KR100824210B1 - The percolate paving material hardener where the loess and the tree are included and the manufacturing method - Google Patents
The percolate paving material hardener where the loess and the tree are included and the manufacturing method Download PDFInfo
- Publication number
- KR100824210B1 KR100824210B1 KR1020070119700A KR20070119700A KR100824210B1 KR 100824210 B1 KR100824210 B1 KR 100824210B1 KR 1020070119700 A KR1020070119700 A KR 1020070119700A KR 20070119700 A KR20070119700 A KR 20070119700A KR 100824210 B1 KR100824210 B1 KR 100824210B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- stirring
- wood
- hardener
- manufacturing
- Prior art date
Abstract
Description
본 발명은 황토와 목재가 포함된 투수(透水)포장재용 경화제 및 그 제조방법에 관한 것으로 더욱 상세히는 황토와, 섬유질이 유지될 수 있도록 가늘게 찢은 목재, 모래와, 시멘트를 주재료로 하는 포장재가 재료 간 결속이 우수하고 수분에 대한 내구성을 지니며, 견고한 강성을 유지할 수 있도록 하는 황토와 목재가 포함된 투수(透水)포장재용 경화제 및 그 제조방법에 관한 것이다.The present invention relates to a hardener for a permeable packaging material containing ocher and wood, and to a method for manufacturing the same, and more particularly, ocher, packaging material mainly made of wood, sand, and cement, torn to maintain fiber. The present invention relates to a hardening agent for permeable packaging material containing ocher and wood, which has excellent interlocking properties, has moisture resistance, and maintains rigid rigidity, and a manufacturing method thereof.
일반적으로 토양경화제에 대해서는 특허출원 제1984-0006714호, 특허출원 제2002-0084762호, 특허출원 제2005-0015642호 등에서 언급이 되어 있으나, 상술된 바와 같은 경화제는 토양 특히 황토와 목재류를 교반시켜 고형화시킬 수 없었으며, 고형화가 된다고 하더라도 강성과 내구성을 제공해주지 못해 부서지는 경우가 많았다. 뿐만 아니라 본원 출원권자가 동일자로 출원한 특허출원 제2007-011968호에서 기술된 바와 같이 고형화 된 포장블럭에 투수(透水)가 되지 못하는 문제점이 있었다.Generally, the soil hardener is mentioned in Patent Application No. 1984-0006714, Patent Application No. 2002-0084762, Patent Application No. 2005-0015642, etc., but the curing agent as described above is solidified by stirring the soil, especially loess and wood. It could not be made, and even if solidified, it was often broken because it could not provide rigidity and durability. In addition, there was a problem in that the application of the applicant for the same patent application No. 2007-011968, which is not a pitcher (solid water) in the solidified paving block.
이에 본 발명에서는 상기와 같은 문제점을 일소키 위해 안출 한 것으로 본원출원권자가 출원한 포장재의 재료 즉, 황토, 가늘게 찢은 목재, 모래, 시멘트가 상호 견고한 결합이 되어 강성과 내구성을 지닐 수 있도록 함은 물론, 포장재가 고형화 된 후에 투수(透水)가 될 수 있도록 하는 황토와 목재가 포함된 투수(透水)포장재용 경화제 및 그 제조방법을 제공함에 그 목적이 있다.Therefore, in the present invention, the material of the packaging material filed by the present applicant, that is, ocher, finely torn wood, sand, and cement, has been devised to solve the above problems, so that the rigidity and durability can be achieved. Of course, it is an object of the present invention to provide a hardening agent for a permeable packaging material containing ocher and wood and a method for manufacturing the same, so that the packaging material becomes a water permeable after it is solidified.
상기한 목적을 달성하기 위해 본 발명에서는 물 78~82중량%와, 규산 4~6중량%와, 점도제 4~6중량%와, 인 4~6중량%와, 분말화 한 곤충배설물 4~6중량% 를 준비하여 1차로 물과 규산을 전용교반기에 투입하여 150~180rpm의 속도로 160~200분간 교반을 하고, 상기 1차 교반에서 얻어진 재료에 점도제를 투입하여 150~180rpm의 속도로 50~70분간 2차 교반을 한 다음, 상기 2차 교반에서 얻어진 재료에 인을 투입하여 150~180rpm의 속도로 50~70분간 3차 교반을 한 후, 상기 3차 교반에서 얻어진 재료에 분말화 한 곤충배설물을 투입하여 150~180rpm의 속도로 50~70분간 4차 교반을 함으로써 본 발명에서 제공하는 경화제를 제공하는 것이다.In order to achieve the above object, in the present invention, 78 to 82% by weight of water, 4 to 6% by weight of silicic acid, 4 to 6% by weight of viscosity agent, 4 to 6% by weight of phosphorus, and powdered insect droppings 4 to Prepare 6% by weight of water and silicic acid into a dedicated stirrer first, and stirred for 160 to 200 minutes at a speed of 150 ~ 180rpm, a viscosity agent is added to the material obtained in the first stirring at a speed of 150 ~ 180rpm After 50-70 minutes of secondary agitation, phosphorus was added to the material obtained by the secondary agitation, followed by tertiary stirring for 50 to 70 minutes at a speed of 150 to 180 rpm, and then powdered to the material obtained by the third agitation. It is to provide a curing agent provided by the present invention by adding a insect excrement to the fourth stirring for 50 to 70 minutes at a speed of 150 ~ 180rpm.
본 발명에서 제공하는 황토와 목재가 포함된 투수포장재용 경화제 및 그 제조방법은 황토와 목재류가 포함된 환경친화적 포장재를 상호간에 긴밀한 결속 및 고형화가 되게 함으로써 우수한 강성과 내구성을 유지시켜줌은 물론, 고형화 된 포장블럭은 투수(透水)가 되도록 하는 효과가 있다.The hardening agent for a permeable packaging material containing the ocher and wood provided by the present invention and a method for manufacturing the same by maintaining the close rigidity and solidification of the environmentally friendly packaging material containing ocher and wood to each other, as well as solidification The paved block is effective to be a pitcher (透水).
이하, 첨부된 도면 및 바람직한 실시예에 따라 본 발명을 상세히 설명한다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings and preferred embodiments.
도 1은 본 발명의 바람직한 일실시예에 따른 제조공정도로서 본 발명에서 제공하는 황토와 목재가 포함된 투수포장재용 경화제는,1 is a manufacturing process diagram according to a preferred embodiment of the present invention, the hardener for permeable packaging material containing ocher and wood provided by the present invention,
물 78~82중량%와, 규산 4~6중량%와, 점도제 4~6중량%와, 인 4~6중량%와, 분말화 한 곤충배설물 4~6중량% 를 포함하여 이루어지는 것을 특징으로 한다.78 to 82% by weight of water, 4 to 6% by weight of silicic acid, 4 to 6% by weight of viscosity agent, 4 to 6% by weight of phosphorus, and 4 to 6% by weight of powdered insect droppings. do.
또한 황토와 목재가 포함된 투수 포장재용 경화제의 제조방법은,In addition, the manufacturing method of the hardener for permeable packaging material containing ocher and wood,
물 78~82중량%와, 규산 4~6중량%와, 점도제 4~6중량%와, 인 4~6중량%와, 분말화 한 곤충배설물 4~6중량% 를 준비 및 계근하는 단계;Preparing and weighing 78 to 82% by weight of water, 4 to 6% by weight of silicic acid, 4 to 6% by weight of viscosity agent, 4 to 6% by weight of phosphorus, and 4 to 6% by weight of powdered insect droppings;
상기 물과 규산을 전용교반기에 투입하여 150~180rpm의 속도로 160~200분간 1차 교반 하는 단계;Putting the water and silicic acid into a dedicated stirrer and performing first stirring for 160 to 200 minutes at a speed of 150 to 180 rpm;
상기 1차 교반에서 얻어진 재료에 점도제를 투입하여 150~180rpm의 속도로 50~70분간 2차 교반 하는 단계;Adding a viscous agent to the material obtained in the first stirring and performing a second stirring for 50 to 70 minutes at a speed of 150 to 180 rpm;
상기 2차 교반에서 얻어진 재료에 인을 투입하여 150~180rpm의 속도로 50~70분간 3차 교반 하는 단계;Adding phosphorus to the material obtained in the second stirring to perform third stirring for 50 to 70 minutes at a speed of 150 to 180 rpm;
상기 3차 교반에서 얻어진 재료에 분말화 한 곤충배설물을 투입하여 150~180rpm의 속도로 50~70분간 4차 교반 하는 단계;Putting the powdered insect droppings into the material obtained by the third stirring and stirring the fourth step for 50 to 70 minutes at a speed of 150 to 180 rpm;
상기 교반과정에서 얻어진 경화제를 밀폐용기에 밀봉 포장하는 단계;Sealing packaging the curing agent obtained in the stirring process in an airtight container;
를 포함하여 이루어지는 것을 특징으로 한다.Characterized in that comprises a.
특히 곤충배설물은 일정시간이 경과 하게 되면 고형화가되기 시작하는데 고형화된 곤충배설물을 분말화시킨 다음, 그 분말가루를 투입하여 경화제를 얻는 것이며, 곤충배설물은 점액성분이 있어 접착효과가 강하다.Insect excretion begins to solidify after a certain period of time, but the solidified insect excretion is powdered, and then the powder is added to obtain a hardening agent. Insect excretion has a mucus component, which has a strong adhesive effect.
실제 투수포장재를 제조할 때는 1 lot 개념으로 황토10kg, 목재30kg, 모래20kg, 시멘트 20kg, 경화제 40kg가 사용되기 때문에 본원에서 제조하는 경화제는 1회 제조시 500kg을 제조하여 보관 및 사용한다.When manufacturing the actual permeable packaging material, 10kg of loess, 30kg of wood, 20kg of sand, 20kg of cement, 40kg of hardener are used.
이때는 물 400kg에 규산, 점도제, 인, 곤충배설물을 각각 25kg씩 교반시켜서 제조 및 밀봉 보관할 수도 있고 곧 바로 현장 및 포장블럭 제조용으로 사용하면 된다.In this case, the mixture may be manufactured and sealed by stirring 25 kg of silicic acid, viscous agent, phosphorus, and insect excrement in water of 400 kg, respectively, or may be used immediately for field and packaging block manufacture.
한편, 점도제는 통상의 일반 점도제를 사용하면 무난하다.On the other hand, if a viscous agent is used, a normal general viscosity agent is acceptable.
도 1은 본 발명의 바람직한 일실시예에 따른 제조공정도1 is a manufacturing process according to a preferred embodiment of the present invention
Claims (2)