KR100525646B1 - 법랑용 열간압연강판 제조방법 - Google Patents
법랑용 열간압연강판 제조방법 Download PDFInfo
- Publication number
- KR100525646B1 KR100525646B1 KR10-2001-0054414A KR20010054414A KR100525646B1 KR 100525646 B1 KR100525646 B1 KR 100525646B1 KR 20010054414 A KR20010054414 A KR 20010054414A KR 100525646 B1 KR100525646 B1 KR 100525646B1
- Authority
- KR
- South Korea
- Prior art keywords
- enamel
- steel sheet
- rolled steel
- hot rolled
- less
- Prior art date
Abstract
Description
강의 조성 (중량%) | 열간압연(℃) | 조질압연(%) | ||||||||
C | Mn | P | S | N | Ti | 3(C+N) | 마무리 | 권취 | ||
실시예1 | 0.036 | 0.20 | 0.014 | 0.015 | 0.0068 | 0.135 | 0.1284 | 875 | 643 | 3 |
실시예2 | 0.041 | 0.23 | 0.015 | 0.014 | 0.0058 | 0.146 | 0.1404 | 865 | 605 | 5 |
실시예3 | 0.028 | 0.19 | 0.017 | 0.015 | 0.0063 | 0.130 | 0.1029 | 860 | 635 | 2 |
실시예4 | 0.031 | 0.20 | 0.014 | 0.013 | 0.0057 | 0.128 | 0.1101 | 858 | 603 | 3 |
실시예5 | 0.028 | 0.28 | 0.013 | 0.015 | 0.0048 | 0.130 | 0.0984 | 865 | 598 | 4 |
비교예1 | 0.028 | 0.21 | 0.013 | 0.012 | 0.0050 | 0.136 | 0.0990 | 880 | 630 | - |
비교예2 | 0.030 | 0.21 | 0.016 | 0.011 | 0.0049 | 0.142 | 0.1047 | 950 | 600 | - |
비교예3 | 0.030 | 0.21 | 0.016 | 0.011 | 0.0049 | 0.142 | 0.1047 | 900 | 750 | - |
비교예4 | 0.036 | 0.20 | 0.014 | 0.015 | 0.0068 | 0.230 | 0.1284 | 900 | 700 | - |
비교예5 | 0.004 | 0.23 | 0.011 | 0.063 | 0.0029 | 0.077 | 0.0207 | 850 | 550 | - |
법랑 특성 | ||
법랑층 두께 (㎛) | 표면결함 발생여부 | |
실시예 1 | 254 | 미발생 |
실시예 2 | 242 | 미발생 |
실시예 3 | 253 | 미발생 |
실시예 4 | 220 | 미발생 |
실시예 5 | 232 | 미발생 |
비교예 1 | 241 | 미발생 |
비교예 2 | 223 | 미발생 |
비교예 3 | 241 | 미발생 |
비교예 4 | 263 | 발생 |
비교예 5 | 251 | 미발생 |
법랑 특성 | ||
피쉬스케일 수 | 법랑밀착지수 (PEI 지수) | |
실시예1 | 0 | 98 |
실시예2 | 0 | 99 |
실시예3 | 0 | 100 |
실시예4 | 0 | 97 |
실시예5 | 0 | 97 |
비교예1 | 20 | 93 |
비교예2 | 137 | 84 |
비교예3 | 142 | 86 |
비교예4 | 16 | 88 |
비교예5 | 0 | 93 |
Claims (2)
- C 0.01~0.1 중량%, Mn 0.1~1.0 중량%, P 0.05 중량% 이하, S 0.05 중량% 이하, N 0.015 중량% 이하, Ti 0.05~0.2 중량%를 포함하고, Ti 함량이 C 함량과 N 함량의 합보다 3배 이상 큰 알루미늄 킬드강을 열간압연하여 830~900℃의 온도에서 열간압연을 마무리하는 단계, 및상기 열간압연된 강판을 700℃ 이하의 온도에서 권취한 후, 상기 강판의 표면온도가 25℃ 이하에서 두께의 1~10%로 조질압연을 수행하는 단계를 포함하는 법랑용 열간압연강판 제조 방법.
- 제1항에 있어서,상기 열간압연강판은 두께가 2.0mm 이상인 법랑용 열간압연강판 제조 방법.