KR100215991B1 - 원적외선 방사조성물 및 그 제조방법 - Google Patents
원적외선 방사조성물 및 그 제조방법 Download PDFInfo
- Publication number
- KR100215991B1 KR100215991B1 KR1019970003216A KR19970003216A KR100215991B1 KR 100215991 B1 KR100215991 B1 KR 100215991B1 KR 1019970003216 A KR1019970003216 A KR 1019970003216A KR 19970003216 A KR19970003216 A KR 19970003216A KR 100215991 B1 KR100215991 B1 KR 100215991B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- far
- oxide
- infrared radiation
- raw material
- Prior art date
Abstract
본 발명은 알루미나 76∼88중량%, 산화마그네슘 1.8∼2.2중량%, 산화칼슘 1.8∼2.0중량%, 산화나트륨 1.0~1.4중량%, 산화칼륨 0.1∼0.3중량%, 철분 0.1∼0.3중량% 및 실리카 6∼8중량%를 함유하는 천연광물 분말 7∼10중량%; 증류수 83∼86중량%; 항균조제 1∼2중량%; 우레탄실리콘수지 1∼2중량%; 및 이온화촉매제 2∼3중량%를 혼합하여, 그리고 선택적으로 쾌적향 원료와 대전방지제를 더 첨가하여 조성하는 것으로, 이들을 1,2차 교반에 의해 이온화시켜 방치함으로써 제조된다.이렇게 제조되는 원적외선 방사 조성물은 항균, 방취 기능 및 대전방지 기능이 있어 섬유에 적용시 독특한 천연향기가 발생되어 기분 좋은 향기와 상쾌함 등을 줄수 있을 뿐 아니라 신체 주위의 각종냄새를 제거하여 쾌적한 생활을 영위할 수 있도록 하고, 기존 원료에 비해 가격이 훨씬 싸서 대증화에 용이함은 물론 중성으로 제조 가능하여 섬유 전 분야에 부작용 없이 널리 이용될 수 있는 효과를 갖는다.
Description
본 발명은 원적외선 방사 조성물에 관한 것으로서, 보다 상세하게는 의류 등의 각종 섬유류에 적용되어 쾌적향 발산, 항균, 방취 및 원적외선 방사 기능을 발휘, 인체의 신진대사를 원활하게 할 수 있음은 물론 그 외에도 식물성장촉진제나 기타 건강관련용품 등에 널리 이용될 수 있는 원적외선 방사 조성물과 그 제조방법에 관한 것이다.
원적외선은 물체 내부의 분자운동에 의한 전자력선의 진동파로서, 인체의 신진대사를 원활하게 해 주는 작용을 한다. 따라서 여러 산업분야에 이용되고 있는데, 특히 건강관련용품에 널리 이용되고 있다.
일반적으로 원적외선 방사체는 분말 상태로 제조한 후 이를 그대로 또는 액상으로 만들어 어떠한 물건을 만들거나 또는 코팅, 침적 등의 방법으로 적용하게된다.
특히 의류 등 섬유류에 원적외선 발생 물질을 적용하는 경우, 대부분은 원적외선 물질을 혼합, 가수 및 소성한 후 분말로 만들고 이것을 액상화하여 사용하였으나, 이미 소성 분말화된 원적외선 물질을 물 등에 액상 이온화시키기가 매우 어렵고, 또한 경제성이 떨어치는 단점이 있다.
따라서 섬유류에 쉽게 적용할 수 있는 액상 또는 이온화된 상태의 원적외선방사 조성물 개발이 요구되고 있으며, 그 예로서 한국특허공고 96-15657호에 규산소다, 알루미늄소다, 산화나트륨, 치오황산나트륨, 이산화게 르마늄, 정제 포도당,상백당 등을 각각 30∼40℃에서 용해한 후 혼합하고 금을 염화금산으로 이온화한 것과 질산은을 치오황산은으로 이온화한 것을 상기 혼합액에 첨가한 후 상온에서 48∼72시간 방치하는 것을 특징으로 하는 액상(이온화) 바이오세라믹스의 제조방법이 개시된 바 있다.
그러나 상기한 액상(이온화) 바이오세라믹스의 제조방법은 유기화합물을 이온화하는 것으로, 여기에 사용되는 원료의 대부분이 강한 알칼리성으로서, 이 방법으로 만든 원적외선 발생 액상물질은 pH 11∼12로서 이를 섬유에 적용하면 재질에손상을 주고 가공하는 동안에 일정온도 이상에서 황변 현상이 발생하며, 그리고 촉감에 심한 변화를 주어 그 적용범위가 한정될 수밖에 없었다. 또한 이 방법에 의하면 금과 같은 비싼 원료를 사용하므로 경제성이 떨어질 수밖에 없었다.
이에 본 발명자는 상기의 문제를 해결하기 위하여 연구를 거듭한 바, 알루미나(산화알루미늄) 계열의 천연광물을 초미립자 상태로 분쇄한 후 액상으로 이온화하는 방법에 의해 저렴하고 간단하게 제조되는 액상(이온화) 원적외선 방사 조성물을 제공할 수 있음을 알게 되었다.
즉, 본 발명의 목적은 원적외선의 방사율이 높고 쾌적향 발산, 항균, 방취기능 등을 가지고 있어 인체 건강을 보다 이롭게 할 수 있고, 값싼 원료를 사용하여 저렴하므로 대중화에 용이하며, 중성으로 이온화되어 모든 섬유 재질에 대해서가공시 부작용이 거의 없는 원적외선 방사 조성물 및 그 제조방법을 제공하는 데에 있다.
도 1은 본 발명에 따른 원적외선 방사 조성물의 제조 공정도.
본 발명의 목적을 달성하기 위한 원적외선 방사 조성물은, 알루미나 계열의 천연광물 분말 7∼10중량%, 증류수 83∼86중량%, 항균조제 1∼2중량%, 우레탄실리콘 수지 1∼2중량% 및 이온화촉매제 2∼3중량%로 조성되는 데에 특징이 있으며, 여기에 선택적으로 쾌적향 원료를 전체의 2∼3중량%와 소량의 대전방지제를 더 첨가하여 조성될 수 있는 것이다.
본 발명에서 사용하는 알루미나 계열의 천연광물 분말은 알루미나, 산화마그네슘, 산화칼슘, 산화나트륨, 산화칼륨, 철분 및 실리카(이산화규소) 등을 함유한 것인데, 구체적으로는 알루미나 76∼88중량%, 산화마그네슘 1.8∼2.2중량% , 산화칼슘 1.8∼2.0중량%, 산화나트륨 1.0~1.4중량%, 산화칼륨 0.1∼0.3중량%, 철분0.1∼0.3중량% 및 실리카 6∼8중량%을 함유한 광물 분말을 사용한다.
상기 항균조제와 이온화촉매는 특별히 한정되는 바 없으며, 쾌적향 원료는 천연물질에서 추출된 것으로 인체에 유해하지 않은 꽃 향료, 나무 향료 등을 마이크로캡슐화 하여 사용한다:
또한 원적외선 방사 조성물의 제조방법은, 천연광물 분말, 증류수, 항균조제, 우레탄실리콘수지 및 이온화촉매제를 혼합하는 제 1 공정; 제 1 공정의 혼합물과 지르콘소재세라믹볼을 함께 분쇄기에 넣고 교반하여 원재료를 미립자로 분쇄하는 제 2 공정; 상기 제 2 공정의 처리물에 선택적으로 향료와 대전방지제를 첨가한 후 교반하여 이온화시키는 제 3 공정; 및, 제 3 공정의 처리물을 여과하여 방치하는 제 4 공정을 포함한다.
도 1를 참조하면, 상기 제 1 공정은 단순한 재료의 혼합 공정(S1)이고, 제 2 공정은 순환식 분쇄기를 사용하여 통상 500rpm의 속도로 4시간 정도 진행하는 원재료 미세화, 분쇄 공정(S2)이다. 여기서 지르콘소재세라믹볼은 3Φ정도의 분쇄볼로서 원료의 미세화를 촉진하기 위해 함께 넣어 교반한다. 제 3 공정은 2차 분쇄 이온화 공정(S3)으로 보다 용량이 큰 혼합분쇄기에 제 2 공정의 처리물을 넣어 약500rpm의 속도로 약 2시간 정도 교반하는 과정이고, 제 4 공정은 제 3 공정의 처리물을 여과시스템을 천천히 통과시켜(S4; 여과공정) 그 여과액을 약 1일 정도 상온에서 방치하는 공정(S5)이다.
이러한 제조공정에 있어서, 원료로 사용되는 쾌적향 원료와 대전방지제는 상기 제 1 공정에서 다른 원료와 함께 혼합할 수도 있고, 제 3 공정을 진행시에 혼합물에 첨가할 수도 있다.
본 발명에 따른 이온화된 원적외선 방사 조성물과 타사(특허공고 제96-15657호의 발명)의 액상 바이오세라믹스 제조방법에 의해 제조된 원적외선 방사 조성물의 특성을 상온(35℃)에서 측정하여 비교하면 다음 표 1과 같다.
[표 1] 특성비교표
-스캔-
상기 표 1을 참조하면, 본 발명에 따른 원적외선 방사 조성물은 원적외선 방사율 및 방사강도에 있어서 타사원료 보다 조금 더 우수하고, pH에 있어서 타사원료는 11∼12로서 알칼리성인데 반해 본 발명의 조성물은 3∼11로서 중성 조제가 가능하다.따라서 중성의 원적외선 방사 조성물을 섬유 가공에 사용하면 부작용이 없는 바, 섬유 전 분야에 널리 적용될 수 있다. 또한 본 발명의 조성물은 쾌적향 기능, 항균, 방취 기능 등의 다기능성을 보유하고 있음은 물론 가격면에 있어서도 타사원료의 1/30에 불과할 정도로 경제적이다.
또한 타사원료는 섬유에 가공시 130℃에서 황변 현상이 발생하였는데 반해, 본 발명의 조성물을 섬유에 적용한 경우에는 황변 현상을 발견할 수 없었다. 이와같이 본 발명의 조성물이 우레탄계 실리콘 수지를 사용함에도 불구하고 황변 현상이 발생하지 않은 것은 우레탄계 수지의 사용량이 매우 적고 또한 이온화 과정에서 다른 성분이 우레탄계 수지에 작용하여 특성을 변화시켰기 때문이라고 생각된다.
이상에서 상세히 설명한 바와 같이, 본 발명에 따른 원적외선 방사 조성물은 항균, 방취 기능 및 대전방지 기능이 있어 각종 섬유에 적용시 독특한 천연향기가 발생되어 기분 좋은 향기와 상쾌함 등을 줄 수 있을 뿐 아니라 신체 주위의 각종냄새를 제거하여 쾌적한 생활을 영위할 수 있도록 하고, 기존 원료에 비해 가격이 훨씬 싸서 대중화에 용이함은 물론 중성으로 제조 가능하여 섬유 전 분야에 부작용없이 널리 이용될 수 있는 효과를 갖는다.
Claims (4)
- 알루미나 76∼88중량%, 산화마그네슘 1.8∼2.2중량%, 산화칼슘 1.8∼2.0중량%, 산화나트륨 1.0∼1.4중량%, 산화칼륨 0.1∼0.3중량%, 철분 0.1∼0.3중량% 및 실리카 6∼8중량%를 함유하는 천연광물 분말 7∼10중량%; 증류수 83∼86중량%; 항균조제 1∼2중량%; 우레탄실리콘수지 1∼2중량%; 및, 이온화촉매제 2∼3중량%를 혼합하여서 된 원적외선 방사 조성물.
- 제 1 항에 있어서, 추가로 쾌적향 원료를 조성물 전체에 대하여 4∼5중량%로 더 첨가하여 조성되는 것을 특징으로 하는 원적외선 방사 조성물.
- 제 1 항에 있어서, 추가로 대전방지제를 더 첨가하여 조성되는 것을 특징으로 하는 원적외선 방사 조성물.
- 천연광물 분말, 증류수, 항균조제, 우레탄실리콘수지 및 이온화촉매제를 혼합하는 제 1 공정; 제 1 공정의 혼합물과 지르콘소재세라믹볼을 함께 분쇄기에 넣고 교반하여 원재료를 미립자로 분쇄하는 제 2 공정; 상기 제 2 공정의 처리물에 선택적으로 향료와 대전방지제를 침가한 후 교반하여 이온화시키는 제 3 공정; 및, 제 3 공정의 처리물을 여과하여 방치하는 제 4 공정을 포함하는 원적외선방사 조성물의 제조방법.