KR100450752B1 - Polymer electrolytes using polymer blend based on cationic polymer and method for preparing the same - Google Patents
Polymer electrolytes using polymer blend based on cationic polymer and method for preparing the same Download PDFInfo
- Publication number
- KR100450752B1 KR100450752B1 KR10-2002-0027060A KR20020027060A KR100450752B1 KR 100450752 B1 KR100450752 B1 KR 100450752B1 KR 20020027060 A KR20020027060 A KR 20020027060A KR 100450752 B1 KR100450752 B1 KR 100450752B1
- Authority
- KR
- South Korea
- Prior art keywords
- polymer
- acrylonitrile
- lithium
- electrolyte
- polymer blend
- Prior art date
Abstract
아크릴로니트릴계 고분자와 양이온성 고분자가 혼합된 고분자 브렌드를 이용한 비수계 이차전지용 고분자 전해질 및 그 제조 방법에 관하여 개시한다. 본 발명에 따른 고분자 전해질의 제조 방법에서는 아크릴로니트릴 반복 단위를 포함하는 고분자 및 양이온성 고분자를 브렌딩하여 고분자 브렌드를 준비한다. 상기 고분자 브렌드 및 무기물을 공용매에 용해시켜 고분자 브렌드 용액을 제조한다. 상전환법에 의해 상기 고분자 브렌드 용액으로부터 다공성 고분자 필름을 형성한다. 상기 다공성 고분자 필름을 리튬염이 용해된 전해액에 함침시킨다.Disclosed are a polymer electrolyte for a non-aqueous secondary battery using a polymer blend in which an acrylonitrile-based polymer and a cationic polymer are mixed, and a manufacturing method thereof. In the method for preparing a polymer electrolyte according to the present invention, a polymer blend is prepared by blending a polymer including an acrylonitrile repeating unit and a cationic polymer. The polymer blend and the inorganic material are dissolved in a cosolvent to prepare a polymer blend solution. A porous polymer film is formed from the polymer blend solution by a phase inversion method. The porous polymer film is impregnated into an electrolyte solution in which lithium salt is dissolved.
Description
본 발명은 고분자 전해질 및 그 제조 방법에 관한 것으로, 보다 상세하게는 아크릴로니트릴계 고분자와 양이온성 고분자가 혼합된 고분자 브렌드를 이용한 비수계 이차전지용 고분자 전해질 및 그 제조 방법에 관한 것이다.The present invention relates to a polymer electrolyte and a method for manufacturing the same, and more particularly, to a polymer electrolyte for a non-aqueous secondary battery using a polymer blend in which an acrylonitrile-based polymer and a cationic polymer are mixed, and a method for manufacturing the same.
최근, 전기, 전자, 통신 및 컴퓨터 산업이 급속하게 발전함에 따라 고성능, 고안정성의 이차전지에 대한 수요는 점점 증대되고 있다. 특히, 전자기기의 소형화, 박형화 및 경량화가 급속도로 이루어지고 있으며, 사무 자동화 분야에 있어서는 데스크탑형 컴퓨터에서 랩탑형, 노트북형 컴퓨터로 소형 및 경량화 되고 있고, 캠코더, 셀룰러폰 등의 휴대용 전자기기도 급속하게 확산되고 있다.Recently, with the rapid development of the electric, electronic, communication and computer industries, the demand for high performance and high stability secondary batteries is increasing. In particular, the miniaturization, thinning, and lightening of electronic devices are rapidly made. In the field of office automation, small and light weights are being reduced from desktop computers to laptop and notebook computers, and portable electronic devices such as camcorders and cellular phones are also rapidly being used. Is spreading.
이와 같은 전자기기의 소형화, 경량화 및 박형화 경향에 맞추어 이들에게 전력을 공급하는 이차전지에 대해서도 고성능화가 요구되고 있다. 즉, 기존의 납축전지 또는 니켈-카드뮴 전지 등을 대체할 수 있으며, 소형화 및 경량화되면서 에너지 밀도가 높고, 반복해서 충방전이 가능한 리튬 이차전지 (Lithium Rechargeable Batteries)의 개발이 급속하게 진행되고 있다.In accordance with the trend toward miniaturization, weight reduction and thinning of such electronic devices, high performance is also required for secondary batteries that supply power to them. That is, it is possible to replace the existing lead acid battery or nickel-cadmium battery, etc., and the development of lithium secondary batteries (Lithium Rechargeable Batteries) that have high energy density and repeatable charge / discharge while being miniaturized and lightweight.
리튬 이차전지는 리튬 이온의 삽입(intercalation) 및 탈리(deintercalation)가 가능한 물질을 활물질로 사용하여 제조한 양극 또는 음극과, 그 사이에 리튬 이온이 이동할 수 있는 유기 전해액 또는 고분자 전해질을 사용하여 제조한 전지로서, 리튬 이온이 상기 양극 및 음극에서 삽입/탈리 될 때의 산화/환원 반응에 의해 전기에너지를 생성한다.A lithium secondary battery is prepared by using a positive electrode or a negative electrode made of a material capable of intercalation and deintercalation of lithium ions as an active material, and an organic electrolyte or polymer electrolyte in which lithium ions can move between them. As a battery, electric energy is generated by an oxidation / reduction reaction when lithium ions are inserted / desorbed at the positive and negative electrodes.
리튬 이차전지의 양극은 리튬의 전극 전위보다 약 3 ∼ 4.5V 높은 전위를 나타내며, 리튬 이온의 삽입/탈리가 가능한 전이 금속과 리튬과의 복합 산화물이 주로 사용된다. 그 예로서 리튬코발트옥사이드(LiCoO2), 리튬니켈옥사이드(LiNiO2), 리튬망간옥사이드(LiMnO2) 등을 들 수 있다. 또한, 음극은 구조적, 전기적 성질을유지하면서 리튬 이온을 가역적으로 받아들이거나 공급할 수 있는 리튬 금속 또는 리튬 합금, 또는 리튬 이온의 삽입/탈리시의 케미칼 포텐셜이 금속 리튬과 거의 유사한 탄소계 물질이 주로 사용된다.The positive electrode of a lithium secondary battery has a potential of about 3 to 4.5 V higher than the electrode potential of lithium, and a complex oxide of a transition metal and lithium capable of insertion / desorption of lithium ions is mainly used. Examples thereof include lithium cobalt oxide (LiCoO 2 ), lithium nickel oxide (LiNiO 2 ), lithium manganese oxide (LiMnO 2 ), and the like. In addition, the cathode is mainly made of lithium metal or lithium alloy capable of reversibly accepting or supplying lithium ions while maintaining structural and electrical properties, or a carbon-based material having a chemical potential similar to that of metallic lithium upon insertion / deletion of lithium ions. do.
리튬 이차전지는 전해질의 종류에 따라 구별되는데, 액체 전해질을 사용하는 종래의 리튬 이온 전지(Lithium Ion Battery, LIB)와 구분하여 고분자 전해질을 사용하는 것을 리튬 고분자 전지(Lithium Polymer Battery, LPB)라고 한다. 액체 전해질을 이용하는 리튬 이온 전지는 안정성 문제가 제기되고 있어 이를 보완한 전극물질과 안전 장치를 장착하는 방법 등이 대안으로 제시되고 있다. 그러나, 제조 단가가 비싸고 대용량화하기 곤란하다는 문제점이 있다. 이에 반해, 리튬 고분자 전지는 보다 저렴한 비용으로 제조할 수 있고, 크기나 모양을 원하는 대로 조절할 수 있으며, 안전하고 단위 중량당 에너지 밀도가 높으며, 적층에 의해 고전압화, 대용량화가 가능하다는 많은 장점을 지니고 있어 차세대 첨단 전지로서 주목받고 있다.Lithium secondary batteries are classified according to the type of electrolyte, and a polymer electrolyte is distinguished from a lithium ion battery (LIB) using a liquid electrolyte and is called a lithium polymer battery (LPB). . Lithium ion batteries using liquid electrolytes have raised stability issues, and alternatively, electrode materials and safety devices installed therein have been proposed. However, there is a problem that the manufacturing cost is expensive and difficult to increase the capacity. In contrast, lithium polymer batteries can be manufactured at a lower cost, can be sized and shaped as desired, are safe, have high energy density per unit weight, and have high voltage and large capacity by lamination. It is attracting attention as a next generation advanced battery.
리튬 고분자 전지가 상업화되기 위해 고분자 전해질이 갖추어야 할 요건으로는 우선 이온 전도 특성, 기계적 물성 및 리튬 전극과의 계면 안정성 등이 우수해야 함을 들 수 있다. 따라서, 이러한 요건을 만족하는 고분자 전해질을 개발하고자 하는 연구가 많이 진행되고 있다. 초기에는 주로 폴리에틸렌옥사이드, 폴리프로필렌옥사이드 등에 염을 첨가한 후 공용매에 녹여 캐스팅하여 제조하는 무용매계 고분자 전해질 (참조: 유럽 특허 제78505호 및 미합중국 특허 제5,102,752호)에 관한 연구가 오랫동안 진행되어 왔으나, 이들은 상온 전도도가 매우 낮다는 문제점이 있었다.In order for the lithium polymer battery to be commercialized, the polymer electrolyte must first have excellent ion conduction properties, mechanical properties, and interface stability with a lithium electrode. Therefore, many studies have been conducted to develop polymer electrolytes satisfying these requirements. Initially, studies on solvent-free polymer electrolytes (refer to European Patent No. 78505 and U.S. Patent No. 5,102,752) mainly made by adding salt to polyethylene oxide, polypropylene oxide, and then melting and casting in a co-solvent have been conducted for a long time. However, these have the problem that the room temperature conductivity is very low.
다른 예로서, 폴리아크릴로니트릴, 폴리메틸메타크릴레이트, 폴리비닐클로라이드, 폴리비닐리덴플루오라이드 등의 범용성 고분자에 에틸렌카보네이드, 프로필렌카보네이트 등의 유기 용매를 염 및 공용매와 함께 녹여 필름의 형태로 제조하여 10-3S/cm 이상의 높은 이온 전도도를 나타내는 젤 고분자 전해질들에 관한 연구가 진행되었다 (참조: K.M. Abraham et al., J. Electrochem. Soc., 142, 1789, 1995). 그러나, 이러한 젤 고분자 전해질은 첨가된 유기 용매의 양에 따라 기계적 물성이 열화되는 단점이 있고, 실제로 리튬 고분자 전지에 적용되었을 때 특수한 공정 조건 및 공용매의 제거 등 자동화 공정과 관련된 부분에 있어서 많은 문제점을 안고 있다.As another example, organic solvents such as ethylene carbonate and propylene carbonate are dissolved in a general-purpose polymer such as polyacrylonitrile, polymethyl methacrylate, polyvinyl chloride, and polyvinylidene fluoride together with salts and cosolvents to form a film. A study has been made on gel polymer electrolytes prepared in the present invention having high ionic conductivity of 10 −3 S / cm or more (KM Abraham et al., J. Electrochem. Soc., 142, 1789, 1995). However, these gel polymer electrolytes have a disadvantage in that mechanical properties deteriorate according to the amount of added organic solvent, and when applied to a lithium polymer battery, many problems are associated with the automation process such as removal of special process conditions and cosolvents. Is holding.
최근에는, 다공성 고분자 매트릭스를 먼저 제조하고, 이를 양극 및 음극과 적층한 후, 얻어진 필름을 액체 전해질에 함침시키는 방법이 제안되었다 (참조: J.M. Tarascon et al., Solid State Ionics, 86-88, 49, 1996, 미합중국 특허 제5,456,000호).Recently, a method of preparing a porous polymer matrix first, laminating it with a positive electrode and a negative electrode, and then impregnating the obtained film with a liquid electrolyte has been proposed (see JM Tarascon et al., Solid State Ionics, 86-88, 49). , 1996, United States Patent No. 5,456,000).
상기 고분자 매트릭스의 재료로 널리 사용되는 비닐리덴플루오라이드계 공중합체는 전기화학적으로는 안정적이나, 낮은 표면 에너지, 액체 전해질과의 낮은 친화성 등으로 인해 전해액의 함침 특성이 그리 좋지 않다. 또한, 시간 경과 및 충방전의 지속에 따라 전지 내에서 액체 전해질이 스며 나오고 휘발하는 현상이 발생한다. 이는 고분자 매트릭스의 이온 전도도의 저하 뿐 만 아니라 전지의 전체 저항을 증가시키는 결과를 초래하여, 결국 장시간 후 용량의 지속적인 감소 및 고율충방전 특성을 저하시키는 근본적인 원인이 된다.The vinylidene fluoride-based copolymer widely used as a material of the polymer matrix is electrochemically stable, but the impregnation characteristics of the electrolyte are not very good due to low surface energy and low affinity with the liquid electrolyte. In addition, as the time elapses and the charge and discharge continue, the liquid electrolyte leaks out and evaporates in the battery. This not only lowers the ionic conductivity of the polymer matrix but also increases the overall resistance of the battery, which eventually becomes a fundamental cause of the continuous reduction of capacity and high rate charge / discharge characteristics after a long time.
본 발명의 목적은 상기한 바와 같은 종래 기술에서의 문제점들을 해결하고자 하는 것으로서, 다공성 고분자 매트릭스를 기초로 하여 간단한 제조 공정에 의하여 얻어질 수 있으며, 우수한 이온 전도도 및 양이온 수율 특성을 제공할 수 있는 고분자 전해질의 제조 방법을 제공하는 것이다.An object of the present invention is to solve the problems in the prior art as described above, can be obtained by a simple manufacturing process based on a porous polymer matrix, a polymer that can provide excellent ionic conductivity and cation yield properties It is to provide a method for producing an electrolyte.
본 발명의 다른 목적은 전해질 내에서 전해액의 함침 및 유지 특성을 향상시킬 수 있고, 양이온 수율을 향상시킬 수 있으며, 이온 전도도를 향상시킬 수 있는 고분자 전해질을 제공하는 것이다.Another object of the present invention is to provide a polymer electrolyte capable of improving the impregnation and retention characteristics of the electrolyte in the electrolyte, improving the cation yield, and improving the ionic conductivity.
도 1은 본 발명의 바람직한 실시예에 따른 고분자 전해질의 제조 방법을 설명하기 위한 플로차트이다.1 is a flowchart illustrating a method of manufacturing a polymer electrolyte according to a preferred embodiment of the present invention.
도 2는 본 발명의 바람직한 실시예들에 따른 고분자 전해질에서 양이온성 고분자의 함량에 따른 액체 전해질의 함침량을 나타낸 그래프이다.2 is a graph showing the impregnation amount of the liquid electrolyte according to the content of the cationic polymer in the polymer electrolyte according to the preferred embodiments of the present invention.
도 3은 본 발명의 바람직한 실시예들에 따른 고분자 전해질에서 양이온성 고분자의 함량에 따른 이온 전도도를 나타낸 그래프이다.3 is a graph showing the ion conductivity according to the content of the cationic polymer in the polymer electrolyte according to the preferred embodiments of the present invention.
도 4는 본 발명의 바람직한 실시예들에 따른 고분자 전해질에서 양이온성 고분자의 함량에 따른 양이온 수율을 나타낸 그래프이다.4 is a graph showing the cation yield according to the content of the cationic polymer in the polymer electrolyte according to the preferred embodiments of the present invention.
상기 목적을 달성하기 위하여, 본 발명에 따른 고분자 전해질의 제조 방법에서는 아크릴로니트릴 반복 단위를 포함하는 고분자 및 양이온성 고분자를 브렌딩하여 고분자 브렌드를 준비한다. 상기 고분자 브렌드 및 무기물을 공용매에 용해시켜 고분자 브렌드 용액을 제조한다. 상전환법에 의해 상기 고분자 브렌드 용액으로부터 다공성 고분자 필름을 형성한다. 상기 다공성 고분자 필름을 리튬염이 용해된 전해액에 함침시킨다.In order to achieve the above object, in the method for producing a polymer electrolyte according to the present invention, a polymer blend is prepared by blending a polymer including an acrylonitrile repeating unit and a cationic polymer. The polymer blend and the inorganic material are dissolved in a cosolvent to prepare a polymer blend solution. A porous polymer film is formed from the polymer blend solution by a phase inversion method. The porous polymer film is impregnated into an electrolyte solution in which lithium salt is dissolved.
상기 아크릴로니트릴 반복 단위를 포함하는 고분자는 폴리아크릴로니트릴, 아크릴로니트릴과 부타디엔의 공중합체, 아크릴로니트릴과 메타크릴로니트릴의 공중합체, 아크릴로니트릴과 메틸아크릴레이트의 공중합체, 아크릴로니트릴과 부타디엔과 아크릴산의 삼원공중합체, 아크릴로니트릴과 부타디엔과 스티렌의 삼원공중합체, 및 아크릴로니트릴과 비닐리덴클로라이드와 메틸메타크릴레이트의 삼원공중합체로 이루어지는 군에서 선택되는 어느 하나로 이루어진다.The polymer containing the acrylonitrile repeating unit may be a polyacrylonitrile, a copolymer of acrylonitrile and butadiene, a copolymer of acrylonitrile and methacrylonitrile, a copolymer of acrylonitrile and methyl acrylate, and acryl Terpolymers of nitrile, butadiene and acrylic acid, terpolymers of acrylonitrile, butadiene and styrene, and terpolymers of acrylonitrile, vinylidene chloride and methyl methacrylate.
상기 양이온성 고분자는 폴리에틸렌이민, 폴리라이신, 폴리에틸비닐피리디늄 브로마이드, 폴리디메틸아미노에틸메타크릴레이트 및 폴리오르니틴으로 이루어지는 군에서 선택되는 어느 하나로 이루어진다.The cationic polymer is made of any one selected from the group consisting of polyethyleneimine, polylysine, polyethylvinylpyridinium bromide, polydimethylaminoethyl methacrylate and polyornithine.
상기 고분자 브렌드중 아크릴로니트릴 반복 단위를 포함하는 고분자와 양이온성 고분자와의 중량비는 99:1 ∼ 1:99의 범위 내에서 선택 가능하다.The weight ratio of the polymer containing the acrylonitrile repeating unit and the cationic polymer in the polymer blend can be selected within the range of 99: 1 to 1:99.
상기 무기물은 실리카, 탈크, 알루미나(Al2O3), γ-LiAlO2, TiO2, 제올라이트 또는 이들의 혼합물로 이루어진다.The inorganic material consists of silica, talc, alumina (Al 2 O 3 ), γ-LiAlO 2 , TiO 2 , zeolite or mixtures thereof.
상기 공용매는 디메틸포름아마이드, 디메틸설폭사이드, N-메틸피롤리돈 또는 이들의 혼합물로 이루어진다.The cosolvent consists of dimethylformamide, dimethylsulfoxide, N-methylpyrrolidone or mixtures thereof.
본 발명에 따른 고분자 전해질의 제조 방법에 있어서, 상기 다공성 고분자 필름을 형성하기 위하여, 상기 고분자 브렌드 용액을 캐스팅한다. 상기 캐스팅된 고분자 브렌드 용액을 비용매에 함침시켜 고분자 필름을 형성한다. 상기 고분자 필름을 라미네이션하여 상기 다공성 고분자 필름을 형성한다.In the method for producing a polymer electrolyte according to the present invention, in order to form the porous polymer film, the polymer blend solution is cast. The cast polymer blend solution is impregnated into a non-solvent to form a polymer film. The polymer film is laminated to form the porous polymer film.
상기 비용매는 물, 에탄올, 메탄올, 아세톤, 디에틸에테르, 헥산 또는 이들의 혼합물로 이루어진다.The nonsolvent consists of water, ethanol, methanol, acetone, diethyl ether, hexane or mixtures thereof.
상기 전해액은 에틸렌카보네이트, 프로필렌카보네이트, 디메틸카보네이트, 디에틸카보네이트, 메틸에틸카보네이트, 테트라하이드로퓨란, 2-메틸테트라하이드로퓨란, 디메톡시에탄, 메틸포르메이트, 에틸포르메이트, 감마-부티로락톤 또는 이들의 혼합물로 이루어진다.The electrolyte solution is ethylene carbonate, propylene carbonate, dimethyl carbonate, diethyl carbonate, methyl ethyl carbonate, tetrahydrofuran, 2-methyltetrahydrofuran, dimethoxyethane, methyl formate, ethyl formate, gamma-butyrolactone or these It consists of a mixture of
상기 리튬염은 리튬퍼클로레이트(LiClO4), 리튬트리플레이트(LiCF3SO3), 리튬헥사플루오로포스페이트(LiPF6), 리튬테트라플루오로보레이트(LiBF4), 리튬트리플루오로메탄설포닐이미드(LiN(CF3SO2)2) 또는 이들의 혼합물로 이루어진다.The lithium salt is lithium perchlorate (LiClO 4 ), lithium triflate (LiCF 3 SO 3 ), lithium hexafluorophosphate (LiPF 6 ), lithium tetrafluoroborate (LiBF 4 ), lithium trifluoromethanesulfonylimide (LiN (CF 3 SO 2 ) 2 ) or mixtures thereof.
상기 다른 목적을 달성하기 위하여, 상기 기술한 바와 같은 방법으로부터 얻어진 고분자 전해질을 제공한다.In order to achieve the above another object, there is provided a polymer electrolyte obtained from the method as described above.
본 발명에 따른 고분자 전해질은 기계적 물성이 우수한 아크릴로니트릴 반복 단위를 포함하는 고분자와 양이온성 고분자가 혼합된 고분자 브렌드를 이용하여 제조된 다공성 고분자로부터 얻어지는 것으로, 양이온성 고분자가 브렌드 형태로 도입되어 음이온과의 상호 작용력이 증대되어 양이온 수율이 향상되고, 리튬염의 해리도가 증가되기 때문에 이온 전도도가 증가될 수 있다. 또한, 유기 용매와 다공성 고분자 매트릭스 간의 상용성이 증대되어 누액 현상이 방지되며, 리튬 전극과의 접촉시 음이온 분해의 억제에 의한 계면 저항의 증가가 억제될 수 있다.The polymer electrolyte according to the present invention is obtained from a porous polymer prepared by using a polymer blend including a polymer containing an acrylonitrile repeating unit having excellent mechanical properties and a cationic polymer, and the cationic polymer is introduced in a blend form to form an anion. Since the interaction force with the cation increases, the cation yield is improved, and the dissociation degree of the lithium salt is increased, thereby increasing the ionic conductivity. In addition, the compatibility between the organic solvent and the porous polymer matrix is increased to prevent leakage, and an increase in interfacial resistance due to suppression of anion decomposition upon contact with the lithium electrode may be suppressed.
본 명세서에서는 본 발명에 의한 고분자 재료를 리튬 이차전지용 고분자 전해질로서 사용하는 경우를 예로 들어 설명하고 있으나, 본 발명은 이에 한정되지 않으며, 비수계 이차전지용 고분자 매트릭스, 고분자 전해질 또는 분리막 등의 용도로 광범위하게 응용될 수 있다.In the present specification, a case in which the polymer material according to the present invention is used as a polymer electrolyte for a lithium secondary battery has been described as an example, but the present invention is not limited thereto, and the present invention is not limited thereto. Can be applied.
다음에, 본 발명의 바람직한 실시예들에 대하여 첨부 도면을 참조하여 상세히 설명한다. 하기 실시예들은 본 발명의 이해를 돕기 위하여 예시한 것에 불과하며, 본 발명의 범위가 이에 한정되는 것으로 해석되어져서는 안된다.Next, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. The following examples are merely illustrated to aid the understanding of the present invention, and the scope of the present invention should not be construed as being limited thereto.
도 1은 본 발명의 바람직한 실시예에 따른 고분자 전해질의 제조 방법을 설명하기 위한 플로차트이다.1 is a flowchart illustrating a method of manufacturing a polymer electrolyte according to a preferred embodiment of the present invention.
도 1을 참조하면, 먼저 아크릴로니트릴 반복 단위를 포함하는 고분자 및 양이온성 고분자를 브렌딩하여 고분자 브렌드를 준비한다 (단계 10).Referring to FIG. 1, first, a polymer blend is prepared by blending a polymer including an acrylonitrile repeating unit and a cationic polymer (step 10).
상기 아크릴로니트릴 반복 단위를 포함하는 고분자는 폴리아크릴로니트릴, 아크릴로니트릴과 부타디엔의 공중합체, 아크릴로니트릴과 메타크릴로니트릴의 공중합체, 아크릴로니트릴과 메틸아크릴레이트의 공중합체, 아크릴로니트릴과 부타디엔과 아크릴산의 삼원공중합체, 아크릴로니트릴과 부타디엔과 스티렌의 삼원공중합체, 및 아크릴로니트릴과 비닐리덴클로라이드와 메틸메타크릴레이트의 삼원공중합체로 이루어지는 군에서 선택되는 어느 하나로 이루어질 수 있다.The polymer containing the acrylonitrile repeating unit may be a polyacrylonitrile, a copolymer of acrylonitrile and butadiene, a copolymer of acrylonitrile and methacrylonitrile, a copolymer of acrylonitrile and methyl acrylate, and acryl Terpolymers of nitrile, butadiene and acrylic acid, terpolymers of acrylonitrile, butadiene and styrene, and terpolymers of acrylonitrile, vinylidene chloride and methyl methacrylate. .
상기 양이온성 고분자는 폴리에틸렌이민, 폴리라이신, 폴리에틸비닐피리디늄 브로마이드, 폴리디메틸아미노에틸메타크릴레이트 또는 폴리오르니틴으로 이루어질 수 있다.The cationic polymer may be made of polyethyleneimine, polylysine, polyethylvinylpyridinium bromide, polydimethylaminoethyl methacrylate or polyornithine.
상기 고분자 브렌드중 아크릴로니트릴 반복 단위를 포함하는 고분자와 양이온성 고분자와의 중량비는 99:1 ∼ 1:99의 범위 내에서 다양하게 선택될 수 있다. 또한, 상기 고분자 브렌드중 아크릴로니트릴 반복 단위를 포함하는 고분자 및 양이온성 고분자는 각각 분자량에 있어서 제한이 없으며, 예를 들면 10,000 ∼ 1,000,000의 범위에서 다양하게 선택될 수 있다. 상기 아크릴로니트릴 반복 단위를 포함하는 고분자 내에서 아크릴로니트릴의 함량은 30 ∼ 99몰%의 범위로 하는 것이 바람직하다.The weight ratio of the polymer including the acrylonitrile repeating unit in the polymer blend and the cationic polymer may be variously selected within the range of 99: 1 to 1:99. In addition, the polymer and the cationic polymer including the acrylonitrile repeating unit in the polymer blend is not limited in each molecular weight, for example, may be variously selected in the range of 10,000 to 1,000,000. The content of acrylonitrile in the polymer containing the acrylonitrile repeating unit is preferably in the range of 30 to 99 mol%.
상기와 같이 제조된 고분자 브렌드와 무기물을 공용매에 용해시켜 고분자 브렌드 용액을 제조한다 (단계 20). 여기서, 상기 무기물은 상기 고분자 브렌드로부터 후속 공정에서 얻어지는 고분자 필름의 기계적 물성을 증가시키기 위하여 첨가되는 것으로, 예를 들면 실리카, 탈크, 알루미나(Al2O3), γ-LiAlO2, TiO2, 제올라이트 또는 이들의 혼합물로 이루어질 수 있다.A polymer blend solution prepared as described above is dissolved in a cosolvent to prepare a polymer blend solution (step 20). Here, the inorganic material is added to increase the mechanical properties of the polymer film obtained in a subsequent process from the polymer blend, for example, silica, talc, alumina (Al 2 O 3 ), γ-LiAlO 2 , TiO 2 , zeolite Or a mixture thereof.
상기 무기물은 고분자의 중량을 기준으로 1 ∼ 1000 중량%, 바람직하게는 1 ∼ 500 중량의 양으로 함유될 수 있다.The inorganic material may be contained in an amount of 1 to 1000% by weight, preferably 1 to 500% by weight, based on the weight of the polymer.
상기 공용매는 디메틸포름아마이드, 디메틸설폭사이드, N-메틸피롤리돈 또는 이들의 혼합물로 이루어진다.The cosolvent consists of dimethylformamide, dimethylsulfoxide, N-methylpyrrolidone or mixtures thereof.
단계 20에서 제조된 고분자 브렌드 용액을 이용하여 상전환법에 의해 다공성 고분자 필름을 형성한다 (단계 30). 보다 구체적으로 설명하면, 먼저 상기 고분자 브렌드 용액을 유리판에 캐스팅하고, 상기 캐스팅된 고분자 브렌드 용액을 비용매에 함침시켜 고분자 필름을 형성한다. 그 후, 상기 고분자 필름을 라미네이션하여 원하는 다공성 고분자 필름을 형성한다.Using the polymer blend solution prepared in step 20 to form a porous polymer film by the phase inversion method (step 30). More specifically, first, the polymer blend solution is cast on a glass plate, and the cast polymer blend solution is impregnated into a non-solvent to form a polymer film. Thereafter, the polymer film is laminated to form a desired porous polymer film.
상기 비용매는 물, 에탄올, 메탄올, 아세톤, 디에틸에테르, 헥산 또는 이들의 혼합물로 이루어질 수 있다.The non-solvent may be composed of water, ethanol, methanol, acetone, diethyl ether, hexane or a mixture thereof.
상기 다공성 고분자 필름을 리튬염이 용해된 전해액에 함침시켜, 상기 다공성 고분자 필름에 상기 전해액을 담지시킨다 (단계 40).The porous polymer film is impregnated in an electrolyte solution in which lithium salt is dissolved, and the electrolyte solution is supported on the porous polymer film (step 40).
상기 전해액으로는 리튬 전지에 관한 기술 분야에서 널리 알려져 있는 것이면 어느 것이나 사용 가능하며, 본 발명에서 사용 가능한 구체적인 예를 들면 에틸렌카보네이트, 프로필렌카보네이트, 디메틸카보네이트, 디에틸카보네이트, 메틸에틸카보네이트, 테트라하이드로퓨란, 2-메틸테트라하이드로퓨란, 디메톡시에탄, 메틸포르메이트, 에틸포르메이트, 감마-부티로락톤 또는 이들의 혼합물을 사용할 수 있다. 상기 전해액은 고분자의 중량을 기준으로 1 ∼ 2000 중량%, 바람직하게는 1 ∼ 1000 중량%의 양으로 사용될 수 있다.As the electrolyte solution, any one can be used as long as it is widely known in the technical field of a lithium battery, and specific examples that can be used in the present invention include ethylene carbonate, propylene carbonate, dimethyl carbonate, diethyl carbonate, methyl ethyl carbonate, and tetrahydrofuran. , 2-methyltetrahydrofuran, dimethoxyethane, methylformate, ethylformate, gamma-butyrolactone or mixtures thereof can be used. The electrolyte may be used in an amount of 1 to 2000 wt%, preferably 1 to 1000 wt%, based on the weight of the polymer.
본 발명에서 사용 가능한 리튬염의 예를 들면, 리튬퍼클로레이트(LiClO4), 리튬트리플레이트(LiCF3SO3), 리튬헥사플루오로포스페이트(LiPF6), 리튬테트라플루오로보레이트(LiBF4), 리튬트리플루오로메탄설포닐이미드(LiN(CF3SO2)2) 등이 있으며, 이들의 혼합물을 사용하는 것도 가능하다. 상기 리튬염은 고분자의 중량을 기준으로 1 ∼ 200 중량%, 바람직하게는 1 ∼ 100 중량%의 양으로 사용될 수 있다.Examples of lithium salts usable in the present invention include lithium perchlorate (LiClO 4 ), lithium triplate (LiCF 3 SO 3 ), lithium hexafluorophosphate (LiPF 6 ), lithium tetrafluoroborate (LiBF 4 ), and lithium tree Fluoromethanesulfonylimide (LiN (CF 3 SO 2 ) 2 ), and the like, and mixtures thereof may be used. The lithium salt may be used in an amount of 1 to 200% by weight, preferably 1 to 100% by weight, based on the weight of the polymer.
다음에, 상기 설명한 바와 같은 본 발명에 따른 고분자 전해질의 제조 방법을 구체적으로 구현한 실시예들에 대하여 설명한다.Next, exemplary embodiments of the method for manufacturing the polymer electrolyte according to the present invention as described above will be described in detail.
실시예 1Example 1
아크릴로니트릴 반복 단위를 포함하는 고분자인 폴리아크릴로니트릴과, 양이온성 고분자인 폴리에틸렌이민(PEI)을 중량비가 95:5가 되도록 혼합하고 디메틸설폭사이드에 녹여 균일한 용액을 얻었다. 여기에 상기 사용된 고분자의 중량을 기준으로 20중량%의 TiO2를 첨가하였다. 그 결과 얻어진 고분자 브렌드 용액을 유리판에 캐스팅하고, 즉시 비용매인 물에 함침시켜 상전환법에 의해 필름 형상을 얻었다. 얻어진 필름내의 비용매를 증발시킨 후, 진공 건조시켜 다공성 고분자 필름을 형성하였다. 이와 같이 얻어진 다공성 고분자 필름에 대하여 라미네이션 공정을 거쳐 두께가 30 m 이하가 되게 조절하였다. 제조된 필름을 아르곤 분위기의 글로브박스로 옮겼다. 그 후, 에틸렌카보네이트 및 프로필렌카보네이트가 1:1의 몰비로 혼합된 혼합 용매를 제조하고, 여기에 리튬헥사플루오로포스페이트를 1몰 농도가 되도록 첨가한 후, 여기에 상기 얻어진 다공성 고분자 필름을 함침시켜 원하는 고분자 전해질을 제조하였다.Polyacrylonitrile, which is a polymer containing acrylonitrile repeating units, and polyethyleneimine (PEI), which is a cationic polymer, were mixed in a weight ratio of 95: 5, and dissolved in dimethyl sulfoxide to obtain a uniform solution. To this was added 20% by weight of TiO 2 based on the weight of the polymer used. The resulting polymer blend solution was cast on a glass plate and immediately impregnated with water, which is nonsolvent, to obtain a film shape by a phase inversion method. The nonsolvent in the obtained film was evaporated and then dried in vacuo to form a porous polymer film. The porous polymer film thus obtained was adjusted to have a thickness of 30 m or less through a lamination process. The prepared film was transferred to an argon atmosphere glove box. Thereafter, a mixed solvent in which ethylene carbonate and propylene carbonate were mixed at a molar ratio of 1: 1 was prepared, and lithium hexafluorophosphate was added thereto at a 1 molar concentration, and then the porous polymer film obtained was impregnated therein. The desired polymer electrolyte was prepared.
실시예 2Example 2
아크릴로니트릴 반복 단위를 포함하는 고분자인 폴리아크릴로니트릴과, 양이온성 고분자인 폴리에틸렌이민(PEI)을 중량비가 90:10인 것을 제외하고, 실시예 1에서와 동일한 방법으로 고분자 전해질을 제조하였다.A polymer electrolyte was prepared in the same manner as in Example 1, except that polyacrylonitrile, which is a polymer including an acrylonitrile repeating unit, and polyethyleneimine (PEI), which is a cationic polymer, had a weight ratio of 90:10.
실시예 3Example 3
아크릴로니트릴 반복 단위를 포함하는 고분자인 폴리아크릴로니트릴과, 양이온성 고분자인 폴리에틸렌이민(PEI)을 중량비가 85:15인 것을 제외하고, 실시예 1에서와 동일한 방법으로 고분자 전해질을 제조하였다.A polyelectrolyte was prepared in the same manner as in Example 1, except that polyacrylonitrile, which is a polymer including an acrylonitrile repeating unit, and polyethyleneimine (PEI), which is a cationic polymer, had a weight ratio of 85:15.
실시예 4Example 4
아크릴로니트릴 반복 단위를 포함하는 고분자인 폴리아크릴로니트릴과, 양이온성 고분자인 폴리에틸렌이민(PEI)을 중량비가 80:20인 것을 제외하고, 실시예 1에서와 동일한 방법으로 고분자 전해질을 제조하였다.A polymer electrolyte was prepared in the same manner as in Example 1, except that polyacrylonitrile, which is a polymer including an acrylonitrile repeating unit, and polyethyleneimine (PEI), which is a cationic polymer, had a weight ratio of 80:20.
비교예Comparative example
아크릴로니트릴계 고분자 만을 사용한 것을 제외하고, 실시예 1에서와 동일한 방법으로 고분자 전해질을 제조하였다.A polymer electrolyte was prepared in the same manner as in Example 1, except that only acrylonitrile-based polymer was used.
도 2는 실시예 1 내지 실시예 4 및 비교예에서 얻어진 결과로부터, 양이온성 고분자인 폴리에틸렌이민(PEI)의 함량에 따른 다공성 매트릭스 내로의 전해액의 함침 특성을 나타낸 그래프이다.2 is a graph showing the impregnation characteristics of the electrolyte solution into the porous matrix according to the content of polyethyleneimine (PEI), which is a cationic polymer, from the results obtained in Examples 1 to 4 and Comparative Examples.
본 발명에 따른 실시예 1 내지 실시예 4의 경우는 비교예에서 얻어진 고분자 전해질의 경우보다 함침률이 높고, 양이온성 고분자의 함량이 증가할수록 함침률이 증가하였다. 이는 다공성 고분자 매트릭스 내에 존재하는 양이온성기와 전해액간의 상호 작용의 증가에 의한 것임을 알 수 있다.In Examples 1 to 4 according to the present invention, the impregnation rate is higher than that of the polymer electrolyte obtained in the comparative example, and the impregnation rate increases as the content of the cationic polymer increases. It can be seen that this is due to the increase in the interaction between the cationic group and the electrolyte in the porous polymer matrix.
도 3은 실시예 1 내지 실시예 4 및 비교예에서 얻어진 결과로부터, 양이온성 고분자인 폴리에틸렌이민(PEI)의 함량에 따른 이온 전도 특성을 나타낸 그래프이다. 도 3의 결과로부터, 본 발명에 따른 실시예 1 내지 실시예 4의 경우는 각각 상온에서 비교예의 경우보다 10-3S/cm를 훨씬 상회하는 높은 이온 전도도를 나타내는 것을 알 수 있다.Figure 3 is a graph showing the ion conduction properties according to the content of polyethyleneimine (PEI) as a cationic polymer from the results obtained in Examples 1 to 4 and Comparative Examples. From the results of FIG. 3, it can be seen that in Examples 1 to 4 according to the present invention, each exhibits high ionic conductivity far higher than 10 −3 S / cm at room temperature than in the comparative example.
도 4는 실시예 1 내지 실시예 4 및 비교예에서 얻어진 결과로부터, 양이온성 고분자인 폴리에틸렌이민(PEI)의 함량에 따른 양이온 수율 (transference number)을 나타낸 그래프이다. 도 4의 결과로부터, 본 발명에 따른 실시예 1 내지 실시예 4의 경우는 각각 양이온성 고분자의 함량이 증가할수록 양이온 수율이 증가하는 것을 알 수 있다. 이는, 브렌드된 양이온성 고분자가 전해액 내의 음이온들을 효과적으로 잡아주기 때문이라는 것을 알 수 있다.Figure 4 is a graph showing the cation yield (transference number) according to the content of polyethyleneimine (PEI) as a cationic polymer from the results obtained in Examples 1 to 4 and Comparative Examples. 4, it can be seen that in Examples 1 to 4 according to the present invention, the cation yield increases as the content of the cationic polymer increases. It can be seen that the blended cationic polymer effectively traps the anions in the electrolyte.
본 발명에 따른 고분자 전해질에서는 기계적 물성이 우수한 아크릴로니트릴 반복 단위를 포함하는 고분자와 양이온성 고분자가 혼합된 고분자 브렌드를 이용하여 제조된 다공성 고분자 필름에 리튬염이 용해된 전해액을 함침시켜 얻어지는 것으로, 양이온성 고분자가 브렌드 형태로 도입되어 음이온과의 상호 작용력이 증대되어 양이온 수율이 향상되고, 리튬염의 해리도가 증가되기 때문에 이온 전도도가 증가될 수 있다. 또한, 유기 용매와 다공성 고분자 매트릭스 간의 상용성이 증대되어 누액 현상이 방지되며, 리튬 전극과의 접촉시 음이온 분해의 억제에 의한 계면 저항의 증가가 억제될 수 있다. 또한, 본 발명에 따른 고분자 전해질의 제조 방법은 기존의 젤 고분자 전해질에 비하여 제조가 용이하며, 다공성 고분자 매트릭스를 기초로 하여, 상전환법에 의한 간단한 제조 공정에 의하여 우수한 이온 전도도 및 양이온 수율 특성을 제공할 수 있는 고분자 전해질을 얻을 수 있다.In the polymer electrolyte according to the present invention, it is obtained by impregnating an electrolyte solution in which lithium salt is dissolved in a porous polymer film prepared by using a polymer blend including a polymer containing an acrylonitrile repeating unit having excellent mechanical properties and a cationic polymer. Since the cationic polymer is introduced in the form of a blend and the interaction force with the anion is increased, the cation yield is improved, and the dissociation degree of the lithium salt is increased, thereby increasing the ionic conductivity. In addition, the compatibility between the organic solvent and the porous polymer matrix is increased to prevent leakage, and an increase in interfacial resistance due to suppression of anion decomposition upon contact with the lithium electrode may be suppressed. In addition, the manufacturing method of the polymer electrolyte according to the present invention is easier to prepare than the conventional gel polymer electrolyte, and based on the porous polymer matrix, excellent ion conductivity and cation yield characteristics by a simple manufacturing process by the phase inversion method A polymer electrolyte that can be provided can be obtained.
이상, 본 발명을 바람직한 실시예를 들어 상세하게 설명하였으나, 본 발명은 상기 실시예에 한정되지 않고, 본 발명의 기술적 사상의 범위 내에서 당 분야에서 통상의 지식을 가진 자에 의하여 여러가지 변형이 가능하다.The present invention has been described in detail with reference to preferred embodiments, but the present invention is not limited to the above embodiments, and various modifications can be made by those skilled in the art within the scope of the technical idea of the present invention. Do.
Claims (11)