KR100822719B1 - Far infrared ray radiant composite fiber and clothes manufactured using the same - Google Patents

Far infrared ray radiant composite fiber and clothes manufactured using the same Download PDF

Info

Publication number
KR100822719B1
KR100822719B1 KR1020070045024A KR20070045024A KR100822719B1 KR 100822719 B1 KR100822719 B1 KR 100822719B1 KR 1020070045024 A KR1020070045024 A KR 1020070045024A KR 20070045024 A KR20070045024 A KR 20070045024A KR 100822719 B1 KR100822719 B1 KR 100822719B1
Authority
KR
South Korea
Prior art keywords
far
weight
infrared radiation
infrared ray
fiber
Prior art date
Application number
KR1020070045024A
Other languages
Korean (ko)
Inventor
권태문
Original Assignee
권태문
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 권태문 filed Critical 권태문
Priority to KR1020070045024A priority Critical patent/KR100822719B1/en
Application granted granted Critical
Publication of KR100822719B1 publication Critical patent/KR100822719B1/en

Abstract

Far-infrared ray-radiating textile and clothes manufactured by using the textile are provided to impart a health care function to the textile through radiation of far-infrared rays, by producing the textile where a far-infrared ray-radiating layer is deposited on a textile fabric. Far-infrared ray-radiating textile comprises a textile fabric, and a far-infrared ray-radiating layer(3) deposited on the far-infrared ray-radiating fabric. The far-infrared ray-radiating layer contains 30-90 wt% of selenium, 1-30 wt% of titanium, 1-30 wt% of germanium, 1-30 wt% of elvan, 1-30 wt% of loess, 1-30 wt% of jade, and 1-30 wt% of tourmaline. The far-infrared ray-radiating fabric is deposited through physical vapor deposition including vapor deposition and sputtering. Further, the Far-infrared ray-radiating textile comprises laminating on the far-infrared ray-radiating layer.

Description

원적외선 방사 섬유 및 이를 이용하여 제작된 의복{FAR INFRARED RAY RADIANT COMPOSITE FIBER AND CLOTHES MANUFACTURED USING THE SAME}FIR INFRARED RAY RADIANT COMPOSITE FIBER AND CLOTHES MANUFACTURED USING THE SAME}

도 1 및 도 2는 본 발명의 일 실시예에 따른 원적외선 방사 섬유의 사시도이다. 1 and 2 are perspective views of far-infrared radiation fibers according to an embodiment of the present invention.

< 도면의 주요 부분에 대한 부호의 설명 > <Description of Symbols for Main Parts of Drawings>

1: 섬유 원단 20: 원적외선 방사층1: textile fabric 20: far infrared ray emitting layer

본 발명은 원적외선 방사 섬유 및 이를 이용하여 제작된 의복에 관한 것으로, 섬유 원단에 셀레늄 입자를 코팅하여 원적외선을 방사하는 섬유의 제작을 통해 인체에 활력을 줄 수 있고, 이를 사용하는 사용자의 면역력을 높일 수 있는 원적외선 방사 섬유 및 이를 이용하여 제작된 의복에 관한 것이다.The present invention relates to a far-infrared radiation fiber and a garment produced using the same, which can give vitality to the human body by manufacturing selenium particles on the fabric to emit far-infrared rays, thereby enhancing the immunity of the user using the same. The present invention relates to far-infrared radiation fibers and garments made using the same.

일반적으로, 원적외선 섬유는 함유된 여러가지 광물질로 인하여 체온이나 외 부의 가시광선에 의해서, 인체의 체액이 흡수할 수 있는 파장대의 원적외선을 방사하게 되는데 이것이 우리 몸의 대부분을 차지하는 체액을 활성화시켜 보온, 온열 효과를 가져와 혈액순환 등에 영향을 주며 신체내에 땀을 분비시켜 신진대사를 촉진시키는 역할을 하는 것으로 알려져 있다.In general, far-infrared fiber emits far-infrared rays in the wavelength range that can be absorbed by human body fluids by body temperature or external visible light due to various minerals contained in it, which activates body fluids that occupy most of our body to keep warm and heat. It is known to have an effect on blood circulation and secrete sweat in the body to promote metabolism.

이와 같은 이유로 원적외선 물질을 이용한 제품들이 건축용, 섬유용, 산업용, 난방용, 식품용 등 여러분야에 응용이 되고 있다.For this reason, products using far-infrared materials are applied to all of you, such as construction, textile, industrial, heating, and food.

원적외선 섬유를 제조하는 종래의 방법들은 원적외선 효능을 발휘하는 물질로서 Al2O3 , MgO, SiO2, ZrO2 등의 천연맥 반석을 주로 사용하고 있는바, 상기 물질들은 모두 경도가 높은 물질이므로 제조공정상 설비의 마모를 일으킬 뿐만 아니라 입자의 모양과 크기가 불균일하므로 제사시 팩압을 상승시키는 등의 문제점을 가지고 있다.Conventional methods for producing far-infrared fibers mainly use natural veins such as Al 2 O 3 , MgO, SiO 2 , ZrO 2 as materials exhibiting far-infrared efficacy. In addition to causing wear of the normal equipment, the shape and size of the particles are non-uniform, so there is a problem such as increasing the pack pressure during sacrifice.

그리고, 종래의 원적외선 섬유는 섬유 원단에 원적외선 방사특성을 부여하는 것이 복잡하고 생산원가가 높을 뿐만아니라 상온에서 방사성이 미미하고, 원적외선 방사 코팅이 섬유의 촉감 및 외관을 손상시키며, 원적외선 방사 코팅이 쉽게 떨어져나가는 등의 단점이 있어서 그 적용에 많은 제한이 따른다.In addition, the conventional far-infrared fiber is not only complicated to give the far-infrared radiation characteristics to the fabric fabric, the production cost is high, the radiation is insignificant at room temperature, the far-infrared radiation coating damages the feel and appearance of the fiber, the far-infrared radiation coating is easy There are disadvantages, such as falling off, and so many restrictions apply to the application.

본 발명은 상기와 같은 문제점을 고려하여, 화학 기상 증착 및 물리 증착 법을 이용하여 섬유 원단에 원적외선을 방사하는 원적외선 방사층을 증착하여 원적외 선 방사를 통해 면역력을 향상시키고, 성인병과 스트레스 해소 및 피로 회복에 유익한 원적외선 방사 섬유 및 이를 이용하여 제작된 의복을 제공하는 것을 그 목적으로 한다.In view of the above problems, the present invention, by using a chemical vapor deposition and physical vapor deposition method to deposit a far-infrared radiation layer to the far-infrared radiation on the textile fabric to improve immunity through far-infrared radiation, and to relieve the adult disease and stress and It is an object of the present invention to provide far-infrared radiation fibers and garments made using the same, which are beneficial for fatigue recovery.

상술한 목적을 달성하기 위한 본 발명의 일측면은 섬유 원단 및 상기 섬유 원단 상에 증착된 원적외선 방사층을 포함하고, 상기 원적외선 방사층은 30 내지 90 중량%의 셀레늄, 1 내지 30 중량%의 티타늄, 1 내지 30중량%의 게르마늄, 1 내지 30 중량%의 맥반석, 1 내지 30 중량%의 황토, 1 내지 30 중량%의 옥과, 1 내지 30 중량%의 토르말린을 포함하는 것을 특징으로 하는 원적외선 방사 섬유를 제공한다. One aspect of the present invention for achieving the above object comprises a fiber fabric and a far-infrared radiation layer deposited on the fiber fabric, the far-infrared radiation layer is 30 to 90% by weight selenium, 1 to 30% by weight titanium Far-infrared radiation fiber comprising 1 to 30% by weight germanium, 1 to 30% by weight elvanite, 1 to 30% by weight ocher, 1 to 30% by weight jade and 1 to 30% by weight tourmaline. To provide.

상기 원적외선 방사층은 진공 증착 및 스퍼터링을 포함하는 물리 기상 증착법을 통해 증착되는 것을 특징으로 한다. The far-infrared radiation layer is deposited by physical vapor deposition including vacuum deposition and sputtering.

상기 원적외선 방사층 상에 마련된 라미네이팅지를 더 포함하는 것을 특징으로 한다. It further comprises a laminating paper provided on the far infrared ray emitting layer.

상기 원적외선 방사층은 세도우 마스크에 의해 상기 섬유 원단 상에 패터닝되는 것을 특징으로 한다. The far-infrared radiation layer is characterized in that it is patterned on the fiber fabric by a shadow mask.

또한, 본 발명의 다른 일 측면은 제1항 내지 제 4 항 중 어느 한 항의 원적외선 방사 섬유로 제작된 의복을 제공한다. Further, another aspect of the present invention provides a garment made of the far-infrared radiation fiber of any one of claims 1 to 4.

또한 본 발명의 또다른 일 측면은 섬유 원단을 마련하는 단계 및 물리 기상 증착법을 이용하여 상기 섬유 원단 상에 30 내지 90 중량%의 셀레늄, 1 내지 30 중량%의 티타늄, 1 내지 30중량%의 게르마늄, 1 내지 30 중량%의 맥반석, 1 내지 30 중량%의 황토, 1 내지 30 중량%의 옥과, 1 내지 30 중량%의 토르말린을 포함하는 원적외선 방사층을 형성하는 단계를 포함하는 것을 특징으로 하는 원적외선 방사 섬유 제작 방법을 제공한다. In still another aspect of the present invention, there is provided a step of preparing a fiber fabric and 30 to 90% by weight of selenium, 1 to 30% by weight of titanium, and 1 to 30% by weight of germanium on the fiber fabric by using physical vapor deposition. Far infrared rays comprising the step of forming a far infrared ray emitting layer comprising 1 to 30% by weight of elvan, 1 to 30% by weight of ocher, 1 to 30% by weight of jade, and 1 to 30% by weight of tourmaline. Provided is a method of producing a spinning fiber.

상기 물리 기상 증착법으로 진공 증착 및 스퍼터링을 사용하는 것을 특징으로 한다. Vacuum deposition and sputtering are used as the physical vapor deposition method.

이하에서 본 발명의 구성을 첨부된 도면에 의하여 상세히 설명하면 다음과 같다. Hereinafter, the configuration of the present invention will be described in detail with reference to the accompanying drawings.

도 1 및 도 2는 본 발명의 일 실시예에 따른 원적외선 방사 섬유의 사시도이다. 1 and 2 are perspective views of far-infrared radiation fibers according to an embodiment of the present invention.

도 1 및 도 2를 참조하면, 본 실시예에 따른 원적외선 방사 섬유는 섬유원단(1)과 섬유 원단(1) 상에 증착된 원적외선 방사층(3)을 포함한다. 1 and 2, the far-infrared radiation fiber according to the present embodiment includes a fiber fabric 1 and a far-infrared radiation layer 3 deposited on the fiber fabric 1.

섬유 원단(1)으로는 천연섬유, 재생 섬유 및 합성 섬유를 사용한다. 천연 섬유로는 면 섬유, 마섬유, 모 섬유 및 견 섬유를 사용할 수 있고, 재생 섬유로는 레이온 및 아세테이트를 사용할 수 있으며, 합성 섬유로는 나이론, 아크릴, 폴리에스테르 및 폴리우레탄 등을 사용할 수 있다. 물론, 폴리에스터섬유, 유리섬유, 아라미드섬유 및 내열 절연 기능성을 가진 섬유원단을 사용할 수도 있다. As the fiber fabric 1, natural fibers, recycled fibers and synthetic fibers are used. Cotton fibers, hemp fibers, wool fibers and silk fibers may be used as natural fibers, rayon and acetate may be used as regenerated fibers, and nylon, acrylic, polyester and polyurethane may be used as synthetic fibers. . Of course, it is also possible to use polyester fibers, glass fibers, aramid fibers and fiber fabrics with heat-resistant insulating functionality.

원적외선 방사층(3)은 증착 기술 즉, 코팅 기술을 이용하여 피코팅재인 섬유 원단(1)이 손상되지 않는 방법을 사용한다. 즉, 본 실시예에서는 저온에서 증착을 수행할 수 있는 물리 기상 증착법(Phisical Vapor Deposition; PVD)을 사용한다. 이러한 물리 기상 증착법으로 스퍼터링 (Sputtering), 전자빔증착법 (E-beam evaporation), 열증착법 (Thermal evaporation), 레이저분자빔증착법 (L-MBE, Laser Molecular Beam Epitaxy), 펄스레이저증착법 (PLD, Pulsed Laser Deposition)을 사용한다. 바람직하게는 진공 증착이나 스퍼터링을 통해 원적외선 방사층(3)을 형성한다. 진공 증착은 고진공속에서 저항가열이나 전자빔을 이용하여 물질을 증발시켜 증발 원자 및 분자가 피코팅재에 응고하여 피목이 이루어진다. 스퍼터링은 불활성기체 분위기에서 수 KV의 고전극간 전압에 의한 이상 방전으로 불활성 이온이 타겟에 충돌하여 타겟물질을 진공중으로 때려 피코팅재에 응고시켜 피복을 한다. The far-infrared radiation layer 3 uses a method in which the fibrous fabric 1, which is the coating material, is not damaged by using a deposition technique, that is, a coating technique. That is, in this embodiment, physical vapor deposition (PVD), which can perform deposition at low temperature, is used. Such physical vapor deposition methods include sputtering, e-beam evaporation, thermal evaporation, laser molecular beam deposition (L-MBE, laser molecular beam epitaxy), pulsed laser deposition (PLD) ). Preferably, the far infrared radiation layer 3 is formed by vacuum deposition or sputtering. In vacuum deposition, material is evaporated by using resistance heating or electron beam at high vacuum, and vaporization atoms and molecules solidify onto the coating material, thereby forming a wood. Sputtering is an abnormal discharge caused by the voltage between the high electrodes of several KV in an inert gas atmosphere, and inert ions collide with the target, thereby vacuuming the target material in a vacuum to coagulate the coated material.

상술한 공정을 통해 제작된 원적외선 방사층(3)은 셀레늄, 티타늄 및 게르마늄을 포함한다. 여기에 맥반석, 황토, 옥 및 토르말린을 더 포함할 수 있다. 이때, 셀레늄의 함량을 가장 높게 가져 가는 것이 바람직하다. 여기서, 원적외선 방사층(2)은 30 내지 90 중량%의 셀레늄, 1 내지 30 중량%의 티타늄, 1 내지 30중량%의 게르마늄, 1 내지 30 중량%의 맥반석, 1 내지 30 중량%의 황토, 1 내지 30 중량%의 옥과, 1 내지 30 중량%의 토르말린을 포함한다. 원적외선 방사층(3)에 1 내지 30 중량%의 세라믹이 더 첨가될 수 있다. 이는 각각의 요소들의 특징에 따라 그 첨가량이 변화할 수 있기 때문이다. The far infrared ray emitting layer 3 produced through the above-described process includes selenium, titanium, and germanium. It may further include elvan, loess, jade and tourmaline. At this time, it is preferable to take the highest content of selenium. Here, the far-infrared radiation layer 2 is 30 to 90% by weight selenium, 1 to 30% by weight titanium, 1 to 30% by weight germanium, 1 to 30% by weight elvanite, 1 to 30% by weight ocher, 1 To 30 weight percent jade and 1 to 30 weight percent tourmaline. 1 to 30% by weight of ceramic may be further added to the far infrared ray emitting layer 3. This is because the amount of addition may vary depending on the characteristics of the respective elements.

그러나 상술한 바와 같이 셀레늄의 첨가량이 가장 많은 것이 바람직하다. However, as mentioned above, it is preferable that the addition amount of selenium is the largest.

상술한 셀레늄(selenium)은 주기율표 제6B족에 속하는 산소족원소의 하나이고 우리 몸에 필수적인 미량원소(무기질)로서, 항산화효소(Glutathione peroxidase)의 구성 성분으로 산화적 손상을 방지하여 지방의 과산화로 생긴 자유기(Free radical)로부터 세포와 세포막을 보호한다. 대부분의 세포가 이 효소를 포함하고 있어 셀레늄은 광범위한 보호작용을 한다. 즉, 자유기가 세포를 상하게 하고 몇 가지 만성질환을 일으키는 원인이 될 수 있기 때문에, 우리 몸은 항산화제와 같이 자유기의 양을 조절하는 방어체계가 있다. 이와 같은 방어체계 즉, 면역체계와 갑상선의 정상적인 기능을 위해서 셀레늄은 필수적인 요소이다. 셀레늄은 방사율(5 ~20㎛)은 0.904 이고, 방사 에너지(W/㎡·㎛, 37℃)는 3.49×102이다.Selenium is one of the oxygen family elements belonging to group 6B of the periodic table and is an essential trace element (inorganic substance) in our body. Protects cells and membranes from free radicals. Most cells contain this enzyme, so selenium has a wide range of protective actions. That is, because free radicals can damage cells and cause some chronic diseases, our bodies have a defense system that regulates the amount of free radicals, such as antioxidants. Selenium is essential for the normal functioning of this defense, the immune system and the thyroid gland. Selenium has an emissivity (5-20 µm) of 0.904 and an emission energy (W / m 2 · µm, 37 ° C) of 3.49 × 10 2 .

셀레늄은 이온화 작용, 혈액촉진작용, 육성 효과, 발한 효과 및 진통 효과를 갖는다. 이뿐아니라, 유해 전자파를 차단하는 효과와, 수맥파를 차단하는 효과를 가지고 있습니다. 따라서, 셀레늄을 상기 원적외선 방사층(3)에 첨가할 경우에는 신경통, 요통, 관절염, 근육통 디스크 등에 효과가 있고, 숙면 효과가 있기 때문에 현대인들의 스트레스 해소와 피로회복에 좋고 불면증에 효과가 있다. 그리고, 미세 혈관을 팽창시켜 혈액 순환을 도와주며 성인병(고혈압, 신장병, 당뇨병, 심장질환 등)치료에 빠른 효과가 있다.Selenium has ionization action, blood promoting action, upbringing effect, sweating effect and analgesic effect. In addition to this, it has the effect of blocking harmful electromagnetic waves and the effect of blocking water vein waves. Therefore, the addition of selenium to the far-infrared radiation layer (3) is effective in neuralgia, low back pain, arthritis, myalgia discs, etc., and has a good night's sleep, which is good for stress relief and fatigue recovery of modern people and insomnia. In addition, it helps to circulate blood vessels by expanding microcirculation and has a rapid effect in treating adult diseases (hypertension, kidney disease, diabetes, heart disease, etc.).

도 3은 본 실시예에 따른 셀레늄을 포함하는 원적외선 방사 섬유의 원적외선 방사 에너지를 측정한 결과이고, 도 4는 본 실시예에 따른 셀레늄을 포함하는 원적 외선 방사 섬유의 원적외선의 방사율을 측정한 결과이다. 3 is a result of measuring the far-infrared radiation energy of the far-infrared radiation fiber containing selenium according to the present embodiment, Figure 4 is a result of measuring the emissivity of the far-infrared radiation of the far infrared radiation fiber containing selenium according to this embodiment. .

도 3 및 도 4는 한국 원적외선 응용 평가연구원에 의뢰하여 측정한 결과이ㄷ다. 이는 37℃에서 실성을 하였고, FT-IR 스펙트로미터(Spectrometer)를 이용한 블랙 바디(Block body) 대비 측정 결과이다. 도 3 및 도 4의 그래프에서와 같이 방사율은 0.904이고, 방사 에너지는 3.49×102이다. 3 and 4 are the results measured by the request of the Korea Far Infrared Ray Evaluation Institute. This was performed at 37 ° C., and is a result of the black body (Block body) measurement using the FT-IR Spectrometer. As shown in the graphs of FIGS. 3 and 4, the emissivity is 0.904 and the radiant energy is 3.49 × 10 2 .

상술한 원적외선 방사층(3)은 복수의 층으로 제작될 수 있다. 그리고, 도시되지 않았지만, 원적외선 방사층(3)은 섬유 원단(1)의 상측면 및 하측면에도 형성될 수 있다. 도 1에서는 섬유 원단(1)의 전체에 원적외선 방사층(3)이 형성됨을 도시하였다. 하지만, 이에 한정되지 않고, 일정한 패턴 형태로 원적외선 방사층(3)이 섬유 원단(1) 상에 형성될 수 있다. 이때, 원적외선 방사층(3)이 일정한 패턴 형상으로 섬유 원단(1)에 형성되기 위해서는 진공 증착 또는 스퍼터링 공정시 세도우 마스크를 이용하여 원적외선 방사층(3)을 섬유 원단(1)에 형성하는 것이 바람직하다. 즉, 제작하고자 하는 패턴 형성의 개구부를 갖는 세도우 마스크를 섬유 원단(1) 상에 배치시킨 다음 물리 기상 증착법을 통해 원적외선 방사층(3)을 형성하게 되면 원하는 패턴으로 원적외선 방사층(3)이 제작될 수 있다. The far-infrared radiation layer 3 described above may be made of a plurality of layers. And, although not shown, the far infrared ray emitting layer 3 may be formed on the upper side and the lower side of the fiber fabric (1). In FIG. 1, the far-infrared radiation layer 3 is formed on the entire fiber fabric 1. However, the present invention is not limited thereto, and the far infrared ray emitting layer 3 may be formed on the fiber fabric 1 in a predetermined pattern form. In this case, in order to form the far-infrared radiation layer 3 on the fiber fabric 1 in a predetermined pattern shape, forming the far-infrared radiation layer 3 on the fiber fabric 1 by using a shadow mask during vacuum deposition or sputtering process. desirable. That is, when a shadow mask having an opening for pattern formation to be manufactured is disposed on the fabric fabric 1 and then the far infrared ray emitting layer 3 is formed by physical vapor deposition, the far infrared ray emitting layer 3 is formed in a desired pattern. Can be made.

또한, 본 실시예의 원적외선 방사층(3)은 이에 한정되지 않고, 인쇄 방법을 이용하여 제작할 수 있다. 즉, 별도의 코팅 물질을 제작한 다음 이를 섬유 원단(1) 상에 코팅하여 제작할 수 있다. In addition, the far-infrared radiation layer 3 of a present Example is not limited to this and can be manufactured using a printing method. That is, it can be produced by coating a separate coating material and then coating it on the fiber fabric (1).

코팅 물질은 0.01 내지 10 중량%의 셀레늄과, 80 내지 99.99 중량%의 수지 와, 0.1 내지 10 중량%의 기능성 충진제를 포함한다. 본 실시예에서는 수지로 실리콘 수지, 불소 수지, 폴리에스텔 수지 및 폴리아마이드 수지 중 적어도 어느 하나를 사용한다. 물론 앞서 언급한 수지를 사용할 수 있다. 그리고, 상기 기능성 충진제는 티타늄, 게르마늄, 맥반석, 황토, 옥, 토르말린 및 세라믹 중 적어도 어느 하나를 사용한다. 여기서, 기능성 충진제로 복수의 요소가 첨가되는 경우 이들 요소는 각기 동일 양으로 첨가되거나 서로 다른 양으로 첨가될 수 있다. 즉, 상기 기능성 충진제의 요소 각각은 각기 0 내지 100 중량% 범위 내에서 첨가될 수 있다. 그리고 모든 요소가 0 중량%인 경우는 존재하지 않는 것이 당연하다. 그리고, 상기 기능성 충진제는 1nm 내지 10㎛ 단위의 분말상으로 첨가되는 것이 좋다. The coating material comprises 0.01 to 10 wt% selenium, 80 to 99.99 wt% resin, and 0.1 to 10 wt% functional filler. In this embodiment, at least one of a silicone resin, a fluororesin, a polyester resin, and a polyamide resin is used as the resin. Of course, the aforementioned resins can be used. In addition, the functional filler uses at least one of titanium, germanium, elvan, loess, jade, tourmaline and ceramic. Here, when a plurality of elements are added as functional fillers, these elements may be added in the same amount or in different amounts, respectively. That is, each of the elements of the functional filler may be added in the range of 0 to 100% by weight, respectively. Of course, if all the elements are 0% by weight, it does not exist. In addition, the functional filler is preferably added in a powder form of 1nm to 10㎛ unit.

물론 이에 한정되지 않고, 코팅 물질는 80 내지 95 중량%의 수지와, 5 내지 20 중량%의 셀레늄을 포함하는 기능성 충진제를 포함할 수 있다. 기능성 충진제로는 셀레늄, 티타늄, 게르마늄, 맥반석, 황토, 옥 및 토르말린을 포함한다. 이때, 셀레늄의 함량을 가장 높게 가져 가는 것이 바람직하다. 여기서, 기능성 충진제는 30 내지 80 중량%의 셀레늄, 1 내지 30 중량%의 티타늄, 1 내지 30중량%의 게르마늄, 1 내지 30 중량%의 맥반석, 1 내지 30 중량%의 황토, 1 내지 30 중량%의 옥과, 1 내지 30 중량%의 토르말린을 포함한다. 기능성 충진제로 1 내지 30 중량%의 세라믹이 더 첨가될 수 있다. 이는 각각의 요소들의 특징에 따라 그 첨가량이 변화할 수 있기 때문이다. Of course, the present invention is not limited thereto, and the coating material may include a functional filler including 80 to 95% by weight of resin and 5 to 20% by weight of selenium. Functional fillers include selenium, titanium, germanium, elvan, loess, jade and tourmaline. At this time, it is preferable to take the highest content of selenium. Here, the functional filler is 30 to 80% by weight selenium, 1 to 30% by weight titanium, 1 to 30% by weight germanium, 1 to 30% by weight elvanite, 1 to 30% by weight ocher, 1 to 30% by weight Jade and 1 to 30% by weight of tourmaline. 1 to 30% by weight of ceramic may be further added as the functional filler. This is because the amount of addition may vary depending on the characteristics of the respective elements.

또한, 도 2에 도시된 바와 같이 원적외선 방사층(3) 상에 라미네이팅지(5)로 코팅 처리할 수 있다. 이와 같이 라미네이팅지(5)로 코팅하여 물빨래나 드라이크리 닝과 같은 세척 작업에도 내구성과 내약품성 및 난연성을 갖게 한다. In addition, as shown in FIG. 2, the far-infrared radiation layer 3 may be coated with a laminating paper 5. In this way it is coated with a laminating paper (5) to have durability and chemical resistance and flame retardant even in the washing operations such as water washing or dry cleaning.

본 발명은 이에 한정되지 않고, 다양한 섬유 직물로 제작된 제품을 제공할 수 있다. 섬유 직물 및 이 직물로 제조된 물품, 예컨대 의복 또는 신발 등에 사용될 수 있다. 이와 같이 원적외선 방사층(3)이 그 표면에 증착된 섬유 원단(1)은 옥, 게류마늄, 세라믹과 같은 원적외선을 발생하는 원적외선 방사층(3)을 포함한 외부 피복재를 제작하여 인체에 환력을 줄 수 있다. 그리고, 라미네이팅지(5)로 코팅하여 물빨래나 드라이크리닝과 같은 세척 작업에도 내구성과 내약품성은 물론 내화기능을 갖는다. The present invention is not limited thereto, and may provide a product made of various textile fabrics. Fiber fabrics and articles made from these fabrics, such as garments or shoes. As described above, the fiber fabric 1 in which the far-infrared radiation layer 3 is deposited on the surface of the fiber fabric 1 produces an outer coating material including the far-infrared radiation layer 3 that generates far-infrared rays such as jade, germanium, and ceramics to give the human body a breath force. Can be. And, by coating with laminating paper (5) has a durability and chemical resistance as well as a fire-proof function even in washing operations such as water washing or dry cleaning.

도 5는 본 실시예에 따른 셀레늄을 포함하는 원적외선 방사 섬유로 제작된 복대의 착용 전후의 신체의 열을 측정한 사진이다. 도 6은 본 실시예에 따른 셀레늄을 포함하는 원적외선 방사 섬유로 제작된 무릎 보호대의 착용 전후의 신체의 열 측정 결과 사진이다. 5 is a photograph of the body heat measured before and after wearing a stomach band made of far-infrared radiation fiber containing selenium according to the present embodiment. Figure 6 is a photograph of the thermal results of the body before and after wearing the knee protector made of far-infrared radiation fiber containing selenium according to this embodiment.

도 5의 사진에서와 같이 원적외선 방사 섬유로 제작된 복대를 착용한 경우에는 복수의 체온이 증가함을 알 수 있고, 도 6의 사진에서와 같이 원적외선 방사 섬유로 제작된 무릎 보호대를 착용한 경우에는 무릎 영역의 체온이 증가됨을 알 수 있다. 이와 같이 본 실시예의 원적외선 방사 섬유로 의복 및 다양한 제품을 제작하여 신체에 작용하게 될 경우 인체의 면역력을 향상시키고, 성인병과 스트레스 해소 및 피로 회복에 유익하게 작용할 수 있다. When wearing a bag made of far-infrared radiation fiber as shown in the photo of Figure 5 it can be seen that a plurality of body temperature increases, when wearing a knee protector made of far-infrared radiation fiber as shown in the photo of FIG. It can be seen that the body temperature in the knee region is increased. As described above, when the clothing and various products are manufactured by using the far-infrared radiation fiber of the present embodiment, the human body may improve the immunity of the human body, and may work to relieve stress and relieve fatigue and adult diseases.

상술한 바와 같이 본 발명은 섬유 원단에 원적외선 방사층을 증착 법으로 증착하여 인체에 쾌적함을 줄 수 있고, 이온화 작용, 혈액촉진작용, 육성 효과, 발한 효과 및 진통 효과를 줄 수 있다. As described above, the present invention may give comfort to the human body by depositing a far-infrared radiation layer on a textile fabric, and may give an ionization effect, blood promoting effect, growth effect, sweating effect, and analgesic effect.

또한, 본 발명은 섬유 원단으로 라미네이팅 처리하여, 물빨래는 물론 드라이크리닝과 같은 세척 작업에도 내구성과 내약품성은 물론 난연성을 갖는 레져용 자킷, 신발창, 장갑, 모자, 방한복 등의 제품들을 유리하게 제조할 수 있다.In addition, the present invention can be advantageously manufactured products such as jackets, soles, gloves, hats, winter clothes, etc. having a durability and chemical resistance, as well as flame retardant in washing operations such as water washing as well as dry cleaning by laminating the fiber fabric. have.

Claims (7)

섬유 원단; 및 Textile fabrics; And 상기 섬유 원단 상에 증착된 원적외선 방사층을 포함하고, A far infrared ray emitting layer deposited on the fiber fabric, 상기 원적외선 방사층은 30 내지 90 중량%의 셀레늄, 1 내지 30 중량%의 티타늄, 1 내지 30중량%의 게르마늄, 1 내지 30 중량%의 맥반석, 1 내지 30 중량%의 황토, 1 내지 30 중량%의 옥과, 1 내지 30 중량%의 토르말린을 포함하는 것을 특징으로 하는 원적외선 방사 섬유.The far-infrared radiation layer is 30 to 90% by weight selenium, 1 to 30% by weight titanium, 1 to 30% by weight germanium, 1 to 30% by weight ganbanite, 1 to 30% by weight ocher, 1 to 30% by weight Far-infrared radiation fiber comprising jade of, and 1 to 30% by weight of tourmaline. 제 1 항에 있어서, The method of claim 1, 상기 원적외선 방사층은 진공 증착 및 스퍼터링을 포함하는 물리 기상 증착법을 통해 증착되는 것을 특징으로 하는 원적외선 방사 섬유.The far infrared radiation layer is far infrared radiation fiber, characterized in that deposited through the physical vapor deposition method including vacuum deposition and sputtering. 제 1 항에 있어서, The method of claim 1, 상기 원적외선 방사층 상에 마련된 라미네이팅지를 더 포함하는 것을 특징으로 하는 원적외선 방사 섬유.Far-infrared radiation fiber further comprises laminating paper provided on the far-infrared radiation layer. 제 1 항에 있어서, The method of claim 1, 상기 원적외선 방사층은 세도우 마스크에 의해 상기 섬유 원단 상에 패터닝되는 것을 특징으로 하는 원적외선 방사 섬유.And said far-infrared radiation layer is patterned on said fiber fabric by a shadow mask. 제1항 내지 제 4 항 중 어느 한 항의 원적외선 방사 섬유로 제작된 의복.A garment made of the far-infrared radiation fiber of claim 1. 섬유 원단을 마련하는 단계; 및Preparing a fiber fabric; And 물리 기상 증착법을 이용하여 상기 섬유 원단 상에 30 내지 90 중량%의 셀레늄, 1 내지 30 중량%의 티타늄, 1 내지 30중량%의 게르마늄, 1 내지 30 중량%의 맥반석, 1 내지 30 중량%의 황토, 1 내지 30 중량%의 옥과, 1 내지 30 중량%의 토르말린을 포함하는 원적외선 방사층을 형성하는 단계를 포함하는 것을 특징으로 하는 원적외선 방사 섬유 제작 방법.30 to 90% by weight selenium, 1 to 30% by weight titanium, 1 to 30% by weight germanium, 1 to 30% by weight elvan, 1 to 30% by weight ocher on the fabric fabric using physical vapor deposition And forming a far-infrared radiation layer comprising 1 to 30% by weight of jade and 1 to 30% by weight of tourmaline. 제 6 항에 있어서, The method of claim 6, 상기 물리 기상 증착법으로 진공 증착 및 스퍼터링을 사용하는 것을 특징으로 하는 원적외선 방사 섬유 제작 방법.Far infrared radiation fiber manufacturing method characterized in that the vacuum vapor deposition and sputtering by the physical vapor deposition method.
KR1020070045024A 2007-05-09 2007-05-09 Far infrared ray radiant composite fiber and clothes manufactured using the same KR100822719B1 (en)