 3), oil absorption; 7.5 g oil / 100 g pigment, maximum residual magnetic flux density (? M); 200 (A m 2 / kg), iron powder; 8-12 wt% of a gray-based magnetic pigment or a yellow-based magnetic pigment and a mixed magnetic pigment of a gray-based magnetic pigment having a Fe> 97% (purity) property; 15 to 25% by weight of at least one selected from the group consisting of urethane-modified alkyd varnishes, epoxy-modified alkyd varnishes, polyester-modified alkyd varnishes, rosin-modified alkyd varnishes, melamine-modified alkyd varnishes, amide-modified alkyd varnishes, and acrylic-modified alkyd varnishes; And at least 15 to 25 wt% of alkyd resin varnishes, phenolic resin varnishes, urea resin varnishes, melamine resin varnishes, polyurethane resin varnishes, and at least 15 to 25% by weight. Water-insoluble intaglio ink composition having.
Figure 112008004442118-pat00030
Figure 112008004442118-pat00030
 [상기 식에서 M1과 M2는 각각 무금속, 금속, 금속 산화물 또는 금속 할라이드에서 선택된 것으로서 서로 같거나 다른 것일 수 있으며, R1 내지 R16은 각각 수소원자, 할로겐원자, 수산기, 아미노기, 히드록시술포닐기, 아미노술포닐기, 알킬기, 탄소수 1∼20의 치환기를 갖는 알킬기, SR17, SR18, OR19, NHR20 또는 NHR21에서 선택된 것으로 각각 동일하거나 다른 것일 수 있으며, 여기서, R17은 치환기를 가진 페닐기, 알킬기 또는 탄소수 1∼20의 알킬기이고, R18은 탄소수 1∼20의 알콕시기를 가진 페닐기이며, R19, R20은 각각 치환기를 가진 페닐기, 아릴알킬기 또는 탄소수 1∼20의 알킬기이고, R21은 치환기를 가진 탄소수 1∼20의 알킬기이며, n은 1∼20의 정수이다.][Wherein M 1 and M 2 are each selected from a metal free, metal, metal oxide or metal halide, and may be the same or different from each other, and R 1 to R 16 are each a hydrogen atom, a halogen atom, a hydroxyl group, an amino group, or a hydroxyl group; Selected from a sulfonyl group, an aminosulfonyl group, an alkyl group, an alkyl group having 1 to 20 carbon atoms, SR 17 , SR 18 , OR 19 , NHR 20, or NHR 21 , and each of R 17 is A phenyl group having an substituent, an alkyl group or an alkyl group having 1 to 20 carbon atoms, R 18 is a phenyl group having an alkoxy group having 1 to 20 carbon atoms, and R 19 and R 20 are each a phenyl group having an substituent, an arylalkyl group or an alkyl group having 1 to 20 carbon atoms R 21 is an alkyl group having 1 to 20 carbon atoms having a substituent, and n is an integer of 1 to 20.] 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 제 1항에 있어서,The method of claim 1, 상기 우레탄변성 알키드바니시는 산가 30 내지 35, 점도 300 내지 400poise(25℃), 중량평균 분자량 20,000 내지 25,000이고; 알키드수지 바니시는 산가 65 내지 70, 점도 400 내지 700poise(25℃), 중량평균 분자량 8,000 내지 12,000;인 것을 특징으로 하는 자성 특성과 적외선 흡수 특성을 동시에 갖는 수불식 요판잉크 조성물.The urethane-modified alkyd varnish has an acid value of 30 to 35, a viscosity of 300 to 400 poise (25 ° C.), and a weight average molecular weight of 20,000 to 25,000; Alkyd resin varnish has an acid value of 65 to 70, a viscosity of 400 to 700 poise (25 ℃), a weight average molecular weight of 8,000 to 12,000; water-insoluble intaglio ink composition having both magnetic properties and infrared absorption properties at the same time. 제 12항에 있어서,The method of claim 12, 상기 우레탄변성 알키드바니시와 알키드수지 바니시를 1:1 내지 1:1.5 중량비로 사용하는 것을 특징으로 하는 자성 특성과 적외선 흡수 특성을 동시에 갖는 수불식 요판잉크 조성물.The urine-modified alkyd varnish and the alkyd resin varnish is a water-insoluble intaglio ink composition having both magnetic properties and infrared absorption characteristics, characterized in that using a weight ratio of 1: 1 to 1: 1.5. 제 1항에 있어서,The method of claim 1, 지방족탄화수소계 용제; 글리콜에테르계 용제; 왁스; 분산제; 착색안료; 체질안료; 건조제; 및 탈수피마자유지방산;을 더 포함하는 것을 특징으로 하는 자성 특성과 적외선 흡수 특성을 동시에 갖는 수불식 요판잉크 조성물.Aliphatic hydrocarbon solvents; Glycol ether solvents; Wax; Dispersants; Pigmented pigments; Sieving pigments; drier; And dehydrated castor oil fatty acid; and a water-insoluble intaglio ink composition having both magnetic properties and infrared absorption properties. 제 14항에 있어서,The method of claim 14, 상기 지방족탄화수소계 용제는 비점범위가 290 내지 340℃인 고비점 지방족석유계 용제를 수불식 요판잉크 전체 조성물에 대하여 3 내지 7 중량% 사용하는 것을 특징으로 하는 자성 특성과 적외선 흡수 특성을 동시에 갖는 수불식 요판잉크 조성물.The aliphatic hydrocarbon-based solvent is a water having both magnetic properties and infrared absorption characteristics, characterized in that a high boiling point aliphatic petroleum solvent having a boiling point range of 290 to 340 ° C. is used in an amount of 3 to 7% by weight based on the total number of water-insoluble intaglio inks. Intaglio intaglio ink composition. 제 14항에 있어서,The method of claim 14, 상기 글리콜에테르계 용제는 디에틸렌글리콜 모노부틸에테르, 디에틸렌글리콜 모노에틸에테르, 디에틸렌글리콜 모노메틸에테르로 이루어진 군에서 선택되는 1종 이상을 수불식 요판잉크 전체 조성물에 대하여 2 내지 5 중량% 사용하는 것을 특징으로 하는 자성 특성과 적외선 흡수 특성을 동시에 갖는 수불식 요판잉크 조성물.The glycol ether solvent is used at least one selected from the group consisting of diethylene glycol monobutyl ether, diethylene glycol monoethyl ether, diethylene glycol monomethyl ether 2 to 5% by weight of the total composition A water-insoluble intaglio ink composition having both magnetic properties and infrared absorption characteristics at the same time. 제 14항에 있어서,The method of claim 14, 상기 왁스는 몬탄에스테르 석검왁스와 파라핀왁스의 혼합물인 것을 특징으로 하는 자성 특성과 적외선 흡수 특성을 동시에 갖는 수불식 요판잉크 조성물.The wax is a water-insoluble intaglio ink composition having both magnetic properties and infrared absorption characteristics, characterized in that the mixture of montan ester stone gum wax and paraffin wax. 제 17항에 있어서,The method of claim 17, 상기 왁스는 융점 68 내지 71℃의 파라핀왁스와 융점 98 내지 105℃, 산값 10 내지 15, 비누화값 120 내지 150의 몬탄에스테르 석검왁스를 1:3.5 내지 4.5 중량비로 혼합한 혼합왁스를 수불식 요판잉크 전체 조성물에 대하여 5 내지 6 중량% 사용하는 것을 특징으로 하는 자성 특성과 적외선 흡수 특성을 동시에 갖는 수불식 요판잉크 조성물.The wax is a water-insoluble intaglio ink in which a mixed wax obtained by mixing paraffin wax having a melting point of 68 to 71 ° C., a montan ester stone gum wax having a melting point of 98 to 105 ° C., an acid value of 10 to 15, and a saponification value of 120 to 150 in a weight ratio of 1: 3.5 to 4.5. Water-insoluble intaglio ink composition having both magnetic properties and infrared absorption properties, characterized in that 5 to 6% by weight based on the total composition. 제 1항에 있어서,The method of claim 1, 지방족탄화수소계 용제 3 내지 7중량％; 글리콜에테르계 용제 2 내지 5중량％; 왁스 5 내지 6중량％; 분산제 4 내지 7중량％; 착색안료 7 내지 12중량%; 체질안료 20 내지 25중량%; 건조제 0.5 내지 1.5중량％; 및 탈수피마자유지방산 1 내지 3 중량%;을 더 함유하는 것을 특징으로 하는 자성 특성과 적외선 흡수 특성을 동시에 갖는 수불식 요판잉크 조성물.3 to 7% by weight of an aliphatic hydrocarbon solvent; 2 to 5% by weight of a glycol ether solvent; 5 to 6 weight percent wax; 4 to 7% dispersant; Coloring pigments 7 to 12% by weight; Sieving pigment 20 to 25% by weight; 0.5 to 1.5 weight percent of a desiccant; And 1 to 3% by weight of dehydrated castor oil fatty acid. 제 1항 또는 제 12항 내지 제 19항에서 선택되는 어느 한 항에 따른 자성 특성과 적외선 흡수 특성을 동시에 갖는 수불식 요판잉크 조성물로 인쇄된 은행권.A banknote printed with a water-insoluble intaglio ink composition having both magnetic properties and infrared absorption properties according to any one of claims 1 or 12 to 19. 제 20항의 은행권의 적외선 흡수 특성과 자성 특성으로 위변조 은행권을 식별하는 방법.A method for identifying counterfeit banknotes by means of infrared absorption and magnetic properties of the banknote of claim 20. 제 21항에 있어서,The method of claim 21, 적외선 최대 흡수 파장(λmax)가 800 내지 900nm인 것을 특징으로 하는 위변조 은행권을 식별하는 방법.A method for identifying a forgery banknote, characterized in that the infrared maximum absorption wavelength (λ max ) is between 800 and 900 nm. 제 1항 또는 제 12항 내지 제 19항에서 선택되는 어느 한 항에 따른 자성 특성과 적외선 흡수 특성을 동시에 갖는 수불식 요판잉크 조성물로 인쇄된 유가증권.A securities printed with a water-insoluble intaglio ink composition having both magnetic properties and infrared absorption properties according to any one of claims 1 or 12 to 19 selected. 제 23항의 유가증권의 적외선 흡수 특성과 자성 특성으로 위변조 유가증권을 식별하는 방법.A method for identifying counterfeit securities by infrared absorption and magnetic properties of the securities of claim 23. 제 24항에 있어서,The method of claim 24, 적외선 최대 흡수 파장(λmax)가 800 내지 900nm인 것을 특징으로 하는 위변조 유가증권을 식별하는 방법.A method for identifying counterfeit security, characterized in that the infrared maximum absorption wavelength (λ max ) is between 800 and 900 nm.
KR1020060059819A 2006-06-29 2006-06-29 The water wiping intaglio ink composition with magnetic and infrared absorption characteristics KR100825270B1 (en)