KR100749519B1 - The melamine resin concrete form panel manufacture method and the product - Google Patents
The melamine resin concrete form panel manufacture method and the product Download PDFInfo
- Publication number
- KR100749519B1 KR100749519B1 KR1020050082306A KR20050082306A KR100749519B1 KR 100749519 B1 KR100749519 B1 KR 100749519B1 KR 1020050082306 A KR1020050082306 A KR 1020050082306A KR 20050082306 A KR20050082306 A KR 20050082306A KR 100749519 B1 KR100749519 B1 KR 100749519B1
- Authority
- KR
- South Korea
- Prior art keywords
- melamine resin
- melamine
- formwork
- kraft paper
- plywood
- Prior art date
Abstract
본 발명은, The present invention,
멜라민 수지 20 ~ 40 중량부, 포름알데히드 30 ~ 50 중량부와 에틸렌글리콜을 5 중량부, 수산화 나트륨 1 중량부의 비율로 하여서 되는 멜라민 수지의 액상 제조공정과, The liquid phase manufacturing process of melamine resin which makes 20-40 weight part of melamine resin, 30-50 weight part of formaldehyde, 5 weight part of ethylene glycol, and 1 weight part of sodium hydroxide,
45 ~ 69 g/㎡ 의 경량 무게를 갖는 크레프트 페이퍼를 190 ~ 210 %의 함침률로 상기 제 1 공정에 의해 제조된 멜라민 수지에 함침 처리한 후, 120 ~ 150 ℃ 의 온도를 유지하는 건조로를 60 ~ 180 초간 통과시켜 건조 및 반경화되는 상태로 되도록 하는 멜라민 함침 크래프트 페이퍼(Kraft paper) 제조공정과, After drying the kraft paper having a light weight of 45 to 69 g / m 2 to the melamine resin prepared by the first process at an impregnation rate of 190 to 210%, the drying furnace was maintained at a temperature of 120 to 150 ° C. Melamine impregnated kraft paper manufacturing process to pass through ~ 180 seconds to be dried and semi-cured state,
최하부에 페놀함침 크레프트 페이퍼(TEGO 필름)이 위치되도록 한 후, 그 상면으로 합판을 적층하고, 상기 합판 상면으로 상기의 제 2 공정에 의해 얻게 된 멜라민 함침 크레프트 페이퍼를 적층하고, 그 상면으로 다시 미함침 된 30 g/㎡ ~ 60 g/㎡ 의 무게를 갖는 글래스 페이퍼(GLASS PAPER)를 적층한 후 그 상면으로 다시 멜라민 함침 크래프트 페이퍼를 적층하되 각 적층면마다 접착층이 형성되도록 하여 다단 적층하는 적층공정과, After placing the phenol impregnated kraft paper (TEGO film) at the lowermost part, the plywood is laminated on the upper surface, and the melamine impregnated kraft paper obtained by the second process is laminated on the upper surface of the plywood, and then pushed back to the upper surface. Lamination process of laminating glass paper (Glass paper) having impregnated 30 g / ㎡ ~ 60 g / ㎡ weight and then laminating the melamine impregnated kraft paper on its upper surface to form an adhesive layer on each lamination surface and,
상기 적층공정에 의해 적층된 상태에 있는 거푸집패널을 20 kgf/㎠ ~ 25 kgf/㎠ 의 단위압력을 갖는 열압 프레스에서 170 ℃ 의 온도를 120 ~ 180 초간 유지하며 열압 프레싱 하는 열압 프레싱 공정과, A hot pressing process for pressing the formwork panels laminated by the lamination process in a hot press having a unit pressure of 20 kgf / cm 2 to 25 kgf / cm 2 while maintaining a temperature of 170 ° C. for 120 to 180 seconds;
상기 열압 프레싱 공정에 의해 제조된 거푸집 패널의 반제품을 48시간 자연 냉각에 의해 건조시키는 건조공정으로 구성되는 것을 특징으로 하여, Characterized in that it comprises a drying step of drying the semi-finished product of the formwork panel manufactured by the hot pressure pressing process by natural cooling for 48 hours,
내, 알카리성 및 평활성이 우수하고, 크랙 현상 등이 발생되지 않으며 내충격성 및 수회에 걸친 사용 회수의 증가 및 콘크리트 타설 후 판면과의 우수한 이형성을 얻을 수 있게 되는 효과를 기대할 수 있는 거푸집용 패널을 제조하기 위한 방법 및 그 거푸집용 패널을 제공하기 위한 것이다.Manufactures formwork panels with excellent alkali resistance and smoothness, no cracking phenomenon, impact resistance and increased number of times of use, and excellent releasability with plate after concrete casting It is to provide a method and a panel for formwork thereof.
멜라민 수지, 거푸집 패널 Melamine resin, die panel
Description
도 1은 본 발명의 각 공정을 도시한 공정도이고,1 is a process chart showing each process of the present invention,
도 2는 본 발명의 거푸집 합판을 이루는 단면도를 도시한 도면이다.2 is a view showing a cross-sectional view of the formwork plywood of the present invention.
도 3은 본 발명에 의한 제품을 이용하여 내알카리성 시험을 한 상태의 사진이고,3 is a photograph of the alkali resistance test state using the product according to the present invention,
도 4는 종래의 제품을 이용하여 내알카리성 시험을 한 상태의 사진이다.4 is a photograph of an alkali resistance test using a conventional product.
※ 도면 중 주요부호에 대한 간단한 설명※ Brief description of the main symbols in the drawings
S1; 멜라민 수지의 액상 제조공정S1; Melamine Resin Liquid Phase Manufacturing Process
S2; 멜라민 함침 크래프트 페이퍼(Kraft paper) 제조공정S2; Melamine-impregnated kraft paper manufacturing process
S3; 적층공정S3; Lamination Process
S4; 열압 프레싱 공정S4; Hot pressing process
S5; 건조공정S5; Drying process
1. 접착층1. Adhesive layer
10; 페놀함침 크레프트 페이퍼 20; 합판10; Phenol impregnated
30; 멜라민함침 크레프트 페이퍼 40; 미함침 글래스 페이퍼30; Melamine impregnated
본 발명은 멜라민 수지를 이용하여 함침처리한 크래프트 페이퍼 사용으로 인한 내, 알카리성 및 평활성이 우수하고, 크랙 현상 등이 발생되지 않으며 내충격성 및 수회에 걸친 사용 회수의 증가 및 콘크리트 타설 후 판면과의 우수한 이형성을 얻도록 하기 위한 거푸집용 패널을 제조하기 위한 방법 및 그 거푸집용 패널을 제공하기 위한 것이다.The present invention is excellent in alkali resistance and smoothness due to the use of kraft paper impregnated with melamine resin, no cracking, etc., and the impact resistance and increase in the number of times of use and excellent after the concrete casting It is to provide a method for producing a formwork panel and to obtain a formwork panel to obtain a releasability.
일반적으로 콘크리트의 표면을 균일하거나 매끄럽게 처리되도록 받쳐주는 거푸집용 합판은 재사용되는 주기가 많을 뿐만 아니라, 사용시간이 길어 상기 목재로 이루어진 합판에 콘크리트에 섞여진 물등의 수분이 스며들게되어 합판의 형태를 변형시키거나 썩게 만들므로 사용주기가 짧아지는 문제점이 있다.In general, the formwork plywood that supports the surface of the concrete to be treated uniformly or smoothly is not only reused frequently, but also has a long use time, so that the plywood made of wood is infiltrated with moisture such as water mixed with concrete to deform the shape of the plywood. There is a problem in that the use cycle is shortened because it makes or to rot.
이와같이 일반적으로 사용되는 콘크리트 거푸집용 합판의 재단면에는 페인트를 뿜칠하거나 붓칠하여 얇은 도막을 형성시켜 사용하고 있으나, 목재 성장시 수분이 이동하는 통로인 도관(導管)은 완전히 차단할 만큼 도막두께를 형성하기 어려운 문제점이 있다.As such, a thin film is formed by spraying or painting paint on the cutting surface of a concrete formwork plywood.However, a conduit, which is a passage through which moisture moves during wood growth, is formed so as to completely block the film thickness. There is a difficult problem.
또한, 종래와 같이 형성된 거푸집용 합판을 사용할 때에는, 합판이 쉽게 변형되기때문에 상기의 변형된 형태에 의해 양생되는 콘크리트의 표면을 변형시키기 때문에 재작업을 실시해야하는 번거로움 문제점이 발생되고 있다.In addition, when using the formwork plywood formed as in the prior art, since the plywood is easily deformed, since the surface of the concrete to be cured by the deformed form is deformed, the trouble of having to rework occurs.
한편, 합판의 재료인 원목은 대부분 수입에 의존하고 있으므로 합판을 사용하는 거푸집용 패널은 제조 비용이 고가이며, 국제적으로 원목 가격이 불안정하므로 합판 가격 역시 심한 변동을 일으켜 소비자들의 안정적인 구매가 힘들다. 아울러, 합판의 표면에는 나뭇결이 존재하므로 이 합판 거푸집으로 시공되는 구조물의 표면이 매끄럽지 못하다. 또한, 테고 필름(tego film)을 접착시킨 합판의 경우, 합판 표면에 존재하는 나뭇결로 인해 테고 필름과 합판의 접착 상태가 약하여 거푸집의 사용 횟수가 증가하면 합판으로부터 테고 필름이 박리되는 현상이 수시로 발생한다.On the other hand, since most of the timber, the material of plywood, depends on imports, formwork panels using plywood are expensive to manufacture and internationally unstable timber prices cause severe fluctuations in plywood, making it difficult for consumers to purchase. In addition, since the wood grain exists on the surface of the plywood, the surface of the structure to be constructed with this plywood formwork is not smooth. In addition, in the case of plywood bonded to the tego film, due to the wood grain present on the surface of the plywood, the adhesion state between the tego film and the plywood is weak, so that when the number of use of the formwork increases, the tego film peels off from the plywood. do.
중밀도 섬유판인 MDF(Medium Density Fiber Board)는 1979년 국내에 소개되어 일반 가구, 악기, 실내 장식재, 사무용 가구, 전자 제품 외장재 등으로 사용되어 왔다. MDF는 수입 원목 중 제재목으로 사용할 수 없는 소경목, 산림 간벌시 발생하는 간벌재, 산림 화재시 베어낸 화상목, 제재소의 폐자재, 건설 현장에서 발생하는 각종 폐자재 등을 원료로 하여 제조되므로 제조 비용이 저렴하고, 자원을 재활용할 수 있다는 장점이 있다. Medium Density Fiber Board (MDF), a medium-density fiberboard, was introduced in 1979 in Korea and has been used for general furniture, musical instruments, interior decoration, office furniture, and electronics exterior materials. MDF is manufactured using raw materials such as small timbers that cannot be used as lumber among imported timbers, thinning materials that occur during forest thinning, burned wood cut during forest fires, waste materials for sawmills, and various waste materials generated at construction sites. This is inexpensive and has the advantage of recycling resources.
그러나 요소 수지를 사용하여 목재 섬유들을 접착시킨 종래의 MDF는 평균 휨강도가 406㎏f/㎠, 팽창율이 7.2%(두께가 12㎜인 MDF 기준)로 강도 및 방수성이 약하다. 따라서 이를 콘크리트 거푸집용 패널로 사용할 경우, 콘크리트 타설(打設)시 수분과의 접촉에 의해 패널의 부풀음 현상이 발생하고, 이로 인해 패널의 강도가 저하된다. 아울러, 콘크리트 타설시 발생하는 충격과 거푸집 제거시 거푸집간의 충 돌로 인해 패널이 심하게 파손될 수 있다. 따라서, 요소 수지를 사용하여 목재 섬유들을 접착시킨 종래의 MDF는 가구재 이외의 용도로는 사용하기가 어렵다.However, the conventional MDF bonded with wood fibers using urea resin has a weak strength and waterproofness with an average bending strength of 406 kgf / cm 2 and an expansion ratio of 7.2% (based on MDF having a thickness of 12 mm). Therefore, when it is used as a panel for concrete formwork, the swelling of the panel occurs due to contact with moisture during concrete pouring, thereby lowering the strength of the panel. In addition, the panel may be severely damaged due to the impact generated during the concrete pouring and the collision between the molds when removing the formwork. Therefore, the conventional MDF to which wood fibers are bonded using urea resin is difficult to use for applications other than furniture.
일반적으로 거푸집은 철근 콘크리트 공사를 하기 위해 일시적으로 사용하는 형틀로서, 나무로 만는 것, 합판으로 짠 것, 철판으로 만든 것 등 많은 종류의 것이 통용화 되어 사용되고 있는 실정이며, 그 적용은 각 공사의 특성 및 조건등을 고려하여 선택 채용하고 있다.In general, formwork is a form temporarily used for reinforced concrete construction, and many kinds of things such as wood, woven from plywood, and iron plate are commonly used. It is selected and adopted in consideration of characteristics and conditions.
상기의 거푸집으로 초기 기초공사시 그 구조물이나 건축물의 구조에 따라 형틀을 만들어 완료 한 상태에서, 콘크리트를 상기 거푸집내에 주입 충진하는 타설공정을 거친 다음, 일정시간동안 대기(大氣)상태에서 콘크리트 양생(養生)과정을 통해 굳은 상태가 되면, 거푸집을 철거하여 완성된 철근 콘크리트 구조물 또는 건축물의 형상을 얻을 수 있었음은 주지된 바와 같다.After the formwork is completed according to the structure or the structure of the building during the initial foundation work, after the pouring process, the concrete is poured into the formwork and poured into the formwork. It is well known that when the hardened state is obtained through the 養生 process, the form is removed to obtain the shape of the completed reinforced concrete structure or building.
이른바, 콘크리트 구조물의 축조를 위한 거푸집 시공은 다량의 가설재와 과다한 설치기간, 고기능의 인력과 장비 등을 필요로 하는 매우 중요한 공정으로 그 작업 공정과 소요 설비의 선택은 후속의 타 공정과의 상관적 관계를 형성하여 지대한 영향을 미치게 되고, 축조된 건축물의 향후 내구성, 안정성을 결정짓는 주요 요인으로 작용되어 표준화된 시공방법 및 설비가 도입될 필요가 있는 부분이다.So-called formwork for the construction of concrete structures is a very important process that requires a large amount of temporary materials, excessive installation periods, high-skilled manpower and equipment, and the selection of the work process and the required equipment has a correlation with other processes. It is a part that needs to introduce a standardized construction method and equipment as it plays a major role in determining the future durability and stability of the constructed building.
최근, 산업화 영향에 따른 각종 토목, 건축구조물의 축조기술 발전은 도시, 농촌을 망라하고 급격하게 발전되는 추세이며, 생활의 질적 향상에 따른 평준화를 가능하게 한 요인으로 기능하고 있다.Recently, the development of construction technology of various civil and building structures in accordance with the industrialization effect is a trend that is rapidly developed, covering urban and rural areas, and functions as a factor that enables the leveling according to the improvement of quality of life.
특히 콘크리트 구조물의 발달은 사회 각 부문 중 그 중요도가 높아 대표적 구조물로 자리매김되고 있는바, 이와같이 그 콘크리트 구조물이 각광(脚光) 받는 이유는 우수한 내구성과 견고한 강도(强度), 원자재인 각종 골재(骨材)의 구입이 용이하다는 점과, 비교적 시공이 간단하다는 이점이 있어, 일반 주거용 주택이나 아파트 및 각종 용도의 고층건물이나, 교량, 터널 또는 도로공사등을 포함하는 사회간접자본시설에 매우 광범위하게 적용되고 있는 실정이다.In particular, the development of concrete structures is one of the most important social sectors, and thus they are positioned as representative structures.The reason why the concrete structures are spotlighted is that they have excellent durability, solid strength, and various aggregates that are raw materials. I) It is easy to purchase and relatively simple in construction, and it is very widely used for social overhead capital facilities including general residential houses, apartments, high-rise buildings for various uses, bridges, tunnels or road works. It is being applied.
상기와 같은 요인들에 의해 거푸집을 구성하는 거푸집 패널에 대한 지대한 관심이 모아지고 있으며, 특히 거푸집 패널을 일회용으로 사용하지 않고 반영구적인 사용이 가능하도록 하기 위한 연구와 실험등이 계속되고 있다.Due to the above factors, a great deal of attention has been gathered on the formwork panel constituting the formwork, and researches and experiments for enabling semi-permanent use without using the formwork panel in particular are continuing.
본 발명은 목재류의 합판(MDF, HDF등 고,중,저밀도 압축강화목을 포함하여)으로 되는 거푸집 패널의 개선에 관한 것이므로, 합판등의 거푸집 패널에 의한 종래 거푸집의 설치 및 철거후에 재사용에 따른 문제점등을 살펴본다.The present invention relates to the improvement of formwork panels made of timber plywood (including high, medium and low density compressed hardened wood, such as MDF, HDF), and according to reuse after installation and removal of conventional formwork by formwork panels such as plywood. Examine the problem.
종래 건축물이나 구조물등의 콘크리트 타설을 위해서 상기한 바와 같이 합판등으로 되는 거푸집 패널을 이용하여 거푸집을 축조한 상태에서 콘크리트를 타설하게 되는데, 보통 콘크리트의 몰탈에 포함되는 수분에 의해 거푸집 패널의 부식이나 썩음 현상등을 유발하게 되는 문제가 있어, 이와같은 문제점을 보완하기 위해 일반 방수합판 즉 내수합판을 사용하고 있었으나, 상기 방수합판등의 내수합판은 콘크리트와 합판의 접착성으로 인하여 거푸집 탈형후에는 다수의 콘크리트 잔재물이 부착되는 상태이므로 그 사용회수에 따라 콘크리트 잔재물의 부착률이 상승되어, 콘크 리트 양생 후 평활한 콘크리트면을 얻기가 어려우므로 그 전용(轉用) 횟수가 2~3회 이상의 사용이 불가능하게 되는 등의 문제점이 있었다.Conventionally, in order to pour concrete such as buildings or structures, concrete is poured in the form of formwork using formwork panels made of plywood as described above, and corrosion of formwork panels is usually caused by moisture contained in mortar of concrete. There is a problem that causes the rot, etc. To solve this problem, a general waterproof plywood, that is, a water-resistant plywood was used, but the water-resistant plywood such as waterproof plywood due to the adhesiveness of concrete and plywood after a number of formwork demoulding As the concrete residues are attached, the adhesion rate of concrete residues increases according to the number of times of use, and it is difficult to obtain smooth concrete surface after concrete curing. There were problems such as becoming impossible.
또한 이러한 단점을 일부 보완하기 위해 합판 표면층에 코팅층을 형성하는 코팅합판이 개발되어 사용되고 있으나, 이 역시 콘크리트와 합판의 접착성으로 인하여 그 전용횟수가 7~8회를 넘지 못하고 폐기처분하게 되는 문제점이 있었다.In addition, in order to make up for some of these drawbacks, a coated plywood was formed and used to form a coating layer on the surface of the plywood, but this problem is also due to the adhesiveness of concrete and plywood, which is not disposed more than 7 to 8 times and disposed of. there was.
이와같은 이유등으로 인하여, 고층의 건물 축조시 7,8층까지 거푸집패널을 사용한 후, 그 이상의 층수에 재차 거푸집을 설치하여 콘크리트를 타설하기 위해서는 새로운 거푸집 패널을 구비하여 사용하여야 하므로, 그 자재 구매비용 및 시공비용등을 추가 부담하여야 하는 문제점이 있으며, 이와 아울러 건축공사비의 증가 요인으로 작용되는 등의 문제점이 있었다.For this reason, when building a high-rise building, use the formwork panel up to 7,8th floor, and then install the formwork on more floors and install new formwork panel. There is a problem in that the additional costs and construction costs, and at the same time acts as an increase factor of the construction cost.
따라서 이와같은 문제점을 감안하여 공사 현장에서는 거푸집 패널을 사용할 시, 상기 거푸집 패널 표면층에 박리제(剝離劑)를 도포하여 콘크리트의 잔재물이 거푸집 패널 표면에 부착되는 것을 방지함과 동시에 수분침투를 방지하고 있으나, 이와같은 경우에도 근본적인 해결책이 되지 않고 있으며, 오히려 비용을 증가시키게 됨은 물론 박리제(剝離劑)를 사용하여 콘크리트를 타설함에도 불구하고 3~4층이후 부터는 양생된 콘크리트의 표면층이 거칠게 되고, 거푸집 패널 표면층 역시 콘크리트 잔재물 부착으로 인해 불량하게 되는 등의 문제가 있으며, 콘크리트의 표면층의 불평활성으로 인하여 거푸집 탈형(脫刑) 작업후에 콘크리트 표면층을 고르게 하기 위한 견출(見黜)작업을 따로 수행하여야 하므로 이에따른 인건비와 공사비의 상승 및 공기(工期)의 증가를 가져오는 등의 여러 문제점이 지적되고 있다.Therefore, in consideration of such problems, when using the formwork panel, by applying a release agent (剝離 劑) to the surface layer of the formwork panel to prevent the remnants of concrete adhere to the formwork panel surface and at the same time to prevent moisture penetration In this case, even though it is not a fundamental solution, the cost is not only increased, but the surface layer of the cured concrete becomes rough after 3-4 layers even though the concrete is poured using a release agent. The surface layer also has problems such as poor adhesion due to the adhesion of concrete residues.As a result of the inactivation of the surface layer of the concrete, it is necessary to separately perform the extraction work for leveling the concrete surface layer after formwork. Increase in labor and construction costs and air Several problems have been pointed out, such as the increase of).
한편 이와같은 문제를 감안하여 합성수지재 패널을 사용하고 있는 경우도 있으나, 상기 합성수지 패널의 경우 무게가 가볍고 콘크리트벽 시공시 평활성을 유지할 수 있는 장점이 있는 반면에, 합성수지의 특성으로 인하여 수축율이 심하고 강도(强度)가 약하여 하중(荷重)이 집중되는 집중분포하중을 받을 경우 상기 합성수지 패널이 쉽게 휘게 되어 콘크리트의 시공이 매우 불량하게 되는 문제는 물론, 사용후 폐기에 의한 환경오염문제등을 유발시키게 되는 문제점등이 있었다.On the other hand, in consideration of such a problem, a synthetic resin panel may be used, but the synthetic resin panel has a light weight and an advantage of maintaining smoothness when constructing a concrete wall, while the shrinkage ratio is high and strength due to the characteristics of the synthetic resin. When the load is concentrated and the concentrated load is concentrated, the panel is easily bent and the construction of concrete becomes very poor, and it causes environmental pollution by disposal after use. There were problems.
이와는 달리 좀더 근본적 문제해결을 위해 대한민국 특허청에 출원되어 공개된 특허출원 제 2000-7738 호에 의한 『 말단에 자유 -NCO가 노출되어 있는 폴리우레탄 및 말단에 자유 -NCO를 갖는 우레탄 경화제를 포함하는 콘크리트 거푸집 합판용 도료 조성물과 이에 의해 도장된 콘크리트 거푸집 합판 및 상기 도료 조성물의 제조방법등을 특징』으로 하는 특허가 출원되어 있는바, 위 특허는 콘크리트의 박리성이 우수하고 그 전용횟수를 크게 증가시키게 되는 장점을 가지고 있으나, 그 조성물을 제조하는 공정이 번잡하고, 그 도료의 조성물 제조에 의한 첨가제(添加劑) 및 치환제, 경화제등 많은 수의 조성물제가 포함되어 그 조건을 충족하여야 하므로, 제조공정이 까다롭고 이에따른 도료제의 생산비용의 과다에 의한 거푸집 패널의 생산비 증가를 가져오게 되는 등의 문제점을 피할 수 없다.On the contrary, according to Patent Application No. 2000-7738, filed with the Korean Intellectual Property Office for a more fundamental problem solving, `` Concrete comprising polyurethane having free -NCO exposed at the end and urethane curing agent having free -NCO at the end. The patent application is characterized in that the coating composition for the formwork plywood and the concrete formwork plywood and the method of manufacturing the coating composition coated thereby, the patent is excellent in the peelability of the concrete and greatly increase the number of times However, the process of preparing the composition is complicated, and a large number of composition agents such as additives, substituents, and curing agents by the preparation of the composition of the paint must be included to satisfy the conditions. Increasing the production cost of formwork panels due to excessive production costs Problems such as
한편 상기의 예와는 달리 대한민국 특허청에 기출원되어 등록된 특허등록 제231359호의 경우에는 폴리에틸렌패널을 목재패널에 접착제로 접착하여 제작되는 폴 리에틸렌패널이 부착된 복합거푸집패널을 제공하고 있는 것으로, 이와같은 경우에 합성수지에 해당되는 폴리에틸렌패널을 목재패널에 접착제로 접합시킬 경우, 무기물(無機物)에 해당되는 폴리에틸렌패널과 유기물(有機物)에 해당되는 목재합판을 접착제로 완벽하게 접착시키는 것이 매우 어렵고, 또한 상기한 바와 같이 합성수지(合成樹脂)의 특성상 기온의 변화에 상당히 민감하게 되므로 여름과 겨울등 외부의 온도와 콘크리트 몰탈의 온도차이가 상당히 심하고, 폴리에틸렌패널과의 온도차이 변화에 따른 상기 폴리에틸렌패널의 변형율이 극심하게 되어 수축/팽창이 심하게 일어나게 됨에 따라 평활한 표면층을 갖는 콘크리트 양생에 치명적인 문제점이 지적되고 있다.On the other hand, unlike the above example, in the case of Patent Registration No. 231359, filed and registered with the Korean Intellectual Property Office, to provide a composite formwork panel with a polyethylene panel produced by bonding the polyethylene panel to the wood panel with an adhesive, In such a case, when the polyethylene panel corresponding to the synthetic resin is bonded to the wooden panel with an adhesive, it is very difficult to completely bond the polyethylene panel corresponding to the inorganic material and the wooden plywood corresponding to the organic material with the adhesive, In addition, as described above, due to the nature of the synthetic resin (synthesis of the synthetic resin) is very sensitive to changes in temperature, so the temperature difference between the outside temperature and concrete mortar, such as summer and winter is quite severe, and the temperature difference of the polyethylene panel Strain becomes severe and severe shrinkage / expansion occurs Critical issues in the cured concrete having a smooth surface along has been pointed out.
한편 폴리에스테르 필름층의 접착력을 강화하기 위해 『콘크리트구조물 축조시 사용되는 거푸집용 패널에 적어도 일측면에는 방수시트를 부착하는 것을 특징으로 하고, 상기 방수시트는 폴리에스테르필름으로 되며, 패널과 접하게 되는 방수시트 일측면은 코로나 방전처리되어 패널과의 접착력이 상승되도록 하는 것』이 대한민국 특허청에 출원되어 선등록된 실용신안등록 제219580호에 의해 개시되고 있으나, 도체의 주위에 강한 불평등 전계가 발생했을 때 전계가 강한 부분에만 생기는 국부방전인 코로나 방전(corona discharge)을 수행하기 위해서, 폴리에스테르 필름층에 직경이 작은 구멍을 무수히 천공하여 그 구멍에 접착제를 충진 한 후, 방전 처리하여 접착하게 되므로 그 작업과정이 대단히 번잡하게 되는 문제점이 있으며, 방전과정에서 기압이 낮아지게 되면 점점 불안정하게 되는 현상이 발생되어 완전한 접착 및 장시간의 접착효과가 저하되는 등의 문제점이 있으며, 국부적 방전에 따라 거푸집 표면에 전체적으로 균일하게 폴리에스테르 필름을 접착하는 것이 대단히 어려움은 물론, 상기한 고안에서는 이와같은 문제점을 해결할 어떠한 수단도 제시되고 있지 않다.Meanwhile, in order to reinforce the adhesive force of the polyester film layer, the waterproof sheet is attached to at least one side of the formwork panel used in the construction of the concrete structure, and the waterproof sheet is made of the polyester film and is in contact with the panel. One side of the waterproof sheet is treated with corona discharge to increase the adhesive strength with the panel. ”However, it is disclosed by Utility Model Registration No. 219580, which was filed with the Korean Intellectual Property Office, but a strong inequality was generated around the conductor. In order to perform corona discharge, which is a local discharge generated only at a strong electric field, a hole having a small diameter is drilled in the polyester film layer, and after the filler is filled with an adhesive, it is discharged and bonded. There is a problem that the working process is very complicated, and the air pressure in the discharge process If it is lowered, there is a problem that the unstable phenomenon occurs, such that the complete adhesion and long-term adhesion effect is reduced, it is very difficult to adhere the polyester film uniformly on the formwork surface according to the local discharge, of course, One design does not suggest any means to solve this problem.
또한 이와는 달리, 폴리에스테르 필름을 합판 즉 거푸집 패널 일면에 고무계열의 접착제를 도포한 후, 그 접착제층 상면으로 폴리에스테르 필름을 적층시키고, 고무롤 사이를 통과시켜 가접착시킨 후 냉압프레스에 가접착된 상태의 거푸집 패널을 삽입한 다음, 최소한 24시간의 양생 기간을 거쳐 접착력이 유지되는 거푸집 패널을 얻는 방법이 있으나, 냉압프레스에 의한 가압력에 의해 접착제를 가압, 접착하게 되므로 필름층과 패널간의 접착력이 저하되고, 24시간 정도의 양생공정을 거쳐야 하므로 롤링된 패널을 적재, 적층하기 위한 넓은 작업장소를 요하게 되는 문제점이 있으며, 외부온도 즉 냉압프레스시 작업장소등의 외부온도 조건에 따라 접착력에 상당한 차이점이 발견되고 있음을 알게 되었다.In addition, the polyester film is applied to the plywood, that is, a rubber-based adhesive on one side of the formwork panel, and then the polyester film is laminated on the upper surface of the adhesive layer, and is temporarily bonded by passing through the rubber rolls and then temporarily bonded to the cold press. After inserting the formwork panel in the state, there is a method of obtaining a formwork panel in which the adhesive strength is maintained through a curing period of at least 24 hours, but the adhesive force between the film layer and the panel is applied because the adhesive is pressed and adhered by a pressing force by a cold press. Since it is degraded and needs to undergo a curing process for about 24 hours, there is a problem of requiring a wide working place for loading and laminating rolled panels. Significant differences in adhesive strength depending on external temperature conditions such as working temperature during cold press work It was found that this is being discovered.
이외에, 멜라민 수지를 이용하는 거푸집 패널 등이 있는데, 예를 들면 대한민국 특허청에 출원되어 공개된 공개특허 2000-28348 호의 경우, 목재 칩(chip)으로부터 제조한 목재 섬유(fiber)에 멜라민 수지를 도포, 건조시킨 후 매트상으로 성형하고, 열압함으로써 전체 패널의 79-82중량%인 목재 섬유 및 이 목재 섬유들을 상호 접착시키는 것으로서 전체 패널의 12-15중량%인 멜라민 수지를 포함하며, 밀 도가 750-850㎏/㎥인 중밀도 섬유판을 제조한다. 이 중밀도 섬유판의 표면에 크라프트(kraft)지에 페놀 수지를 함침시킨 테고 필름(tego film)을 부착시킨 후 이를 거푸집용 패널로 사용하는 기술에 대하여 공개되어 있다.In addition, there is a formwork panel using melamine resin, and the like, for example, Patent Application No. 2000-28348 published and filed with the Republic of Korea, the melamine resin is applied to the wood fibers (fiber) made from wood chips (chip) And then formed into a mat, and hot pressed to include 79-82% by weight of wood fibers of the entire panel and melamine resins of 12-15% by weight of the entire panel as the mutual bonding of the wood fibers, with a density of 750-850. A medium density fiberboard of kg / m 3 was produced. The technique of attaching a tego film impregnated with phenolic resin to kraft paper on the surface of the medium density fiberboard and using it as a formwork panel is disclosed.
그러나, 이와같은 기술의 경우 멜라민 수지의 특성을 이용하되 도포되는 과정을 거친 다음, 크라프트지에 페놀 수지를 함침시킨 테고 필름을 부착하여, 전체적 표면은 방수성을 향상시키는 역할을 하는 테고 필름에 의한 거푸집을 제공하고 있으나, 내마모성 테스트에 의한 결과 1200 회 정도의 테스트 회수에 그치고, 알칼리 테스트에서는 약한 성질을 나타내어 시멘트 등의 알칼리성에 의해 표면이 부식되는 현상이 발생되어 사용 회수에 한계를 갖는 것으로 나타났다.However, in the case of such a technique, using the characteristics of the melamine resin, but after applying the process, and then attached to the Tego film impregnated with phenolic resin on the kraft paper, the overall surface serves to improve the formability by Tego film Although it is provided, the wear resistance test results in only about 1200 tests, the alkali test showed a weak property, the surface corrosion caused by the alkali, such as cement appeared to have a limit in the number of times of use.
따라서 본 발명은 상기한 여러 문제점 등을 해결하고, 본원인에 의해 출원된 다수 산업재산권의 기술적 구성으로부터 개량된 기술에 의한 거푸집용 패널의 제조방법 및 그 거푸집 패널을 제공하는데 그 목적이 있다.Accordingly, an object of the present invention is to solve the above-mentioned problems and to provide a method for manufacturing a formwork panel and a formwork panel by the technology improved from the technical configuration of a number of industrial property rights filed by the present applicant.
특히, 본원인의 동일 계열사에 해당되는 (주)신광보드텍에서는 이와 같은 문제점을 해결하기 위해 특허등록 제 464631 호와 같은 내용의 거푸집패널을 개발, 시공처리하고 있는바, 본 발명에서는 폴리에스테르 필름의 접착 형성에 의존하지 않고 멜라민 수지를 이용한 콘크리트 패널을 제공하되, 그 표면강도 등의 물성을 증대시키기 위해 개발, 시험하여 일반적인 TEGO 합판보다도 내충격성이나 사용 회수 및 이형성 등을 증대하기 위한 거푸집 패널을 제공하는데 목적이 있다.Particularly, in order to solve such a problem, Shinkwang Boardtech Co., Ltd., which belongs to the same affiliated company of the present company, develops and constructs a formwork panel having the same contents as Patent Registration No. 464631, in the present invention, a polyester film To provide concrete panels using melamine resins without relying on the adhesion formation of them, form and develop panels to increase the physical properties such as surface strength and form impact panels to increase impact resistance, number of uses, and mold release properties compared to general TEGO plywood. The purpose is to provide.
또한 본 발명의 목적은 가격이 저렴하고, 시공되는 구조물의 표면 품질을 향상시킬 수 있는 거푸집용 패널을 제공하기 위함이다.It is also an object of the present invention to provide a formwork panel which is low in cost and can improve the surface quality of the structure to be constructed.
본 발명의 다른 목적은 방수성, 강도 및 작업성이 우수한 거푸집용 패널을 제공하기 위함이다.Another object of the present invention is to provide a panel for formwork having excellent waterproofness, strength and workability.
상기한 목적을 달성하기 위한 본 발명은,
멜라민 수지 20 ~ 40 중량부, 포름알데히드 30 ~ 50 중량부와 에틸렌글리콜을 5 중량부, 수산화 나트륨 1 중량부의 비율로 하여서 되는 멜라민 수지의 액상 제조공정(S1)과,
45 ~ 69 g/㎡ 의 경량 무게를 갖는 크레프트 페이퍼를 190 ~ 210 %의 함침률로 상기 제 1 공정(S1)에 의해 제조된 멜라민 수지에 함침 처리한 후, 120 ~ 150 ℃ 의 온도를 유지하는 건조로를 60 ~ 180 초간 통과시켜 건조 및 반경화되는 상태로 되도록 하는 멜라민 함침 크래프트 페이퍼(Kraft paper) 제조공정(S2)과,
최하부에 페놀함침 크레프트 페이퍼(TEGO 필름)(10)이 위치되도록 한 후, 그 상면으로 합판(20)을 적층하고, 상기 합판(20) 상면으로 상기의 제 2 공정(S1)에 의해 얻게 된 멜라민 함침 크레프트 페이퍼(30)를 적층하고, 그 상면으로 다시 미함침 된 30 g/㎡ ~ 60 g/㎡ 의 무게를 갖는 글래스 페이퍼(GLASS PAPER)(40)를 적층한 후 그 상면으로 다시 멜라민 함침 크래프트 페이퍼(30)를 적층하되 각 적층면마다 접착층(1)이 형성되도록 하여 다단 적층하는 적층공정(S3)과,
상기 적층공정(S3)에 의해 적층된 상태에 있는 거푸집패널(100)을 20 kgf/㎠ ~ 25 kgf/㎠ 의 단위압력을 갖는 열압 프레스에서 170 ℃ 의 온도를 120 ~ 180 초간 유지하며 열압 프레싱 하는 열압 프레싱 공정(S4)과,
상기 열압 프레싱 공정(S4)에 의해 제조된 거푸집 패널(100)의 반제품을 48시간 자연 냉각에 의해 건조시키는 건조공정(S5)으로 구성되는 것을 특징으로 한다.The present invention for achieving the above object,
20 to 40 parts by weight of melamine resin, 30 to 50 parts by weight of formaldehyde, 5 parts by weight of ethylene glycol and 1 part by weight of sodium hydroxide, and the liquid phase manufacturing process of melamine resin (S1),
After impregnating the kraft paper having a light weight of 45 ~ 69 g / ㎡ at 190 ~ 210% impregnation of the melamine resin produced by the first step (S1), and maintaining a temperature of 120 ~ 150 ℃ Melamine-impregnated kraft paper manufacturing process (S2) to pass through the drying furnace for 60 to 180 seconds to be dried and semi-cured state,
After placing the phenol-impregnated kraft paper (TEGO film) 10 at the lowermost part, the
Pressing the formwork panel 100 in the laminated state by the lamination step (S3) in a hot press with a unit pressure of 20 kgf / cm 2 to 25 kgf / cm 2 while maintaining a temperature of 170 ° C. for 120 to 180 seconds Hot pressing process (S4),
It characterized in that it comprises a drying step (S5) for drying the semi-finished product of the formwork panel 100 manufactured by the hot-pressing step (S4) by natural cooling for 48 hours.
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
이하 본 발명의 바람직한 실시예를 들어 설명한다.Hereinafter will be described a preferred embodiment of the present invention.
(제 1 공정 ; (1st process; S1S1 - 멜라민 수지의 액상 제조공정) -Liquid phase manufacturing process of melamine resin)
멜라민 수지는 내수성, 내약품성, 내알칼리성이 우수한 성질을 갖는 것으로 나타나 있다.Melamine resin has been shown to have excellent properties in water resistance, chemical resistance and alkali resistance.
또한, 경화되는 온도가 105℃ 정도로 사용하기 편리하여, 방수성 및 강도가 우수한 거푸집용 패널을 제공할 수 있다. In addition, the temperature to be cured is convenient to use about 105 ℃, it is possible to provide a formwork panel excellent in waterproofing and strength.
그러나, 이러한 우수한 성질을 갖는 멜라민 수지를 이용하여 합판 등에 도포하거나 또는 코팅 처리할 때 합판의 표면상으로 나타나는 나이테의 방향으로 크랙 현상이 발생되는 문제로 인하여, 합판측에 사용하더라도 널리 알려져 있는 페놀함침을 이용한 페놀 함침 크래프트 페이퍼(TEGO 필름)를 이용하게 되는바, 상기의 페놀 함침 크레프트 페이퍼를 이용하였을 때의 문제점은 상술한 바와 같다.However, due to the problem that cracks occur in the direction of the rings appearing on the surface of the plywood when the melamine resin having such excellent properties is applied to or coated on the plywood, the phenol impregnation is well known even when used on the plywood side. Phenol-impregnated kraft paper (TEGO film) using the bar, the problem when using the phenol-impregnated kraft paper is as described above.
본 발명에서는 상기와 같이 합판패널의 나이테 무늬로 인해 발생될 수 있는 크랙 현상 등을 방지하기 위한 공정을 제시하여 그 문제점을 극복하고자 하였다.In the present invention, to overcome the problems by presenting a process for preventing cracks that may occur due to the ring pattern of the plywood panel as described above.
멜라민 수지 20 ~ 40 중량부, 포름알데히드 30 ~ 50 중량부와 에틸렌글리콜을 5 중량부, 수산화 나트륨 1 중량부의 비율로 하여 공지의 수단 및 방법에 의해 액상화 하여, 멜라민수지를 얻는다.20-40 weight part of melamine resin, 30-50 weight part of formaldehyde, and ethylene glycol are liquefied by a well-known means and method in the ratio of 5 weight part and 1 weight part of sodium hydroxide, and a melamine resin is obtained.
(제 2 공정 ; (2nd process; S2S2 - 멜라민 -Melamine 함침Impregnation 크래프트Craft 페이퍼( Paper ( KraftKraft paperpaper ) 제조공정)) Manufacture process)
상기 제 1 공정에 의해 얻게 된 멜라민 수지에 크레프트 페이퍼(Kraft paper)를 이용하여 함침 처리하게 되는 공정인바, 45 ~ 69 g/㎡ 의 크레프트 페이퍼를 190~210 %의 함침률로 상기 멜라민 수지를 함침 처리한다.The process of impregnating the melamine resin obtained by the first process using kraft paper, impregnating the melamine resin with the impregnation rate of 190-210% of 45 ~ 69 g / ㎡ kraft paper Process.
이와같이 멜라민 수지가 함침 처리된 멜라민 함침 크레프트 페이퍼(30)를 120 ~ 150 ℃ 의 온도를 유지하는 건조로를 60 ~ 180 초간 통과시켜 건조 및 반 경화되는 상태에 이르게 한다.As such, the melamine-impregnated melamine-impregnated
(제 3 공정 ; (3rd process; S3S3 - 적층 공정) -Lamination process)
본 공정은 제 2 공정(S1)에 의해 반 경화되는 상태로 멜라민 수지가 함침 처리된 멜라민 함침 크레프트 페이퍼(30)를 이용하여, 적층하기 위한 공정이다.This process is a process for laminating | stacking using the melamine impregnated
먼저, 도 2 에서 보는바와 같이 최하부에는 일반적으로 상용화 되고 있는 페놀수지를 함침한 페놀함침 크레프트 페이퍼(즉 TEGO 필름)(10)이 위치되도록 하고, 그 페놀함침 크레프트 페이퍼(10) 상면으로 합판(20)을 적층하고, 상기 합판(20) 상면으로 상기의 제 2 공정(S1)에 의해 얻게 된 멜라민 함침 크레프트 페이퍼(30)를 적층하고, 그 상면으로 다시 미함침 글래스 페이퍼(GLASS PAPER)(40)를 적층하게 된다.First, as shown in FIG. 2, the phenol-impregnated kraft paper (that is, TEGO film) 10 impregnated with a phenol resin generally commercialized is positioned at the lowermost part, and the
여기서, 상기 글래스 페이퍼(40)는 한국 카본에서 생산된 제품을 사용하였는바, 그 무게는 30 g/㎡ ~ 60 g/㎡ 를 갖는 경량의 글래스 페이퍼(Glass Paper)를 이용하였다.Here, the
한편, 상기의 미함침 글래스 페이퍼(40) 상면으로 다시 제 2 공정(S2)을 거 쳐 얻게 되는 멜라민 함침 크래프트 페이퍼(30)를 적층하게 된다.Meanwhile, the melamine-impregnated
이와같이 상기 수지등이 미함침된 글래스 페이퍼(Glass Paper)를 가운데에 위치되도록 한 상태에서 그 상하로 각각 멜라민 함침 크래프트 페이퍼(Kraft paper)(30)를 위치시키게 되면, 멜라민 함침 크래프트(30)에 발생되는 크랙 현상이 방지됨을 알게 되었다.In this way, when the resin or the like impregnated glass paper (Glass Paper) is located in the center of the melamine impregnated kraft paper (Kraft paper) 30 is placed on the top and bottom, respectively, it occurs in the melamine impregnated craft (30) It has been found that the crack phenomenon is prevented.
이때, 각각의 적층면마다 접착층(1)을 형성하여 가접되는 상태에 있게 한다.At this time, the adhesive layer 1 is formed on each laminated surface to be in a state of being welded.
(제 4 공정 ; (4th process; S4S4 - - 열압Heat pressure 프레싱Pressing 공정) fair)
본 공정은 상기한 제 3 공정인 적층공정(S3)을 거쳐 상기한 순서에 의해 적층된 상태에서 상기한 접착층(1)에 의해 가접되어 있는 거푸집패널(100)을 20 kgf/㎠ ~ 25 kgf/㎠ 의 단위압력을 갖는 열압 프레스에서 170 ℃ 의 온도를 120 ~ 180 초간 유지하며 열압 프레싱하게 된다.This process is 20 kgf / ㎠ ~ 25 kgf / to formwork panel 100 which is welded by the adhesive layer (1) in the state of being laminated by the above procedure through the lamination step (S3) which is the third step. In a thermopress press having a unit pressure of cm 2, the pressurized press is maintained while maintaining a temperature of 170 ° C. for 120 to 180 seconds.
(제 5 공정 ; (5th process; S5S5 - 건조공정) -Drying process)
본 공정은 상기한 제 4 공정인 열압 프레싱 공정(S4)을 거쳐 각각 적층구조사이의 접착층(1)간의 견고한 접합성을 갖는 거푸집패널(100)을 얻은 다음에, 자연 건조 상태에서 약 48 시간 건조시켜 완성된 거푸집패널(100)을 얻게 된다.This process obtains the formwork panel 100 having a firm bond between the adhesive layers 1 between the laminated structures, respectively, through the hot pressing process S4, which is the fourth process, and then dried for about 48 hours in a natural dry state. The finished formwork panel 100 is obtained.
상기한 각 공정을 거쳐 얻게 된 본 발명의 거푸집패널(100)을 이용하여, 내알카리성 테스트와 내마모성 테스트, 한열 반복시험 등을 공지의 방법을 통하여 실험한 결과 아래의 표와 같은 결과를 얻게 되었다.Using the formwork panel 100 of the present invention obtained through each of the above process, the alkali resistance test, abrasion resistance test, thermal repetition test and the like through a well-known method as a result of the results shown in the table below.
< 표 1 > 기존 TEGO 필름에 의한 거푸집 패널과 본 발명에 의한 거푸집 패널간 물성비교 테스트 결과 <Table 1> Property comparison test result between formwork panel using existing TEGO film and formwork panel according to the present invention
표에서 보는 바와 같이 개발 거푸집 패널은 본 발명의 공정에 의해 생산된 시료패널을 이용하였고, 종래 거푸집 패널 1은 패널 상하에 각각 45g 규격의 TEGO 필름이 부착된 패널에 의해 시험하였으며, 종래 거푸집 패널 2는 패널 상하에 각각 45g 규격의 TEGO 필름이 부착되어지되 상면측으로 동일 규격으로 되는 또 다른 TEGO 필름에 의한 2매의 TEGO 필름이 부착되는 거푸집 패널을 의미한다.As shown in the table, the development formwork panel used a sample panel produced by the process of the present invention, the conventional formwork panel 1 was tested by a panel with a 45g standard TEGO film attached to the top and bottom of the panel, the conventional formwork panel 2 Means a formwork panel to which a TEGO film of 45g standard is attached to the top and bottom of the panel, but two TEGO films are attached to each other by another TEGO film having the same standard on the upper side.
먼저, 5% NaOH 의 분위기내에서 12시간 동안 내알칼리성 시험을 한 결과, 본 발명에 의해 개발되는 거푸집 패널(100) 에서는 도 3의 사진에서 보는 바와 같이 그 표면으로 변화가 거의 발생 되지 않고 있음을 확인할 수 있다.First, as a result of an alkali resistance test for 12 hours in an atmosphere of 5% NaOH, in the formwork panel 100 developed according to the present invention, as shown in the photograph of FIG. You can check it.
그러나, 이와는 달리 종래 거푸집 패널 1, 2 등에서는 도 4의 사진에서 보는바와 같이 변색 되거나 또는 표면이 부풀어 오르는 현상을 발견할 수 있었다.However, unlike the conventional formwork panel 1, 2, etc., the phenomenon of discoloration or swelling of the surface was found as shown in the photograph of FIG.
따라서, 내알칼리성에 대한 강한 내성은 본원 발명에 의해 제시되는 거푸집패널의 중요한 인자로 작용되어 사용빈도수의 증가 및 우수한 이형 성질을 갖는 거푸집 패널을 얻을 수 있게 된다.Therefore, the strong resistance to alkali resistance acts as an important factor of the formwork panel proposed by the present invention, and thus it is possible to obtain a formwork panel having an increase in the frequency of use and excellent release properties.
한편, 80℃ 의 조건에서 2시간 및 20℃ 조건에서의 2시간 동안 2회 반복 하며 한열 반복 시험을 실시한 결과, 전체 거푸집패널에서 아무런 변화가 일어나지 않음을 확인 할 수 있다.On the other hand, the result of repeating the thermal test twice for 2 hours at 80 ℃ and 2 hours at 20 ℃ conditions, it can be seen that no change occurs in the entire formwork panel.
아울러 내마모성 테스트의 경우, AA180의 마모지를 사용하여,500g의 하중으로 60 rpm 시험속도에 의해 테스트 되었으며, 50 % 마모시에는 종료하고 200 회전 후 교체하는 방식으로 테스트 한 결과, 본원에 의한 거푸집패널의 경우 1,600 회 정도에서도 내마모성을 갖는 것으로 확인되고 있으며, 그 이외에 종래 거푸집패널 1은 650회, 종래 거푸집패널 2는 1,400 회 정도에서 그치고 있어, 종래 TEGO 필름으로 되는 거푸집패널보다 그 내마모성이 우수한 것을 확인할 수 있다.In addition, the wear resistance test, using the AA180 wear paper, was tested at a test speed of 60 rpm at a load of 500g, and when tested at 50% wear by replacing after 200 revolutions, In the case of 1,600 times, it has been confirmed that the wear resistance is, and in addition, the conventional formwork panel 1 is only 650 times, the conventional formwork panel 2 is stopped at about 1,400 times, it can be confirmed that the wear resistance is superior to the formwork panel made of the conventional TEGO film. have.
한편, 본 발명에 의한 거푸집 패널(100)과 종래의 거푸집 패널 1,2를 각각 100 ℃ 의 온도범위에서 약 2시간 가량 삶은 결과 본 발명에서의 거푸집 패널(100) 에서는 표면에 약간의 기포가 발생되는 반면에, 종래 거푸집 패널 1,2 의 표면층에서는 본 발명의 거푸집 패널(100)보다도 많은 수의 기포가 발생되었다.On the other hand, the formwork panel 100 and the conventional formwork panel 1 and 2 according to the present invention are boiled for about 2 hours at a temperature range of 100 ° C., respectively. On the other hand, in the surface layer of the formwork panels 1 and 2, more bubbles were generated than the formwork panel 100 of the present invention.
상기의 표에 의한 물성시험에서 보는 바와 같이, 본 발명에 의한 거푸집 패널의 경우 종래의 거푸집 패널보다 내알칼리성이 상당히 우수한 장점을 갖고 있음을 알 수 있으며, 내마모성이 종래의 타 거푸집 패널보다 상대적으로 우수함을 알 수 있었다.As shown in the physical property test according to the above table, it can be seen that the formwork panel according to the present invention has an advantage of considerably better alkali resistance than the conventional formwork panel, and the wear resistance is relatively superior to other formwork panels. And it was found.
따라서 본 발명의 상기한 각 공정을 거쳐 얻게 되는 거푸집 패널의 경우, Therefore, in the case of the formwork panel obtained through each of the above-described steps of the present invention,
멜라민 수지를 이용하여 함침처리한 크래프트 페이퍼 사용으로 인한 내, 알카리성 및 평활성이 우수하고, 크랙 현상 등이 발생되지 않으며 내충격성 및 수회에 걸친 사용 회수의 증가 및 콘크리트 타설 후 판면과의 우수한 이형성을 얻을 수 있게 되는 효과를 기대할 수 있다.Excellent resistance against alkali, smoothness and smoothness due to the use of kraft paper impregnated with melamine resin, no cracking, etc. You can expect the effect to be possible.
이상에서는 본 발명을 특정의 바람직한 실시예를 들어 도시하고 설명하였으나, 본 발명은 상기한 실시예에 한정되지 아니하며 본 발명의 정신을 벗어나지 않는 범위 내에서 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 다양한 변경과 수정이 가능할 것이다.Although the present invention has been shown and described with reference to certain preferred embodiments, the present invention is not limited to the above-described embodiments and has ordinary skill in the art to which the present invention pertains without departing from the spirit of the present invention. Various changes and modifications may be made by the user.
Claims (8)