KR100773046B1 - The making device a multiplex floor rib pipe and method - Google Patents
The making device a multiplex floor rib pipe and method Download PDFInfo
- Publication number
- KR100773046B1 KR100773046B1 KR1020060026917A KR20060026917A KR100773046B1 KR 100773046 B1 KR100773046 B1 KR 100773046B1 KR 1020060026917 A KR1020060026917 A KR 1020060026917A KR 20060026917 A KR20060026917 A KR 20060026917A KR 100773046 B1 KR100773046 B1 KR 100773046B1
- Authority
- KR
- South Korea
- Prior art keywords
- molding
- pipe
- extrusion
- cooling water
- rib
- Prior art date
Abstract
본 발명은 합성수지 등 파이프형으로 구성되는 관재의 중공부내에 리브(힘살rib)을 일체로 성형하기 위한 관재 압출성형방법 및 그 장치에 관한 것으로서, 더욱 상세히는 관재의 휨강도와 지지력 증강, 보온력강화, 소음방지 등을 증대하기 위한 목적으로 관재내의 중공부에 일자형, 십자형 등으로 구성되는 힘살을 일체로 압출성형 할 수 있도록 한 리브가 일체로 성형되는 관재 압출성형장치 및 그 방법에 관한 것이다.The present invention relates to a pipe extrusion molding method and apparatus for integrally forming a rib in a hollow portion of a pipe, such as a synthetic resin, more specifically, to the bending strength and bearing capacity of the pipe, strengthening the thermal insulation, The present invention relates to a pipe extrusion molding device and a method of forming a rib integrally formed to integrally extruding a force of a straight line, cross, or the like in a hollow part of a pipe for the purpose of increasing noise prevention.
본 발명에서는 합성수지, 폐비닐, 폐플라스틱, 알미늄재 등 재질로 구성되는 원형, 사각, 다각형 등의 관재를 구성하고 그 내측 중공부내에 리브(rib)를 일체로 성형하기 위한 관재 압출성형방법 및 그 장치를 제공하되, 본 발명은 알미늄, 합성수지와 함께 폐비닐, 폐플라스틱 등 재생가능한 수지류를 각각 또는 혼합 공급하여 견고한 성형물을 얻을 수 있도록 한 폐자원의 재활용을 목적으로 함과, 공급원료를 고압력으로 압출성형하여 관재의 견고성을 증대함과, 상기 목적을 달성하기 위하여 수평으로 구성되는 용융압출기와 이 수평 용용압출기로부터 공급된 용융수지를 수직상태의 성형압출장치에서 압출성형함과,In the present invention, a pipe extrusion method for forming a rib, such as a round, square, polygon, made of synthetic resin, waste vinyl, plastic, aluminum, and the like and integrally forming ribs in the inner hollow portion thereof, and the same In the present invention, the present invention aims at recycling waste resources to obtain a solid molding by supplying aluminum or synthetic resin with recycled resins such as waste vinyl, waste plastic, etc., respectively, or by mixing and supplying a high pressure feedstock. By extrusion molding to increase the rigidity of the pipe, and to achieve the above object, the melt extruder formed horizontally and the molten resin supplied from the horizontal melt extruder by extrusion molding in a vertical extrusion molding apparatus,
상기 성형압출장치의 성형금형 끝단이 성형압출장치의 하부로 구성되는 냉각수조의 냉각수에 인입된 상태로 성형하여 성형물이 성형과 냉각이 함께 이루어지면서 고압축에 의한 견고성의 향상과 크랙 발생방지, 찌그러짐방지를 이룰 수 있고 성형된 성형물은 컷팅장치로 절단하여 일정길이의 성형물을 얻을 수 있도록 하는 것이다.The molding die end of the molding extrusion device is molded into the cooling water of the cooling water tank constituted by the lower part of the molding extrusion apparatus, and the molding is formed together with the cooling, thereby improving the firmness and preventing cracking and preventing crushing. The molded article can be formed and cut by a cutting device to obtain a molded article of a certain length.
관재, 리브(힘살rib) Tube, rib
Description
도 1은 본 발명의 성형장치를 보인 설명도.1 is an explanatory view showing a molding apparatus of the present invention.
도 2는 본 발명 관재를 성형하기 위한 일실시예의 성형금형 사시도.Figure 2 is a perspective view of a molding die of one embodiment for molding the present invention pipe member.
도 3의 (a)(b)(c)는 본 발명에 의해 성형되는 일실시예의 관재를 도시한 단면도. Figure 3 (a) (b) (c) is a cross-sectional view showing a tube of an embodiment molded by the present invention.
도 4는 본 발명의 성형을 하기 위한 설명도.4 is an explanatory diagram for forming the present invention.
* 도면의 주요부분에 사용된 부호의 설명 *Explanation of symbols used in the main part of the drawing
100; 관재 110; 중공부 120; 리브 100; Tube 110;
200; 이송관 300; 용융압출기 301; 홉퍼200;
400; 성형압출장치 401; 용융수지저장부 402; 압출실린더400;
403; 성형틀 500; 성형금형 601; 냉각수 403; Molding die 500; Molding
600; 냉각수조 610; 컷팅장치600;
본 발명은 합성수지 등 파이프형으로 구성되는 관재의 중공부내에 리브(힘살 rib)를 일체로 성형하기 위한 관재 압출성형방법 및 그 장치에 관한 것으로서, 더욱 상세히는 관재의 휨강도와 지지력 증강, 보온력강화, 소음방지 등을 증대하기 위한 목적으로 관재내의 중공부에 일자형, 십자형 등으로 구성되는 힘살을 일체로 압출성형 할 수 있도록 한 리브가 일체로 성형되는 관재 압출성형장치 및 그 방법에 관한 것이다.The present invention relates to a pipe extrusion molding method and apparatus for integrally forming ribs (hollow ribs) in a hollow part of a pipe, such as a synthetic resin, more specifically, to increase the bending strength and bearing capacity of the pipe, strengthening the thermal insulation, The present invention relates to a pipe extrusion molding device and a method of forming a rib integrally formed to integrally extruding a force of a straight line, cross, or the like in a hollow part of a pipe for the purpose of increasing noise prevention.
합성수지관 또는 알미늄관 등을 원료로 하는 압출성형관재는 사각재와 원형관재 또는 다각재를 이루고 그 내면이 빈상태의 중공부로 구성되어진다.Extruded tubular material made of synthetic resin tube or aluminum tube, etc., consists of a rectangular tube and a circular tube or a polygonal tube, and is composed of a hollow portion having an empty inner surface.
이러한 중공상태의 관재는 가볍고 적은 원료의 소모와 압출성형에 따른 생산의 용이성으로 대량생산성이 충족되는 한편 그 사용용도가 다양하여 많은 분야에서 대량으로 사용되고 있다.Such hollow tube materials are used in large quantities in many fields due to their light weight, low consumption of raw materials, and ease of production due to extrusion molding, while achieving mass productivity.
이러한 관재는 상, 하수관, 전기, 통신 선로 등의 용도와 함께 이와 달리 많은 지지력이 요구되는 농촌의 비닐하우스 기초부재로서 사용되고 또는 사각 등의 각재로 구성되어 건축물의 기초부재와 건설현장에서의 토류벽 등에 이용되고 있다.These pipes are used as foundation materials of rural houses that require a lot of support, along with water, sewage pipes, electricity, and communication lines. It is used.
그러나 비닐하우스 기초부재 또는 건설현장의 토류벽 등에서 사용될 때에는 중공상태의 관재가 쉽게 휨되는 문제와 그 지지력이 약해 쉽게 부러지거나 휘어지는 문제가 발생되고 있다.However, when used in the vinyl house base member or the earth wall of the construction site, the problem that the hollow tube is easily bent and its support strength is weak, so that the problem is easily broken or bent.
이에 의하여 농촌에서 비닐하우스의 기초부재로 사용 될 때 하절기의 강우량이 많거나 또는 동절기의 폭설로 눈 무게를 지지하지 못하므로 휨되거나 절단 등으로 하우스가 내려 앉아 하우스농사의 폐농과 피해를 입히는 재해가 매년 발생되고 있어 사회문제로서 또는 농촌의 고소득 사업에 지대한 피해를 입히고 있고 이와 달 리 건설비용을 줄이기 위한 건설현장에서는 토류벽이 터지는 문제 등이 발생된다.As a result, when used as a basic member of a plastic house in rural areas, there is a lot of rainfall during the summer season or the snowfall cannot be supported by snowfall in the winter. As it occurs every year, it causes serious damage to high-income projects in rural areas, and on the other hand, the earth wall breaks at construction sites to reduce construction costs.
이에 따라 상기한 폐단을 개선하기 위하여 중공상태의 관재내에 일체로 구성되는 리브를 십자형 등으로 더 구성시켜 관재의 견고성을 증대하도록 한 선행기술들이 다수 알려진바 있다.Accordingly, in order to improve the closed end, many prior arts have been known to further increase the rigidity of the pipe by further configuring the ribs integrally formed in the hollow pipe in a cross shape or the like.
일예로 대한민국 특허 10-0463215호는 압출 방향으로 관재를 압출 성형하기 위한 다이스에 제1구멍과 제2구멍으로 분할되어 관재 내에 하나 이상의 리브가 형성되는 선행기술의 다이스에 의한 관재의 내측 공간에 중간벽이 성형되는 관재의 압출 성형 방법과, 또 다른 특허 등록특허 10-0484617호에서는 코아커버와 연결된 원통형 본체에 코아가 끼워져 고정되고 1 압출기에서 공급되는 성형수지가 이송되는 이송통로와 코아의 중심에 제 2압출기와 연결된 중심보강재 압출관이 배치되는 압출성형기용 압출다이 및 공개특허 10-2004-0052944호의 융융한 재료를 다이스 양측으로 공급하는 압출기로 관의 외벽면을 형성하는 외경 사이싱과 관의 내벽면을 형성하는 내경 사이싱구비하는 다층관의 일체화 압출성형장치가 알려진바 있다.For example, Korean Patent No. 10-0463215 discloses an intermediate wall in an inner space of a pipe by a prior art die in which one or more ribs are formed in a die for extruding the pipe in the extrusion direction so that at least one rib is formed in the pipe. In the extrusion molding method of the pipe member to be molded, and another patent registration No. 10-0484617 core is inserted into the cylindrical body connected to the core cover is fixed to the center of the transfer passage and the core conveying the molding resin supplied from the extruder 1 Extrusion die for extruder in which center reinforcement extruder pipe connected to extruder is arranged and extruder for supplying melted material of Korean Patent No. 10-2004-0052944 to both sides of die and outer diameter sising to form outer wall surface of pipe BACKGROUND OF THE INVENTION An integrated extrusion molding apparatus of a multilayer tube having internal diameter sizing forming a wall has been known.
이상의 기술들은 중공부로 형성되는 관재에 그 휨방지와 지지력의 강화를 위하여 중공부내세 리브를 구성하기 위한 것이나, 그 구성의 방법과 장치에서 압출금형에 외경과 내경 및 리브가 압출되도록 하기 위한 금형 및 그 방법에 관한 것이다. The above techniques are for constructing hollow inner ribs to prevent bending and strengthening of bearing capacity in a pipe member formed of hollow parts, but in the method and apparatus of the configuration, a mold for extruding the outer diameter, the inner diameter, and the ribs into an extruded mold. It is about a method.
이러한 선행기술들에서의 문제는 그 성형장치가 수평으로 구성됨으로서 공지와 같이 압출금형에서 성형되는 부재를 다시 진공압 등에 한 당김과 함께 냉각장치를 거치도록 구성되어지고 이때 냉각속도와 당김에 의한 찌그러짐과 크랙 및 접하 부의 요입부 발생과 그 두께가 일률적이지 못하면서 강도가 극히 약한 단점이 발생하게 되는 것이다.The problem with these prior arts is that the molding apparatus is configured horizontally so that it is configured to pass through the cooling apparatus together with pulling the member formed in the extrusion mold into vacuum pressure or the like as it is known, and at this time, the cooling speed and the distortion caused by the pulling The occurrence of over cracks and indentations in the abutment and its thickness are not uniform, resulting in extremely weak strength.
또한 상기한 선행장치들은 그 이론상 성형이 가능한 것으로 기재하고 있으나 실질적인 성형에서는 발명자의 의도한 강도 또는 사용가능한 강도를 이룰 수 없는 상태의 성형과 재생원료를 사용할 수 없는 폐단으로 고가의 생산원가를 요구하게 되고 또한 폐비닐 등을 이용할 수 없어 수지와 혼합된 재료를 이용할 수 없으므로 고가의 원료를 사용하여야 하는 문제도 함께 가지고 있다.In addition, the above-mentioned prior art devices are described as theoretically possible to be molded, but in actual molding, it is possible to achieve expensive production costs due to the molding in a state in which the inventor's intended strength or usable strength cannot be achieved and a closed end in which recycled raw materials cannot be used. In addition, since waste vinyl and the like cannot be used, a material mixed with resin cannot be used, which also has a problem of using expensive raw materials.
본 발명에서는 상기와 같은 종래의 문제점을 개선하기 위하여 발명된 것으로 특히, 합성수지, 폐비닐, 폐플라스틱, 알미늄재 등 재질로 구성되는 원형, 사각, 다각형 등의 관재를 구성하고 그 내측 중공부내에 리브(rib)을 일체로 성형하기 위한 관재 압출성형방법 및 그 장치를 제공하되, 본 발명은 알미늄, 합성수지와 함께 폐비닐, 폐플라스틱 등 재생가능한 수지류를 각각 또는 혼합 공급하여 견고한 성형물을 얻을 수 있도록 한 폐자원의 재활용을 목적으로 함과, 공급원료를 고압력으로 압출성형하여 관재의 견고성을 증대함과, 상기 목적을 달성하기 위하여 수평으로 구성되는 용융압출기와 이 수평 용용압출기로부터 공급된 용융수지를 수직상태의 성형압출장치에서 압출성형함과,The present invention is invented to improve the conventional problems as described above, in particular, constitutes a pipe, such as circular, square, polygonal, made of synthetic resin, waste vinyl, waste plastic, aluminum material and the like and ribs in the inner hollow portion (Rib) to provide a pipe extrusion molding method and apparatus therefor, the present invention is to provide a solid molding by separately or mixed supply of renewable resins such as waste vinyl, waste plastic with aluminum, synthetic resin For the purpose of recycling a waste resource, extrusion of the feedstock at high pressure to increase the rigidity of the pipe material, and to achieve the above object, a horizontal melt melt extruder and a molten resin supplied from the horizontal melt extruder Extrusion molding in a vertical extrusion molding apparatus,
상기 성형압출장치의 성형금형 끝단이 성형압출장치의 하부로 구성되는 냉각수조의 냉각수에 인입된 상태로 성형하여 성형물이 성형과 냉각이 함께 이루어지면서 고압축에 의한 견고성의 향상과 크랙 발생방지, 찌그러짐방지를 이룰 수 있고 성형된 성형물은 컷팅장치로 절단하여 일정길이의 성형물을 얻을 수 있도록 하는 것이다.The molding die end of the molding extrusion device is molded into the cooling water of the cooling water tank constituted by the lower part of the molding extrusion apparatus, and the molding is formed together with the cooling, thereby improving the firmness and preventing cracking and preventing crushing. The molded article can be formed and cut by a cutting device to obtain a molded article of a certain length.
상기에서 성형된 성형물은 고열의 압출성형과 함께 냉각되고 수직하강으로 인출됨으로써 고압축에 의한 성형물의 고압축에 의한 견고성을 향상시킬 수 있고 수직 하강성형으로 휨, 찌그러짐 방지로 상품성을 향상시킬 수 있다.The molded article is cooled with high-temperature extrusion molding and drawn out in the vertical down to improve the rigidity by the high compression of the molding by high compression, and to improve the commerciality by preventing bending and crushing in the vertical down molding.
본 발명의 성형물은 관재의 중공부내에 리브가 구성되어 관재의 휨강도와 지지력 증강, 보온력강화, 소음방지 등을 증대하기 위하여 관재내의 중공부에 일자형, 십자형 등으로 구성되는 리브를 일체로 구성한다.In the molding of the present invention, the ribs are formed in the hollow part of the pipe so that the ribs of the straight pipe, cross, etc. are integrally formed in the hollow part of the pipe in order to increase the bending strength, the support force, the heat retention, the noise prevention, and the like of the pipe.
본 발명의 상기 목적을 달성하기 위한 구성을 첨부 도면에 의해 그 바람직한 실시예를 보다 상세히 설명한다.The preferred embodiment of the present invention will be described in detail with reference to the accompanying drawings.
도 1은 본 발명의 성형장치를 보인 설명도이고 도 2는 본 발명 관재를 성형하기 위한 일실시예의 성형금형 사시도이며 도 3의 (a)(b)(c)는 본 발명에 의해 성형되는 일실시예의 관재를 도시한 단면도. 그리고 도 4는 본 발명의 성형을 하기 위한 설명도이다.1 is an explanatory view showing a molding apparatus of the present invention, Figure 2 is a perspective view of a molding mold of an embodiment for forming the present invention pipe member and Figure 3 (a) (b) (c) is a molded by the present invention Sectional drawing which shows the pipe | tube of an Example. 4 is an explanatory diagram for forming the present invention.
상기 도면에 도시된 바와 같이 원통, 사각, 다각형 등의 관재(100)내 중공부(110)에 하나이상의 복수개 리브(120)를 성형하기 위한 성형금형(300)과 용융압출기(300)로 구성되는 통상의 압출성형기에 있어서,As shown in the figure is composed of a
본 발명은 수지 등의 원료를 공급하기 위한 홉퍼(301)와 공급된 원료를 고열로 용융시켜 이송하는 수평상태로 구성되는 용융압출기(300)와 The present invention is a melter extruder (300) consisting of a hopper (301) for supplying a raw material such as resin and the horizontal state to melt and transport the supplied raw material at high heat and
상기 용융압출기(300)의 이송관(200)으로부터 공급된 잴 상태의 용융수지를 저장하는 용융수지저장부(401)를 구비하고 수직방향의 상단에 구성되는 압출실린더(402)와 하단에 성형틀(403)을 구비하여 복수의 리브(120)가 형성되는 성형금형(500)을 구성하는 수직상태의 성형압출장치(400)를 구성한다.
상기 성형금형(500)은 수직으로 기다란 형태를 이루고 상부로부터 고, 중, 저열을 제공하는 히터를 구비하여 성형물이 성형을 이룰 수 있도록 한다. The
그리고 상기 수직 상태의 성형압출장치(400) 하부로 냉각수(601)가 충진되는 냉각수조(600)를 구비하되, 상기 길이방향으로 구성되는 성형금형(500)의 끝단부가 냉각수(601)에 잠기도록 냉각수(601)를 충진시켜 구성된다.And a
상기 냉각수조(600)에는 성형금형(500)으로부터 성형되어 인출되는 성형물관재(100)을 절단 가능한 컷팅장치(610)가 더 구성되는 것이 바람직하다.Preferably, the
냉각수조(600)는 지면에 깊이로 구성하거나 또는 기체를 높이 구성하여 그 하부로 구성할 수 있으며, 또한 성형물 관재(100)의 크기에 따라 그 깊이가 설정되는 것이 바람직하다.The
그리고 냉각수조(600)의 상중하점부에 미도시된 온도센서를 구비시켜 가열히터를 제어하여 냉각수(601)의 온도를 제어함으로 성형물 관재(100)의 냉각속도와 크랙방지, 비틀림방지 등 효과를 이루도록 함과 함께 성형금형(500)의 끝단부가 냉각수(601)에 잠수되도록 미도시된 수위센서와 냉각수공급펌프를 더 구성시켜 냉각수 수위가 일정한 높이로 유지되도록 한다.And by providing a temperature sensor not shown in the upper and lower points of the
이러한 본 발명의 구성은 공급된 수지를 용융시킨 용융압출기(300)로부터 공 급된 용융수지가 수직방향으로 구성되는 성형압출장치(400)에서 강제적으로 하강 압출하여 압축강도를 높이게 된다.Such a configuration of the present invention is to forcibly lower and extrude the molten resin supplied from the
강제적인 압출은 폐비닐 등에서 인입된 불순물이 고압력으로 압축되어져 성형물 관재(100)내의 기포방지와 기밀(氣密)한 성형물 관재(100)를 형성하여 견고성을 증대하게 되는 것이다.The forced extrusion is to increase the rigidity by forming the airtight and airtight molded
즉, 용융수지가 압축실린더(402)의 피스톤으로 압축되어 성형금형(500)을 통과하면서 성형될 때, 성형금형(500)의 끝단부에서 성형물 관재(100)가 1차 냉각되어짐으로 이 성형물 관재(100)는 성형금형(500)에서 인출이 억제되고 이때 상부의 성형압출장치(400)의 압축실린더(402) 피스톤이 강제적으로 압축 하강하여 성형물 관재(100)내의 기포제거와 고압력으로의 압축으로 성형물 관재(100)의 강도를 증강시키게 되는 것이다.That is, when the molten resin is compressed by the piston of the
이상과 같은 본 발명의 작용효과를 보다 상세히 설명하면, 도 4의 본 발명의 성형을 하기 위한 설명도에서와 같이 농어촌에서 사용 후 폐기되는 각종 폐비닐, 음료수용기, 생활용품의 사용 후 폐기되는 각종 폐플라스틱과 재생가능한 수지를 수거하여 본 발명의 재생원료로서 사용하게 된다.Referring to the operation and effect of the present invention in more detail as described above, as shown in the explanatory diagram for forming the present invention of Figure 4, a variety of discarded after the use of various waste vinyl, beverage containers, household goods discarded after use in rural areas Waste plastics and renewable resins are collected and used as recycled materials of the present invention.
즉, 수거된 재생원료는 압축과정과 컷팅과정을 거처 용융압출기(300)로 공급가능하도록 가공하여 용융압출기(300)의 홉퍼(301)를 통해 공급시킨다.That is, the collected recycled raw materials are processed to be supplied to the
홉퍼(301)로 공급된 재생원료는 상기 용융압출기(300)에서 공지된 바와 같이 고열로 용융되고 이송스크류를 통해 이동하여 도 1도에서 표기된 성형압출장치(400)의 용융수지저장부(401)로 이송된다.The recycled raw material supplied to the
용용수지저장부(401)로 이송된 재생원료가 일정량 충진되면 상부의 압축실린더(402)의 피스톤이 하강하여 상기 용융수지저장부(401)내의 재생원료를 하강으로 가압시켜 이 재생원료는 성형틀(403)에 고정된 성형금형(500)을 통해 성형물 관재(100)를 형성하게 된다.When the recycled raw material transferred to the molten
이때 성형물 관재(100)는 상부로부터 고, 중, 저열 상태의 성형금형(500)을 통과하면서 서서히 냉각된 후 냉각수(601)에 잠수된 끝단부의 저온에서 급냉각되어 성형물 관재(100)의 견고성을 유지하여 인출을 억제시키게 된다.At this time, the
이와 같이 인출이 억제된 상태에서 상부의 피스톤은 계속 하강되어 성형물을 고압축하게 되고 고압축으로 성형물내의 기포제거와 기밀성을 한층 높여 성형물의 견고성을 유지하게 되는 것이다.In this way, the upper piston is continuously lowered in the state in which the extraction is suppressed, thereby compressing the molded article by high compression, and maintaining the firmness of the molded article by increasing the bubble removal and airtightness in the molded article by high compression.
상기 성형금형(500)을 통과한 성형물 관재(100)는 다시 냉각수조(600)의 냉각수(601)에 의해 상온상태로 냉각되며 성형물 관재(100)의 인출 길이가 충족되면 컷팅장치(610)가 가동되어 절단하게 되는 것이며 절단된 성형물 관재(100)는 크레인등의 인출장치에 의해 인출하게 된다. The
그리고 성형물 관재(100)의 급냉각 또는 저속냉각을 인한 크랙과 휨 등을 방지하기 위하여 냉각수(601)온도를 제어하고 냉각수(601)가 성형금형(500)을 일정한 깊이로 잠수시키기 위한 수위센서와 냉각수 공급펌프가 구비되어 냉각수온도와 수위를 조절한다.And in order to prevent cracks and warpage due to rapid cooling or low-speed cooling of the
이상과 같은 본 발명은 종래의 저압축으로 인한 성형물내의 기포발생과 기밀성이 없어 그 강도가 약한 문제점을 개선하고 압출 성형물을 인출하기 위하여 외측 면과 내측면에 각각 대칭방향으로 진공흡입과 냉각을 동시에 실시하여 발생되는 장치의 복잡성과 성형물 외주면에서 진공흡착에 의한 요철발생 및 인출과정에서의 절단등의 문제점을 간단히 개선하는 효과를 가진다.In the present invention as described above, there is no bubble generation and airtightness in the molding due to the conventional low compression to improve the problem of weak strength and to simultaneously draw the vacuum suction and cooling in the symmetrical direction on the outer surface and the inner surface in order to take out the extrusion molding It has the effect of simply improving the complexity of the device generated by the implementation and problems such as irregularities generated by vacuum adsorption and cutting in the drawing process on the outer peripheral surface of the molding.
또한 수평인출에서는 기다란 성형물의 휨으로 직선상태의 성형물을 얻을수 없는 폐단도 함께 방지할 수 있으며 그구성이 간단하여 제작이 용이하고 고장이 없는 장점을 발휘하게 되는 것이다.In addition, in the horizontal drawing, it is possible to prevent the closed end of the molded article in a straight state due to the warpage of the long molded article.
본 발명은 합성수지등의 관재 중공부에 리브를 구성하여 관재의 견고성과 휨성을 증강시켜 농어촌의 비닐하우스 기초부재와 건축현장에서의 토류방지벽 또는 각종 건축자재로서 사용가능하도록 관재의 견고성을 충족시키기 위한 것이며 이러한 본 발명은 각종 이물질이 포함된 폐비닐, 폐플라스틱 등의 재생자원을 이용하여 원형, 사각, 다각형 등의 관재를 구성함과 함께 그 내측 중공부내에 리브(rib)을 일체로 성형하되, 수평으로 구성되는 용융압출기와 이 수평 용용압출기로부터 공급된 용융수지를 수직상태의 성형압출장치에서 압출성형함과, 성형금형이 성형압출장치의 하부로 구성되는 냉각수조의 냉각수에 인입된 상태로 성형하여 고압축에 의한 견고성의 향상과 크랙 발생방지, 찌그러짐 방지를 이룰 수 있는 특징과 관재의 중공부내에 리브를 일체로 성형하는 효과 및 재생자원을 이용함으로써 환경오염방지 및 원가절감을 효과를 창출할 수 있는 유용한 발명이다.The present invention is to form a rib in the hollow portion of the pipe, such as synthetic resin to enhance the rigidity and warpage of the pipe to meet the rigidity of the pipe so that it can be used as a base member of the rural house of farming and fishing villages and earth barriers or various building materials in the construction site The present invention is intended to form a rib (rib) in the inner hollow portion while forming a circular, square, polygonal, etc., using recycled resources such as waste vinyl, waste plastic, etc. containing various foreign matter. And extrusion molding of the melt extruder formed horizontally and the melted resin supplied from the horizontal melt extruder in a vertical molding extrusion apparatus, and molding the mold into the cooling water of the cooling water tank composed of the lower part of the molding extrusion apparatus. Rigidity in the hollow part of the pipe and the features that can improve the robustness, prevent cracks, and prevent crushing by high compression It is a useful invention that can create environmental protection and cost reduction effect by using the integral molding effect and renewable resources.
Claims (4)