KR100434800B1 - 우레탄/아크릴레이트 하이브리드 고무계 도막방수제 - Google Patents
우레탄/아크릴레이트 하이브리드 고무계 도막방수제 Download PDFInfo
- Publication number
- KR100434800B1 KR100434800B1 KR10-2001-0028971A KR20010028971A KR100434800B1 KR 100434800 B1 KR100434800 B1 KR 100434800B1 KR 20010028971 A KR20010028971 A KR 20010028971A KR 100434800 B1 KR100434800 B1 KR 100434800B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- urethane
- rubber
- water
- Prior art date
Abstract
본 발명은 건축 및 토목 구조물의 방수재료인 수성 우레탄/아크릴레이트 하이브리드 고무계 도막방수제에 관한 것으로, 100중량부의 수분산 우레탄/아크릴레이트 하이브리드 고무에 30∼50중량부의 폴리올레핀 수분산체, 15∼25중량부의 스티렌-부타디엔고무 및 20∼30중량부의 충진제로 이루어진 것을 특징으로 한다. 본 발명에 의한 방수제는 인장강도, 접착강도 및 신장율 등의 기계적 물성이 우수할 뿐만 아니라 내약품성, 내후성 및 내수성이 우수하여 건축 및 토목 구조물의 도막방수제로 이용할 수 있는 효과가 있다.
Description
본 발명은 건축 및 토목 구조물의 방수재료인 수성 우레탄/아크릴레이트 하이브리드 고무계 도막방수제에 관한 것으로, 특히 우레탄과 아크릴레이트가 혼합되어 있는 하이브리드 고무를 사용하여 기계적 특성, 내수성 및 내구성을 향상시킨 도막방수제를 제공하기 위한 것이다.
종래에는 환경공해나 독성에 대해 작업자의 안정성을 고려하여 우레탄계의 방수제가 주로 사용되었으나, 상기한 우레탄계 방수제는 디부틸프탈레이트 또는 염소화파라핀 등의 가소제가 첨가되기 때문에 시간의 경과에 따라 가소 물질이 휘발되어 본래의 고무특성이 훼손되거나 자외선에 의한 변색과 노화, 습윤면의 발포로 인해서 접착불량이 발생하며 내수성이 떨어지고 단가가 비싸다는 문제점이 있었다.
또한 아크릴고무계를 단독으로 사용한 방수제는 강도가 약하기 때문에 기계적 물성이 떨어져 방수특성이 저하되는 문제점이 있었다.
본 발명은 상기와 같은 종래기술의 문제점을 해결하기 위해 안출된 것으로,아크릴수지 만을 단독으로 사용하였을 때 보다 기계적 물성, 내약품성, 내수성 및 접착강도가 우수하고 단가가 저렴하며, 아크릴레이트 수지만을 단독으로 사용하였을 때 보다 방수성 및 내수성이 우수한 수분산 우레탄/아크릴레이트 하이브리드를 사용한 고무계 도막방수제를 제공하는데 목적이 있다.
이하, 본 발명을 상세히 설명하면 다음과 같다.
본 발명의 목적을 달성하기 위한 고무계 도막방수제는 100중량부의 수분산 우레탄/아크릴레이트 하이브리드 고무에 30∼50중량부의 폴리올레핀 수분산체, 15∼25중량부의 스티렌-부타디엔고무 및 20∼30중량부의 충진제로 이루어진 도막방수제를 제공하는 것을 특징으로 한다.
본 발명에서 '중량부'는 각 조성성분의 무게비를 표시한 것이다.
본 발명의 수분산 우레탄/아크릴레이트 하이브리드는 단일 우레탄에 비해 내수성이 우수하고 단가가 저렴하며, 단일 수분산 아크릴에 비해서는 기계적 특성, 내약품성, 내구성 및 접착강도가 우수하다. 또한 수분산 우레탄/아크릴레이트 하이브리드는 본 발명의 도막방수제에서 방수특성을 갖는 물질로서 100중량부를 사용하는 것을 기본으로 한다. 본 발명에 사용하는 수분산 우레탄/아크릴레이트 하이브리드는 20∼50%의 우레탄을 함유하고, 45%의 고형분을 유지하며, 1000∼1300cps의 점도 및 500%의 신장율을 갖는 특성이 있다.
또한, 폴리올레핀 수분산체는 내약품성, 비슬립성 및 뭉침방지성이 우수하여 각종 충진제의 혼합시 뭉침을 방지하고 도막의 내충격성과 내열성을 향상시키기 위해 사용하는 것으로 30∼50중량부가 바람직하다. 30중량부 이하이면 뭉침방지 효과를 충분히 기대할 수 없고, 50중량부 이상이면 원료를 낭비하게 된다. 본 발명에 사용하는 폴리올레핀 수분산체는 20∼50%의 고형분이 포함되어 있고, 800∼1200cps의 점도 및 1∼3㎛의 입자크기와 구형의 입자형태를 갖는 특성이 있다.
상기 폴리올레핀 수분산체는 폴리아세틸렌, 폴리아릴렌, 폴리 1-뷰텐, 폴리 1-데칸 및 폴리에틸렌 등을 사용할 수 있다.
그리고 본 발명에서 사용하는 스티렌-부타디엔 고무(SBR Latex) 또한, 방수특성을 갖는 물질로 15∼25중량부를 사용하는 것이 바람직하다. 15중량부 이하이면 방수 특성을 충분하게 발휘할 수 없게 된다. 상기한 스티렌-부타디엔 고무는 30∼50%의 스티렌고무를 함유하고 50%이상의 고형분 및 400∼800cps의 점도를 갖는 특성이 있다.
충진제는 고무계 방수제에 통상적으로 사용하는 탄산칼슘염, 탈크, 지당 및 바륨을 사용할 수 있지만, 본 발명의 우레탄/아크릴레이트와 상용성이 우수한 탄산칼슘염과 탈크를 사용하는 것이 보다 효과적이다.
또한 본 발명의 도막방수제는 방수제의 기본물성을 변화시키지 않는 범위 내에서 안료, 가소제, 분산제, 소포제, 방부제, 증점제, 보강제, 안정제 및 노화방지제를 첨가할 수 있다.
이하 실시예에 의하여 본 발명을 보다 구체적으로 설명하고자 한다. 이들 실시예는 오로지 본 발명을 설명하기 위한 것으로 본 발명의 요지에 따라 본 발명의 범위가 이들 실시예에 국한되지 않는다는 것은 당업계에서 통상의 지식을 가진 자에게 자명할 것이다.
[실시예1]
중합반응조에 100중량부의 수분산 우레탄/아크릴레이트 하이브리드 고무, 50중량부의 폴리에틸렌 수분산체, 15중량부의 스티렌-부타디엔고무 및 20중량부의 탄산칼슘염을 충진제로 첨가하고 1000rpm의 속도로 4시간동안 상온에서 교반하여 도막방수제를 제조하였다.
[실시예2]
중합반응조에 100중량부의 수분산 우레탄/아크릴레이트 하이브리드 고무, 30중량부의 폴리에틸렌 수분산체, 25중량부의 스티렌-부타디엔고무 및 20중량부의 탄산칼슘염을 충진제로 첨가하고 1000rpm의 속도로 4시간동안 상온에서 교반하여 도막방수제를 제조하였다.
[실시예3]
중합반응조에 100중량부의 수분산 우레탄/아크릴레이트 하이브리드 고무, 30중량부의 폴리에틸렌 수분산체, 15중량부의 스티렌-부타디엔고무 및 30중량부의 탄산칼슘염을 충진제로 첨가하고 1000rpm의 속도로 4시간동안 상온에서 교반하여 도막방수제를 제조하였다.
[실시예4]
폴리에틸렌 수분산체 대신에 폴리아세틸렌을 사용한 것 이외에는 실시예1과 동일한 방법 및 동일한 중량부로 도막방수제를 제조하였다.
[실시예5]
폴리에틸렌 수분산체 대신에 폴리 1-뷰텐을 사용한 것 이외에는 실시예1과 동일한 방법 및 동일한 중량부로 도막방수제를 제조하였다.
[실시예6]
충진제로 탈크를 사용한 것 이외에는 실시예1과 동일한 방법 및 중량부로 도막방수제를 제조하였다.
이상의 각 실시예로 제조된 방수제의 성능을 평가하기 위해 KS규격, KSF 3211, KSF 4918상의 에멀젼형에 의거하여 표준상태에서 솔을 이용하여 시편에 방수제를 바른 후 상온에서 24시간 그리고 40℃에서 120시간동안 양생시킨 후 탈형하고 다시 상온에서 48시간 방치한 후 성능시험을 실시하였으며, 그 결과를 다음의 표1에 나타내었다.
상기 성능시험에 있어서, 내열성과 내한성을 처짐이나 균열이 발생하지 않은 상태를 "○"라 표기하였고, 처짐현상이 조금있고 균열은 거의 없으나 딱딱해진 상태를 "△", 그리고 처짐과 균열이 심한 상태를 "×"로 표시하였다.
상기 표1에서 알 수 있듯이, 본 발명에 의한 도막방수제는 인장강도, 접착강도 및 신장율 등의 기계적 물성이 우수하고, 내약품성, 내후성 및 내수성이 우수하다.
상기한 바와 같이, 본 발명에 의한 도막방수제는 인장강도, 접착강도 및 신장율 등의 기계적 물성이 우수할 뿐만 아니라 내약품성, 내후성 및 내수성이 우수하여 건축 및 토목 구조물의 도막방수제로 이용할 수 있는 효과가 있다.
Claims (5)
100중량부의 수분산 우레탄/아크릴레이트 하이브리드 고무에 30∼50중량부의 폴리올레핀 수분산체, 15∼25중량부의 스티렌-부타디엔고무 및 20∼30중량부의 충진제로 이루어진 우레탄/아크릴레이트 하이브리드 고무계 도막방수제.
제1항에 있어서,
폴리올레핀 수분산체는 폴리아세틸렌, 폴리아릴렌, 폴리 1-뷰텐, 폴리 1-데칸, 폴리에틸렌 중에서 선택된 1종임을 특징으로 하는 우레탄/아크릴레이트 하이브리드 고무계 도막방수제.
제1 또는 제2항에 있어서,
폴리올레핀 수분산체는 20∼50%의 고형분을 포함하고 800∼1200cps의 점도 및 1∼3㎛의 입자크기인 것을 특징으로 하는 우레탄/아크릴레이트 하이브리드 고무계 도막방수제.
제1항에 있어서,
수분산 우레탄/아크릴레이트 하이브리드 고무는 20∼50%의 우레탄을 함유하고, 45%의 고형분을 포함하며 1000∼1300cps의 점도 및 500%의 신장율을 갖는 것을 특징으로 하는 우레탄/아크릴레이트 하이브리드 고무계 도막방수제.
제1항에 있어서,
충진제는 탄산칼슘염, 탈크, 지당, 바륨 중에서 선택된 1종 임을 특징으로 하는 우레탄/아크릴레이트 하이브리드 고무계 도막방수제.