KR100502199B1 - Fasciated spinning multiple ply yarn and fabric - Google Patents
Fasciated spinning multiple ply yarn and fabric Download PDFInfo
- Publication number
- KR100502199B1 KR100502199B1 KR10-2003-0053143A KR20030053143A KR100502199B1 KR 100502199 B1 KR100502199 B1 KR 100502199B1 KR 20030053143 A KR20030053143 A KR 20030053143A KR 100502199 B1 KR100502199 B1 KR 100502199B1
- Authority
- KR
- South Korea
- Prior art keywords
- fiber
- polyester
- fabric
- fibers
- cotton
- Prior art date
Abstract
본 발명은 슬릿형 폴리에스테르 섬유를 심부로 하고, 이 심부의 둘레를 둘러 싼 표면 섬유를 면 섬유로 하여 2층 구조로 결속 방적한 방적사와 이를 사용한 직물에 관한 것이다. 본 발명의 방적사를 사용한 직물은, 격렬한 운동으로 발생한 땀을 친수성 섬유인 표면의 면 섬유에서 먼저 흡수하고, 면 섬유에 흡수된 땀을 폴리에스테르 섬유의 길이 방향으로 형성된 무수한 슬릿에 의한 모세관 현상에 의하여 넓게 확산시킨다. 확산된 수분은 공기와의 접촉면이 넓어지고 또한 폴리에스테르의 함수율이 낮다는 특성으로 인하여 건조가 신속하게 진행한다. 특히, 이러한 일련의 과정은 연속 반복적이 이루어지므로 계속적으로 땀이 발생하여도 즉시 건조가 되어 항상 쾌적한 느낌을 주게 된다. 또한 표면의 면 섬유는 피부에 닿는 촉감이 매우 부드럽기 때문에 폴리에스테르만으로 된 섬유에서 느끼게 되는 거친 불쾌감이 제거된다.The present invention relates to a spun yarn and a fabric using the same, in which a slit polyester fiber is used as a core and a surface fiber wrapped around the core as a cotton fiber. The fabric using the spun yarn of the present invention first absorbs the sweat generated by the violent movement from the cotton fiber on the surface, which is a hydrophilic fiber, and the sweat absorbed by the cotton fiber by capillary phenomenon due to the countless slit formed in the longitudinal direction of the polyester fiber. Spread widely Diffused moisture is rapidly dried due to its wide contact surface with air and low water content of polyester. In particular, this series of processes are repeated continuously so that even if sweat occurs continuously, it immediately dries and always gives a pleasant feeling. In addition, the cotton fibers on the surface are very soft to the skin, eliminating the coarse discomfort felt in polyester-only fibers.
Description
본 발명은 방적사 및 이를 사용하여 제조한 직물에 관한 것으로서, 보다 상세하게는 슬릿(slit)형 폴리에스테르 섬유와 면 섬유를 2층구조로 결속방적한 방적사 및 이 방적사를 사용하여 제조한 직물에 관한 것이다.The present invention relates to a spun yarn and a fabric manufactured using the same, and more particularly, to a spun yarn in which a slit polyester fiber and a cotton fiber are bound and spun in a two-layer structure and a fabric manufactured using the spun yarn. will be.
일반적으로 의류용 섬유는 피부의 온도 및 습도를 유지시키고, 인체에 쾌적한 착용감을 주기 위하여 인체로부터 발산되는 땀과 같은 액상의 물질 등을 신속하게 흡수하여 건조시키는 기능을 갖추어야 한다.In general, clothing fibers should have a function of quickly absorbing and drying liquid substances such as sweat emitted from the human body in order to maintain the temperature and humidity of the skin and give a comfortable fit to the human body.
특히 격렬한 운동으로 인하여 많은 땀을 처리해야 하는 운동복과 같은 스포츠 의류에 있어서는 무엇보다도 땀을 빨리 흡수하여 이를 건조 시킬 수 있는 섬유가 요구된다.In particular, sports clothing such as sportswear that has to deal with a lot of sweat due to vigorous exercise requires a fiber that can absorb the sweat quickly and dry it above all.
이러한 요구를 충족시키기 위한 종래의 기술로는, 미국 특허 제5,736,243호와 미국 특허 제6,458,455호가 있는데, 현재 스포츠의류에는 듀폰(Du Pont)사의 쿨맥스(COOLMAX)라는 상표의 섬유직물이 널리 사용되고 있다. 쿨맥스는 도 1에 도시된 바와 같이 섬유의 단면을 볼록볼록하게 형성하여 섬유에 4개의 골을 형성하였다. 이러한 단면의 섬유가 여러 다발로 합쳐지면 섬유에 형성된 각각의 골은 서로 밀착되어 가는 관의 형성하게 되는 데 땀과 같은 수분이 주위에 닿으면 이러한 관은 모세관 현상을 일으키게 되어 수분을 빨아 들여 넓게 분산시키게 되고, 이에 따라 수분이 빨리 증발하므로 쉽게 건조된다.Conventional techniques for meeting this need include US Pat. No. 5,736,243 and US Pat. No. 6,458,455. Currently, textiles under the trademark COOLMAX of Du Pont are widely used in sports clothing. Coolmax is convexly formed in the cross section of the fiber as shown in Figure 1 to form four bones in the fiber. When the fibers of these cross-sections are combined into bundles, each of the bones formed in the fibers forms a tube that closely adheres to each other. When moisture, such as sweat, touches the surroundings, these tubes cause capillary phenomena, which absorb the moisture and disperse them widely. This causes the moisture to evaporate quickly so that it dries easily.
그러나 이와 같은 뛰어난 기능성에도 불구하고 쿨맥스는 폴리에스테르로 만들어지기 때문에 촉감이 거칠다는 단점을 지니고 있다. 특히 피부와 마찰이 심해지면 피부가 손상된다는 문제점이 지적되고 있다.However, despite its excellent functionality, Coolmax is made of polyester and has the disadvantage of being rough. In particular, it is pointed out that the skin is damaged when friction with the skin becomes severe.
미국 특허 제 5,888,914호는 이와 같은 문제점을 해결하기 위하여 폴리에스테르와 같은 소수성 섬유 85 내지 90 중량%와 면섬유와 같은 친수성 섬유 10 내지 15 중량%의 비율로 혼합을 하였다. 이는 여러 가지 비율로 소수성 섬유와 친수성 섬유를 혼합한 것을 착용테스트를 거쳐서 그 비율을 결정한 것이다.In order to solve this problem, U. S. Patent No. 5,888, 914 mixes 85 to 90 wt% of hydrophobic fibers such as polyester and 10 to 15 wt% of hydrophilic fibers such as cotton. This ratio was determined by mixing a hydrophobic fiber with a hydrophilic fiber in various ratios through a wear test.
소수성 섬유와 친수성 섬유를 혼합하여 촉감이 거칠다는 문제점을 상당히 해소한 이러한 기술은 친수성 섬유만으로 된 직물에 비하면 착용감이 떨어지고, 상기의 쿨맥스와 같은 소수성 섬유만으로 된 직물에 비하면 기능성이 약간 떨어지는 경향이 있다.This technology, which solves the problem of roughness by mixing hydrophobic fibers and hydrophilic fibers, is less comfortable to wear than hydrophilic fibers only, and tends to be slightly less functional than hydrophobic fibers such as Coolmax. have.
본 발명은 촉감에 있어서는 친수성 섬유만으로 된 직물과 같은 착용감을 느낄 수 있으면서도, 빠른 건조라는 기능에 있어서는 소수성 섬유만으로 된 직물에 뒤지지 않는 섬유와 이러한 섬유로 된 직물을 제공하는 것을 목적으로 한다.An object of the present invention is to provide a fabric that can feel the same fit as a woven fabric made of hydrophilic fibers, but which does not lag behind a woven fabric made of only hydrophobic fibers in a quick drying function.
본 발명의 상기의 목적은, 폴리에스테르 섬유를 심부로 하고, 상기 심부를 둘레를 둘러 싼 표면 섬유를 면 섬유로 하여 2층 구조로 결속방적한 방적사와 이를 사용한 직물을 제공하는 것에 의해 달성된다.The above object of the present invention is achieved by providing a spun yarn which is bound and spun in a two-layer structure using polyester fibers as cores and surface fibers surrounding the cores as cotton fibers, and a fabric using the same.
즉, 본 발명에 따른 방적사는 심부를 75 내지 84 중량%의 폴리에스테르 섬유로, 상기 심부를 둘러싸는 표면섬유를 16 내지 25 중량%의 면 섬유로 하여 결속방적한다. That is, the spun yarn according to the present invention binds and spuns the core with 75 to 84% by weight of polyester fiber and the surface fiber surrounding the core with 16 to 25% by weight of cotton fiber.
상기의 폴리에스테르 섬유는 슬릿형 폴리에스테르와 같은 이른바 기능성 폴리에스테르를 사용한다. 슬릿형 폴리에스테르란 가공을 하게 되면 표면에 무수히 많은 가는 슬릿(slit)이 길이 방향으로 형성되는 폴리에스테르를 말한다.The polyester fiber uses a so-called functional polyester such as slit polyester. Slit polyester refers to a polyester in which a myriad of thin slits are formed in the longitudinal direction upon processing.
상기의 결속 방적된 방적사는 이를 감량 가공한다.The bound spun yarn is weight-reduced.
여기서, 폴리에스테르 섬유는 0.7 내지 1.5 데니어(denier)인 것이 바람직하다.Here, it is preferable that polyester fiber is 0.7-1.5 denier.
최적의 촉감과 기능성을 부여하기 위하여는 폴리에스테르 섬유를 80 중량%, 면 섬유는 20 중량%으로 결속방적하는 것이 바람직하다.In order to provide optimal touch and functionality, it is preferable to bind and spun 80% by weight of polyester fiber and 20% by weight of cotton fiber.
본 발명에 따른 방적사로 이루어진 직물은 이를 감량 가공하는 것이 바람직하다.Fabrics made of yarns according to the present invention is preferably to reduce the weight.
본 발명에 따른 방적사는 폴리에스테르에 친수성을 부여하기 위하여 친수성 폴리머 가공재를 사용하는 위킹(wicking) 가공을 할 수 있다.The spun yarn according to the invention can be wicked using a hydrophilic polymer workpiece to impart hydrophilicity to the polyester.
본 발명은 폴리에스테르 섬유와 면 섬유로 2층 구조로 결속방적된 방적사를 이용하여 제조된 직물을 제공한다. 직물의 제조는 일반적인 직물제조 방법에 의하므로 여기서는 언급하지 않는다.The present invention provides a fabric made using a spun yarn bound in a two-layer structure of polyester fibers and cotton fibers. The manufacture of the fabric is by way of the usual fabric making methods and is not mentioned here.
본 발명에 따른 직물에 폴리에스테르의 친수성을 부여하기 위하여 친수성 폴리머 가공재를 사용하는 위킹(wicking) 가공을 할 수 있다. 이를 통하여 폴리에스테르는 친수화 되며 수분의 흡습성이 강화될 수 있다.In order to impart the hydrophilicity of the polyester to the fabric according to the present invention, a wicking process using a hydrophilic polymer workpiece can be performed. Through this, the polyester may be hydrophilized and moisture absorption may be enhanced.
이하 도면에 의거하여 본 발명을 상세하게 설명한다.EMBODIMENT OF THE INVENTION Hereinafter, this invention is demonstrated in detail based on drawing.
도 2는 본 발명의 심부로 사용되는 슬릿형 폴리에스테르 섬유를 확대한 도면이다. 본 발명에 따른 결속방적사는 폴리에스테르 섬유를 심부(1)로 사용하고, 상기 심부에 대하여 면섬유를 표면섬유(2)로 하여 심부를 둘러싸도록 2층 구조로 결속 방적한다. 도시된 바와 같이 상기 방적사에 사용되는 폴리에스테르 섬유(1)에는 슬릿(3)이 형성된 기능성 폴리에스테르 섬유를 사용하는데 이는 감량 가공시 폴리에스테르 섬유에 길이 방향으로 슬릿(slit)이 발생하기 때문이다. 폴리에스테르 섬유는 면이 매끄럽지 않고 많은 주름이 주름(3)이 잡힌 형상이다. 일반적으로 감량 가공은 알칼리로 폴리에스테르 섬유의 표면을 3∼5% 정도 녹이는 감량하게 되는데 이 때 폴리에스테르는 주름을 메우고 있는 부분이 녹으면서 수많은 슬릿(3)이 형성되어 그 결과 거친 폴리에스테르 섬유를 보다 부드럽게 할 수 있다. 그런데 기능성 폴리에스테르의 경우에는 길이 방향으로 주름이 잡힌 형상이므로 감량 가공시 생기는 슬릿이 길이 방향으로 형성된다. 따라서 본 발명의 경우에 있어서는 감량 가공을 하면 폴리에스테르 섬유(1) 표면에 길이 방향으로 무수히 많은 슬릿(3)이 형성되는데 이러한 미세한 슬릿(slit)들은 일종의 모세관으로 모세관 현상에 의하여 수분을 주변으로 넓게 확산시켜 수분의 신속한 증발을 유도한다.2 is an enlarged view of a slit polyester fiber used as the core of the present invention. The binding spun yarn according to the present invention uses polyester fibers as the core portion 1, and binds and spuns the yarn into a two-layer structure so as to surround the core portion with the cotton fibers as the surface fibers 2 with respect to the core portion. As shown in the figure, the polyester fiber 1 used in the yarn is used a functional polyester fiber in which the slit 3 is formed, because slits are generated in the length direction in the polyester fiber during weight loss processing. Polyester fiber is a shape in which cotton is not smooth and many wrinkles are gathered with the wrinkles 3. In general, the weight loss process is about 3 to 5% of the surface of the polyester fiber with alkali to reduce the weight. At this time, the polyester is filled with pleats and many slits (3) are formed, resulting in coarse polyester fiber. I can make it softer. However, in the case of the functional polyester, since the shape is wrinkled in the longitudinal direction, slits generated during the weight loss processing are formed in the longitudinal direction. Therefore, in the case of the present invention, when the weight loss processing, a myriad of slits 3 are formed on the surface of the polyester fiber 1 in the longitudinal direction, and these fine slits are a kind of capillary tube, which expands the water around the capillary phenomenon. Diffusion leads to rapid evaporation of moisture.
도 3은 본 발명에 따른 2층 구조 결속방적사를 확대한 도면이다.3 is an enlarged view of the two-layered binding yarn in accordance with the present invention.
도시된 바에서 알 수 있듯이, 본 발명에 따른 방적사는 심부를 75 내지 84 중량%의 폴리에스테르 섬유(1)로, 상기 심부를 둘러싸는 표면섬유를 16 내지 25 중량%의 면 섬유(2)로 하여 2층 구조로 결속방적한다. 이러한 2층 구조의 결속방적사로 이루어진 직물은, 착용자가 운동을 하면서 흘리는 땀을 친수성 섬유인 표면의 면 섬유(2)로 먼저 흡수하고, 면 섬유에 흡수된 땀이 폴리에스테르 섬유(1)의 길이 방향으로 형성된 무수한 슬릿에 의한 모세관 현상에 의하여 넓게 퍼지면서 확산시키다. 확산된 수분은 공기와의 접촉면이 넓어지고 또한 폴리에스테르의 함수율(공정수분율: 0.4%)이 낮다는 소수성 섬유의 특성으로 인하여 건조가 신속하게 진행한다. 특히, 이러한 일련의 과정은 연속 반복적이 이루어지므로 계속적으로 땀이 발생하여도 즉시 건조가 되어 항상 쾌적한 느낌을 주게 된다. 또한 표면의 면 섬유는 피부에 닿는 촉감이 매우 부드럽기 때문에 폴리에스테르만으로 된 섬유에서 느끼게 되는 거친 불쾌감이 제거된다.As can be seen, the yarn according to the invention is made from 75 to 84% by weight of polyester fibers (1) in the core, and from 16 to 25% by weight of cotton fibers (2) in the surface fibers surrounding the core. And bind and spin in a two-layer structure. The fabric composed of the two-layer bundled yarn is first absorbed by the cotton fiber (2) on the surface of the surface of the hydrophilic fiber while the wearer is working out, and the sweat absorbed by the cotton fiber is the length of the polyester fiber (1). It spreads widely by capillary phenomenon caused by countless slits formed in the direction. Diffused moisture is rapidly dried due to the property of hydrophobic fibers, which have a wide contact surface with air and low polyester moisture content (process water content: 0.4%). In particular, this series of processes are repeated continuously so that even if sweat occurs continuously, it immediately dries and always gives a pleasant feeling. In addition, the cotton fibers on the surface are very soft to the skin, eliminating the coarse discomfort felt in polyester-only fibers.
본 발명에 따른 방적사는 일반적인 직물제조방법에 의하여 직물을 형성하게 되는데, 이렇게 만들어진 직물은 이를 감량 가공할 수 있다. 본 발명에 따른 방적사를 방적사 상태에서 감량 가공하지 않은 경우에는 직물상태에서 감량 가공을 할 수 있으며, 상기 방적사를 감량 가공한 경우에도 필요에 따라 직물을 2차 감량 가공할 수도 있다.The spun yarn according to the present invention is to form a fabric by a general fabric manufacturing method, the fabric thus made can be processed to reduce it. When the spinning yarn according to the present invention is not weight-reduced in the state of spinning yarns, weight loss processing may be performed in the fabric state, and even if the yarns are weight-reduced, the fabric may be secondaryly weight-reduced as needed.
또한 상기 직물은 이를 위킹 가공처리할 수 있는데 이는 폴리에스테르의 표면에 친수성을 부여하기 위한 것으로 이를 통하여 수분의 흡수성을 강화하게 된다.In addition, the fabric can be wicked, which is to impart hydrophilicity to the surface of the polyester to thereby enhance the absorption of moisture.
표 1은 젖은 상태에서 10분 경과후 본 발명에 따른 직물과 다른 섬유의 직물들의 건조 정도를 비교 시험한 표이다.Table 1 is a comparison test of the degree of drying of the fabric of the fabric and other fibers according to the invention after 10 minutes in the wet state.
[표 1]TABLE 1
본 발명에 따른 직물은 건조 시간이 가장 짧은 것으로 알려진 쿨맥스와 거의 동일한 건조정도를 나타내고 있음을 알 수 있다.It can be seen that the fabric according to the invention exhibits almost the same degree of drying as Coolmax, which is known to have the shortest drying time.
표 2는 상기 시험에서 30분이 경과 후의 상태를 나타낸 것이다.Table 2 shows the state after 30 minutes in the test.
[표 2]TABLE 2
이상에서 알 수 있듯이 본 발명에 따른 직물은 30분이 경과된 후에는 약 93%정도 건조된 것을 알 수 있다. 이를 통하여 본 발명에 따른 직물은 다른 섬유로 된 직물과 비교할 때 월등히 향상된 기능을 지니면서도 면섬유와 같은 촉감을 주기 때문에 기능성과 착용감 모두를 충족 시킨다는 것을 알 수 있다.As can be seen from the above, the fabric according to the present invention can be seen that after about thirty minutes is dried by about 93%. Through this, it can be seen that the fabric according to the present invention satisfies both functionality and fit because it gives a touch like cotton fiber while having a significantly improved function compared to other fabrics.
본 발명에 따른 방적사 및 이를 이용한 직물은, 운동시 발생하는 땀을 표면의 면 섬유를 통하여 즉시 흡수시키고, 수분의 통로가 형성된 폴리에스테르 섬유로 된 심부의 모세관 현상을 통하여 폴리에스테르 섬유가 흡수한 수분을 넓게 확산시키게 된다. 수분이 확산되게 되면 젖은 옷이 빨리 마르게 된다. 또한 면 섬유를 표면 섬유로 사용하기 때문에 그 촉감이 매우 부드러워 쾌적한 착용감을 주게 된다.The yarn and the fabric using the same according to the present invention, the sweat generated during exercise immediately absorbs through the cotton fiber on the surface, the moisture absorbed by the polyester fiber through the capillary phenomenon of the core of the polyester fiber formed the passage of the moisture It spreads widely. As moisture spreads, wet clothing dries quickly. In addition, since cotton fibers are used as surface fibers, the feel is very soft, giving a comfortable fit.
도 1은 4개의 채널이 형성된 종래의 기술에 의한 섬유를 확대도,1 is an enlarged view of a fiber according to the related art in which four channels are formed;
도 2는 본 발명의 슬릿형 폴리에스테르 섬유의 확대도,2 is an enlarged view of a slit polyester fiber of the present invention,
도 3은 본 발명에 따른 방적사를 확대한 도면이다.3 is an enlarged view of the yarn in accordance with the present invention.
<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>
1: 심부 2: 표면 섬유1: core 2: surface fiber
3: 슬릿3: slit
Claims (9)