KR100720735B1 - The rainwater manhole of water permeability type and the making method thereof - Google Patents

The rainwater manhole of water permeability type and the making method thereof Download PDF

Info

Publication number
KR100720735B1
KR100720735B1 KR1020050063044A KR20050063044A KR100720735B1 KR 100720735 B1 KR100720735 B1 KR 100720735B1 KR 1020050063044 A KR1020050063044 A KR 1020050063044A KR 20050063044 A KR20050063044 A KR 20050063044A KR 100720735 B1 KR100720735 B1 KR 100720735B1
Authority
KR
South Korea
Prior art keywords
permeable
rainwater
manhole
water
concrete composition
Prior art date
Application number
KR1020050063044A
Other languages
Korean (ko)
Other versions
KR20070008097A (en
Inventor
염진포
Original Assignee
우일산업개발주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 우일산업개발주식회사 filed Critical 우일산업개발주식회사
Priority to KR1020050063044A priority Critical patent/KR100720735B1/en
Publication of KR20070008097A publication Critical patent/KR20070008097A/en
Application granted granted Critical
Publication of KR100720735B1 publication Critical patent/KR100720735B1/en

Abstract

본 발명은 보도나 차도의 도로변에 설치되는 우수(雨水) 맨홀에 관한 것으로, 더욱 상세하게는 내부가 빈 직육면체형으로 하부는 막혀있고 상부는 유입구가 형성되어 있는 통상의 우수맨홀에 있어서, 우수맨홀의 하단부에서부터 상부쪽 1/5 내지 1/4 높이까지는 내부에 유입된 우수가 지중으로 자연 배출되도록 투수성 콘크리트조성물로 형성된 투수부로 되어 있고 상기 투수부의 상부는 내부에 유입된 우수가 투수되지 못하도록 비투수성 콘크리트조성물로 형성된 비투수부로 되어 있되 상기 비투수부의 일측면 하부에는 배수관이 구비되어 있어 일정높이의 우수는 배수관을 통해 배수됨과 동시에 상기 투수부에 고여 있는 우수는 땅속으로 자연 배수되도록 되어 있는 것을 특징으로 하는 투수식 우수맨홀 및 그 제조방법에 관한 것이다. The present invention relates to a rainwater manhole installed on the side of a sidewalk or a roadway, and more particularly, in a rainwater manhole having a hollow inside and a lower portion thereof and a top portion thereof formed with an inlet. From the lower part of the upper part to the upper 1/5 to 1/4 height, the rainwater flows into the ground to be naturally discharged into the ground. The non-permeable part formed by the water-based concrete composition, but one side lower portion of the non-permeable part is provided with a drain pipe so that the rain of a certain height is drained through the drain pipe and the rain stuck to the permeable part is to be naturally drained into the ground. The present invention relates to a water-permeable rainwater manhole and a manufacturing method thereof.

투수식 우수맨홀, 투수부, 비투수부, 배수관, 유입구 Storm Manhole, Pitcher, Non-Pitcher, Drain, Inlet

Description

투수식 우수맨홀 및 그 제조방법{The rainwater manhole of water permeability type and the making method thereof}The rainwater manhole of water permeability type and the making method

도 1은 본 발명에 따른 투수식 우수맨홀의 사시개략도.1 is a perspective schematic view of a water-permeable rainwater manhole according to the present invention.

도 2는 본 발명에 따른 투수식 우수맨홀의 단면개략도.Figure 2 is a schematic cross-sectional view of the water-permeable rainwater manhole according to the invention.

도 3은 본 발명에 따른 투수식 우수맨홀의 배수관을 통해 우수가 배출되는 동시에 투수부를 통해 땅속으로 투수되는 상태를 도시한 단면 개략도.Figure 3 is a schematic cross-sectional view showing a state in which rainwater is discharged through the water discharge pipe of the water-permeable rainwater manhole according to the present invention through the pitcher into the ground.

<도면의 주요부분에 대한 부호의 설명>  <Description of the symbols for the main parts of the drawings>

1 : 투수식 우수맨홀 2 : 유입구1: Pitcher Type Excellent Manhole 2: Inlet

삭제delete

3 : 투수부 4 : 비투수부3: pitcher 4: non-pitcher

삭제delete

5 : 배수관5: drain pipe

본 발명은 보도나 차도의 도로변에 설치되는 우수(雨水) 맨홀에 관한 것으로, 더욱 상세하게는 내부가 빈 직육면체형으로 하부는 막혀있고 상부는 유입구가 형성되어 있는 통상의 우수맨홀에 있어서, 우수맨홀의 하단부에서부터 상부쪽 1/5 내지 1/4 높이까지는 내부에 유입된 우수가 지중으로 자연 배출되도록 투수성 콘크리트조성물로 형성된 투수부로 되어 있고 상기 투수부의 상부는 내부에 유입된 우수가 투수되지 못하도록 비투수성 콘크리트조성물로 형성된 비투수부로 되어 있되 상기 비투수부의 일측면 하부에는 배수관이 구비되어 있어 일정높이의 우수는 배수관을 통해 배수됨과 동시에 상기 투수부에 고여 있는 우수는 땅속으로 자연 배수되도록 되어 있는 것을 특징으로 하는 투수식 우수맨홀 및 그 제조방법에 관한 것이다. The present invention relates to a rainwater manhole installed on the side of a sidewalk or a roadway, and more particularly, in a rainwater manhole having a hollow inside and a lower portion thereof and a top portion thereof formed with an inlet. From the lower part of the upper part to the upper 1/5 to 1/4 height, the rainwater flows into the ground to be naturally discharged into the ground. The non-permeable part formed by the water-based concrete composition, but one side lower portion of the non-permeable part is provided with a drain pipe so that the rain of a certain height is drained through the drain pipe and the rain stuck to the permeable part is to be naturally drained into the ground. The present invention relates to a water-permeable rainwater manhole and a manufacturing method thereof.

일반적으로 도심지에 설치된 통상의 우수맨홀은 보도나 차도의 도로변에 설치되어 도로변을 따라 흐르는 우수(雨水)를 모아 하천으로 방류시키도록 되어 있는 것으로, 내부가 빈 직육면체형으로 하부는 막혀있고 상부는 유입구가 형성되어 있으며 전체적으로 시멘트, 자갈, 모래, 물, 혼화제 등이 일정비율로 혼합되어 공극율이 5~8% 정도로 유지되도록 다짐 작업된 비투수성 콘크리트 조성물로 형성되어 있어 내부로 유입된 우수가 벽체나 바닥면을 통해서는 외측으로 투수되지 못하도록 되어 있고 우수맨홀의 일측면 하부에 구비된 배수관을 통해서만 배출되어 상기 배수관을 통해 연결된 하천 등으로 방류되도록 되어 있었다.In general, the rainwater manhole installed in the downtown area is installed on the side of the sidewalk or roadway to collect rainwater flowing along the roadside and discharge it into the river. Is composed of cement, gravel, sand, water, admixture, etc., and is made of non-permeable concrete composition that is compacted to maintain the porosity of 5 ~ 8% by mixing at a certain ratio. It is not to be permeable to the outside through the surface was discharged only through the drain pipe provided on one side lower portion of the rain manhole to be discharged to the river and the like connected through the drain pipe.

그러나, 상기와 같이 도심지에 설치된 종래의 통상적인 우수맨홀은 전체적으로 비투수성 콘크리트조성물로 되어 있고 상기 우수맨홀로 우수(雨水)를 유입시키도록 되어 있는 도로포장면 또한 아스팔트 포장 등의 비투수층으로 되어 있어 우수는 땅속으로 스며들지 못하며 비투수층인 도로포장면을 따라 우수맨홀 내부로 곧 바로 유입되고 비투수성 콘크리트조성물로 된 우수맨홀의 내부로 유입된 우수는 우수맨홀의 벽체나 바닥면을 통해서는 외측으로 투수되지 않고 전량 배수관을 통해 하천으로만 방류되도록 되어 있어 땅속의 지하수 자원확보가 어렵게 되고 도심지의 도로변에 심어진 가로수의 성장에 필요한 수분을 충분히 공급하지 못하며 홍수시에는 급격한 우수의 증가로 하천이 범람하게 되거나 또는 우수맨홀을 통해 역류되는 문제점이 있었다.However, the conventional rainwater manhole conventionally installed in the city center is made of a non-water-permeable concrete composition as a whole, and the road pavement surface in which rainwater flows into the rainwater manhole is also made of a non-water-permeable layer such as asphalt pavement. Rainwater does not penetrate into the ground and flows directly into the rainwater manhole along the non-permeable road pavement and flows into the rainwater manhole made of non-permeable concrete composition to the outside through the wall or floor of the rainwater manhole. It is difficult to secure groundwater resources in the ground because it is only discharged to the river through the drainage pipe, not permeable, and it does not supply enough water for the growth of roadside trees planted on the roadside in the downtown area. Or have a problem that flows back through the storm manhole The.

본 발명은 상기와 같은 문제점들을 해결하기 위한 것으로, 우수맨홀의 하부에 형성된 투수부를 통해 일정 높이까지의 우수는 우수맨홀의 바닥면이나 하부벽체를 통해 투수되어 땅속으로 스며들도록 함으로써 땅속의 지하수 자원을 확보하고 도심지의 도로변에 심어진 가로수 등의 성장에 필요한 수분을 공급함과 동시에 홍수시에는 우수맨홀로 유입된 우수가 일정량씩 땅속으로 지속적으로 투수되어 우수가 하천으로만 방류되는 것을 방지하여 하천이 범람하거나 우수맨홀을 통해 역류되는 것을 방지하도록 하는 것에 그 목적이 있다.The present invention is to solve the above problems, the rainwater to a certain height through the permeable portion formed in the lower part of the rainwater manhole is permeated through the bottom surface or lower wall of rainwater manhole so that the groundwater resources in the ground It secures water and supplies necessary water for the growth of roadside trees planted on roadsides in urban areas, and at the same time, floods flow by preventing rainwater from being discharged only into rivers by preventing the rainwater that has flowed into the rainwater manhole continuously into the ground. The purpose is to prevent backflow through the storm manhole.

이러한 목적을 달성하기 위하여 내부가 빈 직육면체형으로 하부는 막혀있고 상부는 유입구가 형성되어 있는 통상의 우수맨홀에 있어서, 우수맨홀의 하단부에서부터 상부쪽 1/5 내지 1/4 높이까지는 투수성 콘크리트조성물로 형성된 투수부로 되어 있고 상기 투수부의 상부는 내부에 유입된 우수가 투수되지 못하도록 비투수성 콘크리트조성물로 형성된 비투수부로 되어 있되 상기 비투수부의 일측면 하부에는 배수관이 구비되어 있어 일정높이의 우수는 배수관을 통해 배수됨과 동시에 상기 투수부에 고여 있는 우수는 땅속으로 자연 배수되도록 되어 있는 것에 본 발명의 특징이 있다. In order to achieve this purpose, in a conventional rainwater manhole having a hollow inside and having a hollow bottom, and having an inlet formed therein, a permeable concrete composition is formed from the bottom of the rainwater manhole to the height of 1/5 to 1/4 of the upper portion. It is made of a water-permeable part and the upper part of the water-permeable part is a non-water-permeable part formed of a non-water-permeable concrete composition so that the rainwater introduced into the inside is not permeable. At the same time being drained through the rainwater accumulated in the permeable part is characterized in that the natural drainage to the ground.

이하 본 발명에 따른 바람직한 구성을 도면에 의해 상세히 설명하면 다음과 같다.Hereinafter, the preferred configuration according to the present invention will be described in detail with reference to the drawings.

본 발명에 따른 투수식 우수맨홀(1)은 도 1 내지 3에 도시된 바와 같이 보도나 차도의 도로변에 설치되어 도로변을 따라 흐르는 우수(雨水)를 모아 하천으로 방류시키도록 되어 있는 것으로, 전체적으로 내부가 빈 직육면체형으로 하부는 막혀 있고 상부는 유입구(2)가 형성되어 있으며, 우수맨홀(1)의 하단부에서부터 상부쪽 1/5 내지 1/4 높이까지는 내부에 유입된 우수가 지중으로 자연 배출되도록 투수성 콘크리트조성물로 형성된 투수부(3)로 되어 있고 상기 투수부(3)의 상부는 내부에 유입된 우수가 투수되지 못하도록 비투수성 콘크리트조성물로 형성된 비투수부(4)로 되어 있되 상기 비투수부(4)의 일측면 하부에는 배수관(5)이 구비되어 있어 일정높이의 우수는 배수관(5)을 통해 배수됨과 동시에 상기 투수부(3)에 고여 있는 우수는 땅속으로 자연 배수되도록 되어 있다.Water-permeable rainwater manhole (1) according to the present invention is installed on the side of the sidewalk or roadway as shown in Figures 1 to 3 to collect rainwater (flow water) flowing along the roadside to discharge into the river as a whole It is a hollow cuboid, the lower part is blocked and the upper part is formed with an inlet (2). From the lower part of the rainwater manhole (1) to the upper 1/5 to 1/4 height, the rainwater introduced into the ground is naturally discharged into the ground. The permeable part 3 formed of a permeable concrete composition, and the upper part of the permeable part 3 is a non-permeable part 4 formed of a non-permeable concrete composition to prevent the rainwater flowing into the inside of the permeable part ( 4) the drain pipe 5 is provided at the lower side of one side, so that the rainwater having a predetermined height is drained through the drainage pipe 5, and the rainwater accumulated in the pitcher 3 is naturally drained into the ground. It is supposed to be.

상기 투수부(3)는 우수맨홀(1)의 일정높이까지 우수가 고여 있는 상태에서 서서히 투수되면서 땅속으로 스며들도록 하는 부분으로, 우수맨홀(1)의 바닥면과 하부벽체 부분을 구성하도록 우수맨홀(1)의 하단부에서부터 상부쪽 1/5 내지 1/4 높이까지 투수성 콘크리트조성물로 형성되어 있어 내측에 유입된 우수가 투수되면서 땅속으로 스며들도록 되어 있되, 상기 투수부(3)를 형성하는 투수성 콘크리트조성물은 시멘트와 골재와 물과 혼화제가 일정비율로 혼합되고 전체 공극율이 10 ~ 30% 정도로 유지되도록 다짐 작업되어 1.0 × 10-1 ~ 5.0 × 10-1 cm/sec의 투수계수를 지니도록 되어 있어 우수맨홀(1)의 내측으로 유입된 우수가 소정의 시간동안 고여 있으면서 우수맨홀(1)의 바닥면과 하부벽체부분에 해당하는 투수부(3)를 통해 서서히 투수되어 땅속으로 스며들도록 되어 있다. The permeable part 3 is a part to permeate into the ground while slowly permeating in a state where the rainwater is standing up to a certain height of the rainwater manhole 1, and the rainwater manhole to form a bottom surface and a lower wall portion of the rainwater manhole 1. It is formed of a permeable concrete composition from the lower end of (1) to the upper side 1/5 to 1/4 height, so that the rainwater flowing into the ground is permeated into the ground, but the pitcher forming the pitcher (3) The concrete concrete composition has a permeability coefficient of 1.0 × 10 -1 to 5.0 × 10 -1 cm / sec by mixing cement, aggregate, water and admixture in a constant ratio and compacting to maintain the total porosity of about 10 to 30%. The rainwater flowing into the rainwater manhole 1 is accumulated for a predetermined period of time, and gradually penetrates through the pitcher 3 corresponding to the bottom surface and the lower wall portion of the rainwater manhole 1, and soaks into the ground. It is registered.

본 발명에서 상기 투수부(3)를 형성하는 투수성 콘크리트조성물은 통상적으로 알려진 시멘트와 물과 골재와 혼화제가 일정비율로 혼합된 것으로, 시멘트는 포틀랜드 시멘트가 사용되며, 혼화제로는 고성능 감수제가 사용되는데 상기 고성능 감수제는 투수성 콘크리트조성물의 배합시 단위수량(單位水量)을 감소시킴으로써 콘크리트 조성물의 강도저하를 방지하기 위한 화학혼화제로서 통상 필요에 따라 선택적으로 사용되며 시멘트 전체중량에 대하여 0.01~5중량% 첨가되고 주로 나프탈렌계, 멜라민계, 폴리올계 및 폴리카본산계를 단독 또는 1종이상 혼합하여 사용되고, 물은 시멘트에 대하여 20~50중량% 정도로 첨가 혼합되며, 골재는 쇄석골재로서 입도조정된 직경 5~25mm 골재를 투수성 콘크리트조성물 1㎥ 당 40~60부피%가 되도록 첨가 혼합된다.In the present invention, the permeable concrete composition forming the permeable part 3 is a mixture of a known cement, water, aggregate, and admixture in a constant ratio, cement is used as a portland cement, and a high performance water reducing agent is used as the admixture. The high-performance water-reducing agent is a chemical admixture for preventing the strength decrease of the concrete composition by reducing the unit quantity during the blending of the water-permeable concrete composition, usually used as needed, and optionally 0.01 to 5 weight based on the total weight of the cement. % Is added and mainly used naphthalene-based, melamine-based, polyol-based and polycarboxylic acid-based alone or mixed with one or more species, water is added and mixed in about 20 to 50% by weight relative to the cement, aggregate aggregate size as crushed aggregate 5 to 25mm aggregate is added and mixed to 40 to 60% by volume per 1㎥ of permeable concrete composition.

상기 골재는 한국산업규격(KSF 2527)에 따라 골재크기 13~2.5mm 골재는 19mm 체를 전부 통과하고 13mm 체의 통과중량백분율이 90~100%, 10mm 체의 통과중량백분율이 40~75%, 5mm 체의 통과중량백분율이 5~25%, 2.5mm 체의 통과중량백분율이 0~ 10%, 1.2mm 체의 통과중량백분율이 5%이하인 것을 사용하며, 골재크기 10~2.5mm 골재는 13mm 체를 전부통과하고 10mm 체의 통과중량백분율이 85~100%, 5mm 체의 통과중량백분율이 10~30%, 2.5mm 체의 통과중량백분율이 0~10%, 1.2mm 체의 통과중량백분율이 5% 이하인 것을 사용하게 된다.The aggregate according to the Korea Industrial Standard (KSF 2527), the aggregate size 13 ~ 2.5mm aggregate passes all 19mm sieve, 90% to 100% passing weight percentage of 13mm sieve, 40 ~ 75% passing weight percentage of 10mm sieve, The 5% sieve weight percentage is 5-25%, the 2.5mm sieve weight percentage is 0-10%, and the 1.2mm sieve weight percentage is less than 5%, and the aggregate size 10-2.5mm aggregate is 13mm sieve. The through weight percentage of the 10 mm sieve is 85-100%, the through weight percentage of the 5 mm sieve is 10-30%, the passing weight percentage of the 2.5 mm sieve is 0-10%, and the passing weight percentage of the 1.2 mm sieve is 5%. Use less than%.

상기 비투수부(4)는 우수맨홀(1)의 중간벽체 및 상부벽체를 구성하도록 투수부(3)의 상부에 형성되어 있고 내부에 유입된 우수가 외측으로 투수되지 못하도록 전체적으로 비투수성 콘크리트조성물로 형성되어 있으며 비투수부(4)의 일측면 하부에는 통상의 배수관(5)이 구비되어 있되 상기 배수관(5)은 투수부(3)의 경계면 바로 위쪽에 위치되어 있어 상기 투수부(3)의 상부쪽에 고여있는 우수는 배수관(5)을 통해 하천 등으로 방류되도록 되어 있고 배수관(5) 하부에 고여있는 우수는 상기 투수부(3)를 통해 투수되어 땅속으로 스며들도록 되어 있으며, 상기 비투수부(4)를 형성하는 비투수성 콘크리트조성물은 시멘트와 골재와 물과 혼화제가 일정비율로 혼합되고 전체 공극율이 5~8% 정도로 유지되도록 다짐 작업되어 물이 투수되지 못하도록 되어 있어 우수맨홀(1)의 내측으로 유입된 우수가 우수맨홀(1)의 중간벽체와 상부벽체부분에 해당하는 비투수부(4)를 통해서는 투수되지 못하고 하부에 구비된 배수관(5)을 통해서만 방류되도록 되어 있다. The non-permeable part 4 is formed on the upper part of the permeable part 3 so as to constitute the middle wall and the upper wall of the rain manhole 1, and is formed entirely of a non-permeable concrete composition to prevent the rainwater flowing into the outside. In the lower part of one side of the non-water permeable part 4, a normal drain pipe 5 is provided, and the drain pipe 5 is located directly above the boundary of the water permeable part 3, so The rainwater that is standing is discharged to the river through the drain pipe (5), and the rainwater that is accumulated in the bottom of the drain pipe (5) is permeated through the pitcher (3) to penetrate into the ground, the non-water permeability (4) The non-permeable concrete composition that forms the cement is mixed with cement, aggregate, water and admixture at a constant ratio, and is compacted so that the overall porosity is maintained at about 5-8%. Rainwater introduced into the hole 1 is not permeable through the non-permeable portion 4 corresponding to the middle wall and the upper wall portion of the rain manhole 1, and is discharged only through the drain pipe 5 provided at the lower portion. have.

본 발명에서 상기 비투수부(4)를 형성하는 비투수성 콘크리트조성물은 통상적으로 알려진 시멘트와 물과 골재와 혼화제가 일정비율로 혼합된 것으로, 시멘트는 포틀랜드 시멘트가 사용되며, 혼화제로는 고성능 감수제가 사용되는데 상기 고성능 감수제는 비투수성 콘크리트조성물의 배합시 단위수량(單位水量)을 감소시킴으로써 콘크리트 조성물의 강도저하를 방지하기 위한 화학혼화제로서 통상 필요에 따라 선택적으로 사용되며 시멘트 전체중량에 대하여 0.01~5중량% 첨가되고 주로 나프탈렌계, 멜라민계, 폴리올계 및 폴리카본산계를 단독 또는 1종이상 혼합하여 사용되고, 물은 시멘트에 대하여 40~60중량% 정도로 첨가 혼합되며, 골재는 자갈과 모래의 혼합물로서 비투수성 콘크리트조성물 1㎥ 당 40~60부피%가 되도록 첨가 혼합되어 비투수성 콘크리트조성물의 공극율을 5~8%로 유지하도록 되어 있되, 자갈은 입도조정된 직경 5~25mm의 자갈이 사용되며 모래는 직경 0.1~2.0mm의 모래가 사용되고 자갈과 모래의 배합비율은 1 : 0.7~0.8의 중량비로 혼합된 것이 사용된다.In the present invention, the non-permeable concrete composition forming the non-permeable part 4 is a mixture of a known cement, water, aggregate, and admixture in a fixed ratio, cement is used as a portland cement, and a high performance water reducing agent is used as the admixture. The high-performance water-reducing agent is a chemical admixture for preventing the strength reduction of the concrete composition by reducing the unit water amount when mixing the non-permeable concrete composition, usually used selectively as needed, 0.01 to 5% by weight of the total weight of the cement % Is added and mainly used naphthalene-based, melamine-based, polyol-based and polycarboxylic acid-based alone or mixed with one or more species, water is added and mixed in about 40 to 60% by weight relative to cement, aggregate is bitter as a mixture of gravel and sand Non-permeable concrete by adding and mixing to 40 ~ 60% by volume per 1㎥ of aqueous concrete composition The porosity of the composition is to be maintained at 5-8%, but the gravel is a particle size of 5 ~ 25mm gravel is used, the sand is 0.1 ~ 2.0mm diameter sand and the ratio of gravel and sand is 1: 0.7 ~ Mixtures in a weight ratio of 0.8 are used.

본 발명에 따른 투수식 우수맨홀(1)의 제작과정은 다음과 같다.The manufacturing process of the pitcher type excellent manhole (1) according to the present invention is as follows.

우수맨홀(1)의 유입구(2) 부분이 하부쪽으로 위치되도록 거꾸로 뒤짚힌 상태의 우수맨홀용 성형틀에 먼저 통상의 시멘트와 물과 자갈과 모래와 혼화제가 일정비율로 혼합되어 공극율이 5~8%로 다짐 작업된 비투수성 콘크리트조성물을 상기 성형틀의 3/4~4/5 높이까지 채워 넣어 비투수부(4)를 형성한 다음, 상기 비투수성 콘크리트조성물이 굳지 않은 상태에서 곧 바로 통상의 시멘트와 물과 골재와 혼화제가 일정비율로 혼합되고 공극율이 10~30%로 다짐작업되어 1.0×10-1~ 5.0×10-1 cm/sec의 투수계수를 지니도록 되어 있는 투수성 콘크리트조성물을 나머지 높이까지 전체적으로 채워 넣어 투수부(3)를 형성한 후, 50~60℃의 온도에서 8~10시간 정도 초기양생하고 탈형하여 상온에서 6~8일간 2차 양생하고 상기 비투수부(4)의 일측면 하부에 배수관(5)을 일체로 관통 연설하여 본 발명에 따른 투수식 우수맨홀(1)을 완성하게 된다. First, the cement and water, gravel, sand and admixture are mixed in a constant ratio in the molding mold for rainwater manhole, which is inverted so that the inlet (2) portion of the rainwater manhole (1) is positioned downward. Fill the non-permeable concrete composition compacted by% to the height of 3/4 to 4/5 of the forming mold to form the non-permeable portion 4, and then immediately cement in the state where the non-permeable concrete composition is not hardened. Water, aggregate, and admixture are mixed in a certain ratio, and the porosity is compacted to 10 ~ 30% so that the water-permeable concrete composition having a permeability coefficient of 1.0 × 10 -1 to 5.0 × 10 -1 cm / sec After filling up to the height as a whole to form the permeable part (3), the initial curing at 50 ~ 60 ℃ temperature for about 8 to 10 hours and demoulded, the second curing at room temperature for 6 to 8 days and the work of the non-permeable part (4) Integrated drain pipe (5) through the lower side Set to the permeability equation is finished solid manhole (1) according to the present invention.

상기 제작과정에서 성형틀에 비투수부(4)를 먼저 채워넣어 거꾸로 형성하는 이유는 공극율이 큰 투수부(3)를 성형틀에 먼저 채워 넣게 되면, 비투수부(4)의 하중에 의해 투수부(3)가 압착되어 투수율이 떨어지게 되는 문제점이 발생하게 되므로 공극율이 큰 투수부(3)가 상부쪽에 위치되도록 거꾸로 제작하게 된다.The reason why the non-permeable part 4 is firstly filled in the forming mold in the manufacturing process is that the permeable part 3 having a large porosity is first filled in the molding die, and the permeable part 4 is loaded by the load of the non-permeable part 4. 3) is pressed, so that the problem that the permeability is lowered, so the permeability (3) having a large porosity is made upside down to be located on the upper side.

상기와 같이 본 발명에 의하면 우수맨홀의 하부에 형성된 투수부를 통해 일정 높이까지의 우수는 우수맨홀의 바닥면과 하부벽체부분을 통해 투수되어 땅속으 로 스며들도록 함으로써 땅속의 지하수 자원을 확보하고 도심지의 도로변에 심어진 가로수 등의 성장에 필요한 수분을 공급함과 동시에 홍수시에는 우수맨홀로 유입된 우수가 투수부를 통해 일정량씩 땅속으로 지속적으로 투수되어 우수가 하천으로만 방류되는 것을 방지하여 하천이 범람하거나 우수맨홀을 통해 역류되는 것을 방지하도록 하는 효과가 있다. As described above, according to the present invention, the rainwater up to a certain height through the pitcher formed in the lower part of the rainwater manhole is permeated through the bottom surface and the lower wall of the rainwater manhole, so as to penetrate into the ground, thereby securing groundwater resources in the ground and At the same time, it supplies water necessary for the growth of roadside trees planted on the roadside, and during the flood, the rainwater flowing into the rainwater manhole is continuously pumped into the ground by a certain amount to prevent rainwater from being discharged only into the river. There is an effect to prevent backflow through the manhole.

Claims (3)

보도나 차도의 도로변에 설치되어 도로변을 따라 흐르는 우수를 모아 하천으로 방류시키도록 되어 있으며 내부가 빈 직육면체형으로 하부는 막혀있고 상부는 유입구가 형성되어 있되 일부는 시멘트와 물과 골재와 혼화제가 일정비율로 혼합된 통상의 비투수성 콘크리트조성물로 형성되어 있고 일부는 내부에 유입된 우수가 지중으로 투수되어 자연 배출되도록 투수성 콘크리트조성물로 형성된 우수맨홀에 있어서, It is installed on the side of the sidewalk or roadway to collect rainwater flowing along the side of the road and discharge it into the river. The inside is empty rectangular shape, the lower part is blocked and the upper part is formed with inlet, but some of the cement, water, aggregate and admixture are constant. In the rainwater manhole formed of a permeable concrete composition is formed of a conventional non-permeable concrete composition mixed in proportion and partly so that the rainwater flows into the ground and is naturally discharged, 상기 우수맨홀(1)의 하단부에서부터 상부쪽 1/5 내지 1/4 높이까지는 투수성 콘크리트조성물로 형성된 투수부(3)로 되어 있고, 상기 투수부(3)의 상부는 내부에 유입된 우수가 투수되지 못하도록 비투수성 콘크리트조성물로 형성된 비투수부(4)로 되어 있되, 상기 비투수부(4)의 일측면 하부에는 상기 투수부(3)와의 경계면 바로 위쪽에 배수관(5)이 구비되어 있어 일정높이의 우수는 배수관(5)을 통해 배수됨과 동시에 우수맨홀(1)의 바닥면과 하부벽체부분에 해당하는투수부(3)에 고여 있는 우수는 상기 투수부(3)를 통해 서서히 투수되어 땅속으로 자연 배수되도록 되어 있는 것을 특징으로 하는 투수식 우수맨홀.From the lower end of the rain manhole (1) to the upper side 1/5 to 1/4 height of the permeable part (3) formed of a permeable concrete composition, the upper part of the water permeable part (3) The non-permeable part (4) formed of a non-permeable concrete composition so as not to be permeable, but a lower portion of one side of the non-permeable part (4) is provided with a drain pipe (5) just above the interface with the permeable part (3) Rainwater is drained through the drain pipe (5) and at the same time rainwater accumulated in the permeable part (3) corresponding to the bottom surface and the lower wall portion of the rainwater manhole (1) is slowly permeated through the permeable part (3) into the ground Pitcher-type excellent manhole, characterized in that the natural drainage. 제1항에 있어서, 상기 투수부(3)는 시멘트와 골재와 물과 혼화제가 일정비율로 혼합되고, 전체 공극율이 10-30% 정도이고, 1.0×10-1 - 5.0×10-1 ㎝/sec의 투수계수를 지니도록 되어 있는 투수성 콘크리트 조성물로 되어 있는 것을 특징으로 하는 투수식 우수맨홀.According to claim 1, wherein the permeable part 3 is a mixture of cement, aggregate, water and admixture in a constant ratio, the total porosity is about 10-30%, 1.0 × 10 -1-5.0 × 10 -1 cm / Water-permeable manhole, characterized in that the permeable concrete composition is to have a permeability coefficient of sec. 내부가 빈 직육면체형으로 하부는 막혀있고 상부는 유입구가 형성되도록 우수맨홀용 성형틀에 시멘트와 물과 골재와 혼화제가 일정비율로 혼합된 통상의 비투수성 콘크리트조성물을 채워 넣은 다음, 일정시간동안 양생하고 탈형한 후, 일측면 하부에 배수관을 관통 연결하여 제조되는 우수맨홀의 제조방법에 있어서, The inside is filled with a rectangular parallelepiped type, and the upper part is filled with an ordinary non-permeable concrete composition in which cement, water, aggregate, and admixture are mixed at a predetermined ratio so that the inlet is formed, and then cured for a predetermined time. After demolding, in the manufacturing method of rainwater manhole manufactured by connecting the drain pipe through the lower side, 상기 우수맨홀(1)의 유입구(2) 부분이 하부쪽으로 위치되도록 거꾸로 뒤짚힌 상태의 우수맨홀용 성형틀에 먼저 시멘트와 물과 자갈과 모래와 혼화제가 일정비율로 혼합되어 공극율이 5~8%로 다짐 작업된 비투수성 콘크리트조성물을 상기 성형틀의 3/4~4/5 높이까지 채워 넣어 비투수부(4)를 형성한 다음, 상기 비투수성 콘크리트조성물이 굳지 않은 상태에서 곧 바로 시멘트와 물과 골재와 혼화제가 일정비율로 혼합되고 공극율이 10~30%로 다짐 작업 되어 1.0×10-1 ~5.0×10-1cm/sec의 투수계수를 지니도록 되어 있는 투수성 콘크리트조성물을 나머지 높이까지 전체적으로 채워 넣어 투수부(3)를 형성한 후 50~60℃의 온도에서 8~10시간 정도 초기양생하고 탈형하여 상온에서 6~8일간 2차 양생하여 제조되는 것을 특징으로 하는 투수식 우수맨홀의 제조방법. Cement, water, gravel, sand and admixture are mixed at a constant ratio in the molding mantle for rainwater manhole, which is inverted so that the inlet (2) portion of the rainwater manhole (1) is positioned downward, and the porosity is 5-8%. Filling the non-permeable concrete composition to the height of 3/4 ~ 4/5 of the molding frame to form a non-permeable part (4), immediately after the non-permeable concrete composition is not hardened with cement and water Aggregate and admixture are mixed in a certain ratio and the porosity is compacted to 10 ~ 30% so that the permeable concrete composition which has a permeability coefficient of 1.0 × 10 -1 to 5.0 × 10 -1 cm / sec to the rest of the height After forming the permeable part (3) after the initial curing for about 8 to 10 hours at a temperature of 50 ~ 60 ℃ and demoulding to manufacture a water-permeable excellent manhole, characterized in that the secondary curing for 6 to 8 days at room temperature Way.
KR1020050063044A 2005-07-13 2005-07-13 The rainwater manhole of water permeability type and the making method thereof KR100720735B1 (en)