KR100716222B1 - Sheet coating membrane complex drainage member and manufacturing method - Google Patents

Sheet coating membrane complex drainage member and manufacturing method Download PDF

Info

Publication number
KR100716222B1
KR100716222B1 KR1020060074892A KR20060074892A KR100716222B1 KR 100716222 B1 KR100716222 B1 KR 100716222B1 KR 1020060074892 A KR1020060074892 A KR 1020060074892A KR 20060074892 A KR20060074892 A KR 20060074892A KR 100716222 B1 KR100716222 B1 KR 100716222B1
Authority
KR
South Korea
Prior art keywords
layer
waterproofing
asphalt
coating
coating film
Prior art date
Application number
KR1020060074892A
Other languages
Korean (ko)
Inventor
박영준
박성락
Original Assignee
주식회사 한양엔티
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 한양엔티 filed Critical 주식회사 한양엔티
Priority to KR1020060074892A priority Critical patent/KR100716222B1/en
Application granted granted Critical
Publication of KR100716222B1 publication Critical patent/KR100716222B1/en

Abstract

본 발명은 방수층의 균일한 품질 수준을 확보하고, 견고하게 부착될 수 있도록 한 도막-시트 복합 방수재 및 그 제작방법을 제공하기 위한 것으로, 상기의 목적을 달성하기 위한 도막-시트 복합 방수재의 구체적인 수단은, 폴리에스테르계 장섬유 또는 단섬유에 도막 방수재와 시트 방수재가 각기 도포 함침되어 있는 도막 방수 보강재층과; 상기 도막 방수 보강재층의 일면에 폴리머로 개량된 개량 아스팔트 컴파운드, 합성고무를 이용한 고무화 아스팔트 컴파운드, 수용성 고무 아스팔트 컴파운드에서 택일된 어느 하나가 도포되어 있는 아스팔트 방수층과; 상기 아스팔트 방수층의 노출면에 일정 구간 길이방향으로 부직포가 부착된 보강부직포층과; 상기 아스팔트 방수층의 노출면에 보강부직포층을 제외한 나머지 부분에 규사가 살포되어서 형성된 규사층으로 이루어진 것을 특징으로 한다.The present invention is to provide a coating-sheet composite waterproofing material and a method of manufacturing the same to ensure a uniform quality level of the waterproofing layer, and to be firmly attached, the specific means of the coating-sheet composite waterproofing material for achieving the above object Silver, the coating film waterproofing reinforcing material layer each impregnated with a coating film waterproofing material and sheet waterproofing material in polyester long fiber or short fiber; An asphalt waterproof layer coated on one surface of the coating film waterproofing reinforcing material layer, which is selected from an improved asphalt compound polymerized, a rubberized asphalt compound using synthetic rubber, and a water-soluble rubber asphalt compound; A reinforcing nonwoven fabric layer having a nonwoven fabric attached to the exposed surface of the asphalt waterproofing layer in a longitudinal direction; It characterized in that the silica sand layer formed by spraying the silica sand on the remaining portion except the reinforcing nonwoven fabric layer on the exposed surface of the asphalt waterproof layer.

방수, 시트, 도막, 방수재, 아스팔트, 보강재, 부직포 Waterproof, sheet, coating, waterproof, asphalt, reinforcement, non-woven

Description

도막-시트 복합 방수재 및 그 제작방법{Sheet coating membrane complex drainage member and manufacturing method}Coating-sheet composite waterproofing material and its manufacturing method {Sheet coating membrane complex drainage member and manufacturing method}

본 명세서에서 첨부되는 다음의 도면들은 본 발명의 바람직한 실시예를 예시하는 것이며, 후술하는 발명의 상세한 설명과 함께 본 발명의 기술사상을 더욱 이해시키는 역할을 하는 것이므로, 본 발명은 그러한 도면에 기재된 사항에만 한정되어서 해석되어서는 아니된다.The following drawings, which are attached in this specification, illustrate preferred embodiments of the present invention, and together with the detailed description of the present invention, serve to further understand the technical spirit of the present invention. It should not be construed as limited to.

도 1은 본 발명에 따른 도막-시트 복합 방수재의 단면도.1 is a cross-sectional view of the coating-sheet composite waterproofing material according to the present invention.

도 2는 본 발명에 따른 도막-시트 복합 방수재에 적용되는 도막 방수 보강재층의 구성도.Figure 2 is a block diagram of a coating film waterproof reinforcing material layer applied to the coating film-sheet composite waterproofing material according to the present invention.

도 3은 도 1은 본 발명에 따른 도막-시트 복합 방수재의 부분 사시도.3 is a partial perspective view of the coating-sheet composite waterproofing material according to the present invention.

도 4는 본 발명에 따른 도막-시트 복합 방수재의 시공 상태도.Figure 4 is a construction state of the coating-sheet composite waterproofing material according to the present invention.

도 5는 본 발명에 따른 도막-시트 복합 방수재간의 접합부 예시도.Figure 5 is an illustration of the junction between the coating film-sheet composite waterproofing material according to the present invention.

도 6은 도막-시트 복합 방수재의 제작공정도6 is a manufacturing process chart of the coating film-sheet composite waterproofing material

<도면의 주요 부분에 대한 부호의 설명><Explanation of symbols for the main parts of the drawings>

11: 도막 방수 보강재층11: coating film reinforcement layer

12: 아스팔트 방수층12: asphalt waterproof layer

13: 보강부직포층13: reinforcing nonwoven fabric layer

14: 규사층14: silica sand layer

21: 도막 방수재21: coating waterproof

22: 시트 방수재22: sheet waterproofing material

본 발명은 각종 건물의 방수를 위해 사용되는 방수재에 관한 것으로, 특히 방수를 위한 방수재 도포 및 양생 작업 없이 현장에서 즉시 시공이 간편하게 이루어지도록 함과 동시에 견고하게 부착 시공될 수 있도록 한 도막-시트 복합 방수재 및 그 제작방법에 관한 것이다.The present invention relates to a waterproofing material used for waterproofing various buildings, and in particular, a coating-sheet composite waterproofing material which allows for easy installation at the same time without the application and curing of the waterproofing material for waterproofing, and at the same time firmly attached construction. And it relates to a manufacturing method.

종래의 방수층 시공 방법인 시트 방수재와 도막 방수재를 적용한 복합 방수층의 형성 방법으로, 현장에서 시트 방수재 설치 후 일정시간이 지난 다음 도막 방수재를 상기 시트 방수재상에 도포하는 방식을 이용하였다.As a method of forming a composite waterproof layer applying a sheet waterproofing material and a coating waterproofing material, which is a conventional waterproofing layer construction method, a method of applying a coating waterproofing material on the sheet waterproofing material after a predetermined time after installing the sheet waterproofing material in the field was used.

그러나 이러한 현장 설치 및 도포 방법은, 콘크리트 등 건물의 바탕면에 직접 시트 방수재를 설치한 이후 도막 방수재를 도포하여 형성하는 방법으로, 시트재의 경우는 균일한 바탕면을 제공함으로서 일정 품질 확보가 가능한 반면, 이후 적용되는 도막방수층은 현장시공이 작업자의 숙련도에 따라 영향을 받기 때문에 일정한 방수층의 두께 확보가 어려운 문제가 있다.However, in the field installation and application method, the sheet waterproofing material is directly installed on the base surface of a building such as concrete, and then the coating waterproofing material is applied. In the case of the sheet material, it is possible to secure a certain quality by providing a uniform base surface. Since the coating layer is applied after the site construction is affected by the skill of the operator, there is a problem that it is difficult to secure the thickness of a certain waterproof layer.

특히, 도막 방수층 형성하는 주된 방법이 롤러를 사용하여 도포하는 방식이므로 이러한 경향이 더욱 심화된다. 또한 시트 방수재와 도막 방수재간 균일한 합 착 및 일체화하기 어렵기 때문에, 결국 제품의 품질관리가 용이하지 않은 문제점이 있으며, 도막재 도포 작업 중 발생하는 물리적 충격에 의한 방수층 손상을 막을 수 없어 방수력이 저하되고 공정이 간편하지 못하여 시공공정성 관리 및 작업성이 저하되는 문제점이 있다.In particular, since the main method of forming the coating film waterproofing layer is a method of applying using a roller, this tendency is further intensified. In addition, since it is difficult to uniformly bond and integrate between the sheet waterproofing material and the coating film waterproofing material, there is a problem in that the quality control of the product is not easy, and thus the waterproofing layer is not prevented due to physical shocks generated during the coating material coating work. There is a problem in that the construction process management and workability is degraded because the process is not easy and low.

더욱이, 기존의 일편향 아스팔트는 견고한 시트상태를 유지하기 어려우며, 시공 온도가 높은 경우 연화되어 손상이 발생함으로 제품상의 불량과 시공상의 품질이 균일하게 되기 어렵다.In addition, the conventional one-sided asphalt is difficult to maintain a solid sheet state, and if the construction temperature is high, the softening and damage occurs, it is difficult to uniformity in the product defects and construction quality.

따라서 본 발명은 상기와 같은 제반적인 사정을 감안하여 창출된 것으로, 방수층의 균일한 품질 수준을 확보하고, 견고하게 부착될 수 있도록 한 도막-시트 복합 방수재 및 그 제작방법을 제공함에 그 목적이 있다.Accordingly, the present invention has been made in view of the above-mentioned circumstances, and an object thereof is to provide a coating-sheet composite waterproofing material and a method of manufacturing the same, which ensures a uniform quality level of the waterproofing layer and is firmly attached. .

상기의 목적을 달성하기 위한 본 발명의 구체적인 수단은,Specific means of the present invention for achieving the above object,

폴리에스테르계 장섬유 또는 단섬유에 칼라마감처리된 도막 방수층이 각기 도포 함침되어 있는 도막 방수 보강재층과;A coating film waterproofing reinforcement layer each of which is coated and impregnated with a coating film waterproofing layer coated with polyester long fibers or short fibers;

상기 도막 방수 보강재층의 일면에 폴리머로 개량된 개량 아스팔트 컴파운드, 합성고무를 이용한 고무화 아스팔트 컴파운드, 수용성 고무 아스팔트 컴파운드에서 택일된 어느 하나가 도포되어 있는 아스팔트 방수층과;An asphalt waterproof layer coated on one surface of the coating film waterproofing reinforcing material layer, which is selected from an improved asphalt compound polymerized, a rubberized asphalt compound using synthetic rubber, and a water-soluble rubber asphalt compound;

상기 아스팔트 방수층의 노출면에 일정 구간 길이방향으로 부직포가 부착된 보강부직포층과;A reinforcing nonwoven fabric layer having a nonwoven fabric attached to the exposed surface of the asphalt waterproofing layer in a longitudinal direction;

상기 아스팔트 방수층의 노출면에 보강부직포층을 제외한 나머지 부분에 규 사가 살포되어서 형성된 규사층으로 이루어진 것을 특징으로 한다.It characterized by consisting of a silica sand layer formed by spraying the silica on the remaining portion except the reinforcing non-woven fabric layer on the exposed surface of the asphalt waterproof layer.

또한 본 발명에 따르면, 상기 도막 방수층에 적용되는 칼라코팅마감재는 아크릴계 1액형 상온 경화용 코팅재인 것을 특징으로 한다.In addition, according to the present invention, the color coating finish material applied to the coating layer is characterized in that the acrylic one-component room temperature curing coating material.

또한 본 발명에 따르면, 상기 도막 방수재는 시멘트 혼입 폴리머계로 이루어진 것을 특징으로 한다.In addition, according to the present invention, the coating film waterproofing material is characterized in that consisting of cement-based polymer system.

또한 본 발명에 따르면, 상기 시트 방수재는 아스팔트 컴파운드로 이루어진 것을 특징으로 한다.In addition, according to the present invention, the sheet waterproofing material is characterized in that it is made of asphalt compound.

또한 본 발명에 따르면, 상기 부직포는 폴리에스테르 부직포인 것을 특징으로 한다.According to the present invention, the nonwoven fabric is characterized in that the polyester nonwoven fabric.

또한 본 발명에 따르면, 상기 아스팔트 방수층은 상기 도막 방수 보강재층에 대해 일측으로 편향된 구조를 갖는 것을 특징으로 한다.In addition, according to the present invention, the asphalt waterproof layer is characterized in that it has a structure biased to one side with respect to the coating film waterproof reinforcement layer.

또한, 본 발명에 따른 도막-시트 복합 방수재의 제작방법은,In addition, the manufacturing method of the coating-sheet composite waterproofing material according to the present invention,

(a) 일방에 권취된 폴리에스테르계 장섬유 또는 단섬유를 풀어서 타방으로 권취 이송시키는 단계와;(a) unwinding the polyester long fibers or short fibers wound on one side and wound up to the other side;

(b) 상기 섬유의 일면에 도막 방수재를 1회 이상 도포 건조시킨 후 시트 방수재를 합착시켜서 도막 방수 보강재층을 형성하는 단계와;(b) forming a coating film waterproofing reinforcing material layer by coating and drying the coating film waterproofing material on one surface of the fiber one or more times and then bonding the sheet waterproofing material;

(c) 상기 도막 방수 보강재층의 일면에 폴리머로 개량된 개량 아스팔트 컴파운드, 합성고무를 이용한 고무화 아스팔트 컴파운드, 수용성 고무 아스팔트 컴파운드에서 택일된 어느 하나가 도포되어 있는 아스팔트 방수층을 형성하는 단계와;(c) forming an asphalt waterproof layer coated on one surface of the coating film waterproofing reinforcement layer with any one selected from an improved asphalt compound improved by polymer, rubberized asphalt compound using synthetic rubber, and water-soluble rubber asphalt compound;

(d) 상기 아스팔트 방수층의 노출면에 부직포와 규사를 부착 및 살포시켜서 보강부직포층과 규사층을 형성하는 단계로 제작된다.(d) attaching and spreading the nonwoven fabric and the silica sand on the exposed surface of the asphalt waterproofing layer to form a reinforcing nonwoven fabric layer and the silica sand layer.

바람직하게, 본 발명은 상기 (c)단계에서 아스팔트 방수층을 도막 방수 보강재층의 일측으로 노출 편향시켜서 제작된다.Preferably, the present invention is produced by exposing the asphalt waterproofing layer to one side of the coating waterproofing reinforcement layer in the step (c).

이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 상세히 설명한다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

본 발명에 따른 도막-시트 복합 방수재(10)는 도 1에서와 같이 도막 방수 보강재층(11), 아스팔트 방수층(12), 보강부직포층(13) 및 규사층(14)으로 구성되어 있다.The coating-sheet composite waterproofing material 10 according to the present invention is composed of a coating film waterproofing reinforcement layer 11, an asphalt waterproofing layer 12, a reinforcing nonwoven fabric layer 13, and a silica sand layer 14 as shown in FIG. 1.

도막 방수 보강재층(11)은 도 2와 같이 폴리에스테르계 장섬유(23)(또는 단섬유)에 칼라마감도막 방수재(21)와 시트 방수재(22)가 각기 도포 함침되어 있는 구성이다.The coating film waterproofing reinforcing material layer 11 is a structure in which the color finish coating waterproofing material 21 and the sheet waterproofing material 22 are apply | coated and impregnated in polyester long fiber 23 (or short fiber) like FIG.

이때 폴리에스테르계 장섬유(23)는 그 중량이 100~140

Figure 112006056778463-pat00001
이고 견고한 구조 형성을 위해 니들 펀칭 처리된 것이 바람직하다.At this time, the polyester-based long fiber 23 has a weight of 100 ~ 140
Figure 112006056778463-pat00001
And needle punched to form a rigid structure.

또한 칼라마감도막 방수재(21)는 EVA, VAE, Acryl, Acryl-Styrener에멀젼과 부기분체구성이 알루미나 시멘트, 규사의 분체가 혼합 형성된 시멘트 폴리머 혼입 도막재와 그 상부에 아크릴계 1액형 상온 경화용 칼라코팅재로 처리된다.In addition, the color finish coating waterproofing material 21 is a cement polymer mixed coating material in which EVA, VAE, Acryl, Acryl-Styrener emulsion and aerosol powder composition are formed by mixing alumina cement and powder of silica sand, and an acrylic one-component type room temperature curing color coating material thereon. Is treated as.

이때, 상기 아크릴계 1액형 상온 경화용 칼라코팅재는 Styrene-Acryl계 에멀젼(Tg; -13℃, 고형분 48±1%), 무기착색안료, 탄산칼슘으로 이루어진다.At this time, the acrylic one-component room temperature curing color coating material is made of a Styrene-Acryl emulsion (Tg; -13 ℃, solid content 48 ± 1%), inorganic pigments, calcium carbonate.

상기 아스팔트 방수층(12)은 합성수지 APP(Atactic Polypropylen), 합성고무 SBS(Styrene Butadiene Styrene) 등의 폴리머로 개량된 개량 아스팔트 컴파운드, 합성고무를 이용한 고무화 아스팔트 컴파운드, 수용성 고무 아스팔트 컴파운드에서 택일될 수 있다.The asphalt waterproof layer 12 may be selected from an improved asphalt compound improved with a polymer such as synthetic resin APP (Atactic Polypropylen), synthetic rubber SBS (Styrene Butadiene Styrene), rubberized asphalt compound using synthetic rubber, water-soluble rubber asphalt compound. .

상기 보강부직포층(13)은 상기 아스팔트 방수층(12)의 노출면에 일정 구간 길이방향으로 부직포가 부착되어 구성된 보강층이다. 이때 부직포는 압착 처리를 통해 아스팔트 방수층(12)의 표면에 부착된다.The reinforcing nonwoven fabric layer 13 is a reinforcing layer formed by attaching a nonwoven fabric in a lengthwise direction to an exposed surface of the asphalt waterproofing layer 12. At this time, the nonwoven fabric is attached to the surface of the asphalt waterproof layer 12 through a pressing process.

이때 보강부직포층(13)은 아스팔트 방수층(12)의 노출부의 훼손 및 변형 안정성을 위한 것이다. 즉, 보강부직포층(13)은 아스팔트의 점착성에 의한 취급 중 굴곡, 꺽임, 접힘 등으로 손상되는 것을 방지하게 된다.At this time, the reinforcing nonwoven fabric layer 13 is for the damage and deformation stability of the exposed portion of the asphalt waterproof layer 12. That is, the reinforcing nonwoven fabric layer 13 is prevented from being damaged by bending, bending or folding during handling due to the adhesiveness of the asphalt.

본 실시예에서 부직포는 폭이 약 100~250mm인 단섬유 폴리에스테르 부직포로서 30~100

Figure 112006056778463-pat00002
를 적용하며, 제조시 텐션(tension) 불균일에 의한 시트 변형을 방지하기 위해서는 50~70
Figure 112006056778463-pat00003
을 적용함이 바람직하다.In this embodiment, the nonwoven fabric is a short fiber polyester nonwoven fabric having a width of about 100 to 250 mm and is 30 to 100.
Figure 112006056778463-pat00002
In order to prevent sheet deformation due to tension unevenness during manufacturing, 50 ~ 70
Figure 112006056778463-pat00003
It is preferable to apply.

상기 규사층(14)은 상기 아스팔트 방수층(12)의 노출면에 보강부직포층(13)을 제외한 나머지 부분에 규사가 살포되어서 형성된 것이다. 본 실시예에서 규사의 입도는 200~450㎛로 하였다.The silica sand layer 14 is formed by spraying silica on the remaining portion of the asphalt waterproof layer 12 except for the reinforcing nonwoven fabric layer 13. The particle size of silica sand in this example was set to 200 ~ 450㎛.

한편, 본 발명에서 개량 아스팔트를 압출하여 아스발트 방수층(12)을 구성할 시 도 3과 같이 평향되게 구성할 수 있다.On the other hand, when the asphalt asphalt waterproof layer 12 is configured by extruding the improved asphalt in the present invention can be configured to be flat as shown in FIG.

즉, 도막 방수 보강재층(11)의 일방향 날개부가 15~50mm로 노출 편향되며, 타 방향의 부위에서는 아스팔트 방수층(12)이 약 30~50mm 노출 편향될 수 있도록 형성된다. That is, the one-way wing portion of the coating waterproof reinforcement layer 11 is exposed to 15 to 50 mm, and the asphalt waterproof layer 12 is formed to be exposed to about 30 to 50 mm in the other direction.

특히 아스팔트 방수층(12)이 노출되는 부위의 하부에 100~250mm 폭의 부직포를 압착 처리하는 동시에 규사를 살포하여 압착 처리함으로서 아스팔트 방수층(12)의 노출부를 보강하는 효과를 가질 수 있다.In particular, the non-woven fabric having a width of 100 to 250 mm in the lower portion of the exposed portion of the asphalt waterproofing layer 12 may be compressed, and at the same time, the silica sand may be sprayed to compress the exposed portion.

한편, 상기 보강부직포층(13)과 아스팔트 방수층(12)과의 사이에 보강을 더욱 강화하기 위해 약 100mm의 유리섬유메쉬가 더 삽입되어 구성될 수 있다.Meanwhile, in order to further reinforce the reinforcement between the reinforcing nonwoven fabric layer 13 and the asphalt waterproofing layer 12, a glass fiber mesh of about 100 mm may be further inserted.

이와 같이 구성된 도막-시트 복합 방수재의 제조 방법을 도 6을 참조하여 설명한다.The manufacturing method of the coating-sheet composite waterproofing material comprised in this way is demonstrated with reference to FIG.

먼저, 일방에 권취된 폴리에스테르계 장섬유 또는 단섬유를 풀어서 타방으로 권취 이송시킨다.First, the polyester-based long fibers or short fibers wound on one side are unwound and rolled up to the other side.

다음, 상기 섬유의 일면에 상기한 도막 방수재를 1회 이상 도포 건조시킨 후 시트 방수재를 합착시켜서 도막 방수 보강재층(11)을 형성게 된다.Next, the coating film waterproofing material is coated on one surface of the fiber one or more times, and then the sheet waterproofing material is bonded to form the coating film waterproofing reinforcing material layer 11.

다음, 상기 도막 방수 보강재층(11)의 일면에 폴리머로 개량된 개량 아스팔트 컴파운드, 합성고무를 이용한 고무화 아스팔트 컴파운드, 수용성 고무 아스팔트 컴파운드에서 택일된 어느 하나가 도포되어 있는 아스팔트 방수층(12)을 형성하게 된다.Next, on one surface of the coating film waterproofing reinforcement layer 11, an improved asphalt compound made of polymer, an asphalted asphalt compound using synthetic rubber, and an asphalt waterproofing layer 12 coated with any one selected from a water-soluble rubber asphalt compound are formed. Done.

이때 아스팔트 방수층(12)을 도막 방수 보강재층(11)의 일측으로 노출 편향시켜서 제작될 수 있다.In this case, the asphalt waterproof layer 12 may be manufactured by exposing and deflecting one side of the coating layer waterproof reinforcement layer 11.

다음, 상기 아스팔트 방수층(12)의 노출면에 부직포와 규사를 부착 및 살포 시켜서 보강부직포층(13)과 규사층(14)을 형성시키게 된다.Next, the nonwoven fabric and the silica sand are attached and sprayed on the exposed surface of the asphalt waterproof layer 12 to form the reinforcing nonwoven fabric layer 13 and the silica sand layer 14.

이와 같이 구성된 시트-도막 복합 방수재(10)는 도막방수층이 이미 형성되어 있어 현장시공이 작업자의 숙련도에 따라 영향을 받지 않기 때문에 일정한 방수층의 두께 확보가 용이하다. The sheet-coating composite waterproofing material 10 configured as described above is easily formed to have a constant waterproofing layer because the waterproofing layer is already formed so that the field construction is not affected by the skill of the operator.

또한, 시트방수재(22)와 장섬유(22)간의 균일한 합착 및 일체화가 이루어져 제품의 도막방수층 품질관리가 용이하며, 시공시 별도의 도막재 도포 작업이 불필요하여 종래와 같이 시공 작업 중 발생하는 물리적 충격에 의한 방수층 손상을 막을 수 있다. 따라서 방수력이 저하되는 문제점이 없고 시공공정성 관리 및 작업성이 향상된다.In addition, the uniform waterproofing and integration between the sheet waterproofing material 22 and the long fiber 22 is easy to control the quality of the coating film waterproof layer of the product, and during the construction it is not necessary to apply a separate coating material coating material is generated during the construction work as in the prior art It can prevent the damage of waterproof layer by physical shock. Therefore, there is no problem of deterioration of waterproofing power and construction processability management and workability are improved.

이렇게 제조된 시트-도막 복합 방수재는 다음의 단계에 따라 시공된다.The sheet-coated composite waterproofing material thus prepared is constructed according to the following steps.

제 1단계로 건물의 바탕면에 바탕 정리와 모서리 보강 처리가 이루어지고, 제 2단계로 시트-도막 복합 방수재(10)의 설치와 고정이 이루어지고, 제 3단계로 조인트 용융-융합과 실링이 이루어지고, 제 4단계로 마감 코팅재 도포 단계로 시공된다.In the first step, the grounding and corner reinforcement treatment is performed on the base surface of the building, and in the second step, installation and fixing of the sheet-coated composite waterproofing material 10 are performed, and in the third step, the joint melting-fusion and sealing It is made, and the fourth step is to construct the finishing coating material application step.

시공 단계별 내용을 상세히 설명하면, 부분적인 열화 부분과 모서리부 균열 및 파손 부위는 보수재를 사용하여 바탕 정리를 한 다음, 절연구조를 가지는 모서리 보강재를 벽체용 우레탄을 사용하여 고정 설치한다.Detailed description of the construction stages, partial deterioration and corner cracks and breaks are grounded using a repair material, and then the corner reinforcement having an insulating structure is fixed using urethane for walls.

바탕면 약 200mm 방수층 고정 부위에 우레탄계, 아스팔트계, 고무아스팔트계 등의 고정용 접착제(40)를 도포한 다음 칼라 처리된 도막-시트 복합 방수재(10)의 보강부직포층(13)을 이루는 부직포 부위에 도 4와 같은 구조가 되도록 설치하도록 하며, 인접 설치된 도막-시트 복합 방수재에 의해 형성된 접합부는 도 5와 같이 열풍 및 자착에 의한 용융-융합 처리가 되며, 방수재(10)의 일면 돌출된 날개 보강부위는 액상형의 우레탄계 실링재(30)(또는 2액형 시멘트계 수용성 실링재) 처리를 하여 2중 겹침 보강구조가 형성되도록 한다.Non-woven fabric portion forming the reinforcing nonwoven fabric layer 13 of the coating film-sheet composite waterproofing material 10 coated with a fixing adhesive 40 such as urethane, asphalt, rubber asphalt, etc. on the base surface fixed part of 200 mm waterproof layer To be installed as shown in Figure 4, the junction formed by the adjacent coating film-sheet composite waterproofing material is melt-fusion treatment by hot air and self-adjustment as shown in Figure 5, the reinforcement of the wing protruding one surface of the waterproofing material 10 The part is treated with a liquid urethane-based sealing material 30 (or two-component cement-based water-soluble sealing material) to form a double overlap reinforcement structure.

이후 방수층 상부에 노출의 경우 수용성 아크릴계 또는 우레탄 아크릴계 보호 코팅재를, 비노출의 경우 누름콘크리트, 모르타르 등을 마감 처리함으로서 방수 공사가 완료하게 된다.After the waterproof layer is exposed to the water-soluble acrylic or urethane acrylic protective coating material, in the case of non-exposed pressed concrete, mortar and the like finish the waterproofing work is completed.

이상과 같이, 본 발명은 비록 한정된 실시예와 도면에 의해 설명되었으나, 본 발명은 이것에 의해 한정되지 않으며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 본 발명의 기술사상과 아래에 기재될 청구범위의 균등범위 내에서 다양한 수정 및 변형이 가능함은 물론이다.As described above, although the present invention has been described by way of limited embodiments and drawings, the present invention is not limited thereto, and the technical idea of the present invention and the following by those skilled in the art to which the present invention pertains. Of course, various modifications and variations are possible within the scope of equivalents of the claims to be described.

상술한 바와 같이 본 발명에 따르면, 도막 방수재가 균일하게 함침 또는 도포되어 균일하고 우수한 방수층을 갖는 고품질의 확보가 가능하다.As described above, according to the present invention, the coating film waterproofing material is uniformly impregnated or applied to ensure a high quality having a uniform and excellent waterproofing layer.

또한 별도로 현장에서 도포 및 양생하는 작업이 제거되므로 작업인력 및 시공기간이 단축되고, 1회의 설치 시공으로 완성된 방수층 설치가 가능하고, 도막이 이미 부여되어 있고 양생이 불필요한 시트-도막 복합 방수재가 제공된다.In addition, since the work to apply and cure in the field is eliminated separately, the manpower and construction period can be shortened, and the completed waterproof layer can be installed by one installation construction, and the sheet-coated composite waterproof material is already provided and unnecessary curing is provided. .

특히, 본 발명은 아스팔트 방수층에 보강부직포가 부착되어 있어 접합부가 되는 아스팔트 노출부의 품질 안정성을 높이게 된다.In particular, the present invention is a reinforcing nonwoven fabric is attached to the asphalt waterproof layer is to improve the quality stability of the asphalt exposed portion to be joined.

Claims (8)

폴리에스테르계 장섬유 또는 단섬유에 칼라마감처리된 도막 방수층이 각기 도포 함침되어 있는 도막 방수 보강재층(11)과;A coating film waterproofing reinforcement layer 11 each of which is coated and impregnated with a coating film waterproofing layer coated with polyester long fibers or short fibers; 상기 도막 방수 보강재층(11)의 일면에 합성수지 APP, 합성고무 SBS 등의 폴리머로 개량된 개량 아스팔트, 합성고무를 이용한 고무화 아스팔트, 아스팔트 컴파운드에서 택일된 어느 하나가 도포되어 있는 아스팔트 방수층(12)과;Asphalt waterproof layer 12 which is coated on one surface of the coating film waterproofing reinforcing material layer 11 is improved asphalt, polymerized rubber, such as synthetic resin APP, synthetic rubber SBS, rubberized asphalt using synthetic rubber, one selected from the asphalt compound and; 상기 아스팔트 방수층의 노출 하부면에 일정 구간 길이방향으로 부직포가 부착된 보강부직포층(13)과;A reinforcing nonwoven fabric layer 13 having a nonwoven fabric attached to the exposed lower surface of the asphalt waterproofing layer in a longitudinal direction; 상기 아스팔트 방수층의 노출면에 보강부직포층을 제외한 나머지 부분에 규사가 살포되어서 형성된 규사층(14)으로 이루어진 것을 특징으로 하는 도막-시트 복합 방수재.Coating-sheet composite waterproofing material, characterized in that consisting of a silica sand layer 14 is formed by spraying the silica sand on the remaining portion except the reinforcing non-woven fabric layer on the exposed surface of the asphalt waterproof layer. 제 1항에 있어서,The method of claim 1, 상기 도막 방수 보강재층(11)에는 EVA, VAE, Acryl, Acryl-Styrener에멀젼과 부기분체구성이 알루미나 시멘트, 규사의 분체가 혼합 형성된 시멘트 폴리머 혼입 도막재와 그 상부에 아크릴계 1액형 상온 경화용 칼라코팅재가 처리된 것을 특징으로 하는 도막-시트 복합 방수재.The coating film waterproof reinforcing material layer 11 is a cement polymer mixed coating material formed by mixing the powder of EVA, VAE, Acryl, Acryl-Styrener emulsion, and alumina cement, alumina cement, silica sand, and acrylic one-component type room temperature curing color coating material thereon. Coating-sheet composite waterproofing material, characterized in that the treated. 제 2항에 있어서,The method of claim 2, 상기 아크릴계 1액형 상온 경화용 칼라코팅재는 Styrene-Acryl계 에멀젼, 무기착색안료, 탄산칼슘으로 이루어진 것을 특징으로 하는 도막-시트 복합 방수재.The acrylic one-component room temperature curing color coating material is a coating film-sheet composite waterproofing material, characterized in that consisting of Styrene-Acryl-based emulsions, inorganic coloring pigments, calcium carbonate. 제 1항에 있어서,The method of claim 1, 상기 부직포는 폭 100~250mm, 중량 50~70g/㎡의 단섬유 폴리에스테르 부직포인 것을 특징으로 하는 도막-시트 복합 방수재.The non-woven fabric is a 100-250mm width, 50-70g / ㎡ short-fiber polyester nonwoven fabric, characterized in that the coating film-sheet composite waterproofing material. 제 1항에 있어서,The method of claim 1, 상기 보강부직포층(13)과 아스팔트 방수층(12)과의 사이에 유리섬유메쉬가 더 삽입된 것을 특징으로 하는 도막-시트 복합 방수재.Coating-sheet composite waterproofing material, characterized in that the glass fiber mesh is further inserted between the reinforcing non-woven fabric layer 13 and the asphalt waterproofing layer (12). 제 1항에 있어서,The method of claim 1, 상기 아스팔트 방수층(12)은 상기 도막 방수 보강재층(11)에 대해 일측으로 편향된 구조를 갖는 것을 특징으로 하는 도막-시트 복합 방수재.The asphalt waterproof layer 12 is a coating film-sheet composite waterproof material, characterized in that it has a structure biased to one side with respect to the coating film waterproof reinforcement layer (11). 도막-시트 복합 방수재의 제작방법에 있어서,In the manufacturing method of the coating-sheet composite waterproofing material, (a) 일방에 권취된 폴리에스테르계 장섬유 또는 단섬유를 풀어서 타방으로 권취 이송시키는 단계와;(a) unwinding the polyester long fibers or short fibers wound on one side and wound up to the other side; (b) 상기 섬유의 일면에 도막 방수재를 1회 이상 도포 건조시킨 후 시트 방수재를 합착시켜서 도막 방수 보강재층(11)을 형성하는 단계와;(b) forming a coating film waterproofing reinforcing material layer (11) by coating and drying the coating film waterproofing material on one surface of the fiber one or more times and then bonding the sheet waterproofing material to the surface; (c) 상기 도막 방수 보강재층의 일면에 합성수지 APP, 합성고무 SBS 등의 폴리머로 개량된 개량 아스팔트, 합성고무를 이용한 고무화 아스팔트, 아스팔트 컴파운드에서 택일된 어느 하나를 도포시켜서 아스팔트 방수층(12)을 형성하는 단계와;(c) the asphalt waterproof layer 12 is applied to one surface of the coating film waterproofing reinforcement layer by applying any one selected from the improved asphalt, polymerized rubber such as synthetic resin APP, synthetic rubber SBS, rubberized asphalt using synthetic rubber, and asphalt compound. Forming; (d) 상기 아스팔트 방수층(12)의 노출면에 부직포와 규사를 부착 및 살포시켜서 보강부직포층(13)과 규사층(14)을 형성하는 것을 특징으로 하는 도막-시트 복합 방수재의 제조방법.(d) a method of manufacturing a coating-sheet composite waterproofing material, characterized in that the reinforcing nonwoven fabric layer (13) and the silica sand layer (14) are formed by attaching and spreading the nonwoven fabric and the silica sand on the exposed surface of the asphalt waterproof layer (12). 제 7항에 있어서,The method of claim 7, wherein 상기 (c)단계에서 아스팔트 방수층(12)을 도막 방수 보강재층(11)의 일측으로 노출 편향시키는 것을 특징으로 하는 도막-시트 복합 방수재.The coating film-sheet composite waterproofing material, characterized in that (b) in the step (b) exposing the asphalt waterproofing layer 12 to one side of the coating waterproofing reinforcement layer (11).
KR1020060074892A 2006-08-08 2006-08-08 Sheet coating membrane complex drainage member and manufacturing method KR100716222B1 (en)