KR100494993B1 - Waterproof Agent Comprising Alkylalkoxysilane and High Polymer - Google Patents
Waterproof Agent Comprising Alkylalkoxysilane and High Polymer Download PDFInfo
- Publication number
- KR100494993B1 KR100494993B1 KR10-2002-0030697A KR20020030697A KR100494993B1 KR 100494993 B1 KR100494993 B1 KR 100494993B1 KR 20020030697 A KR20020030697 A KR 20020030697A KR 100494993 B1 KR100494993 B1 KR 100494993B1
- Authority
- KR
- South Korea
- Prior art keywords
- alkylalkoxysilane
- water
- emulsion cream
- present
- weight
- Prior art date
Abstract
본 발명은 실란계 방수제에 관한 것으로서, 보다 상세하게는 알킬알콕시실란 및 고분자 화합물을 포함하는 에멀션 크림 및 이를 유효 성분으로 포함하는 토건용 침투성 방수제에 관한 것이다.The present invention relates to a silane-based waterproofing agent, and more particularly, to an emulsion cream containing an alkylalkoxysilane and a high molecular compound and a permeable waterproofing agent for civil engineering comprising the same as an active ingredient.
본 발명은 투수 저항성이 개선되어 방수성이 증진된 알킬알콕시실란 에멀션 크림 및 이를 포함하는 침투성 방수제를 제공하며 본 발명의 에멀션 크림 및 침투성 방수제는 알킬알콕시실란 및 고분자 화합물을 포함하여 발수성 뿐만 아니라 무기질 재료의 모세관까지 완전히 막아 현저히 증진된 방수성을 나타내므로, 별도의 방수 마감이 필요없이 큰 수압이 작용하는 부위에 사용될 수 있다.The present invention provides an alkylalkoxysilane emulsion cream having improved permeability resistance and improved waterproofness, and a permeable waterproofing agent comprising the same. The emulsion cream and permeable waterproofing agent of the present invention include an alkylalkoxysilane and a high molecular compound. It completely blocks up to the capillary tube to show significantly enhanced water resistance, so that it can be used in areas where large water pressure is applied without requiring a separate waterproof finish.
Description
본 발명은 실란계 방수제에 관한 것으로서, 보다 상세하게는 알킬알콕시실란 및 고분자 화합물을 포함하는 에멀션 크림 및 이를 유효 성분으로 포함하는 토건용 침투성 방수제에 관한 것이다.The present invention relates to a silane-based waterproofing agent, and more particularly, to an emulsion cream containing an alkylalkoxysilane and a high molecular compound and a permeable waterproofing agent for civil engineering comprising the same as an active ingredient.
구조물 중 다공성 무기 건축 재료, 예컨대, 콘크리트 등은 다공성 재료에 포함된 모세관을 통한 물의 흡수로 인하여 침식으로 인한 피해가 발생할 수 있다. 이를 방지하기 위하여 모세관에 발수제, 즉 소수성 물질을 얇게 도포하여 물의 흡수를 차단하게 된다.Porous inorganic building materials, such as concrete, among the structures can cause damage due to erosion due to absorption of water through capillaries contained in the porous material. To prevent this, a thin layer of water repellent, that is, hydrophobic material, is applied to the capillary to block water absorption.
이러한 발수제로는 실란 등의 실리콘 화합물 및 불소 수지 등의 고분자 화합물 등 매우 다양한 재료들이 사용된다. 현재 가장 많이 사용되는 재료로는 실리콘 화합물이 주종을 이루고 있으며 실란은 이러한 발수제로서 매우 효과적인 재료로 알려져 있다. As such a water repellent, a wide variety of materials such as silicone compounds such as silane and polymer compounds such as fluorine resin are used. Currently, the most commonly used material is silicone compound, and silane is known to be a very effective material for such a water repellent.
실란은 분자의 크기가 작은 단량체로서, 재료에 침투된 후 발수성이 부과된다. 즉, 실란은 대기 중의 수분과 반응하여 실란올로 전환된 후 고분자화되어 발수성을 갖게 된다. 따라서, 이를 표면에 도포하는 경우 구조물의 내구성이 현저히 증가하게 된다. 특히, 알킬알콕시실란은 침투성이 뛰어나며 화학 반응에 의해 강한 소수성 층을 형성할 수 있으므로 다공성 무기 건축 재료에 대한 발수제로서 유용한 것으로 알려져 있다.Silane is a small molecule monomer, impregnated with water repellency after penetration into the material. That is, the silane reacts with moisture in the air, is converted into silanol, and then polymerized to have water repellency. Therefore, the durability of the structure is significantly increased when it is applied to the surface. In particular, alkylalkoxysilanes are known to be useful as water repellents for porous inorganic building materials because they have excellent permeability and can form strong hydrophobic layers by chemical reactions.
한편, 침투성 발수제는 콘크리트 등을 재료로 한 무기 건축 구조물에 도포 시 침투 후 반응하여 콘크리트 내부에 발수력을 발생시켜 물의 흡수를 차단하는 것이다.On the other hand, the permeable water repellent is to block the absorption of water by generating a water-repellent force inside the concrete by reacting after infiltration when applied to the inorganic building structure made of concrete and the like.
예컨대, 대한민국 특허 제 227922 호는 알킬알콕시실란의 입자 크기가 2-10 ㎛이며 농도가 5-70 중량%인 에멀션을 개시하고 있다. 그러나, 이는 알킬알콕시실란의 함량이 너무 높아 경제적이지 못할 뿐만 아니라 표면 발수력이 발생하여 다른 피착 재료의 부착 시 접착력이 나빠지는 문제점이 있다. 또한 알킬알콕시실란의 농도가 70% 이하일 경우 물의 농도가 상대적으로 증가하여 장기 보존 시 층 분리가 발생하여 성능이 저하되는 문제점이 있다. For example, Korean Patent No. 227922 discloses an emulsion in which the alkylalkoxysilane has a particle size of 2-10 μm and a concentration of 5-70% by weight. However, it is not economical because the content of the alkylalkoxysilane is too high, there is a problem in that the surface water repellency is generated, the adhesion is worse when the adhesion of the other adherend material. In addition, when the concentration of the alkylalkoxysilane is 70% or less, the concentration of water is relatively increased, resulting in a problem of deterioration in performance due to layer separation during long-term storage.
또한, 대한민국 공개특허 제 2001-93323 호는 유기 용제를 포함하는 알킬알콕시실란계 발수제를 개시하고 있으며 실란의 일부를 유기 용제로 대체함으로써 가격이 비교적 싸고 다른 피착 재료의 접착력을 향상시켰으나, 비교적 큰 수압이 작용하는 부위, 예컨대, 지하 구조물 또는 수로 박스 등에서는 수압을 작용시키는 투수에 대한 저항성이 적어 그 사용이 제한되며 별도의 방수 처리가 필요하다는 단점이 있다.In addition, Korean Patent Laid-Open Publication No. 2001-93323 discloses an alkylalkoxysilane-based water repellent comprising an organic solvent, and by replacing a part of the silane with an organic solvent, it is relatively inexpensive and improves the adhesion of other adherent materials, but relatively large hydraulic pressure. This action site, for example, underground structures or waterway boxes have a low resistance to water permeability to act on the water pressure is limited in its use and has a disadvantage in that a separate waterproof treatment is required.
따라서, 경제적이면서도 내구성 및 다른 피착 재료의 접착력이 저하되지 않으며, 발수 및 방수 능력을 겸비하여 큰 수압이 작용하는 부위에서도 사용 가능한 침투성 방수제의 개발이 절실히 요구되고 있다. Therefore, there is an urgent need to develop a permeable waterproofing agent which is economical and does not degrade durability and adhesion of other adherent materials, and has a water repellency and waterproofing ability and can be used even at a site where a large water pressure is applied.
본 명세서에 인용된 특허 문헌의 개시 내용은 그 전체로서 본 명세서에 참조로 삽입되어 본 발명이 속하는 기술 분야의 수준 및 본 발명의 내용이 보다 명확하게 설명된다.The disclosure of the patent documents cited herein is incorporated by reference herein in its entirety, and the level of the technical field to which the present invention belongs and the contents of the present invention are more clearly described.
본 발명자들은 경제적이면서도 내구성 및 다른 피착 재료의 접착력이 저하되지 않으며, 큰 수압이 작용하는 부위에서도 사용 가능한 침투성 방수제를 개발하기 위하여 예의 연구 노력한 결과, 실란의 일부를 유기 용제로 대체하여 실란의 함량을 낮추고 여기에 고분자 화합물을 첨가하여 제조된 에멀션 크림이 표면 발수력이 발생되지 않고 투수 저항성이 현저히 개선됨을 확인함으로써, 본 발명을 완성하였다.The present inventors have diligently researched to develop a permeable waterproofing agent that is economical, durable and does not degrade the adhesion of other adherent materials, and can be used even at a site where a large hydraulic pressure is applied. As a result, by replacing a part of the silane with an organic solvent, The present invention was completed by confirming that the emulsion cream prepared by lowering and adding a polymer compound therein did not generate surface water repellency and significantly improved water permeability.
따라서, 본 발명의 목적은 투수 저항성이 개선되어 방수성이 증진된 알킬알콕시실란 에멀션 크림을 제공하는 것이다.Accordingly, it is an object of the present invention to provide an alkylalkoxysilane emulsion cream having improved water permeability and enhanced water resistance.
본 발명의 다른 목적은 침투성 방수제를 제공하는 것이다. Another object of the present invention is to provide a permeable waterproofing agent.
본 발명의 다른 목적 및 이점은 하기의 실시예 및 청구범위에 의해 명확하게 된다.Other objects and advantages of the invention will be apparent from the following examples and claims.
본 발명의 일 양태에 따르면, 본 발명은 알킬알콕시실란, 고분자 화합물, 유기 용제 및 에멀션화제를 포함하는 방수성이 증진된 에멀션 크림을 제공한다.According to one aspect of the present invention, the present invention provides an emulsion cream having improved water resistance including an alkylalkoxysilane, a high molecular compound, an organic solvent, and an emulsifier.
본 명세서에 사용된 용어 "에멀션 크림"은 물에 혼화성이 없는 오일상으로 이루어진 에멀션계의 페이스트 (paste) 상 물 함유 조성물을 의미하며, "알킬알콕시실란 에멀션 크림"은 유효 성분으로서 알킬알콕시실란을 포함하는 에멀션 크림을 의미한다.As used herein, the term "emulsion cream" means an emulsion-based water-containing composition consisting of an oil phase which is incompatible with water, and "alkylalkoxysilane emulsion cream" refers to an alkylalkoxysilane as an active ingredient. It means an emulsion cream comprising a.
본 명세서에 사용된 용어 "발수성"이란 고체의 표면 장력에 의한 물의 흡수를 막을 수 있도록 고체의 표면을 소수성으로 전환하여 물을 배척해 내는 특성을 의미하며, "발수제"란 이러한 특성을 갖는 물질을 의미한다. As used herein, the term "water repellent" refers to a property of discharging water by converting the surface of the solid into hydrophobic so as to prevent the absorption of water by the surface tension of the solid, and "water repellent" refers to a material having such a property. it means.
소수성은 고체와 물이 이루는 각도인 접촉각이 90°보다 큰 경우를 말하며, 침투에 의한 발수의 원리는 구조물의 내구성을 향상시키므로 널리 사용되고 있다. 그러나, 이러한 고체의 표면 젖음 거동의 변화 현상에 의한 물의 침입 방어 체계는 강한 수압의 작용이 있을 경우 이러한 소수성만으로는 물의 배척력이 부족하여 물은 모세관을 통하여 침투되게 된다. 따라서, 0.3 ㎏f/㎠ 이상의 큰 수압에서는 발수력만으로는 물의 흡수를 차단하기가 어렵기 때문에, 별도의 방수 처리가 필요하다.Hydrophobicity refers to the case where the contact angle, which is the angle between the solid and the water, is greater than 90 °, and the principle of water repellency by penetration is widely used because it improves the durability of the structure. However, the water intrusion defense system due to the change of the surface wetting behavior of the solid, when there is a strong hydraulic pressure action, such hydrophobicity alone lacks the water repelling force and the water penetrates through the capillary tube. Therefore, at a large water pressure of 0.3 kgf / cm 2 or more, it is difficult to block the absorption of water only by the water repellency, so that a separate waterproofing treatment is required.
본 명세서에서 사용된 용어 "방수성"은 콘크리트와 같은 무기질 구조물 내의 모세관을 완전히 막아 물의 흡수가 완전히 차단되는 것을 의미하며, 투수비가 특정 비율 이하이면 발수제와 구분하여 "방수제"라 한다. 투수비는 0.3 ㎏f/㎠의 압력으로 물을 투과시켰을 경우 재료의 무게 증가량을 발수제 또는 방수제를 사용하지 않았을 경우와 상대적으로 비교한 값이다. 예컨대, 모르타르 방수제의 경우, 방수제가 사용되지 않을 때와 비교하여 투수비가 60% 이하인 것으로 규정하고 있다 (한국주택공사).As used herein, the term "waterproof" means completely blocking the capillary in an inorganic structure such as concrete to completely block the absorption of water, and when the water permeability ratio is less than a certain ratio, it is referred to as "waterproof". Permeability ratio is a value comparing the weight increase of the material when water permeated at a pressure of 0.3 kgf / cm 2 compared with the case where no water repellent or waterproof agent is used. For example, the mortar waterproofing agent has a permeability ratio of 60% or less compared to when no waterproofing agent is used (Korea Housing Corporation).
또한, "침투성 방수제"는 콘크리트 등의 무기질 구조물에 도포 시 침투된 후 모세관을 완전히 막아 물의 흡수를 차단하게 된다.In addition, the "permeable waterproofing agent" is to penetrate during application to inorganic structures such as concrete to completely block the capillary tube to block the absorption of water.
본 발명자들은 알킬알콕시실란에 고분자 화합물을 첨가할 경우 투수비가 현저하게 감소하여 발수성 뿐만 아니라 우수한 방수성을 나타냄을 발견하였다. The present inventors have found that the addition of a high molecular compound to the alkylalkoxysilane significantly reduces the water permeability ratio, thereby exhibiting excellent water repellency as well as water resistance.
본 발명의 에멀션 크림에 유효 성분으로 포함되는 알킬알콕시실란은 콘크리트 등에 결합할 수 있고 가교될 수 있는 3 관능기를 가지며, 콘크리트 중에 흡수된 후 수분과 반응하여 실란올 중간체를 거쳐 가교되어 실리콘 고분자를 형성하게 되고, 상기 알킬기는 수분의 흡수를 방지하는 소수체를 구성하게 된다 (Michael Roth, Siliconates-silicon resin-silane-siloxanes, 1982).The alkylalkoxysilane included as an active ingredient in the emulsion cream of the present invention has a trifunctional group capable of binding to and crosslinking in concrete, etc., absorbed in concrete and reacted with moisture to be crosslinked through silanol intermediates to form a silicone polymer. The alkyl group constitutes a hydrophobic to prevent the absorption of moisture (Michael Roth, Siliconates-silicon resin-silane-siloxanes , 1982).
본 발명의 바람직한 구현예에 따르면, 본 발명의 알킬알콕시실란의 함량은 10-70 중량%이며, 보다 바람직하게는 20-50 중량%이다. 상기 알킬알콕시실란의 함량이 10 중량% 미만인 경우는 침투성 및 발수성이 저하되는 문제점이 있고, 70 중량% 이상일 경우는 에멀션 상의 입자 크기가 증가하여 장기 보관시 보관 안정성이 저하되는 문제점이 있다.According to a preferred embodiment of the present invention, the content of the alkylalkoxysilane of the present invention is 10-70% by weight, more preferably 20-50% by weight. When the content of the alkylalkoxysilane is less than 10% by weight, there is a problem that the permeability and water repellency are lowered. When the content of the alkylalkoxysilane is 70% by weight or more, the particle size of the emulsion is increased so that the storage stability is lowered during long-term storage.
본 발명의 바람직한 구현예에 따르면, 본 발명의 에멀션 크림에 포함되는 알킬알콕시실란은 2-12 개의 탄소 원자를 갖는 알킬기 및 2-4 개의 탄소 원자를 갖는 알콕시기를 갖는다. 상기 알킬기의 크기가 작을 경우는 발수력이 작으며 너무 클 경우는 침투성이 저하된다. 또한, 알콕시기의 탄소의 수가 1개의 경우에는 침투 이전에 반응하기 쉬워 침투성이 저하되는 문제점이 있으므로 적어도 2개 이상으로 구성되어야 한다.According to a preferred embodiment of the present invention, the alkylalkoxysilane included in the emulsion cream of the present invention has an alkyl group having 2-12 carbon atoms and an alkoxy group having 2-4 carbon atoms. When the size of the alkyl group is small, the water repellency is small, and when too large, the permeability is lowered. In addition, when the number of carbons in the alkoxy group is one, it is easy to react before permeation, so that the permeability is lowered.
바람직하게는, 상기 알킬기는 메틸, 에틸, n-프로필, 이소프로필, n-부틸, n-펜틸, 이소펜틸, 네오펜틸, t-펜틸, n-헥실, n-헵틸, n-옥틸, 이소옥틸, n-노닐, n-데실, n-도데실, 시클로펜틸, 시클로헥실, 4-에틸시클로헥실, 시클로헵틸 또는 메틸시클로헥실 기 등이며, 할로겐 등으로 치환된 알킬기도 사용될 수 있다.Preferably, the alkyl group is methyl, ethyl, n-propyl, isopropyl, n-butyl, n-pentyl, isopentyl, neopentyl, t-pentyl, n-hexyl, n-heptyl, n-octyl, isooctyl , n-nonyl, n-decyl, n-dodecyl, cyclopentyl, cyclohexyl, 4-ethylcyclohexyl, cycloheptyl or methylcyclohexyl group, and the like. An alkyl group substituted with halogen or the like can also be used.
바람직하게는, 상기 알콕시기는 에톡시, n-프로폭시, 이소프로폭시, n-부톡시, 이소부톡시, s-부톡시, t-부톡시, n-펜틸옥시 및 n-헥실옥시 기 등이다.Preferably, the alkoxy group is an ethoxy, n-propoxy, isopropoxy, n-butoxy, isobutoxy, s-butoxy, t-butoxy, n-pentyloxy, n-hexyloxy group, or the like. .
본 발명의 가장 바람직한 구현예에 따르면, 상기 알킬알콕시실란은 n-옥틸에톡시실란이다.According to the most preferred embodiment of the present invention, the alkylalkoxysilane is n-octylethoxysilane.
또한, 본 발명의 에멀션 크림에 유효 성분으로 포함되는 고분자 화합물은 알킬알콕시실란의 표면 발수력으로 인한 부착력 저하 정도를 감소시켜 표면 부착력 및 표면 보호능을 개선시킨다. 또한, 큰 수압이 작용하는 부위에 사용되어 무기질 재료의 표면 및 모세관의 입구에 결합하여 모세관을 막음으로써 방수성을 부여한다. 고분자 화합물은 상기 알킬알콕시실란과 반응하지 않아야 하고 실란 또는 유기 용제와의 혼합 시 어떠한 영향도 주지 않고 용해되어 있어야 하며 콘크리트 등에 적용하였을 경우 반응에 의하여 결합되어 이탈되지 않아야 한다. In addition, the polymer compound included as an active ingredient in the emulsion cream of the present invention improves the surface adhesion and surface protection by reducing the degree of adhesion decrease due to the surface water repellency of the alkylalkoxysilane. In addition, it is used at the site where a large hydraulic pressure acts to bind to the surface of the inorganic material and the inlet of the capillary tube to impart waterproofness by blocking the capillary tube. The high molecular compound should not react with the alkylalkoxy silane and should be dissolved without any influence upon mixing with the silane or the organic solvent, and should not be separated by the reaction when applied to concrete.
본 발명의 바람직한 구현예에 따르면, 상기 고분자 화합물의 함량은 1-80 중량%이며, 보다 바람직하게는 3-50 중량%이다. 상기 고분자 화합물의 함량이 1 중량% 이하인 경우는 모세관을 충분히 막지 못하여 수압이 작용될 경우 방어하지 못하는 문제점이 있고, 80 중량% 이상인 경우는 알킬알콕시실란의 침투력에 나쁜 영향을 주는 문제점이 있다.According to a preferred embodiment of the present invention, the content of the polymer compound is 1-80% by weight, more preferably 3-50% by weight. When the content of the polymer compound is 1% by weight or less, there is a problem in that it does not sufficiently block the capillary tube and thus does not defend when water pressure is applied. In the case where the content of the polymer compound is 80% by weight or more, there is a problem that adversely affects the penetration of the alkylalkoxysilane.
본 발명의 바람직한 구현예에 따르면, 상기 고분자 화합물의 분자량은 1,000-2,000,000이며, 보다 바람직하게는 3,000-1,000,000이다. 상기 고분자 화합물의 분자량이 1,000 미만이거나 2,000,000을 초과할 경우는 알킬알콕시실란이 무기질 재료로 침투하는 데 방해가 되거나 콘크리트 모세관의 기공을 막을 수 없다는 문제점이 있으며 특히 분자량이 너무큰 경우 기공의 충진을 할 수 없어 표면 손상시 방수성이 나빠질 수 있다. 바람직하게는 상기 고분자 화합물은 아크릴, 메타아크릴, 클로로프렌, 에틸렌옥사이드 부가물, 아크릴 공중합체, 폴리프로필렌 부가물 또는 이들의 조합의 벌크 또는 용액 중합된 고분자물이다. 또한 고분자 화합물 대신 실리카 졸 등의 반응성 물질로 모세관을 충진하여 수압의 작용에 저항할 수 있도록 할 수도 있다. According to a preferred embodiment of the present invention, the molecular weight of the polymer compound is 1,000-2,000,000, more preferably 3,000-1,000,000. If the molecular weight of the high molecular compound is less than 1,000 or more than 2,000,000, there is a problem that the alkylalkoxysilane can prevent the penetration of the inorganic material or prevent the pores of the concrete capillary. Especially, if the molecular weight is too large, the pores may be filled. If the surface is damaged, the waterproofness may be deteriorated. Preferably the polymer compound is a bulk or solution polymerized polymer of acrylic, methacrylic, chloroprene, ethylene oxide adduct, acrylic copolymer, polypropylene adduct or combinations thereof. In addition, the capillary may be filled with a reactive material such as silica sol instead of a high molecular compound so as to resist the action of hydraulic pressure.
본 발명의 가장 바람직한 구현예에 따르면, 상기 고분자 화합물은 폴리아크릴레이트이다.According to the most preferred embodiment of the present invention, the high molecular compound is polyacrylate.
또한, 본 발명의 에멀션 크림에 유효 성분으로 포함되는 유기 용제는 알킬알콕시실란의 표면 발수력으로 인한 부착력 저하 정도를 감소시키며, 알킬알콕시실란의 함량을 감소시킴으로써 경제적인 효과를 얻을 수 있다. In addition, the organic solvent included as an active ingredient in the emulsion cream of the present invention reduces the degree of adhesion deterioration due to the surface water repellency of the alkyl alkoxysilane, and economic effects can be obtained by reducing the content of the alkyl alkoxysilane.
본 발명의 바람직한 구현예에 따르면, 상기 유기 용제의 함량은 1-80 중량%이며, 보다 바람직하게는 20-70 중량%이다. 상기 유기 용제는 인체에 유해성이 적으며 고분자의 용해성이 우수한 것이 바람직하다. 또한, 바람직하게는 상기 유기 용제의 끓는점은 80-220℃이며, 보다 바람직하게는 90-150℃이다. 상기 유기 용제의 끓는점이 80℃ 미만일 경우에는 알킬알콕시실란이 쉽게 증발되므로 침투성이 저하되는 문제점이 있으며, 220℃를 초과할 경우에는 상기 고분자 화합물의 사슬에 잔존하여 가소제 역할을 함으로써 고분자 화합물의 약화가 유발되어 콘크리트 표면에서부터 박리되는 문제점이 있다.According to a preferred embodiment of the present invention, the content of the organic solvent is 1-80% by weight, more preferably 20-70% by weight. The organic solvent is preferably less harmful to the human body and excellent in solubility of the polymer. In addition, the boiling point of the organic solvent is preferably 80-220 ° C, more preferably 90-150 ° C. If the boiling point of the organic solvent is less than 80 ℃ alkyl alkoxysilane is easily evaporated, there is a problem that the permeability is lowered. If it exceeds 220 ℃, the weakening of the polymer compound by remaining in the chain of the polymer compound to act as a plasticizer There is a problem caused by peeling from the concrete surface.
본 발명의 바람직한 구현예에 의하면, 상기 유기 용제는 6-12 개의 탄소 원자를 갖는 지방족 및 방향족 탄화수소이며, 보다 바람직하게는 알켄, 크실렌, 톨루엔, 트리메틸벤젠 또는 테트라메틸벤젠 등이고, 가장 바람직하게는 크실렌이다.According to a preferred embodiment of the present invention, the organic solvent is an aliphatic and aromatic hydrocarbon having 6-12 carbon atoms, more preferably alkene, xylene, toluene, trimethylbenzene or tetramethylbenzene, and most preferably xylene to be.
본 발명의 바람직한 구현예에 따르면, 본 발명의 에멀션 크림에 유효 성분으로 포함되는 에멀션화제의 함량은 1-20 중량%이며, 보다 바람직하게는 2-5 중량%이다. 상기 에멀션화제의 함량이 1 중량% 미만일 경우에는 충분한 에멀션화가 이루어지지 않는 문제점이 있고, 20 중량%를 초과할 경우에는 알킬알콕시실란의 발수력이 감소하여 장기간의 침수 시 발수력을 기대할 수 없을 뿐만 아니라 고분자 화합물의 내수성에 악영향을 미치는 문제점이 있다.According to a preferred embodiment of the present invention, the amount of the emulsifier included as an active ingredient in the emulsion cream of the present invention is 1-20% by weight, more preferably 2-5% by weight. If the amount of the emulsifier is less than 1% by weight, there is a problem in that sufficient emulsification is not achieved. If the amount of the emulsifier is greater than 20% by weight, the water repellency of the alkylalkoxysilane decreases, so that water repellency cannot be expected during prolonged immersion. But there is a problem that adversely affects the water resistance of the polymer compound.
본 발명의 바람직한 구현예에 따르면, 상기 에멀션화제는 음이온성 에멀션화제, 비이온성 에멀션화제, 양이온성 에멀션화제, 양쪽성 에멀션화제 또는 이들의 조합으로부터 최소 1 종 이상 선택된다. 보다 바람직하게는 상기 에멀션화제는 비이온성 에멀션화제이며, 보다 더 바람직하게는 폴리옥시에틸렌 알킬에테르, 가장 바람직하게는 폴리옥시에틸렌노닐페닐에테르이다. According to a preferred embodiment of the present invention, the emulsifier is selected from at least one of an anionic emulsifier, a nonionic emulsifier, a cationic emulsifier, an amphoteric emulsifier or a combination thereof. More preferably the emulsifier is a nonionic emulsifier, even more preferably polyoxyethylene alkyl ether, most preferably polyoxyethylene nonylphenyl ether.
본 발명의 다른 양태에 따르면, 본 발명은 상기 알킬알콕시시란 에멀션 크림을 유효 성분으로 포함하는 침투성 방수제를 제공한다.According to another aspect of the present invention, the present invention provides a permeable waterproofing agent comprising the alkylalkoxysilane emulsion cream as an active ingredient.
본 발명의 바람직한 구현예에 따르면, 본 발명의 침투성 방수제에 포함되는 에멀션 크림은 알킬알콕시실란 10-70 중량%, 고분자 화합물 1-80 중량%, 유기 용제 1-80 중량% 및 에멀션화제는 1-20 중량%를 포함하는 혼합물을 1500 rpm 이상의 고속 교반기에서 교반하여 완전히 크림상이 되었을 때 에멀션화를 종결하여 제조된다. 상기 에멀션 크림은 입자 크기 2-20 ㎛ 이하 및 점도 1000 cps 이상을 갖는다. 본 발명의 에멀전 크림을 포함하는 침투성 방수제를 콘크리트 등의 무기질 재료의 구조물에 도포할 경우 응집에 의하여 투명하게 변화하면서 알킬알콕시실란이 서서히 재료의 모세관으로 침투된 후 탈수 반응을 거쳐 모세관 내에서 실리콘 중합체로 전환하게 되어 모세관 표면을 발수성으로 변화하게 한다. 또한, 고분자 화합물은 표면과 모세관의 입구에 결합하여 모세관으로의 물의 침입을 막는 우수한 방수성을 나타낸다. 그러나 제조 시 교반 속도가 낮아 완전한 크림상이 되지 않을 경우는 알킬알콕시실란이 쉽게 가수분해되어 층의 분리가 발생하여 성능이 저하되고 벽체 등에 사용 시 흘러내리게 되는 문제점이 있다. 또한, 알킬알콕시실란이 고분자 화합물과 결합하며 상기 고분자 화합물은 반응에 의하여 불용성 고분자로 석출되게 된다. 따라서, 완전한 크림상으로 제조하는 것이 바람직하다.According to a preferred embodiment of the present invention, the emulsion cream included in the permeable waterproofing agent of the present invention is 10-70% by weight of alkylalkoxysilane, 1-80% by weight of the high molecular compound, 1-80% by weight of the organic solvent, and 1-% of the emulsifier. The mixture comprising 20% by weight is prepared by stirring in a high speed stirrer of at least 1500 rpm to complete the emulsification when it is completely creamy. The emulsion cream has a particle size of 2-20 μm or less and a viscosity of at least 1000 cps. When the permeable waterproofing agent including the emulsion cream of the present invention is applied to a structure made of inorganic material such as concrete, the alkylalkoxysilane gradually penetrates into the capillary of the material while being transparently changed by agglomeration, and then depolymerized into the silicone polymer in the capillary Conversion of the capillary surface to water repellency. In addition, the polymer compound binds to the surface and the inlet of the capillary tube and exhibits excellent waterproofing property to prevent ingress of water into the capillary tube. However, when the stirring speed is low during manufacture, the alkyl alkoxysilane is easily hydrolyzed to separate the layers, resulting in deterioration of performance and deterioration in performance when used in walls and the like. In addition, the alkylalkoxysilane is combined with the polymer compound, and the polymer compound is precipitated as an insoluble polymer by the reaction. Therefore, it is desirable to prepare a complete cream.
이때 유입되는 공기가 많아 기포가 많이 존재할 경우 보존 안정성이 저하될 수 있으므로 실리콘계 또는 지방산계의 소포제를 사용하여 기포 발생을 억제하는 것이 바람직하다. 장기 보관을 위하여 혼합액에 방부제를 첨가할 수도 있다. 그러나, 6개월 정도의 보관을 위하여는 크게 필요치 않은데, 이는 소량의 알킬알콕시실란이 물과 반응하여 형성된 알코올에 의하여 세균의 번식이 억제되기 때문인 것으로 추정된다. At this time, if there are a lot of air bubbles are present, the storage stability may be reduced, so it is preferable to suppress the generation of bubbles by using a silicone- or fatty acid-based antifoaming agent. Preservatives may be added to the mixture for long term storage. However, it is not very necessary for 6 months of storage because it is assumed that the propagation of bacteria is suppressed by the alcohol formed by the reaction of a small amount of alkylalkoxysilane with water.
알킬알콕시실란 및 유기 용제를 크림상으로 에멀션화한 후, 고분자 및 유기 용제를 에멀션화제가 포함된 물에 별도로 크림상으로 제조하여 두 종류의 크림을 입자가 손상되지 않는 범위의 교반 속도에서 혼합하여 사용하여도 성능은 동일하다. After emulsifying the alkylalkoxysilane and the organic solvent into the cream phase, the polymer and the organic solvent are separately prepared in the cream phase in water containing the emulsifier, and the two kinds of creams are mixed at a stirring speed in a range where the particles are not damaged. Even when used, the performance is the same.
본 발명의 에멀션 크림을 포함하는 침투성 방수제를 콘크리트 등의 무기질 구조물에 적용하였을 경우 침투된 정도는 구조물의 일부분을 절단하여 침수시키면 물에 적셔지지 않은 발수 부분을 뚜렷이 구분할 수 있다. 또한, 3 ㎏f/㎠의 수압 작용 시 투수비가 현저하게 감소하여 지하 구조물의 벽체 및 바닥의 방수에 적합하다. 또한 발수 분분이 20년 이상의 내구성을 갖게 되며 별도의 방수 마감이 필요 없고 도색 등의 일반적인 마감만으로 완전하게 방수 효과를 볼 수 있다. When the permeable waterproofing agent including the emulsion cream of the present invention is applied to an inorganic structure such as concrete, the degree of permeation can be clearly distinguished from the water-repellent part not wetted by water by cutting a part of the structure. In addition, when the hydraulic action of 3 kgf / ㎠ remarkably reduced the permeability ratio is suitable for waterproofing walls and floors of underground structures. In addition, the water-repellent powder has a durability of more than 20 years, and does not require a separate waterproof finish, and can be completely waterproof by only a general finish such as painting.
이하, 실시예를 통하여 본 발명을 더욱 상세히 설명하고자 한다. 이들 실시예는 오로지 본 발명을 보다 구체적으로 설명하기 위한 것으로서, 본 발명의 요지에 따라 본 발명의 범위가 이들 실시예에 의해 제한되지 않는다는 것은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 있어서 자명할 것이다.Hereinafter, the present invention will be described in more detail with reference to Examples. These examples are only for illustrating the present invention in more detail, and the scope of the present invention is not limited by these examples in accordance with the gist of the present invention to those skilled in the art. Will be self-evident.
실시예Example
실시예 1: 실리카 졸을 포함하는 알킬알콕시실란 에멀션 크림 제조 및 성능 시험 Example 1 Preparation and Performance Test of Alkylalkoxysilane Emulsion Cream Including Silica Sol
하기 표 1과 같은 함량으로 조성된 알킬알콕시실란, 유기 용제, 실리카 졸 및 에멀션화제 혼합물인 용액 1을 용액 2에 서서히 떨어뜨리면서 약 1500 rpm으로 고속 교반하여 알킬알콕시실란 에멀션 크림을 제조하고, 콘크리트에서의 성능 (침투성, 투수 저항성 및 부착력)을 시험하였다. 그 결과는 하기 표 2에 나타나 있다.To prepare a alkyl alkoxysilane emulsion cream by rapidly stirring at about 1500 rpm while slowly dropping the solution 1, a mixture of alkyl alkoxysilane, organic solvent, silica sol and emulsifier in the content as shown in Table 1 to Solution 2, The performance (permeability, permeability resistance and adhesion) was tested. The results are shown in Table 2 below.
상기한 조성으로 제조된 에멀션 크림의 콘크리트에서의 성능 (침투 깊이, 투수비, 흡수비, 접착강도 및 내구성)을 다음의 방법으로 검사하고 그 결과를 하기 표 2에 나타내었다. The performance (infiltration depth, permeability ratio, absorption ratio, adhesive strength and durability) in concrete of the emulsion cream prepared with the above composition was examined by the following method and the results are shown in Table 2 below.
1. 침투 깊이 측정1. Penetration depth measurement
시멘트 340 ㎏, 모래 768 ㎏, 자갈 941 ㎏ 및 물 173 ㎏을 단위 부피로 하여 콘크리트를 제조하여 지름10 ㎝ x 높이 10 ㎝의 원형 실린더 몰드를 만들고 이것을 14일 동안 항온항습기에서 보존한 후 온도 50℃ , 상대습도 50%의 조건으로 14일 동안 건조시켰다. 여기에 방수제 시료 150 ㏄/㎡를 도포하고 동일 조건에서 14일 동안 보존한 후 중심부를 파괴하였다. 파괴면을 물에 담그면 쉽게 젖는 부위와 젖지 않는 부위로 뚜렷하게 구별할 수 있으며 이를 버어니어 켈리퍼스로 0.1 ㎜ 단위까지 읽었다.Concrete was prepared using a unit volume of 340 kg of cement, 768 kg of sand, 941 kg of gravel, and 173 kg of water to make a circular cylinder mold 10 cm in diameter and 10 cm in height. , And dried for 14 days at 50% relative humidity. The waterproof agent sample 150 ㏄ / ㎡ was applied to it and stored for 14 days under the same conditions, and then the center was destroyed. When the fracture surface is immersed in water, it can be clearly distinguished into the wet and non-wet areas, which are read up to 0.1 mm by vernier calipers.
2. 투수비 및 흡수비 측정2. Permeability ratio and absorption ratio measurement
투수비 및 흡수비는 "KS F 2451 건축용 시멘트 방수제 시험 방법"을 이용하여 측정하였다. 투수비 및 흡수비의 계산식은 하기 수학식 1 및 2와 같다.Permeability ratio and absorption ratio were measured using "KS F 2451 Building Cement Waterproofing Test Method". The formula of permeability ratio and absorption ratio is shown in the following formulas (1) and (2).
상기 투수비는 방수성에 대한 지표로서 그 수치가 작을수록 방수성이 우수한 것으로 볼 수 있으며, 상기 흡수비는 발수성에 대한 지표로서 그 수치가 작을수록 발수성이 우수한 것으로 볼 수 있다.The water permeability ratio is an indicator for waterproofness, and the smaller the value, the better the waterproofness. The water absorption ratio is an index for the water repellency, the smaller the number may be regarded as excellent water repellency.
3. 압축전단 접착강도 측정3. Compression shear adhesion strength measurement
압축전단 접착강도는 "ASTM C 882" 및 "콘크리트에 대한 에폭시-수지 시스템의 접착 강도 측정 방법 (Test method for bond strength of epoxy-resin systems for concrete, American Society for Testing and Materials)"에 의하여 실시하였다. 압축전단 접착강도의 계산식은 하기 수학식 3과 같다.Compressive shear strength was tested by "ASTM C 882" and "Test method for bond strength of epoxy-resin systems for concrete, American Society for Testing and Materials ". . The formula for compressive shear adhesion strength is as shown in Equation 3 below.
상기 표 2에 나타난 바와 같이, 상기 에멀션 크림은 우수한 침투성, 투수 저항성, 흡수 차단성 및 부착력을 나타냄을 알 수 있다.As shown in Table 2, it can be seen that the emulsion cream exhibits excellent permeability, permeability resistance, absorption barrier property and adhesion.
4. 내구성 시험4. Durability Test
상기 에멀션 크림의 내구성을 시험하기 위하여, 콘크리트의 표면을 철 브러쉬를 이용하여 30회 문질러 코팅된 표면을 제거한 후 상기 에멀션 크림을 적용하고 투수비 및 흡수비를 측정하여, 상기 표 2의 결과와 비교하였다. 그 결과는 하기 표 3에 나타나 있다.In order to test the durability of the emulsion cream, the surface of the concrete was rubbed 30 times with an iron brush to remove the coated surface, and then the emulsion cream was applied and the permeability ratio and the absorption ratio were measured and compared with the results of Table 2 above. It was. The results are shown in Table 3 below.
상기 표 3에 나타난 바와 같이, 상기 에멀션 크림의 투수비 및 흡수비는 콘크리트의 코팅된 표면을 제거하기 전과 제거한 후가 비슷하게 측정되었다. 코팅된 표면의 제거는 구조물의 사용에 따른 마모를 의미하므로, 상기 에멀션 크림은 시간의 경과 또는 구조물의 사용에 의한 마모에 대해서도 우수한 내구성을 나타냄을 알 수 있다.As shown in Table 3, the permeability ratio and the absorption ratio of the emulsion cream were similarly measured before and after removing the coated surface of the concrete. Since the removal of the coated surface means abrasion with the use of the structure, it can be seen that the emulsion cream exhibits excellent durability against wear over time or the use of the structure.
실시예 2: 고분자 화합물을 포함하는 알킬알콕시실란 에멀션 크림의 제조 및 성능 시험Example 2: Preparation and Performance Test of Alkylalkoxysilane Emulsion Creams Containing High Molecular Compounds
실리카 졸 대신 폴리아크릴레이트를 사용한 것을 제외하고는 상기 실시예 1과 동일한 방법으로 에멀션 크림을 제조하고, 하기 표 4과 같은 조성으로 상기 폴리아크릴레이트, 알킬알콕시실란 및 유기 용제의 함량을 변화시켜 상기 실시예 1과 동일한 방법으로 각 에멀션 크림의 성능을 시험하였다. 이때 사용된 폴리아크릴레이트는 중량 평균 분자량이 8000 g/mole이다. 그 결과는 하기 표 4에 나타나 있다. Except for using a polyacrylate instead of a silica sol to prepare an emulsion cream in the same manner as in Example 1, by changing the content of the polyacrylate, alkyl alkoxysilane and organic solvent in the composition shown in Table 4 The performance of each emulsion cream was tested in the same manner as in Example 1. The polyacrylate used at this time has a weight average molecular weight of 8000 g / mole. The results are shown in Table 4 below.
상기 표 4에 나타난 바와 같이, 폴리아크릴레이트를 사용하였을 경우에도 실리카 졸을 사용하였을 때와 마찬가지로 침투성 및 투수 저항성 등의 성능이 동일하게 유지되었다. 특히, 폴리아크릴레이트를 사용하였을 경우에는 이를 전혀 사용하지 않은 경우보다 투수비가 현저히 감소하였다. 이것은 분자 화합물에 의해 모세관의 미세 공극의 충진이 이루어졌기 때문인 것으로 판단된다. 또한, 폴리아크릴레이트를 4.88% 이상 사용할 경우는 투수비가 더 이상 크게 감소하지 않았다. 따라서, 본 발명의 에멀션 크림은 우수한 투수 저항성을 가짐을 알 수 있다. 또한, 상기 에멀션 크림들을 콘크리트에 처리하고 표면에 모르타르를 부착시켰을 경우 아무 것도 처리하지 않은 것과 비교하여 압축전단 접착강도가 증가되었다. 한편, 고분자 화합물의 함량이 25%인 경우에는 부착력 및 투수성의 성능에는 변화가 없으나 처리된 표면이 어두워졌으므로 고분자 막이 형성된 것으로 판단된다. 또한 표면 제거 전, 후의 성능 시험 결과, 역시 실리카 졸을 이용하였을 때와 동일한 결과를 얻었다. 따라서, 본 발명의 에멀션 크림은 알킬알콕시실란의 표면 발수력을 감소시켜 피착 재료에 대한 우수한 부착력을 가짐을 알 수 있으며 표면 손상 후에도 방수성이 유지되고 있음을 알 수 있다.As shown in Table 4, even when polyacrylate was used, the performances such as permeability and water resistance were maintained the same as when silica sol was used. In particular, the use of polyacrylate significantly reduced the permeability ratio than when not used at all. This is believed to be due to the filling of the micropores of the capillary with the molecular compound. In addition, when using more than 4.88% polyacrylate, the permeability ratio did not decrease significantly any more. Therefore, it can be seen that the emulsion cream of the present invention has excellent permeability resistance. In addition, when the emulsion creams were treated with concrete and mortar was attached to the surface, the compressive shear adhesive strength was increased compared with that without any treatment. On the other hand, when the content of the polymer compound is 25%, there is no change in the performance of adhesion and water permeability, but the treated surface is darkened, so it is determined that the polymer film is formed. In addition, as a result of the performance test before and after surface removal, the same result as when using a silica sol was obtained. Therefore, it can be seen that the emulsion cream of the present invention has excellent adhesion to the adherend material by reducing the surface water repellency of the alkylalkoxysilane, and it can be seen that the waterproofness is maintained even after the surface damage.
실시예 3: 고분자 화합물만을 포함하는 에멀션 크림의 성능 시험 Example 3: Performance Test of Emulsion Cream Containing Only High Polymer Compound
하기 표 5의 조성으로 알킬알콕시실란이 포함되고 고분자 화합물이 전혀 포함되지 않은 에멀션 크림 (A)과, 하기 표 6의 조성으로 고분자 화합물이 포함되고 알킬알콕시실란이 전혀 포함되지 않은 에멀션 크림 (B)을 제조한 후 6 rpm의 속도로 교반하여 성능을 비교하였다. 그 결과는 하기 표 7에 나타나 있다.Emulsion cream (A) containing an alkylalkoxysilane in the composition of Table 5 and no polymer compound at all, and emulsion cream (B) containing a high molecular compound and no alkylalkoxysilane in the composition of Table 6 below After the preparation was stirred at a speed of 6 rpm to compare the performance. The results are shown in Table 7 below.
상기 표 7에 나타난 바와 같이, 고분자 화합물 만을 에멀션 크림화 하였을 경우 투수비 및 흡수비는 모두 만족할 만큼 확보되었으나, 침투성이 확보되지 않았다. 한편, 알킬알콕시실란 만을 크림화하였을 경우에는 투수비가 현저히 증가하여 투수 저항성이 개선되지 않았다. As shown in Table 7, when only the polymer compound was emulsion creamed, the permeability ratio and the absorption ratio were both satisfied enough, but permeability was not secured. On the other hand, when only the alkyl alkoxysilane was creamed, the permeability ratio was significantly increased, so that the permeability resistance was not improved.
또한, 상기 에멀션 크림의 내구성을 시험하기 위하여, 콘크리트의 표면을 철 브러쉬를 이용하여 30회 문질러 코팅된 표면을 제거한 후 상기 A 및 B 에멀션 크림을 적용하고 각 에멀션 크림의 투수비 및 흡수비를 비교하였다. 그 결과는 하기 표 8에 나타나 있다.In addition, in order to test the durability of the emulsion cream, the surface of the concrete was rubbed 30 times with an iron brush to remove the coated surface and then apply the A and B emulsion cream and compare the permeability ratio and absorption ratio of each emulsion cream. It was. The results are shown in Table 8 below.
상기 표 8에 나타난 바와 같이, 코팅된 표면을 제거하였을 경우, 고분자 화합물만을 사용한 경우에는 표면 제거 전보다 투수비 및 흡수비가 현저히 증가하여 투수 저항성이 감소되었다. 한편, 알킬알콕시실란 만을 사용한 경우에는 투수비 및 흡수비가 표면 제거 전과 비슷하게 측정되어 여전히 낮은 투수 저항성을 나타내었다. 따라서, 에멀션 크림의 내구성을 증진시키기 위해서는 알킬알콕시실란 및 고분자 화합물을 함께 포함시켜야 함을 알 수 있다.As shown in Table 8, when the coated surface was removed, the permeability ratio and the absorption ratio were significantly increased than before the surface removal when the polymer compound was used, thereby reducing the permeation resistance. On the other hand, when only alkylalkoxysilane was used, the permeability ratio and the absorption ratio were measured similarly before the surface removal, and still showed low permeability resistance. Therefore, it can be seen that the alkylalkoxysilane and the polymer compound must be included together to enhance the durability of the emulsion cream.
실시예 4: 알킬알콕시실란 및 고분자 화합물을 각각 에멀션화하여 혼합한 경우의 성능 시험 Example 4: Performance test when the alkylalkoxysilane and the high molecular compound were each emulsified and mixed
상기 표 1과 같은 조성으로 에멀션 크림을 제조하되, 알킬알콕시실란 및 유기 용제를 크림상으로 에멀션화한 후, 고분자 및 유기 용제를 에멀션화제가 포함된 물에 별도로 크림상으로 제조하여 두 종류의 크림을 입자가 손상되지 않는 범위의 교반 속도에서 혼합하였다. 상기 에멀션 크림의 성능을 실시예 1의 에멀션 크림과 비교하였다. 그 결과는 하기 표 9에 나타나 있다.To prepare an emulsion cream with the composition as shown in Table 1, after emulsifying the alkyl alkoxysilane and the organic solvent in the form of a cream, the polymer and organic solvent separately prepared in a cream form in water containing the emulsifier, two types of cream The mixture was mixed at a stirring speed in a range where the particles were not damaged. The performance of the emulsion cream was compared with the emulsion cream of Example 1. The results are shown in Table 9 below.
상기 표 9에 나타난 바와 같이, 본 발명의 에멀션 크림을 제조할 때, 각 유효 성분을 모두 혼합하여 에멀션화하였을 경우와 알킬알콕시실란 및 고분자 화합물을 각각 에멀션화하였을 경우의 성능은 크게 차이가 나지 않았다. 이것은, 알킬알콕시실란이 먼저 흡수되어 발수층을 형성하고 고분자는 느리게 운반되어 콘크리트의 모세관을 막아 방수력을 발생시키기 때문이다. 따라서, 알킬알콕시실란과 고분자 화합물을 각각 에멀션화한 후 혼합하여 사용하여도 동일한 성능을 나타냄을 알 수 있다.As shown in Table 9, when preparing the emulsion cream of the present invention, the performance of the emulsion and the alkyl alkoxysilane and the polymer compound when all the active ingredients are mixed and did not differ significantly. . this is, This is because the alkylalkoxysilane is first absorbed to form a water repellent layer, and the polymer is slowly transported to block the capillary of concrete to generate a waterproofing force. Therefore, it can be seen that the same performance is obtained even when the alkylalkoxysilane and the polymer compound are used after being emulsified, respectively.
이상으로 본 발명의 특정한 부분을 상세히 기술하였는 바, 당업계의 통상의 지식을 가진 자에게 있어서 이러한 구체적인 기술은 단지 바람직한 구현예일 뿐이며, 이에 본 발명의 범위가 제한되는 것이 아닌 점은 명백하다. 따라서, 본 발명의 실질적인 범위는 첨부된 청구항과 그의 등가물에 의하여 정의된다고 할 것이다.Having described the specific part of the present invention in detail, it is apparent to those skilled in the art that the specific technology is merely a preferred embodiment, and the scope of the present invention is not limited thereto. Thus, the substantial scope of the present invention will be defined by the appended claims and equivalents thereof.
이상에서 상세히 설명하였듯이, 본 발명은 투수 저항성이 개선되어 방수성이 증진된 알킬알콕시실란 에멀션 크림 및 이를 포함하는 침투성 방수제를 제공한다. 본 발명의 에멀션 크림 및 침투성 발수제는 알킬알콕시실란 및 고분자 화합물을 포함하여 발수성 뿐만 아니라 무기질 재료의 모세관까지 완전히 막아 현저히 증진된 방수성을 나타내므로, 별도의 방수 마감이 필요 없이 큰 수압이 작용하는 부위에 사용될 수 있으며, 침투성, 부착력 및 내구성이 우수하다.As described in detail above, the present invention provides an alkylalkoxysilane emulsion cream with improved permeability resistance and a permeable waterproofing agent including the same. The emulsion cream and the permeable water repellent agent of the present invention include alkylalkoxysilane and a high molecular compound to completely repel not only the water repellency but also the capillary of the inorganic material, thereby showing remarkably enhanced water resistance. It can be used and has excellent permeability, adhesion and durability.
Claims (12)