KR100718445B1 - Decoration panel of thermosetting resins and manufacturing method thereof - Google Patents
Decoration panel of thermosetting resins and manufacturing method thereof Download PDFInfo
- Publication number
- KR100718445B1 KR100718445B1 KR1020060035732A KR20060035732A KR100718445B1 KR 100718445 B1 KR100718445 B1 KR 100718445B1 KR 1020060035732 A KR1020060035732 A KR 1020060035732A KR 20060035732 A KR20060035732 A KR 20060035732A KR 100718445 B1 KR100718445 B1 KR 100718445B1
- Authority
- KR
- South Korea
- Prior art keywords
- paper
- thermosetting resin
- decorative plate
- kraft paper
- present
- Prior art date
Abstract
본 발명은 화장판의 크라프트지 층 또는 무늬지 층에 염을 일정 함량으로 부가한 열경화성수지를 함침함으로 색상에 대한 제한이 없으며 전도성이 우수하여 전자파 차단효과가 우수한 열경화성수지 화장판 및 그 제조방법에 관한 것으로, 본 발명의 열경화성수지 화장판은 크라프트지, 무늬(모양)지, 보호지(overlay paper)로 이루어지는 화장판에 있어서, 상기 화장판을 구성하는 크라프트지 및 무늬(모양)지의 하나 또는 그 전부는 열경화성수지에 염을 일정량으로 혼합한 수지를 코팅 또는 함침하여 이루어짐을 특징으로 한다.The present invention is not limited to color by impregnating a thermosetting resin with a predetermined amount of salt added to the kraft paper layer or patterned layer of the decorative plate and excellent in electromagnetic shielding effect thermosetting resin decorative plate and its manufacturing method The thermosetting resin decorative plate of the present invention comprises a kraft paper, a pattern paper and an overlay paper, wherein one or all of the kraft paper and the pattern paper constituting the decorative board. Is characterized in that it is made by coating or impregnating a resin mixed with a predetermined amount of salt in the thermosetting resin.
상기와 같이 구성되는 본 발명의 열경화성수지 화장판은 기재층이 특정의 색에 제한되지 않으므로 모양지의 사용에 제한이 없고 크라프트지 뿐 아니라 무늬지에도 염을 함침함으로 전도성을 부여할 수 있어 화장판의 다양한 변형 및 모양의 제공이 가능하고, 또한 우수한 전자파 차단효과도 가질 뿐 아니라, 본 발명에 따른 제조 방법에 의해 용이하게 제조됨으로 제조원가가 저렴하고 또한 폐기시 환경오염을 유발하지 않는 환경 친화적 화장판을 제공하는 유용한 발명이다.The thermosetting resin decorative plate of the present invention configured as described above is not limited to a specific color of the base layer, so there is no restriction on the use of paper and impregnated with salt as well as kraft paper to impart conductivity to the decorative plate. It is possible to provide various modifications and shapes, and also has excellent electromagnetic wave blocking effect, and is easily manufactured by the manufacturing method according to the present invention, which is low in manufacturing cost and does not cause environmental pollution when disposed of. It is a useful invention to provide.
화장판, 크라프트지, 모양지, 카본블랙, 전도성 Vanity board, kraft paper, shape paper, carbon black, conductive
Description
도 1은 본 발명에 따른 열경화성수지 화장판의 단면도이다.1 is a cross-sectional view of a thermosetting resin decorative plate according to the present invention.
* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings
1 --- 크라프트지 층 2 --- 무늬지 층1 --- kraft paper layer 2 --- patterned paper layer
3 --- 보호층 3 --- protective layer
본 발명은 열경화성수지 화장판 및 그 제조방법에 관한 것으로, 보다 자세하게는 화장판의 크라프트지 층 또는 무늬지 층에 염을 일정 함량으로 부가한 열경화성수지를 함침함으로 색상에 대한 제한이 없으며 전도성이 우수하여 전자파 차단효과가 우수한 열경화성수지 화장판 및 그 제조방법에 관한 것이다.The present invention relates to a thermosetting resin decorative plate and a method for manufacturing the same, and more particularly, by impregnating a thermosetting resin with a predetermined amount of salt in a kraft paper layer or a patterned paper layer of the decorative plate, there is no restriction on color and excellent conductivity. The present invention relates to a thermosetting resin decorative plate having excellent electromagnetic wave blocking effect and a method of manufacturing the same.
일반적으로 합판, 중밀도섬유판(MDF), 하드보드(hardboard), 파티클보드(particle board)와 같은 소위 목질계 기초재 뿐 아니라 기타의 각종 재질의 판 표면에는 표면 보호, 모양 부여, 전도성이나 난연성 등과 같은 특정의 기능을 부여 등의 목적으로 지(紙), 열가소성수지 시이트, 열경화성수지 함침지 등으로 구성되는 화장 시이트를 적층, 고착하여 화장피복층을 형성하는데, 이러한 화장피복층을 일반적으로 화장판이라고 통칭하는데, 이러한 화장판은 도포용 건축판, 가구류의 표면장식판 등 각종 용도로 이용되고 있는데, 자세하게는 기능용 크린룸, 전산실의 전도성바닥 및 내장재, 난연성이 요구되는 각종 내장재, 건축구조물 및 내장용, 파티숀 표면재, 화장실칸막이 도어의 표면재, 바닥재, 산업용 책상 등 가구내ㆍ외장재, 연구실의 실험대 등으로도 사용되며, 호텔, 식당, 다방 등의 벽, 천정, 바닥재, 진열대, 안내대의 장식용, 실내 경기장의 코트, 이동식 칸막이 등, 철도 및 지하철 차량 내장, 버스, 선박 내장용, 컴퓨터실 및 기계실의 바닥재, 엘리베이터 내부벽, 전자조립작업대, 전기절연체 대용 등 그 용도가 아주 광범위하다.In general, surface protection, shaping, conductivity or flame retardancy may be applied to the surface of boards of various materials as well as so-called wood based materials such as plywood, medium density fiber board (MDF), hard board, and particle board. For the purpose of imparting such a specific function, a cosmetic sheet composed of paper, a thermoplastic resin sheet, a thermosetting resin impregnated paper, or the like is laminated and adhered to form a cosmetic coating layer, which is generally referred to as a makeup plate. However, these decorative boards are used for various purposes such as application plates for building and surface decoration plates of furniture, and more specifically, functional clean rooms, conductive floors and interior materials of computer rooms, various interior materials requiring flame retardancy, architectural structures and interiors, and parties. Shaun surface material, surface material of toilet partition door, flooring material, interior and exterior furniture such as industrial desk, laboratory table etc. Walls, ceilings, floors, display stands, guides for decoration of hotels, restaurants, cafes, courtyards of indoor stadiums, mobile partitions, interiors of railway and subway vehicles, buses, ship interiors, floors of computer and machine rooms, elevators Its use is very wide such as internal wall, electronic assembly work table, and electric insulator substitute.
그런데, 이러한 화장판은 각각 그 구성을 달리함으로 화장판이 점착되는 가구 등에 기능성을 부여하기 위해 각종의 특성이 부여되는데, 예를 들어 화장판에 난연성을 부여함으로 화장판이 가공된 설비나 가구 등에 난연성을 부여하거나, 또는 화장판에 무늬를 부여하여 그 기능성을 향상하여오고 있는 실정이다.By the way, such a makeup plate is given a variety of properties in order to impart functionality to the furniture and the like to which the makeup plate is adhered by varying its configuration, for example, by providing a flame retardancy to the makeup plate, the flame retardancy to the equipment or furniture processed It is a situation to improve the functionality by giving or giving a pattern to a makeup board.
특히, 근년에 들어서는 전자기기의 급속한 개발과 사용의 급증으로 인하여 인체에 유해하다고 알려진 전자파가 일상생활에 과도하게 발생되고 있어 생활환경을 해치고 있으며, 따라서 이러한 문제점을 해결하기 위하여 각종의 전자파를 차단 할 수 있는 화장판이 제안되었는데, 이와 같이 화장판이 전자파를 차단하는 기본적인 원리는 화장판에 전도성을 부여함으로서 대기 중의 방전된 전자파를 흡수하여 제거하는 방식인데, 예를 들어 종래에는 전자파 방지용 화장판으로서, 전도성이 강한 카본블랙 파우더를 크라프트지에 코팅하거나 함침시킨 것을 기재로 하여 화장판을 제조하였는데, 구체적으로는 전도성 열경화성수지 화장판은 크라프트지에 전도성 카본블랙 파우더 혹은 염료를 코팅하거나 함침용 수지에 혼합하여 함침하는 방식으로 작업이 이루어지며 그 후 표면에 보호지(overlay paper)를 적층하고 성형하여 전도성 열경화성수지 화장판을 제작하였다.In particular, in recent years, due to the rapid development and use of electronic devices, electromagnetic waves, which are known to be harmful to the human body, are excessively generated in everyday life, thus harming the living environment. Therefore, in order to solve these problems, The basic principle of blocking the electromagnetic waves is a method of absorbing and removing the discharged electromagnetic waves in the air by applying conductivity to the cosmetic plate. For example, conventionally, a cosmetic plate for preventing electromagnetic waves, The strong carbon black powder was coated on or impregnated with kraft paper to prepare a decorative plate. Specifically, the conductive thermosetting resin decorative plate was coated with conductive carbon black powder or dye on kraft paper or mixed with impregnating resin to impregnate it. The way things work After that, a protective paper (overlay paper) was laminated and molded on the surface to prepare a conductive thermosetting resin decorative plate.
그러나, 이와 같이 제조된 화장판은 혼합된 카본블랙이 전도성이 약하여 완전한 전자파 흡수효과가 약하고, 더욱이 일정 두께 이상을 가지는 모양지가 사용될 경우에는 전도성이 더욱 약화되어 전자파 흡수효과가 미미할 뿐 아니라, 상기 카본블랙은 흑색이기 때문에 기재층은 항상 흑색이 된다는 단점이 있었다. 더욱이 이러한 색상이 제한된다는 단점을 해소하기 위해 거의 동일한 특성을 갖는 카본화이트 파우더를 사용하여 흰 색상을 표현할 수 있지만 이 경우에도 특정한 색상인 흰색에 제한될 뿐 아니라, 카본화이트는 고가의 제품이라 제조단가가 상승하고 카본블랙에 비하여 전도성이 떨어진다는 단점이 있다. However, the decorative plate thus prepared is weak in conductivity because the mixed carbon black is weak in conductivity, and furthermore, when a shape paper having a predetermined thickness or more is used, the conductivity is further weakened, so that the electromagnetic wave absorption effect is insignificant. Since black is black, there is a disadvantage that the base layer is always black. Moreover, in order to solve the drawback of this limited color, carbon white powder having almost the same characteristics can be used to express a white color, but in this case, the white color is not only limited to a specific color, but carbon white is an expensive product. There is a disadvantage that the rise and the conductivity is inferior to the carbon black.
따라서, 이러한 문제점을 해결하기 위하여 대한민국 특허출원 제2005-0027132호는 "페놀수지나 요소수지중에서 선택된 어느 한가지의 열경화성수지를 함침시킨 크라프트지를 기재로하여 그 위에 메라민수지나 요소수지중에서 선택된 어느 한가지의 열경화성수지를 함침시킨 모양지 및 보호지(overlay paper)를 차례로 적층한 후 열압착시켜 화장판을 제조함에 있어서, 상기 모양지와 보호지중 어느 한가지나 또는 두가지 모두에 함침할 열경화성 합성수지에 산화티탄(티탄화이트;TiO2)를 상기 열경화성 합성수지 전체함량에 대하여 1~10wt%를 첨가하여 혼합한 다음 화장판을 제조하는 것으로 구성됨을 특징으로하는 전도성 화장판"을 개시하고 있으며, 동 제2003-0061960호는 "목판에 화장재를 접착하고 코팅하여 되는 인테리어용 화장판에 있어서, 숯 목초액으로 되는 유해파차단기능 내지 원적외선을 방출하는 기능성희석액을 더 포함하여 되는 유해파차단 목판(1)에, 분말로 구성된 유해파 차단기능 내지 음이온을 방출하는 기능성분말을 더 포함하여 되는 유해파차폐 접착제(2A)가 도포되어지고, 그 상부에는 숯 목초액으로 되는 유해파차단기능 내지 방부기능을 갖는 기능성희석액을 더 포함하여 된 유해파차단 화장재(3)가 가접착되어진 후, 금이나 은으로 되는 유해파차단분말 내지 항균기능을 더 포함하는 희석액이 분무되어 열압하는 것으로 되는 유해파차단 접착판재(6)를 제공하고, 상기 유해파차단 접착판재(6)의 상면에 분말로 구성된 금 내지 은으로 되는 유해파차단 물질을 포함하고 있는 도료 내지 내오염 기능성도료를 더 포함하여 되는 차폐도료에 의해 코팅층(7A)이 형성되어 있는 구성을 갖는 것을 특징으로 하는 유해파차단 화장판"을 개시하고 있다.Accordingly, in order to solve this problem, Korean Patent Application No. 2005-0027132 discloses "Kraft paper impregnated with any one of thermosetting resins selected from phenolic resins and urea resins. Titanium oxide (titanium (titanium oxide) on the thermosetting synthetic resin to be impregnated in either or both White; TiO2) is added to 1 to 10wt% of the total amount of the thermosetting synthetic resin, and then mixed with a conductive plate, characterized in that consisting of producing a decorative plate ", 2003-0061960 discloses" In the interior decorative board that is bonded and coated with a cosmetic material on a wooden board, the charcoal wood vinegar The harmful shielding adhesive (2A) is further applied to the harmful shielding wooden board (1), which further comprises a harmful shielding function or a functional diluent which emits far infrared rays, further comprising a functional ingredient emitting a harmful wave blocking function or anion composed of powder. After the harmful blocking material (3), which further comprises a harmful diluent having a charcoal wood vinegar, or a functional diluent having an antiseptic function, is temporarily bonded to the upper portion thereof, the harmful blocking agent powder or antibacterial function is formed of gold or silver. Further comprising a harmful barrier blocking plate 6 which is sprayed by a diluent liquid containing a further thermal pressure, and containing a harmful barrier material consisting of gold or silver made of powder on the upper surface of the harmful barrier blocking plate 6 It has a structure in which the coating layer 7A is formed by the shielding paint which further contains a fouling-resistant functional paint. It discloses a barrier screen yuhaepa pad "as.
그러나, 상기의 방법으로는 화장판의 제조비용이 상승할 뿐 아니라 전자파 흡수효과가 만족스럽지 않다 단점이 있다.However, the above-mentioned method not only increases the manufacturing cost of the decorative plate but also has a disadvantage in that the electromagnetic wave absorption effect is not satisfactory.
따라서, 본 발명의 목적은 상기한 종래의 문제점을 해결하기 위해 안출된 것으로, 우수한 전자파 차단효과를 가지도록 일정수준 이상의 전도성을 갖는 열경화성수지 화장판을 제공하기 위한 것이다.Accordingly, an object of the present invention is to provide a thermosetting resin decorative plate having a conductivity of a predetermined level or more to have a good electromagnetic wave blocking effect to be devised to solve the above-mentioned conventional problems.
본 발명의 다른 목적은 기재층 등이 특정한 색상에 제한되지 않는 열경화성수지 화장판을 제공하기 위한 것이다.Another object of the present invention is to provide a thermosetting resin decorative plate, the base layer is not limited to a specific color.
본 발명의 또 다른 목적은 상기 본 발명의 목적을 충족하는 열경화성수지 화장판의 제조방법을 제공하기 위한 것이다.Still another object of the present invention is to provide a method of manufacturing a thermosetting resin decorative plate meeting the object of the present invention.
본 발명자 등은 상기 목적을 달성하기 위하여 예의 연구한 결과 화장판의 일정한 층에 특정한 염을 일정 함량으로 부가함으로 상기한 종래의 문제점을 해결한 열경화성수지 화장판 및 그 제조방법을 제공할 수 있게 됨으로 본 발명을 완성하게 되었다.The present inventors, as a result of earnest research to achieve the above object, it is possible to provide a thermosetting resin decorative plate and a method of manufacturing the same by adding a specific salt to a certain layer of the decorative plate in a predetermined amount. The present invention has been completed.
상기한 본 발명의 목적을 달성하기 위한 열경화성수지 화장판은;Thermosetting resin decorative plate for achieving the above object of the present invention;
크라프트지, 무늬(모양)지, 보호지(overlay paper)로 이루어지는 화장판에 있어서, 상기 화장판을 구성하는 크라프트지 및 무늬(모양)지의 하나 또는 그 전부는 열경화성수지에 염을 일정량으로 혼합한 수지를 코팅 또는 함침하여 이루어짐을 특징으로 한다.In a makeup plate composed of kraft paper, pattern paper, or overlay paper, one or all of the kraft paper and pattern paper constituting the makeup board is a resin in which a salt is mixed in a predetermined amount with a thermosetting resin. Characterized in that the coating or impregnation is made.
본 발명의 다른 구성에 따르면, 상기 염은 열경화성수지 100중량부에 대해 1 내지 4중량부로 혼합됨이 바람직한데, 1중량부 미만으로 혼합되면 전도성이 낮아 바람직하지 않고 4중량부를 초과하면 제조된 열경화성수지 화장판의 물성이 약화되어 바람직하지 않다.According to another constitution of the present invention, the salt is preferably mixed in an amount of 1 to 4 parts by weight based on 100 parts by weight of the thermosetting resin. It is not preferable because the physical properties of the resin decorative plate are weakened.
본 발명의 다른 구성에 따르면, 상기 염은 특정한 것에 한정되지는 않지만 바람직하기로는 염화나트륨(NaCl) 또는 염화칼슘(CaCl2)이다.According to another configuration of the present invention, the salt is not limited to a specific one, but is preferably sodium chloride (NaCl) or calcium chloride (CaCl 2 ).
본 발명의 다른 구성에 따르면, 상기 본 발명의 일 구성에 따라 일정한 조성비로 염이 부가된 열경화성 수지 혼합물에 일반적으로 사용되는 잉크용 염료를 부가하여 특정의 색상을 부여함을 특징으로 한다.According to another configuration of the present invention, according to one configuration of the present invention, it is characterized by adding a dye for an ink generally used in a thermosetting resin mixture to which a salt is added at a constant composition ratio to impart a specific color.
본 발명에 따른 화장판의 일층을 구성하는 상기 표면보호지는 멜라민수지로 함침된 오버레이로써 모양(무늬)지층을 보호하는 역할을 하며, 상기 수지가 함침된 모양지층에서 함침되어지는 수지는 멜라민, 요소, 페놀, 에폭시, 불소 수지가 많이 사용되고 있고, 상기 기재층은 통상적으로 페놀수지 혹은 크레졸수지로 함침된 크라프트지로써 여러 매수의 기재를 사용하여 원하는 두께를 맞추는 역할을 한다.The surface protective paper constituting the first layer of the decorative plate according to the present invention serves to protect the shape (pattern) layer as an overlay impregnated with melamine resin, the resin impregnated in the resin layer impregnated with the resin is melamine, urea , Phenol, epoxy, fluorine resins are used a lot, and the base layer is a kraft paper impregnated with a phenol resin or cresol resin typically serves to match the desired thickness using a number of substrates.
본 발명의 다른 구성에 따른 열경화성수지 화장판의 제조방법은;Method for producing a thermosetting resin decorative plate according to another configuration of the present invention;
열경화성 수지 100중량부에 대해 염 1 내지 4중량부를 부가하고 혼합하여 열경화성 수지혼합물을 제조하는 단계;Preparing a thermosetting resin mixture by adding and mixing 1 to 4 parts by weight of salt with respect to 100 parts by weight of the thermosetting resin;
상기 단계에서 얻어진 열경화성 수지혼합물에 크라프트지 및 무늬(모양)지의 하나 또는 그 전부를 일정시간 함침시키는 함침단계; 및An impregnation step of impregnating the thermosetting resin mixture obtained in the step with one or all of kraft paper and pattern paper; And
상기 열경화성 수지혼합물이 함침된 크라프트지와 무늬(모양)지를 적층하고 그 위에 보호지(overlay paper)를 순차로 적층하여 접함함으로서 화장판을 제조함을 특징으로 한다.The thermosetting resin mixture is impregnated with a kraft paper and a pattern (shape) paper laminated, and a protective paper (overlay paper) on top of each other by laminating a contact to produce a decorative plate.
본 발명의 다른 구성에 따르면, 상기 함침단계는 상기 열경화성 수지혼합물을 크라프트지 및 무늬(모양)지의 하나 또는 그 전부에 일반적인 방법으로 일정두께로 도포하는 도포단계로 대체될 수 있다.According to another configuration of the present invention, the impregnation step may be replaced by an application step of applying the thermosetting resin mixture to one or all of the kraft paper and the pattern (shape) paper at a predetermined thickness in a general manner.
상기와 같이 구성되는 본 발명의 열경화성수지 화장판은 종래에 사용하던 카본 블랙을 대체하여 염을 사용함으로 기재층이 특정의 색에 제한되지 않으므로 모양지의 사용에 제한이 없어 화장판의 다양한 변형 및 모양의 제공이 가능하고, 또한 우수한 전자파 차단효과도 가질 뿐 아니라, 본 발명에 따른 제조 방법에 의해 용이하게 제조됨으로 제조원가가 저렴하고 또한 폐기시 환경오염을 유발하지 않는 환경 친화적 화장판이다. 특히, 본 발명은 상기와 같이 전도성을 부여하기 위해 열경화성수지에 염을 혼합하여 사용함으로 전도성 부가에 따라 색상의 제한이 전혀 없으며, 따라서 여기에 원하는 색상의 잉크용 염료를 더 부가함으로 원하는 색상을 자유롭게 표현할 수 있다는 효과가 있어 제품의 사용범위를 더욱 확대하여 그 효용성을 증가할 수 있다. 또한 상기 염이 부가된 열경화성 수지는 크라프트지 뿐 아니라 무늬지에도 염을 사용할 수 있게 됨으로 전도성을 더욱 향상시킬 수 있다.The thermosetting resin decorative plate of the present invention configured as described above is not limited to the use of paper because the base layer is not limited to a specific color by using a salt in place of the carbon black used in the prior art. It is possible to provide, and also has an excellent electromagnetic shielding effect, and is easily manufactured by the manufacturing method according to the present invention is an environmentally friendly decorative plate that is low in manufacturing cost and does not cause environmental pollution when disposed. In particular, the present invention by using a salt mixed with the thermosetting resin in order to give the conductivity as described above, there is no limitation of the color according to the addition of conductivity, and therefore, the desired color can be freely added by adding a dye for ink of the desired color here There is an effect that can be expressed can be extended to extend the usefulness of the product. In addition, the thermosetting resin to which the salt is added can further improve conductivity by allowing the salt to be used not only in kraft paper but also in patterned paper.
이하 본 발명을 첨부 도면을 참고로 하여 보다 자세하게 설명한다. Hereinafter, the present invention will be described in more detail with reference to the accompanying drawings.
도 1은 본 발명의 열경화성수지 화장판의 단면을 개략적으로 나타내는 도면이다. 도 1에 도시된 바와 같이 본 발명에 따른 열경화성수지 화장판은 크라프트지(1), 무늬(모양)지(2), 보호지(overlay paper)(3)가 순차적으로 적층되고 접합되어 이루어지는데, 상기 크라프트지(1)와 무늬(모양)지(2) 중 적어도 하나 이상은 열경화성 수지 100중량부에 대해 염 1 내지 4중량부를 부가하고 혼합하여 얻어진 열경화성 수지혼합물이 함침되거나 코팅되어져 제조된다.1 is a view schematically showing a cross section of the thermosetting resin decorative plate of the present invention. As shown in Figure 1, the thermosetting resin decorative plate according to the present invention is made of kraft paper (1), pattern (shape) paper (2), protective paper (overlay paper) (3) are sequentially laminated and bonded, At least one of the
이하, 본 발명을 실시예 및 비교예에 의해 보다 자세히 설명하지만 본 발명의 범위가 여기에 한정되는 것이 아님은 물론이다.Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples, but the scope of the present invention is not limited thereto.
실시예Example 1 One
멜라민 수지 100중량부에 대해 염화칼슘 1중량부를 부가 후 혼합하여 열경화성 수지혼합물을 제조하였다. 상기 혼합물에 크라프트지를 침지하여 열경화성 수지혼합물을 함침시킨 후, 크라프트지, 무늬(모양)지, 보호지를 순차적으로 적층하여 융착하여 화장판을 제조하였다.1 part by weight of calcium chloride was added to 100 parts by weight of the melamine resin and mixed to prepare a thermosetting resin mixture. Kraft paper was immersed in the mixture to impregnate the thermosetting resin mixture, and kraft paper, pattern paper, and protective paper were sequentially laminated and fused to prepare a decorative plate.
상기와 같이 제조된 화장판에 대해 내끓임성 및 전도성을 측정하여 다음 표 1에 나타냈다.Boiling resistance and conductivity of the decorative plate prepared as described above were measured and shown in Table 1 below.
실시예Example 2 2
염화칼슘을 2중량부 사용하는 외에는 실시예 1과 동일하게 하여 화장판을 제 조하였다. 상기와 같이 제조된 화장판에 대해 내끓임성 및 전도성을 측정하여 다음 표 1에 나타냈다.A decorative plate was produced in the same manner as in Example 1 except that 2 parts by weight of calcium chloride was used. Boiling resistance and conductivity of the decorative plate prepared as described above were measured and shown in Table 1 below.
실시예Example 3 3
염화칼슘을 3중량부 사용하는 외에는 실시예 1과 동일하게 하여 화장판을 제조하였다. 상기와 같이 제조된 화장판에 대해 내끓임성 및 전도성을 측정하여 다음 표 1에 나타냈다.A decorative plate was prepared in the same manner as in Example 1 except that 3 parts by weight of calcium chloride was used. Boiling resistance and conductivity of the decorative plate prepared as described above were measured and shown in Table 1 below.
실시예Example 4 4
염화칼슘을 4중량부 사용하는 외에는 실시예 1과 동일하게 하여 화장판을 제조하였다. 상기와 같이 제조된 화장판에 대해 내끓임성 및 전도성을 측정하여 다음 표 1에 나타냈다.A decorative plate was prepared in the same manner as in Example 1 except that 4 parts by weight of calcium chloride was used. Boiling resistance and conductivity of the decorative plate prepared as described above were measured and shown in Table 1 below.
실시예Example 5 5
염화칼슘 대신 염화나트륨을 사용하는 외에는 실시예 4와 동일하게 하여 화장판을 제조하였다. 상기와 같이 제조된 화장판에 대해 내끓임성 및 전도성을 측정하여 다음 표 1에 나타냈다.A decorative plate was prepared in the same manner as in Example 4 except that sodium chloride was used instead of calcium chloride. Boiling resistance and conductivity of the decorative plate prepared as described above were measured and shown in Table 1 below.
비교예Comparative example 1 One
염화칼슘을 5중량부 사용하는 외에는 실시예 1과 동일하게 하여 화장판을 제 조하였다. 상기와 같이 제조된 화장판에 대해 내끓임성 및 전도성을 측정하여 다음 표 1에 나타냈다.A makeup plate was produced in the same manner as in Example 1 except that 5 parts by weight of calcium chloride was used. Boiling resistance and conductivity of the decorative plate prepared as described above were measured and shown in Table 1 below.
비교예Comparative example 2 2
통상의 화장판 제조 방법에 따라 크리프트지에 카본블랙 파우더가 혼합된 멜라민 수지를 함침하는 외에는 실시예 1과 동일하게 하여 화장판을 제조하였다. 상기와 같이 제조된 화장판에 대해 내끓임성 및 전도성을 측정하여 다음 표 1에 나타냈다.A cosmetic plate was manufactured in the same manner as in Example 1 except that the melamine resin containing carbon black powder was impregnated with kraft paper according to a conventional cosmetic plate manufacturing method. Boiling resistance and conductivity of the decorative plate prepared as described above were measured and shown in Table 1 below.
상기와 같이 구성되는 본 발명의 열경화성수지 화장판은 종래에 사용하던 카본 블랙을 대체하여 염을 사용함으로 기재층이 특정의 색에 제한되지 않으므로 모양지의 사용에 제한이 없고 크라프트지 뿐 아니라 무늬지에도 염을 함침함으로 전도성을 부여할 수 있어 화장판의 다양한 변형 및 모양의 제공이 가능하고, 또한 우수한 전자파 차단효과도 가질 뿐 아니라, 본 발명에 따른 제조 방법에 의해 용이하게 제조됨으로 제조원가가 저렴하고 또한 폐기시 환경오염을 유발하지 않는 환경 친화적 화장판을 제공하는 유용한 발명이다.The thermosetting resin decorative plate of the present invention configured as described above is not limited to the use of paper because the base layer is not limited to a specific color by using a salt in place of the conventionally used carbon black, and not only kraft paper but also pattern paper It can impart conductivity by impregnating the salt, and thus it is possible to provide various deformations and shapes of the decorative plate, and also has excellent electromagnetic wave blocking effect, and is easily manufactured by the manufacturing method according to the present invention, which makes production cost low and It is a useful invention to provide an environmentally friendly decorative plate that does not cause environmental pollution during disposal.
Claims (6)