KR100341003B1 - method for waterproofing using the epoxy mortar - Google Patents

method for waterproofing using the epoxy mortar Download PDF

Info

Publication number
KR100341003B1
KR100341003B1 KR1019990057824A KR19990057824A KR100341003B1 KR 100341003 B1 KR100341003 B1 KR 100341003B1 KR 1019990057824 A KR1019990057824 A KR 1019990057824A KR 19990057824 A KR19990057824 A KR 19990057824A KR 100341003 B1 KR100341003 B1 KR 100341003B1
Authority
KR
South Korea
Prior art keywords
epoxy
weight
waterproofing agent
mortar
waterproofing
Prior art date
Application number
KR1019990057824A
Other languages
Korean (ko)
Other versions
KR20010056180A (en
Inventor
강문수
Original Assignee
강문수
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 강문수 filed Critical 강문수
Priority to KR1019990057824A priority Critical patent/KR100341003B1/en
Publication of KR20010056180A publication Critical patent/KR20010056180A/en
Application granted granted Critical
Publication of KR100341003B1 publication Critical patent/KR100341003B1/en

Abstract

본 발명은 에피클로로히드린과 비스페놀 A를 중합시킨 에폭시수지, 셀룰로오스와 알칼리 수용액 및 디에틸황산을 반응시켜 만든 메틸셀룰로오스 유화제, 소포제, 경화제로 구성된 에폭시 방수제에 시멘트와 규사를 혼합한 에폭시 모르터를 이용한 방수방법에 관한 것이다.The present invention uses an epoxy mortar mixed with cement and silica sand in an epoxy waterproofing agent composed of an epoxy resin polymerized with epichlorohydrin and bisphenol A, a methylcellulose emulsifier made by reacting cellulose with an aqueous alkali solution and diethyl sulfate, an antifoaming agent, and a curing agent. It relates to a waterproof method.

본 발명의 방수용 에폭시수지 모르터는 수용성 에폭시 방수제에 시멘트와 규사를 혼합한 것이며, 여기에 폴리프로필렌 섬유를 더 추가할 수도 있다.The waterproof epoxy resin mortar of the present invention is a mixture of cement and silica sand in a water-soluble epoxy waterproofing agent, and polypropylene fibers may be further added thereto.

수용성 에폭시 방수제는 본 출원인의 특허 제24,531호에 개시된 방수제 조성물을 이용한다. 상기 에폭시 방수제 조성물에 시멘트와 규사를 혼합하여 본 발명의 방수용 에폭시 모르터를 제조한다. 시멘트는 상기 에폭시 방수제 중량의 1.5∼2배를 혼합하며, 규사의 중량은 상기 에폭시 방수제 중량의 3∼3.5배로 배합한다. 규사는 입경 2-3㎜의 것을 사용한다.The water soluble epoxy waterproofing agent utilizes the waterproofing composition disclosed in Applicant's Patent No. 24,531. Cement and silica sand are mixed with the epoxy waterproofing agent composition to prepare an epoxy mortar for waterproofing of the present invention. Cement mixes 1.5 to 2 times the weight of the epoxy waterproofing agent, and the weight of silica sand is blended to 3 to 3.5 times the weight of the epoxy waterproofing agent. Silica sand uses a particle diameter of 2-3 mm.

에폭시 모르터의 인장강도를 증진시키기 위하여 폴리프로필렌 섬유를 더 첨가할 수 있다. 폴리프로필렌 섬유는 상기 에폭시 방수제 중량의 5% 정도를 첨가한다. 폴리프로필렌 섬유를 첨가할 경우 상기 섬유가 에폭시 모르터 내에서 인장보강재로 기능하여 에폭시 모르터의 인장강도를 개선함으로써 수축균열의 발생을 저감시킬 수 있다.Polypropylene fibers may be further added to enhance the tensile strength of the epoxy mortar. The polypropylene fiber adds about 5% of the weight of the epoxy waterproofing agent. When the polypropylene fiber is added, the fiber functions as a tensile reinforcing material in the epoxy mortar to improve the tensile strength of the epoxy mortar, thereby reducing the occurrence of shrinkage cracks.

Description

에폭시 모르터를 이용한 방수방법 {method for waterproofing using the epoxy mortar}Method for waterproofing using the epoxy mortar}

본 발명은 에폭시 모르터를 이용한 방수방법에 관한 것이다. 보다 구체적으로, 에피클로로히드린과 비스페놀 A를 중합시킨 에폭시수지, 셀룰로오스와 알칼리 수용액 및 디에틸황산을 반응시켜 만든 메틸셀룰로오스 유화제, 소포제, 경화제로 구성된 에폭시 방수제에 시멘트와 규사를 혼합한 에폭시 모르터를 이용한 방수방법에 관한 것이다.The present invention relates to a waterproof method using an epoxy mortar. More specifically, epoxy mortar mixed with cement and silica sand in an epoxy waterproofing agent comprising an epoxy resin polymerized with epichlorohydrin and bisphenol A, a methylcellulose emulsifier made by reacting cellulose with an aqueous alkali solution and diethyl sulfate, an antifoaming agent, and a curing agent. It relates to a waterproof method used.

현재 구조물의 방수 공법으로써 시멘트 모르터 방수, 쉬트 방수, 에폭시 방수 등 여러 가지 공법들이 사용되고 있다. 상기 공법들은 나름대로의 장단점을 가지고 있으며, 이중 시멘트 모르터 방수 공법은 가장 비용이 저렴하고, 시멘트를 이용함으로써 구조체인 콘크리트와의 동질성이 커서 널리 이용되고 있는 공법이다. 그러나, 시멘트 모르터 방수는 시멘트 모르터의 특성상 경화과정에서 균열이 발생하는 문제가 있고, 들뜨거나 외부의 충격에 의해 쉽게 파손되는 단점이 있다. 또한, 인장강도가 상대적으로 작아 구조체에 균열이 발생하는 경우 방수층도 함께 파단되는 문제점이 있다.Currently, various methods such as cement mortar waterproofing, sheet waterproofing, and epoxy waterproofing have been used as waterproofing methods for structures. The above methods have their advantages and disadvantages, and the double cement mortar waterproofing method is the most inexpensive, and is widely used because of its homogeneity with concrete as a structure by using cement. However, the cement mortar waterproof has a problem that cracks occur during the curing process due to the characteristics of the cement mortar, and is easily damaged by excitation or external impact. In addition, when the tensile strength is relatively small, a crack occurs in the structure, there is a problem that the waterproof layer is also broken together.

에폭시 방수의 경우 방수 성능이 우수하고 인장강도가 커서 구조체의 변형에도 쉽게 파손되지 않는 장점이 있으나, 물이 있는 곳에서는 접착력이 발휘되지 않고 열에 약한 단점이 있다. 또한, 초벌용으로 사용되는 솔벤트는 밀폐공간에서 작업시 안전사고가 발생할 수 있으며 발화의 위험이 있다.Epoxy waterproof has the advantage of excellent waterproof performance and tensile strength is not easy to break even in the deformation of the structure, but there is a disadvantage that the adhesive strength is not exhibited in the place where water is present. In addition, the solvent used for primary use may cause a safety accident when working in a closed space and there is a risk of fire.

본 발명의 목적은 습기가 있는 곳에서도 시공이 가능한 방수용 에폭시 수지 모르터를 이용한 방수방법을 제공하는 것이다.An object of the present invention is to provide a waterproof method using a waterproof epoxy resin mortar that can be constructed even in the presence of moisture.

본 발명의 다른 목적은 방수 모르터의 수축 균열을 억제할 수 있고, 외부 충격에 의한 파손, 부식 및 동해 등에 대한 저항성이 우수한 에폭시 수지 모르터를 이용한 방수방법을 제공하는 것이다.Another object of the present invention is to provide a waterproofing method using an epoxy resin mortar that can suppress the shrinkage cracking of the waterproofing mortar, and is excellent in resistance to breakage, corrosion, and freeze caused by external impact.

본 발명의 방수용 에폭시수지 모르터는 수용성 에폭시 방수제에 시멘트와 규사를 혼합한 것이며, 여기에 폴리프로필렌 섬유를 더 추가할 수도 있다.The waterproof epoxy resin mortar of the present invention is a mixture of cement and silica sand in a water-soluble epoxy waterproofing agent, and polypropylene fibers may be further added thereto.

수용성 에폭시 방수제는 본 출원인의 특허 제24,531호에 개시된 방수제 조성물을 이용한다. 상기 방수제 조성물의 구성은 다음과 같다.The water soluble epoxy waterproofing agent utilizes the waterproofing composition disclosed in Applicant's Patent No. 24,531. The configuration of the waterproofing agent composition is as follows.

에폭시 당량 184-194, 점도 11,000-14,000 센티포아즈의 고분자 액상 수지에 셀룰로오스, 아세톤, 염기성화합물을 반응시켜 얻은 메틸셀룰로오스를 상기 수지에대하여 약 0.2-1중량%의 양으로 첨가하고 이 혼합액에 에폭시 수지에 대해 약 2중량%의 물을 가해 충분히 교반한다. 이 혼합액에 라노린, 로진, 콜레스테린, 레시틴, 다가알콜의 지방산 에스테르, 알킬페놀과 에틸렌 옥시드나 프로필렌 옥시드의 공중합체 등과 같은 냉수 및 유기용매에 가용성인 유화제를 상기 에폭시 수지에 대하여 약 2-5중량%로 첨가하고 물을 천천히 가하면서 800-1,200RPM으로 교반하여 균일하게 유화시킨다. 이때 발생되는 기포를 제거하기 위하여 실리콘 오일을 소량 첨가한다. (이렇게하여 얻은 혼합물을 이후 A라 칭한다.) 상기의 균일 혼합물(A)는 내수성, 내약품성, 내산성, 내구성 등이 우수하여 방수제로서 탁월한 효과를 나타낸다. 상기에서 사용된 에폭시 수지는 종래의 시판 에폭시 수지와 상이한 것으로서 에폭시 당량 184-194, 점도 11,000-14,000인 것이 본 발명의 방수제 원료로서 바람직하다.Methyl cellulose obtained by reacting cellulose, acetone, and a basic compound with a polymer liquid resin having an epoxy equivalent of 184-194 and a viscosity of 11,000-14,000 centipoise was added in an amount of about 0.2-1% by weight relative to the resin, and epoxy was added to the mixture. About 2% by weight of water is added to the resin, followed by stirring sufficiently. In this mixture, emulsifiers soluble in cold water and organic solvents such as lanolin, rosin, cholesterine, lecithin, fatty acid esters of polyhydric alcohols, copolymers of alkylphenols and ethylene oxide or propylene oxide, and the like are about 2-5 to the epoxy resin. Add by weight and stir at 800-1,200 RPM while slowly adding water to emulsify uniformly. A small amount of silicone oil is added to remove bubbles generated at this time. (The mixture thus obtained is hereinafter referred to as A.) The above-mentioned homogeneous mixture (A) is excellent in water resistance, chemical resistance, acid resistance, durability, etc., and shows an excellent effect as a waterproofing agent. The epoxy resin used above is different from the conventional commercial epoxy resin, and epoxy equivalent 184-194 and viscosity 11,000-14,000 are preferred as the waterproofing agent raw material of the present invention.

상기의 균일한 에폭시 혼합물(A)와는 별도로 디카르복실산과 디아민류와 중축합에 의해 얻어진 폴리아미드 HO(CORCONH-CH2CH2NH)nH를 상기 혼합물(A)에 배합하여 경화성을 증진시킨다. 이러한 폴리아미드는 시판의 것을 사용하여도 가능하나 점도 2,500-4,500 센티포아즈, 산도 2-4, 활성수소당량 90-110의 저점도 폴리아미드이어야 한다. 상기 에폭시수지 혼합물(A)중의 에폭시 당량에 대하여 상기 폴리아미드의 활성수소당량비로 배합한 후 전술한 유화제를 첨가하면서 300-400RPM의 속도로 균일하게 될 때까지 교반한다. 이때 발생되는 기포를 제거하기 위해 소량의 실리콘 오일과 같은 소포제를 첨가하면서 수행한다.Apart from the homogeneous epoxy mixture (A) described above, polyamide HO (CORCONH-CH 2 CH 2 NH) n H obtained by polycondensation with dicarboxylic acid and diamines is blended into the mixture (A) to improve curability. . Such polyamides may be commercially available but should be low viscosity polyamides having a viscosity of 2,500-4,500 centipoise, an acidity of 2-4, and an active hydrogen equivalent weight of 90-110. The epoxy equivalent in the epoxy resin mixture (A) is blended at an active hydrogen equivalent ratio of the polyamide and then stirred until it is uniform at a speed of 300-400 RPM while adding the emulsifier described above. In this case, a small amount of antifoaming agent such as silicone oil is added to remove air bubbles.

실제 시공을 간편하게 하기 위해서 상기 에폭시수지 혼합물(A)와는 별도로 폴리아미드 조성물을 만들어 보관, 운송한 후 시공시 혼합물(A)와 폴리아미드 조성물을 1:1로 배합하여 사용할 수 있다. 폴리아미드 조성물의 제조는 상기 폴리아미드 30중량부에 전술한 유화제 0.5-1.5중량부를 가하고 물과 소포제 0.3-0.8 중량부를 넣고 균일하게 될 때까지 교반한다.In order to simplify the actual construction, the polyamide composition may be prepared and stored and transported separately from the epoxy resin mixture (A), and then mixed with the mixture (A) and the polyamide composition in a 1: 1 ratio. In preparing the polyamide composition, 0.5-1.5 parts by weight of the emulsifier described above is added to 30 parts by weight of the polyamide, and 0.3-0.8 parts by weight of water and an antifoaming agent are stirred until uniform.

상기 에폭시 혼합물(A)와 폴리아미드 조성물로 구성되는 에폭시 방수제에 시멘트와 규사를 혼합하여 본 발명의 방수용 에폭시 모르터를 제조한다. 시멘트는 상기 에폭시 방수제 중량의 1.5∼2배를 혼합하며, 규사의 중량은 상기 에폭시 방수제 중량의 3∼3.5배로 배합한다. 규사는 입경 2-3㎜의 것을 사용한다.The epoxy waterproofing mortar of the present invention is prepared by mixing cement and silica with an epoxy waterproofing agent composed of the epoxy mixture (A) and the polyamide composition. Cement mixes 1.5 to 2 times the weight of the epoxy waterproofing agent, and the weight of silica sand is blended to 3 to 3.5 times the weight of the epoxy waterproofing agent. Silica sand uses a particle diameter of 2-3 mm.

에폭시 모르터의 인장강도를 증진시키기 위하여 폴리프로필렌 섬유를 더 첨가할 수 있다. 폴리프로필렌 섬유는 상기 에폭시 방수제 중량의 5% 정도를 첨가한다. 이때 사용하는 폴리프로필렌 섬유는 에폭시 모르터에서 분산을 고려하여 단섬유가 바람직하다. 폴리프로필렌 섬유 대신에 다른 종류의 무기, 유기 섬유로 대체할 수도 있다. 폴리프로필렌 섬유를 첨가할 경우 상기 섬유가 에폭시 모르터 내에서 인장보강재로 기능하여 에폭시 모르터의 인장강도를 개선함으로써 수축균열의 발생을 저감시킬 수 있다.Polypropylene fibers may be further added to enhance the tensile strength of the epoxy mortar. The polypropylene fiber adds about 5% of the weight of the epoxy waterproofing agent. The polypropylene fiber used at this time is preferably a short fiber in consideration of dispersion in the epoxy mortar. Instead of polypropylene fibers, other types of inorganic and organic fibers may be substituted. When the polypropylene fiber is added, the fiber functions as a tensile reinforcing material in the epoxy mortar to improve the tensile strength of the epoxy mortar, thereby reducing the occurrence of shrinkage cracks.

실시예Example

표 1은 본 발명의 방수용 에폭시 모르터의 성능을 확인하기 위한 실험결과이다. 배합비는 중량비로 에폭시 방수제 : 시멘트 : 모래 = 1 : 2 : 3의 비율로 혼합하였으며, 에폭시 방수제는 에폭시 혼합물(A)와 폴리아미드 조성물 1:1의 비율로혼합하였다.Table 1 is an experimental result for confirming the performance of the waterproof epoxy mortar of the present invention. The mixing ratio was mixed in the ratio of epoxy waterproofing agent: cement: sand = 1: 2: 3, and the epoxy waterproofing agent was mixed in the ratio of the epoxy mixture (A) and the polyamide composition 1: 1.

응결시간(길모아시험)Condensation time (Gillmore test) 흡수비Absorption ratio 투수비Pitching cost 안정성(침수방법)Stability (immersion method) 초결(분)First minute 종결(시간:분)Termination (hour: minute) 1시간1 hours 5시간5 hours 24시간24 hours 0.1㎏f/㎠0.1㎏f / ㎠ 150150 5:305:30 0.590.59 0.600.60 0.610.61 0.620.62 이상없음clear 압축강도(㎏f/㎠)Compressive strength (㎏f / ㎠) 휨강도(㎏f/㎠)Flexural strength (㎏f / ㎠) 접착강도(㎏f/㎠)Adhesive strength (㎏f / ㎠) 내충격성1㎏×100㎝Impact Resistance 1㎏ × 100㎝ 내마모성(g)Abrasion Resistance (g) 187187 6565 1212 이상없음clear 0.060.06

본 발명의 방수용 에폭시 모르터를 이용한 방수방법에 대하여 설명한다. 먼저 방수를 하고자 하는 바탕면을 정리한다. 바탕면은 요철이 없도록 면정리를 하고 미세한 균열 부위는 사전에 시멘트 페이스트 등으로 메꿔놓는다. 표면의 이물질을 제거한 후 물청소를 실시한다. 본 발명의 에폭시 모르터는 수용성 에폭시를 사용함으로써 물이나 습기가 있는 곳에서도 충분히 시공이 가능하고 소정의 접착력을 얻을 수 있다. 바탕정리가 완료되면 상기 에폭시 방수제와 시멘트를 중량비 1:1로 혼합한 다음 바탕면에 도포하여 바탕면에 에폭시와 시멘트 페이스트가 침투되도록 한다. 다음 에폭시 방수제와 시멘트를 중량비 1:3으로 혼합하여 방수하고자 하는 바탕면에 도포하며, 바로 이어서 에폭시 방수제와 시멘트와 규사를 혼합한 에폭시 모르터를 두께 4-6㎜ 정도로 도포한다.상기 에폭시 모르터에는 에폭시 모르터의 인장강도를 증진시켜 수축균열을 저감시키기 위하여 폴리프로필렌 섬유를 더 첨가할 수 있다. 폴리프로필렌 섬유는 상기 에폭시 방수제 중량의 5% 정도를 첨가한다. 이 때 사용하는 폴리프로필렌 섬유는 에폭시 모르터에서의 분산을 고려하여 단섬유가 바람직하다. 또한 상기 폴리프로필렌 섬유 대신에 다른 종류의 무기 또는 유기 섬유로 대체할 수도 있다.상기 에폭시 모르터에 첨가된 섬유는 에폭시 모르터내에서 인장보강재로 기능하여 에폭시 모르터의 인장강도를 개선함으로써 수축균열의 발생을 저감시킬 수 있다.도포된 에폭시 모르터를 소정의 강도가 발현될 때 까지 양생하면 방수층이 완성된다. 본 발명의 에폭시 모르터는 방수용은 물론 벽면 미장용으로도 사용가능하다.The waterproof method using the waterproof epoxy mortar of the present invention will be described. First, clean up the surface to be waterproofed. The base surface is trimmed so that there are no irregularities, and the minute cracks are filled with cement paste in advance. Remove foreign substances on the surface and clean the water. The epoxy mortar of the present invention can be sufficiently applied even in the presence of water or moisture by using a water-soluble epoxy, and can obtain a predetermined adhesive force. When the grounding is completed, the epoxy waterproofing agent and cement are mixed in a weight ratio of 1: 1, and then applied to the base surface to allow the epoxy and cement paste to penetrate the base surface. Next, the epoxy waterproofing agent and cement are mixed at a weight ratio of 1: 3 and applied to the base surface to be waterproofed, followed by an epoxy mortar mixed with the epoxy waterproofing agent and cement and silica sand with a thickness of about 4-6 mm. Polypropylene fiber may be further added to increase the tensile strength of the mortar to reduce shrinkage cracking. The polypropylene fiber adds about 5% of the weight of the epoxy waterproofing agent. The polypropylene fiber used at this time is preferably short fiber in consideration of dispersion in an epoxy mortar. It is also possible to substitute other types of inorganic or organic fibers instead of the polypropylene fibers. The fibers added to the epoxy mortar function as a tensile reinforcing material in the epoxy mortar to improve the tensile strength of the epoxy mortar to prevent the occurrence of shrinkage cracks. The coated epoxy mortar is cured until a predetermined strength is developed to complete the waterproof layer. The epoxy mortar of the present invention can be used not only for waterproofing but also for plastering walls.

본 발명의 에폭시 모르터는 압축강도나 접착강도가 우수하고 내충격성이 우수하여 방수층 시공후 하자의 발생을 줄일 수 있다. 또한, 종래의 시멘트 모르터 방수제에서 균열이 발생하는 문제를 해결함으로써 방수성능의 향상을 기할 수 있다.Epoxy mortar of the present invention is excellent in compressive strength or adhesive strength and excellent impact resistance can reduce the occurrence of defects after the waterproof layer construction. In addition, it is possible to improve the waterproof performance by solving the problem of cracking in the conventional cement mortar waterproofing agent.

Claims (4)

삭제delete 삭제delete 삭제delete 방수하고자 하는 바탕면을 청소하고;Clean the surface to be waterproofed; 방수 부위에 에폭시 방수제와 시멘트를 중량비 1:1로 혼합한 혼합물을 도포하고;Applying a mixture of epoxy waterproofing agent and cement in a weight ratio of 1: 1 to the waterproofing site; 상기 에폭시 방수제와 시멘트를 중량비 1:3으로 혼합한 혼합물을 도포하고; 그리고,Applying a mixture of the epoxy waterproofing agent and cement in a weight ratio of 1: 3; And, 상기 에폭시 방수제, 상기 에폭시 방수제 중량의 1.5∼2배의 시멘트 및 상기 에폭시 방수제 중량의 3∼3.5배의 규사로 구성되는 에폭시 모르터를 도포하는 단계;Applying an epoxy mortar comprising the epoxy waterproofing agent, 1.5 to 2 times the weight of the epoxy waterproofing agent and silica sand 3 to 3.5 times the weight of the epoxy waterproofing agent; 로 구성되며,Consists of, 상기 에폭시 방수제는 에폭시 당량 184∼194이고 점도가 11,000∼14,000 센티포아즈인 에폭시 수지 65∼70 중량부와 메틸셀룰로오스 0.2∼1 중량부, 유화제 2∼5 중량부, 소포제 0.5∼2 중량부, 물 22.2∼32.3 중량부로 조성된 에폭시수지 혼합물 및 점도가 2,500∼4,500이고, 산가가 2∼4, 활성수소당량 90∼110의 저점도 폴리아미드 25∼33 중량부, 소포제 0.∼1 중량부, 유화제 0.5∼1.5 중량부, 물 62.5∼74.3 중량부로 조성된 폴리아미드로 구성되고,The epoxy waterproofing agent is an epoxy equivalent of 184 to 194 and the viscosity of 11,000 to 14,000 centipoise epoxy resin 65 to 70 parts by weight, methyl cellulose 0.2 to 1 part by weight, emulsifier 2 to 5 parts by weight, antifoaming agent 0.5 to 2 parts by weight, water Epoxy resin mixture composed of 22.2 to 33.3 parts by weight and viscosity of 2,500 to 4,500, acid value 2 to 4, 25 to 33 parts by weight of low viscosity polyamide with active hydrogen equivalent weight 90 to 110, defoamer 0. to 1 part by weight, emulsifier It consists of a polyamide composed of 0.5 to 1.5 parts by weight, 62.5 to 74.3 parts by weight of water, 상기 에폭시 모르터에는 상기 에폭시 방수제 중량의 0.05배의 유기질 섬유, 무기질 섬유 및 폴리프로필렌 섬유중 어느 하나를 더 첨가하는 것을 특징으로 하는 에폭시 모르터를 이용한 방수방법.The epoxy mortar waterproof method further comprises any one of the organic fiber, inorganic fiber and polypropylene fiber of 0.05 times the weight of the epoxy waterproofing agent.
KR1019990057824A 1999-12-15 1999-12-15 method for waterproofing using the epoxy mortar KR100341003B1 (en)