KR100329037B1 - A sea-island type composite fiber for warp knitting, and a process of preparing for the same - Google Patents
A sea-island type composite fiber for warp knitting, and a process of preparing for the same Download PDFInfo
- Publication number
- KR100329037B1 KR100329037B1 KR1020010074133A KR20010074133A KR100329037B1 KR 100329037 B1 KR100329037 B1 KR 100329037B1 KR 1020010074133 A KR1020010074133 A KR 1020010074133A KR 20010074133 A KR20010074133 A KR 20010074133A KR 100329037 B1 KR100329037 B1 KR 100329037B1
- Authority
- KR
- South Korea
- Prior art keywords
- island
- sea
- composite fiber
- component
- yarn
- Prior art date
Abstract
본 발명은 경편용 해도형 복합섬유에 관한 것이다. 본 발명은 알칼리 이용해성의 공중합 폴리에스테르를 해성분으로 사용하고 주성분인 폴리에틸렌테레프탈레이트가 90몰% 이상인 폴리에스테르를 도성분으로 사용하여 방사 직접 연신 방식으로 제조된 경편용 해도형 복합섬유에 있어서, 해성분 용출후의 도성분 원사 결정배향도(Fc)가 0.80∼0.90인 것을 특징으로 한다. 본 발명으로 제조한 해도형 복합섬유는 열수축 특성이 양호하여 기모성이 우수하며, 경편지의 촉감 및 외관을 향상 시킨다.The present invention relates to a island-in-the-sea composite fiber for warp knitting. The present invention relates to a warp island-in-the-sea composite fiber prepared by spinning direct stretching method using an alkali-soluble copolyester as a sea component and a polyester whose main component is polyethylene terephthalate of 90 mol% or more as a island component. It is characterized in that the degree-of-component yarn crystal orientation (Fc) after dissolution is 0.80 to 0.90. The island-in-the-sea composite fiber produced by the present invention has excellent heat shrinkage characteristics, and has excellent brushing properties, and improves the feel and appearance of warp knitted paper.
Description
본 발명은 경편용 해도형 복합섬유 및 그의 제조방법에 관한 것이다. 구체적으로 본 발명은 해성분 용출후 도성분 원사의 물성이 우수하여 최종 제품인 기모 경편지의 품질을 향상시킬 수 있는 경편용 해도형 복합섬유 및 그의 제조방법에 관한 것이다.The present invention relates to warp island-in-sea composite fiber and a method for producing the same. Specifically, the present invention relates to a warp island-in-sea composite fiber for improving the quality of the brushed warp knitted fabric, which is excellent in physical properties of seaweed-based yarn after dissolution of the sea component, and a manufacturing method thereof.
해도형 복합섬유를 사용하여 경편지를 제조하는 경편공정은 제편속도가 빠르기 때문에 고품질의 원사특성, 특히 원사의 매끄러운 특성이 요구된다. 또한 경편지를 제조하는 후가공공정은 감량, 기모, 염색 등의 복잡한 여러 단계를 거쳐야 하기 때문에 해성분 용출후 도성분 원사 결정배향도(Fc)의 내부구조 특성이 서로 적절하게 조절 되어야 한다.The warp knitting process for producing warp knitted fabrics using island-in-the-sea composite fibers requires high quality yarn properties, particularly smooth properties of yarns, because the knitting speed is high. In addition, since the post-processing process for manufacturing warp knitted paper has to go through various complicated steps such as weight loss, brushing, and dyeing, the internal structure characteristics of the island-based yarn crystal orientation (Fc) after seawater dissolution must be properly adjusted.
구체적으로 해도형 복합섬유의 해성분과 도성분 각각의 내부구조에 따라 특정되는 원사물성은 경편지 제조에 매우 중요하다.Specifically, the yarn property specified by the sea component and the internal structure of each island component of the island-in-the-sea composite fiber is very important for producing warp knitted paper.
해도형 복합섬유는 알칼리 이용해성(易容解性) 폴리머를 해성분으로 사용하고 섬유형성성 폴리머를 도성분으로 사용하여 이들을 해도형으로 복합 방사하여 제조되며, 주로 극세섬유를 제조하기 위한 목적으로 생산되고 있다.The island-in-the-sea composite fiber is manufactured by using an alkali-soluble polymer as a sea component and a fiber-forming polymer as a island component, and composite spinning them into an island-in-the-sea type, mainly for the purpose of producing ultrafine fibers. Is being produced.
다시 말해 해도형 복합섬유 제조후 이를 알칼리 용액으로 처리하여 알칼리 이용해성 폴리머인 해성분을 용출하므로서 도성분만으로 구성되는 극세섬유를 제조하게 된다.In other words, after preparing the island-in-the-sea composite fiber, it is treated with an alkaline solution to elute the sea component which is an alkali-soluble polymer, thereby producing an ultrafine fiber composed only of the island component.
이와 같이 해도형 복합섬유로부터 극세섬유를 제조하는 방법은 직접방사로 극세섬유를 제조하는 방법에 비해 방사 및 연신조업성이 우수하고 보다 세섬도인 극세섬유를 얻을 수 있는 장점이 있는 한편, 제직 또는 편직후 가공공정에서 해성분 폴리머를 유기용제 등으로 용출, 제거하는 공정이 필요하다.As described above, the method of manufacturing the ultrafine fibers from the island-in-the-sea composite fiber has the advantages of superior spinning and stretching operations and more fineness of fine fibers compared to the method of manufacturing the ultrafine fibers by direct spinning. After knitting, the process of eluting and removing the sea component polymer with an organic solvent in a processing step is required.
일반적으로 경편용 해도형 복합섬유에 사용되는 해성분 폴리머로는 알칼리 이용해성 공중합 폴리에스테르가 주로 사용된다. 그 이유는 특수 장치 및 회수 처리 비용이 많이 드는 유기용제를 사용하지 않고도 일반 폴리에스테르 직물의 감량 가공에 널리 적용되는 알칼리 용액 및 감량 설비에서 해성분의 용출이 가능하기 때문이다.Generally, as the sea component polymer used in warp knitted island-in-the-sea composite fiber, alkali-soluble copolyester is mainly used. The reason for this is that the dissolution of the sea component is possible in alkaline solutions and weight reduction facilities which are widely applied in weight reduction processing of general polyester fabrics without the use of special equipment and costly organic solvents.
도성분 폴리머가 나일론인 경우 해성분 용출시 나일론이 알칼리 용액에 의해 침해되는 정도가 매우 낮기 때문에 해성분의 용출 속도는 크게 중요하지 않으나, 도성분이 폴리에스테르인 경우는 알칼리에 취약하므로 해성분의 용출 속도가 낮은 경우 해성분이 완전히 용출되기 전에 도성분이 침해되어 용출후 원사 물성이 급격히 저하된다. 이로 인해 경편지의 기모성이 불량하게 되며 목표하는 최종 제품의 외관,촉감이 발현되기 곤란하다.When the water-based polymer is nylon, the dissolution rate of the sea component is not very important because the degree of nylon invasion by the alkaline solution is very low when the sea component is eluted. If the speed is low, the island component is violated before the sea component is completely eluted, and the yarn physical properties are drastically lowered after the eluting. This results in poor brushability of the warp knitted fabric and it is difficult to express the appearance and feel of the target final product.
반면 해성분의 용출속도가 빠르면 상기 문제들의 발생을 억제할 수 있을 뿐만 아니라 알칼리 농도,용출온도 및 시간을 감소시킬 수 있기 때문에 용출 비용의 절감과 함께 생산성을 증대시킬 수 있는 장점도 있다.On the other hand, if the dissolution rate of the sea component is fast, not only the occurrence of the above problems can be suppressed, but also the alkali concentration, elution temperature and time can be reduced, thereby reducing the elution cost and increasing productivity.
그러나 해성분의 용출 속도를 높이기 위해서는 공중합 화합물의 함량을 증가시켜야 하나, 과다하게 공중합 화합물의 함량이 증가하면 용출성은 향상되는 반면 폴리머의 융점이 없어지고 연화점만이 존재하는 무정형 폴리머가 되어 제사하는 것이 곤란하게 된다.However, in order to increase the dissolution rate of the sea component, the content of the copolymer compound should be increased. However, when the content of the copolymer compound is excessively increased, the elution property is improved, but the melting point of the polymer is eliminated and it is an amorphous polymer having only a softening point. It becomes difficult.
해도형 복합섬유 제조에 사용되는 알칼리 이용출성 폴리에스테르를 제조하는 종래 기술로서는, 첫째 폴리에스테르 중합공정 중에 디메틸-5-설포이소프탈레이트소디움솔트(이하 "DMIS"라고 한다) 또는 저분자량의 폴리알킬렌글리콜(이하 "PAG"라고 한다)을 공중합 시키는 방법과, 둘째 폴리에스테르와 고분자량의 PAG를 블랜딩 하는 방법과 셋째 폴리에스테르 중합체와 고분자량의 PAG를 블랜딩 하는 방법들이 알려져 있다.Conventional techniques for producing alkali-soluble polyesters used in the production of islands-in-the-sea composite fibers include, firstly, dimethyl-5-sulfoisophthalate sodium salt (hereinafter referred to as "DMIS") or low molecular weight polyalkyls during the polyester polymerization process. A method of copolymerizing lene glycol (hereinafter referred to as "PAG"), a method of blending a second polyester and a high molecular weight PAG, and a method of blending a third polyester polymer and a high molecular weight PAG are known.
이상에서 설명한 알칼리 이용출성 폴리에스테르를 해성분으로 사용하고 폴리에스테르를 도성분으로 사용하여 방사, 연신 및 가연 처리하는 방법으로 해도형 복합섬유를 제조하는 경우에는, 원사의 평활성(Flat property)이 저하되어 제편성이 불량해지는 문제가 있다.When the island-in-the-sea composite fiber is produced by the method of spinning, stretching and flaming by using the alkali-soluble polyester as described above as the sea component and the polyester as the island component, the flat property of the yarn is lowered. There is a problem that the knitting is poor.
보다 구체적으로 가연(False Twisting) 처리된 원사는 벌키(Bulky) 하기 때문에 고속 경편시 제편성이 저하된다. 또한 해성분 용출후의 원사물성이 나빠서 경편후 계속되는 기모공정에서 기모성이 저하되고 경편지의 외관 및 품질이 나빠지는 문제가 있었다.More specifically, since false twisted yarns are bulky, the knitting performance of the high speed warp knitting is reduced. In addition, since the raw material property after the sea component elution was bad, there was a problem that the brushing property is deteriorated and the appearance and quality of the warp knitted paper are deteriorated in the subsequent raising process after warp knitting.
본 발명의 목적은 이와 같은 문제점을 해결하기 위하여, 경편기의 니들과 원사간의 마찰이 작아 공정통과성이 좋아지는 원사 특성(이하 "평활성" 이라고 한다) 및 원사물성이 우수하여 경편용 원사로 특히 유용한 해도형 복합섬유를 제공하기 위한 것이다. 또다른 본 발명의 목적은 경편용 원사로 특히 적합한 해도형 복합섬유의 제조방법을 제공하고자 한다.The purpose of the present invention is to solve such problems, the yarn between the needle and the yarn of the warp knitting machine is less useful because the yarn properties (hereinafter referred to as "smooth") and the yarn property is particularly useful as warp knitting yarns It is to provide an island-in-the-sea composite fiber. Another object of the present invention is to provide a method for producing a island-in-the-sea composite fiber particularly suitable as warp knitting yarn.
도 1은 본 발명의 공정 개략도1 is a process schematic diagram of the present invention
※도면중 주요부분에 대한 부호 설명※ Explanation of main parts in drawings
1 : 방사구금 2 : 제1고뎃로울러1: spinneret 2: first go roller
3 : 제2고뎃로울러 4 : 와인더3: second gourd roller 4: winder
이와 같은 과제들을 달성하기 위한 본 발명의 경편용 해도형 복합섬유는 알칼리 이용해성의 공중합 폴리에스테르를 해성분으로 사용하고 주성분인 폴리에틸렌테레프탈레이트가 90몰% 이상인 폴리에스테르를 도성분으로 사용하여 방사 직접 연신 방식으로 제조된 경편용 해도형 복합섬유로서, 해성분 용출후의 도성분 원사결정배향도(Fc)가 0.80∼0.90인 것을 특징으로 한다.In order to achieve the above problems, the warp island-in-the-sea composite fiber of the present invention uses an alkali-soluble co-polyester as a sea component and direct stretching using a polyester terephthalate of 90 mol% or more as a main component. The island-in-the-sea island composite fiber for warp knitting prepared by the method, characterized in that the island component yarn crystal orientation (Fc) after dissolution of the sea component is 0.80 to 0.90.
또한 본 발명의 경편용 해도형 복합섬유의 제조방법은 알칼리 이용해성의 공중합 폴리에스테르를 해성분으로 사용하고 주성분인 폴리에틸렌테레프탈레이트가 90몰% 이상인 폴리에스테르를 도성분으로 사용하여 방사 직접 연신 방식으로 경편용 해도형 복합섬유를 제조함에 있어서, 아래 조건을 동시에 충족시킴을 특징으로 한다.In addition, the method for producing a warp island-in-the-sea composite fiber of the present invention uses an alkali-soluble copolyester as a sea component, and a warp knit using a direct-stretching method using a polyester whose main component is polyethylene terephthalate of 90 mol% or more. In preparing the water-soluble composite fiber, it is characterized by satisfying the following conditions simultaneously.
- 아 래 --Below-
·제1고뎃로울러의 속도(V1) : 1,000m/분∼5,000m/분Speed of the first high roller (V 1 ): 1,000 m / min to 5,000 m / min
·제2고뎃로울러의 속도(V2) : 1,500m/분∼6,000m/분Speed of the second high roller (V 2 ): 1500m / min to 6,000m / min
·제1고뎃로울러 상의 원사 모듈러스: 5∼35g/dYarn modulus on the first high roller: 5-35 g / d
·제2고뎃로울러 상의 원사 결정화도(Xc) : 25∼45%Yarn crystallinity (Xc) on the second high roller: 25 to 45%
이하 본 발명을 상세하게 설명한다.Hereinafter, the present invention will be described in detail.
먼저, 본 발명에서는 알칼리 이용해성인 공중합 폴리에스테르를 해성분 폴리머로 사용하고, 주성분인 폴리에틸렌테레프탈레이트가 90몰% 이상인 폴리에스테르를 도성분 폴리머로 사용하여, 이들을 통상의 해도형 복합방사구금(1)으로 복합방사한다.First, in the present invention, an alkali-soluble copolyester is used as a sea component polymer, and a polyester having 90 mol% or more of polyethylene terephthalate as a main component is used as a island component polymer, and these are used as a conventional island-in-the-sea composite spinneret (1). Compound spinning with.
이때 상기 해성분 폴리머로는 폴리에틸렌테레프탈레이트에 DMIS를 3∼15몰% 공중합 하고, 여기에 다시 수평균 분자량이 8,000 이상인 폴리에틸렌글리콜 4∼20중량%를 첨가하여 제조한 알칼리 이용성 공중합 폴리에스테르를 사용할 수 있다.In this case, an alkali-soluble copolyester prepared by copolymerizing 3-15 mol% of DMIS to polyethylene terephthalate and adding 4-20 wt% of polyethylene glycol having a number average molecular weight of 8,000 or more can be used. have.
계속해서 본 발명은 방사된 원사를 제1고뎃로울러(2) 및 제2고뎃로울러(3)를 통과시키면서 연신하고, 와인더(4)로 권취하여 해도형 복합섬유를 제조한다. 다시말해 본 발명은 방사와 연신을 동일공정에서 실시하는 방사 직접 연신 공법으로 제조한다.Subsequently, the present invention draws the spun yarn while passing through the first go roller 2 and the second go roller 3, and winds it up with a winder 4 to produce an island-in-the-sea composite fiber. In other words, the present invention is produced by the spinning direct stretching method in which spinning and stretching are performed in the same process.
본 발명은 방사, 연신 및 가연 공법으로 벌키(Bulky)한 해도형 복합섬유를 제조하는 방법과 비교시, 평활한 특성을 갖는 원사를 제조할 수 있어서, 고속경편에 더욱 유리한 장점이 있다.The present invention can produce a yarn having a smooth characteristic, compared to the method for producing a bulky islands-in-the-sea composite fiber by spinning, stretching and flammable method, there is a more advantageous advantage for high-speed warp knitting.
이때 제1고뎃로울러의 속도(V1)는 1,000∼5,000m/분으로 더욱 바람직하게는 1,000∼3,000m/분으로, 제2고뎃 로울러의 속도(V2)를 1,500m/분∼6,000m/분으로 설정한다. 제1고뎃로울 러(2) 및 제2고뎃로울러(3)의 속도가 상기 범위보다 낮으면 원사가 충분하게 배향결정화 되지않아 향후 기모공정에서 커팅이 불균일하게 되며 감량공정에서는 감량을 콘트롤 할 수 없게 된다.At this time, the speed of the first high roller (V 1 ) is 1,000 to 5,000 m / minute, more preferably 1,000 to 3,000 m / minute, the second high roller speed (V 2 ) 1,500 m / minute to 6,000 m / Set to minutes. If the speed of the first high roller (2) and the second high roller (3) is lower than the above range, the yarn will not be sufficiently oriented crystallization, the cutting will be uneven in the raising process in the future, the weight loss process can not control the weight loss do.
또한 제1고뎃로울러 및 제2고뎃로울러의 속도가 상기 범위를 초과하는 경우에는 원사내 도성분의 복굴절율 및 결정화도가 저하되어 본 발명의 원사 물성을 만족시킬 수 없고, 그로인해 경편작업성 등이 저하되는 문제가 발생된다.In addition, when the speed of the first high roller and the second high roller exceeds the above range, the birefringence rate and crystallinity of the island component in the yarn are lowered, so that the yarn physical properties of the present invention cannot be satisfied. The problem of deterioration arises.
제1고뎃로울러 및 제2고뎃로울러의 속도를 조절하는 것 외에도 연신온도, 연신배율, 냉각조건, 해도형 폴리머의 용융점도 등을 적절하게 조절하므로서 제사공정 각 단계에서의 원사물성들을 관리 할 수 있다.In addition to controlling the speeds of the first and second rollers, it is possible to manage the yarn properties at each stage of the weaving process by appropriately adjusting the stretching temperature, the draw ratio, the cooling conditions, and the melt viscosity of the island-in-the-sea polymer. .
먼저, 제1고뎃로울러 상의 원사 모듈러스는 5∼35g/d가 되도록 조절한다.제1고뎃로울러 상의 원사 모듈러스가 상기 범위를 벗어나는 경우에는 원사에 부여되는 응력이 과도해져 원사 다발이 터지거나 사절이 발생하여 방사조업성이 저하되는 문제가 발생 된다.First, the yarn modulus on the first high roller is adjusted to be 5 to 35 g / d. If the yarn modulus on the first high roller is out of the above range, the stress applied to the yarn becomes excessive and the bundle of yarns burst or the thread is broken. This causes a problem of deterioration in spinning operability.
또한 제2고뎃로울러 상의 원사 결정화도는 25∼45%가 되도록 제조조건을 설정한다. 만약 상기 범위보다 낮은 경우에는 연신구간 내에서 스트레치에 의한 장력이 작아 원사의 주행성이 나빠져 고뎃로울러 간의 감김 현상이 발생하여 연신공정이 곤란해지며 원사물성이 저하되고, 상기 범위보다 높은 경우에는 필라멘트가 고배향 결정화 되어 스티프 (Stiff) 해져 경편용 원사로 부적합한 문제가 발생된다.In addition, the manufacturing conditions are set such that the degree of crystallinity of the yarn on the second roller is 25 to 45%. If it is lower than the above range, the tension due to stretch is small in the drawing section, so that the running performance of the yarn is deteriorated, the winding phenomenon between the high rollers occurs, the drawing process is difficult, and the material property is lowered. High orientation crystallization and stiffness cause problems that are not suitable for warp knitting yarns.
제1고뎃로울러 상의 원사 모듈러스는 캡쳐를 사용하여 방사중인 사도상 원사를 제1고뎃로울러 후단부에서 절단하는 것과 거의 동시에 제1고뎃로울러 선단부에서 절단한 다음, 제1고뎃로울러 표면상에 권사된 필라멘트를 절단 즉시 샘플로 채취하여 후술하는 방법으로 원사 물성들을 측정한 값이다.The yarn modulus on the first roller is cut at the front end of the first roller and then wound on the surface of the first roller, almost simultaneously with the capture of the spinning aspirated yarn at the rear end using capture. It is a value taken from the sample immediately after cutting to measure the physical properties of the yarn by the method described below.
더욱 구체적으로 샘플 채취시에는 제1고뎃로울러에 권사된 필라멘트층 중에서 제1고뎃로울러 표면에 위치하는 필라멘트를 채취하며, 제1고뎃로울러 온도에 의해 원사물성이 변하는 것을 방지하기 위해 절단 즉시 채취 한다.More specifically, during sampling, the filament located on the surface of the first gourd roller is collected from the filament layer wound on the first gourd roller, and immediately cut to prevent the change of yarn properties by the first gourd roller temperature.
제2고뎃로울러 상의 원사 결정화도(Xc)는 캡쳐를 사용하여 방사중인 사도상 원사를 제2고뎃로울러의 선단부와 후단부에서 동시에 절단하고, 제2고뎃로울러 표면상에 권사된 필라멘트를 절단 즉시 샘플로 채취하여 후술하는 방법으로 원사 물성들을 측정한 값이다.The yarn crystallinity (Xc) on the second gourd roller is used to capture the spinning aspirated yarn at the leading end and the back end of the second gourd roller at the same time, and the wound filament on the surface of the second gourd roller as a sample immediately after cutting. It is a value obtained by measuring the yarn properties by the method described later.
이와 같이 방사 직접 연신 방법으로 제조, 권취된(도 1의 4) 본 발명의 경편용 해도형 복합섬유는 해성분 폴리머 용출후의 도성분 원사 결정배향도(Fc)가 0.80∼0.90 이다.Thus, the island-in-the-sea island composite fiber for warp knitted fabric of the present invention manufactured and wound by the spinning direct stretching method (4 in FIG. 1) has a degree-of-component yarn crystal orientation (Fc) of 0.80 to 0.90 after elution of the sea component polymer.
이상에서 살펴본 바와 같이 본 발명의 해도형 복합섬유는 해성분 폴리머 용출후의 도성분 원사의 내부구조[결정배향도(Fc)]가 적절하게 조화되어 있다. 그 결과 원사단면 형성성, 기모성 및 촉감 등이 우수하며, 기모 및 해성분 용출시 원사물성 저하가 최소화 된다. 그 결과 본 발명의 해도형 복합섬유는 기모 경편지 제조용 원사로 특히 적합하다.As described above, in the island-in-the-sea composite fiber of the present invention, the internal structure (crystal orientation degree (Fc)) of the island-based yarn after elution of the sea component polymer is suitably harmonized. As a result, the yarn cross-section formation, brushing properties and feel is excellent, and the reduction of the yarn properties during raising and seaweed dissolution is minimized. As a result, the island-in-the-sea composite fiber of the present invention is particularly suitable as a yarn for producing brushed warp knitted paper.
본 발명의 원사(복합섬유)는 해성분 용출전의 단사섬도가 2∼5데니어, 해성분 용출후의 단사섬도가 0.001∼0.3데니어 이다. 해성분 용출전의 해도형 복합섬유의 총섬도는 경편지의 후도 등을 고려하여 50∼150데니어인 것이 바람직 하나, 상기 총섬도를 특별하게 한정하는 것은 아니다.The yarn (composite fiber) of the present invention has a single yarn fineness of 2 to 5 deniers before sea component elution and a 0.001 to 0.3 denier after single sea component elution. The total fineness of the island-in-the-sea composite fiber before sea component elution is preferably 50 to 150 denier in consideration of the thickness of the warp knitted fabric, etc., but the total fineness is not particularly limited.
본 발명의 해도형 복합섬유로 경편지를 제편한 다음, 알칼리 용액으로 해성분을 용출하고, 기모하여 기모 경편지를 제조한다. 해성분의 용출은 해도형 복합섬유를 1% 농도의 수산화나트륨 용액(욕비 = 10:1)에서 95℃로 30분간 처리하여 실시한다.After knitting the warp knitted paper with the island-in-the-sea composite fiber of the present invention, the sea component is eluted with an alkaline solution and brushed to prepare a brushed warp knit. The dissolution of the sea component is carried out by treating the island-in-sea composite fiber with 95 ° C. for 30 minutes in a 1% sodium hydroxide solution (bath ratio = 10: 1).
본 발명의 해도형 복합섬유는 원사물성 특성에 기인하여 상기 해성분 용출공정이나 기모공정에서 원사 모듈러스 저하가 최소화 된다. 그 결과 기모성이 향상되며, 최종제품인 경편지의 외관 및 촉감이 우수하게 된다.The island-in-the-sea composite fiber of the present invention has minimal yarn modulus in the sea component eluting process or raising process due to its yarn property. As a result, the raising property is improved, and the appearance and feel of the warp knitted fabric as the final product are excellent.
본 발명에 있어서, 원사물성은 아래와 같이 평가 하였다.In the present invention, the yarn physical properties were evaluated as follows.
·강도 / 모듈러스Strength / Modulus
인스트롱 회사의 인장시험기로 10회 측정(시료길이: 25cm, 인장속도: 30cm/분) 하여 평균값을 구한다. 여기서 모듈러스는 초기 모듈러스를 의미한다.The average value is obtained by measuring ten times with a tensile tester of Instron Co., Ltd. (sample length: 25 cm, tensile speed: 30 cm / min). Here modulus means initial modulus.
·밀도(ρ)Density (ρ)
해도형 복합섬유를 노말헵탄과 카본테트라클로라이드 혼합용매로 구성된 밀도계(일본 시바야마 회사제품, 모델명 : Model SS)에 투입하여 23℃에서 1일동안 방치 후, 해성분과 도성분이 통합된 벌크한 상태의 밀도를 측정한다.The island-in-the-sea composite fiber was added to a density meter (normally manufactured by Shibayama, Japan, Model SS) consisting of a mixed solvent of normal heptane and carbon tetrachloride, and left at 23 ° C. for 1 day. Measure the density of
·결정화도[Xc(%)]Crystallinity [Xc (%)]
상기의 밀도(ρ)값을 바탕으로 이론적인 폴리에스테르의 완전 결정영역의 밀도값(ρc=1.457g/㎤)과 완전 비결정영역의 밀도값(1.336g/㎤)을 이용하여 아래 공식으로 구한다.Based on the density (ρ) value, the following formula is obtained by using the theoretical density value of the complete crystal region of polyester (ρc = 1.457 g / cm 3) and the density value of the complete amorphous region (1.336 g / cm 3).
·결정배향도(Fc)Crystal orientation (Fc)
X-선 회절분석기로 결정의 (010)면과 (100)면에 대해 방위각 주사(azimuthal scanning)를 행하여 결정배향의 특성을 나타내는 피크(peak)의 반가폭(FWHM, Full width at half-maximum intensity)을 측정하여 도성분의 결정배향도(Fc)를 계산하였다. 단, 해성분은 완전 무정형 상태이므로 방위각 주사에 의하여 나타난 피크를 전부 도성분의 결정면에 의한 피크로 간주한다. 반가폭(FWHM)으로부터 결정배향도(Fc)를 계산한 식은 다음과 같다.Full width at half-maximum intensity (FWHM) showing the characteristics of crystal orientation by performing azimuthal scanning on the (010) and (100) planes of the crystal with an X-ray diffractometer. ) Was calculated to calculate the crystal orientation (Fc) of the island components. However, since the sea component is completely amorphous, all peaks resulting from the azimuth scan are regarded as peaks due to the crystal plane of the island component. The equation for calculating the crystal orientation (Fc) from the full width (FWHM) is as follows.
이하 실시예 및 비교실시예를 통하여 본 발명을 더욱 구체적으로 살펴 본다. 그러나 본 발명이 하기 실시예에만 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples. However, the present invention is not limited only to the following examples.
실시예 1Example 1
디메틸-5-설포이소프탈레이트소디움이 4몰% 공중합 되어 있는 공중합 폴리에스테르에 수평균 분자량이 8,500인 폴리에틸렌글리콜 8중량%를 첨가하여 알칼리 이용해성 폴리머를 제조한다. 제조된 상기 알칼리 이용해성 폴리머를 해성분으로 사용하고, 고유점도가 0.65인 폴리에틸렌테레프탈레이트를 도성분으로 사용하여, 이들을 288℃에서 도성분 수가 36개인 해도형 복합방사 구금을 통해 방사한다. 계속해서 방사된 원사를 속도가 1,500m/분인 80℃의 제1고뎃로울러와 속도가 4,300m/분인 125℃의 제2고뎃로울러 사이에서 연신하고, 계속해서 4,257m/분의 권취속도로 권취하여 75데니어 24필라멘트의 해도형 복합섬유를 제조한다. 이때 방사구금 직하의 냉각조건은 상대습도 100%, 냉각풍 온도 20℃, 냉각풍 속도 0.4m/초 로 설정 하였다. 또한 제1고뎃로울러 상의 원사 모듈러스는 18.1g/d, 제2고뎃로울러 상의 원사 결정화도는 33.24%로 각각 설정 하였다. 이와 같이 제조한 해도형 복합섬유를 95℃의 1% NaOH 용액에서 해도형 복합섬유를 30분 동안 처리하여 해성분을 용출한다. 해성분 용출후의 도성분 단사섬도는 0.06 데니어 이다. 해성분 용출후의 원사물성을 앞에서 설명한 방법으로 평가한 결과는 표 2와 같다.상기 해도형 복합섬유를 표면조직의 원사로 사용하고, 섬도가 5데니어 이고, 비등수수축율이 28%인 공중합 폴리에스터 원사(고수축 원사)를 이면조직의 원사로 하여, 밀도가 23본/CM인 경편지를 제조한다. 이때 이면조직용 원사의 사용비율은 가공편지 전체중량에 대하여 26중량%로 한다. 이렇게 제조된 경편생지를 50% 수축되도록 기모한 다음, 계속해서 예비셋트(190℃)→감량(NaOH 농도 1% O.W.S, 98℃×30분)→염색(분산염료)→버핑가공→최종셋트(180℃)하여 가공 경편지 를 제조한 결과 기모성이 양호 하였고, 경편지의 외관 및 촉감이 우수 하였다.An alkali-soluble polymer is prepared by adding 8% by weight of polyethylene glycol having a number average molecular weight of 8,500 to a copolyester copolymerized with 4 mol% of dimethyl-5-sulfoisophthalate sodium. Using the prepared alkali-soluble polymer as a sea component, and polyethylene terephthalate having an intrinsic viscosity of 0.65 as a island component, they are spun through a island-in-the-sea composite spinneret having 36 island components at 288 ° C. The spun yarn was then drawn between a first high roller at 80 ° C. with a speed of 1,500 m / min and a second high roller at 125 ° C. with a speed of 4,300 m / min, and then wound at a winding speed of 4,257 m / min. A sea island type composite fiber of 75 denier 24 filaments is prepared. At this time, the cooling conditions immediately below the spinneret were set at a relative humidity of 100%, a cooling wind temperature of 20 ° C., and a cooling wind speed of 0.4 m / sec. In addition, the yarn modulus of the yarn on the first go roller was 18.1 g / d, and the degree of crystallinity of the yarn on the second go roller was 33.24%. The island-in-the-sea composite fiber thus prepared is treated with a island-in-the-sea composite fiber for 30 minutes in a 1% NaOH solution at 95 ° C. to elute the sea component. The island component single yarn fineness after sea component elution is 0.06 denier. The results of evaluating the yarn physical properties after dissolution of the sea component by the method described above are shown in Table 2. Co-polyester polyester having the island-in-the-sea composite fiber as the yarn for the surface structure, having 5 deniers of fineness and 28% boiling shrinkage Using a yarn (high shrink yarn) as a yarn of the backside structure, a warp knitted fabric having a density of 23 copies / CM is produced. In this case, the use ratio of yarn for backside tissue is 26% by weight based on the total weight of the processed letter. After raising the warp dough to be 50% shrinkage, and then preliminary set (190 ℃) → weight loss (NaOH concentration 1% OWS, 98 ℃ × 30 minutes) → dyeing (dispersant) → buffing → final set ( 180 ° C.), the processed warp knitted fabrics were fabricated with good brushing and had excellent appearance and feel.
실시예 2 ∼ 실시예 3 및 비교실시예 1 ∼ 비교실시예 2Example 2-Example 3 and Comparative Example 1-Comparative Example 2
제조조건을 표 1과 같이 변경한 것을 제외하고는 실시예 1과 동일한 공정 및 조건으로 75데니어 24필라멘트의 해도형 복합섬유를 제조한다. 단, 권취속도는 제2고뎃로울러 속도보다 1% 느리게 설정 하였다. 이와 같이 제조한 해도형 복합섬유를 95℃의 1% NaOH 용액에서 해도형 복합섬유를 30분 동안 처리하여 해성분을 용출한 다음, 해성분 용출후 원사물성을 앞에서 설명한 방법으로 평가한 결과는 표 2와 같다.Except for changing the manufacturing conditions as shown in Table 1 in the same process and conditions as in Example 1 to prepare a island-like composite fiber of 75 denier 24 filaments. However, the winding speed was set 1% slower than the second high roller speed. The islands-in-sea composite fiber prepared in this way was treated with island-in-sea composite fiber in 95% 1% NaOH solution for 30 minutes to elute the sea component, and then the raw material properties were evaluated by the method described above. Same as 2.
본 발명의 경편용 해도형 복합섬유는 해성분 용출후의 원사물성이 우수하여 경편지 제조시 기모성이 우수하게 되고, 촉감 및 외관이 우수한 경편지를 제조 할 수 있다. 이와 같은 효과로 인해 본 발명의 해도형 복합섬유는 기모 경편지 제조에 특히 유용하다.The island-in-the-sea composite fiber for warp knitted fabric of the present invention has excellent yarn property after dissolution of the sea component, and has excellent brushability in the manufacture of warp knits, and can produce warp knits with excellent feel and appearance. Because of this effect, the island-in-the-sea composite fiber of the present invention is particularly useful for producing brushed warp knits.
Claims (5)