KR100676937B1 - Water soluble film for skin care and wound repair and method for their preparation - Google Patents
Water soluble film for skin care and wound repair and method for their preparation Download PDFInfo
- Publication number
- KR100676937B1 KR100676937B1 KR1020050046620A KR20050046620A KR100676937B1 KR 100676937 B1 KR100676937 B1 KR 100676937B1 KR 1020050046620 A KR1020050046620 A KR 1020050046620A KR 20050046620 A KR20050046620 A KR 20050046620A KR 100676937 B1 KR100676937 B1 KR 100676937B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- skin
- water
- film
- acid
- Prior art date
Abstract
본 발명은 피부미용 및 상처치료용 수용성 필름 및 그 제조방법에 관한 것으로, 합성 고분자 물질 0.01-20중량%, 천연 고분자 물질 0.01-20중량%, 피부친화성 증진제 0.1-10중량%, 천연생체물질 0.1-10중량%, 다가알코올 1-20중량%, 기능첨가제 0.01-10중량%, 방부제 0.01-2중량% 및 물 8-98.76중량%를 포함하여 구성되고, 2-3,000㎛의 두께를 가지며 피부 접착시 용해가능한 피부미용 및 상처치료용 수용성 필름, 및 그 제조방법이 제공된다.The present invention relates to a water-soluble film for skin care and wound treatment and a method of manufacturing the same, 0.01-20% by weight of synthetic polymer material, 0.01-20% by weight of natural polymer material, 0.1-10% by weight of skin affinity enhancer, natural biomaterial 0.1-10% by weight, polyalcohol 1-20% by weight, functional additive 0.01-10% by weight, preservative 0.01-2% by weight and water 8-98.76% by weight, has a thickness of 2-3,000㎛ Provided are water-soluble films for skin care and wound treatment that are soluble upon adhesion, and methods for their preparation.
본 발명의 피부미용 및 상처치료용 수용성 필름은 피부 접착시 수분으로 인해 서서히 용해되면서 유효성분이 신속하게 경피속으로 전달되므로 상처의 치유를 촉진시키고 피부미용에 유용하게 활용될 수 있다. The water-soluble film for skin care and wound treatment of the present invention may be usefully used to promote healing of the skin and to effectively heal the wound since the active ingredient is rapidly delivered into the percutaneous skin while slowly dissolving due to moisture during skin adhesion.
필름, 피부, 미용, 침투, 상처치료 Film, skin, beauty, penetration, wound treatment
Description
도 1은 본 발명의 피부미용 및 상처치료용 필름의 모식도를 나타낸 것으로, (1)은 유효성분을 첨가한 수용성 필름을 나타내며, (2)는 방수 필름을 나타낸 것이다. Figure 1 shows a schematic diagram of the skin care and wound treatment film of the present invention, (1) shows a water-soluble film to which the active ingredient is added, (2) shows a waterproof film.
본 발명은 피부미용 및 상처치료용 수용성 필름 및 그 제조방법에 관한 것으로, 보다 상세하게는 피부 접착시 피부의 수분에 의해 서서히 용해가능하여 피부미용 및 상처치료에 효과적으로 적용될 수 있는 피부미용 및 상처치료용 수용성 필름에 관한 것이다.The present invention relates to a water-soluble film for skin care and wound treatment, and a method of manufacturing the same, and more particularly, skin care and wound treatment that can be effectively dissolved in skin beauty and wound treatment by being gradually dissolved by skin moisture. It relates to a water-soluble film for.
피부미용을 위하여 미용제를 함유한 하이드로겔을 이용할 경우에는 하이드로겔을 피부에 붙인 후 치료용 약물을 사용하는 경우보다 상대적으로 단시간 이내에 제거해야 하므로 미용제가 신속히 피부속으로 전달될 필요성이 크게 요구된다. 즉, 피부미용시 피부에 적용한 하이드로겔은 그 속에 함유되어 있는 미용제가 다량 신속하게 하이드로겔에서 부터 피부로 전달될 수 있어야 한다. 이와 같은 특성을 만족시키기 위해서는 하이드로겔이 종래의 것에 비하여 미용제가 피부 속으로 신속하고 고르게 전달되는 특징을 가져야 한다.When using a hydrogel containing a cosmetic agent for skin beauty, it is necessary to remove the hydrogel quickly into the skin after attaching the hydrogel to the skin and removing it within a relatively short time than using a therapeutic drug. . In other words, the hydrogel applied to the skin during skin beauty should be able to be delivered from the hydrogel to the skin in a large amount quickly the cosmetic agent contained therein. In order to satisfy these characteristics, the hydrogel should have a characteristic that the cosmetic agent is delivered quickly and evenly into the skin as compared with the conventional one.
한편, 우리 몸을 밖에서 감싸고 있는 피부는 일상생활에서 여러 가지 위험한 물리적 손상에 노출되어 있다. 따라서 피부의 기계적 손상, 타박상, 화상등 우리 주위에서 많은 요인들로 인해 상처가 발생한다. 상처는 사람의 조직이 가지는 해부학적인 연속성이 외부의 작용에 의해 그 본래의 연속성을 상실한 상태를 말한다. 예를 들어 우리의 피부는 표피, 진피, 피하지방으로 이루어져 있는데 베이거나 넘어지는 등의 외상에 의해서 이러한 표피나 진피, 피하지방 등의 연속성이 상실한 이것을 상처라고 한다.On the other hand, the skin that surrounds our body is exposed to various dangerous physical damages in everyday life. Thus, many factors around us, such as mechanical damage to the skin, bruises, burns, and wounds occur. A wound is a state in which the anatomical continuity of a human tissue has lost its original continuity by external action. For example, our skin is composed of epidermis, dermis, and subcutaneous fat, and the continuity of such epidermis, dermis, and subcutaneous fat is lost due to trauma such as cuts and falls.
일반적으로 창상, 외상 등과 같은 피부의 상처를 효과적으로 치료하기 위하여 드레싱(Wound dressing)을 사용한다. 상처치료용 드레싱이 가져야 할 특성으로는 상처와의 접촉면에서 적당한 습기의 유지능력이 필요하고, 상처분비물의 조절능력, 상처에 대한 드레싱의 부착 및 제거의 용이성, 외부의 상처부위간의 공기 및 수증기 관통성, 외부에 대한 상처부위의 단열성, 박테리아의 침입에 대한 저항성, 인체에 대한 무독성, 우수한 기계적 물성등이 요구된다.In general, dressing is used to effectively treat wounds of the skin such as wounds and traumas. Wound dressings require the ability to maintain adequate moisture at the contact surface with wounds, the ability to control wound secretions, ease of attachment and removal of dressings to wounds, and air and vapor penetration between external wounds. It is required to have sex, thermal insulation of wounds, resistance to bacterial invasion, nontoxicity to human body, and excellent mechanical properties.
상처치료용 드레싱은 19세기 후반부터 연구가 활성화되었으며 자연으로부터 얻은 소재로부터 벗어나 상처치료용 드레싱의 급격한 발전은 1942년 합성고분자인 메틸셀룰로오스로 만들어진 드레싱이 Pickrell에 의해서 개발되면서 진척되었다. 의학 기술의 발달과 더불어 상처치료 과정에 대한 관심이 증대되면서 많은 연구가 시도되어 왔다. 상처가 나면 예전에는 딱지가 않도록 하거나 그냥 거즈로 치료하는 건조 드레싱 방법을 사용했다. 이러한 드레싱 방법은 상처를 더디게 낫게 하고 드레싱할 때 통증을 수반한다. 그런데 1962년 동물학자인 Winter가 상처를 습윤한 상태로 유지할 때 더 빠르게 치유되고 통증을 감소시킨다는 것을 발표한 이후로 건조 드레싱보다 습윤 드레싱의 우수성이 많은 의학자들에 의하여 입증되었다. 그 과정의 중간 형태로 나온 것이 바세린 거즈나 소프라 투르 등이다. 때문에 최근 몇 년 정도 전까지도 바세린 거즈나 소프라 투르 등으로 치료를 했지만 바세린 거즈나 소프라 투르도 상처의 표면에 달라붙어 건조되기 때문에 상처의 치유를 더디게 하고 통증을 수반한다. Hinman과 Maibach은 상처부위에서 습기가 상처치유에 미치는 효과에 대한 이론을 확립하였으며, 1970년경에 Michael 등은(Michael Z. C., Hu and Mark Reeves, Biosorption of Uranium by Pseud omonas Aeruginosa Strain CSU Immobilized in a Novel Matrix, Biotechnology Progress, 13(1), 1997) 상처부위에서 적당한 수분을 함유하고 가피가 생성되지 않은 조건에서 상피세포의 이동이 활발하고, 상처치유 기간이 단축됨을 밝혔다. 특히 Winter는 상피 재형성이 상처부위가 건조된 상태보다 적당히 수분을 함유한 상태에서 40% 정도 빠른 효과를 나타낸다고 실험적으로 증명하였다. 이들은 상처분비물이 존재하지 않는 건조된 상태에서는 가피를 생성하는 콜라겐에 의해 상피세포의 활동이 제한받으며, 상처분비물이 피부를 재생하는데 필요한 성장인자를 많이 함유한다는 것을 보였다. 1980년경에 이르러 고분자 합성기술의 비약적인 발전과 의료기술의 발달로 인하여 많은 사람들이 상처치료용 드레싱의 개발을 시도하였다. 이들 드레싱은 단순히 상처를 덮고 상처분비물을 흡수하는 단계에 그치지 않고 적당한 수분을 함유하여 상피 재형성을 돕고 박테리아 침입을 막으며, 피부 성장 요소의 삽입등 다양한 방면으로 연구가 진행되고 있다. Wound dressings have been active since the late 19th century. The rapid development of wound dressings away from natural materials was promoted in 1942 by the development of Pickrell's dressing made of methylcellulose, a synthetic polymer. With the development of medical technology, interest in the wound healing process has increased, and many studies have been attempted. In the past, they used a dry dressing method to prevent scabs or just treat them with gauze. This dressing method slows the wound and involves pain when dressing. However, since 1962, zoologist Winter announced that heals faster and reduces pain when keeping wounds wet, many medical practitioners have demonstrated the superiority of wet dressing over dry dressing. Intermediate forms of the process include Wasserine gauze and Sopra Tour. Therefore, in recent years, it was treated with petrolatum gauze or sopra tour, but petrolatum gauze and sopra tour also adhere to the surface of the wound and dry, which slows the healing of the wound and entails pain. Hinman and Maibach established a theory of the effect of moisture on wound healing, and by 1970 Michael et al. (Michael ZC, Hu and Mark Reeves, Biosorption of Uranium by Pseud omonas Aeruginosa Strain CSU Immobilized in a Novel Matrix , Biotechnology Progress, 13 (1), 1997) It was found that epithelial cell migration was active and wound healing time was shortened under conditions that contained adequate moisture in the wound and had no skin. In particular, Winter proved experimentally that epithelial remodeling was about 40% faster than moderately moisturized than wounded. They showed that in the dried state where no wound secretion is present, the activity of epithelial cells is limited by the collagen that produces the skin, and that the wound secretion contains many growth factors necessary to regenerate the skin. By the 1980s, due to the rapid development of polymer synthesis technology and the development of medical technology, many people tried to develop the dressing for wound treatment. These dressings are not just covering the wounds and absorbing the secretions, but also contain adequate moisture to help epithelial remodeling, prevent bacterial invasion, and insert skin growth factors.
종래에는 피부의 상처를 보호하기 위하여 단순히 덮개 또는 흡수용 밴드로 상처부위를 덮음으로써 상처치료를 촉진시켰고, 더 나아가서는 상처 부위에 소독제나 항생물질을 포함하는 연고를 바른 다음에 드레싱을 하였다. 그러나 상처부위에 상처치료를 촉진시킬 수 있는 연고형 약제를 바르고 상처 보호를 위한 드레싱을 하는 것은 상처치료의 촉진면에서는 어느 정도 효과가 있으나 연고형 약제를 피부의 상처부위에 바를 때 통증을 수반하게 될 뿐만 아니라 상처 부위에 발라진 연고의 높은 흐름성으로 인하여 드레싱 후 연고가 드레싱 밖으로 흘러나오는 현상이 빈번하게 발생한다. 이러한 연고의 누출은 상처치료효과를 감소시킬 뿐만 아니라 시각적 및 촉각적 불쾌감을 주는 문제가 있다. Conventionally, in order to protect the wound of the skin, the wound treatment was facilitated by simply covering the wound with a cover or an absorption band, and further, dressing was applied after applying an ointment containing an antiseptic or antibiotic to the wound. However, applying an ointment that can promote wound healing and dressing to protect the wound is somewhat effective in promoting wound healing, but it is accompanied by pain when applying ointment to the wound of the skin. In addition, due to the high flowability of the ointment applied to the wound site, the phenomenon that the ointment flows out of the dressing frequently occurs after dressing. Such ointment leakage not only reduces the effect of healing the wound, but also has a problem of visual and tactile discomfort.
이에 본 발명은 피부 접착시 피부의 수분에 의해 서서히 용해가능하여 피부미용제 혹은 치료용 약물이 신속히 피부속으로 전달될 수 있는 피부미용 및 상처치 료용 수용성 필름을 제공하고자 한다.Accordingly, the present invention is to provide a water-soluble film for skin care and wound care that can be slowly dissolved by the moisture of the skin when the skin is adhered, so that the skin cosmetic or therapeutic drug can be quickly delivered into the skin.
또한 본 발명은 상기 피부미용 및 상처치료용 수용성 필름의 제조방법을 제공하고자 한다.In another aspect, the present invention is to provide a method for producing a water-soluble film for skin care and wound treatment.
본 발명의 일 견지에 의하면, According to one aspect of the invention,
폴리비닐피롤리돈(PVP), 폴리비닐알코올(PVA), 폴리에틸렌옥사이드(PEO), 폴리비닐아크릴산(PVAc) 및 폴리메타아크릴산(PMAc)으로 구성된 그룹으로부터 선택된 적어도 하나의 합성 고분자 물질 0.01-20중량%,0.01-20 weight of at least one synthetic polymeric material selected from the group consisting of polyvinylpyrrolidone (PVP), polyvinyl alcohol (PVA), polyethylene oxide (PEO), polyvinyl acrylic acid (PVAc) and polymethacrylic acid (PMAc) %,
젤라틴, 아가, 카라기난, 알기네이트, 키토산, 키토산 유도체, 전분, 풀루란, 갈락토만난, 글루코만난, 구아껌, 로카스트 빈 껌, 플루로닉, 알긴, 잔탄 및 겔란으로 구성된 그룹으로부터 선택된 적어도 하나의 천연 고분자 물질 0.01-20중량%, At least one selected from the group consisting of gelatin, agar, carrageenan, alginate, chitosan, chitosan derivatives, starch, pullulan, galactomannan, glucomannan, guar gum, locust bean gum, pluronic, algin, xanthan and gellan 0.01-20% by weight natural polymer,
세라마이드, 코직산, α-히드록시산 및 β-히드록시산, 레티놀, 비타민 C, 비타민 C 유도체, 비타민 A, 비타민 E, 엘라스틴, 아미노산, 알로에, 병풀 추출물, 감초추출물, 마치현추출물, 베타글루칸, 프로테오글루칸, 구아바, 포도씨앗 추출물, 카모마일 및 히알루로닉산으로 구성된 그룹으로부터 선택된 적어도 하나의 피부친화성 증진제 0.1-10중량%, Ceramide, kojic acid, α-hydroxy acid and β-hydroxy acid, retinol, vitamin C, vitamin C derivative, vitamin A, vitamin E, elastin, amino acid, aloe, centella extract, licorice extract, portulaca extract, betaglucan, pro 0.1-10% by weight of at least one skin affinity enhancer selected from the group consisting of theoglucan, guava, grape seed extract, chamomile and hyaluronic acid,
당귀, 어성초, 상황버섯, 석류, 감자, 오미자, 영지버섯, 황기, 알로에, 녹차, 인삼, 목초액, 솔잎, 은행잎, 프로폴리스, 뽕잎 또는 누에로 부터 추출된 적어 도 하나의 천연생체물질 0.1-10중량%, At least one natural biomaterial extracted from Angelica, Echochocho, Situary mushroom, Pomegranate, Potato, Schisandra chinensis, Ganoderma lucidum, Astragalus, Aloe, Green tea, Ginseng, Wood vinegar, Pine needle, Ginkgo leaf, Propolis, Mulberry leaf or Silkworm weight%,
다가알코올 1-20중량%, Polyhydric alcohol 1-20% by weight,
기능첨가제 0.01-10중량%, 0.01-10% by weight of functional additives,
방부제 0.01-2중량% 및 0.01-2% by weight of preservatives and
물 8-98.76중량%를 포함하여 구성되고, Comprises 8-98.76% by weight of water,
2-3,000㎛의 두께를 가지며 피부 접착시 용해가능한 피부미용 및 상처치료용 수용성 필름이 제공된다.There is provided a water-soluble film for skin care and wound treatment having a thickness of 2-3,000 μm and soluble in skin adhesion.
본 발명의 다른 견지에 의하면, According to another aspect of the present invention,
상온에서 물 8-98.76중량%, 폴리비닐피롤리돈(PVP), 폴리비닐알코올(PVA), 폴리에틸렌옥사이드(PEO), 폴리비닐아크릴산(PVAc) 및 폴리메타아크릴산(PMAc)으로 구성된 그룹으로부터 선택된 적어도 하나의 합성 고분자 물질 0.01-20중량%, 및 젤라틴, 아가, 카라기난, 알기네이트, 키토산, 키토산 유도체, 전분, 풀루란, 갈락토만난, 글루코만난, 구아껌, 로카스트 빈 껌, 플루로닉, 알긴, 잔탄 및 겔란으로 구성된 그룹으로부터 선택된 적어도 하나의 천연 고분자 물질 0.01-20중량%를 혼합하고 이를 30-80℃로 승온하여 용해시키는 단계;At least 8-98.76% by weight of water, polyvinylpyrrolidone (PVP), polyvinyl alcohol (PVA), polyethylene oxide (PEO), polyvinyl acrylic acid (PVAc) and polymethacrylic acid (PMAc) at least at room temperature 0.01-20% by weight of one synthetic polymer, and gelatin, agar, carrageenan, alginate, chitosan, chitosan derivatives, starch, pullulan, galactomannan, glucomannan, guar gum, locust bean gum, pluronic, algin Mixing 0.01-20% by weight of at least one natural high molecular material selected from the group consisting of xanthan and gellan and dissolving it by raising the temperature to 30-80 ° C;
상기 용액을 30-80℃로 유지시키면서 다가알코올 1-20중량%, 세라마이드, 코직산, α-히드록시산 및 β-히드록시산, 레티놀, 비타민C, 비타민C 유도체, 비타민 A, 비타민 E,엘라스틴, 아미노산, 알로에, 병풀 추출물, 감초추출물, 마치현추출물, 베타글루칸, 프로테오글루칸, 구아바, 포도씨앗 추출물, 카모마일 및 히알루로 닉산으로 구성된 그룹으로부터 선택된 적어도 하나의 피부친화성 증진제 0.1-10중량%, 기능첨가제 0.01-10중량%, 방부제 0.01-2중량%, 및 당귀, 어성초, 상황버섯, 석류, 감자, 오미자, 영지버섯, 황기, 알로에, 녹차, 인삼, 목초액, 솔잎, 은행잎, 프로폴리스, 뽕잎 또는 누에로 부터 추출된 천연생체물질 0.1-10중량%를 첨가하고 혼합하는 단계;1-20% by weight of polyhydric alcohol, ceramide, kojic acid, α-hydroxy acid and β-hydroxy acid, retinol, vitamin C, vitamin C derivatives, vitamin A, vitamin E, elastin, while maintaining the solution at 30-80 ° C. 0.1-10% by weight of at least one skin affinity enhancer selected from the group consisting of: amino acids, aloes, centella extracts, licorice extracts, portulaca oleracea extracts, betaglucans, proteoglucans, guavas, grape seed extracts, chamomile and hyaluronic acid, 0.01-10% by weight of functional additives, 0.01-2% by weight of preservatives, and Angelica, Echoseong, Sichuan mushroom, Pomegranate, Potato, Schisandra chinensis, Ganoderma lucidum, Astragalus, Aloe, Green tea, Ginseng, Wood vinegar, Pine needle, Ginkgo leaf, Propolis, Mulberry leaf Or adding and mixing 0.1-10% by weight of a natural biomaterial extracted from silkworms;
상기 용액을 2-3,000㎛의 두께를 갖는 일정한 크기로 성형한 후 30-90℃에서 1분내지 30분동안 건조시키는 단계;Molding the solution to a constant size having a thickness of 2-3,000 μm and then drying at 30-90 ° C. for 1 minute to 30 minutes;
로 이루어짐을 특징으로 하는 피부 접착시 용해가능한 피부미용 및 상처치료용 수용성 필름 제조방법이 제공된다.Provided is a method for preparing a water-soluble film for dissolving skin and wound treatment upon adhesion of the skin to be made.
이하 본 발명에 대하여 보다 상세히 설명한다.Hereinafter, the present invention will be described in more detail.
본 발명의 피부미용 및 상처치료용 수용성 필름은 피부치료 및 피부미용제를 함유한 수용성 필름으로 피부에 부착시 소량의 수분(예, 필름 중량에 대한 1%의 수분)으로도 용해가능하게 되어 피부친화성 증진제 등의 유효성분이 다량으로 피부속으로 신속하게 전달될 수 있는 것을 특징으로 한다. The water-soluble film for skin care and wound treatment of the present invention is a water-soluble film containing skin treatment and skin care agent so that it can be dissolved even with a small amount of water (eg, 1% water by weight of the film) when attached to the skin. An active ingredient such as an affinity enhancer is characterized in that it can be quickly delivered into the skin in large quantities.
본 발명의 피부미용 및 상처치료용 수용성 필름은 피부에 적용되어 밀착되었을 때 피부의 수분에 의하여 서서히 용해됨으로써 수용액상태로 변화하여 필름과 피부사이의 친화성을 최적으로 향상시켜서 미용제나 상처치료제와 같은 유효성분이 피부로 잘 전달되게 하는 특성이 있으며, 또, 상기 필름내에는 이러한 유효성분의 피부 전달을 증진시키는 천연 친화성 증진제가 함유되어 있어서 만족할 만한 양의 유효성분이 신속하게 경피속으로 전달될 수 있는 특징을 갖는 것이다. 그러므로 본 발명에서는 필름이 피부와 접촉시 피부에 존재하는 소량의 수분에 의해 용해되어 수용액상태로 변화하는 것을 특징으로 하는 신규의 피부미용 및 상처치료용 수용성 필름을 제공한다. The water-soluble film for skin care and wound treatment of the present invention is gradually dissolved by the moisture of the skin when it is applied to the skin and is changed into an aqueous solution to optimally improve the affinity between the film and the skin, such as a cosmetic or wound treatment. The active ingredient is well-transmitted to the skin, and the film contains a natural affinity enhancer that enhances the skin delivery of such an active ingredient, so that a satisfactory amount of the active ingredient can be delivered to the percutaneously rapidly. It has characteristics. Therefore, the present invention provides a novel water-soluble film for skin care and wound treatment, characterized in that the film is dissolved by a small amount of moisture present in the skin when it comes into contact with the skin and changed into an aqueous solution.
위와 같은 특징을 갖기 위하여 본 발명의 필름에는 특정 합성고분자 물질과 천연고분자 물질로 조성된 필름형성 물질이 포함되며 이와 더불어 인체피부와 친화성을 향상시킬 수 있는 친화성 증진제와 천연생체물질이 함유된다. In order to have the above characteristics, the film of the present invention includes a film-forming material composed of a specific synthetic polymer material and a natural polymer material, and also contains an affinity enhancer and a natural biomaterial which can improve affinity with human skin. .
본 발명의 피부미용 및 상처치료용 수용성 필름은 필름 조성물의 총 중량을 기준으로 폴리비닐피롤리돈(PVP), 폴리비닐알코올(PVA), 폴리에틸렌옥사이드(PEO), 폴리비닐아크릴산(PVAc) 및 폴리메타아크릴산(PMAc)으로 구성된 그룹으로부터 선택된 적어도 하나의 합성 고분자 물질 0.01-20중량%, 젤라틴, 아가, 카라기난, 알기네이트, 키토산, 키토산 유도체, 전분, 풀루란, 갈락토만난, 글루코만난, 구아껌, 로카스트 빈 껌, 플루로닉, 알긴, 잔탄 및 겔란으로 구성된 그룹으로부터 선택된 적어도 하나의 천연 고분자 물질 0.01-20중량%, 세라마이드, 코직산, α-히드록시산 및 β-히드록시산, 레티놀, 비타민C, 비타민C 유도체, 비타민 A, 비타민 E,엘라스틴, 아미노산, 알로에, 병풀 추출물, 감초추출물, 마치현추출물, 베타글루칸, 프 로테오글루칸, 구아바, 포도씨앗 추출물, 카모마일 및 히알루로닉산으로 구성된 그룹으로부터 선택된 적어도 하나의 피부친화성 증진제 0.1-10중량%, 당귀, 어성초, 상황버섯, 석류, 감자, 오미자, 영지버섯, 황기, 알로에, 녹차, 인삼, 목초액, 솔잎, 은행잎, 프로폴리스, 뽕잎 또는 누에로 부터 추출된 적어도 하나의 천연생체물질 0.1-10중량%, 다가알코올 1-20중량%, 기능첨가제 0.01-10중량%, 방부제 0.01-2중량% 및 물 8-98.76중량%로 조성된다. Water-soluble films for skin care and wound treatment of the present invention is based on the total weight of the film composition polyvinylpyrrolidone (PVP), polyvinyl alcohol (PVA), polyethylene oxide (PEO), polyvinyl acrylic acid (PVAc) and poly 0.01-20% by weight of at least one synthetic polymeric material selected from the group consisting of methacrylic acid (PMAc), gelatin, agar, carrageenan, alginate, chitosan, chitosan derivatives, starch, pullulan, galactomannan, glucomannan, guam, 0.01-20% by weight of at least one natural polymer selected from the group consisting of locust bean gum, pluronic, algin, xanthan and gellan, ceramide, kojic acid, α-hydroxy acid and β-hydroxy acid, retinol, vitamin C, Vitamin C Derivatives, Vitamin A, Vitamin E, Elastin, Amino Acids, Aloe, Centella Extract, Licorice Extract, Portulaca Extract, Beta Glucan, Proteaglucan, Guava, Grape Seed Extract 0.1-10% by weight of at least one skin affinity enhancer selected from the group consisting of chamomile and hyaluronic acid, Angelica, Echo herb, Situary mushroom, Pomegranate, Potato, Schisandra chinensis, Ganoderma lucidum, Astragalus, Aloe, Green tea, Ginseng, Wood vinegar, 0.1-10% by weight of at least one natural biomaterial, 1-20% by weight of polyhydric alcohol, 0.01-10% by weight of functional additive, 0.01-2% by weight of preservative, and water extracted from pine needles, ginkgo leaf, propolis, mulberry leaf or silkworm The composition is 8-98.76% by weight.
본 발명자들은 상기 각 성분들이 이러한 범위로 함유되어 필름을 형성하는 경우에, 피부에 적용시 피부에 존재하는 소량(예, 적어도 1%의 수분함량)의 수분에 의해 필름 조성물이 수용액상태로 변화하는 특성을 가지고 이에 따라 필름 조성물내에 함유되어 있는 성분들이 피부에 고르고 신속하게 밀착되고 침투되는 것을 발견하였다.The inventors of the present invention found that when each of the above components is contained in such a range to form a film, the film composition is changed into an aqueous solution by a small amount of moisture (eg, at least 1% water content) present in the skin when applied to the skin. It has been found that the properties and therefore the components contained in the film composition are evenly and quickly adhered and penetrated to the skin.
본 발명의 필름 조성물에 있어서, 필름 형성물질로서 합성 고분자 물질 및 천연 고분자 물질이 사용되며, 여기서, 상기 합성 고분자 물질은 폴리비닐피롤리돈(PVP), 폴리비닐알코올(PVA), 폴리에틸렌옥사이드(PEO), 폴리비닐아크릴산(PVAc) 및 폴리메타아크릴산(PMAc)으로 구성된 그룹으로부터 선택되며, 천연 고분자 물질은 젤라틴, 아가, 카라기난, 알기네이트, 키토산, 키토산 유도체, 전분, 풀루란, 갈락토만난, 글루코만난, 구아껌, 로카스트 빈 껌, 플루로닉, 알긴, 잔탄 및 겔란으로 구성된 그룹으로부터 선택된다.In the film composition of the present invention, a synthetic polymer material and a natural polymer material are used as the film forming material, wherein the synthetic polymer material is polyvinylpyrrolidone (PVP), polyvinyl alcohol (PVA), polyethylene oxide (PEO). ), Polyvinylacrylic acid (PVAc) and polymethacrylic acid (PMAc), and natural polymers are gelatin, agar, carrageenan, alginate, chitosan, chitosan derivatives, starch, pullulan, galactomannan, glucomannan , Guar gum, locust bean gum, pluronic, algin, xanthan and gellan.
이때, 상기 합성 고분자 물질 및 천연 고분자 물질은 조성물의 총 중량을 기준으로 각각 0.01-20중량%씩 함유되며, 만일 이러한 범위를 벗어나는 경우, 필름형 태로 형성되지 않거나 그 형태를 유지할 수 없으며 피부에 접착되어도 수분에 의해 용해되지 않을 수 있다.At this time, the synthetic polymer material and the natural polymer material is contained in each of 0.01-20% by weight based on the total weight of the composition, if out of this range, it is not formed in a film form or can not maintain its shape and adheres to the skin Even if it is, it may not be dissolved by moisture.
상기 피부친화성 증진제는 인체피부와의 친화성을 향상시켜주어 필름 조성물에서부터 피부로 미용제 또는 약물이 다량으로 신속하게 전달되도록 하는 역할을 하는 물질로서 이들은 세라마이드, 코직산, α-히드록시산 및 β-히드록시산, 레티놀, 비타민C, 비타민C 유도체, 비타민 A, 비타민 E,엘라스틴, 아미노산, 알로에, 병풀 추출물, 감초추출물, 마치현추출물, 베타글루칸, 프로테오글루칸, 구아바, 포도씨앗 추출물, 카모마일 및 히알루로닉산으로 구성된 그룹으로부터 선택되며, 그 함량은 조성물의 총 중량을 기준으로 0.1-10중량%가 바람직하다. 이러한 피부친화성 증진제는 그 함량이 너무 적은 경우에는 그 효과가 미미하며, 함량이 너무 많은 경우에는 수용해성이 저하될 수 있다.The skin affinity enhancer improves the affinity with the human skin and is a material that serves to quickly deliver a large amount of cosmetics or drugs from the film composition to the skin, such as ceramide, kojic acid, α- hydroxy acid and β Hydroxy acids, retinol, vitamin C, vitamin C derivatives, vitamin A, vitamin E, elastin, amino acids, aloe, centella extract, licorice extract, portulaca oleracea extract, beta glucan, proteoglucan, guava, grape seed extract, chamomile and It is selected from the group consisting of hyaluronic acid, the content of which is preferably 0.1 to 10% by weight based on the total weight of the composition. If the skin affinity enhancer is too small in content, the effect is insignificant, and in the case of too much content, water solubility may be reduced.
마찬가지로, 상기 천연생체물질은 인체피부와 친화성을 향상시켜주는 역할을 하는 물질로서 식물, 동물 또는 광물로부터 추출한 천연물이며 이에 한정하는 것은 아니지만 당귀, 어성초, 상황버섯, 석류, 감자, 오미자, 영지버섯, 황기, 알로에, 녹차, 인삼, 목초액, 솔잎, 은행잎, 프로폴리스, 뽕잎 또는 누에 등의 추출물이 유용하며, 그 함량은 조성물의 총 중량을 기준으로 0.1-10중량%이다. 이러한 천연생체물질은 그 함량이 너무 적은 경우, 그 효과가 미미하며 너무 많은 경우에는 수용해성이 저하될 수 있다.Similarly, the natural biological material is a material that serves to improve affinity with human skin and is a natural product extracted from plants, animals, or minerals, but is not limited to Angelica, Echochocho, Situary Mushroom, Pomegranate, Potato, Schisandra chinensis and Ganoderma lucidum. Extracts such as Astragalus, Aloe, Green Tea, Ginseng, Herbal Extract, Pine Needle, Ginkgo Leaf, Propolis, Mulberry Leaf or Silkworm, etc. are useful, and their content is 0.1-10% by weight based on the total weight of the composition. If the content of these natural biomaterials is too small, the effect is negligible, and in too many cases, the water solubility may be reduced.
상기 다가 알코올은 본 발명의 하이드로겔 조성물이 피부에 밀착되고 침투될 수 있도록 하는 물질로서 수용성 액상으로서 폴리에틸렌글리콜(PEG), 폴리프로필렌 글리콜(PPG), 1,3-부틸렌글리콜(1,3-BG), 글리세린, 솔비톨, 자일리톨 및 에리스리톨로 구성된 그룹으로부터 선택되며, 그 함량은 조성물의 총 중량을 기준으로 1-20중량%이다. 이러한 다가 알코올은 그 함량이 너무 적은 경우, 피부에 접착되어도 수분에 의해 용해되지 않을 수 있으며 그리고 너무 많은 경우에는 조성물이 필름형태로 형성되지 않는 문제가 발생할 수 있다.The polyhydric alcohol is a material that allows the hydrogel composition of the present invention to be in close contact with and penetrate the skin as a water-soluble liquid polyethylene glycol (PEG), polypropylene glycol (PPG), 1,3-butylene glycol (1,3- BG), glycerin, sorbitol, xylitol and erythritol, the content of which is 1-20% by weight based on the total weight of the composition. If the content of such polyhydric alcohol is too small, it may not be dissolved by water even if it is adhered to the skin, and in too many cases may cause a problem that the composition is not formed into a film form.
상기 기능첨가제는 필름에 안정성과 기능성을 부여할 수 있는 첨가제로서 메틸파라벤(MP), 프로필파라벤(PP), 코직산, α-히드록시산, 이미다졸리디닐우레아, 트윈80 및 레티놀 등이 유용하다. 이러한 기능첨가제는 조성물의 총 중량을 기준으로 0.01-10중량% 포함되며, 만일 그 함량이 너무 적은 경우, 보관 안정성이 저하되어 장기간 보존 유지되지 않으며 그리고 너무 많은 경우에는 수용해성이 저하되는 문제가 발생할 수 있다.As the functional additive, an additive capable of imparting stability and functionality to the film, methyl paraben (MP), propyl paraben (PP), kojic acid, α-hydroxy acid, imidazolidinyl urea, tween 80 and retinol are useful. . These functional additives are contained in an amount of 0.01 to 10% by weight based on the total weight of the composition, if the content is too small, the storage stability is lowered and not maintained for a long time, and if too much water solubility problem occurs Can be.
방부제는 방부 목적으로 사용되는 약물로서, 미생물의 증식으로 일어나는 물질 부패를 막는 약물이므로 미생물, 특히 부패균의 발육을 억제하거나 살균하는 작용을 위해 첨가된다. 본 발명에 사용되는 방부제로는 예를 들어, 파라옥시 향산 에스텔류, 페녹시에탄올, 이미다졸리디닐 우레아 및 페노닙 등을 포함한다. 이러한 방부제는 총 중량을 기준으로 0.01-2중량% 포함되며, 만일 그 함량이 너무 적은 경우, 장기간 보존 유지되지 않으며 그리고 너무 많은 경우에는 인체에 유해할 수 있다.Preservatives are drugs used for preservative purposes, and are drugs for preventing the decay of substances caused by the growth of microorganisms, and thus are added for the purpose of inhibiting or sterilizing the growth of microorganisms, especially decayed bacteria. Preservatives used in the present invention include, for example, paraoxy aromatic acid esters, phenoxyethanol, imidazolidinyl urea, phenonib, and the like. Such preservatives are included 0.01-2% by weight based on the total weight, if the content is too small, it is not maintained for a long time and too much can be harmful to the human body.
물은 필름 조성물의 주성분으로서 조성물의 총 중량을 기준으로 8-98.76중량%로 포함되며, 그 함량이 너무 적은 경우, 피부에 접착되어도 수분에 의해 용해되 지 않을 수 있으며 너무 많은 경우에는 필름형태로 형성되지 않거나 그 형태를 유지할 수 없다.Water is included in the composition of 8-98.76% by weight based on the total weight of the composition as a main component of the film composition, if the content is too small, even if adhered to the skin may not be dissolved by water and in too many cases in the form of a film It is not formed or cannot maintain its form.
한편, 본 발명의 필름은 다음과 같은 방법을 통해 제조될 수 있다.On the other hand, the film of the present invention can be produced through the following method.
상온에서 우선 물과 상기 합성 고분자 물질 그리고 천연 고분자 물질을 혼합하고 이를 30-80℃로 승온하여 용해시키고 이 용액을 30-80℃로 유지시키면서 다가알코올, 친화성 증진제, 기능첨가제, 방부제 및 천연생체물질를 혼합시킨다. 이때 혼합되는 각 성분 및 그 양은 본 발명의 필름 조성물에 대하여 앞서 설명한 바와 같다. 마찬가지로 이때 혼합되는 각 성분의 유용한 예는 앞서 설명한 바와 같다. 그 다음 상기 용액을 2-3,000㎛의 두께를 갖는 일정한 크기로 30-90℃에서 1분내지 30분동안 건조시켜 본 발명의 필름을 제조한다.At room temperature, water, the synthetic polymer, and the natural polymer are mixed first, and then dissolved by raising the temperature to 30-80 ° C., while maintaining the solution at 30-80 ° C., while maintaining the solution at 30-80 ° C. Mix the materials. At this time, each component to be mixed and the amount thereof are as described above for the film composition of the present invention. Likewise useful examples of each component to be mixed are as described above. The solution is then dried at 30-90 ° C. for 1 minute to 30 minutes to a constant size with a thickness of 2-3,000 μm to produce a film of the present invention.
본 발명의 피부미용 및 상처치료용 필름은 2-3,000㎛의 두께를 갖도록 형성된다. 만일 필름의 두께가 2㎛미만인 경우에는 필름 형성이 불가능하며, 또한 3,000㎛를 넘는 경우에는 피부 접착시 밀착성 및 착용감이 불쾌한 문제가 발생할 수 있다. 또한 본 발명의 필름은 사각형, 원형 또는 타원형 등 기타 다양한 모양일 수 있다. Skin care and wound treatment film of the present invention is formed to have a thickness of 2-3,000㎛. If the thickness of the film is less than 2㎛ impossible film formation, and if the thickness is more than 3,000㎛ may cause a problem that the adhesion and wearing uncomfortable during skin adhesion. In addition, the film of the present invention may be a variety of other shapes such as square, round or oval.
또한, 상기 피부미용 및 상처치료용 필름은 적당한 습기의 유지능력이 필요하고, 상처분비물의 조절능력, 외부의 상처부위 간의 공기 및 수증기 관통성, 외부 에 대한 상처부위의 단열성, 박테리아의 침입에 대한 저항성등이 요구되는 방수 필름을 더 구비할 수 있다. 이는 상기 피부미용 및 상처치료용 필름의 양면 또는 한쪽 면을 덮을 수 있으며 또한 제거가능 하도록 디자인될 수 있다. 이러한 방수 필름으로는 예를 들면, 열 접착성을 가지며 빛과 약물의 투과성이 없는 알루미늄 막이 코팅된 폴리에스테르 필름으로 구성될 수 있다. 그밖에도 폴리에스테르(PET), 폴리비닐알콜(PVA), 폴리비닐클로라이드(PVC), 폴리에틸렌(PE), 폴리우레탄(PU), 에틸렌 비닐 아세테이트 필름이 사용될 수 있다. 이러한 방수 필름의 두께는 이로 한정하는 것은 아니나 상기 수용성 필름과 동일한 두께를 가질 수 있다. In addition, the skin care and wound treatment film needs the ability to maintain adequate moisture, the ability to control the discharge of the wound, air and water vapor permeability between the external wound, the insulation of the wound on the outside, invasion of bacteria It may be further provided with a waterproof film requiring resistance. It can cover both or one side of the skin care and wound care film and can be designed to be removable. Such a waterproof film may be composed of, for example, a polyester film coated with an aluminum film having heat adhesiveness and having no light and drug permeability. In addition, polyester (PET), polyvinyl alcohol (PVA), polyvinyl chloride (PVC), polyethylene (PE), polyurethane (PU), ethylene vinyl acetate film may be used. The thickness of the waterproof film is not limited thereto, but may have the same thickness as the water-soluble film.
도 1에 방수 필름이 구비된 본 발명의 피부미용 및 상처치료용 수용성 필름을 모식적으로 나타내었다. 도 1에서 (가)는 본 발명의 수용성 필름을 나타내고 (나)는 방수 필름을 나타낸다.Figure 1 schematically shows a water-soluble film for skin care and wound treatment of the present invention provided with a waterproof film. In Figure 1 (a) represents a water-soluble film of the present invention (b) represents a waterproof film.
이와 같이 제조된 본 발명의 필름은 피부 접촉시 수분에 의해 서서히 용해되어 유효성분들이 피부로 침투되므로 상처의 치유를 촉진시키고, 상처를 입기 전의 상태로 가능한 가깝게 되돌려서 상처로 인한 아픔을 줄이고, 심한 흉터가 생기는 것을 방지하기 위한 제제로써, 상처가 난 후 초기에 상처 부위를 수용성 필름으로 압박하여 지혈을 할 수 있으며, 수용성 필름에서 유효성분이 서서히 방출되어 상처의 치유를 촉진시키고, 손상된 피부의 재생을 도와주며, 상처치유과정에서 피부의 재생이 가급적 빠르게 이루어지게 하여 흉터가 생기지 않게 도와주는 상처 치료 및 피부미용에 사용된다. 뿐만 아니라, 본 발명의 필름은 피부미용, 아토피, 입속 상처치료, 각질제거, 여드름 치료, 흉터제거, 밴드 등에 이용될 수 있다.The film of the present invention prepared as described above is gradually dissolved by moisture upon skin contact, so that the active ingredients penetrate into the skin, promoting healing of the wound, and returning as close as possible to the state before the wound, reducing pain caused by the wound, and As a preparation for preventing scars, hemostasis can be achieved by compressing the wound area with a water-soluble film at the initial stage after the wound, and the active ingredient is gradually released from the water-soluble film to promote healing of the wound and regeneration of damaged skin. It is used for wound healing and skin beauty to help prevent scars by helping skin regenerate as quickly as possible during wound healing. In addition, the film of the present invention can be used for skin care, atopy, oral wound treatment, exfoliation, acne treatment, scar removal, bands and the like.
이하 본 발명의 실시예는 본 발명의 일부분을 보다 구체적으로 설명하고 있으나 본 발명의 범주가 이에 한정되는 것은 아니다. Hereinafter, embodiments of the present invention will be described in more detail a part of the present invention, but the scope of the present invention is not limited thereto.
<실시예><Example>
실시예 1 - 7 (필름의 제조)Examples 1-7 (Preparation of Film)
상온에서 1ℓ가열용기에 교반하면서 하기 표 1에 나타낸 바와 같이 각 성분을 혼합하였다. 먼저 탈이온수에 필름 형성제인 고분자 물질을 첨가하고 60℃로 승온한 후 그 용액을 60℃로 유지시키면서 나머지 물질들을 첨가하였다. 피부친화성 증진제 및 기능첨가제를 나중에 첨가하였다. Each component was mixed as shown in Table 1 while stirring in a 1 L heating vessel at room temperature. First, a high molecular material as a film former was added to deionized water, and the temperature was raised to 60 ° C, and the remaining materials were added while maintaining the solution at 60 ° C. Skin affinity enhancers and function additives were added later.
그 다음, 이와 같이 제조된 혼합 용액을 1,000㎛의 두께를 갖는 5x5cm의 크기로 성형한 후 상온에서 5시간동안 건조하여 본 발명의 필름을 제조하였다. 필름형성제의 함량이 증가하면 할수록 강도가 강한 필름을 제조할 수 있었으며, 다가알코올류의 함량이 많을수록 유연한 필름을 제조할 수 있었다. Then, the mixed solution thus prepared was molded into a size of 5 × 5 cm having a thickness of 1,000 μm, and then dried at room temperature for 5 hours to prepare a film of the present invention. Increasing the content of the film-forming agent was able to produce a film with a strong strength, the more the polyhydric alcohol content was able to produce a flexible film.
실시예 8- 용해도 시험Example 8-Solubility Tests
실시예 1-7과 같은 방법으로 제조된 수용성 필름에 필름 무게에 대한 물의 함량을 0, 1, 5, 10, 20, 50%로 변화시켜 필름의 용해성 정도를 측정하였다. 그 결과를 표 2에 나타내었다. The degree of solubility of the film was measured by changing the water content to 0, 1, 5, 10, 20, and 50% of the water-soluble film prepared in the same manner as in Example 1-7. The results are shown in Table 2.
실험결과 수분이 없을 경우 필름은 전혀 용해되지 않았지만 필름 무게 대한 1%의 수분으로도 필름이 용해되었다. 따라서, 본 발명의 수용성 필름은 1%의 소량의 수분으로도 충분히 용해성을 나타냄을 알 수 있었다. In the absence of water, the film did not dissolve at all, but the film was dissolved even with 1% moisture relative to the film weight. Therefore, it was found that the water-soluble film of the present invention exhibits sufficient solubility even with a small amount of water of 1%.
( X; 용해되지 않음, △; 일부 용해됨, O; 완전 용해됨 )(X; not dissolved, Δ; partially dissolved, O; completely dissolved)
실시예 9 - 항균성 시험Example 9 Antibacterial Test
실시예 1로 제조된 본 발명의 피부 접착시 용해가 가능한 수용성 필름을 한국원사직물시험연구원(FITI)에 의뢰하여, 필름의 항균도 시험방법(필름밀착법, (FC-TM-20)-2001)으로 항균성 시험을 수행하였다. 그 결과를 하기 표 3에 나타내었다(본 발명의 피부 접착시 용해가 가능한 수용성 필름은 실시예 1의 피부 접착시 용해가 가능한 수용성 필름을 제조하고 충분히 컨디셔닝 시켜 준비됨).A water-soluble film that can be dissolved upon adhesion to the skin of the present invention prepared in Example 1 was commissioned by Korea Textile Testing Institute (FITI) to test the antimicrobial degree of the film (film adhesion method, (FC-TM-20) -2001 The antimicrobial test was performed. The results are shown in Table 3 below (the water-soluble film dissolvable upon skin adhesion of the present invention is prepared by preparing a water-soluble film dissolvable upon skin adhesion of Example 1 and sufficiently conditioned).
참고로, 직물의 항균도 시험방법(필름밀착법(FC-TM-20)-2001))은 일반적으로 다음과 같이 이루어진다.For reference, the antimicrobial test method of the fabric (film adhesion method (FC-TM-20) -2001) is generally made as follows.
① 시험균 전배양 : 시험균의 활성도를 높이기 위해 시행① Pre-cultivation of test bacteria: To increase the activity of test bacteria
② 시료 및 미가공포(또는 표준포)에 시험균 접종 : 미가공포에서 접종후 즉시 균을 중화용액을 이용하여 추출② Inoculation of test bacteria in samples and unprocessed cells (or standard cells): Extract the bacteria immediately after inoculation from the untreated cells using neutralizing solution.
③ 접종한 시료 및 표준포를 18시간 배양③ Incubate the inoculated sample and standard cloth for 18 hours
④ 배양된 시료 및 표준포에서 중화용액을 이용하여 균을 추출④ Extract the bacteria from the cultured sample and standard cloth using neutralization solution
⑤ ②와 ④의 추출액을 단계별로 희석하여 배지에서 배양⑤ Dilute extracts of ② and ④ step by step and incubate in medium
⑥ 배양된 배지에서 균수측정 후 살균율 및 정균율 계산⑥ Calculation of bactericidal rate and bacteriostatic rate after measuring the number of bacteria in cultured medium
*항균가공제품과 대조편에 공시균을 접종하여 배양한 후, 생균수를 측정하여, 항균가공제품(가공포)과 대조편(표준포)을 비교함으로써 균의 성장을 억제하는 활성도(정균감소율)는 다음과 같이 수학식 1에 의해 계산된다.* Inoculation of antibacterial processed products and control pieces by inoculation with the test bacteria, and measuring the number of live bacteria, and comparing the antibacterial products (processed fabrics) and the control pieces (standard fabrics), the activity of inhibiting the growth of bacteria (bactericidal reduction rate) ) Is calculated by
(B=가공포의 배양후 균수, C=표준포의 배양후 균수)(B = number of bacteria after culture of processed cells, C = number of bacteria after culture of standard cells)
*공시균: 1) 스타필로코커스 아우레우스(Staphylococcus aureus) ATCC 6538Species: 1) Staphylococcus aureus ATCC 6538
2) 클렙시엘라 뉴모니아(Klebsiella pneumoniae) ATCC 43522) Klebsiella pneumoniae ATCC 4352
상기 표 2에 나타낸 바와 같이, 본 발명의 피부 접착시 용해가 가능한 수용성 필름은 스타필로코커스 아우레우스(Staphylococcus aureus) 및 클렙시엘라 뉴모니아(Klebsiella pneumoniae)에 대하여 모두 99.9%이상의 정균율을 나타내어 매우 우수한 항균성을 가짐을 알 수 있다.As shown in Table 2, the water-soluble film that can be dissolved during skin adhesion of the present invention has a bacteriostatic ratio of 99.9% or more for Staphylococcus aureus and Klebsiella pneumoniae . It can be seen that it has very good antimicrobial properties.
본 발명의 피부 접착시 용해가 가능한 수용성 필름은 피부 접착시 수분으로 인해 서서히 용해되면서 유효성분이 신속하게 경피속으로 전달될 수 있는 특징을 갖는 것으로써, 피부에 적용시 상처의 치유를 촉진시키고, 상처를 입기 전의 상태로 가능한 가깝게 되돌려서 상처로 인한 아픔을 줄이고, 심한 흉터가 생기는 것을 방지하기 위한 제제로써, 상처가 난 후 초기에 상처 부위를 수용성 필름으로 압박하여 지혈을 할 수 있으며, 수용성 필름에서 유효성분이 서서히 방출되어 상처의 치유를 촉진시키고, 손상된 피부의 재생을 도와주며, 상처치유과정에서 피부의 재생이 가급적 빠르게 이루어지게 하여 흉터가 생기지 않게 도와주는 상처 치료용 드레싱 및 피부미용 팩제로 유용하게 활용될 수 있다. 특히, 본 발명의 수용성 필름은 상처치료, 피부미용, 아토피, 입속 상처치료, 각질제거, 여드름 치료, 흉터제거, 밴드 등에 효과적으로 활용될 수 있다.The water-soluble film that can be dissolved during skin adhesion of the present invention has a feature that the active ingredient can be quickly delivered into the percutaneous body while being dissolved gradually due to moisture during skin adhesion, thereby promoting wound healing when applied to the skin, and It is a preparation to reduce the pain caused by wounds and to prevent severe scars by returning as close as possible to the state before wearing, and to hemostasis by compressing the wound site with a water-soluble film at the beginning after the wound. The active ingredient is gradually released to promote healing of wounds, to help rejuvenate damaged skin, and to regenerate the skin as quickly as possible during wound healing, and to be useful as a wound dressing and skin care pack to help prevent scars. Can be utilized. In particular, the water-soluble film of the present invention can be effectively used for wound treatment, skin care, atopy, oral wound treatment, exfoliation, acne treatment, scar removal, bands.
Claims (7)