KR100746176B1 - Magnetic adhesive tape and a method for manufacturing the magnetic adhesive tape - Google Patents

Magnetic adhesive tape and a method for manufacturing the magnetic adhesive tape Download PDF

Info

Publication number
KR100746176B1
KR100746176B1 KR1020050071734A KR20050071734A KR100746176B1 KR 100746176 B1 KR100746176 B1 KR 100746176B1 KR 1020050071734 A KR1020050071734 A KR 1020050071734A KR 20050071734 A KR20050071734 A KR 20050071734A KR 100746176 B1 KR100746176 B1 KR 100746176B1
Authority
KR
South Korea
Prior art keywords
tape
adhesive
self
adhesive tape
release agent
Prior art date
Application number
KR1020050071734A
Other languages
Korean (ko)
Other versions
KR20060101168A (en
Inventor
훙-치 우
Original Assignee
훙-치 우
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 훙-치 우 filed Critical 훙-치 우
Publication of KR20060101168A publication Critical patent/KR20060101168A/en
Application granted granted Critical
Publication of KR100746176B1 publication Critical patent/KR100746176B1/en

Abstract

자기접착테이프 및 자기접착테이프 제조방법이다. 고효능 이형제와 개질제가 연자성 재료에 첨가되고 서로 혼합되어 이형가능(releasable) 표면을 가지는 스트립형 연자성 기재(substrate)를 형성한다. 기재의 한 면은 정제되거나 거칠게 되고 고효능 접착층으로 피복된다. 기재는 릴에 감긴다. 감긴 기재의 외부 끝은 사용을 위해 한 조각씩 밖으로 끌어 당겨진다. 따라서, 자기접착테이프를 제조할 때, 어떠한 이형제도 테이프에 피복할 필요가 없다. 그러므로, 제조시간은 단축되고 비용은 절감된다.Self-adhesive tape and self-adhesive tape manufacturing method. High potency release agents and modifiers are added to the soft magnetic material and mixed with each other to form a strip-like soft magnetic substrate having a releasable surface. One side of the substrate is purified or roughened and coated with a high potency adhesive layer. The substrate is wound on a reel. The outer end of the wound substrate is pulled out one piece for use. Therefore, when producing the self-adhesive tape, no release agent needs to be coated on the tape. Therefore, manufacturing time is shortened and cost is saved.

자기접착테이프, 제조시, 이형제, 첨가 Self-adhesive tape, during manufacture, release agent, addition

Description

자기접착테이프 및 자기접착테이프 제조방법{Magnetic adhesive tape and a method for manufacturing the magnetic adhesive tape}Magnetic adhesive tape and a method for manufacturing the magnetic adhesive tape

도 1은 본 발명의 제조공정 흐름;1 is a manufacturing process flow of the present invention;

도 2는 본 발명의 제품의 사시도; 및2 is a perspective view of a product of the present invention; And

도 3은 본 발명의 다른 제품의 사시도.3 is a perspective view of another product of the present invention.

* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings

60 : 얇은 테이프 63 : 접착제60: thin tape 63: adhesive

65 : 자기접착테이프 66 : 줄무늬65: self adhesive tape 66: stripes

본 발명은 자기(magnetic)접착테이프 및 자기접착테이프 제조방법에 관한 것으로, 더 상세하게는 접착성 및 자기인력(magnetic attraction) 둘 다를 가지는 자기접착테이프에 관한 것이다.The present invention relates to a magnetic adhesive tape and a method for manufacturing the magnetic adhesive tape, and more particularly, to a magnetic adhesive tape having both adhesiveness and magnetic attraction.

기존의 접착테이프는 일상 생활에서 폭 넓게 사용되고 있다. 기존의 접착테이프의 한 면은 접착제로 피복되어 있다. 이 테이프는 릴에 감긴다. 사용시, 테이프의 외부 끝은 밖으로 끌어 당겨지고 물품에 부착하기 위해 조각들로 절단된다.Conventional adhesive tapes are widely used in daily life. One side of the conventional adhesive tape is coated with an adhesive. This tape is wound on a reel. In use, the outer end of the tape is pulled out and cut into pieces to attach to the article.

기존의 단면 접착테이프의 테이프 몸체는 주로 PVC 또는 EVA와 같은 연성 플라스틱 재료로 이루어진다. 접착층이 테이프 몸체의 한 면에 피복된다. 테이프 몸체는 릴에 감긴다.The tape body of conventional single-sided adhesive tape is mainly made of soft plastic material such as PVC or EVA. An adhesive layer is coated on one side of the tape body. The tape body is wound on a reel.

상기 기존의 접착테이프는 필요에 따라 개량되거나 변형될 수 있다. 예를 들면, 얇은 연자성(soft magnetic) 스트랩이 기재(substrate)로서 사용될 수 있다. 이형제와 접착제는 기재의 두 면들에 각각 피복될 수 있다. 대만특허출원 제93202971호는 자기접착테이프를 개시하고 있다. 접착층이 자성 기재의 한 면에 피복되어 있다. 이형제는 자성 기재의 다른 면에 피복되어 있다. 감을 때, 이형제는 접착층이 다른 면에 접착하는 것을 방지한다. 그러므로, 사용되었을 때, 접착테이프는 감기지 않을 수 있다.The existing adhesive tape may be improved or modified as necessary. For example, a thin soft magnetic strap can be used as the substrate. The release agent and the adhesive may be coated on both sides of the substrate, respectively. Taiwan Patent Application No. 93202971 discloses a self-adhesive tape. The adhesive layer is coated on one side of the magnetic substrate. The release agent is coated on the other side of the magnetic substrate. When wound, the release agent prevents the adhesive layer from adhering to the other side. Therefore, when used, the adhesive tape may not be wound.

본 발명은 이형제를 테이프에 피복할 필요가 없는 자기접착테이프 및 자기접착테이프 제조방법을 제공함에 있다.The present invention provides a self-adhesive tape and a method for producing a self-adhesive tape which do not require a release agent to be coated on the tape.

본 발명의 주된 목적은 자기접착테이프 및 자기접착테이프 제조방법을 제공함에 있다. 고효능 이형제와 개질제가 연자성 재료에 직접 첨가되고 서로 혼합되어 전체 표면이 고른 이형(離型)효과를 가지는 테이프를 형성한다. 테이프의 한 면은 정제되거나 거칠게 되고 고효능 접착층으로 피복된다. 접착층은 테이프의 표면으로부터 쉽게 박리되지 않고 그래서 테이프의 접착력은 향상된다. 더구나, 당해 자기접착테이프를 제조할 때, 임의의 이형제로 테이프를 피복하는 것이 필요하지 않다. 그러므로, 제조절차가 단순화된다.It is a main object of the present invention to provide a self-adhesive tape and a self-adhesive tape manufacturing method. High-efficiency release agents and modifiers are added directly to the soft magnetic material and mixed with each other to form a tape having an even release effect on the entire surface. One side of the tape is purified or roughened and coated with a high potency adhesive layer. The adhesive layer does not easily peel off from the surface of the tape so that the adhesive strength of the tape is improved. Moreover, when producing the self-adhesive tape, it is not necessary to coat the tape with any release agent. Therefore, the manufacturing procedure is simplified.

본 발명의 추가의 목적은 상기 자기접착테이프 및 그 제조방법을 제공함에 있다. 테이프를 만들 때, 테이프의 표면은 엠보서(embosser)로 동시에 돋을새김되어 밀집한 줄무늬(dense stripe)들이 형성된다. 돋을새김된 표면의 줄무늬들에 의해, 테이프는 어떠한 칼도 사용하지 않고 손으로 찢을 수 있어 테이프의 이용을 용이하게 한다.It is a further object of the present invention to provide a self-adhesive tape and a method of manufacturing the same. When making a tape, the surface of the tape is embossed at the same time to form dense strips. With the stripes of the embossed surface, the tape can be torn by hand without using any knife to facilitate the use of the tape.

위의 목적들에 의하면, 본 발명의 자기접착테이프는 고효능 이형제 및 개질제가 연자성 재료에 첨가되고 서로 혼합되어 이형가능(releasable) 표면을 가진 스트립형 연자성 기재를 형성하게끔 만들어진다. 기재의 한 면은 정제되거나 거칠게 되고 고효능 접착층으로 피복된다. 이 기재는 릴에 감긴다. 감긴 기재의 외부 끝은 사용을 위해 한 조각씩(또는 한 부분씩) 밖으로 끌어당겨 질 수 있다. 따라서, 기재의 한 면은 물품의 뒷면에 접착하기 위한 접착층으로 피복된다. 기재의 다른 면은 벽면 또는 판면(board face)에 끌어 당겨져 부착하기 위한 자기인력을 가진다.According to the above objects, the self-adhesive tape of the present invention is made such that a high-efficiency release agent and a modifier are added to the soft magnetic material and mixed with each other to form a strip soft magnetic substrate having a releasable surface. One side of the substrate is purified or roughened and coated with a high potency adhesive layer. This substrate is wound on a reel. The outer end of the wound substrate can be pulled out one piece (or one part) for use. Thus, one side of the substrate is covered with an adhesive layer for adhering to the back side of the article. The other side of the substrate has a magnetic force to attract and attach to the wall or board face.

이하 본 발명의 바람직한 실시예가 첨부 도면들을 참조하여 상세히 설명될 것이다.DESCRIPTION OF THE PREFERRED EMBODIMENTS Preferred embodiments of the present invention will now be described in detail with reference to the accompanying drawings.

이제 도 1 및 2를 참조한다. 본 발명의 자기접착테이프는 바륨, 스트론튬, 루비듐, 코발트, 붕소 또는 산화제2철 분말과 같은 자화가능 재료(10), 고무/플라스틱복합재료(20), 포화지방산에스테르유도체와 같은 고효능 이형제(30), 및 유화칼슘비누 및 지방산의 혼합물과 같은 개질제(40)로부터 만들어진다. 위의 재료들은 고르게 혼합된(50) 후 얇은 테이프(60)로 만들어진다. 그 후, 테이프(60)의 적어도 한 면은 롤러들로 닦이거나 화학적으로 정제되거나(거칠게 되거나) 또는 아크(arc)에 의해 분극화된다(61). 그 후 테이프(60)는 자화된다(62). 그 후 정제된 면은 접착제(63)로 피복된다. 그 후 테이프(60)는 벗겨지고 감기어(64) 자기접착테이프(65)를 형성한다.Reference is now made to FIGS. 1 and 2. The self-adhesive tape of the present invention is a highly effective release agent such as magnetizable material (10), rubber / plastic composite material (20), saturated fatty acid ester derivative (30), such as barium, strontium, rubidium, cobalt, boron or ferric oxide powder. ) And a modifier 40 such as a mixture of calcium soap and fatty acid. The above materials are evenly mixed 50 and then made into a thin tape 60. Thereafter, at least one side of the tape 60 is wiped with rollers, chemically purified (roughed) or polarized 61 by an arc. The tape 60 is then magnetized 62. The purified side is then covered with adhesive 63. The tape 60 is then peeled off and wound 64 to form a self-adhesive tape 65.

제조 시, 고효능 이형제(30)가 테이프(60)에 첨가된다. 그러므로, 전체 테이프(60) 자체의 표면은 높은 이형 능력을 가진다. 따라서, 그 표면에는 접착제가 거의 접착할 수 없다. (표면처리 후, 접착력은 향상될 수 있다.) 그러므로, 감긴 후, 접착제가 없는 표면은 접착제 피복을 가지는 표면으로부터 쉽게 이형(또는 분리)될 수 있다.In manufacture, a high potency release agent 30 is added to the tape 60. Therefore, the surface of the entire tape 60 itself has a high release ability. Therefore, the adhesive hardly adheres to the surface. (After surface treatment, the adhesion may be improved.) Therefore, after winding, the surface without adhesive can be easily released (or separated) from the surface with the adhesive coating.

게다가, 형성 절차 중 접착제가 없는 테이프(60) 표면이 엠보서로써 밀집하게 돋을새김되어 줄무늬들(66, 도 3에 보인 것 참조)을 형성하는 경우, 테이프(60)는 어떠한 칼도 이용하지 않고 손으로 찢어낼 수 있다. 더구나, 테이프의 돋을새김된 표면의 줄무늬들(66)은 이형능력(releasability)을 향상시키기 위해 테이프 표면과 접착피복물인 접착제(63) 사이의 접촉면적을 축소할 수 있다.In addition, in the case where the surface of the adhesive-free tape 60 is embossed with an embosser to form streaks 66 (see FIG. 3) during the forming procedure, the tape 60 is hand-free without using any knife. You can tear it off. Moreover, the stripes 66 of the embossed surface of the tape can reduce the contact area between the tape surface and the adhesive 63, the adhesive coating, to improve releasability.

위의 실시예는 본 발명을 예로써 설명하기 위한 사용된 것뿐이고 본 발명의 범위를 제한하기 위해 의도된 것은 아니다. 위의 실시예의 많은 변형들이 본 발명의 정신으로부터 벗어남 없이 만들어질 수 있다.The above embodiments are only used to illustrate the present invention by way of example and are not intended to limit the scope of the present invention. Many variations of the above embodiments can be made without departing from the spirit of the invention.

이상 설명한 바와 같이, 본 발명에 의하면, 위의 자기접착테이프를 제조할 때, 어떠한 이형제도 테이프에 피복할 필요가 없다. 그러므로, 제조시간은 단축되 고 비용은 절감된다. 더욱이, 전체 테이프는 균일하고 신뢰성 있는 이형(또는 분리) 효과를 가진다. 표면 처리 후, 테이프는 접착제와 테이프를 확고히 접합하기 위해 접착제로 피복된다. 돋을새김된 표면의 줄무늬들에 의해, 테이프는 어떠한 칼도 사용하지 않고 손으로 찢어낼 수 있어 테이프의 사용을 용이하게 한다. As described above, according to the present invention, when producing the above self-adhesive tape, no release agent needs to be coated on the tape. Therefore, manufacturing time is shortened and cost is saved. Moreover, the entire tape has a uniform and reliable release (or separation) effect. After surface treatment, the tape is coated with an adhesive to firmly bond the adhesive and the tape. The stripes of the embossed surface allow the tape to be torn off by hand without using any knife to facilitate the use of the tape.

Claims (12)

자기접착테이프에 있어서, 고효능 이형제가 첨가된 기다란 자기테이프를 포함하여, 테이프의 전체 표면이 높은 이형능력을 가지고, 테이프의 한 면은 접착층과의 접착력을 향상시키도록 표면처리된 후 접착층으로 피복되어 있는 자기접착테이프.In self-adhesive tape, the entire surface of the tape has a high release ability, including an elongated magnetic tape to which a high-efficiency release agent is added, and one side of the tape is coated with an adhesive layer after surface treatment to improve adhesion to the adhesive layer. Self-adhesive tape. 삭제delete 제1항에 있어서, 테이프의 표면은 그 표면이 아크에 의해 분극화되도록 표면처리된 자기접착테이프.2. The self-adhesive tape of claim 1 wherein the surface of the tape is surface treated such that the surface is polarized by an arc. 제1항 또는 제3항에 있어서, 테이프의 표면은 밀집한 줄무늬들을 가지게끔 돋을새김된 자기접착테이프.4. The self-adhesive tape of claim 1 or 3, wherein the surface of the tape is embossed to have dense stripes. 자기접착테이프를 제조하기 위한 방법에 있어서,In the method for producing a self-adhesive tape, 자화가능 재료, 고무/플라스틱복합재료, 고효능 이형제 및 개질제를 서로 혼합하고 그 혼합물을 균일하게 섞는 단계;Mixing the magnetizable material, the rubber / plastic composite material, the high potency release agent and the modifier with each other and uniformly mixing the mixture; 상기 혼합물로부터 얇은 테이프를 만드는 단계;Making a thin tape from the mixture; 테이프의 적어도 한 면을 그 한 면과 접착제 사이의 접착력을 형상시키도록 표면 처리하는 단계;Surface treating at least one side of the tape to form an adhesion between the one side and the adhesive; 테이프를 자화하는 단계; 및Magnetizing the tape; And 처리된 면에 접착제를 피복하는 단계를 포함하는 자기접착테이프 제조방법.Self-adhesive tape manufacturing method comprising the step of coating the adhesive on the treated surface. 삭제delete 제5항에 있어서, 테이프의 상기 면은 그 면이 아크에 의해 분극화되도록 표면 처리되는 자기접착테이프 제조방법.6. The method of claim 5 wherein the face of the tape is surface treated such that the face is polarized by an arc. 제5항 또는 제7항에 있어서, 고효능 이형제는 포화지방산에스테르유도체인 자기접착테이프 제조방법.The method for producing a self-adhesive tape according to claim 5 or 7, wherein the high-efficiency release agent is a saturated fatty acid ester derivative. 제5항 또는 제7항에 있어서, 개질제는 유화칼슘비누 및 지방산의 혼합물인 자기접착테이프 제조방법.8. The method of claim 5 or 7, wherein the modifier is a mixture of calcium soap and fatty acid. 제5항 또는 제7항에 있어서, 얇은 테이프를 만들 때, 테이프의 표면은 엠보서로써 동시에 돋을새김되어 줄무늬들을 형성하는 자기접착테이프 제조방법.8. A method according to claim 5 or 7, wherein when making a thin tape, the surface of the tape is embossed simultaneously with embossers to form stripes. 제8항에 있어서, 얇은 테이프를 만들 때, 테이프의 표면은 엠보서로써 동시 에 돋을새김되어 줄무늬들을 형성하는 자기접착테이프 제조방법.The method of claim 8, wherein when making a thin tape, the surface of the tape is embossed simultaneously with embossers to form streaks. 제9항에 있어서, 얇은 테이프를 만들 때, 테이프의 표면은 엠보서로써 동시에 돋을새김되어 줄무늬들을 형성하는 자기접착테이프 제조방법.10. The method of claim 9, wherein when making a thin tape, the surface of the tape is embossed simultaneously with embossers to form streaks.
KR1020050071734A 2005-03-16 2005-08-05 Magnetic adhesive tape and a method for manufacturing the magnetic adhesive tape KR100746176B1 (en)