KR100213318B1 - Control method of thickness and width of steel plate in continuous rolling - Google Patents

Control method of thickness and width of steel plate in continuous rolling Download PDF

Info

Publication number
KR100213318B1
KR100213318B1 KR1019950051881A KR19950051881A KR100213318B1 KR 100213318 B1 KR100213318 B1 KR 100213318B1 KR 1019950051881 A KR1019950051881 A KR 1019950051881A KR 19950051881 A KR19950051881 A KR 19950051881A KR 100213318 B1 KR100213318 B1 KR 100213318B1
Authority
KR
South Korea
Prior art keywords
rolling
weight
slab
thickness
width
Prior art date
Application number
KR1019950051881A
Other languages
Korean (ko)
Other versions
KR970033155A (en
Inventor
정병완
Original Assignee
이구택
포항종합제철주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이구택, 포항종합제철주식회사 filed Critical 이구택
Priority to KR1019950051881A priority Critical patent/KR100213318B1/en
Publication of KR970033155A publication Critical patent/KR970033155A/en
Application granted granted Critical
Publication of KR100213318B1 publication Critical patent/KR100213318B1/en

Abstract

본 발명은 제철소의 후강판 압연공정에서 후강판압연재의 두께 및 폭을 조정하는 방법에 관한 것으로써, 슬라브의 중량이 부족할 경우 중량부족 정도에 따라 압연가능여부를 결정하고, 가능한 범위내에서 압연목표 두께 및 폭을 조정하여 압연함으로써 압연판길이가 보상되어 압연강판길이 부족을 방지할 수 있는 후강판 압연재의 두께 및 폭 조정방법을 제공하고자 하는데, 그 목적이 있다.The present invention relates to a method for adjusting the thickness and width of a thick steel plate rolling material in a steel plate rolling process of a steel mill. It is to provide a method for adjusting the thickness and width of a thick steel sheet rolled material that can compensate for the lack of the length of the rolled steel sheet by compensating the rolled sheet length by adjusting the target thickness and width by rolling.

본 발명은 후강판압연방법에 있어서, 설계지시 중량(ORDWT)을 설정하는 단계; 슬라브가 가열로에 인입되기전에 슬라브의 중량(MEWT)을 측정하는 단계; 측정슬라브중량(MEWT)이 상기 설계지시중량(ORDWT)보다 큰지여부를 판단하고 측정슬라브중량이 상기 설계지시 중량보다 큰 경우에는 통상의 방법으로 압연하고, 적은 경우에는 슬라브의 두께, 폭 및 길이에 대한 압연허용 한계치수를 구하는 단계; 상기에서 구한 슬라비의 두께, 폭 및 길이에 대한 압연허용 한계치수를 이용하여 압연허용 한계중량(LOWWT)을 구하는 단계; 상기 측정슬라브중량(MEWT)이 압연허용 한계중량(LOWWT)보다 큰지여부를 판단하고, 측정슬라브 중량(MEWT)에 대응되는 압연오차 계수값에 해당되는 압연오차 보정계수(K')를 구하는 단계; 상기에서 구한 압연오차 보정계수(K')를 이용하여 압연목표두께(TATH) 및 목표폭(TAWD)를 구하는 단계; 및 상기와 같이 구한 압연목표두께(TATH)및 압연목표폭(TAWD)이 얻어지도록 압연조건을 제어하여 후강판 압연하는 단계를 포함하여 구성되는 후강판 압연재의 두께 및 폭조정방법을 그 요지로한다.The present invention is a thick steel plate rolling method, comprising: setting a design order weight (ORDWT); Measuring the weight of the slab (MEWT) before the slab is introduced into the furnace; It is judged whether the measuring slab weight (MEWT) is larger than the design instruction weight (ORDWT). If the measuring slab weight is larger than the design instruction weight, the measuring slab weight is rolled by the usual method. Obtaining a limit of rolling allowance for the; Calculating a rolling allowable limit weight (LOWWT) using the rolling allowable limit dimension for the thickness, width, and length of the slabs obtained above; Determining whether the measurement slab weight MEWT is greater than the allowable rolling weight LOWWT, and obtaining a rolling error correction coefficient K 'corresponding to a rolling error coefficient value corresponding to the measurement slab weight MEWT; Obtaining a rolling target thickness TATH and a target width TAWD using the rolling error correction coefficient K 'obtained above; And a method for adjusting the thickness and width of the thick steel plate rolling material comprising the step of controlling the rolling conditions so that the obtained rolling target thickness (TATH) and the rolling target width (TAWD) obtained as described above are obtained. do.

Description

후강판 압연재의 두께 및 폭 조정방법How to adjust thickness and width of thick steel roll

제1도는 본 발명에 따라 후강판 압연재의 두께 및 폭을 조정하는 순서를 나타내는 플로우챠트.1 is a flowchart showing a procedure for adjusting the thickness and width of a thick steel sheet rolling material according to the present invention.

제2도는 본 발명에 있어 압연 오차 조정계수(K')를 구하는 과정을 설명하기 위한 설명도.2 is an explanatory diagram for explaining a process of obtaining a rolling error adjustment coefficient K 'in the present invention.

본 발명은 제철소의 후강판 압연공정에서 후강판 압연재의 두께 및 폭을 조정하는 방법에 관한 것으로서, 보다 상세하게는 후강판압연재의 중량부족에 의해 발생되는 압연완료제품의 길이부족을 방지하기 위한 후강판 압연재의 두께 및 폭조정 방법에 관한 것이다.The present invention relates to a method for adjusting the thickness and width of a thick steel sheet rolling material in a steel plate rolling process of a steel mill, and more particularly, to prevent the shortage of the length of the rolled finished product caused by the lack of weight of the thick steel sheet rolling material. It relates to a thickness and width adjustment method of the thick steel sheet rolling material for.

후강판 압연은 다른 압연고정과 다르게 압연 완료후의 치수 즉 두께, 폭 및 길이가 모두 규격 대비 만족되어야 한다. 따라서 정해진 제품의 두께, 폭 및 길이를 만족시키기 위해서는 소재 설계시에 치수 제어오차 범위를 고려하여 압연 목표치수를 결정한다.The thick steel plate rolling, unlike other rolling fixings, must satisfy all dimensions, i.e. thickness, width and length, after the completion of rolling. Therefore, in order to satisfy the specified thickness, width and length of the product, the rolling target dimension is determined by considering the range of dimensional control errors in the material design.

일반적으로 소재 설계시에 결정하는 압연 목표치수는 제품두께에 두께제어 오차를 가산하여 압연 목표두께를 결정하고, 압연 목표폭은 제품폭에 폭내기 압연 오차, 양엣지(Edge)절단량 및 캠버(Camber) 보정량 등을 고려하여 결정하며 최종적으로 압연판 길이는 제품길이에 압연후 발생하는 양 끝단의 불균일 변형부인 크롭(Crop)량 및 중간 분할절단량을 고려하여 결정한다. 압연 목표두께, 폭 및 길이가 결정되면 압연목표두께×폭×길이×비중×=중량에 의해 슬라브(Slab)의 중량을 결정한다.In general, the rolling target dimension determined at the time of designing the material determines the rolling target thickness by adding the thickness control error to the product thickness, and the rolling target width is the width width of the product, the rolling error, the edge cutting amount, and the camber ( Finally, the length of the rolled sheet is determined in consideration of the crop amount and the intermediate splitting amount, which are non-uniform deformation parts at both ends generated after rolling, on the product length. When the rolling target thickness, width and length are determined, the weight of the slab is determined by the rolling target thickness x width x length x specific gravity x = weight.

이와 같은 방식으로 슬라브 중량이 결정되면 이 중량을 만족할 수 있는 슬라브의 두께, 폭 및 길이가 설계되어 연속주조 또는 분괴압연기에 의해 슬라브가 제조된다.When the slab weight is determined in this way, the slab thickness, width and length are designed to satisfy this weight, and the slab is manufactured by continuous casting or crushing mill.

이때, 제조된 슬라브의 두께, 폭 및 길이는 슬라브 제조공정에서의 치수제어 오차 및 슬라브 표면의 홈 제거를 위한 스카핑(Scarfing)등에 의해 설계시의 치수대비 적은 경우가 발생하여 실제 슬라브의 중량은 소재설계 당시의 중량보다 적어져서 이 소재로 압연을 실시했을 경우에는 중량부족에 의해 압연완료 후의 판의 길이가 부족하게되어 제품화될 수 없는 문제점이 있다.At this time, the thickness, width, and length of the manufactured slab are less than the dimensions of the design due to the dimensional control error in the slab manufacturing process and the scarfing to remove the grooves of the slab surface. When the rolled material is less than the weight at the time of the material design, there is a problem in that the length of the plate after the completion of rolling is insufficient due to lack of weight and cannot be commercialized.

이에, 본 발명자는 상기한 종래방법의 문제점을 개선시키기 위하여 연구를 행하고, 그 결가에 근거하여 본 발명을 제안하게 된 것으로써, 본 발명은 슬라브의 중량이 부족할 경우 중량부족 정도에 따라 압연가능여부를 결정하고, 가능한 범위내에서 압연먹표 두께 및 폭을 조정하여 후강판 압연함으로써, 압연판길이가 보상되어 압연강판 길이 부족을 방지할 수 있는 후강판 압연재의 두께 및 폭 조정방법을 제공하고자 하는데, 그 목적이 있다.Thus, the present inventors have made a study to improve the problems of the conventional method described above, and based on the absence of the present invention to propose the present invention, the present invention can be rolled according to the degree of lack of weight when the weight of the slab is insufficient To determine the thickness, and to adjust the thickness and width of the rolled steel sheet within the possible range, by rolling the thick steel sheet, to provide a method of adjusting the thickness and width of the thick steel sheet rolled material to compensate the lack of the length of the rolled steel sheet to compensate , Its purpose is.

이하, 본 발명에 대하여 설명한다.EMBODIMENT OF THE INVENTION Hereinafter, this invention is demonstrated.

본 발명은 후강판 압연방법에 있어서, 설계지시 중량(ORDWT)을 설정하는 단계; 슬라브가 가열로에 인입되기전에 슬라브의 중량(MEWT)을 측정하는 단계; 측정 슬라브 중량(MEWT)이 상기 설계지시 중량(ORDWT)보다 큰지 여부를 판단하고, 측정 슬라브 중량이 상기 설계지시 중량보다 큰 경우에는 통상의 방법으로 압연하고, 적은 경우에는 슬라브의 두께, 폭 및 길이에 대한 압연허용 한계치수를 하기식 (1)(2) 및 (3)에 의해 구하는 단계;The present invention is a thick steel sheet rolling method, comprising: setting a design order weight (ORDWT); Measuring the weight of the slab (MEWT) before the slab is introduced into the furnace; It is determined whether the measured slab weight (MEWT) is greater than the design instruction weight (ORDWT), and if the measured slab weight is larger than the design instruction weight, the thickness is rolled in the usual manner, and if less, the thickness, width and length of the slab. Obtaining the rolling allowance limit for the following formula (1) (2) and (3);

상기에서 구한 슬라브의 두께, 폭 및 길이에 대한 압연허용 한계치수를 이용하여 하기식(4)에 의해 압연허용 한계중량(LOWWT)을 구하는 단계;Obtaining a rolling allowable limit weight (LOWWT) by the following equation (4) using the obtained roll allowable limit dimension for the thickness, width and length of the slab obtained above;

상기 측정 슬라브 중량(MEWT)이 압연허용 한계중량(LOWWT)보다 큰지여부를 판단하고, 측정슬라브 중량(MEWT)이 압연허용 한계중량(LOWWT)보다 작은 경우에는 가열로의 장입을 취소하고, 큰 경우에는 압연오차계수와 슬라브 중량과의 상관관계로부터 측정슬라브 중량(MEWT)에 대응되는 압연오차 계수값에 해당되는 압연오차 보정계수(K')를 구하는 단계; 상기에서 구한 압연오차 보정계수(K')를 이용하여 하기식(5) 및 (6)에 의해 압연목표두께(TATH) 및 목표폭(TAWD)를 구하는 단계; 및It is determined whether the measured slab weight (MEWT) is greater than the allowable rolling weight (LOWWT), and if the measured slab weight (MEWT) is smaller than the allowable rolling weight (LOWWT), the charging of the heating furnace is canceled. Calculating a rolling error correction coefficient K 'corresponding to a rolling error coefficient value corresponding to the measured slab weight MEWT from the correlation between the rolling error coefficient and the slab weight; Obtaining a rolling target thickness (TATH) and a target width (TAWD) by the following equations (5) and (6) using the obtained rolling error correction coefficient (K '); And

상기와 같이 구한 압연목표두께(TATH) 및 압연목표폭(TAWD)이 얻어지도록 압연조건을 제어하여 후강판 압연하는 단계를 포함하여 구성되는 후강판 압연재의 두께 및 폭 조정방법에 관한 것이다.It relates to a method for adjusting the thickness and width of a thick steel sheet rolling material comprising the step of rolling the thick steel sheet by controlling the rolling conditions so that the rolling target thickness (TATH) and the rolling target width (TAWD) obtained as described above are obtained.

이하, 본 발명을 제1도 및 제2도를 통해 상세히 설명한다.Hereinafter, the present invention will be described in detail with reference to FIGS. 1 and 2.

본 발명에 따라 후판압연재의 두께 및 폭을 조정하기 위해서는 설계지시 중량(ORDWT)를 설정해야한다.In order to adjust the thickness and width of the thick plate rolling material according to the present invention, the design instruction weight (ORDWT) should be set.

다음에, 제1도에 나타난 바와 같이 슬라브가 가열로에 인입되기전에 슬라브의 중량(MEWT)을 측정한다.Next, as shown in FIG. 1, the weight of the slab (MEWT) is measured before the slab is introduced into the heating furnace.

다음에, 측정 슬라브 중량(MEWT)이 상기 설계지시 중량(OREWT)보다 큰지여부를 판단한다.Next, it is determined whether the measured slab weight MEWT is greater than the design indication weight OROWT.

이때, 측정 슬라브 중량(MEWT)이 설계지시중량(ORDWT)보다 큰 경우에는 통상적인 방법으로 압연하고, 적은 경우에는 하기식(1)(2) 및 (3)에 의해 슬라브의 두께, 폭 및 길이에 대한 압연 허용한계치수를 구한다.At this time, when the measured slab weight (MEWT) is larger than the design instruction weight (ORDWT), the slab is rolled in the usual manner, and when the slab weight (MEWT) is smaller, the thickness, width, and length of the slab are represented by the following formulas (1) (2) and (3). Calculate the tolerance limit for rolling.

상기 두께 제어오차(σ1), 폭 제어오차(σ2) 및 크롭제어 오차(σ3)는 각 공정의 설비 능력 및 제어 정도(精度)에 따라 다르게 나타나는 값으로 조업 실적을 토대로 구해지는 상수이다.The thickness control error sigma 1, the width control error sigma 2, and the crop control error sigma 3 are values that appear differently depending on the facility capability and the control accuracy of each process, and are constants obtained based on operational results.

상기와 같이, 압연허용 한계치수가 구해지면 다음에는 체적 x 비중=중량의 법칙에 따라 하기 식(4)와 같이 작업가능 한계중량(LOWWT)을 구한다.As described above, when the limit of rolling allowance is obtained, the workable limit weight (LOWWT) is then calculated as in the following equation (4) according to the law of volume x specific gravity = weight.

다음에, 상기 측정 슬라브 중량(MEWT)이 압연한계 허용 중량(LOWWT)보다 큰지여부를 판단한다.Next, it is determined whether the measurement slab weight MEWT is larger than the rolling limit allowable weight LOWWT.

이때, 측정슬라브 중량(MEWT)이 압연허용 한계중량(LOWWT)보다 작은 경우에는 가열로의 장입을 취소하고, 큰 경우에는 압연오차 계수(K)와 슬라브 중량과의 상관관계로부터 측정 슬라브 중량(MEWT)에 대응되는 압연오차 계수값에 해당되는 압연오차 보정 계수(K')를 구한다.At this time, if the measuring slab weight MEWT is smaller than the allowable rolling weight LOWWT, the charging of the furnace is canceled, and when the measuring slab weight MEWT is smaller than the allowable rolling weight (LOWWT), the measuring slab weight MEWT is determined from the correlation between the rolling error coefficient K and the slab weight. The rolling error correction coefficient (K ') corresponding to the rolling error coefficient value corresponding to) is obtained.

상기, 압연 오차계수(K)는 공장의 불량을 관리 목표에 결정된다. 즉 K값을 크게하면 불량율은 감소하지만 소재설계 실수율이 저하하여 전체적으로 생산실수율을 저하를 초래하고, K값을 작게하면 불량율이 높아지게된다.The rolling error coefficient K is determined as a management target for the defect of the factory. In other words, if the K value is increased, the defective rate decreases, but the material design error rate decreases, resulting in lowering the overall production yield rate. If the K value is decreased, the defective rate increases.

따라서 압연 오차계수(K)는 생산 실수율 및 불량율을 고려하여 설정해야 하며 일반적으로 후판공장의 경우는 불량을 0.82%를 허용하는 2.4정도가 적정한 값으로 알려져 있고, 압연 허용한계 오차계수(KL)는 2.0이 적정한 값이다.Therefore, rolling error coefficient (K) should be set in consideration of production error rate and defective rate. In general, in case of heavy plate factory, about 2.4 is allowed as 0.82% of defect, and rolling tolerance coefficient (KL) is 2.0 is an appropriate value.

상기한 압연오차 보정계수(K')를 구하는 방법의 일례를 제2도에 의해 설명하면 다음과 같다.An example of the method for obtaining the above-described rolling error correction coefficient K 'will be described with reference to FIG.

즉, 제2도에 나타난 바와 같이, 횡축을 압연오차계수 값으로 하고 종축을 슬라브 중량으로 하여 종축의 슬라브 측정중량(MEWT)에 대응되는 값을 횡축으로 구하면 그 값이 압연오차 조정계수(K')이며, 이는 하기식(7)과 같이 표시될 수 있다.That is, as shown in FIG. 2, when the horizontal axis is the rolling error coefficient value and the vertical axis is the slab weight, a value corresponding to the slab measurement weight (MEWT) of the vertical axis is obtained from the horizontal axis, and the value is the rolling error adjustment coefficient (K '). ), Which may be represented as in the following formula (7).

즉, 제2도에서, (K'-KL) : (K-KL)=(MEWT-LOWWT) : (ORDWT-LOWWT)이므로,That is, in FIG. 2, since (K'-KL): (K-KL) = (MEWT-LOWWT): (ORDWT-LOWWT),

[여기서, K : 소재 설계시에 반영하는 압연오차 계수.[Where, K: rolling error coefficient reflected in material design.

PRDWT : 소재설계시 지시된 중량]PRDWT: Indicated weight in material design]

다음에, 상기에서 구한 압연오차 보정계수(K')를 이용하여 하기식(5) 및 (6)에 의해 압연목표두께(TATH) 및 목표폭(TAWD)를 구한다.Next, using the rolling error correction coefficient K 'obtained above, the rolling target thickness TATH and the target width TAWD are obtained by the following equations (5) and (6).

[여기서, TATH : 압연 목표 두께[Here, TATH: Rolling Target Thickness

K ' : 측정중량에 의해 계산된 압연오차 계수]K ': rolling error coefficient calculated by measured weight]

[여기서, TAWD : 압연목표 폭][Where, TAWD: rolling target width]

상기와 같이 구한 압연목표두께(TATH) 및 압연목표폭(TAWD)이 얻어지도록 압연조건을 제어하여 후강판 압연 하므로써, 길이부족의 위험부담이 두께 및 폭으로 분한되어 길이 부족 발생율이 현저히 감소된다.By controlling the rolling conditions so that the rolling target thickness TATH and the rolling target width TAWD obtained as described above are obtained, the thick steel sheet is rolled, so that the risk of shortage is divided into thickness and width, and the incidence of length shortage is significantly reduced.

상술한 바와 같이, 본 발명은 평량기에서 측정한 슬라브의 실제중량을 소지 설계 당시의 설계 지시중량과 비교하여 중량 부족정도에 따라 압연 목표치수를 조정하여 압연함으로써 압연길이 부족을 방지하여 실수율을 향상시킬수 있는 효과가 있는 것이다.As described above, the present invention compares the actual weight of the slab measured in the weighing machine with the design indication weight at the time of the design, and adjusts the rolling target dimension according to the degree of weight shortage to prevent the rolling length shortage, thereby improving the error rate. There is an effect that can be made.

Claims (1)

후강판 압연 방법에 있어서, 설계지시 중량(OREWT)을 설정하는 단계; 슬라브가 가열로에 인입되기전에 슬라브의 중량(MEWT)을 측정하는 단계; 측정 슬라브 중량(MEWT)이 상기 설계지시 중량(ORDWT)보다 큰지 여부를 판단하고, 측정 슬라브 중량이 상기 설계지시 중량보다 큰 경우에는 통상의 방법으로 압연하고, 적은 경우에는 슬라브의 두께, 폭 및 길이에 대한 압연허용 한계치수를 하기식(1)(2) 및 (3)에 의해 구하는 단계;A thick steel plate rolling method, comprising: setting a design order weight (OREWT); Measuring the weight of the slab (MEWT) before the slab is introduced into the furnace; It is determined whether the measured slab weight (MEWT) is greater than the design instruction weight (ORDWT), and if the measured slab weight is larger than the design instruction weight, the thickness is rolled in the usual manner, and if less, the thickness, width and length of the slab. Obtaining the rolling allowance limit for the following formula (1) (2) and (3); 상기에서 구한 슬라브의 두께, 폭 및 길이에 대한 압연허용 한계치수를 이용하여 하기식(4)에 의해 압연허용 한계중량(LOWWT)을 구하는 단계;Obtaining a rolling allowable limit weight (LOWWT) by the following equation (4) using the obtained roll allowable limit dimension for the thickness, width and length of the slab obtained above; 상기 측정 슬라브 중량(MEWT)이 압연허용 한계중량(LOWWT)보다 큰지여부를 판단하고, 측정슬라브 중량(MEWT)이 압연허용 한계중량(LOWWT)보다 작은경우에는 가열로로의 장입을 취소하고, 큰 경우에는 압연오차 계수와 슬라브 중량과의 상관관계로부터 측정 슬라브 중량(MEWT)에 대응되는 압연오차 계수값에 해당되는 압연오차 보정계수(K')를 구하는 단계; 상기에서 구한 압연오차 보정계수(K')를 이용하여 하기식(5) 및 (6)에 의해 압연목표두께(TATH) 및 목표폭(TAWD)를 구하는 단계; 및It is determined whether the measured slab weight MEWT is greater than the allowable rolling weight LOWWT. If the measured slab weight is less than the allowable rolling weight LOWWT, the charging to the heating furnace is canceled, and In the case, calculating a rolling error correction coefficient K 'corresponding to the rolling error coefficient value corresponding to the measured slab weight MEWT from the correlation between the rolling error coefficient and the slab weight; Obtaining a rolling target thickness (TATH) and a target width (TAWD) by the following equations (5) and (6) using the obtained rolling error correction coefficient (K '); And 상기와 같이 구한 압연목표두께(TATH) 및 압연목표폭(TAWD)이 얻어지도록 압연조건을 제어하여 후강판 압연하는 단계를 포함하여 구성되는 후강판 압연재의 두께 및 폭조정방법.A method for adjusting the thickness and width of a thick steel plate rolling material comprising the step of controlling the rolling conditions to obtain a rolling target thickness (TATH) and a rolling target width (TAWD) obtained as described above, and rolling the thick steel sheet.
KR1019950051881A 1995-12-19 1995-12-19 Control method of thickness and width of steel plate in continuous rolling KR100213318B1 (en)