KR100384128B1 - A duplex thin wall insulation wire - Google Patents

A duplex thin wall insulation wire Download PDF

Info

Publication number
KR100384128B1
KR100384128B1 KR10-2001-0014549A KR20010014549A KR100384128B1 KR 100384128 B1 KR100384128 B1 KR 100384128B1 KR 20010014549 A KR20010014549 A KR 20010014549A KR 100384128 B1 KR100384128 B1 KR 100384128B1
Authority
KR
South Korea
Prior art keywords
polyester copolymer
insulated wire
thermoplastic polyester
insulator
resin
Prior art date
Application number
KR10-2001-0014549A
Other languages
Korean (ko)
Other versions
KR20020074647A (en
Inventor
김상철
김현석
이건주
Original Assignee
엘지전선 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 엘지전선 주식회사 filed Critical 엘지전선 주식회사
Priority to KR10-2001-0014549A priority Critical patent/KR100384128B1/en
Publication of KR20020074647A publication Critical patent/KR20020074647A/en
Application granted granted Critical
Publication of KR100384128B1 publication Critical patent/KR100384128B1/en

Abstract

본 발명은 지하철이나 철도 차량에서 신호 전달 및 기기 제어를 위하여 사용되는 전선에 관한 것으로, 1차 절연체(1)로서 가교 폴리올레핀, 폴리부틸렌테레프탈레이트(PBT), 열가소성 폴리에스터계 공중합체로 구성되며, 2차 절연체(3)로서 열가소성 폴리에스터계 공중합체로 구성되는 것을 특징으로 한다. 본 발명은 박육 상태에서도 높은 기계적 물성을 유지하면서 우수한 난연성과 절연성능을 가지는 전선 피복의 구조에 관한 것이다.The present invention relates to a wire used for signal transmission and device control in a subway or railroad vehicle, and is composed of a crosslinked polyolefin, polybutylene terephthalate (PBT), and a thermoplastic polyester copolymer as the primary insulator (1). It is characterized by consisting of a thermoplastic polyester copolymer as the secondary insulator (3). The present invention relates to a structure of an electric wire coating having excellent flame retardancy and insulation performance while maintaining high mechanical properties even in a thin state.

Description

2중 박육 절연 전선{A duplex thin wall insulation wire}A duplex thin wall insulation wire

본 발명은 피복 전선에 관한 것으로, 보다 상세하게는 지하철이나 철도 차량에서 신호 전달 및 기기 제어를 위하여 사용되는 2중 박육 절연 전선(7)에 관한 것이다.The present invention relates to shielded wires, and more particularly to a double thin insulated wire (7) used for signal transmission and device control in subway or rail vehicles.

시스템이 정밀화되고 복잡해지면서 각종 전기/전자 기기의 소형, 경량화가 이루어지고 있는 추세이며, 이에 따른 기기 내부 온도의 증가와 공간 축소로 인하여 여기에 적용되는 전선도 점점 박육화되고 있다. 또한, 박육 상태에서도 점점 더높은 물성과 고내열성이 요구되고 있으며 일반용 전선에 비하여 우수한 난연성과 함께 연소시 매우 낮은 연기 밀도를 나타내도록 요구된다.As the system becomes more precise and complicated, various electric / electronic devices are becoming smaller and lighter, and the wires applied thereto are becoming thinner due to the increase in the internal temperature of the device and the reduction of space. In addition, even in a thin state, higher physical properties and high heat resistance are required, and it is required to exhibit a very low smoke density upon combustion with excellent flame retardancy compared to general electric wires.

이러한 고성능/박육 전선의 수요는 지하철 및 철도 차량 부문에서 급증하고 있으며 종래의 염화 폴리올레핀 (chlorinated polyolefin)(13) 절연 재료를 적용하기에는 많은 문제점이 있다. 염화 폴리올레핀(13)의 경우에는 절연 두께를 0.8 ㎜ 이하로 줄이기가 불가능하며 난연성이 우수한 반면에 연소시 연기의 발생량이 매우 많을 뿐더러 유독 가스의 발생이 심해서 화재에 대한 안전성이 떨어진다.The demand for such high performance / thin wires is rapidly increasing in the subway and railway vehicle sectors, and there are many problems in applying the conventional chlorinated polyolefin (13) insulation material. In the case of the chlorinated polyolefin (13), it is impossible to reduce the insulation thickness to 0.8 mm or less, and excellent flame retardancy, while the generation of smoke during combustion, and the generation of toxic gas is severe, so the safety of fire is low.

도 2는 종래의 와이어(9)의 단면도를 나타내었다. 도 2에 도시된 바와 같이, 종래의 와이어(9)의 구조는 도체(11)와 상기 도체(11)를 감싸고 있는 염화 폴리올레핀(13)으로 구성된 단일 절연체 구조이다.2 shows a cross-sectional view of a conventional wire 9. As shown in FIG. 2, the structure of the conventional wire 9 is a single insulator structure composed of a conductor 11 and a chlorinated polyolefin 13 surrounding the conductor 11.

본 발명은 상기와 같은 문제점을 해결하기 위해 안출된 것으로서, 본 발명의 목적은 지하철이나 철도 차량에서 신호 전달 및 기기 제어를 위하여 사용되는 전선에 대하여 박육 상태에서도 높은 기계적 물성을 유지하면서 우수한 난연성과 절연성능을 가지는 2중 박육 절연 전선(7)을 제공하는 것이다.The present invention has been made to solve the above problems, an object of the present invention is excellent flame retardancy and insulation while maintaining high mechanical properties even in the thin state with respect to the wire used for signal transmission and device control in subway or railway vehicles It is to provide a double thin insulated wire 7 having performance.

상기와 같은 본 발명의 목적은 1차 절연체(1)는 가교 폴리올레핀, 폴리부틸렌 테레프탈레이트 (polybuthylene terephthalate), 열가소성 폴리에스터계 공중합체로 구성되며, 2차 절연체(3)는 열가소성 폴리에스터계 공중합체로 구성되는 것을 특징으로 하는 2중 박육 절연 전선(7)에 의하여 달성된다.The object of the present invention as described above is that the primary insulator (1) is composed of a crosslinked polyolefin, polybutylene terephthalate (polybuthylene terephthalate), a thermoplastic polyester-based copolymer, the secondary insulator (3) is a thermoplastic polyester-based air It is achieved by a double thin insulated wire 7, characterized in that it is composed of coalescence.

도체와 절연체로서 이루어진 것을 와이어(wire)라 정의하고, 여러 가닥의 와이어를 집합하여 시스체(sheath)로서 보호한 것을 케이블(cable)이라 정의한다. 본 발명에서는 케이블에 사용되는 시스체를 와이어에 적용하여 2중 박육 절연 전선을 설계하였다. 즉, 와이어의 절연체는 각각 절연체와 시스체(sheath)의 기능을 가지도록 이중 절연으로 설계하였다.A wire made of a conductor and an insulator is defined as a wire, and a cable formed by collecting several strands of wire and protecting it as a sheath is defined as a cable. In the present invention, the sheath body used for the cable was applied to the wire to design a double thin insulated wire. That is, the insulator of the wire is designed by double insulation so as to have the function of the insulator and the sheath, respectively.

본 발명에서는 고성능/고난연 전선 피복용 조성물을 위하여 열가소성 폴리에스터계 공중합체(polyester copolymer)를 단독 사용하거나, 경도가 다른 수지들을 블렌드한 수지를 매트릭스로 하여 표면 처리된 수산화마그네슘 난연 충전재를 단독 사용하거나 멜라민 시아누레이트 등의 난연재와 혼용하는 기술을 적용하였다. 상기 열가소성 폴리에스터계 공중합체에 관해서는 난 할로겐(non-halogen)으로 난연화시킨 조성물을 전선 피복재에 적용하였다. 또한, 와이어의 절연체를 도 1에 도시된 것처럼 2중 절연으로 설계하여 각각에 절연체와 시스체(sheath)로서의 기능을 부여함에 따라 고성능/박육 전선을 특징으로 하는 2중 박육 절연 전선(7)을 개발할 수 있었다.In the present invention, a thermoplastic polyester copolymer is used alone or a magnesium hydroxide flame retardant filler surface-treated using a resin blended resin having a different hardness as a matrix for a high performance / high flame retardant wire coating composition. Or a technique used with a flame retardant such as melamine cyanurate was applied. As for the thermoplastic polyester copolymer, a composition flame-retardant with non-halogen was applied to the electric wire coating material. In addition, as shown in FIG. 1, the insulator of the wire is designed to be double insulated to give each of the functions as an insulator and a sheath, thereby providing a double thin insulated wire 7 featuring high performance / thin wires. Could develop.

본 발명에서 얻어진 2중 박육 절연 전선(7)은 종래의 와이어(9)에 비하여 절연 두께를 0.3㎜ 이하로 줄이는 것이 가능하여 크기 및 무게의 감소와 더불어 설치 공간도 크게 축소시킬 수 있었다. 연소시 유독가스 발생량의 감소 뿐 아니라 연기의 발생량도 염화 폴리올레핀(13)을 사용했을 때보다 10 % 수준으로 감소하여 화재에 대한 안정성도 크게 향상되었다. 또한, 열가소성 폴리에스터계 공중합체를 이용한 2중 절연 설계를 적용함에 따라 종래의 할로겐프리 (halogen free) 전선에 비해서 내유성, 내환경성의 개선 뿐 아니라 내마모성, 노치에 대한 저항성 (resistanceto notch propagation), 내절단특성, 가열변형 등의 특성도 크게 개선되었다.The double thin insulated wire 7 obtained in the present invention can reduce the insulation thickness to 0.3 mm or less as compared with the conventional wire 9, which can reduce the size and weight and greatly reduce the installation space. In addition to the reduction of the amount of toxic gas generated during combustion, the amount of smoke generated was also reduced to 10% level compared with the use of chlorinated polyolefin (13), which greatly improved the fire safety. In addition, by applying a double insulation design using a thermoplastic polyester-based copolymer, as well as improved oil resistance and environmental resistance as compared to conventional halogen-free wires, wear resistance, resistance to notch propagation, Characteristics such as cutting characteristics and heat deformation were also greatly improved.

본 발명의 그 밖의 목적, 특정한 장점 및 신규한 특징들은 첨부된 도면들과 연관되어지는 이하의 상세한 설명과 바람직한 실시예로부터 더욱 분명해질 것이다.Other objects, specific advantages and novel features of the present invention will become more apparent from the following detailed description and the preferred embodiments associated with the accompanying drawings.

도 1은 본 발명의 일 실시예에 따른 2중 박육 전선의 단면도이다.1 is a cross-sectional view of a double thin wire according to an embodiment of the present invention.

도 2는 종래에 사용된 와이어의 단면도이다.2 is a cross-sectional view of a wire conventionally used.

*도면의 주요 부분에 대한 부호 설명* Explanation of symbols on the main parts of the drawings

1 : 1차 절연체 3 : 2차 절연체1: primary insulator 3: secondary insulator

5 : 도체 7 : 2중 박육 절연 전선5: conductor 7: double thin insulated wire

9 : 종래의 와이어 11 : 도체9: conventional wire 11: conductor

13 : 염화 폴리올레핀13: chlorinated polyolefin

이하 본 발명에 따른 2중 박육 절연 전선의 구성에 대해 설명하기로 한다.Hereinafter, the configuration of the double thin insulated wire according to the present invention will be described.

도 1은 본 발명의 일 실시예에 따른 2중 박육 절연 전선의 단면도이다. 도 1에 도시된 바와 같이, 본 발명에서 2중 절연은 다음과 같은 두 가지로 기능을 구분하여 설계하였다.1 is a cross-sectional view of a double thin insulated wire according to an embodiment of the present invention. As shown in Figure 1, in the present invention, the double insulation is designed by dividing the function into two as follows.

첫째, 1차 절연체(1)는 절연성능, 내열성과 기계적 물성을 갖도록 2차 절연체(3)는 난연성과 저발연성, 내유성을 극대화할 수 있도록 재료를 선정하였다. 이를 위하여 1차 절연체(1)에는 폴리부틸렌 테레프탈레이트(polybuthylene terephthalate), 절연 성능을 높인 폴리에스터계 공중합체(polyester copolymer)를 적용하였고, 2차 절연체(3)에는 난연성을 높인 폴리에스터계 공중합체(polyester copolymer)를 적용하였다.First, the primary insulator (1) has a material selected so that the secondary insulator (3) to maximize the flame retardancy, low smoke resistance, oil resistance to have insulation performance, heat resistance and mechanical properties. To this end, polybutylene terephthalate and a polyester copolymer having high insulation performance are applied to the primary insulator 1, and a polyester-based air having high flame retardancy is applied to the secondary insulator 3. A polyester copolymer was applied.

둘째, 1차 절연체(1)는 절연 성능, 내열성, 자기 소화성 수준의 난연성을 부여하고 2차 절연체(3)는 난연성, 저발연성, 내유성, 높은 기계적 물성을 갖도록 설계하였다. 이를 위하여 1차 절연체(1)에는 절연 성능을 높인 폴리에스터계 공중합체와 난연 가교 폴리올레핀(crosslinked polyolefin)을 적용하였고, 2차 절연체(3)에는 고강도 난연 폴리에스터계 공중합체를 적용하였다. 두 경우 모두 사용된 고분자 조성물은 난 할로겐(non halogen)으로 난연된 재료로서 연소시 유독성 가스의발생이 전혀 없다.Second, the primary insulator 1 is designed to give flame retardancy of insulation performance, heat resistance and self-extinguishing level, and the secondary insulator 3 is designed to have flame retardancy, low smoke resistance, oil resistance, and high mechanical properties. For this purpose, a polyester copolymer having high insulation performance and a flame retardant crosslinked polyolefin were applied to the primary insulator 1, and a high strength flame retardant polyester copolymer was applied to the secondary insulator 3. In both cases, the polymer composition used is a non-halogen flame-retardant material and generates no toxic gas upon combustion.

본 발명에서 적용된 난연 재료의 특징은 열가소성 폴리에스터계 공중합체를 단독 사용하거나 경도가 다른 수지들을 블렌드한 매트릭스 수지를 사용하였다. 또한, 스테아릭산, 올레익산, 아미노 실란, 비닐 실란, 스테아릭산/실란, 고분자 물질 등으로 표면 처리한 수산화마그네슘 난연 충전재를 단독 사용하거나, 수산화마그네슘 난연 충전재를 멜라민 시아누레이트와 혼용한 조성물을 사용하였다. 그리고, 절연성능 향상을 위하여 폴리부틸렌 테레프탈레이트(polybuthylene terephthalate)를 블렌드하거나, 올레핀 공중합 수지(olefinic cololymer resin)와 변성 올레핀 공중합 수지(modified olefinic copolymer resin)를 첨가함에 따라 무기 난연재의 충전량을 증가시켜 난연 특성을 향상시켰다.The characteristics of the flame-retardant material applied in the present invention was the use of a thermoplastic polyester copolymer alone or a matrix resin blended resins of different hardness. In addition, a magnesium hydroxide flame retardant filler surface-treated with stearic acid, oleic acid, amino silane, vinyl silane, stearic acid / silane, a polymer material, etc. may be used alone, or a composition in which the magnesium hydroxide flame retardant filler is mixed with melamine cyanurate is used. It was. In order to improve the insulation performance, the amount of inorganic flame retardant is increased by blending polybutylene terephthalate or by adding an olefinic copolymer resin and a modified olefinic copolymer resin. Improved flame retardant properties.

본 발명에서 얻어진 2중 박육 절연 전선(7)은 종래의 와이어(9)에 비하여 60%의 절연 두께 감소와 45%의 중량이 감소된 제품이다. 또한, 3.0 kgf/㎟ 이상의 높은 인장강도와 200% 이상의 신율을 갖는다. 본 발명에서 얻어진 2중 박육 절연 전선(7)은 국제전기표준회의 (International Electrotechnical Commission ; IEC) 332-1을 만족하는 수준의 난연성을 가지며 IEC-1034의 저발연 특성을 만족하는 고난연성과 저발연 특성이 우수한 제품이다.The double thin insulated wire 7 obtained in the present invention is a product having a 60% insulation thickness reduction and a 45% weight reduction compared to the conventional wire 9. It has a high tensile strength of 3.0 kgf / mm 2 or more and an elongation of 200% or more. The double thin insulated wire 7 obtained in the present invention has a flame retardancy that satisfies the International Electrotechnical Commission (IEC) 332-1, and high flame retardancy and low smoke that satisfies the low smoke characteristics of IEC-1034. It is a product with excellent characteristics.

이하 상기와 같은 구성을 갖는 본 발명의 2중 박육 절연 전선(7)에 대한 작용 및 실시예에 대해 설명하기로 한다.Hereinafter, the operation and the embodiment of the double thin insulated wire 7 of the present invention having the configuration as described above will be described.

본 발명에서 변성 올레핀 공중합체 수지(modified olefinic copolymer resin)는 올레핀(olefin)의 함량을 증가시킴에 따라 분자의 극성을 증가시켜 무기난연재와의 친화성을 향상시키는 작용을 한다. 또한, 비닐 실란이나 아미노 실란으로 표면 처리한 수산화마그네슘은 수지 매트릭스(matrix) 내에 잘 분산되는 동시에 수지 매트릭스 내의 적절한 결합력을 유지하는 작용을 한다. 이는 무기 난연재의 고충전 및 연소 후 단단한 챠르(char)의 형성에 기여한다. 또한, 수산화마그네슘에 대하여 스테아릭산, 올레익산, 아미노실란, 바이닐 실란, 스테아릭산/실란, 기타 고분자물질 등으로 표면 처리하여 절연성능을 비교/검토함으로써 효과적으로 절연성능을 조절할 수 있다.Modified olefin copolymer resin (modified olefinic copolymer resin) in the present invention increases the polarity of the molecule by increasing the content of the olefin (olefin) serves to improve the affinity with the inorganic flame retardant. In addition, magnesium hydroxide surface-treated with vinyl silane or amino silane disperses well in the resin matrix and maintains a proper binding force in the resin matrix. This contributes to the formation of a hard char after high charge and combustion of the inorganic flame retardant. In addition, it is possible to effectively control the insulation performance by comparing / reviewing the insulation performance by treating the magnesium hydroxide with stearic acid, oleic acid, aminosilane, vinyl silane, stearic acid / silane, and other polymer materials.

그리고, 절연성능을 향상시키기 위하여 코폴리에테르-에스터 (co-poly(ether-ester)) 수지와 코폴리에스터-에스터 (co-poly(ester-ester))수지의 단독 또는 혼용물에 상용성이 있는 폴리부틸렌 테레프탈레이트를 블렌드하여 매트릭스로 사용하였다. 열가소성 폴리에스터계 수지는 강직구조와 유연구조의 구성비에 따라 경도, 인장강도, 신율 등의 물성과 체적고유저항과 같은 전기적 특성을 다양하게 조절할 수 있다.In addition, in order to improve insulation performance, compatibility with co-poly (ether-ester) resin and co-poly (ester-ester) resin alone or in a mixture Polybutylene terephthalate was blended and used as matrix. Thermoplastic polyester-based resin can control various physical properties such as hardness, tensile strength, elongation and electrical properties such as volume specific resistance according to the ratio of the rigid structure and the flexible structure.

<실시예><Example>

절연체의 구성 성분Component of Insulator 비교예1Comparative Example 1 비교예2Comparative Example 2 비교예3Comparative Example 3 비교예4Comparative Example 4 실시예1Example 1 실시예2Example 2 실시예3Example 3 1차절연체Primary Insulator 염화폴리에틸렌Polyethylene chloride 가교폴리에틸렌Crosslinked polyethylene 폴리에스터공중합체Polyester copolymer 폴리부틸렌테레프탈레이트Polybutylene terephthalate 폴리부틸렌테레프탈레이트Polybutylene terephthalate 폴리에스터계공중합체Polyester Copolymer 가교폴리올레핀Crosslinked polyolefin 1차절연체두께(㎜)Primary Insulator Thickness (mm) 0.30.3 0.30.3 0.30.3 0.150.15 0.150.15 0.150.15 0.150.15 2차절연체Secondary insulator -- -- -- 가교폴리에틸렌Crosslinked polyethylene 폴리에스터계공중합체Polyester Copolymer 폴리에스터계공중합체Polyester Copolymer 폴리에스터계공중합체Polyester Copolymer 2차절연체두께(㎜)Secondary Insulator Thickness (mm) -- -- -- 0.150.15 0.150.15 0.150.15 0.150.15

각 실시예의 물성Physical Properties of Each Example 비교예1Comparative Example 1 비교예2Comparative Example 2 비교예3Comparative Example 3 비교예4Comparative Example 4 실시예1Example 1 실시예2Example 2 실시예3Example 3 강도(kgf/㎟)Strength (kgf / mm2) 1.021.02 1.051.05 2.922.92 4.014.01 3.973.97 3.713.71 3.453.45 신율(%)% Elongation 243243 295295 324324 3535 264264 298298 375375 절연저항(MΩkm)(a)Insulation Resistance (MΩkm) (a) 통과Pass 통과Pass 미달Under 통과Pass 통과Pass 통과Pass 통과Pass 난연성(b)Flame retardant (b) 통과Pass 미달Under 통과Pass 미달Under 통과Pass 통과Pass 통과Pass 연기밀도(c)Smoke density (c) 미달Under 통과Pass 통과Pass 통과Pass 통과Pass 통과Pass 통과Pass

a : 전선 1km에 걸리는 저항. 요구 수준은 500 이상.a: resistance over 1 km of wire. The required level is 500 or more.

b : IEC 332-1 난연 시험 규격에 준하여 시험하였다. 요구수준은 연소길이 200 ㎜ 이하.b: Tested according to IEC 332-1 flame retardant test standard. The required level is less than 200 mm of combustion length.

c : IEC 1034 에 준하여 시험하였다. 요구 수준은 투과율 90% 이상.c: Tested according to IEC 1034. The required level is more than 90% transmittance.

상기 언급한 바와 같은 본 발명에 따른 2중 박육 절연 전선(7)에 의하면, 종래의 와이어(9)에 비하여 절연두께를 0.3 mm 이하로 줄였으며 크기 및 무게의 감소와 더불어 설치 공간도 크게 축소시킬 수 있다. 또한, 연소시 유독 가스 발생량의 감소와 연기발생량도 염화 폴리올레핀(13)을 사용했을 때보다 10 % 수준으로 감소하여 화재에 대한 안정성도 크게 향상되었다. 그리고, 내유성, 내환경개선, 내마모성, 노치에 대한 저항성, 내절단특성, 가열변형 등의 특성도 크게 개선되었다.According to the double thin insulated wire 7 according to the present invention as mentioned above, the insulation thickness is reduced to 0.3 mm or less compared to the conventional wire 9, and the installation space is greatly reduced along with the reduction in size and weight. Can be. In addition, the reduction of the amount of toxic gases generated during combustion and the amount of smoke are also reduced to 10% level than when using the chlorinated polyolefin (13), so that the stability to fire is greatly improved. In addition, properties such as oil resistance, environmental improvement, wear resistance, notch resistance, cutting resistance, and heat deformation were greatly improved.

비록 본 발명이 상기 언급된 바람직한 실시예와 관련하여 설명되어졌지만, 발명의 요지와 범위로부터 벗어남이 없이 다양한 수정이나 번형을 하는 것이 가능하다. 따라서 첨부된 특허청구범위는 본 발명의 요지에 속하는 이러한 수정이나 변형을 포함한다.Although the present invention has been described in connection with the above-mentioned preferred embodiments, it is possible to make various modifications or variations without departing from the spirit and scope of the invention. Accordingly, the appended claims include such modifications and variations as fall within the spirit of the invention.

Claims (6)

도체(5);Conductor 5; 상기 도체(5)를 감싸는, 가교 폴리올레핀 (crosslinked polyolefin), 폴리부틸렌테레프탈레이트(polybuthylene terephthalate)와 열가소성 폴리에스터계 공중합체(polyester copolymer)를 블랜드한 메트릭스 수지로 구성되는 1차 절연체(1); 및A primary insulator (1) comprising a matrix resin blending a crosslinked polyolefin, a polybutylene terephthalate, and a thermoplastic polyester copolymer surrounding the conductor 5; And 상기 1차 절연체(1)를 감싸는 열가소성 폴리에스터계 공중합체(polyester copolymer)로 구성되는 2차 절연체(3);로 이루어지는 것을 특징으로 하는 2중 박육 절연 전선(7).Double insulated wire (7), characterized in that consisting of; a secondary insulator (3) consisting of a thermoplastic polyester copolymer surrounding the primary insulator (1). 제 1 항에 있어서, 상기 열가소성 폴리에스터계 공중합체(polyester copolymer)는 코폴리에테르-에스터 수지 (co-poly(ether-ester) resin), 코폴리에스터-에스터 수지(co-poly(ester-ester) resin)를 단독 혹은 2종 이상 혼합하여 구성되는 것을 특징으로 하는 2중 박육 절연 전선(7).According to claim 1, wherein the thermoplastic polyester copolymer (polyester copolymer) is a co-poly (ether-ester) resin (co-poly (ether-ester) resin), copolyester-ester resin (co-poly (ester-ester) Double thin insulated wire (7), characterized by consisting of a single resin or a mixture of two or more resins). 제 1 항에 있어서, 상기 열가소성 폴리에스터계 공중합체(polyester copolymer)에 대하여 올레핀 공중합체(olefinic copolymer)와 변성올레핀 공중합체(modified olefinic copolymer)를 혼합하여 구성되는 것을 특징으로 하는 2중 박육 절연 전선(7).2. The double thin insulated wire according to claim 1, wherein an olefin copolymer and a modified olefinic copolymer are mixed with the thermoplastic polyester copolymer. (7). 제 1 항에 있어서, 상기 열가소성 폴리에스터계 공중합체(polyester copolymer)에 대하여 수산화마그네슘, 멜라민 시아누레이트를 단독 혹은 혼합하여 구성되는 것을 특징으로 하는 2중 박육 절연 전선(7).2. The double thin insulated wire (7) according to claim 1, wherein magnesium hydroxide and melamine cyanurate are formed singly or mixed with the thermoplastic polyester copolymer. 제 1 항에 있어서, 상기 가교 폴리올레핀(crosslinked polyolefin)은 난 할로겐 (non halogen)으로 난연시킨 조성물로 구성되는 것을 특징으로 하는 2중 박육 절연 전선(7).2. The double thin insulated wire according to claim 1, wherein the crosslinked polyolefin is composed of a composition flame retarded with non halogen. 제 4 항에 있어서, 스테아릭산, 올레익산, 아미노 실란, 스테아릭산/실란, 비닐실란, 고분자 물질 중 택일된 것으로 상기 수산화마그네슘의 표면을 처리한 것으로 구성되는 것을 특징으로 하는 2중 박육 절연 전선(7).The double thin insulated wire according to claim 4, wherein the surface of the magnesium hydroxide is selected from stearic acid, oleic acid, amino silane, stearic acid / silane, vinyl silane, and a polymer material. 7).
KR10-2001-0014549A 2001-03-21 2001-03-21 A duplex thin wall insulation wire KR100384128B1 (en)