KR100375665B1 - 불연성 폴리올레핀 수지조성물 및 이를 이용한알루미늄복합판넬의 제조방법 - Google Patents
불연성 폴리올레핀 수지조성물 및 이를 이용한알루미늄복합판넬의 제조방법 Download PDFInfo
- Publication number
- KR100375665B1 KR100375665B1 KR10-2000-0078617A KR20000078617A KR100375665B1 KR 100375665 B1 KR100375665 B1 KR 100375665B1 KR 20000078617 A KR20000078617 A KR 20000078617A KR 100375665 B1 KR100375665 B1 KR 100375665B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- density polyethylene
- resin composition
- polyolefin resin
- low density
- Prior art date
Abstract
Description
구 분 | 실시예 1 | 실시예 2 | 실시예 3 | 비교예 1 | |
조 성(중량%) | 저밀도 폴리에틸렌 | 20 | 25 | 15 | 20 |
수산화마그네슘 | 70 | 75 | 80 | 70 | |
본 발명의 상용화제 | 10 | 10 | 5 | 10 | |
불연성 | 표면시험 | 적합 | 적합 | 적합 | 적합 |
부가시험 | 적합 | 적합 | 적합 | 적합 | |
가스유해성 | 마우스 시험 | 적합 | 적합 | 적합 | 적합 |
유연성 | 최소벤딩한계(mmR) | 70 | 65 | 73 | 72 |
압출작업성 | 압출부하(A) | 25.7 | 26.2 | 27.1 | 42.6 |
자열발생정도(℃) | +3 | +5 | +7 | +32 | |
두께균일성 | 최종제품의 두께편차(%) | 0.2 | 0.1 | 0.2 | 2.4 |
구 분 | 비교예 2 | 비교예 3 | 비교예 4 | |
조 성(중량%) | 저밀도 폴리에틸렌 | 30 | 40 | 20 |
수산화마그네슘 | 70 | 50 | 70 | |
본 발명의 상용화제 | - | 10 | - | |
그라프트 선형저밀도폴리에틸렌 공중합체 | - | - | 10 | |
불연성 | 표면시험 | 적합 | 부적합 | 적합 |
부가시험 | 적합 | 부적합 | 적합 | |
가스유해성 | 마우스 시험 | 적합 | 부적합 | 적합 |
유연성 | 최소벤딩한계(mmR) | 벤딩불가 | 57 | 125 |
압출작업성 | 압출부하(A) | 26.1 | 21.7 | 27.3 |
자열발생정도(℃) | +6 | +3 | +7 | |
두께균일성 | 최종제품의 두께편차(%) | 0.7 | 0.3 | 0.5 |
Claims (7)
- 저밀도 폴리에틸렌 15~25중량%, 수산화마그네슘 65~80중량% 및 상용화제 5~10중량%를 포함하는 불연성 폴리올레핀 수지조성물에 있어서, 상기 상용화제가 에틸렌계 불포화 카르복실산, 에틸렌계 불포화 카르복식산 안하이드라이드 또는 에스테르계 단량체가 선형저밀도 폴리에틸렌 100중량부 대비 0.25 내지 5중량부 그라프트된 선형저밀도 폴리에틸렌 공중합체, 그라프트 되지 않은 선형저밀도 폴리에틸렌, 에틸렌비닐아세테이트 및 폴리스티렌으로 구성된 것임을 특징으로 하는 불연성 폴리올레핀 수지조성물.
- 제 1항에 있어서, 상기 저밀도 폴리에틸렌의 밀도가 0.89~0.925/cm3이고, 용융지수가 4~50 g/10분인 것을 특징으로 하는 불연성 폴리올레핀 수지조성물.
- 제 1항에 있어서, 상기 수산화마그네슘의 입자크기가 1~10㎛인 것을 특징으로 하는 불연성 폴리올레핀 수지조성물.
- 제 1항에 있어서, 상기 상용화제는 그라프트된 선형저밀도 폴리에틸렌 공중합체 20~30중량%, 그라프트 되지 않은 선형저밀도 폴리에틸렌 15~25중량%, 비닐아세테이트 함량이 15%인 에틸렌비닐아세테이트 30~40중량% 및 폴리스티렌 5~15중량%으로 구성됨을 특징으로 하는 불연성 폴리올레핀 수지 조성물.
- 제 1항의 불연성 폴리올레핀 수지조성물을 심재로 사용하여 내화성이 우수한 알루미늄복합판넬을 제조함에 있어서, L/D가 24∼27인 150φmm 일축압출기를 사용하는 것을 특징으로 하는 알루미늄복합판넬의 제조방법.
- 제 5항에 있어서, 상기 일축압축기에서 압축비가 2.0∼2.4이고, 덜미지부(Dulmage Section)을 갖는 일축스크류를 사용하여 압출기내 용융부에서 자열발생을 저하시키는 것을 특징으로 하는 알루미늄복합판넬의 제조방법.
- 제 5항에 있어서, 용융된 수지가 하향식 티다이를 통해서 시트로 성형압출되도록 하여 시트의 처짐현상을 방지하는 것을 특징으로 하는 알루미늄복합판넬의 제조방법.