KR100192935B1 - Composition for wall paper coating - Google Patents

Composition for wall paper coating Download PDF

Info

Publication number
KR100192935B1
KR100192935B1 KR1019960069458A KR19960069458A KR100192935B1 KR 100192935 B1 KR100192935 B1 KR 100192935B1 KR 1019960069458 A KR1019960069458 A KR 1019960069458A KR 19960069458 A KR19960069458 A KR 19960069458A KR 100192935 B1 KR100192935 B1 KR 100192935B1
Authority
KR
South Korea
Prior art keywords
weight
composition
resin
phthalate
wallpaper
Prior art date
Application number
KR1019960069458A
Other languages
Korean (ko)
Other versions
KR19980050621A (en
Inventor
신종헌
Original Assignee
심광명
풍원물산주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 심광명, 풍원물산주식회사 filed Critical 심광명
Priority to KR1019960069458A priority Critical patent/KR100192935B1/en
Publication of KR19980050621A publication Critical patent/KR19980050621A/en
Application granted granted Critical
Publication of KR100192935B1 publication Critical patent/KR100192935B1/en

Abstract

본 발명은 합성수지와 원적외선 방사성의 세라믹스재료를 일정한 범위로 배합하여 원지에 코팅처리 하므로서 사용시 인체에 유해한 라돈 등을 흡수 제거하는 대신 인체에 유익한 원적외선이 다량 방상 되도록 하면서 탈취성 보온성, 보습성, 항균성등이 개선되어 콘크리트 구조물로 된 주택의 단점을 개선한 벽지조성물의 제공에 관한 것이다.The present invention is a combination of a synthetic resin and far-infrared radioactive ceramics material in a certain range, so that the coating treatment on the base paper to absorb a large amount of far-infrared rays beneficial to the human body while absorbing and removing the harmful radon when used, while deodorizing warmth, moisture retention, antibacterial properties, etc. This improvement relates to the provision of a wallpaper composition that improves the shortcomings of houses with concrete structures.

Description

건강증진 및 보호기능을 갖는 합성수지재 벽지 코팅용 조성물Synthetic resin wallpaper coating composition with health promotion and protection

본 발명은 합성수지재 벽지 코팅용 조성물에 관한 것이다. 특히 합성수지를 기재로하여 보온, 보습, 방충, 통풍 및 원적외선 방사기능이 우수한 세라믹스재질을 이용하여 사용시 인체의 건강을 증진시킬 수 있도록 구성한 벽지조성물에 관한 것이다.The present invention relates to a composition for coating a synthetic resin wallpaper. In particular, the present invention relates to a wallpaper composition configured to improve the health of the human body by using a ceramic material having excellent thermal insulation, moisture retention, insect repellent, ventilation, and far-infrared radiation function based on a synthetic resin.

합성수지를 기재로 사용한 벽지가 다양하게 제공되고 있으며 특히, 발포벽지의 경우 흡음 단열성이 뛰어나고 색상이 변하지 아니하므로 널리 이용되고 있다.Wallpapers using synthetic resins have been provided in various ways, and in particular, foamed wallpapers have been widely used because they have excellent sound absorption insulation and do not change color.

그러나 합성수지 특유의 불투수성 때문에 이면이 습기가 차면서 부패되는 현상이 심하며, 세멘트 골격체의 특이성 때문에 라돈방출이 되어 인체에 유해한 것으로 인정되고 있다.However, due to the water impermeability of synthetic resins, the back surface is very humid and decayed, and due to the peculiarity of the cement skeleton, radon is released and is considered to be harmful to the human body.

한국 특허공고 제94-3069호는 250메시이상의 맥반석 5-20중량%와 건축물 내장용 도포제 80-95중량%을 배합하여 실내등을 도포함에 따라 탈취 및 재습효과를 얻고 있으나 단순도포제로 사용될 뿐 벽지로의 이용은 불가능하다.Korean Patent Publication No. 94-3069 combines 5-20% by weight of ganban stone of more than 250 mesh and 80-95% by weight of interior coating agent to obtain deodorizing and rehumidifying effect by applying indoor light. Is not available.

그 외에도 원적외선 방사 기능을 갖는 세라믹재를 세멘트와 혼합사용하고 있고 심지어는 황토를 이용한 온돌 시스템도 채용되어 오고 있다.In addition, ceramic materials having a far-infrared radiation function are mixed with cement, and even ondol systems using ocher have been adopted.

본 발명은 합성수지와 원적외선 방사성의 세라믹스재료를 일정한 범위로 배합하여 원지에 코팅처리 하므로서 사용시 인체에 유해한 라돈 등을 흡수제거하는 대신 인체에 유익한 원적외선이 다량 방사 되도록 하면서 탈취성 보온성, 보습성, 항균성등이 개선되어 콘크리트 구조물로 된 주택의 단점을 개선한 벽지조성물의 제공에 목적이 있다.The present invention is a combination of a synthetic resin and far-infrared radioactive ceramics material in a certain range, so that the coating process on the base paper, while absorbing and removing radon harmful to the human body when used, so that the far-infrared radiation beneficial to the human body is radiated, deodorizing insulation, moisture retention, antibacterial properties, etc. This improvement is aimed at providing a wallpaper composition that improves the shortcomings of houses made of concrete structures.

제1도의 (a)(b)(c)(d)도는 본 발명의 제조공정을 도시한 공정개념도.(A) (b) (c) (d) of FIG. 1 is a process conceptual diagram which shows the manufacturing process of this invention.

제2도는 본 발명의 벽지의 단면구도임.2 is a cross-sectional view of the wallpaper of the present invention.

* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings

1 : 롤러 2 : 저장조1 roller 2 reservoir

3 : 가열조 4 : 롤러3: heating bath 4: roller

5 : 원지층 6 : 중탄산나트륨처리층5: base layer 6: sodium bicarbonate treatment layer

7 : 코팅층7: coating layer

본 발명의 전체적인 제조공정은 제1도의 (a)(b)(c)(d)에서 공정 순서의 개념을 도시하며, 제조된 벽지의 단면도가 제2도에 도시되고 있다.The overall manufacturing process of the present invention shows the concept of the process sequence in (a) (b) (c) (d) of FIG. 1, and a cross-sectional view of the manufactured wallpaper is shown in FIG.

본 발명은 PVC, PE 등의 합성수지재에 충진제, 가소제, 발포제 등을 혼련 배합하여준 벽지용 수지조성물에 있어서, 디부틸프탈레이트, 디옥틸프탈레이트, 디이소데실프탈레이트, 부틸라우릴프탈레일, 디트리데실프탈레이트, 부틸벤질프탈레이트중의 어느하나 또는 이들의 혼합물로 되는 가소제 55-65중량%, 프레온가스 또는 아조디 카본아미드와 같은 발포제 2-3중량%, 스테아린산바륨, 스테아린산아연, 스테아린산칼슘 또는 스테아린산카드뮴 중의 어느하나 또는 이들의 혼합물로 되는 안정제 2-3중량%, 티타늄디옥사이드 10-12중량%와 탄산칼슘 25-30중량%로 되는 혼합물 I을 최종조성물의 중량을 기준으로 35-45중량%와; PVC, PE중의 어느하나로 또는 합성수지 80-90중량%, 세라믹원석분말 20-30중량%, 수지개질제 5-10중량%, 점도억제제 3-5중량%로 구성되는 혼합물 II을 최종조성물의 중량을 기준으로 45-52중량%와, PVC-공중합수지 5-8중량%, 변성아크릴수지 18-20중량%, 폴리에스터 폴리올수지 5-8중량%, 톨루엔 22-27중량%, 메틸에틸케톤 32-37중량%, 무수제올라이트 8-12중량%로 되는 혼합물 III을 최종조성물의 중량을 기준으로 6-10중량%로 구성된 벽지용 수지조성물이다.In the resin composition for wallpaper in which a filler, a plasticizer, a foaming agent, and the like are kneaded with a synthetic resin material such as PVC and PE, the present invention includes dibutyl phthalate, dioctyl phthalate, diisodecyl phthalate, butyl lauryl phthalrail, and ditri. 55-65% by weight of plasticizer of any of decylphthalate, butylbenzylphthalate or mixtures thereof, 2-3% by weight of blowing agent such as freon gas or azodi carbonamide, barium stearate, zinc stearate, calcium stearate or cadmium stearate A mixture I of 2-3% by weight of stabilizer, 10-12% by weight of titanium dioxide and 25-30% by weight of calcium carbonate, comprising 35-45% by weight based on the weight of the final composition; Mixture II of any one of PVC, PE or 80-90% by weight of synthetic resin, 20-30% by weight of ceramic raw material powder, 5-10% by weight of resin modifier, 3-5% by weight of viscosity inhibitor, based on the weight of final composition 45-52% by weight, 5-8% by weight PVC-polymer, 18-20% modified acrylic resin, 5-8% polyester polyol resin, 22-27% toluene, 32-37 methyl ethyl ketone It is a resin composition for wallpaper which consists of 6-10 weight% of mixture III which consists of 8 weight% and 8-12 weight% of anhydrous zeolites based on the weight of the final composition.

본 발명에서 사용된 세라믹스 재료는 명반석, 규각, 게르마늄, 제오라이트로 되는 원석을 동일 중량비로 분쇄혼합한 것이며 적어도 600메시이상의 입도를 갖는 것이다.The ceramic material used in the present invention is a mixture of alum, quartz, germanium and zeolite in the same weight ratio, and has a particle size of at least 600 mesh.

본 발명의 조성물은 다음과 같이 제조된다.The composition of the present invention is prepared as follows.

먼저 혼합물 I의 발포제, 안정제, 티타늄디옥사이드를 순서대로 가소제에 용해시킨 후 탄산칼슘을 넣어 잘 교반시켜 준다.First, the blowing agent, stabilizer, and titanium dioxide of the mixture I are dissolved in a plasticizer in order, and then calcium carbonate is added and stirred well.

제조된 혼합물 I에 합성수지를 넣어 가열용해한 후 세라믹스 재료를 첨가후 다시 20분이상 교반혼합하고, 수지개질제를 다시 넣고 10분이상 교반하여 준다.After dissolving the synthetic resin in the prepared mixture I and heating it, the ceramic material is added and stirred and mixed again for at least 20 minutes, and the resin modifier is added again and stirred for at least 10 minutes.

이같이 제조된 것에 PVC-공중합수지, 변성아크릴수지, 폴리에스터 폴리올수지, 톨루엔을 메틸에틸케톤에 넣고 20-30분간 교반혼합후 무수제올라이트를 넣고 15-20분가량 교반하여 목적한 코팅용 조성물을 얻는다.Thus prepared PVC-copolymer, modified acrylic resin, polyester polyol resin and toluene were put into methyl ethyl ketone, stirred and mixed for 20-30 minutes, anhydrous zeolite was added and stirred for about 15-20 minutes to obtain the desired coating composition. .

이상의 코팅조성물을 기초로한 벽지제조 공정을 첨부도면에 의거하여 설명한다.The wallpaper manufacturing process based on the above coating composition is demonstrated based on an accompanying drawing.

[원지후면가공공정][Back surface processing process]

일정한 무늬등이 형성되기전의 원지충(5)후면에 중탄산나트륨 5중량%가 배합된 중탄산나트륨수용액을 분무한 다음 건조시켜 원지(5)의 후면에 중탄산나트륨처리층(6)을 구성한다.A sodium bicarbonate solution containing 5% by weight of sodium bicarbonate was sprayed onto the back of the paperworm 5 before the formation of a predetermined pattern, and then dried to form a sodium bicarbonate treated layer 6 on the back of the paper 5.

[1차 코팅공정][1st coating process]

후면 중탄산나트륨 처리된 원지를 원통형태의 롤러(1)에 장착후 본 발명의 혼합물 I과 II가 배합된 재료가 담긴 코팅액 저장조(2)에 통과시켜 상면에 코팅되도록 한다.After the back surface sodium bicarbonate treated base material is mounted on the cylindrical roller 1, it is passed through the coating liquid reservoir 2 containing the mixture I and II of the present invention to be coated on the top surface.

이어서 220-260℃로 되는 가열조(3)에 통과시켜 경화처리하여 코팅층(7)을 구성한다.Subsequently, it is passed through a heating bath 3 of 220-260 ° C. and cured to form a coating layer 7.

[인쇄공정][Printing process]

1차 코팅이 된 원지를 인쇄기 롤러(4)에 걸러준 다음 공지의 방법으로 인쇄 처리하여 인쇄층(8)을 구성하고 인쇄부분이 손상되지 않도록 혼합물III으로 표면처리한 다음 50-60m/분의 속도로 230-240℃로 건조시켜 최종표면 코팅층(9)을 구성한다.The primary coated paper is filtered through a printing machine roller 4, and then printed by a known method to form a printed layer 8, and surface treated with a mixture III so as not to damage the printed portion, and then 50-60 m / min Drying at 230-240 ° C. at a rate constitutes the final surface coating layer 9.

본 발명의 세라믹스 재료의 성분은 다음과 같다.The component of the ceramic material of this invention is as follows.

본 발명의 벽지를 사용한 원적외선 방사시험 결과는 다음과 같다.Far infrared radiation test results using the wallpaper of the present invention are as follows.

상용기기 : FT-IR 스텍트로미터Commercial device: FT-IR Strobometer

시험기간 : 한국건자제 시험연구원Period: Korea Institute of Construction Testing

서울시 금천구 가산동 233-5233-5, Gasan-dong, Geumcheon-gu, Seoul

시험일시 : 1996. 12. 13.Test Date: December 13, 1996

상기 성분을 함유한 명반석의 특성은 다음과 같다.The characteristics of alumite containing the above components are as follows.

1) 강한 흡착력을 갖고 있고 다공성이므로 표면적이 매우 넓고 모세관 현상을 이용, 중금속 세균 오염물질 등을 흡착 제거시킨다.1) As it has strong adsorption power and is porous, it has a very large surface area and uses a capillary phenomenon to adsorb and remove heavy metal bacterial contaminants.

즉, 촉매작용을 통한 음이온 교환 능력이 뛰어나다.That is, the anion exchange ability through the catalysis is excellent.

2) 45여종의 인체의 필수 미네랄을 용출하여 혈액의 알카리성을 유지하여 몸의 성장 호르몬 형성 등의 작용을 한다.2) It elutes 45 kinds of essential minerals of the human body to maintain the alkalinity of the blood and act as the body's growth hormone formation.

3) 풍부한 용존산소를 용출하여 화학적 산소요구량과 생화학적 산소요구량을 풍부하게 하여 방부작용과 함께 생체에 활력을 준다.3) By eluting abundant dissolved oxygen, it enriches chemical oxygen demand and biochemical oxygen demand and gives vitality to the living body with antiseptic action.

4) 원적외선을 90%이상 방사, 공명 흡수작용으로 식품의 선도를 유지시켜 맛의 증가와 함께 신진대사 등을 촉진시키는 특성을 갖는다.4) It maintains the freshness of food by emitting more than 90% of far infrared rays and resonant absorption, and promotes metabolism with increasing taste.

5) 명반석은 화성암류중 장석반암에 속하는 것으로 중생대말부터 신생대초에 걸쳐 분출 및 관입되어 긴세월동안의 풍화작용 등에 의해 장석과 석영의 결정이 고루 섞여 있는 원석이다.5) Alumite is belonging to feldspar rock among igneous rocks. It is a gemstone that is fused with feldspar and quartz crystals by eruption and intrusion from the end of the mesozoic to the new generation.

이상의 특징에 따라 본 발명은 다음의 효과를 갖는다.According to the above characteristics, this invention has the following effects.

1) 인체의 신진대사 촉진 작용1) the metabolic promoting effect of the human body

시멘트의 독성이 있는 일반주택과 3층 이상의 APT에서는 신이 인간에 준 천혜의 선물인 흙에서 방사되는 원적외선의 혜택을 받지 못한다.Cement toxic houses and APTs above the third floor do not benefit from far-infrared radiation from the earth, God's gift to man.

이러한 문제점의 개선택으로 원적외선을 90%이상 방사하는 신비의 광석인 명반석을 원료로 한 건강벽지를 선택 하므로서 인간의 환경을 생각하는 주거공간을 창조할 수 있다.By choosing such a problem, it is possible to create a living space that considers the human environment by selecting a health wallpaper made from alumite, a mysterious ore that emits more than 90% of far infrared rays.

본 발명품인 건강벽지에서 90%이상 방사되는 원적외선 에너지는 생체에 흡수되는 특성을 갖고 있어 이렇게 흡수된 에너지는 인체의 신진대사를 촉진해 주므로 피로회복, 노화방지 혈액순환 활성화에 탁월한 효과를 제공한다.The far-infrared energy emitted by 90% or more in the health wallpaper of the present invention has the property of being absorbed by the living body, and thus the absorbed energy promotes the metabolism of the human body, thereby providing an excellent effect on fatigue recovery and anti-aging blood circulation activation.

2) 쾌적한 주거환경창조2) Creating a pleasant living environment

본 건강벽지는 명반석의 독특한 흡착특성인 냄새제거, 공기정화, 독성중독, 습도조절 등에 뛰어난 효과를 발휘하며, 생물의 성장 촉진과 고효율의 복사 난방효과를 제공하는 한편, 고유원료의 독특한 향균성이 일반세균은 물론 대장균과 곰팡이의 서식을 방지하여 쾌적한 주거환경을 창조하여 준다.This health wallpaper has an excellent effect on deodorization, air purification, toxic poisoning, and humidity control, which are unique adsorption characteristics of alum. It creates a pleasant living environment by preventing the growth of E. coli and mold as well as general bacteria.

3) 시멘트 공해 해소3) Eliminate Cement Pollution

현대 건축물의 대부분을 차지하고 있는 시멘트는 우리 인체에 유해한 강알칼리성분을 갖고 있으며, 시멘트가 경화되면서 발출하는 강알카리성분은 인간의 피부를 상하게 할 뿐 아니라 인체의 혈액순환과 각종 신경을 교란시켜 현대의 각종 성인병과 신경성 질환 증세를 유발하며, 주거형태의 고층화로 인한 고층빌딩 증후군 역시 지기(地氣)의 차단과 시멘 콘크리트의 인체 유해성 등이 그 중요한 원인으로 알려져 있다.Cement, which occupies most of modern buildings, has strong alkalis that are harmful to our human body, and strong alkalis, which are emitted when the cement hardens, not only damage the human skin but also disrupt the blood circulation and various nerves of the human body. It causes the symptoms of adult diseases and neurological diseases, and the high-rise building syndrome caused by the high-rise of the housing type is also known to be the main cause of the blockage of the ground and the human hazard of cement concrete.

특히 시멘트, 대리석, 벽돌 등의 건축자재에서 조금씩 방출되는 라돈가스(RADON GAS)가 인체내에 흡입되면 폐암의 발생 위험이 높은 것으로 보고 되었다.In particular, when radon gas (RADON GAS), which is gradually released from building materials such as cement, marble, and brick, is inhaled into the human body, a high risk of lung cancer has been reported.

명반석을 활용한 본 발명 벽지는 강알카리성분을 중화시키고 각종 유해물질을 흡수하여 쾌적한 주거 환경의 제공은 물론 현대인의 각종 성인병을 해방시켜 주는 기능성 건강벽지이다.The present invention wallpaper using alum is a functional health wallpaper that neutralizes strong alkalis and absorbs various harmful substances to provide a comfortable living environment as well as to liberate various adult diseases of modern people.

Claims (2)

PVC, PE 등의 합성수지재에 충진재, 가소제, 발포제 등을 혼련 배합하여 준 벽지용 수지조성물에 있어서, 디부틸프탈레이트, 디옥틸프탈레이트, 디이소데실프탈레이트, 부틸라우릴프탈레일, 디트리데실프탈레이트, 부틸벤질프탈레이트중의 어느하나 또는 이들의 혼합물로 되는 가소제 55-65중량%, 프레온가스 또는 아조디 카본아미드와 같은 발포제 2-3중량%, 스테아린산바륨, 스테아린산아연, 스테아린산칼슘 또는 스테아린산카드뮴 중의 어느하나 또는 이들의 혼합물로 되는 안정제 2-3중량%, 티타늄디옥사이드 10-12중량%와 탄산칼슘 25-30중량%로 되는 혼합물 I을 최종조성물의 중량을 기준으로 35-45중량%와; PVC, PE중의 어느하나로 또는 합성수지 80-90중량%, 600메시이상의 입도를 갖는 세라믹원석분말 20-30중량%, 수지개질제 5-10중량%, 점도억제제 3-5중량%로 구성되는 혼합물 II을 최종조성물의 중량을 기준으로 45-52중량%와, PVC-공중합수지 5-8중량%, 변성아크릴수지 18-20중량%, 폴리에스터 폴리올수지 5-8중량%, 톨루엔 22-27중량%, 메틸에틸케톤 32-37중량%, 무수제올라이트 8-12중량%로 되는 혼합물 III을 최종조성물의 중량을 기준으로 6-10중량%로 구성된 건강증진 및 보호기능을 갖는 합성수지재 벽지 코팅용 조성물.In the resin composition for wallpaper in which synthetic resin materials such as PVC and PE are kneaded with a filler, a plasticizer, and a foaming agent, dibutyl phthalate, dioctyl phthalate, diisodecyl phthalate, butyl lauryl phthalate, ditridecyl phthalate, 55-65% by weight of plasticizer of any one or mixtures of butylbenzylphthalate, 2-3% by weight of blowing agent such as freon gas or azodi carbonamide, barium stearate, zinc stearate, calcium stearate or cadmium stearate Or from 35 to 45% by weight, based on the weight of the final composition, mixture I comprising 2-3% by weight stabilizer, 10-12% by weight titanium dioxide and 25-30% by weight calcium carbonate, which are mixtures thereof; Mixture II composed of any one of PVC and PE or 20-30% by weight of ceramic raw material powder having a particle size of 80-90% by weight of synthetic resin, 600 mesh or more, 5-10% by weight of resin modifier, and 3-5% by weight of viscosity inhibitor 45-52% by weight, 5-8% by weight of PVC-copolymer, 18-20% by weight of modified acrylic resin, 5-8% by weight of polyester polyol resin, 22-27% by weight of toluene, 32-37% by weight of methyl ethyl ketone, 8-12% by weight of anhydrous zeolite A composition for coating a synthetic resin wallpaper having a health promotion and protection function consisting of 6-10% by weight based on the weight of the final composition. 제1항에 있어서, 세라믹원석분말은 명반석, 규각, 게르마늄, 제오라이트로 되는 원석을 동일 중량비로 분쇄혼합한 것을 특징으로 하는 건강증진 및 보호기능을 갖는 합성수지재 벽지 코팅용 조성물.The composition of claim 1, wherein the ceramic gemstone powder is mixed with alum, quartz, germanium, and zeolite in the same weight ratio.
KR1019960069458A 1996-12-21 1996-12-21 Composition for wall paper coating KR100192935B1 (en)