KR100460715B1 - Natural Leather and the Production Method - Google Patents
Natural Leather and the Production Method Download PDFInfo
- Publication number
- KR100460715B1 KR100460715B1 KR10-2002-0023506A KR20020023506A KR100460715B1 KR 100460715 B1 KR100460715 B1 KR 100460715B1 KR 20020023506 A KR20020023506 A KR 20020023506A KR 100460715 B1 KR100460715 B1 KR 100460715B1
- Authority
- KR
- South Korea
- Prior art keywords
- moisture
- resin
- permeable
- natural leather
- leather
- Prior art date
Abstract
본 발명은, 항균효과를 갖는 천연피혁에 관한 것으로서, 보다 상세하게는 색상 및 촉감 등의 연출에 따른 장식효과에 한정된 종래 천연피혁의 단조로움으로부터 벗어나, 음이온 및 원적외선의 방사와 항균, 유해가스 흡착분해, 탈취작용 등의 기능을 더함으로써 착용시 착용자의 건강을 증진시킬 수 있도록 한 항균효과를 갖는 천연피혁 및 그 제조방법에 관한 것이다.The present invention relates to a natural leather having an antimicrobial effect, and more specifically, from the monotony of the conventional natural leather limited to the decorative effect according to the production of color and touch, etc., radiation of negative ions and far infrared rays, antibacterial and harmful gas adsorption The present invention relates to a natural leather having an antimicrobial effect and to a method of manufacturing the same, which promotes wearer's health when worn by adding functions such as decomposition and deodorization.
이같은 본 발명은, 천연피혁의 표면에, 수지 100중량%에 대하여 2∼10중량%의 흡습성물질과 미량의 안료를 첨가한 제1투습성수지를 도포하여 안정적인 결합피막을 형성하는 제1단계와; 상기 제1단계에서 건조된 제1투습성수지 표면에 원적외선을 방사하는 세라믹 미세분말을 6∼12중량% 혼합한 제2투습성수지를 도포하여 기능성 피막층을 형성하는 제2단계; 및 상기 제2단계를 통해 형성된 제2투습성수지의 표면에는 내마모성 우레탄수지로 보호피막을 형성하는 제3단계로 이루어지는 것을 특징으로 한다.The present invention comprises a first step of forming a stable bonding film by applying a first moisture-permeable resin added to the surface of the natural leather with a moisture absorbent of 2 to 10% by weight relative to 100% by weight of the resin and a small amount of pigment; A second step of forming a functional coating layer by applying a second moisture-permeable resin mixed with 6 to 12% by weight of ceramic fine powder that emits far infrared rays on the surface of the first moisture-permeable resin dried in the first step; And a third step of forming a protective film of a wear-resistant urethane resin on the surface of the second moisture-permeable resin formed through the second step.
Description
본 발명은, 항균효과를 갖는 천연피혁에 관한 것으로서, 보다 상세하게는 색상 및 촉감 등의 연출에 따른 장식효과에 한정된 종래 천연피혁의 단조로움으로부터 벗어나, 음이온 및 원적외선의 방사와 항균, 유해가스 흡착분해, 탈취작용 등의 기능을 더함으로써 착용시 착용자의 건강을 증진시킬 수 있도록 한 항균효과를 갖는 천연피혁 및 그 제조방법에 관한 것이다.The present invention relates to a natural leather having an antimicrobial effect, and more specifically, from the monotony of the conventional natural leather limited to the decorative effect according to the production of color and touch, etc., radiation of negative ions and far infrared rays, antibacterial and harmful gas adsorption The present invention relates to a natural leather having an antimicrobial effect and to a method of manufacturing the same, which promotes wearer's health when worn by adding functions such as decomposition and deodorization.
피혁은 자연으로부터 천연적으로 얻는 천연피혁과, 인위적인 가공에 의해 생산하는 인조피혁으로 그게 나뉘어 진다. 천연피혁은 가축으로부터 얻어지는 천연소재를 이용한 것으로써 그 질감이나 촉감이 뛰어날 뿐만 아니라 유연성이 좋다는 특성이 있으며, 수지를 합성하여 제조하는 인조피혁은 성형성과 더불어 물리적 강도가 우수한 특성을 가지고 있어 의류, 소파, 가방 등 다양한 상품 분야에서 폭넓게 사용되고 있다.Leather is divided into natural leather obtained naturally from nature and artificial leather produced by artificial processing. Natural leather is made of natural materials obtained from livestock, which not only has excellent texture and feel, but also has good flexibility, and artificial leather manufactured by synthesizing resin has excellent physical strength as well as formability. It is widely used in various product fields such as bags.
한편, 근자에 들어서는 피혁제품의 기능을 단순히 물리적 강도, 구조, 성능, 외관 및 유연성 등의 특성에만 국한하지 않고, 사용자의 건강에 관련되는 요소를 부가하여 피혁 제품을 제조하는 수많은 방법이 개발되고 있다.On the other hand, in recent years, a number of methods for manufacturing leather products have been developed by adding not only the physical strength, structure, performance, appearance, flexibility, etc. to the functions of leather products, but also factors related to user's health. .
그 일 예로써, 피혁 제품에 온열작용물질 혹은, 음(-)이온 및 원적외선을 방출하는 물질을 부가하거나 혹은, 전자파 및 수맥파 등을 차단하는 물질을 첨부하는 등의 개발이 그것이다.For example, the development of adding a thermally active substance or a substance emitting negative ions and far infrared rays to a leather product, or attaching a substance that blocks electromagnetic waves and water waves.
음(-)이온은, 공기중에 보이지 않는 세균이나 박테리아 등을 살균하여 배양을 방지해 줌으로서 강력한 항균작용을 제공하며, 또한 유해한 오존을 음이온 산소로 만드는 과정에서 H2O가 생성됨으로 신선한 공기를 공급하는 한편, 수분조절이 용이하고 음이온 효과로 악취를 화학적 산화 분해해 냄새를 제거하는 것으로 잘 알려져 있다.Negative ions provide strong antibacterial activity by sterilizing invisible bacteria or bacteria in the air to prevent cultivation, and H 2 O is generated in the process of making harmful ozone into anion oxygen. On the other hand, it is well known that it is easy to control moisture and to remove odor by chemical oxidative decomposition of odor by anion effect.
또한, 원적외선은, 물체에 도달했을 때 잘 흡수되는 성질이 있으므로 침투력이 강해서 사람의 몸도 이 적외선을 쐬면 따뜻해진다. 예를 들어 30℃의 물속에서는 따뜻한 기운을 거의 느끼지 못하지만, 같은 온도의 햇볕을 쐬고 앉아 있으면 따스함을 느낄 수 있는데 그 이유는 햇볕 속에 포함되어 있는 원적외선이 피부 깊숙이 침투하여 열을 만들기 때문이다. 이러한 열작용은 각종 질병의 원인이 되는 세균을 없애는 데 도움이 되고, 모세혈관을 확장시켜 혈액순환과 세포조직 생성에 도움을 준다. 또 세포를 구성하는 수분과 단백질 분자에 닿으면 세포를 1분에 2,000번씩 미세하게 흔들어줌으로써 세포조직을 활성화하여 노화방지, 신진대사 촉진, 만성피로 등 각종 성인병 예방에 효과가 있는 것으로 검증되고 있다. 그밖에도 발한작용 촉진, 통증완화, 중금속 제거, 숙면, 탈취, 방균, 곰팡이 번식방지, 제습, 공기정화 등의 효과가 있어 주택 및 건축자재, 주방기구, 섬유·의류·침구류, 의료기구, 찜질방 등의 여러 분야에 쓰이고 있다.In addition, since far infrared rays have a property of being absorbed well when they reach an object, the penetration power is strong, and the human body also warms up when the human body radiates this infrared ray. For example, you can hardly feel the warm energy in the water at 30 ℃, but sitting in the sun at the same temperature can feel warm because the infrared rays contained in the sun penetrates deep into the skin to create heat. This heat action helps to eliminate the bacteria that cause various diseases, and helps to expand the capillaries and blood circulation and tissue formation. In addition, when it touches the water and protein molecules that make up the cells, it is proven to be effective in preventing various adult diseases such as aging, promoting metabolism, and chronic fatigue by activating cell tissues by shaking the cells minutely 2,000 times per minute. In addition, it promotes sweating, pain relief, heavy metal removal, sleep, deodorization, antibacterial, mold propagation prevention, dehumidification, and air purification, so it is effective in housing and building materials, kitchen utensils, textiles, clothing, bedding, medical equipment, jjimjilbang. It is used in many fields.
그러나, 피혁 가공시 음(-)이온 및 원적외선을 방출하는 물질을 일체로 투입하여 코팅하거나 제조하는 것은 결코 쉬운일이 아니다. 따라서, 국내 특허공개 96-41515호에 개시되고 있듯이 PVC수지 조성물에 소정의 세라믹 파우더를 혼합하는 방법으로 시트를 제조하여 인조피혁을 생산하여 왔다. 이러한 방법 이외에도 통상의 피혁 표면에 세라믹 파우더 등이 혼합된 수지를 요철형상으로 부착하여 지압 또는 장식적 효과를 제공하고 있기도 하다.However, it is not easy to coat or manufacture by integrating negative ions and materials that emit far infrared rays in leather processing. Therefore, as disclosed in Korean Patent Publication No. 96-41515, artificial leather has been produced by manufacturing a sheet by mixing a predetermined ceramic powder in a PVC resin composition. In addition to such a method, a resin having mixed ceramic powder or the like is attached to the surface of a conventional leather in an uneven shape to provide acupressure or a decorative effect.
하지만, 상기 세라믹 파우더의 첨가는 수지와 혼합하는 방식으로 성형되는 인조피혁에 적합할 뿐, 천연피혁에 적용시는 부착에 어려움이 있고, 더욱이 가죽의 경화를 촉진하는 등 부작용을 보이고 있는 것이었으며, 피혁에 상기 요철형상의 돌기를 부착하는 경우 역시, 피혁 제품의 잦은 굴곡에 의해 부착된 돌기가 쉽게 떨어져 나가는 등 외관과 유연성을 크게 떨어트려 품질의 저하와 상품성을 크게 떨어트리는 결과를 가져오게 되는 것이었다.However, the addition of the ceramic powder is only suitable for artificial leather that is molded by mixing with a resin, it is difficult to adhere when applied to natural leather, and further has shown side effects such as promoting the hardening of leather, In the case of attaching the uneven protrusions to the leather, the attached protrusions are easily detached due to frequent bending of the leather product, which greatly reduces the appearance and flexibility, resulting in a significant deterioration in quality and productability. .
즉, 피혁제품에서 원적외선이 방출될 수 있도록 세라믹 파우더를 부착하는 작업은 피혁 제조공정의 복잡성으로 인하여 이루어질 수 없었다. 특히 피혁제품은 제조공정중 사용되는 여러종류의 약품과 원적외선 방출물질이 서로 작용하여 가죽의 품질을 떨어뜨릴 수 있기 때문에, 피혁에서 원적외선이 방출되도록 하기 위해서는 피혁의 표면에 원적외선 방출물질을 코팅하는 방법이 사용되고 있다. 그러나, 표면에 원적외선 방출물질을 코팅하는 경우 제품의 반복된 사용에 의해 원적외선 방출물질이 떨어져 나가게 되어 원적외선 방출효과를 얻을 수 없게 되는 문제점이 지적되고 있는 것이다.That is, the operation of attaching the ceramic powder to emit far infrared rays from the leather product could not be made due to the complexity of the leather manufacturing process. In particular, since leather products can degrade the quality of leather by interacting with various chemicals and far-infrared emitters used during the manufacturing process, in order to release far-infrared rays from the leather, a method of coating the far-infrared emitters on the surface of the leather Is being used. However, when the far-infrared emitter is coated on the surface, it is pointed out that the far-infrared emitter is released by repeated use of the product and thus the far-infrared emitter cannot be obtained.
본 발명자들은 상기와 같은 문제점을 해결하기 위하여 안정된 결합방법을 강구한 결과, 원료피혁의 표면에 탄력성과 투습성 및 유연성을 각기 보유하는 수지재를 이용하여 습윤코팅층을 형성하고, 그 위에 세라믹 미세분말을 포함하는 기능성 피막층을 구성하여 줌으로서, 피혁의 성질을 저해함이 없는 안정화된 가공 피혁을 제공할 수 있다는 사실에 접근하고 본 발명을 완성하기에 이르렀다.The present inventors have devised a stable bonding method to solve the above problems, and as a result, to form a wet coating layer using a resin material each having elasticity, moisture permeability and flexibility on the surface of the raw material leather, and the ceramic fine powder thereon By constructing a functional coating layer comprising the same, the present inventors have approached the fact that a stabilized processed leather can be provided without impairing the properties of the leather.
본 발명은 인체에 유익한 음(-)이온과 원적외선 방사물질을 함께 지니는 방사체 조성물을 첨가하여, 음(-)이온분자 800 이상, 그리고 원적외선 방사율 0.85 ~ 0.92% 이상의 범위를 유지하도록 하고, 이를 통해 악화된 생활환경으로 부터 산성화된 체질의 개선 및 각종 질병에 대한 예방 치료능력이 우수한 피혁제품을 제공하는데 그 주된 목적이 있는 것이다.The present invention is added to the emitter composition having a negative (-) ion and a far infrared radiation material beneficial to the human body, to maintain a range of more than 800 negative (+), and far infrared emissivity 0.85 ~ 0.92%, thereby deteriorating The main purpose is to improve the acidified constitution from the living environment and to provide leather products with excellent preventive treatment ability against various diseases.
본 발명의 다른 목적은, 항균, 항곰팡이 및 유해가스 흡착분해작용 등의 기능을 제공하는 원적외선 방사물질을 안정적으로 결합하며, 장시간 사용후에도 동일한 성질을 그대로 유지하는 항균효과를 갖는 천연피혁 및 그 제조방법을 제공하는데 있다.Another object of the present invention is to combine the far-infrared radiation material that provides functions such as antibacterial, anti-mold and harmful gas adsorption decomposition stably, and natural leather having the antibacterial effect to maintain the same properties even after prolonged use and its manufacture To provide a method.
도 1은 본 발명의 항균효과를 갖는 천연피혁의 개략적인 단면 구조도.1 is a schematic cross-sectional structure diagram of a natural leather having an antibacterial effect of the present invention.
도 2의 (a)(b)는 세라믹 미세입자의 원적외선 방사율 및 방사에너지 그래프.Figure 2 (a) (b) is a far-infrared emissivity and radiation energy graph of the ceramic microparticles.
도 3의 (a)(b)는 본 발명에 따른 기능성 피혁으로부터의 원적외선 방사율 및 방사에너지 그래프.Figure 3 (a) (b) is a far-infrared emissivity and radiation energy graph from the functional leather according to the present invention.
도 4는 본 발명에 따른 기능성 피혁와 미가공 상태의 피혁간의 유해가스 흡착 분해작용을 테스트 한 비교 그래프4 is a comparison graph of the harmful gas adsorption decomposition test between the functional leather and the raw leather in accordance with the present invention
상기 목적들을 달성하기 위한 본 발명은, 천연피혁의 표면에, 수지 100중량%에 대하여 2∼10중량%의 흡습성물질과 미량의 안료를 첨가한 제1투습성수지를 도포하여 안정적인 결합피막을 형성하는 제1단계와; 상기 제1단계에서 건조된 제1투습성수지 표면에 원적외선을 방사하는 세라믹 미세분말을 6∼12중량% 혼합한 제2투습성수지를 도포하여 기능성 피막층을 형성하는 제2단계를 통해 제공되는 것을 특징으로 한다. 그리고, 상기 제2단계를 통해 형성된 제2투습성수지의 표면에는 내마모성 우레탄수지로 보호피막을 선택적으로 형성하는 제3단계를 제공한다.The present invention for achieving the above object, to form a stable bonding film by applying a first moisture-permeable resin to the surface of the natural leather added a moisture content of 2 to 10% by weight relative to 100% by weight resin and a small amount of pigments A first step; It is provided through the second step of forming a functional coating layer by applying a second moisture-permeable resin mixed with 6 to 12% by weight of ceramic fine powder that emits far infrared rays on the surface of the first moisture-permeable resin dried in the first step. do. In addition, the surface of the second moisture-permeable resin formed through the second step provides a third step of selectively forming a protective film with a wear-resistant urethane resin.
다시말해, 본 발명의 세라믹 처리된 천연피혁은, 수지 100중량%에 대하여 2∼10중량%의 흡습성물질과 미량의 안료를 첨가한 제1투습성수지를 도포하여 안정적인 결합피막을 형성하고; 그 표면에 원적외선을 방사하는 세라믹 미세분말을 6∼12중량% 혼합한 제2투습성수지를 도포하여 기능성 피막층을 형성하며; 상기 기능성 피막층의 상면에는 다시 내마모성 우레탄수지로 형성되는 보호피막을 선택적으로 구성하여 줌으로서 기능성이 우수한 고부가가치의 피혁제품을 제공할 수 있게 되는 것이다.In other words, the ceramic-treated natural leather of the present invention is coated with a first moisture-permeable resin containing 2-10% by weight of a hygroscopic material and a trace amount of pigment to 100% by weight of a resin to form a stable bond film; Applying to the surface a second moisture-permeable resin mixed with 6 to 12% by weight of ceramic fine powder that emits far infrared rays to form a functional coating layer; The upper surface of the functional coating layer is to provide a high value-added leather product with excellent functionality by selectively configuring a protective film formed of the wear-resistant urethane resin again.
이때, 상기 투습성수지는, 에치렌 초산비닐 공축합체, 아크릴산 또는 메타크릴산, 에스텔류, 아크릴에스텔과 염화비닐 또는 염화비닐리덴과의 공축합물로서 인장탄성률이 1㎜ 이상인 것이 바람직하게 사용된다.At this time, the moisture-permeable resin is preferably an elastic modulus of 1 mm or more as the ethylene vinyl acetate co-condensate, acrylic acid or methacrylic acid, esters, acrylic esters and vinyl chloride or vinylidene chloride.
상기 흡습성물질은, 실리카, 알루미나계 활성탄소, 제오라이트, 다공질세라믹 등 무기재료 중 적어도 하나 이상이 사용되며, 이는 수지와의 친화성과 경시변화, 점도등 물성변화가 일어나지 아니하도록 실란으로 표면처리된 것이 사용된다. 상기 실란은, 경시, 증점, 겔화 현상이 일어나지 아니하도록 CnH2n+1로 표시되는 탄소수 10 이상의 장쇄 알키드알콕시실란이 바람직하게 사용된다.As the hygroscopic material, at least one or more of inorganic materials such as silica, alumina-based activated carbon, zeolite, porous ceramics, etc. are used, which is surface-treated with silane so that physical properties such as affinity with the resin, change with time, viscosity, and the like do not occur. Used. As the silane, a long-chain alkyd alkoxysilane having 10 or more carbon atoms, preferably represented by C n H 2n + 1 , is preferably used so as not to cause a thickening and gelation phenomenon with time.
이하 본 발명의 바람직한 실시예를 상세히 설명하기로 한다.Hereinafter, a preferred embodiment of the present invention will be described in detail.
본 발명에 사용되는 원료 피혁은, 통상의 전처리 과정에 따라, 완전 건조상태에 있는 원피에 수분을 투입하여 원래의 가죽 상태로 만드는 수적공정과, 불순물을 제거하는 석회석 공정을 수행하고, 이어서 이를 필요한 두께로 가공하는 분활공정을 수행하며, 재석회석 공정 및 탈회공정, 그리고 효회공정, 침산공정, 유성공정, 세수 물짜기공정, 세빙공정 및 재유성공정, 염색공정, 중화공정, 가지공정, 도장공정을 거쳐 완성된 가죽을 사용하게 된다.Raw material leather used in the present invention, according to the usual pre-treatment process, performs a water-soaking process to add moisture to the raw skin in a completely dry state to make the original leather, and limestone process to remove impurities, and then It carries out the division process to the thickness, ash limestone process and deliming process, and hyohoe process, pickling process, oil process, washing water process, washing process and re-oil process, dyeing process, neutralization process, eggplant process, painting process Through the finished leather will be used.
본 발명에 따르면 이같은 원피(10)의 표면에, 흡습성물질과 미량의 안료를 첨가한 투습성수지를 소정의 두께로 도포함으로서 형성되는 안정적인 결합피막(12)과, 건조된 상기 결합피막(12)의 상부에 제공되며 세라믹 미세분말을 포함하는 기능성 피막층(14)을 형성하되, 상기 세라믹 미세분말은 수지와의 친화성과 경시변화, 점도등 물성변화가 일어나지 아니하도록 실란으로 표면처리하여 사용한다.According to the present invention, on the surface of such raw skin 10, a stable bonding film 12 formed by coating a moisture-absorbing substance and a trace amount of a moisture-containing resin to a predetermined thickness, and dried of the bonding film 12 A functional coating layer 14 is formed on the upper portion and includes a ceramic fine powder, and the ceramic fine powder is used by surface treatment with silane so that physical properties such as affinity with a resin, changes over time, and viscosity do not occur.
다시말해, 원피(10)의 표면에 코팅되는 제1피막으로서의 투습성수지는, 수지 100중량%에 대하여 2∼10중량%의 흡습성물질과 미량의 안료를 첨가한 것으로서 이는 원피(10) 위에 안정적인 결합피막(12)을 형성하게 된다.In other words, the moisture-permeable resin as the first film to be coated on the surface of the raw skin 10 is added to 2 to 10% by weight of the hygroscopic material and a small amount of pigment with respect to 100% by weight of the resin, which is a stable bond on the raw material 10 The film 12 is formed.
상기 결합피막(12)을 구성하는 주재로서 사용되는 투습성수지는, 에치렌 초산비닐 공축합체, 아크릴산 또는 메타크릴산, 에스텔류, 아크릴에스텔과 염화비닐 또는 염화비닐리덴과의 공축합물로서 인장탄성률이 1㎜ 이상인 것이 바람직하게 사용된다.The moisture-permeable resin used as the main material of the bonding film 12 is a tensile modulus of elasticity as a co-condensation product of ethylene vinyl acetate, acrylic acid or methacrylic acid, esters, acrylic esters and vinyl chloride or vinylidene chloride. It is used preferably that this is 1 mm or more.
그리고, 결합피막(12)에 첨가되는 흡습성물질은, 실리카, 알루미나계 활성탄소, 제오라이트 또는 다공질세라믹 등 무기재료 중 적어도 하나 이상이 단독 또는 혼합 사용되는 것이며, 수지와의 친화성과 경시변화, 점도등 물성변화가 일어나지 아니하도록 그 표면을 실란으로 표면처리하여 사용하게 되는데, 이는 80℃, 습도 10% 이하에서 습성 경화되고, 원형 탈회기에서 분리되어 1㎜ 이하의 입자로 성형된 것이 사용된다. 이때, 실란은 경시, 증점, 겔화 현상이 일어나지 아니하도록 CnH2n+1로 표시되는 탄소수 10 이상의 장쇄 알키드알콕시실란이 바람직하다.As the hygroscopic material added to the bonding film 12, at least one or more of inorganic materials such as silica, alumina-based activated carbon, zeolite, or porous ceramics are used alone or in combination. The surface of the surface is treated with silane so as not to cause a change in physical properties. It is wet cured at 80 ° C. and humidity of 10% or less, and is separated from a circular delimizer and molded into particles of 1 mm or less. In this case, the silane is preferably a long-chain alkyd alkoxysilane having 10 or more carbon atoms represented by C n H 2n + 1 so as not to cause thickening, gelation or aging.
흡습성물질에 실란을 표면 처리하여 얻은 충진제를 수지공축합물에 배합하여 결합피막(12)인 투습성 접착용 수지조성물을 제조하게 되는 것으로서, 이와같이 제조된 결합피막(12)은 원피(10)와의 결합 뿐만 아니라, 후술될 세라믹 미세분말을 포함하는 기능성 피막층(14)과의 안정적인 결합을 가능하게 한다.The filler obtained by surface-treating the silane on the hygroscopic material is blended with the resin co-condensate to produce a moisture-permeable adhesive resin composition, which is the bond coat 12, wherein the bond coat 12 thus prepared is bonded to the raw skin 10. In addition, it enables a stable coupling with the functional film layer 14 including the ceramic fine powder to be described later.
상기 결합피막(12)인 투습성 접착용 수지조성물은, 비장탄, 죽탄, 황토 전기석 중 선택된 하나 이상의 재료를 -5℃에서 냉각 분쇄하고, 이를 수지공축합물에 배합하여서 되는 투습성을 갖는 수지이다.The moisture-permeable adhesive resin composition as the bonding film 12 is a resin having moisture permeability which is obtained by cold-pulverizing at least one material selected from charcoal, bamboo charcoal, and ocher tourmaline at -5 ° C, and blending it in the resin co-condensate.
이러한 흡습성물질은 피혁의 외부 혹은 내부로부터 발생하는 습기를 차단 또는 흡수하게 되는 것으로서, 내부로부터 발생하는 열(예를 들어, 체열, 기후 변화, 난방 등에 의한 열)에 의해 발생되는 습기를 흡수 또는 방출하는데 매우 유용하며, 이로 인해 피혁이 변질되거나 부패하는 것을 방지하게 된다.The hygroscopic material is to block or absorb moisture generated from the inside or outside of the leather, and absorbs or releases moisture generated by heat generated from the inside (for example, body heat, climate change, heat, etc.). It is very useful to prevent the deterioration or decay of leather.
이같은 결합피막(12)의 표면에는 원적외선을 방사하는 세라믹 미세분말을 6∼12중량% 혼합한 제2피막으로서의 투습성수지를 도포하여 기능성 피막층(14)을 형성하게 된다.The functional coating layer 14 is formed on the surface of the bonding coating 12 by applying a moisture-permeable resin as a second coating containing 6 to 12% by weight of ceramic fine powder emitting far-infrared rays.
기능성 피막층(14)을 구성하는 투습성수지는 또한, 상기 제1피막의 구성에 사용된 수지와 마찬가지로 에치렌 초산비닐 공축합체, 아크릴산 또는 메타크릴산, 에스텔류, 아크릴에스텔과 염화비닐 또는 염화비닐리덴과의 공축합물이 사용된다.The moisture-permeable resin constituting the functional coating layer 14 is also similar to the resin used in the composition of the first coating, ethylene vinyl acetate, acrylic acid or methacrylic acid, esters, acrylic and vinyl chloride or vinylidene chloride. Cocondensates of and are used.
상기 세라믹 미세분말은, 항균, 방균, 항곰팡이, 유해가스 흡착분해 및 원적외선 방사작용을 하여 생활환경을 쾌적하고 건강하게 유지시키기 위하여 첨가되는 것으로서, 200~325 메쉬의 입도로 분쇄된 석분을 이용하는 것이며, 바람직하게는 300 메쉬의 입도 범위의 맥반석 또는 흑운모쇄석을 이용한다.The ceramic fine powder is added to maintain a pleasant and healthy living environment by antibacterial, antibacterial, anti-mold, harmful gas adsorption decomposition and far-infrared radiation, it is to use the crushed stone powder with a particle size of 200 ~ 325 mesh Preferably, elvan or biotite crushed stone in the particle size range of 300 mesh is used.
이는 200 메쉬이하로 분쇄된 큰 입자를 이용시에는, 큰 입자의 세라믹이 수지와와 잘 혼합되지 않게 됨으로써 점성 및 강도를 저하시키게 될 뿐만 아니라, 수지 배합을 위한 교반시 커터를 손상시킬 수 있기 때문이다. 또한, 325 메취 이상 작은 입자 이용시에는, 세라믹 자체의 분자구조 및 물성이 변하게 되어 세라믹의 효능을 저하시킬 수 있기 때문이다.This is because when using large particles pulverized to 200 mesh or less, the ceramics of the large particles do not mix well with the resin, thereby reducing the viscosity and strength, as well as damaging the cutter during stirring for resin blending. . In addition, when using particles smaller than 325 mesothes, the molecular structure and physical properties of the ceramic itself may be changed, which may lower the effectiveness of the ceramic.
상기 맥반석 이나 흑운모 대신에 백운모, 석영 또는 맥반석 등이 이용될 수 있으나, 그 효능이 희토광물을 상당량 함유한 맥반석이나 흑운모에 미치지 못함은물론이다. 이는 이들이 인체에 유익한 원적외선을 다량 방사시킬 뿐만 아니라, 차음, 항균, 방균, 항곰팡이 및 유해가스 흡착 분해작용이 탁월하여 생활환경을 쾌적하게 유지시키는 작용을 하며, 특히 상기 맥반석이나 흑운모에 함유된 게르마늄이 유해가스 중화작용 및 음이온 방출작용을 함으로써 생활환경을 더욱 쾌적하고 건강하게 유지시켜 주기 때문이다.Instead of the gangue stone or biotite, dolomite, quartz, or gangue stone may be used, but the effect does not reach the gangue stone or biotite containing a considerable amount of rare earth minerals. This not only emits a large amount of far-infrared rays, which are beneficial to the human body, but also has excellent sound insulation, antibacterial, antibacterial, antifungal and harmful gas adsorption and decomposing action, and maintains a comfortable living environment. This is because neutralizing the harmful gas and releasing the anion keeps the living environment more comfortable and healthy.
도 2의 (a)와 (b)는 50℃의 실온에서 세라믹의 원적외선 방사율 및 방사에너지를 측정하고, 그 결과를 그래프로 나타낸 것으로서, 실선으로 도시된 바와 같이, 이들 세라믹은 5~20㎛의 원적외선 파장 범위에서 0.93%의 방사율과 4.31×102W/㎡·㎛의 방사에너지를 나타냈다. 그리고, 제2도의 (b)에서, 실선으로 도시된 세라믹의 방사에너지는, 점선으로 도시된 인체의 방사에너지와 비교하여 볼 때, 파장에 따른 방사 에너지의 분포가 매우 유사한 것으로 나타났다. 이를 통하여 세라믹으로부터 방사된 원적외선 파장은 인체에 적합할 뿐만 아니라 인체에서의 흡수가 매우 용이하다는 것을 알 수 있다.2 (a) and 2 (b) measure far-infrared emissivity and radiant energy of ceramics at room temperature of 50 ° C., and show the results in graphs. As shown by solid lines, these ceramics are 5-20 μm. In the far infrared wavelength range, the emissivity was 0.93% and the emission energy was 4.31 x 102 W / m 2 · µm. And, in Figure 2 (b), the radiation energy of the ceramic shown by the solid line, compared with the radiation energy of the human body shown by the dotted line, the distribution of the radiation energy according to the wavelength was found to be very similar. Through this, it can be seen that the far-infrared wavelength emitted from the ceramic is not only suitable for the human body but also very easily absorbed by the human body.
이와같이 형성된 상기 기능성 피막층(14)의 상면에는 다시 내마모성 우레탄수지로 형성되는 보호피막을 선택적으로 구성하여 줌으로서 기능성이 우수한 고부가가치의 피혁제품을 제공할 수 있게 되는 것이다.The upper surface of the functional coating layer 14 formed as described above may provide a high value-added leather product having excellent functionality by selectively forming a protective film formed of a wear-resistant urethane resin.
[ 실시예 1 ]Example 1
먼저, 흡습성물질 중 하나인 제오라이트를 3.5g 첨가한 투습성수지 100g을 피혁에 도포하였다.First, 100 g of a moisture-permeable resin to which 3.5 g of zeolite, which is one of hygroscopic substances, was added, was applied to the leather.
다음, 건조 완료된 도포면에 음(-)이온 800 이상, 원적외선 방사율이 0.85%이상인 세라믹스 805g을 투습성수지 100g에 혼합하여 도포하였다. 이때 착색안료 적당량 투입하여 시각적인 효과를 시도하였다.Next, 805 g of ceramics having a negative (-) ion of 800 or more and far infrared emissivity of 0.85% or more were mixed and applied to 100 g of a moisture-permeable resin on the dried coated surface. At this time, an appropriate amount of coloring pigment was added to try a visual effect.
그 후에, 건조 완료된 도포면에 유연성, 절곡성, 평활성 등을 가지면서도 음(-)이온 및 원적외선으로 인한 효과를 제공할 수 있도록 내마모성 수지 중 하나인 고형분의 우레탄 30％를 코팅하여 최종 건조시켰다.Thereafter, 30% of the solid urethane, which is one of the wear-resistant resins, was coated and finally dried to provide the effect of negative (-) ions and far infrared rays on the dried coated surface while having flexibility, bendability, smoothness, and the like.
이와 같이 제조된 피혁은, 수지에 배합된 세라믹 미세분말의 약리작용에 의하여, 상기 피혁 가공물은 차음, 항균, 방균, 항곰팡이 및 유해가스 흡착분해작용을 할 뿐만 아니라 다량의 원적외선을 방사하여, 생활환경을 쾌적하고 건강하게 만들어 주었다.Thus produced leather, by the pharmacological action of the ceramic fine powder blended in the resin, the leather processed product not only the sound insulation, antibacterial, antibacterial, anti-mold and harmful gas adsorption decomposition, but also emits a large amount of far infrared rays, life It made the environment pleasant and healthy.
도 3의 (a)와 (b)는 상기 실시예 1에 따른 가공된 피혁으로부터의 원적외선 방사율 및 방사에너지를 40℃의 실온에서 측정하고, 그 결과를 그래프로 나타낸 것이다. 그 결과, 실선으로 도시된 바와 같이, 5~20㎛의 원적외선 파장 범위에서 0.91%의 방사율과 3.66×102W/㎡·㎛의 방사에너지를 방사시켰으며, 이 또한 파장에 따른 방사에너지의 분포가 인체의 방사에너지 분포와 유사한 것으로 나타났다. 이러한 데이터를 통하여 본 발명의 실시예에서와 같은 방법으로 세라믹 미세분말을 피혁에 안정적으로 결합시킨 경우에도, 세라믹 자체의 방사율 및 방사에너지에 근접한 다량의 원적외선을 방사시킨다는 것을 알 수 있다.(A) and (b) of FIG. 3 measure the far-infrared emissivity and the radiant energy from the processed leather according to Example 1 at room temperature of 40 ° C., and show the results graphically. As a result, as shown by the solid line, the emissivity of 0.91% and the emission energy of 3.66 × 102 W / m 2 · µm were emitted in the far-infrared wavelength range of 5 to 20 µm, and the distribution of the radiation energy according to the wavelength was also determined by the human body. It is similar to the radiation energy distribution of. These data show that even when the ceramic fine powder is stably bonded to the leather in the same manner as in the embodiment of the present invention, it emits a large amount of far infrared rays close to the emissivity and the radiation energy of the ceramic itself.
하기의 표 1은 본 발명에 따른 기능성 피혁과 종래의 미처리 피혁의 유해가스 흡착분해작용을 비교하기 위한 실험 데이타이다. 즉, 2개의 밀폐된 공간에 각각 종래의 피혁 및 본 발명의 기능성 피혁을 펼쳐서 부착한 다음, 각 공간에 500 ppm의 암모니아 가스를 각기 주입시키고, 시간의 경과에 따른 암모니아 가스의 잔류량을 가스검지관으로 측정한 것이다.Table 1 below is experimental data for comparing the harmful gas adsorption decomposition of the functional leather according to the present invention and the conventional untreated leather. That is, the conventional leather and the functional leather of the present invention are unfolded and attached to each of the two enclosed spaces, and 500 ppm of ammonia gas is injected into each space, and the residual amount of ammonia gas is passed over time. It is measured by.
[표 1]TABLE 1
상기 표 1을 참조하면, 가공되지 않은 종래 피혁의 경우에는, 500 ppm의 암모니아가 주입된 다음 120분이 경과된 후에도 450 ppm(90%)의 암모니아가 잔류되는 것으로 나타났다. 반면에, 본 발명에 따른 기능성 피혁의 경우, 500 ppm의 암모니아가 주입된 다음 30분이 경과된 후에는 100 ppm(20%)의 암모니아 만이 잔류되고, 120분이 경과된 후에는 45 ppm의 암모니아 만이 잔류된 것으로 나타났다. 즉, 본 발명의 따른 기능성 피혁을 사용한 경우에는, 120분의 경과후 주입된 암모니아중 91%의 암모니아가 흡수 탈취시킨 것이며, 이러한 실험결과에 의하여, 기능성 피혁이 유해가스를 빠르게 흡수 탈취시켜 생활환경을 쾌적하게 만들어 준다는 것을 확일할 수 있었다. 도 4는 상기 표 1의 데이타를 그래프로 표현한 것이다. 도 4를 통하여, 종래 피혁이 사용된 경우에는, 실선으로 도시된 바와 같이, 시간이 경과되어도 주입된 가스농도가 미미하게 감소되며, 본 발명의 기능성 피혁이 사용된 경우에는, 점선으로 도시된 바와 같이, 시간이 경과됨에 따라 가스농도가 매우 급격하게 감소된다는 것을 시각적으로 확인할 수 있었다.Referring to Table 1, it was shown that in the case of the unprocessed conventional leather, 450 ppm (90%) of ammonia remained after 120 minutes after 500 ppm of ammonia was injected. On the other hand, in the functional leather according to the present invention, only 100 ppm (20%) of ammonia remains after 30 minutes after 500 ppm of ammonia is injected, and only 45 ppm of ammonia remains after 120 minutes. Appeared to be. In other words, when the functional leather according to the present invention is used, 91% of ammonia is absorbed and deodorized after 120 minutes has elapsed. You can be sure that it makes you comfortable. 4 is a graph representing the data of Table 1. 4, when the conventional leather is used, as shown by the solid line, the injected gas concentration is reduced slightly over time, and when the functional leather of the present invention is used, as shown by the dotted line Likewise, it could be visually confirmed that the gas concentration decreases very rapidly with time.
[ 실시예 2 ]Example 2
먼저, 흡습성물질 중 하나인 활성탄소 분말을 3.5g 첨가한 투습성수지 100g을 피혁에 도포하였다. 이때, 색소(안료) 적당량 추가하였다.First, 100 g of a moisture-permeable resin to which 3.5 g of activated carbon powder, which is one of hygroscopic substances, was added, was applied to the leather. At this time, a suitable amount of pigment (pigment) was added.
이어서 건조 완료된 도포면에 세라믹 미세분말 805g과 더불어 토루마린 분말 5g을 투습성수지 100g에 혼합하여 도포하였다.Subsequently, 5 g of tourmaline powder and 805 g of ceramic fine powder were mixed and applied to 100 g of a moisture-permeable resin on the dried coated surface.
그리고, 그 위에 다시 내마모성 수지 중 하나인 가교형 아크릴 수지 100g을 코팅하여 최종 건조시킴으로써 유연성, 절곡성, 평활성, 내마모성 등을 가지면서도 음(-)이온 및 원적외선으로 인한 효과를 제공할 수 있도록 한 피혁을 제조할 수 있었다.Then, by coating 100g of crosslinkable acrylic resin, which is one of the wear resistant resins, and finally drying it, the leather is capable of providing an effect due to negative (-) ions and far infrared rays while having flexibility, bendability, smoothness, and wear resistance. Could be prepared.
이와 같이, 본 발명에서는 피혁에 흡습성물질이 첨가된 투습성수지를 도포하는 단계와, 건조 완료된 도포면에 음(-)이온 및 원적외선 방사물질의 미세분말을 투습성수지에 혼합하여 도포하는 단계와, 그 표면에 내마모성수지를 도포하는 단계를 통한 피혁 가공방법을 통해, 피혁이 가지는 본연의 특성인 유연성, 절곡성, 평활성, 내마모성 등을 가지면서도 음(-)이온 및 원적외선으로 인한 효과를 안정적으로 제공할 수 있게 된다.As described above, in the present invention, a step of applying a moisture-permeable resin to which the hygroscopic material is added to the leather, and mixing and applying a fine powder of negative (-) ion and far-infrared radiation substance to the moisture-permeable resin on the dried coating surface, and the surface thereof Through the leather processing method through applying a wear resistant resin to the leather, it can stably provide effects due to negative (-) ions and far-infrared rays while having the natural characteristics such as flexibility, bendability, smoothness and abrasion resistance. Will be.
전술한 실시예에서는 음(-)이온 및 원적외선 방사물질을 모두 첨가하는 것에 관해 설명하였다. 그러나, 본 발명을 통해 음(-)이온 및 원적외선 방사물질 중 어느 하나를 선택적으로 포함하는 피혁을 제조하는 것 역시 동종자라면 용이하게 판단할 수 있는 것이므로 본 발명의 실시예는 후술될 특허청구범위에 기재된 또 다른 구현을 포함하며, 따라서 특허청구범위에 기재된 바에 의해 비로서 한정될 수 있게 된다.In the above embodiment, the addition of both negative (-) ions and far-infrared radiation materials has been described. However, since it is also possible to easily determine the same type of leather produced by the present invention, the leather containing any one of the negative (-) ions and far-infrared radiation material, embodiments of the present invention will be described in the claims It includes another embodiment described in, and thus can be defined as a ratio as described in the claims.
이상에서 살펴본 바와 같이, 본 발명은 상기한 공정을 통해 가공된 피혁에 음(-)이온 및 원적외선 방출물질을 안정적으로 결합시켜, 완성된 가죽으로부터 양질의 원적외선이 방출될 수 있게 되며, 이를 통해 착용자의 건강 증진을 도모하는 항균효과를 갖는 천연피혁을 제공한다.As described above, the present invention stably combines negative (-) ions and far-infrared emitters with the leather processed through the above process, it is possible to emit high quality far-infrared from the finished leather, thereby It provides natural leather with antibacterial effect to promote health.
Claims (8)