KR100290536B1 - Manufacturing method of activated alumina molding - Google Patents
Manufacturing method of activated alumina molding Download PDFInfo
- Publication number
- KR100290536B1 KR100290536B1 KR1019980054925A KR19980054925A KR100290536B1 KR 100290536 B1 KR100290536 B1 KR 100290536B1 KR 1019980054925 A KR1019980054925 A KR 1019980054925A KR 19980054925 A KR19980054925 A KR 19980054925A KR 100290536 B1 KR100290536 B1 KR 100290536B1
- Authority
- KR
- South Korea
- Prior art keywords
- activated alumina
- water
- producing
- present
- hydration reaction
- Prior art date
Abstract
본 발명은 활성 알루미나 성형체의 제조방법에 관한 것으로서, 더욱 상세하게는 수산화알루미늄(Al(OH)3, 광물명: 깁사이트)을 급속열분해 및 분쇄하여 비정질 알루미나 분말을 만들고 바인더로써 물을 사용하여 구형의 성형체를 제조한 다음, 수분 챔버내에서 전 처리하여 수화 겔 및 의사베마이트 결정핵을 생성시키는 과정과, 계속해서 수화 겔과 의사베마이트 결정핵을 침상의 의사베마이트로 성장시킨 후, 이를 건조하고 소성함으로써 높은 강도, 충분한 비표면적 및 큰 기공부피를 나타낼 뿐만 아니라 제조공정중에 폐수를 전혀 발생시키지 않는 활성 알루미나 성형체의 제조방법에 관한 것이다.The present invention relates to a method for producing an activated alumina molded article, and more particularly, aluminum hydroxide (Al (OH) 3 , mineral name: Gibsite) is rapidly pyrolyzed and pulverized to form amorphous alumina powder and spherical using water as a binder. After forming a molded article of the present invention, the pre-treatment in the moisture chamber to produce a hydrogel and pseudo boehmite crystal nuclei, and then the hydrogel and pseudo boehmite crystal nuclei are grown into a needle-like pseudo boehmite By drying and firing, the present invention relates to a method for producing an activated alumina compact not only showing high strength, sufficient specific surface area and large pore volume, but also generating no waste water during the manufacturing process.
Description
도 1은 본 발명에 따른 활성 알루미나 성형체의 제조공정을 개략적으로 나타낸 공정도이다.1 is a process diagram schematically showing a manufacturing process of an activated alumina molded article according to the present invention.
[발명의 목적][Purpose of invention]
[발명이 속하는 기술분야 및 그 분야의 종래기술][Technical field to which the invention belongs and the prior art in that field]
본 발명은 활성 알루미나 성형체의 제조방법에 관한 것으로서, 더욱 상세하게는 수산화알루미늄(Al(OH)3, 광물명: 깁사이트)을 급속열분해 및 분쇄하여 비정질 알루미나 분말을 만들고 바인더로써 물을 사용하여 구형의 성형체를 제조한 다음, 수분 챔버내에서 전 처리하여 수화 겔 및 의사베마이트 결정핵을 생성시키는 과정과, 계속해서 수화 겔과 의사베마이트 결정핵을 침상의 의사베마이트로 성장시킨 후, 이를 건조하고 소성함으로써 높은 강도, 충분한 비표면적 및 큰 기공부피를 나타낼 뿐만 아니라 제조공정중에 폐수를 전혀 발생시키지 않는 활성 알루미나 성형체의 제조방법에 관한 것이다.The present invention relates to a method for producing an activated alumina molded article, and more particularly, aluminum hydroxide (Al (OH) 3 , mineral name: Gibsite) is rapidly pyrolyzed and pulverized to form amorphous alumina powder and spherical using water as a binder. After forming a molded article of the present invention, the pre-treatment in the moisture chamber to produce a hydrogel and pseudo boehmite crystal nuclei, and then the hydrogel and pseudo boehmite crystal nuclei are grown into a needle-like pseudo boehmite By drying and firing, the present invention relates to a method for producing an activated alumina compact not only showing high strength, sufficient specific surface area and large pore volume, but also generating no waste water during the manufacturing process.
일반적으로 비정질 알루미나 분말은 대략 Al2O3·0.5H2O의 분자식을 가지며ρ-,χ-,r-알루미나와 베마이트의 혼합물로 존재한다. 그중에서 침상의 의사베마이트는 결정성의 베마이트와 기본적으로 같은 결정구조를 가지며, Al2O3몰당 1.3 ∼ 1.8 몰의 물분자를 포함한다. 활성 알루미나는 상기 비정질 알루미나중r-알루미나를 의미하며, 이는 우수한 표면화학적 활성을 나타내므로 배기가스 정화, 석유화학, 화학공업 등에서 촉매담체로서 가장 적합하여서 그 수요의 약 50%를 차지하고 있으며, 또한 염색 및 제지산업에서 탈색제로도 많이 사용되고 있으며 전 산업에 걸쳐 수분흡착제 및 탈취제로 많이 사용되고 있다.Generally, amorphous alumina powder has a molecular formula of approximately Al 2 O 3 .0.5H 2 O and exists as a mixture of ρ- , χ- , r -alumina and boehmite. Among them, acicular pseudo boehmite has a crystal structure basically the same as that of crystalline boehmite, and contains 1.3 to 1.8 moles of water molecules per mole of Al 2 O 3 . Activated alumina refers to r -alumina in the amorphous alumina, which exhibits excellent surface chemical activity and thus is most suitable as a catalyst carrier in exhaust gas purification, petrochemical, chemical industry, etc., and accounts for about 50% of the demand. And it is also widely used as a bleaching agent in the paper industry and is widely used as a moisture adsorbent and a deodorant throughout the industry.
이러한 활성 알루미나 성형체를 제조하기 위한 공지 방법으로는 급속열분해법, 중화법 그리고 알콕사이드법이 있으며, 이들은 모두 수산화알루미늄(Al(OH)3, 깁사이트)을 출발물질로 한다.Known methods for producing such activated alumina compacts include rapid pyrolysis, neutralization, and alkoxide methods, all of which have aluminum hydroxide (Al (OH) 3 , Gibsite) as a starting material.
일반적으로 급속열분해법에 의한 활성 알루미나 성형체 제조는 수산화알루미늄(Al(OH)3, 깁사이트)을 375 ∼ 830℃의 유동상(fluidized bed)에서 급속열분해하여 비정질 알루미나 분말을 만들고, 이를 평균입도가 1 ∼ 7 ㎛ 정도 되게 분쇄한 후, 회전원판형 조립기나 유동상 조립기에서 물을 바인더로 해서 구형의 성형체를 제조한 다음, 수화하여 의사베마이트를 생성시키고, 건조 및 하소하여 활성 알루미나 성형체를 제조한다. 이와 다른 방법으로서, 물과 비정질 알루미나 분말을 혼합한 현탁액에서 수화를 행하고 이를 여과하고 수세하여 의사베마이트를 만든 다음, 질산, 염산, 포름산 등의 산을 첨가시켜 사출조립기로 원통형의 펠렛을 제조하고 이를 건조 및 하소하여 활성 알루미나 성형체를 제조하는 방법이 공지되어 있다.In general, active alumina molded body produced by rapid pyrolysis method is rapidly pyrolyzed aluminum hydroxide (Al (OH) 3 , Gibsite) in a fluidized bed of 375 ~ 830 ℃ to make amorphous alumina powder, the average particle size After pulverizing to about 1 to 7 μm, spherical shaped bodies are prepared by using water as a binder in a rotary disk granulator or fluidized bed granulator, and then hydrated to produce pseudoboehmite, followed by drying and calcining to prepare activated alumina shaped bodies. do. Alternatively, hydrated in a suspension of water and amorphous alumina powder, filtered, washed with water to form pseudoboehmite, and then a cylindrical pellet was prepared by an injection granulator by adding an acid such as nitric acid, hydrochloric acid, or formic acid. It is known to dry and calcinate it to produce activated alumina shaped bodies.
중화법은 수산화알루미늄을 염산, 질산, 황산 등의 산이나 가성소다 등의 알칼리에 녹인 후 중화시키거나, 또는 Al2(SO4)3, AlCl3, Al(NO3)3, NaAlO2또는 명반등의 알루미늄염 수용액을 중화시켜 베마이트 겔(gel)을 얻고 이를 여과, 세척 및 건조후 하소하여 분말형태의r-알루미나로 사용하거나 펠렛으로 제조하는 방법이다.The neutralization method dissolves aluminum hydroxide in an acid such as hydrochloric acid, nitric acid, sulfuric acid, alkali such as caustic soda, and neutralizes it, or Al 2 (SO 4 ) 3 , AlCl 3 , Al (NO 3 ) 3 , NaAlO 2 or alum. It is a method of neutralizing an aqueous aluminum salt solution such as to obtain a boehmite gel (gel), which is then filtered, washed and dried and calcined to use as r -alumina in powder form or as a pellet.
마지막으로, 알콕사이드법은 고순도 알루미늄 금속과 에틸렌을 원료로 알루미늄 알콕사이드를 제조하고 이를 물로 가수분해시켜 의사베마이트를 얻으며 성형, 건조 및 하소하여 담체로 사용하는 방법이다.Finally, the alkoxide method is a method of preparing aluminum alkoxide from high purity aluminum metal and ethylene as a raw material and hydrolyzing it with water to obtain pseudo boehmite, forming, drying and calcining to use as a carrier.
상술한 급속열분해법, 중화법 및 알콕사이드법은 모두 다 최종적으로r-알루미나를 얻을 수 있지만 성형성, 품질, 가격, 그리고 Na 함량 등에서 차이가 있게 된다. 이중 급속열분해법에 의하여 제조된r-알루미나는 제조비용이 저렴하고 충분한 비표면적 및 기공도를 갖고 있어 흡습제, 탈취제, 탈색제, 촉매담체 제조에 많이 적용되고 있다.The rapid pyrolysis method, the neutralization method, and the alkoxide method can all finally obtain r -alumina, but there are differences in moldability, quality, price, and Na content. The r -alumina produced by the rapid pyrolysis method has a low manufacturing cost and a sufficient specific surface area and porosity, so that it is widely applied to the preparation of a hygroscopic agent, a deodorant, a colorant, and a catalyst carrier.
상기에 나타낸 기존의 제조방법은 성형시 불균일한 수분분포와 복잡한 공정 및 하소과정에서 첨가물의 산화로 인한 공해물질 발생과 성형후 전 처리 공정이 도입되지 않으므로 수화반응시 안정한 결정상인 베이어라이트(bayerite)가 생성되어 비표면적과 기공부피를 감소시키고, 또한 현탁액을 수화한 후 여과하는 과정에서 다량의 폐수가 발생하는 단점이 있다. 이에 영국특허 제1,599,374호에서는 비정질 알루미나와 물과의 현탁액을 수화반응시키는 방법이 개시되어 있으나, 이는 과도한 물/알루미나 비율로 인해 베이어라이트의 생성을 억제하기 어려우며, 수화반응 종료후 여과 및 수세과정에서 상기에서 언급한 바와 같이 다량의 폐수가 발생하고, 또한 펠렛을 제조하기 위해서는 가소성이 요구되므로 이때 첨가하는 산 용액으로 인해 하소과정에서 공해물질이 발생하며, 제조공정이 복잡하기 때문에 제조비용이 상승하는 단점이 있다. 또한, 미국특허 제4,797,271호에서는 유동상에서 구형의 성형체를 제조하기 전에 냉수(5℃)로 비정질 알루미나 분말을 전 처리하여 성형체 제조시 분말내의 수분으로 인한 때이른 의사베마이트 생성을 억제시키고 성형성을 개선시키는 방법이 개시된 바 있으나, 이는 냉수로 전 처리하는 예비혼합 공정이 반드시 필요하며 유동상 조립기의 단점중 하나인 3 mm 이상의 구형 성형체를 제조하기가 불가능하기 때문에 성형체의 적용 분야갸 제한되는 단점이 있다.The conventional manufacturing method shown above is a Bayerite which is a stable crystalline phase during the hydration reaction because the generation of pollutants due to the non-uniform water distribution during the molding, the complex process and the calcination process, and the pretreatment process after molding are not introduced. Is generated to reduce the specific surface area and pore volume, and also has a disadvantage in that a large amount of wastewater is generated during the filtration of the suspension after hydration. Therefore, British Patent No. 1,599,374 discloses a method of hydrating a suspension of amorphous alumina and water, but it is difficult to suppress the production of Bayerite due to excessive water / alumina ratio, and the filtration and washing process after completion of the hydration reaction. As mentioned above, since a large amount of waste water is generated and plasticity is required to manufacture pellets, the acid solution to be added causes pollution during calcination, and the manufacturing process is complicated because the manufacturing process is complicated. There are disadvantages. In addition, U.S. Patent No. 4,797,271 also pretreats the amorphous alumina powder with cold water (5 ° C.) before producing spherical shaped bodies in the fluidized bed to suppress premature pseudo-boehmite formation due to moisture in the powders during molding. Although a method of improvement has been disclosed, it is necessary to pre-treat the pre-treatment with cold water, and it is impossible to manufacture spherical molded bodies of 3 mm or more, which is one of the disadvantages of the fluidized bed granulator. have.
[발명이 이루고자 하는 기술적 과제][Technical problem to be achieved]
이에 본 발명자들은 활성 알루미나 성형체 제조시 상기와 같은 문제점을 피하고 수화특성을 개선시켜 성형체의 크기가 균일하고 압축강도가 우수하며 비표면적과 기공도가 높은 활성 알루미나 성형체를 제조하기 위한 방법을 찾기 위해 예비적으로 무정형 알루미나 분말의 수화특성을 상세히 조사하였다. 이를 기초로 상기의 특성을 갖는 활성 알루미나 성형체를 제조하는데에 있어서 비정질 알루미나 분말의 입도, 바인더로서의 물과 알루미나 분말의 몰비, 수화반응 전의 전 처리, 수화반응 온도 및 시간 등이 상당히 영향을 미친다는 사실을 알게 되어 본 발명을 완성하였다.Therefore, the present inventors have avoided the above problems in the production of the activated alumina molded body and improved the hydration characteristics to find a method for manufacturing the activated alumina molded body having a uniform size, excellent compressive strength, and high specific surface area and porosity. In particular, the hydration characteristics of amorphous alumina powder were investigated in detail. The fact that the particle size of amorphous alumina powder, the molar ratio of water and alumina powder as a binder, pretreatment before hydration reaction, hydration reaction temperature and time, etc. have a significant effect in preparing activated alumina compacts having the above characteristics. The present invention has been completed.
따라서, 본 발명에서는 균일한 크기의 구형 성형체를 만들고, 이를 수화시키기 전 적당한 온도 및 상대습도를 가진 용기 내에서 전 처리를 수행하여 액상가교로 이루어진 무정형 알루미나 분말 전체에 고른 수화 겔과 의사베마이트 결정핵을 생성시켜 수화반응이 진행되는 동안 대부분의 무정형 알루미나 분말이 침상의 의사베마이트로 성장됨으로써 상기와 같은 특성을 나타내며 성형체를 제조하는 모든 공정에서 공해물질을 발생하지 않게 하는 활성 알루미나 성형체의 제조방법을 제공하는데 그 목적이 있다.Therefore, in the present invention, a spherical shaped body having a uniform size is formed, and before being hydrated, pre-treatment is performed in a container having a suitable temperature and relative humidity to hydrate gel and pseudo boehmite crystals evenly formed over the entire amorphous alumina powder made of liquid crosslinking. Most amorphous alumina powder is grown as needle-like pseudo-boehmite during the hydration reaction by generating nuclei, thus exhibiting the above characteristics and preventing the generation of pollutants in all processes of manufacturing the molded article. The purpose is to provide.
[발명의 구성 및 작용][Configuration and Function of Invention]
본 발명은 수산화알루미늄(Al(OH)3)을 급속열분해하여 얻은 비정질 알루미나 분말을 물을 바인더로하여 구형의 입상 조립품을 제조하고, 이를 수화, 건조 및 하소하여 활성 알루미나 성형체를 제조하는 방법에 있어서,The present invention provides a spherical granular granulated product obtained by rapid pyrolysis of aluminum hydroxide (Al (OH) 3 ) with water as a binder, and hydrated, dried and calcined to produce an activated alumina molded body. ,
상기 구형의 입상 조립품은 수화반응을 수행하기에 앞서서 수분 챔버에서 5 ∼ 60℃의 온도 및 50 ∼ 100%의 상대습도 조건하에서 30분 ∼ 24시간 동안 숙성시키는 전 처리 과정을 행한 다음, 동일한 수분 챔버내에서 70 ∼ 100℃로 1 ∼ 5시간 수화반응을 수행하는 것을 그 특징으로 한다.The spherical granular assembly is subjected to a pretreatment step of aging for 30 minutes to 24 hours at a temperature of 5 to 60 ° C. and a relative humidity of 50 to 100% in a moisture chamber prior to performing the hydration reaction, and then the same moisture chamber. It is characterized in that the hydration reaction is carried out at 70 to 100 ° C. for 1 to 5 hours.
이와 같은 본 발명을 더욱 상세히 설명하면 다음과 같다.Referring to the present invention in more detail as follows.
본 발명은 활성 알루미나 성형체의 제조방법에 있어서, 비정질 알루미나 분말에 물을 첨가하여 구형의 입상 조립품을 제조하고, 수화반응을 실시하기 전에 적당한 온도와 상대습도를 가진 용기 내에서 전 처리를 실시하여 수화반응에 앞서 수화 겔과 의사베마이트 결정핵을 미리 생성시키는 과정을 도입하는 것을 특징으로 하며, 계속되는 수화반응 과정에서 이를 침상의 의사베마이트로 성장되도록 함으로써 베이어라이트 결정의 생성을 최대한 억제시키고 비표면적, 기공부피, 강도 그리고 흡착특성 등을 증가시켜 흡착제 및 촉매담체로서의 성능 향상과 폐수의 발생을 억제하여 제조원가를 절감할 수 있는 것을 그 특징으로 한다.The present invention provides a method for producing an activated alumina molded body, wherein water is added to an amorphous alumina powder to prepare a spherical granular granulated product, and prior to the hydration reaction, a pretreatment is carried out in a container having a suitable temperature and relative humidity to hydrate. It is characterized by introducing a process for generating hydrated gel and pseudo boehmite crystal nuclei in advance of the reaction, and in the subsequent hydration reaction, it is grown into needle-like pseudo boehmite to suppress the formation of bayerite crystals as much as possible and the specific surface area. By increasing the pore volume, strength and adsorption characteristics, the manufacturing cost can be reduced by improving the performance as an adsorbent and catalyst carrier and suppressing the generation of waste water.
본 발명에서는 우선 평균 입자크기가 60 ㎛인 수산화알루미늄(Al(OH)3, 깁사이트) 분말을 유동상(fluidized bed)이나 로타리 킬른(rotary kiln)에서 375 ∼ 830℃의 온도로 0.05 ∼ 3초 이내에 급속열분해하여 대부분 비정질인ρ-알루미나로 전환시키고, 이를 볼밀(ball mill), 진동밀(vibrating mill) 또는 제트밀(jet mill) 등으로 1 ∼ 7 ㎛ 범위로 미세하게 분쇄하여 비정질 알루미나 분말을 제조한다.In the present invention, aluminum hydroxide (Al (OH) 3 , Gibbsite) powder having an average particle size of 60 μm is first applied at a temperature of 375 to 830 ° C. in a fluidized bed or rotary kiln at 0.05 to 3 seconds. After rapid pyrolysis, most of the amorphous alumina powder is converted into ρ -alumina, which is finely ground in a range of 1 to 7 μm by a ball mill, a vibrating mill, or a jet mill. Manufacture.
그 다음 회전원판형 조립기에서 물을 바인더로 하여 구형의 입상 조립품을 제조하는데, 이때 비정질 알루미나와 물과의 혼합물인 조립품은 액상가교(liquid bridge)를 통해 결합된다. 이때, 바인더로서 사용되는 물은 비정질 알루미나 분말에 대비하여 30 ∼ 50 중량% 정도로 사용하는 것이 바람직한 바, 바인더의 사용량이 너무 적으면 액상가교의 형성이 곤란하고, 상기 범위를 초과하여 과량 사용되면 성형 자체가 불가능해지는 문제가 있다.A spherical granular assembly is then manufactured using water as a binder in a rotating disc granulator, wherein the assembly, which is a mixture of amorphous alumina and water, is joined via a liquid bridge. At this time, the water used as the binder is preferably used to about 30 to 50% by weight compared to the amorphous alumina powder, if the amount of the binder is too small, it is difficult to form a liquid crosslinking, if the excess is used in excess of the molding There is a problem that makes itself impossible.
그런다음 물을 포함하고 있는 수분챔버에서 상기 성형체를 5 ∼ 60℃ 온도로 30분 ∼ 24시간 동안 숙성하여 수화 겔과 의사베마이트 결정핵을 생성시킴으로써 전 처리 과정을 마무리한다. 수화 전 처리에 이용되는 수분챔버는 5 ∼ 60℃ 온도 및 50 ∼ 100%의 상대습도가 유지되도록 한다. 만약 전 처리 온도가 5℃ 미만이면 의사베마이트 결정핵의 생성이 불가능하고, 60℃를 초과하면 수화시 베이어라이트가 많이 생성되며, 또한 상대습도가 50% 미만이면 수화 겔의 형성이 지연되고, 100%를 초과하여 수분이 응축되기 시작하면 성형체간의 응집현상이 일어난다.Then, the molded body is aged in a water chamber containing water at a temperature of 5 to 60 ° C. for 30 minutes to 24 hours to produce a hydrogel and pseudo boehmite crystal nuclei to complete the pretreatment process. The moisture chamber used for the pre-hydration treatment is maintained at a temperature of 5 to 60 ° C. and a relative humidity of 50 to 100%. If the pretreatment temperature is less than 5 ° C, the formation of pseudo boehmite nuclei is impossible, and if the temperature exceeds 60 ° C, a lot of bayerite is produced during hydration, and if the relative humidity is less than 50%, the formation of the hydrogel is delayed. If moisture starts to condense in excess of 100%, agglomeration between moldings occurs.
계속해서 상기 전 처리 과정에 이용된 수분챔버의 내부 온도를 70 ∼ 100℃로 승온하여 1 ∼ 5시간 수화반응을 진행시키면 의사베마이트는 침상의 결정으로 성장하게 된다. 만약, 수화반응의 온도가 70℃ 미만이면 의사베마이트가 적게 형성되며 이로 인하여 흡착특성이 감소하고, 100℃를 초과하면 성형체에 균열이 발생하여 압축강도의 현저한 저하를 초래한다.Subsequently, when the internal temperature of the moisture chamber used in the pretreatment is raised to 70 to 100 ° C. to proceed with the hydration reaction for 1 to 5 hours, the pseudo boehmite grows into needle crystals. If the temperature of the hydration reaction is less than 70 ℃, less pseudo boehmite is formed due to this decreases the adsorption properties, if the temperature exceeds 100 ℃ cracks in the molded body causes a significant decrease in the compressive strength.
상기한 바와 같은 수화반응이 완료되면, 110 ∼ 150℃에서 1 ∼ 3시간 건조시키고 300 ∼ 600℃의 온도로 2 ∼ 5시간 하소한다.When the hydration reaction as described above is completed, it is dried for 1 to 3 hours at 110 to 150 ℃ and calcined at a temperature of 300 to 600 ℃ 2 to 5 hours.
그 결과, 본 발명의 제조방법에 의해 제조된 활성 알루미나 성형체는 비표면적 270 ∼ 400 ㎡/g(BET, 질소흡착), 기공부피 0.4 ∼ 0.9 cc/g, 평균압축강도 120 ∼ 200 kgf/㎠ 그리고 상대습도 100%에서 35 ∼ 45 중량%의 수분흡착특성을 나타낸다.As a result, the activated alumina molded article produced by the production method of the present invention had a specific surface area of 270 to 400 m 2 / g (BET, nitrogen adsorption), pore volume of 0.4 to 0.9 cc / g, average compressive strength of 120 to 200 kgf / cm 2 and Water absorption characteristics of 35 to 45% by weight at 100% relative humidity.
상기에서 설명한 바와 같이 본 발명에 따른 활성 알루미나 성형체 제조방법에서는 첫째, 수화반응을 진행하기전 수분을 포함하고 있는 수분 챔버 내에서 성형체를 특정조건으로 전 처리하여 비정질 알루미나 분말 내부에 수화 겔과 의사베마이트 결정핵을 충분히 생성시키므로써 비교적 짧은 수화반응 시간 동안 비정질 알루미나 대부분을 의사베마이트로 전환시킬 수 있으며, 또한 적은 물/알루미나 몰비로 수화반응을 진행하므로 베이어라이트의 생성이 최대로 억제되어 우수한 흡착 특성 및 촉매 담지능을 갖는 활성 알루미나 성형체를 제조할 수 있고, 둘째, 다른 제조방법에 비해 공정이 단순하고 전체공정에 걸쳐 폐수가 발생하지 않으므로 제조비용을 크게 줄일 수 있는 효과가 있다.As described above, in the method for producing an activated alumina molded article according to the present invention, first, before the hydration reaction is carried out, the molded article is pre-treated under specific conditions in a moisture chamber containing water before the hydration gel and pseudo bead inside the amorphous alumina powder. By producing enough mite crystals, most of the amorphous alumina can be converted to pseudo-boehmite for a relatively short hydration time, and the hydration reaction is carried out at a low water / alumina molar ratio. It is possible to produce an activated alumina molded article having characteristics and catalyst supporting ability. Second, since the process is simple and waste water is not generated throughout the entire process compared to other manufacturing methods, the manufacturing cost can be greatly reduced.
이와 같은 본 발명을 실시예에 의거하여 상세히 설명하면 다음과 같은 바, 본 발명이 이에 한정되는 것은 아니다.When the present invention is described in detail based on the embodiments as follows, the present invention is not limited thereto.
[실시예 1]Example 1
깁사이트(Al(OH)3)를 급속열분해시키고 이를 분쇄한 평균입자 크기가 2.72㎛, 강열감량(800℃, 2시간)이 11.70%인 비정질 알루미나 분말 6 kg을 원료호퍼에 넣고 공급속도를 60 g/분으로 하여 회전원판형 조립기(직경 40cm, 영진기계 제작, 한국)에 투입하고 경사각 45°, 회전수 20 rpm으로 회전시키면서 증류수를 40 g/분으로 분사하여 직경이 5 mm인 구형 조립 입상물을 연속적으로 얻었다.Rapid pyrolysis of Gibbsite (Al (OH) 3 ) and grinding of it were carried out with 6 kg of amorphous alumina powder having an average particle size of 2.72 μm and a loss of ignition (800 ° C., 2 hours) of 11.70%. spherical granular granules with a diameter of 5 mm, injected into a rotating disk-type granulator (40 cm in diameter, manufactured by Youngjin Machinery, Korea) at 40 g / min and spraying distilled water at 40 g / min while rotating at an inclination angle of 45 ° and a rotation speed of 20 rpm. Water was obtained continuously.
상기 조립 입상물을 40℃ 및 상대습도 80%로 유지되고 있는 수분챔버(moisture chamber)에 넣고 1시간 동안 숙성하여 수화 겔 및 의사베마이트 결정핵을 생성시키고, 계속해서 수분챔버의 온도를 100℃로 승온하여 5시간 동안 수화반응을 행한 다음, 이를 꺼내어 150℃로 유지되고 있는 송풍형 건조기에서 1시간 동안 건조시켰다. 그런 다음 이를 회전식 하소로(직경 10 cm, 길이 180 cm, 린드버그사, 모델 54579, 미국)의 원료호퍼에 넣고 진동형 공급장치를 이용해 200 g/분의 속도로 500℃로 유지되고 있는 하소로 내에 투입하여 하소하였다. 이때, 회전식 하소로의 경사각도는 0.5°였으며 회전수는 8 rpm 이었고 체류시간은 20분 이었다. 이렇게 하여 제조된 성형체는 평균압축강도가 120 kgf/㎠, 비표면적 312 ㎡/g (BET, 질소흡착), 기공부피 0.45 cc/g, 그리고 상대습도 100%에서 약 41중량%의 수분흡착 특성을 나타내었다.The granulated granules were placed in a moisture chamber maintained at 40 ° C. and a relative humidity of 80% and aged for 1 hour to produce hydrated gel and pseudo boehmite crystal nuclei. The temperature of the moisture chamber was then 100 ° C. After heating to a hydration reaction for 5 hours, it was taken out and dried for 1 hour in a blow-type dryer that is maintained at 150 ℃. It was then placed in a raw material hopper of a rotary calcination furnace (10 cm in diameter, 180 cm in length, Lindberg, Model 54579, USA) and placed in a calcination furnace maintained at 500 ° C. at a rate of 200 g / min using a vibratory feeder. To be calcined. At this time, the inclination angle of the rotary calcination furnace was 0.5 °, the rotation speed was 8 rpm and the residence time was 20 minutes. The molded product thus obtained had moisture absorption characteristics of about 41 wt% at an average compressive strength of 120 kgf / cm 2, specific surface area of 312 m 2 / g (BET, nitrogen adsorption), pore volume of 0.45 cc / g, and relative humidity of 100%. Indicated.
[실시예 2]Example 2
상기 실시예 1과 동일한 방법으로 구형 조립 입상물을 제조하되, 수분 챔버의 온도를 60℃로 하여 1시간 전처리를 행한 다음, 100℃의 온도로 5시간 수화한 다음, 상기 실시예 1과 동일한 방법으로 물성을 측정한 결과, 성형체의 평균압축강도 약 150 kgf/㎠, 비표면적 325 ㎡/g, 기공부피 0.56 cc/g 그리고 상대습도 100%에서 약 44.7 중량%의 수분흡착 특성을 나타내었다.A spherical granulated granule was prepared in the same manner as in Example 1, but pretreatment was performed for 1 hour with the temperature of the moisture chamber at 60 ° C., followed by hydration at 100 ° C. for 5 hours, followed by the same method as in Example 1. As a result of measuring the physical properties, the average compressive strength of the molded article was about 150 kgf / cm 2, specific surface area of 325 m 2 / g, pore volume 0.56 cc / g, and relative humidity of 100%.
[실시예 3]Example 3
상기 실시예 1과 동일한 방법으로 구형 조립 입상물을 제조하되, 5℃로 냉각된 증류수를 사용하여 성형하고, 20℃의 온도로 유지되는 수분 챔버에서 2시간 전처리한 다음 100℃에서 5시간 수화하였다. 그런 다음 상기 실시예 1과 동일한 방법으로 건조하고 하소하여 물성을 측정한 결과, 성형체의 평균압축강도는 약 165 kgf/㎠, 비표면적 350 ㎡/g, 기공부피 0.73 cc/g, 그리고 상대습도 100%에서 수분 흡착량은 약 45 중량%이었다.A spherical granulated granule was prepared in the same manner as in Example 1, but was molded using distilled water cooled to 5 ° C., pretreated for 2 hours in a moisture chamber maintained at 20 ° C., and then hydrated at 100 ° C. for 5 hours. . Then, in the same manner as in Example 1 and dried and calcined to measure the physical properties, the average compressive strength of the molded body is about 165 kgf / ㎠, specific surface area 350 ㎡ / g, pore volume 0.73 cc / g, and relative humidity 100 The moisture adsorption amount in% was about 45% by weight.
[비교예 1]Comparative Example 1
상기 실시예 1과 동일한 방법으로 제조하되, 다만 수화반응 전 처리를 행하지 않고 곧 바로 수화, 건조 및 하소를 수행하여 활성 알루미나 성형체를 제조하였다. 상기 실시예 1과 동일한 방법으로 물성을 측정한 결과, 성형체의 평균압축 강도는 약 90 kgf/㎠, 비표면적 270 ㎡/g, 기공부피는 0.42 cc/g, 그리고 상대습도 100%에서 약 35 중량%의 수분흡착 특성을 나타내었다.It was prepared in the same manner as in Example 1, except that the active alumina molded body was prepared by performing hydration, drying, and calcining immediately without performing the pre-hydration reaction. As a result of measuring the physical properties in the same manner as in Example 1, the average compressive strength of the molded product was about 90 kgf / cm 2, specific surface area 270 m 2 / g, pore volume 0.42 cc / g, and about 35 weight at 100% relative humidity. Water adsorption characteristics were shown.
[발명의 효과][Effects of the Invention]
상기에서 설명한 바와 같이, 본 발명은 활성 알루미나 성형체를 제조하는 방법에 있어 수화반응을 진행하기전, 전 처리 과정에서 물과 비정질 알루미나 분말과의 최초의 반응으로 인해 형성되는 수화 겔과 의사베마이트 결정핵을 수화반응에 앞서 생성시킴으로써 수화반응시 안정한 결정상인 베이어라이트의 생성이 거의 억제되고 대부분 침상의 의사베마이트 결정으로 성장하게 되어 우수한 물성의 활성 알루미나 성형체를 제조할 수 있을 뿐만 아니라 폐수의 발생이 없고 공정이 단순하여 생산비용을 대폭 줄일 수 있는 효과가 있다.As described above, the present invention relates to a hydrogel and pseudo boehmite crystals formed by the first reaction between water and amorphous alumina powder in the pretreatment process before proceeding with the hydration reaction in the method for producing the activated alumina compact. By generating the nuclei prior to the hydration reaction, the formation of the bayerite, which is a stable crystal phase during the hydration reaction, is almost suppressed, and most of the growth is made of acicular pseudo-boehmite crystals. There is no effect and the process is simple, which can greatly reduce the production cost.
Claims (3)