KR100276371B1 - 앵커식 고정수단을 천공구멍에 고정시키는데 사용되는 2성분-모르타르 및 그 장치 - Google Patents
앵커식 고정수단을 천공구멍에 고정시키는데 사용되는 2성분-모르타르 및 그 장치 Download PDFInfo
- Publication number
- KR100276371B1 KR100276371B1 KR1019930018506A KR930018506A KR100276371B1 KR 100276371 B1 KR100276371 B1 KR 100276371B1 KR 1019930018506 A KR1019930018506 A KR 1019930018506A KR 930018506 A KR930018506 A KR 930018506A KR 100276371 B1 KR100276371 B1 KR 100276371B1
- Authority
- KR
- South Korea
- Prior art keywords
- mortar
- compound
- curable
- curing agent
- component
- Prior art date
Abstract
본 발명에 따른 앵커식 고정수단을 천공구멍에 고정시키기 위한 2성분-모르타르는 무기질계 경화성 화합물로서 수경성 화합물 및/또는 중축합성 화합물을 포함하고 유기질계 경화성 화합물로서 경화성 비닐에스테르를 포함한다. 이러한 2성분-모르타르는 다중챔버형 장치에 배치되는 것이 적합하다.
Description
앵커식 고정수단을 천공구멍에 고정시키기 위해서는 경화성 모르타르 재료, 즉 공지의 소위 2성분-모르타르가 매우 중요한 의미를 가진다. 2성분-모르타르라는 것은 한편으로 하나의 경화제 성분 또는 분리되어 있거나 혼합되어 있는 2이상의 경화성 성분을 포함하고, 다른 한편으로 경화제를 포함하는 재료를 의미한다. 경화성 성분이, 예컨대 혼합 및/또는 반응을 저지하는 분리벽의 파괴에 의해 경화제에 접촉되면, 모르타르가 경화된다. 유기질계의 모르타르 재료는 일찍부터 시장을 점유하고 있는 무기질계의 2성분-모르타르 재료와 함께 상당한 시장 점유율을 차지하고 있다. 이때, 무기질계 또는 유기질계의 모르타르 재료는, 예컨대 가공 기술적 및 비용 기술적 측면에서 재료내에 내재하는 장점 및 단점을 각각 가진다. 이러한 장단점에는 혼합문제, 가사(可使)시간, 경화특성, 온도 의존도, 내식성, 화학안정성 및 노화(老化)안정성이 속한다.
상기한 장점을 서로 결합하기 위하여, 무기질 모르타르로 앵커식 고정수단을 고정시킨 다음, 경화 중에 또는 경화 후에 그 모르타르 재료에 유기질 단량체 또는 다른 적은 분자량의 경화성 화합물을 함침시키는 방식이 이미 제안되어 있다. 이러한 처리방식은 다단계성을 가진다는 단점은 별개로 하더라도, 이미 예컨대 공극률 및/또는 점성도에 의해 제한되는 상이한 함침깊이 때문에 재현가능한 결과를 얻을 수 없다는 단점을 가진다. 또한, 앵커식 고정수단을 천공구멍에 고정시키기 위하여 포틀랜드 시멘트와 경화성 불포화 폴리에스테르(UP)의 혼합물을 기초로 하는 모르타르 재료를 사용하는 것도 이미 시도된 바 있다. 그러나, 혼합의 오차를 피하기 위해 미리 기성품화된 포틀랜드 시멘트/UP의 혼합물은 고정 강도의 노화안정성이 극히 작아 이에 상응하여 앵커식 고정효과가 약해지는 것으로 판명된 점은 별개로 하더라도 예컨대 극히 불충분한 지지수명을 가진다는 현저한 단점을 나타낸다.
따라서, 본 발명의 목적은 상기 모르타르 재료의 단점을 제공하지 않으면서 상기 상이한 모르타르 재료의 장점을 구비하는, 앵커식 고정수단을 천공구멍에 고정시키는데 사용되는 모르타르를 제공하는 것이다.
이러한 목적은 무기질 및 유기질을 기초로 하는 경화성 화합물과 경화제를 함유하고, 필요에 따라서는(반응성) 충전제, 용매, 경화 촉진제 및 응고 촉진제와 같은 촉진제, 점성도 조절제, 안정제 및 다른 통상의 모르타르 성분을 함유하는, 앵커식 고정로드와 같은 앵커식 고정수단을 천공구멍에 고정시키는데 사용되는 이성분 또는 다성분 모르타르에 있어서, 상기 무기질 경화성 화합물은 수경성(水硬性) 화합물 및/또는 무기질 중축합성(重縮合性)화합물을 함유하고, 상기 유기질 경화성 화합물은 경화성 비닐에스테르를 함유함으로써 달성된다.
본 발명에 따른 모르타르는 혼합물 중에 전혀 상이한 종류의 경화성 화합물을 포함하는 경우라 할지라도, 상이한 종류의 화합물의 혼합물을 포함하는 공지의 모르타르보다 극히 우수한 지지력을 가진다. 경화성 불포화 폴리에스테르와 포틀랜드 시멘트를 기초로 하는 공지의 2성분-모르타르의 경우에는 지지력이 보다 약하기 때문에 혼합물의 제조를 사용하기 바로 직전에만 그것도 설치장소에서 수행해야 한다. 부가적으로 경화제도 바로 이때에 혼합되어야 한다. 이러한 처리방식은 번거로을 뿐 아니라 혼합과정이 여러번 있는 경우에는 혼합이 잘못될 위험이 있어 궁극적으로 얻어지는 상기 형태의 모르타르를 쓸모없는 것으로 만들게 된다.
본 발명에 따른 모르타르의 또 다른 장점은 무엇보다도 수축성향이 감소되고 내열형상(耐熱形狀) 안정성이 증가되고, 내화성(耐火性)의 개선 및 기후조건에 대한 저항성이 개선되고 결합강도가 향상되고, 팽창계수가 콘크리트/강철에 비해 더 좋아지며, 장기간의 거동 및 온도변화에 대해 안정성이 좋아진다는데 있다. 특히, 높은 습윤력 때문에 젖어 있는 천공구멍 및/또는 먼지가 많은 천공구멍에도 아무 문제없이 사용할 수 있다는 점에서 유리하다. 탁월한 흡수효과가 달성된다. 또한, 어떠한 경우에도 현저히 양호한 강도와 천공구멍벽에의 접착력을 달성할 수 있게 되어 흡수정도를 측정할 경우 천공벽 사이의 공지의 2성분-결합앵커 시스템, 예컨대 콘크리트와 모르타르 사이에서와 달리 모르타르와 앵커식 고정수단 사이의 박리가 생기지 않는다.
또한, 장기간의 시험시에도 현저한 화학안정성 때문에 예컨대 불포화 폴리에스테르 수지-포틀랜드 시멘트의 모르타르에서 알려져 있는 불량한 변질이 없는 것으로 입증되었다. 아울러, 가소제(可塑劑)를 사용하지 않고도 작업할 수 있음으로 인하여 높은 응집력과 접착력이 보장된다.
바람직하게는 경화가능한 수경성 화합물로서 시멘트, 특히 알루민산염 시멘트가 사용된다. 이러한 알루민산염 시멘트는 주로 반응성 화합물로서 일알루민산칼슘과 같은 알루민산칼슘 및/또는 이알루민산칼슘을 포함하며, 예컨대 산화알루미늄, 규산알루민산칼슘 및 페라이트와 같은 다른 함유물도 포함될 수 있다. Al2O3의 분석값은 필수적인 것은 아니지만, 종종 35%를 넘게 된다. 통상적으로는 과도할 정도로 산화철이 없거나 산화철의 함량이 적은 시멘트, 즉 산화철의 함량이 약 10 중량% 이하, 특히 5 중량% 이하이고, 매우 바람직하게는 2 또는 1 중량% 이하인 시멘트가 효과적인 것으로 판명되었다. 즉, 알루민산염 시멘트와 함께 또는 그대신에 예컨대 산화철 함량이 적은 고로(高爐) 시멘트를 사용하여도 효과적인 것으로 판명되었다. 본 발명의 범위에서 사용할 수 있는 경화가능한 수경성 화합물의 또다른 예는 석고이다. 석고/시멘트 혼합물은 높은 황산염 저항성을 가지는 시멘트를 사용하는 경우에 한해 가능하다.
물 또는 수용액의 존재하에 중축합되는 무기질 재료에는 무엇보다도 규산염재료, 특히 가용성 또는 용해된 SiO2및/또는 무정질 SiO2가 속하며, 이 SiO2는 부분적으로, 예컨대 50 중량%까지 Al2O3로 대체될 수 있다. 이러한 물질은 알칼리 수산화물, 특히 NaOH 및/또는 KOH와, 알칼리 규산염물, 그중에서도 특히 물 유리(water glass) 및/또는 변성 고령토를 포함하며, 수산화물 및/또는 규산염물은 경화를 위한 수용액으로 사용될 수 있다. 이러한 형태의 물질은 예컨대 EP-0148 280에 기재되어 있으며, 기재된 물질은 본 발명의 측면에서 사용될 수 있는 것으로 고려된다.
비닐에스테르로서는 특히 우레탄아크릴레이트 및/또는 에폭시아크릴레이트, 그중에서도 특히 이들의 메타크릴레이트 형태가 효과적인 것으로 판명되었다. 바람직하게는 예컨대 독일연방공화국 공개 공보 OS 39 40 309에 기재된 바와 같은 우레탄아크릴레이트, 예를 들자면 비스페놀-A, 노볼락(Novolac) 또는 디이소시아나이드디페닐메탄, 헥사디이소시아나이드 등의 이소시아나이드를 기초로 하는 비닐에스테르우레탄이 사용된다.
에폭시아크릴레이트에는 무엇보다도 아크릴레이트 형태, 특히 메타크릴레이트 중에서도 디메타크릴레이트 형태의 비스페놀글리시딜-화합물을 기초로 하는 에폭시아크릴레이트가 속한다. 그 중에서도 예컨대 약 500-800의 분자량을 가진 비스페놀-A를 기초로 하는 에폭시메타크릴레이트, 예컨대 약 450-750의 분자량을 가진 비스페놀-F를 기초로 하는 에폭시메타크릴레이트, 예컨대 3-8개의 페놀핵수에 상응하는 750-2000의 분자량을 가진 노볼락을 기초로 하는 에폭시메타크릴 레이트가 사용될 수도 있지만 비스페놀글리시딜-화합물의 디메타크릴레이트 및 다른 비스페놀에폭시드와 함께 또는 그 대신에 에틸렌 산화물이 변태된 비스페놀, 그중에서도 비스페놀 A, F 및 노볼락의 대응하는 메타크릴레이트(아크릴레이트)가 사용될 수 있다.
무기질 경화성 화합물(즉, 경화가능한 수경성 및 중축합성의 화합물)과 유기질 경화성 화합물(비닐에스테르)의 총량은 경화제를 제외하고 전체 모르타르의 30-99 중량%, 특히 40-85 중량%인 것이 적합하다. 본 발명의 양호한 실시예에 따라, 무기질 경화성 화합물과 유기질 경화성 화합물의 중량비는 1:4 내지 3:1, 특히 1:3 내지 2:1이다. 또한, 본 발명에 따른 모르타르는 경화가능한 수경성 화합물 및/또는 중축합성 화합물과 경화성 비닐에스테르와 함께 불포화 에스테르, 에폭시드, 우레탄을 형성할 수 있는 능력을 가진 이소시아나이드와 같은 단일중합체 또는 공중합체로 될 수 있는 화합물을 대개의 경우 적은 양으로 포함한다. 특히, 동시에 확실한 용매기능을 가지는 반응성 희석제가 경화제를 제외하고 모르타르 전체의 1-60 중량%, 바람직하게는 10-40 중량%의 양으로 포함될 수 있다. 반응성 희석제로서는 예컨대 스티롤, α-메틸스티롤, 알킬화된 스티롤, 디비닐벤졸, 저분자 말레산염, 알릴 화합물과 같은 화합물과, (메타)아크릴아미드, 메틸(메타)아크릴레이트, 에틸(메타)아크릴레이트, 프로필(메타)아크릴레이트, 부틸(메타)아크릴레이트, 에틸헥실(메타)아크릴레이트, 네오펜틸글리콜(메타)아크릴레이트, 에틸렌글리콜디(메타)아크릴레이트, 프로필렌글리콜디(메타)아크릴레이트, 부타디올디(메타)아크릴레이트, 글리세린(메타)아크릴레이트, 히드록실알킬(메타)아크릴레이트, 알콕실화된 비스페놀-A-디(메타)아크릴레이트 및 글리시딜메타크릴레이트와 같은 아크릴 화합물과 메타크릴 화합물을 고려할 수 있다. 여기에 명시된 것들과 관련하여, DE-OS 39 40 138에 기재된 바와 같은 싸이클로 지방족의 단일중합체 또는 공중합체로 될 수 있는 화합물이 특히 적합하게 사용된다. 반응성 희석제는 반응성 희석제와 비닐에스테르의 총량에 대하여 5-90중량%, 특히 30-80 중량%의 양으로 포함되는 것이 적합하다.
경화제로서는 방향족 중합체로 될 수 있는 화합물로 알려진 경화제, 즉 과산화화합물이 사용된다. 이러한 화합물로는 디벤조일퍼록사이드, 메틸에틸케톤퍼록사이드, 3차-부틸퍼벤조산염, 싸이클로헥사논퍼록사이드, 라우릴퍼록사이드 및 큐몰하이드로퍼록사이드를 고려할 수 있다. 또한, 과산화물은 가소제를 사용할 필요없이, 예컨대 수용액의 형태로도 사용될 수 있다. 물 또는 수용액은 경화제로서의 역할을 하는 동시에 경화가능한 수경성 화합물을 위한 수화작용제 또는 중축합성 화합물을 위한 반응매체로서의 역할을 한다.
경화제는 과산화물로 되는 한에는 비닐에스테르에 대해 2 내지 20 중량%, 바람직하게는 7 내지 13 중량%의 양으로 투입되며, 수경성 화합물을 위한 경화제 또는 수화작용제로서의 물은 상기 수경성 화합물에 대해 10 내지 80 중량%, 바람직하게는 30 내지 50 중량%의 양으로 사용된다. 또한, 모르타르의 점성도도 물의 양에 의해 영향을 받게 된다. 수용액으로서는 유기 수용액, 예컨대 알콜기의 수용액, NaOH 및 KOH와 같은 알칼리 수산화물의 수용액, 필요에 따라서는 SiO2를 분산시킨 알칼리 수산화물 수용액, 또는 알칼리 규산염 수용액을 특히 중축합성 재료를 경화시키는데 사용될 수 있다. 이러한 용액 대신에 분산액도 적합하다.
이와는 별도로, 원광석 상태의 이산화규소 또는 화성 이산화규소, 벤토나이트, 셀룰로오스, 고령토 등의 공지된 첨가물과 같은 응결제, 용해제, 틱소트로피화제가 포함될 수 있으며, 이들 첨가물은 존재하는 한 통상 0.1-8 중량%의 양으로 존재하게 된다.
필요에 따라 사용되는 통상적인 다른 모르타르 성분에는 모래, 석영, 유리알 및 중공유리알, 강옥, 백묵, 활석, 세라믹과 같은 충전제가 경화제를 제외하고 모르타르 전체의 0-60 중량%, 바람직하게는 10-50 중량%의 양으로 포함된다.
충전제 또는 충전제의 구성성분으로서는 섬유, 예컨대 유리 섬유, 세라믹 섬유, 특히 마이크로 유리섬유 등의 경사 섬유와 같은 무기질 섬유와, 유기질 섬유 중에서도 특히 합성 섬유가 효과적인 것으로 판명되었다. 합성 섬유로는 예컨대 50 내지 150㎛, 바람직하게는 80 내지 120㎛, 특히 약 100㎛의 길이를 가지는 예컨대 폴리에틸렌 섬유 및/또는 폴리프로필렌 섬유를 사용한다. 가늘고 긴 섬유 또는 적당한 금속박이나 굵은 실을 꼬아 접속함으로써 제조되고 예컨대 5 내지 15m2/g의 표면적을 가지는 원섬유를 구비하는 섬유가 특히 적합하다. 충전제로서는 상기한 섬유를 예컨대 중공유리알, 모래 등과 혼합하여 사용할 수 있다. 이러한 섬유를 바람직하게는 전술한 것과 같은 다른 충전제와 함께 수성성분(水性成分) 중에 함유시키는 것이 특히 바람직하고, 수성성분에는 라디칼 경화제를 포함시킬 수 있다. 섬유는 경화제를 제외하고 전체 모르타르 재료의 통상 0.1 내지 5 중량%, 바람직하게는 0.5 내지 3 중량%의 양으로 포함된다.
경화과정 또는 응고과정은 경화제의 양에 의해서 뿐만 아니라 경화촉진제에 의해 영향을 받는다. 수경성 성분에 대해서는, 시멘트에 대하여 0.01-2 중량%의 양인 통상의 응고촉진제 또는 경화촉진제, 예컨대 알칼리 탄화물, 알칼리 수산화물, 알루민산염 외에 유동화제(流動化劑), 예컨대 콘크리이트 유동화제 및 시멘트 혼합물, 예컨대 포틀랜드 시멘트와의 혼합물, 또는 N,N-디메틸아닐린, N,N-디에틸아닐린, N,N-디이소프로필리덴-p-톨루이딘, N,N-디메틸-p-톨루이딘, N,N-비스(2-히드록시에틸)-크실리딘과 같은 아민을 사용할 수 있으며, 또한 비닐에스테르에 대해서는, 예컨대 코발트나프테네이트 또는 코발트 옥토이트와 같은 Co, Mn, Sn 또는 Ce의 염 및/또는 중금속염이 바람직하게는 0.02-1.0 중량%의 양으로 사용될 수 있다.
본 발명의 목적은 경화성 모르타르 성분 및 경화제뿐 아니라, 필요에 따라서는 충전제, 용매, 응고촉진제 및 경화촉진제와 같은 촉진제 및/또는 다른 통상의 모르타르 성분을 포함하는 2성분 모트타르에 의해 앵커식 고정수단을 천공구멍에 고정시키는데 사용되는 2챔버형 및 다중챔버형 장치이며, 이 장치에서 경화성 모르타르 성분은 반응을 저지하는 개재벽에 의해 상기 경화제로부터 분리되고, 상기 장치는 경화성 모르타르 성분으로서 수경성 화합물 및/또는 무기질 중축합성 화합물과 비닐에스테르를 수용하고, 경화제로서 과산화화합물과 물 또는 수용제를 수용한다.
2챔버형 장치 또는 다중챔버형 장치는 금속박제 주머니, 소위 포일 팩으로서 형성될 수 있으며, 공통의 고정 바닥 부분을 구비할 수 있다. 공통의 바닥 부분은 금속박제 주머니에서 분리되어 있는 별도의 채널을 구비하고, 이 채널은 압출관(押出管)에 의해 공통의 압출 구멍에 연통되고, 압출관에는 필요에 따라 정적혼합기로서 관형 혼합요소가 설치될 수 있다. 모르타를 성분을 수용하는 상호 일체로 연결된 금속박제 주머니는 일체로 금속박제 주머니로부터 압출함으로써 배출됨과 동시에 혼합이 일어나 앵커식 고정수단을 천공구멍에 고정시킬 수 있다.
2챔버형 장치는 하나의 챔버내에 경화성 성분을 수용하고, 다른 챔버내에 양경화성 성분용의 경화제를 수용하는 것이 바람직하다. 그러나, 상기 장치는 하나의 챔버내에 비닐에스테르-경화제와 함께 경화가능한 수경성 화합물 또는 중축합성 화합물을 수용하고, 다른 챔버내에 경화가능한 수경성 화합물 또는 중축합성 화합물용의 수용성 경화제와 함께 비닐에스테르를 수용할 수도 있다. 이때에는 종종 용해중개물이 필요하다. 특히 금속박제 주머니를 기초로 하는 다중챔버형 장치에서는, 상이한 경화성 모르타르 재료를 따로 따로 경화제로부터 분리하여 수용할 수 있다.
다중챔버형 장치는 모르타르 성분, 대개의 경우 경화제가 마이크로캡슐화되어 있는 장치를 포함한다. 충전제, 점성도 조절제, 촉진제 등과 같은 다른 모르타르 성분은 공지되어 있는 바와 같이 목적에 합치하도록, 1개의 챔버나 주머니 내에 수용시킬 수 있거나, 재료에 따라 상이한 양으로 2개 이상의 챔버(주머니)에 분배할 수 있다. 이와 함께, 점성도비를 조절할 수도 있으며, 이때에는 단지 경화반응이 너무 빨리 일어나지 않도록 하는 것만 주의하면 된다.
2챔버형 또는 다중챔버형 장치내에 포함되는 모르타르 성분 및 재료의 성질, 그 화학조성, 무게비 또는 백분율로 표시한 분량에 대해서는 개별적으로 전술한 바 있으며, 그 내용은 본 발명에 따른 2챔버형 장치에 대해서도 충분히 유효한 것이다.
2챔버형 또는 다중챔버형 장치로서 금속박제 주머니가 사용되는 한에는, 금속박재와 모르타르 성분이 서로 불활성으로 거동하도록 주의해야 한다. 따라서, 통상적으로 금속박 주머니를 구성하는 금속박의 가소제로서 작용하는 모르타르 성분은 제외된다. 또한, 비닐에스테르의 분자량도 함께 고려해야 한다.
본 발명에 따른 2성분-모르타르 덩어리에 있어서, 또한 본 발명에 따른 2챔버형 장치에 대하여 다음의 전체 조성을 가지는 모르타르 재료가 효과적인 것으로 판명되었다.
이하 본 발명을 실시예 형태로 상술한다(실시예에서의 분량은 중량%임)
[실시예 1]
경화성 유기질 모르타르 화합물:
경화성 무기질 모르타르 화합물의 비율 = 1 : 1 1 : 1.5
[실시예 2]
혼합비 : 성분 A : 성분 B = 3 : 1
[실시예 3]
혼합비 : 성분 A : 성분 B : 3.5 : 1
[실시예 4]
혼합비 : 성분 A : 성분 B = 3.7:1
[실시예 5]
중량%로 표시된 혼합비 : 성분 A : 성분 B = 3:1
[실시예 6]
Claims (16)
- 무기질계 및 유기질계의 경화성 화합물과 경화제를 함유하고, 필요에 따라서는 충전제, 용매, 촉진제 또는 다른 통상의 모르타르 성분을 함유하는, 앵커식 고정수단을 천공구멍에 고정시키는데 사용되는 2성분-모르타르에 있어서, 상기 무기질계 경화성 화합물은 수경성 화합물 또는 중축합성 화합물을 함유하고, 상기 유기질계 경화성 화합물은 경화성 비닐에스테르를 함유하는 것을 특징으로 하는 앵커식 고정수단을 천공구멍에 고정시키는데 사용되는 2성분-모르타르.
- 제1항에 있어서, 상기 경화가능한 수경성 화합물은 시멘트 또는 석고를 포함하는 것을 특징으로 하는 모르타르.
- 제2항에 있어서, 상기 시멘트는 산화철이 없는 또는 산화철이 부족한 시멘트를 포함하는 것을 특징으로 하는 모르타르.
- 제1항 내지 제3항 중 어느 한 항에 있어서, 상기 중축합성 화합물은 중축합성 규산염 화합물을 포함하는 것을 특징으로 하는 모르타르.
- 제1항 내지 제3항 중 어느 한 항에 있어서, 상기 경화성 비닐에스테르는 우레탄아크릴레이트 또는 에폭시아크릴레이트를 포함하는 것을 특징으로 하는 모르타르.
- 제1항 내지 제3항 중 어느 한 항에 있어서, 상기 무기질계 경화성 화합물(수경성 화합물 및 중축합성(中縮合性)화합물)과 경화성 비닐에스테르의 총량은 경화제를 제외하고 모르타르 전체의 30-99 중량%인 것을 특징으로 하는 모르타르.
- 제1항 내지 제3항 중 어느 한 항에 있어서, 상기 무기질계 경화성 화합물(수경성 화합물 및 중축합성 화합물)과 경화성 비닐에스테르의 중량비는 1:4 내지 3:1인 것을 특징으로 하는 모르타르.
- 제1항 내지 제3항 중 어느 한 항에 있어서, 경화제를 제외하고 모르타르 전체의 1-60 중량%의 반응성 희석제 성분을 포함하는 것을 특징으로 하는 모르타르.
- 제1항 내지 제3항 중 어느 한 항에 있어서, 상기 유기질계 화합물에 대한 경화제는 고체 형태, 용해된 형태 또는 분산된 형태의 과산화 화합물을 포함하는 것을 특징으로 하는 모르타르.
- 제1항 내지 제3항 중 어느 한 항에 있어서, 상기 무기질계의 수경성 화합물 또는 중축합성 화합물에 대한 경화제는 물, 수용액 또는 물 분산액을 포함하는 것을 특징으로 하는 모르타르.
- 제1항 내지 제3항 중 어느 한 항에 있어서, 50-150㎛의 섬유길이를 가지는 광물계 미세섬유 또는 유기질계 미세섬유를, 필요에 따라서는 충전제와 함께 포함하는 것을 특징으로 하는 모르타르.
- 제4항에 있어서, 상기 중축합성 규산염 화합물은 가용성 SiO2, 용해된 SiO2또는 무정질 SiO2를 함유하는 물질을 포함하는 것을 특징으로 하는 모르타르.
- 제6항에 있어서, 상기 무기질계 경화성 화합물(수경성 화합물 및 중축합성 화합물)과 경화성 비닐에스테르의 총량은 경화제를 제외하고 모르타르 전체의 40-85 중량%인 것을 특징으로 하는 모르타르.
- 제7항에 있어서, 상기 무기질계 경화성 화합물(수경성 화합물 및 중축합성 화합물)과 경화성 비닐에스테르의 중량비는 1:3 내지 2:1인 것을 특징으로 하는 모르타르.
- 제8항에 있어서, 경화제를 제외하고 모르타르 전체의 10-40 중량%의 반응성 희석제 성분을 포함하는 것을 특징으로 하는 모르타르.
- 경화성 모르타르 성분과 경화제를 함유하고, 필요에 따라서는 충전제, 용매, 촉진제 또는 다른 통상의 모르타르 성분을 함유하며, 반응을 저지하는 개재벽에 의해 경화제로부터 분리되어 있는 제1항 내지 제11항 중 어느 한 항에 따른 경화성 모르타르 성분에 의해 앵커식 고정수단을 천공구멍에 고정시키는데 사용되는 다중챔버형 고정 장치에 있어서, 상기 경화성 모르타르 성분으로서 수경성 화합물 또는 중축합성 화합물과 비닐에스테르가 수용되고, 경화제로서 과산화 화합물과 물 또는 수용액이 수용되는 것을 특징으로 하는 앵커식 고정수단을 천공구멍에 고정시키는데 사용되는 다중챔버형 고정 장치.