KR0156679B1 - 일회용 반창고 - Google Patents
일회용 반창고 Download PDFInfo
- Publication number
- KR0156679B1 KR0156679B1 KR1019960019773A KR19960019773A KR0156679B1 KR 0156679 B1 KR0156679 B1 KR 0156679B1 KR 1019960019773 A KR1019960019773 A KR 1019960019773A KR 19960019773 A KR19960019773 A KR 19960019773A KR 0156679 B1 KR0156679 B1 KR 0156679B1
- Authority
- KR
- South Korea
- Prior art keywords
- nonwoven fabric
- disposable
- pad portion
- adhesive layer
- aid
- Prior art date
Abstract
본 발명은 고흡착성 일회용 구급 반창고에 관한 것으로, 더욱 상세하게는 지지체층과 그 위에 형성된 점착층과 그 위에 형성된 패드부 및 박리지로 이루어진 일회용 반창고에 있어서, 상기 패드부가 소디움폴리아크릴레이트 및 활성탄을 포함하는 부직포와 그의 표면에 라미네이팅되어 있는 상처 박리용 필름으로 이루어져 있는 것을 특징으로 하는 일회용 반창고에 관한 것이다. 본 발명에 따른 반창고는 상처에서 분비되는 분비물을 충분히 흡수, 흡착하고 지형을 촉진시켜 상처의 빠른 치유를 유도한다.
Description
제1도는 본 발명에 따른 고흡착성 일회용 반창고의 평면도를 나타낸 것이고,
제2도는 제1도의 단면도이고,
제3도는 제1도의 구조별 배열 투시도이다.
* 도면의 주요부분에 대한 부호의 설명
1 : 풀리에틸렌계 망목구조의 상처 박리용 필름
2 : 활성탄
3 : 소디움풀리아크릴레이트
4 : 고무계 점착성 또는 합성고무, 풀리우레탄계고무, 아크릴레이트 공중합체 점착층
5 : PVC 필름, 풀리우레탄계 필름 또는 신축성레이온면의 지지체
6 : 패드부
본 발명은 고흡착성 일회용 그급 반창고에 관한 것으로, 더욱 상세하게는 상처에서 분비되는 분비물을 충분히 흡수, 흡착하고 지혈을 촉진시켜 상처의 빠른 치유를 유도하는 일회용 반창고에 관한 것이다.
종래에 사용되어 온 일회용 반창고는, 일반적으로 지지체 층과 지지체층 위에 형성되어 상처 부위에 부착될 수 있도록 해주는 점착층과, 점착층 위에 형성되어 상처에서 분비되는 분비물을 흡수해 주는 패드부와 패드부를 덮고 있는 박리지로 구성되어 있다.
그러나, 이러한 종래의 일회용 반창고는 패드부가 가아제 혹은 부직포만으로 이루어져 있어 분비물이 누출되거나 이들이 상처에 들러붙는 단점이 있었다. 패드부에 아크리놀, 벤잘코니움클로라이드, 도데실피리딘니움클로라이드 등의 약물이 부가되어 있는 경우에는 멸균작용을 나타낼 수 있으나, 공통적으로 분비물이 과량일 때에는 이를 억제할 수 있는 능력이 떨어지고, 약물에 대한 알레르기도 배제할 수 없었다.
한편, 대한민국 특허 공고 제95-5335호에는 패드부에 혈액 응고를 돕는 풀리에틸렌 옥사이드를 사용하여 지혈 효과를 증대시킨 일회용 반창고가 개시되어 있다. 또한, 미합중국 특허 제 3,328,259호에는 카르복시메틸셀룰로이스의 나트륨염을 사용하여 지혈제 함유 상처용 드레싱을 제조하는 방법이 기술되어 있다.
그러나, 상기와 같은 종래 기술에서는 지혈 효과에만 중점을 두어 반창고를 개발한 결과 상처에서 분비되는 분비물이나 오염물을 흡착하는 능력이 떨어지는 문제가 있었다.
이에 본 발명자들은 종래의 일회용 반창고에 비하여 훨씬 빠른 지혈효과를 나타내면서도 분비물 흡수 능력이 뛰어난 일회용 반창고를 개발하기 위하여 부단히 연구한 결과, 다량의 혈액을 함침할 수 있는 소디움폴리아크릴레이트와 천연목재(코코넛껍질, 갈참나무, 적송)에서얻은 활성탄을 동시에 포함하고 있는 패드 층을 포함하여 구성되는 일회용 반창고가 이에 부합되는 효과를 나타낸다는 사실을 알아내어 본 발명을 완성하게 되었다.
따라서, 본 발명의 목적은, 상처에서 배출되는 혈액, 진물, 화농 등의 분비물이나 오염물을 빠르게, 다량 흡착, 흡수함은 물론 신속한 지혈 효과와 상처부위의 수화 현상을 촉진시켜 빠른 치유을 유도하는 고흡착성 일회용 반창고를 제공하고자 하는 것이다.
이를 위하여 본 발명에 의하면, 지지체층과 그 위에 형성된 점착층과 그 위에 형성된 패드부 및 박리지로 이루어진 일회용 반창고에 있어서, 상기 패드부가 소디폴리아크릴레이트 및 활성탄을 포함하는 부직포와 그의 표면에 라미네이팅되어 있는 상처 박리용 필름으로 이루어져 있는 것을 특징으로 하는 일회용 반창고가 제공된다.
이하, 본 발명의 내용을 보다 상세히 설명한다.
본 발명에 있어서 지지체층의 소재로는 기공성 PVC 필름, 폴리우레탄 필름 또는 신축성 레이온을 사용하는 것이 바람직하며, 이의 상부 표면에 항알레르기성 점착제를 도포하여 점착층을 형성시킨다.
항알레르기성 점착제로는 천연 고무, 합성 고무 수지 등에 디펜히드라민, 말레인산클로로페닐아민 등의 항알레르기성 약물을 첨가하여 사용할 수 있다.
다음으로 본 발명의 특징인 패드부는 소디움폴리아크릴레이트와 활성탄을 포함하고 있는 부직포와 이의 표면에 라미네이팅되어 있는 상처박리용 필름으로 구성된다.
상기 부직포는 비스코스레이온 60∼100%의 부직포인 것이 바람직하고, 상처박리용 필름으로는 기공성 저밀도 폴리에틸렌계 필름을 사용하는 것이 바람직하다.
부직포에 분산, 살포할 소디움롤리아크릴레이트는 가교 결합하지 않은 상태이고, 흡수능이 80∼100㎖/g 인 것으로서, 평상시에는 겔상태가 아니며, 수분함량은 10중량% 이하로 충분한 흡수량을 가지는 것이 바람직하다. 이러한 소디움폴리아크릴레이트의 함량은 부직포 전체의 중량을 기준으로 0.01 내지 15%(w/w)가 되도록 하는 것이 바람직하다.
부직포에 전연된 소디움폴리아크릴레이트는 혈액이나 오염물 등을 다량, 신속하게 흡수하는데, 이와 같이 수분 등을 흡수하여 겔상태가 되었을 때의 pH는 상처부위를 자극하지 않도록 7.5±0.3 정도의 중성 상태를 유지해야 한다.
부직포에 분산되는 다른 성분인 활성탄은 코코넛껍질, 갈참나무, 적송 등의 천연목재에서 제조한 것을 사용하는 것이 바람직하며, 특히 입자크기 0.05±0.007㎜, 표면적 1,000±100㎡/㎜인 것이 바람직하다. 이 경우 어떠한 입자보다 흡착 표면적이 넓어져 흡착력이 크게 증대된다. 활성탄의 함량은 부직포 전체의 중량을 기준으로 0.01 내지 15%(w/w)가 되도록 하는 것이 바람직하다.
소디움폴리아크릴레이트와 활성탄을 부직포에 살포할 때에는 물이나. 물-에탄올 혼합액, 사염화탄소, 벤젠, 헥산 등의 용매에 분산시켜 살포하는 것이 바람직하다.
본 발명에 있어서. 패드부를 덮고 있는 상처 박리용 필름은 부직포가 상처 부위에 눌러 붙는 것을 방지해 준다.
마지막으로 패드부와 점착층 위에는 박리지를 적층하여 패드부와 점착층을 오염 등으로부터 보호한다. 박리지로는 실리콘 종이나 폴리프로필렌 등을 사용할 수 있는데, 반창고 사용시에는 이 박리지를 제거한 후 사용한다.
본 발명에 따른 고흡착성 일회용 반창고는 상처부위의 혈액, 진물, 화농 등의 분비물이나 오염물을 다량, 신속하게 흡착, 흡수하므로, 종래의 일회용 반창고에 비해 훨씬 빠른 지혈효과와 수화증대를 나타내고 상처부위를 청결하게 유지하여 신속한 치료를 유도하게 된다.
본 발명을 이하의 실시예에 의하여 더욱 구체적으로 설명한다. 이들 실시예는 본 발명을 예시하기 위하여 제공되는 것으로, 어떠한 형태로든 본 발명의 범위가 이에 의하여 제한되는 것은 아니다.
[실시예 1]
용해조에 소디움롤리아크릴레이트 1㎏, 이소프로필알콜 1,000㎏을 넣고, 서서히 교반하면서 분산을 확인한 다음, 활성탄 0.2㎏을 소량씩 서서히 첨가하였다. 혼합물을 균일액으로 한 후, 레이온사 부직포 제조시 함께 살포하여 전연시켰다. 오븐터널에서 용매를 증발시켜 부직포내에 소디움롤리아크릴레이트와 활성탄올 부직포올 사이에 형성시킨 후 부직포를 감아 올렸다.
소디움폴리아크릴레이트와 활성탄 성분이 전연되어 있는 부직포를 기공성 저밀도 풀리에틸렌계 필름에 라미네이팅시킨 다음, 절단하여 접착제가 도포된 기공성 지지체에 크기에 따라 절단 부착시켰다.
모든 공정은 통상적으로 사용되는 반창고 제조 기계와 일회용 반창고 제작기계 및 포장기를 사용하여 시행되며, 특별히 명기되지 않은 세부적인 시행 공정은 공지의 방법에 따랐다. 전체 공정 시행시에는 외부 오염과 인습에 특별히 주의하였다.
[비교예 1]
혼합조에 이소프로필알콜 29.28㎏을 가하고 빠르게 교반하면서, 폴리에틸렌 옥사이드[유니온 카바이드사의 폴리옥스수지 WSR-301, 분자량 4,000,000]를 0.9㎏ 가하였다. 중합체는 알코올에 분산되지만 용해되지는 않았다. 증류수를 5.82㎏을 가하고 15분 동안 서서히 교반한 후 물을 가하여 폴리에틸렌옥사이드를 빠르게 용해시켰다.
이 과정에서 점도를 측정하고 리버스 피복기를 사용하여 상기용액을 천공된 망상 폴리에틸렌 필름[허클레스, 인코포레이티드에 의해 생산되는 델네트(Delnet) P-53]상에 피복시켰다.
델네트를 폴리옥스 용액의 얇은 필름으로 피복한 후, 가온시킨 오븐위로 통과시켜 용매를 증발시키면 델네트 필름상에 폴리에틸렌옥사이드의 매우 얇은 필름이 피복된 채로 남게 되는데, 이후에 이것을 감아 올렸다.
[비교예 2]
대한약전에 수재된 가아제를 사용하여 일회용 반창고를 제조하였다.
[비교예 3]
폴리에틸렌 망에 아크리놀을 침적시킨 부직포를 라미네이팅하여 일회용 반창고를 제조하였다.
[지혈 시험]
실시예1 및 비교예1 내지 3에 따른 일회용 반창고의 지혈효과를, 실험실에서 반창고가 종종 사용되는 가벼운 절상을 모의한 토끼귀 지혈시험에 의하여 평가하였다.
1. 각각의 토끼에서 마취제[래비트 매직(Rabbit Magic)]를 체중 10㎏±1당 1밀리리터의 누여량으로 1㎖ 주사하였다. 래비트 매직을 이용한 마취는 매일 순조롭게 진행되었다.
2. 양쪽 귀의 안쪽변연의 정맥(medial magic)을 절개하였다. 귀를 평탄한 시험대 위에 높고 정맥의 전체 나비를 절개하는데, 정맥이 완전히 절개되지 않도록 주의하였다. 선택되는 정맥부분은 일관되고 큰 직경을 유지하여야 한다.
3. 절개부위로부터 흐르는 소량의 최초 혈액을 가아제와 탈지면으로 정결히 닦아낸 후, 창상 부위를 충분히 관찰하면 소량의 혈액이 흐른다. 절개부위를 다시 한 번 가아제나 탈지면으로 닦아내고, 즉시 절개부위에 반창고 샘플(배면재는 투명하거나 비침)을 정맥에 대해 수직으로 도포하면서, 동시에 스톱워치(stop watch)를 눌렀다. 창상 부위에 첩포한 샘플에 엄지 손가락으로 약하게 5초 동안 압력을 가하여 샘플과 상처 사이에 적절한 접촉이 이루어지도록 하였다.
4. 가시적인 출혈이 완전히 멈추면, 지혈 시간을 초 단위로 기록한 다음, 새로운 샘플로 단계 2 및 3을 반복하였다.
5. 동일한 귀에 대해 처음에 선택한 부위를 2차 절개하고, 상기한 바와 같이 시험하였다. 한쪽 귀에 대해 2 내지 3회 절개하고 샘플을 일정치 않은 방식으로 교체하였다.
[흡수, 흡착 시험]
실시예1 및 비교예 1 내지 3에 따른 일회용 반창고의 흡수, 흡착효과를, 실험실에서 0.9% 생리식염수를 조제하여 하기의 시험에 의해 평가하였다.
1. 실시예1 및 비교예1 내지 3 에 따라 제조된 일회용 반창고를 각각 10개씩 샘플로 사용하여, 샘플의 번호를 기록하고, 패드부분의 박리필름을 절개하였다.
2. 상기 샘플은 건조 오븐에서 110℃, 10분간 건조시키고, 데시케이타(실리카겔)에서 실온으로 식힌 후, 항온 항습실에서 샘플별로 중량을 달고 기록하였다.
3. 미리 조제해 놓은 0.9% 생리식염수에 1시간 정도 침적시켰다.
4. 각 샘플을 동시에 식염수에서 꺼낸 후 길이방향을 지면에서 수직으로 세우고 잔류액을 스스로 흘러내리게 한 후, 필름에 남아 있는 잔류액을 탈지면이나 네프킨류로 제거하였다.
5. 상기 조작이 완료된 샘플을 될 수 있는 한 빠른 시간내에 번호별로 중량을 정밀하게 측정하였다.
6. 5의 측정값에서 2의 측정값을 뺀 후 각각의 평균값과 표준편차를 구하였다.
상기 방법을 사용하여 얻은 결과, 즉, 각 일회용 반창고의 지혈효과[출혈이 그칠 때까지의 시간(초)와 흡수, 흡착효과[패드 부분에 흡수되는 생리식염수 흡수율(%)]를 표 1에 나타내었다.
지지체가 불투명하여 시험 관찰이 어려운 샘플을 위해 각각의 패드에 투명한 필름 형태의 반창고를 사용하여 샘플의 조건을 동일하게 하였다.
흡수, 흡착에 대한 시험 중 흡수량(㎎)을 흡수율(%)로 환산한 것은 샘플별 규격이 서로 상이함에 따른 것이며, 값은 아래의 식으로 구하였다.
[사람 첩부 시험]
실시예1 및 비교예1 내지 3의 일회용 반창고 샘플을 건강한 성인 남자 50명, 여자 20명의 팔의 안족 부위에 샘플 4개를 일정하게 첩부하고, 사용감 및 24시간 첩부후의 피부 발진 등의 알러지 상태를 관찰하여 판정하였다. 판정기준은 무반응을 0으로 하고, 약간의 홍반이 있는 것을 1, 분명하게 홍반이 있는 것을 2, 발진 이상이 생긴 것을 3으로 하여 판정점의 합계로 판정하였고, 그 결과를 표 2에 나타내었다.
Claims (4)
- 지체층과 그 위에 형성된 점착층과 그위에 형성된 패드부 및 박리지로 이루어진 일회용 반창고에 있어서, 상기 패드부가 소디움폴리아크릴레이트 및 활성탄을 포함하는 부직포와 그의 표면에 라미네이팅 되어 있는 상처 박리용 필름으로 이루어져 있는 것을 특징으로 하는 일회용 반창고.
- 제1항에 있어서, 상기 소디움폴리아크릴레이트는 흡수율이 80∼100㎖/g이고, 수분함량이 10중량% 이하이며, 부직포에 대한 농도가 0.01 내지 15%(w/w)인 것을 특징으로 하는 일회용 반창고,
- 제1항에 있어서, 상기 활성탄은 입자 크기가 0.05±0.007㎜이고, 표면적이 1,000±100㎡/㎜이며, 부직포에 대한 농도가 0.01 내지 15%(w/w)인 것을 특징으로 하는 일회용 반창고.
- 제1항 또는 제3항 중의 어느 한 항에 있어서, 부직포의 재질이 비스코스레이온 60∼100%인 것을 특징으로 하는 일회용 반창고.