JPWO2010074134A1 - Silicon wafer cleaning agent - Google Patents
Silicon wafer cleaning agent Download PDFInfo
- Publication number
- JPWO2010074134A1 JPWO2010074134A1 JP2010544117A JP2010544117A JPWO2010074134A1 JP WO2010074134 A1 JPWO2010074134 A1 JP WO2010074134A1 JP 2010544117 A JP2010544117 A JP 2010544117A JP 2010544117 A JP2010544117 A JP 2010544117A JP WO2010074134 A1 JPWO2010074134 A1 JP WO2010074134A1
- Authority
- JP
- Japan
- Prior art keywords
- water
- cleaning liquid
- silicon wafer
- cleaning
- repellent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
表面に微細な凹凸パターンを有するシリコンウェハ用洗浄剤であり、該洗浄剤は、洗浄液Ａ、洗浄液Ｂを含み、前記洗浄液Ａは水系溶液からなり、洗浄液Ｂは凹凸パターンの凹部を撥水化するものであり、前記洗浄液ＢはシリコンウェハのＳｉと化学的に結合可能なユニットを生じせしめる加水分解性部位、疎水性基を含む撥水性化合物とアルコール溶媒を含むアルコール溶液、および、水または酸性水溶液が混合されてなるものであり、該撥水性化合物は、洗浄液Ｂの総量１００質量％中に０．２〜２０質量％となるように混合されてなる。この洗浄剤によって、パターン倒れを誘発しやすい洗浄工程を改善できる。A cleaning agent for a silicon wafer having a fine concavo-convex pattern on the surface. The cleaning agent includes a cleaning liquid A and a cleaning liquid B. The cleaning liquid A is an aqueous solution, and the cleaning liquid B repels the recesses of the concavo-convex pattern. The cleaning liquid B is a hydrolyzable site that generates a unit capable of chemically bonding to Si of a silicon wafer, an alcohol solution containing a hydrophobic group-containing water-repellent compound and an alcohol solvent, and water or an acidic aqueous solution. The water repellent compound is mixed so as to be 0.2 to 20% by mass in 100% by mass of the total amount of the cleaning liquid B. This cleaning agent can improve a cleaning process that easily induces pattern collapse.
Description
本発明は、半導体デバイス製造において、特に微細でアスペクト比の高い回路パターン化されたデバイスの製造歩留まりの向上を目的としたシリコン基板（ウェハ）の洗浄技術に関する。 The present invention relates to a technique for cleaning a silicon substrate (wafer) for the purpose of improving the manufacturing yield of a device having a circuit pattern that is fine and has a high aspect ratio, particularly in the manufacture of semiconductor devices.
ネットワークやデジタル家電用の半導体デバイスにおいて、さらなる高性能・高機能化や低消費電力化が要求されている。そのため回路パターンの微細化が進行しており、それに伴い製造歩留まりの低下を引き起こすパーティクルサイズも微小化している。その結果、微小化したパーティクルの除去を目的とした洗浄工程が多用されており、その結果、半導体製造工程全体の３〜４割にまで洗浄工程が占めている。 In semiconductor devices for networks and digital home appliances, higher performance, higher functionality, and lower power consumption are required. For this reason, circuit patterns are being miniaturized, and accordingly, the particle size that causes a reduction in manufacturing yield is also miniaturized. As a result, a cleaning process for removing fine particles is frequently used, and as a result, the cleaning process accounts for 30 to 40% of the entire semiconductor manufacturing process.
その一方で、従来行われていたアンモニアの混合洗浄剤による洗浄が、回路パターンの微細化に伴い、その塩基性によるウェハへのダメージが問題となっている。そのため、よりダメージの少ない例えば希フッ酸系洗浄剤への代替が進んでいる。 On the other hand, the conventional cleaning with a mixed ammonia cleaning agent causes a problem of damage to the wafer due to its basicity as the circuit pattern becomes finer. For this reason, replacement with, for example, a dilute hydrofluoric acid-based cleaning agent with less damage is in progress.
これにより、洗浄によるウェハへのダメージの問題は改善されたが、半導体デバイスの微細化に伴うパターンのアスペクト比が高くなることによる問題が顕在化している。すなわち洗浄またはリンス後、気液界面がパターンを通過する時にパターンが倒れる現象を引き起こし、歩留まりを大幅に低下することが大きな問題となっている。 Thus, although the problem of damage to the wafer due to cleaning has been improved, the problem due to the increase in the aspect ratio of the pattern accompanying the miniaturization of the semiconductor device has become apparent. That is, after cleaning or rinsing, the pattern collapses when the gas-liquid interface passes through the pattern, and the yield is greatly reduced.
このパターン倒れは、ウェハを洗浄液またはリンス液から引き上げるときに生じる。これは、パターンのアスペクト比が高い部分と低い部分との間において、残液高さの差ができ、それによってパターンに作用する毛細管力に差が生じることが原因と言われている。 This pattern collapse occurs when the wafer is pulled up from the cleaning liquid or the rinse liquid. This is said to be caused by a difference in residual liquid height between a portion where the aspect ratio of the pattern is high and a portion where the aspect ratio is low, thereby causing a difference in capillary force acting on the pattern.
このため、毛細管力を小さくすれば、残液高さの違いによる毛細管力の差が低減し、パターン倒れが解消すると期待できる。毛細管力の大きさは、以下に示される式で求められるＰの絶対値であり、この式からγ、もしくは、ｃｏｓθを小さくすれば、毛細管力を低減できると期待される。
Ｐ＝２×γ×ｃｏｓθ／Ｓ（γ：表面張力、θ：接触角、Ｓ：パターン寸法）For this reason, if the capillary force is reduced, it can be expected that the difference in capillary force due to the difference in the residual liquid height will be reduced and the pattern collapse will be eliminated. The magnitude of the capillary force is the absolute value of P obtained by the following formula. From this formula, it is expected that the capillary force can be reduced by reducing γ or cos θ.
P = 2 × γ × cos θ / S (γ: surface tension, θ: contact angle, S: pattern dimension)
特許文献１には、γを小さくしてパターン倒れを抑制する手法として気液界面を通過する前に洗浄液を水から２−プロパノールへ置換する技術が開示されている。しかし、この手法では、パターン倒れ防止に有効である一方、γが小さい２−プロパノール等の溶媒は通常の接触角も小さくなり、その結果、ｃｏｓθが大きくなる傾向にある。そのため、対応できるパターンのアスペクト比が５以下である等、限界があると言われている。
また、特許文献２には、ｃｏｓθを小さくしてパターン倒れを抑制する手法として、レジストパターンを対象とする技術が開示されている。この手法は接触角を９０°付近とすることで、ｃｏｓθを０に近づけ毛細管力を極限まで下げることによって、パターン倒れを抑制する手法である。
しかし、この開示された技術はレジストパターンを対象としており、レジスト自体を改質するものであり、さらに最終的にレジストと共に除去が可能であるため、乾燥後の処理剤の除去方法を想定する必要がなく、本目的には適用できない。 However, since the disclosed technique is intended for a resist pattern, it modifies the resist itself, and can be finally removed together with the resist. Therefore, it is necessary to assume a method for removing the treatment agent after drying. Is not applicable to this purpose.
また、半導体デバイスのパターン倒れを防止する手法として、臨界流体の利用や液体窒素の利用等が提案されている。しかし、いずれも一定の効果があるものの、従来の洗浄プロセスと異なり、密閉系もしくはバッチでの処理が必要であるため、スループットなどコスト上問題があった。 In addition, as a technique for preventing pattern collapse of a semiconductor device, use of a critical fluid, use of liquid nitrogen, or the like has been proposed. However, all have certain effects, but unlike conventional cleaning processes, processing in a closed system or batch is necessary, and thus there is a problem in cost such as throughput.
半導体デバイスの製造時には、シリコンウェハ表面は微細な凹凸パターンを有する面とされる。本発明は、表面に微細な凹凸パターンを有するシリコンウェハの製造方法において、パターン倒れを誘発しやすい洗浄工程を改善するための洗浄剤を提供することを課題とする。 At the time of manufacturing a semiconductor device, the surface of the silicon wafer is a surface having a fine uneven pattern. An object of the present invention is to provide a cleaning agent for improving a cleaning process that easily induces pattern collapse in a method for manufacturing a silicon wafer having a fine uneven pattern on the surface.
本発明の洗浄剤は、表面に微細な凹凸パターンを有するシリコンウェハ用洗浄剤であり、該洗浄剤は、洗浄液Ａ、洗浄液Ｂを含み、
前記洗浄液Ａは水系溶液からなり、
洗浄液Ｂは凹凸パターンの凹部を撥水化するものであり、
前記洗浄液Ｂは、シリコンウェハのＳｉと化学的に結合可能なユニットを生じせしめる加水分解性部位、疎水性基を含む撥水性化合物とアルコール溶媒を含むアルコール溶液、および、水または酸性水溶液が混合されてなるものであり、該撥水性化合物は、洗浄液Ｂの総量１００質量％中に０．２〜２０質量％となるように混合されてなる撥水性洗浄液とすることで、洗浄液Ｂにより撥水化されたシリコンウェハ表面の凹部に水が保持されたと仮定したときの毛細管力を２．１ＭＮ／ｍ2以下とせしめるものであることを特徴とする。The cleaning agent of the present invention is a cleaning agent for silicon wafers having a fine uneven pattern on the surface, and the cleaning agent includes cleaning liquid A and cleaning liquid B,
The cleaning liquid A is an aqueous solution,
The cleaning liquid B is for repelling the concave portions of the concave / convex pattern,
The cleaning liquid B is a mixture of a hydrolyzable portion that generates a unit capable of chemically bonding to Si of a silicon wafer, an alcohol solution containing a hydrophobic group-containing water-repellent compound and an alcohol solvent, and water or an acidic aqueous solution. The water-repellent compound is made water-repellent by the cleaning liquid B by making the water-repellent cleaning liquid mixed so as to be 0.2 to 20% by mass in 100% by mass of the total amount of the cleaning liquid B. It is characterized in that the capillary force is 2.1 MN / m 2 or less when it is assumed that water is held in the concave portion of the surface of the silicon wafer.
本発明の洗浄剤において、各洗浄液はそれぞれ独立に使用され、該洗浄液は少なくとも２種類以上使用される。 In the cleaning agent of the present invention, each cleaning solution is used independently, and at least two types of cleaning solutions are used.
また、本発明において、撥水性とは、物品表面の表面エネルギーを低減させて、水やその他の液体と該物品表面との間（界面）で相互作用、例えば、水素結合、分子間力などを低減させる意味である。特に水に対して相互作用を低減させる効果が大きいが、水と水以外の液体の混合液や、水以外の液体に対しても相互作用を低減させる効果を有する。該相互作用の低減により、物品表面に対する液体の接触角を大きくすることができる。 In the present invention, the water repellency means reducing the surface energy of the article surface, and interacting between water or other liquid and the article surface (interface), for example, hydrogen bonding, intermolecular force, etc. It means to reduce. In particular, the effect of reducing the interaction with water is great, but it has the effect of reducing the interaction with a mixed liquid of water and a liquid other than water or a liquid other than water. By reducing the interaction, the contact angle of the liquid with the article surface can be increased.
本発明の表面に微細な凹凸パターンを有するシリコンウェハの洗浄剤では、凹凸パターンが形成されたシリコンウェハの洗浄に際して、洗浄液Ｂは洗浄液Ａの前記シリコンウェハへの供給を経てから前記シリコンウェハへ供給される。さらには、洗浄液Ｂはシリコンウェハ表面の凹部に当該洗浄液とは異なる洗浄液が保持された状態で該異なる洗浄液を置換しながらシリコンウェハ表面に供されてもよい。 In the cleaning agent for a silicon wafer having a fine concavo-convex pattern on the surface of the present invention, when cleaning the silicon wafer having the concavo-convex pattern, the cleaning liquid B is supplied to the silicon wafer after the cleaning liquid A is supplied to the silicon wafer. Is done. Furthermore, the cleaning liquid B may be supplied to the silicon wafer surface while replacing the different cleaning liquid in a state where the cleaning liquid different from the cleaning liquid is held in the concave portion of the silicon wafer surface.
本発明のシリコンウェハ用洗浄剤は、複数の洗浄液からなるもので、凹部に保持された洗浄液を、他の洗浄液で置換しながら用いられるもので、該洗浄剤は、最終的にシリコンウェハ表面から除去される。 The cleaning agent for silicon wafers of the present invention comprises a plurality of cleaning liquids, and is used while replacing the cleaning liquid held in the recesses with other cleaning liquids. Removed.
本発明のシリコンウェハ用洗浄剤にてシリコンウェハ表面が洗浄されている間に、シリコンウェハ表面の凹部は、前記撥水性化合物を含む洗浄液Ｂを一旦保持することになる。この保持によって、凹部表面は撥水性化合物により撥水化された表面状態となる。本発明では、前記撥水性化合物をシリコンウェハのＳｉと化学的に結合可能なユニットを生じせしめる加水分解性部位を有するものとしているので、洗浄剤が凹部から除去されるまで前記撥水化された表面状態をシリコンウェハ表面に保持させることができる。 While the silicon wafer surface is being cleaned with the silicon wafer cleaning agent of the present invention, the recesses on the silicon wafer surface temporarily hold the cleaning liquid B containing the water-repellent compound. By this holding, the surface of the recess becomes a surface state that is water-repellent by the water-repellent compound. In the present invention, since the water-repellent compound has a hydrolyzable portion that generates a unit capable of chemically bonding with Si of the silicon wafer, the water-repellent compound is repelled until the cleaning agent is removed from the recess. The surface state can be held on the silicon wafer surface.
本発明では、洗浄液が凹部から除去、すなわち、乾燥されるとき、前記凹部表面が前記撥水化された表面状態となっているので、毛細管力が小さくなり、パターン倒れが生じにくくなる。洗浄液Ｂにおいて、前記撥水性化合物が０．２質量％未満では、前記凹部表面を十分に撥水化された表面状態としにくい。他方、２０質量％超では、該撥水性化合物が凝集しやすくなり、前記凹部表面を均質に撥水化された表面状態としにくい。その結果、シリコンウェハ表面を光照射又はシリコンウェハを加熱する工程にて、撥水性化合物の凝集に起因して形成された部位の除去のための付加的な光照射時間または加熱時間を要するようになる。 In the present invention, when the cleaning liquid is removed from the recess, that is, dried, the surface of the recess is in the water-repellent surface state, so that the capillary force is reduced and the pattern collapse is less likely to occur. In the cleaning liquid B, if the water-repellent compound is less than 0.2% by mass, it is difficult to make the surface of the recesses sufficiently water-repellent. On the other hand, if it exceeds 20% by mass, the water-repellent compound tends to aggregate and it is difficult to make the surface of the concave portion into a uniformly water-repellent surface state. As a result, in the step of irradiating the surface of the silicon wafer with light or heating the silicon wafer, additional light irradiation time or heating time for removing the portion formed due to aggregation of the water repellent compound is required. Become.
本発明の洗浄剤を用いると、表面に微細な凹凸パターンを有するシリコンウェハの製造方法において、洗浄工程が改善される。従って、本発明の洗浄剤を用いる表面に微細な凹凸パターンを有するシリコンウェハの製造方法は、優れたパターン倒れ防止性を示し、シリコンウェハの生産性向上に奏功する。今後益々高くなると予想される例えば７以上のアスペクト比を有する凹凸パターンにも対応可能であり、より高密度化された半導体デバイス生産のコストダウンを可能とする。しかも従来の装置から大きな変更がなく対応でき、その結果、各種の半導体デバイスの製造に適用可能なものとなる。 When the cleaning agent of the present invention is used, the cleaning process is improved in the method for producing a silicon wafer having a fine uneven pattern on the surface. Therefore, the method for producing a silicon wafer having a fine concavo-convex pattern on the surface using the cleaning agent of the present invention exhibits excellent pattern collapse prevention properties and is effective in improving the productivity of silicon wafers. For example, it is possible to cope with a concavo-convex pattern having an aspect ratio of 7 or more, which is expected to become higher in the future, and it is possible to reduce the cost of producing higher-density semiconductor devices. In addition, the conventional apparatus can be applied without significant change, and as a result, can be applied to the manufacture of various semiconductor devices.
本発明の洗浄剤を用いる表面に微細な凹凸パターンを有するシリコンウェハの好適な洗浄方法は、
シリコンウェハ表面を微細な凹凸パターンを有する面とした後、水系溶液からなる洗浄液Ａを当該面に供し、凹部に洗浄液Ａを保持する工程、
凹部に保持された洗浄液Ａを該洗浄液Ａとは異なる洗浄液ａで置換する工程、
該凹部表面を撥水化するための洗浄液Ｂを該凹部に保持する工程、
洗浄剤を除去する工程
を有する。A suitable cleaning method for a silicon wafer having a fine concavo-convex pattern on the surface using the cleaning agent of the present invention,
A process in which the surface of the silicon wafer is made a surface having a fine concavo-convex pattern, and then the cleaning liquid A made of an aqueous solution is applied to the surface, and the cleaning liquid A is held in the recesses.
A step of replacing the cleaning liquid A held in the recess with a cleaning liquid a different from the cleaning liquid A;
Holding the cleaning liquid B for making the surface of the recess water repellent in the recess,
A step of removing the cleaning agent.
さらに、前記洗浄液Ｂを凹部に保持する工程の後で、凹部に保持された洗浄液Ｂを該洗浄液Ｂとは異なる洗浄液ｂに置換してもよい。また、前記異なる洗浄液ｂへの置換を経て、該凹部に水系溶液からなる水系洗浄液を保持する工程を行うことがより好ましい。 Further, after the step of holding the cleaning liquid B in the recess, the cleaning liquid B held in the recess may be replaced with a cleaning liquid b different from the cleaning liquid B. Further, it is more preferable to perform a step of holding an aqueous cleaning liquid composed of an aqueous solution in the concave portion through substitution with the different cleaning liquid b.
また、前記洗浄剤を除去する工程は、
凹部に保持された洗浄液を乾燥により凹部より除去する工程、
シリコンウェハ表面を光照射、又はシリコンウェハを加熱して該凹部から撥水化された表面状態を除去する工程
を有する。In addition, the step of removing the cleaning agent,
Removing the cleaning liquid retained in the recess from the recess by drying;
A step of removing the surface of the silicon wafer that has been made water-repellent by light irradiation or heating the silicon wafer;
また、前記洗浄剤を除去する工程の、凹部に保持された洗浄液を乾燥により凹部より除去する工程とシリコンウェハ表面を光照射、又はシリコンウェハを加熱する工程の間に、凹部に洗浄液Ｂとは異なる洗浄液ｂを供し、該異なる洗浄液ｂを乾燥により除去する工程を行ってもよいし、前記異なる洗浄液ｂを供した後に該凹部に水系溶液からなる水系洗浄液を保持し、該水系洗浄液を乾燥により除去する工程を行ってもよい。 Further, between the step of removing the cleaning agent in the step of removing the cleaning agent from the recess by drying and the step of irradiating the surface of the silicon wafer with light or heating the silicon wafer, the cleaning solution B is in the recess. A different cleaning solution b may be provided, and the different cleaning solution b may be removed by drying, or after the different cleaning solution b is provided, an aqueous cleaning solution composed of an aqueous solution is held in the recess, and the aqueous cleaning solution is dried. You may perform the process to remove.
前記洗浄液Ｂは、シリコンウェハのＳｉと化学的に結合可能なユニットを生じせしめる加水分解性部位、疎水性基を含む撥水性化合物、アルコール溶媒を含むアルコール溶液、および、水または酸性水溶液が混合されてなるものであり、該撥水性化合物は、洗浄液Ｂの総量１００質量％中に０．２〜２０質量％、好ましくは０．５〜１０質量％となるように混合されてなるものとすることが好ましい。 The cleaning liquid B is a mixture of a hydrolyzable site that generates a unit capable of chemically bonding to Si of a silicon wafer, a water repellent compound containing a hydrophobic group, an alcohol solution containing an alcohol solvent, and water or an acidic aqueous solution. The water-repellent compound is mixed in a total amount of 100% by mass of the cleaning liquid B in an amount of 0.2 to 20% by mass, preferably 0.5 to 10% by mass. Is preferred.
シリコンウェハ表面を微細な凹凸パターンを有する面とするパターン形成工程では、まず、該ウェハ表面にレジストを塗布したのち、レジストマスクを介してレジストに露光し、露光されたレジスト、または、露光されなかったレジストをエッチング除去することによって所望の凹凸パターンを有するレジストを作製する。また、レジストにパターンを有するモールドを押し当てることでも、凹凸パターンを有するレジストを得ることができる。次に、ウェハをエッチングする。このとき、レジストパターンの凹の部分が選択的にエッチングされる。最後に、レジストを剥離すると、微細な凹凸パターンを有するシリコンウェハが得られる。 In the pattern formation process in which the surface of the silicon wafer has a fine concavo-convex pattern, first, after applying a resist to the wafer surface, the resist is exposed through a resist mask, and the exposed resist is not exposed. The resist having a desired concavo-convex pattern is produced by etching away the resist. Moreover, the resist which has an uneven | corrugated pattern can be obtained also by pressing the mold which has a pattern to a resist. Next, the wafer is etched. At this time, the concave portion of the resist pattern is selectively etched. Finally, when the resist is removed, a silicon wafer having a fine uneven pattern is obtained.
なお、シリコンウェハとしては、自然酸化膜や熱酸化膜などの酸化ケイ素膜が表面に形成したもの、あるいは、上記凹凸パターンを形成したときに、該凹凸パターンの表面の少なくとも一部が酸化ケイ素となるものも含まれる。 In addition, as a silicon wafer, a silicon oxide film such as a natural oxide film or a thermal oxide film is formed on the surface, or when the above uneven pattern is formed, at least a part of the surface of the uneven pattern is made of silicon oxide. Is also included.
シリコンウェハ表面を微細な凹凸パターンを有する面とした後、洗浄液Ａで表面の洗浄を行い、乾燥等により洗浄液Ａを除去すると、凹部の幅が小さく、凸部のアスペクト比が大きいと、パターン倒れが生じやすくなる。該凹凸パターンは、図１及び図２に記すように定義される。図１は、表面が微細な凹凸パターン２を有する面とされたシリコンウェハ１の概略平面図を示し、図２は図１中のａ−ａ’断面の一部を示したものである。凹部の幅５は、図２に示すように凸部３と凸部３の間隔で示され、凸部のアスペクト比は、凸部の高さ６を凸部の幅７で割ったもので表される。洗浄工程でのパターン倒れは、凹部の幅が７０ｎｍ以下、特には４５ｎｍ以下、アスペクト比が４以上、特には６以上のときに生じやすくなる。
After the surface of the silicon wafer has a fine uneven pattern, the surface is cleaned with the cleaning liquid A, and the cleaning liquid A is removed by drying or the like. If the width of the concave portion is small and the aspect ratio of the convex portion is large, the pattern collapses. Is likely to occur. The concavo-convex pattern is defined as shown in FIGS. FIG. 1 is a schematic plan view of a
また、図３は、洗浄工程にて凹部４が洗浄液８を保持した状態の模式図を示している。図３の模式図のシリコンウェハは、図１のａ−ａ’断面の一部を示すものである。洗浄工程では、まず水系溶液からなる洗浄液Ａが、凹凸パターン２が形成されたシリコンウェハ１に供される。この際、洗浄液Ａは図３に示したように少なくとも凹部４に保持された状態となる。ついで、凹部４に保持された洗浄液Ａを、洗浄液Ａとは異なる洗浄液ａで置換する。この異なる洗浄液ａの例としては、洗浄液Ｂ、水、水溶性有機溶媒、あるいは、それらの混合物、あるいは、それらに酸、アルカリ、界面活性剤のうち少なくとも１種以上が混合されたもの等が挙げられる。なお、水溶性有機溶媒は、該有機溶媒１００質量％に対して水が５質量％溶けるものが好ましい。また、複数の有機溶媒の混合液であっても良い。特に、この異なる洗浄液として洗浄液Ｂ以外を使用したときは、凹部４に洗浄液Ｂ以外の洗浄液が保持された状態を維持し、該洗浄液を洗浄液Ｂへと置換していくことが好ましい。
FIG. 3 is a schematic view showing a state in which the
次に凹部４に保持された洗浄液Ｂと該洗浄液Ｂとは異なる洗浄液ｂとの置換を経て、該凹部に水系溶液からなる水系洗浄液を保持する場合、この異なる洗浄液ｂの例としては、水系溶液からなる水系洗浄液、水、水溶性有機溶媒、あるいは、それらの混合物、あるいは、それらに酸、アルカリ、界面活性剤のうち少なくとも１種以上が混合されたもの等が挙げられる。特に、この異なる洗浄液ｂとして水系洗浄液以外を使用したときは、凹部４に水系洗浄液以外の洗浄液が保持された状態を維持し、該洗浄液を水系洗浄液へと置換していくことが好ましい。
Next, when the cleaning liquid B held in the
水系溶液からなる水系洗浄液である洗浄液Ａの例としては、水、あるいは、水に水溶性有機溶媒、酸、アルカリのうち少なくとも１種以上が混合された水を主成分（例えば、水の含有率が５０質量％以上）とするもの等が挙げられる。 Examples of the cleaning liquid A that is an aqueous cleaning liquid composed of an aqueous solution include water or water in which at least one of a water-soluble organic solvent, an acid, and an alkali is mixed in water as a main component (for example, the content of water Is 50% by mass or more).
撥水性化合物により撥水化された凹部４に水系洗浄液が保持された場合の模式図を図４に示す。図４の模式図のシリコンウェハは、図１のａ−ａ’断面の一部を示すものである。凹部４の表面は撥水性化合物により撥水化された表面状態１０となっている。そして、前記Ｓｉと化学的に結合可能なユニットによって、撥水化された表面状態１０は、水系洗浄液である９が凹部４から除去されるときもシリコンウェハ表面に保持されている。
FIG. 4 shows a schematic diagram in the case where the aqueous cleaning liquid is held in the
洗浄液Ｂにより撥水化されたシリコンウェハ表面の凹部、すなわち図４に示すような凹部４の表面が撥水性化合物により撥水化された表面状態１０となったとき、該凹部に水が保持されたと仮定したときの毛細管力は２．１ＭＮ／ｍ2以下であることが好ましい。該毛細管力が２．１ＭＮ／ｍ2以下であれば、パターン倒れが発生し難いため好ましい。また、該毛細管力が小さくなると、パターン倒れは更に発生し難くなるため、該毛細管力は１．５ＭＮ／ｍ2以下が特に好ましく、１．０ＭＮ／ｍ2以下がさらに好ましい。さらに、洗浄液との接触角を９０°付近に調整して毛細管力を限りなく０．０ＭＮ／ｍ2に近づけることが理想的である。When the concave portion of the surface of the silicon wafer that has been made water-repellent by the cleaning liquid B, that is, the surface of the
また、洗浄液ＢのシリコンウェハのＳｉと化学的に結合可能なユニットを生じせしめる加水分解性部位と疎水性基を含む撥水性化合物において、該加水分解性部位の例として、メトキシ基、エトキシ基、プロポキシ基、イソプロポキシ基、ブトキシ基等のアルコキシ基、アセトキシ基、トリフルオロアセトキシ基、−ＯＣ（ＣＨ3）＝ＣＨＣＯＣＨ3などのＳｉ−Ｏ−Ｃ結合、クロロ基、ブロモ基などのハロゲン基、イソシアネート基、アミノ基、イソチオシアネート基、アジド基、アセトアミド基、シラザンなどのＳｉ−Ｎ結合、アルキルスルホネート基、パーフルオロアルキルスルホネート基などのＳｉ−Ｏ−Ｓ結合、あるいは、ニトリル基などが挙げられ、該疎水性基の例として、炭化水素基を含む１価の有機基やＣ−Ｆ結合を含む１価の有機基が挙げられる。このような撥水性化合物は、前記加水分解性部位が加水分解して生成する官能基がシリコンウェハの凹凸パターンの酸化ケイ素層のシラノール基と反応するため、ウェハに固定される。これにより、ウェハ表面を疎水性基で覆うことができるので毛細管力を小さくできる。Further, in the water-repellent compound containing a hydrolyzable site and a hydrophobic group that can form a unit chemically bondable to Si of the silicon wafer of the cleaning liquid B, examples of the hydrolyzable site include a methoxy group, an ethoxy group, Alkoxy groups such as propoxy group, isopropoxy group, butoxy group, acetoxy group, trifluoroacetoxy group, Si—O—C bond such as —OC (CH 3 ) ═CHCOCH 3 , halogen groups such as chloro group and bromo group, Examples include Si—N bonds such as isocyanate groups, amino groups, isothiocyanate groups, azide groups, acetamide groups, and silazanes, Si—O—S bonds such as alkyl sulfonate groups and perfluoroalkyl sulfonate groups, and nitrile groups. Examples of the hydrophobic group include a monovalent organic group containing a hydrocarbon group and a C—F bond. Include organic groups are. Such a water-repellent compound is fixed to the wafer because the functional group generated by hydrolysis of the hydrolyzable site reacts with the silanol group of the silicon oxide layer of the concavo-convex pattern of the silicon wafer. Thereby, since the wafer surface can be covered with the hydrophobic group, the capillary force can be reduced.
さらに、洗浄液Ｂにおいて、シリコンウェハのＳｉと化学的に結合可能なユニットを生じせしめる加水分解性部位と疎水性基を含む撥水性化合物が、
ＣmＨ2m+1ＳｉＲsＸ3-s （ｍ＝１〜１８）と
ＣnＦ2n+1ＣＨ2ＣＨ2ＳｉＲtＹ3-t （ｎ＝１〜８）と
からなる群から選ばれる少なくとも一つからなるものとすることが好ましい。ここで、ｓとｔは、０〜２の整数であり、Ｒは、水素原子、または、１価の炭化水素基であり、ＸおよびＹは加水分解性部位である。Furthermore, in the cleaning liquid B, a water-repellent compound containing a hydrolyzable site and a hydrophobic group that gives rise to a unit that can be chemically bonded to Si of the silicon wafer,
C m H 2m + 1 SiR s X 3-s (m = 1-18) and C n F 2n + 1 CH 2 CH 2 SiR t Y 3-t (n = 1-8) It is preferable to consist of at least one. Here, s and t are integers of 0 to 2, R is a hydrogen atom or a monovalent hydrocarbon group, and X and Y are hydrolyzable sites.
このような撥水性化合物により撥水化された表面状態は、シリコンウェハ表面を光照射又はシリコンウェハを加熱する工程にて除去しやすい。 Such a surface state rendered water repellent by the water repellent compound is easy to remove in the process of light irradiation or heating the silicon wafer surface.
ＣmＨ2m+1ＳｉＲsＸ3-s （ｍ＝１〜１８、ｓは０〜２の整数、Ｒは水素原子、または、１価の炭化水素基）で示される撥水性化合物としては、例えば、Ｃ18Ｈ37Ｓｉ（ＯＣＨ3）3、Ｃ10Ｈ21Ｓｉ（ＯＣＨ3）3、Ｃ8Ｈ17Ｓｉ（ＯＣＨ3）3、Ｃ6Ｈ13Ｓｉ（ＯＣＨ3）3、Ｃ3Ｈ7Ｓｉ（ＯＣＨ3）3、ＣＨ3Ｓｉ（ＯＣＨ3）3、Ｃ18Ｈ37Ｓｉ（ＣＨ3）（ＯＣＨ3）2、Ｃ10Ｈ21Ｓｉ（ＣＨ3）（ＯＣＨ3）2、Ｃ6Ｈ13Ｓｉ（ＣＨ3）（ＯＣＨ3）2、Ｃ3Ｈ7Ｓｉ（ＣＨ3）（ＯＣＨ3）2、（ＣＨ3）2Ｓｉ（ＯＣＨ3）2、Ｃ18Ｈ37Ｓｉ（ＣＨ3）2ＯＣＨ3、Ｃ10Ｈ21Ｓｉ（ＣＨ3）2ＯＣＨ3、Ｃ6Ｈ13Ｓｉ（ＣＨ3）2ＯＣＨ3、Ｃ3Ｈ7Ｓｉ（ＣＨ3）2ＯＣＨ3、（ＣＨ3）3ＳｉＯＣＨ3、ＨＳｉ（ＣＨ3）2ＯＣＨ3、Ｃ18Ｈ37Ｓｉ（ＯＣ2Ｈ5）3、Ｃ10Ｈ21Ｓｉ（ＯＣ2Ｈ5）3、Ｃ6Ｈ13Ｓｉ（ＯＣ2Ｈ5）3、Ｃ3Ｈ7Ｓｉ（ＯＣ2Ｈ5）3、ＣＨ3Ｓｉ（ＯＣ2Ｈ5）3、Ｃ18Ｈ37Ｓｉ（ＣＨ3）（ＯＣ2Ｈ5）2、Ｃ10Ｈ21Ｓｉ（ＣＨ3）（ＯＣ2Ｈ5）2、Ｃ6Ｈ13Ｓｉ（ＣＨ3）（ＯＣ2Ｈ5）2、Ｃ3Ｈ7Ｓｉ（ＣＨ3）（ＯＣ2Ｈ5）2、（ＣＨ3）2Ｓｉ（ＯＣ2Ｈ5）2、Ｃ18Ｈ37Ｓｉ（ＣＨ3）2ＯＣ2Ｈ5、Ｃ10Ｈ21Ｓｉ（ＣＨ3）2ＯＣ2Ｈ5、Ｃ6Ｈ13Ｓｉ（ＣＨ3）2ＯＣ2Ｈ5、Ｃ3Ｈ7Ｓｉ（ＣＨ3）2ＯＣ2Ｈ5、（ＣＨ3）3ＳｉＯＣ2Ｈ5、ＨＳｉ（ＣＨ3）2ＯＣ2Ｈ5などのアルキルアルコキシシラン、あるいは、（ＣＨ3）3ＳｉＮＨＳｉ（ＣＨ3）3、Ｃ2Ｈ5Ｓｉ（ＣＨ3）2ＮＨＳｉ（ＣＨ3）2Ｃ2Ｈ5、Ｃ3Ｈ7Ｓｉ（ＣＨ3）2ＮＨＳｉ（ＣＨ3）2Ｃ3Ｈ7、Ｃ6Ｈ13Ｓｉ（ＣＨ3）2ＮＨＳｉ（ＣＨ3）2Ｃ6Ｈ13、Ｃ6Ｈ5Ｓｉ（ＣＨ3）2ＮＨＳｉ（ＣＨ3）2Ｃ6Ｈ5、（ＣＨ3）3ＳｉＮ｛Ｓｉ（ＣＨ3）3｝2、Ｃ2Ｈ5Ｓｉ（ＣＨ3）2Ｎ｛Ｓｉ（ＣＨ3）2Ｃ2Ｈ5｝2、（ＣＨ3）2ＨＳｉＮＨＳｉ（ＣＨ3）2Ｈなどのシラザン化合物、あるいは、前記アルキルアルコキシシランのアルコキシ基をクロロ基、イソシアネート基、アミノ基、ジアルキルアミノ基、−ＮＨＣＯＣＨ3、−Ｎ3、−Ｎ＝Ｃ＝Ｓ、−Ｎ（ＣＨ3）ＣＯＣＨ3、−Ｎ（ＣＨ3）ＣＯＣＦ3、−Ｎ＝Ｃ（ＣＨ3）ＯＳｉ（ＣＨ3）3、−Ｎ＝Ｃ（ＣＦ3）ＯＳｉ（ＣＨ3）3、−ＮＨＣＯ−ＯＳｉ（ＣＨ3）3、−ＮＨＣＯ−ＮＨ−Ｓｉ（ＣＨ3）3、イミダゾール環、オキサゾリジノン環、モルホリン環、アセトキシ基、トリフルオロアセトキシ基、−ＯＣ（ＣＨ3）＝ＣＨＣＯＣＨ3、ニトリル基などに置き換えたアルキルシランを用いることができる。As the water repellent compound represented by C m H 2m + 1 SiR s X 3-s (m = 1 to 18, s is an integer of 0 to 2, R is a hydrogen atom or a monovalent hydrocarbon group), For example, C 18 H 37 Si (OCH 3) 3, C 10 H 21 Si (OCH 3) 3, C 8 H 17 Si (OCH 3) 3, C 6 H 13 Si (OCH 3) 3, C 3 H 7 Si (OCH 3 ) 3 , CH 3 Si (OCH 3 ) 3 , C 18 H 37 Si (CH 3 ) (OCH 3 ) 2 , C 10 H 21 Si (CH 3 ) (OCH 3 ) 2 , C 6 H 13 Si (CH 3 ) (OCH 3 ) 2 , C 3 H 7 Si (CH 3 ) (OCH 3 ) 2 , (CH 3 ) 2 Si (OCH 3 ) 2 , C 18 H 37 Si (CH 3 ) 2 OCH 3 , C 10 H 21 Si (CH 3) 2 OCH 3, C 6 H 13 Si (CH 3) 2 OCH 3, C 3 H 7 Si (CH 3) 2 OCH 3, (CH 3) 3 SiOCH 3, HSi CH 3) 2 OCH 3, C 18 H 37 Si (OC 2 H 5) 3, C 10 H 21 Si (OC 2 H 5) 3, C 6 H 13 Si (OC 2 H 5) 3, C 3 H 7 Si (OC 2 H 5 ) 3 , CH 3 Si (OC 2 H 5 ) 3 , C 18 H 37 Si (CH 3 ) (OC 2 H 5 ) 2 , C 10 H 21 Si (CH 3 ) (OC 2 H 5) 2, C 6 H 13 Si (CH 3) (OC 2 H 5) 2, C 3 H 7 Si (CH 3) (OC 2 H 5) 2, (CH 3) 2 Si (OC 2 H 5) 2, C 18 H 37 Si ( CH 3) 2 OC 2 H 5, C 10 H 21 Si (CH 3) 2 OC 2 H 5, C 6 H 13 Si (CH 3) 2 OC 2 H 5, C 3 H 7 Alkoxyalkoxysilanes such as Si (CH 3 ) 2 OC 2 H 5 , (CH 3 ) 3 SiOC 2 H 5 , HSi (CH 3 ) 2 OC 2 H 5 , or (CH 3 ) 3 SiNHSi (CH 3 ) 3 , C 2 H 5 Si ( CH 3 ) 2 NHSi (CH 3 ) 2 C 2 H 5 , C 3 H 7 Si (CH 3 ) 2 NHSi (CH 3 ) 2 C 3 H 7 , C 6 H 13 Si (CH 3 ) 2 NHSi (CH 3 ) 2 C 6 H 13 , C 6 H 5 Si (CH 3 ) 2 NHSi (CH 3 ) 2 C 6 H 5 , (CH 3 ) 3 SiN {Si (CH 3 ) 3 } 2 , C 2 H 5 Si ( Silazane compounds such as CH 3 ) 2 N {Si (CH 3 ) 2 C 2 H 5 } 2 , (CH 3 ) 2 HSiNHSi (CH 3 ) 2 H, or an alkoxy group of the alkylalkoxysilane is a chloro group or an isocyanate Group, amino group, dialkylamino group, —NHCOCH 3 , —N 3 , —N═C═S, —N (CH 3 ) COCH 3 , —N (CH 3 ) COCF 3 , —N═C (CH 3 ) OSi (CH 3) 3, -N = C (CF 3) OSi (CH 3) 3, -NHCO-OSi ( H 3) 3, -NHCO-NH -Si (CH 3) 3, an imidazole ring, an oxazolidinone ring, morpholine ring, acetoxy group, trifluoroacetoxy group, -OC (CH 3) = CHCOCH 3, replaced etc. nitrile group Alkylsilanes can be used.
また、ＣnＦ2n+1ＣＨ2ＣＨ2ＳｉＲtＹ3-t （ｎ＝１〜８、ｔは０〜２の整数、Ｒは水素原子、または、１価の炭化水素基）で示される撥水性化合物としては、例えば、Ｃ8Ｆ17ＣＨ2ＣＨ2Ｓｉ（ＯＣＨ3）3、Ｃ6Ｆ13ＣＨ2ＣＨ2Ｓｉ（ＯＣＨ3）3、Ｃ4Ｆ9ＣＨ2ＣＨ2Ｓｉ（ＯＣＨ3）3、ＣＦ3ＣＨ2ＣＨ2Ｓｉ（ＯＣＨ3）3、Ｃ8Ｆ17ＣＨ2ＣＨ2Ｓｉ（ＯＣ2Ｈ5）3、Ｃ6Ｆ13ＣＨ2ＣＨ2Ｓｉ（ＯＣ2Ｈ5）3、Ｃ4Ｆ9ＣＨ2ＣＨ2Ｓｉ（ＯＣ2Ｈ5）3、ＣＦ3ＣＨ2ＣＨ2Ｓｉ（ＯＣ2Ｈ5）3、Ｃ8Ｆ17ＣＨ2ＣＨ2Ｓｉ（ＣＨ3）（ＯＣＨ3）2、Ｃ6Ｆ13ＣＨ2ＣＨ2Ｓｉ（ＣＨ3）（ＯＣＨ3）2、Ｃ4Ｆ9ＣＨ2ＣＨ2Ｓｉ（ＣＨ3）（ＯＣＨ3）2、ＣＦ3ＣＨ2ＣＨ2Ｓｉ（ＣＨ3）（ＯＣＨ3）2、Ｃ8Ｆ17ＣＨ2ＣＨ2Ｓｉ（ＣＨ3）2ＯＣＨ3、Ｃ6Ｆ13ＣＨ2ＣＨ2Ｓｉ（ＣＨ3）2ＯＣＨ3、Ｃ4Ｆ9ＣＨ2ＣＨ2Ｓｉ（ＣＨ3）2ＯＣＨ3、ＣＦ3ＣＨ2ＣＨ2Ｓｉ（ＣＨ3）2ＯＣＨ3のフルオロアルキルアルコキシシラン、あるいは、ＣＦ3ＣＨ2ＣＨ2Ｓｉ（ＣＨ3）2ＮＨＳｉ（ＣＨ3）2ＣＨ2ＣＨ2ＣＦ3、Ｃ4Ｆ9ＣＨ2ＣＨ2Ｓｉ（ＣＨ3）2ＮＨＳｉ（ＣＨ3）2ＣＨ2ＣＨ2Ｃ4Ｆ9、Ｃ6Ｆ13ＣＨ2ＣＨ2Ｓｉ（ＣＨ3）2ＮＨＳｉ（ＣＨ3）2ＣＨ2ＣＨ2Ｃ6Ｆ13、Ｃ8Ｆ17ＣＨ2ＣＨ2Ｓｉ（ＣＨ3）2ＮＨＳｉ（ＣＨ3）2ＣＨ2ＣＨ2Ｃ8Ｆ17、ＣＦ3ＣＨ2ＣＨ2Ｓｉ（ＣＨ3）2Ｎ｛Ｓｉ（ＣＨ3）2ＣＨ2ＣＨ2ＣＦ3｝2などのシラザン化合物、あるいは、前記フルオロアルキルアルコキシシランのアルコキシ基をクロロ基、イソシアネート基、アミノ基、ジアルキルアミノ基、ＮＨＣＯＣＨ3、−Ｎ3、−Ｎ＝Ｃ＝Ｓ、−Ｎ（ＣＨ3）ＣＯＣＨ3、−Ｎ（ＣＨ3）ＣＯＣＦ3、−Ｎ＝Ｃ（ＣＨ3）ＯＳｉ（ＣＨ3）3、−Ｎ＝Ｃ（ＣＦ3）ＯＳｉ（ＣＨ3）3、−ＮＨＣＯ−ＯＳｉ（ＣＨ3）3、−ＮＨＣＯ−ＮＨ−Ｓｉ（ＣＨ3）3、イミダゾール環、オキサゾリジノン環、モルホリン環、アセトキシ基、トリフルオロアセトキシ基、−ＯＣ（ＣＨ3）＝ＣＨＣＯＣＨ3、ニトリル基などに置き換えたアルキルシランを用いることができる。Further, it is represented by C n F 2n + 1 CH 2 CH 2 SiR t Y 3-t (n = 1 to 8, t is an integer of 0 to 2, R is a hydrogen atom or a monovalent hydrocarbon group). Examples of the water repellent compound include C 8 F 17 CH 2 CH 2 Si (OCH 3 ) 3 , C 6 F 13 CH 2 CH 2 Si (OCH 3 ) 3 , C 4 F 9 CH 2 CH 2 Si (OCH 3). ) 3, CF 3 CH 2 CH 2 Si (OCH 3) 3, C 8 F 17 CH 2 CH 2 Si (OC 2 H 5) 3, C 6 F 13 CH 2 CH 2 Si (OC 2 H 5) 3, C 4 F 9 CH 2 CH 2 Si (OC 2 H 5) 3, CF 3 CH 2 CH 2 Si (OC 2 H 5) 3, C 8 F 17 CH 2 CH 2 Si (CH 3) (OCH 3) 2 C 6 F 13 CH 2 CH 2 Si (CH 3 ) (OCH 3 ) 2 , C 4 F 9 CH 2 CH 2 Si (CH 3 ) (OCH 3 ) 2 , CF 3 CH 2 CH 2 Si (CH 3 ) ( CH 3) 2, C 8 F 17 CH 2 CH 2 Si (CH 3) 2 OCH 3, C 6 F 13 CH 2 CH 2 Si (CH 3) 2 OCH 3, C 4 F 9 CH 2 CH 2 Si (CH 3 ) 2 OCH 3 , CF 3 CH 2 CH 2 Si (CH 3 ) 2 OCH 3 fluoroalkylalkoxysilane, or CF 3 CH 2 CH 2 Si (CH 3 ) 2 NHSi (CH 3 ) 2 CH 2 CH 2 CF 3 , C 4 F 9 CH 2 CH 2 Si (CH 3 ) 2 NHSi (CH 3 ) 2 CH 2 CH 2 C 4 F 9 , C 6 F 13 CH 2 CH 2 Si (CH 3 ) 2 NHSi (CH 3 ) 2 CH 2 CH 2 C 6 F 13 , C 8 F 17 CH 2 CH 2 Si (CH 3 ) 2 NHSi (CH 3 ) 2 CH 2 CH 2 C 8 F 17 , CF 3 CH 2 CH 2 Si (CH 3 ) 2 N {Si (CH 3 ) 2 CH 2 CH 2 CF 3} silazane compound such as 2, or, the full B alkylalkoxy chloro group the alkoxy group of the silane, isocyanate group, an amino group, a dialkylamino group, NHCOCH 3, -N 3, -N = C = S, -N (CH 3) COCH 3, -N (CH 3) COCF 3, -N = C (CH 3) OSi (CH 3) 3, -N = C (CF 3) OSi (CH 3) 3, -NHCO-OSi (CH 3) 3, -NHCO-NH-Si ( CH 3) 3, an imidazole ring, an oxazolidinone ring, morpholine ring, acetoxy group, trifluoroacetoxy group, -OC (CH 3) = CHCOCH 3, it is possible to use an alkyl silane is replaced with such a nitrile group.
なお、加水分解性部位であるＸやＹは、加水分解反応性の点から、メトキシ基、エトキシ基が特に好ましい。 Note that X and Y, which are hydrolyzable sites, are particularly preferably a methoxy group and an ethoxy group from the viewpoint of hydrolysis reactivity.
洗浄液Ｂは、前記撥水性化合物の加水分解反応を進行させるために水または酸性水溶液を含ませることが好ましい。そして、洗浄液Ｂに含ませる酸性水溶液は、ｐＨ値が５以下、特に０〜４に調整すると加水分解反応が早くなるため好ましい。酸は、硝酸、塩酸、酢酸、硫酸、あるいは、有機酸等を使用することができる。 The cleaning liquid B preferably contains water or an acidic aqueous solution in order to advance the hydrolysis reaction of the water repellent compound. The acidic aqueous solution contained in the cleaning liquid B is preferably adjusted to a pH value of 5 or less, particularly 0 to 4 because the hydrolysis reaction is accelerated. As the acid, nitric acid, hydrochloric acid, acetic acid, sulfuric acid, an organic acid, or the like can be used.
また、洗浄液Ｂ中に含まれることのある水の量は、前記撥水性化合物が有する加水分解によりＳｉと化学的に結合可能なユニットの数に対して、分子数で１〜２００倍量とすることが好ましい。１倍量未満では、加水分解反応が十分に進行しないことがある。また、２００倍量超では、洗浄液Ｂ中の前記撥水性化合物の溶解度が減少することがあり、均質な洗浄液Ｂを得にくくなることや、洗浄液Ｂのポットライフが短くなることがある。特には、水の量は、２〜１００倍量とすることが好ましい。 In addition, the amount of water that may be contained in the cleaning liquid B is 1 to 200 times the number of molecules relative to the number of units that can be chemically bonded to Si by hydrolysis of the water repellent compound. It is preferable. If the amount is less than 1 time, the hydrolysis reaction may not proceed sufficiently. On the other hand, when the amount exceeds 200 times, the solubility of the water-repellent compound in the cleaning liquid B may decrease, and it may be difficult to obtain a homogeneous cleaning liquid B, or the pot life of the cleaning liquid B may be shortened. In particular, the amount of water is preferably 2 to 100 times.
また、洗浄液Ｂ中のアルコール溶媒としては、メタノール、エタノール、１−プロパノール、２−プロパノール等の低級アルコールが特に好ましい。 Further, as the alcohol solvent in the cleaning liquid B, lower alcohols such as methanol, ethanol, 1-propanol, 2-propanol and the like are particularly preferable.
洗浄液Ｂは、前記撥水性化合物とアルコール溶媒とを混合し、水または酸性水溶液を添加、攪拌して得ることが好ましい。ここで、前記撥水性化合物とアルコール溶媒を先に混合すると、撥水性化合物と水または酸性水溶液を処理液中に均質に混合させることが容易である。 The cleaning liquid B is preferably obtained by mixing the water repellent compound and an alcohol solvent, adding water or an acidic aqueous solution, and stirring. Here, when the water-repellent compound and the alcohol solvent are mixed first, it is easy to uniformly mix the water-repellent compound and water or an acidic aqueous solution into the treatment liquid.
洗浄液Ｂは、温度を高くすると、より短時間で前記凹部表面を撥水化された表面状態としやすくなる。均質に撥水化された表面状態となりやすい温度は、１０〜１２０℃、特には２０〜８０℃で保持されることが好ましい。洗浄液Ｂの温度は、凹部４に保持されているときも当該温度に保持することが好ましい。
When the temperature of the cleaning liquid B is increased, the surface of the concave portion is easily made water repellent in a shorter time. It is preferable that the temperature at which the surface state easily becomes water-repellent is easily maintained at 10 to 120 ° C., particularly 20 to 80 ° C. The temperature of the cleaning liquid B is preferably maintained at the temperature even when it is held in the
次に、撥水性化合物により撥水化された凹部４に保持された洗浄剤を除去する工程が行われる。該工程は、
凹部に保持された洗浄液を乾燥により凹部より除去する工程
シリコンウェハ表面を光照射又はシリコンウェハを加熱して該凹部から撥水化された表面状態を除去する工程
を有することが好ましい。Next, a step of removing the cleaning agent held in the
The step of removing the cleaning liquid held in the concave portion from the concave portion by drying It is preferable to have a step of removing the surface state of the silicon wafer surface that has been made water-repellent by light irradiation or heating the silicon wafer.
前記凹部から洗浄液が除去されるときに、凹部に保持されている洗浄液は、水系洗浄液が好ましい。この場合、前記洗浄液Ｂを凹部に保持する工程の後で、凹部に保持された洗浄液Ｂと該洗浄液Ｂとは異なる洗浄液ｂとの置換を経て該凹部に水系洗浄液を保持する工程を行うことが好ましい。なお、前記凹部から洗浄液が除去されるときに、凹部に保持されている洗浄液は、洗浄液Ｂ、あるいは、該異なる洗浄液ｂでも良い。 When the cleaning liquid is removed from the recess, the cleaning liquid held in the recess is preferably an aqueous cleaning liquid. In this case, after the step of holding the cleaning liquid B in the concave portion, a step of holding the aqueous cleaning liquid in the concave portion through replacement of the cleaning liquid B held in the concave portion with a cleaning liquid b different from the cleaning liquid B is performed. preferable. When the cleaning liquid is removed from the recess, the cleaning liquid held in the recess may be the cleaning liquid B or the different cleaning liquid b.
前記の洗浄液を凹部より除去する工程では、洗浄液が乾燥により除去される。当該乾燥は、スピン乾燥法、ＩＰＡ（２−プロパノール）蒸気乾燥、マランゴニ乾燥、加熱乾燥、温風乾燥、真空乾燥などの周知の乾燥方法によって行うことが好ましい。 In the step of removing the cleaning liquid from the recess, the cleaning liquid is removed by drying. The drying is preferably performed by a known drying method such as spin drying, IPA (2-propanol) vapor drying, Marangoni drying, heat drying, hot air drying, or vacuum drying.
前記のシリコンウェハ表面を光照射又はシリコンウェハを加熱する工程では、シリコンウェハ表面の撥水化された表面状態１０が除去される。
In the step of irradiating the silicon wafer surface with light or heating the silicon wafer, the water-
光照射で前記撥水化された表面状態１０を除去する場合、撥水性化合物により撥水化された表面状態１０中のＳｉ−Ｃ結合、Ｃ−Ｃ結合、Ｃ−Ｆ結合を切断することが有効であり、このためには、それらの結合エネルギーである５８〜８０ｋｃａｌ／ｍｏｌ、８３ｋｃａｌ／ｍｏｌ、１１６ｋｃａｌ／ｍｏｌに相当する太陽光線エネルギーである３５０〜４５０ｎｍ、３４０ｎｍ、２４０ｎｍよりも短い波長を含む紫外線を照射することが好ましい。この光源としては、メタルハライドランプ、低圧水銀ランプ、高圧水銀ランプ、エキシマランプ、カーボンアークなどが用いられる。紫外線照射強度は、例えば、照度計（ミノルタ製照射強度計ＵＭ−１０、受光部ＵＭ−３６０〔ピーク感度波長：３６５ｎｍ、測定波長範囲：３１０〜４００ｎｍ〕の測定値で１００ｍＷ／ｃｍ2以上が好ましく、２００ｍＷ／ｃｍ2以上が特に好ましい。なお、照射強度が１００ｍＷ／ｃｍ2未満では前記撥水化された表面状態１０を除去するのに長時間要するようになる。When removing the water-
また、光照射で前記撥水化された表面状態１０を除去する場合、紫外線で前記撥水化された表面状態１０の構成成分を分解すると同時に活性酸素を発生させ、該活性酸素によって前記撥水化された表面状態１０の構成成分を酸化揮発させると、処理時間が短くなるので特に好ましい。この光源としては、低圧水銀ランプやエキシマランプが用いられる。
In addition, when removing the water-
シリコンウェハを加熱する場合、４００〜７００℃、好ましくは、５００〜７００℃でシリコンウェハの加熱を行う。この加熱時間は、１〜６０ｍｉｎ、好ましくは１０〜３０ｍｉｎの保持で行うことが好ましい。また、当該工程では、オゾン照射、プラズマ照射、コロナ放電などを併用してもよい。 When the silicon wafer is heated, the silicon wafer is heated at 400 to 700 ° C, preferably 500 to 700 ° C. The heating time is preferably 1 to 60 minutes, preferably 10 to 30 minutes. In this process, ozone irradiation, plasma irradiation, corona discharge, or the like may be used in combination.
シリコンウェハの表面を微細な凹凸パターンを有する面とすること、凹部に保持された洗浄液を他の洗浄液で置換することは、他の文献等にて種々なされているように、既に確立された技術であるので、本発明では、洗浄液Ｂの評価を中心に行った。また、背景技術等で述べた式
Ｐ＝２×γ×ｃｏｓθ／Ｓ（γ：表面張力、θ：接触角、Ｓ：パターン寸法）から明らかなようにパターン倒れは、洗浄液のシリコンウェハ表面への接触角、すなわち液滴の接触角と、洗浄液の表面張力に大きく依存する。凹凸パターン２の凹部４に保持された洗浄液の場合、液滴の接触角と、パターン倒れと等価なものとして考えてよい毛細管力とは相関性があるので、前記式と撥水化された表面状態１０の液滴の接触角の評価から毛細管力を導き出してもよい。なお、実施例において、前記洗浄液として、水系洗浄液の代表的なものである水を用いた。Establishing the surface of a silicon wafer as a surface having a fine concavo-convex pattern and replacing the cleaning liquid held in the recesses with other cleaning liquids are already established techniques, as has been done in various literatures. Therefore, in the present invention, the cleaning liquid B was mainly evaluated. Further, as is clear from the formula P = 2 × γ × cos θ / S (γ: surface tension, θ: contact angle, S: pattern dimension) described in the background art, the pattern collapse is caused by the cleaning liquid on the silicon wafer surface. It greatly depends on the contact angle, that is, the contact angle of the droplet and the surface tension of the cleaning liquid. In the case of the cleaning liquid held in the
しかしながら、表面に微細な凹凸パターンを有するシリコンウェハの場合、パターンは非常に微細なため、撥水化された表面状態１０自体の撥水性を正確に評価することができない。
However, in the case of a silicon wafer having a fine concavo-convex pattern on the surface, since the pattern is very fine, the water repellency of the water-
撥水性の評価のための水滴の接触角の評価は、ＪＩＳ Ｒ ３２５７「基板ガラス表面のぬれ性試験方法」にもあるように、サンプル（基材）表面に数μｌの水滴を滴下し、水滴と基材表面のなす角度の測定によりなされる。しかし、パターンを有するシリコンウェハの場合、接触角が非常に大きくなる。これは、Ｗｅｎｚｅｌ効果やＣａｓｓｉｅ効果が生じるからで、接触角が基材の表面形状（ラフネス）に影響され、見かけ上の水滴の接触角が増大するためである。 As described in JIS R 3257 “Testing method for wettability of substrate glass surface”, the contact angle of water droplets for water repellency is evaluated by dropping several μl of water droplets on the sample (base material) surface. And measurement of the angle formed by the substrate surface. However, in the case of a silicon wafer having a pattern, the contact angle becomes very large. This is because a Wenzel effect and a Cassie effect occur, and the contact angle is affected by the surface shape (roughness) of the substrate, and the apparent contact angle of water droplets increases.
そこで、本発明では洗浄液Ｂを表面が平滑なシリコンウェハに供して、撥水化された表面状態として、該表面状態を表面に微細な凹凸パターン２が形成されたシリコンウェハ１の撥水化された表面状態１０とみなし、種々評価を行った。
Therefore, in the present invention, the cleaning liquid B is applied to a silicon wafer having a smooth surface to make the surface repellent, and the
詳細を下記に述べる。以下では、洗浄液Ｂが供されたシリコンウェハの評価方法、洗浄液Ｂの調製、そして、シリコンウェハに洗浄液Ｂを供した後の評価結果が述べられる。 Details are described below. In the following, the evaluation method of the silicon wafer provided with the cleaning liquid B, the preparation of the cleaning liquid B, and the evaluation results after supplying the cleaning liquid B to the silicon wafer will be described.
〔洗浄液Ｂが供されたシリコンウェハの評価方法〕
洗浄液Ｂが供されたシリコンウェハの評価方法として、以下の（１）〜（４）の評価を行った。[Method for evaluating silicon wafer provided with cleaning solution B]
As an evaluation method of the silicon wafer provided with the cleaning liquid B, the following (1) to (4) were evaluated.
（１）洗浄液Ｂにより撥水化された表面状態の接触角評価
撥水化されたウェハ表面上に純水約２μｌを置き、水滴とウェハ表面とのなす角（接触角）を接触角計（協和界面科学製：ＣＡ−Ｘ型）で測定した。ここでは撥水化された表面状態の接触角が５０〜１２０°の範囲であったものを合格（表中で○と表記）とした。(1) Evaluation of contact angle of surface state made water-repellent by cleaning liquid B About 2 μl of pure water is placed on the water-repellent wafer surface, and the angle (contact angle) formed between the water droplet and the wafer surface is measured with a contact angle meter ( Kyowa Interface Science Co., Ltd .: CA-X type). Here, the contact angle of the water-repellent surface state in the range of 50 to 120 ° was regarded as acceptable (denoted as “◯” in the table).
（２）毛細管力の評価
下式を用いてＰを算出し、毛細管力（Ｐの絶対値）を求めた。(2) Evaluation of capillary force P was calculated using the following equation, and the capillary force (absolute value of P) was determined.
Ｐ＝２×γ×ｃｏｓθ／Ｓ
ここで、γは表面張力、θは接触角、Ｓはパターン寸法を示す。なお、線幅：４５ｎｍ、アスペクト比：６のパターンでは、ウェハが気液界面を通過するときの洗浄液が水の場合はパターンが倒れやすく、２−プロパノールの場合はパターンが倒れ難い傾向がある。パターン寸法：４５（ｎｍ）、ウェハ表面：酸化ケイ素の場合、洗浄液が、２−プロパノール（表面張力：２２ｍＮ／ｍ、酸化ケイ素との接触角：１°）では毛細管力は０．９８ＭＮ／ｍ2となる。一方、水銀を除く液体の中で表面張力が最も大きい水（表面張力：７２ｍＮ／ｍ、酸化ケイ素との接触角：２．５°）では毛細管力は３．２ＭＮ／ｍ2となる。そこで、中間の２．１ＭＮ／ｍ2を目標とし、水が保持されたときの毛細管力が２．１ＭＮ／ｍ2以下になれば合格（表中で○と表記）とした。P = 2 × γ × cos θ / S
Here, γ is the surface tension, θ is the contact angle, and S is the pattern dimension. In the pattern with a line width of 45 nm and an aspect ratio of 6, the pattern tends to collapse when the cleaning liquid is water when the wafer passes through the gas-liquid interface, and the pattern does not easily collapse when 2-propanol. When the pattern size is 45 (nm) and the wafer surface is silicon oxide, the capillary force is 0.98 MN / m 2 when the cleaning liquid is 2-propanol (surface tension: 22 mN / m, contact angle with silicon oxide: 1 °). It becomes. On the other hand, the capillary force is 3.2 MN / m 2 in water (surface tension: 72 mN / m, contact angle with silicon oxide: 2.5 °) having the largest surface tension among liquids excluding mercury. Therefore, the intermediate 2.1MN / m 2 as the target, the capillary force when the water was retained was evaluated as acceptable if the following 2.1MN / m 2 (expressed as ○ in Table).
（３）洗浄液Ｂにより撥水化された表面状態の除去性
以下の条件でメタルハライドランプのＵＶ光をサンプルに２時間照射した。照射後に水滴の接触角が３０°以下となったものを合格（表中で○と表記）とした。(3) Removability of the surface state rendered water repellent by the cleaning liquid B The sample was irradiated with UV light from a metal halide lamp for 2 hours under the following conditions. A sample having a water droplet contact angle of 30 ° or less after irradiation was regarded as acceptable (denoted as “◯” in the table).
・ランプ：アイグラフィックス製Ｍ０１５−Ｌ３１２（強度：１．５ｋＷ）
・照度：下記条件における測定値が１２８ｍＷ／ｃｍ2
・測定装置：紫外線強度計（ミノルタ製、ＵＭ−１０）
・受光部：ＵＭ−３６０
（受光波長：３１０〜４００ｎｍ、ピーク波長：３６５±５ｎｍ）
・測定モード：放射照度測定-Lamp: M0155-L312 (strength: 1.5 kW) manufactured by Eye Graphics
Illuminance: The measured value under the following conditions is 128 mW / cm 2
Measuring device: UV intensity meter (Minolta, UM-10)
-Light receiving part: UM-360
(Receiving wavelength: 310 to 400 nm, peak wavelength: 365 ± 5 nm)
・ Measurement mode: Irradiance measurement
（４）撥水化された表面状態の除去後のシリコンウェハの表面平滑性評価
原子間力顕微鏡（セイコ−電子製：ＳＰＩ３７００、２．５μｍ四方スキャン）によって表面観察し、中心線平均面粗さ：Ｒａ（ｎｍ）を求めた。なお、Ｒａは、ＪＩＳ Ｂ ０６０１で定義されている中心線平均粗さを測定面に対し適用して三次元に拡張したものであり、「基準面から指定面までの偏差の絶対値を平均した値」として次式で算出した。撥水化された表面状態を除去した後のウェハのＲａ値が１ｎｍ以下であれば、洗浄によってウェハ表面が侵食されていない、および、洗浄液Ｂの残渣がウェハ表面にないとし、合格（表中で○と表記）とした。(4) Evaluation of surface smoothness of silicon wafer after removal of water-repellent surface state Surface observation with an atomic force microscope (Seiko-Electronics: SPI3700, 2.5 μm square scan), centerline average surface roughness : Ra (nm) was determined. Ra is a three-dimensional extension of the centerline average roughness defined in JIS B 0601 to the measurement surface. “The absolute value of the deviation from the reference surface to the specified surface is averaged. The value was calculated by the following formula. If the Ra value of the wafer after removing the water-repellent surface state is 1 nm or less, the wafer surface is not eroded by cleaning, and the residue of the cleaning liquid B is not present on the wafer surface. And written as ○).
実施例１
（１）洗浄液Ｂの調製
先ず、撥水性化合物としてヘキシルトリメトキシシラン〔Ｃ6Ｈ13Ｓｉ(ＯＣＨ3)3〕；１．０ｇ、アルコール溶媒として２−プロパノール；９６．６ｇを混合し、約５分間撹拌した。次いで、０．１Ｎ硝酸水溶液（ｐＨ１．０）；２．４ｇを添加し、約２４時間室温で撹拌した。以上の方法により、洗浄液Ｂの総量に対する撥水性化合物の濃度（以降「撥水性化合物濃度」と記載する）が１．０質量％の洗浄液Ｂを得た。Example 1
(1) Preparation of Cleaning Solution B First, hexyltrimethoxysilane [C 6 H 13 Si (OCH 3 ) 3 ] as a water repellent compound; 1.0 g, 2-propanol as an alcohol solvent; 96.6 g were mixed, and about 5 Stir for minutes. Next, 0.1 g of nitric acid aqueous solution (pH 1.0); 2.4 g was added, and the mixture was stirred at room temperature for about 24 hours. By the above method, a cleaning liquid B having a water repellent compound concentration (hereinafter referred to as “water repellent compound concentration”) of 1.0 mass% with respect to the total amount of the cleaning liquid B was obtained.
（２）シリコンウェハの洗浄
平滑な熱酸化膜付きシリコンウェハ（表面に厚さ１μｍの熱酸化膜層を有するＳｉウェハ）を１質量％のフッ酸水溶液に２ｍｉｎ浸漬し、次いで純水に１ｍｉｎ浸漬した。(2) Cleaning of silicon wafer A silicon wafer with a smooth thermal oxide film (Si wafer having a 1 μm thick thermal oxide film layer on the surface) is immersed in a 1% by mass hydrofluoric acid aqueous solution for 2 minutes, and then immersed in pure water for 1 minute. did.
（３）シリコンウェハ表面への洗浄液Ｂによる表面処理
上記「（１）洗浄液Ｂの調製」で調製した洗浄液Ｂを６０℃に加温し、この洗浄液にシリコンウェハを４８時間浸漬させた。その後、シリコンウェハを純水に１ｍｉｎ浸漬した。最後に、シリコンウェハを純水から取出し、エアーを吹き付けて、表面の水分を除去した。(3) Surface treatment of silicon wafer surface with cleaning liquid B Cleaning liquid B prepared in the above “(1) Preparation of cleaning liquid B” was heated to 60 ° C., and the silicon wafer was immersed in this cleaning liquid for 48 hours. Thereafter, the silicon wafer was immersed in pure water for 1 min. Finally, the silicon wafer was taken out from the pure water and air was blown to remove the moisture on the surface.
得られたウェハを上記「洗浄液Ｂが供されたシリコンウェハの評価方法」に記載した要領で評価したところ、表１に示すとおり、表面処理前の初期接触角が１０°未満であったものが、表面処理後の接触角は６６°となり、撥水性付与効果を示した。また、上記「毛細管力の評価」に記載した式を使って水が保持されたときの毛細管力を計算したところ、毛細管力は１．３ＭＮ／ｍ2であり、毛細管力は小さかった。また、ＵＶ照射後の接触角は１０°未満であり撥水化された表面状態は除去できた。さらに、ＵＶ照射後のウェハのＲａ値は０．５ｎｍ未満であり、洗浄時にウェハは侵食されず、さらにＵＶ照射後に洗浄液Ｂの残渣は残らないことが確認できた。When the obtained wafer was evaluated in the manner described in “Method for evaluating silicon wafer provided with cleaning liquid B”, as shown in Table 1, the initial contact angle before the surface treatment was less than 10 °. The contact angle after the surface treatment was 66 °, which showed the effect of imparting water repellency. Moreover, when the capillary force when water was held was calculated using the formula described in the above “Evaluation of Capillary Force”, the capillary force was 1.3 MN / m 2 and the capillary force was small. Moreover, the contact angle after UV irradiation was less than 10 °, and the water-repellent surface state could be removed. Furthermore, the Ra value of the wafer after UV irradiation was less than 0.5 nm, and it was confirmed that the wafer was not eroded during cleaning, and that no residue of the cleaning liquid B remained after UV irradiation.
実施例２
ヘキシルトリメトキシシランの濃度を３質量％とした以外はすべて実施例１と同じとした。評価結果は表１に示すとおり、表面処理後の接触角は７６°となり、撥水性付与効果を示した。また、水が保持されたときの毛細管力は０．８ＭＮ／ｍ2であり、毛細管力は小さかった。また、ＵＶ照射後の接触角は１０°未満であり撥水化された表面状態は除去できた。さらに、ＵＶ照射後のウェハのＲａ値は０．５ｎｍ未満であり、洗浄時にウェハは侵食されず、さらにＵＶ照射後に洗浄液Ｂの残渣は残らないことが確認できた。Example 2
All were the same as Example 1 except that the concentration of hexyltrimethoxysilane was 3% by mass. As shown in Table 1, the evaluation result showed that the contact angle after the surface treatment was 76 °, indicating the effect of imparting water repellency. Moreover, the capillary force when water was held was 0.8 MN / m 2 , and the capillary force was small. Moreover, the contact angle after UV irradiation was less than 10 °, and the water-repellent surface state could be removed. Furthermore, the Ra value of the wafer after UV irradiation was less than 0.5 nm, and it was confirmed that the wafer was not eroded during cleaning, and that no residue of the cleaning liquid B remained after UV irradiation.
実施例３
シリコンウェハを洗浄液Ｂに９６時間浸漬させた以外はすべて実施例２と同じとした。評価結果は表１に示すとおり、表面処理後の接触角は８８°となり、優れた撥水性付与効果を示した。また、水が保持されたときの毛細管力は０．１ＭＮ／ｍ2であり、毛細管力は小さかった。また、ＵＶ照射後の接触角は１０°未満であり撥水化された表面状態は除去できた。さらに、ＵＶ照射後のウェハのＲａ値は０．５ｎｍ未満であり、洗浄時にウェハは侵食されず、さらにＵＶ照射後に洗浄液Ｂの残渣は残らないことが確認できた。Example 3
All the steps were the same as Example 2 except that the silicon wafer was immersed in the cleaning solution B for 96 hours. As shown in Table 1, the evaluation result showed that the contact angle after the surface treatment was 88 °, indicating an excellent water repellency imparting effect. Moreover, the capillary force when water was held was 0.1 MN / m 2 , and the capillary force was small. Moreover, the contact angle after UV irradiation was less than 10 °, and the water-repellent surface state could be removed. Furthermore, the Ra value of the wafer after UV irradiation was less than 0.5 nm, and it was confirmed that the wafer was not eroded during cleaning, and that no residue of the cleaning liquid B remained after UV irradiation.
実施例４
撥水性化合物にデシルトリメトキシシラン〔Ｃ10Ｈ21Ｓｉ（ＯＣＨ3）3〕を用いた以外はすべて実施例１と同じとした。結果、物性は表１に示すとおり、表面処理後の接触角は７０°となり、撥水性付与効果を示した。また、水が保持されたときの毛細管力は１．１ＭＮ／ｍ2であり、毛細管力は小さかった。また、ＵＶ照射後の接触角は１０°未満であり撥水化された表面状態は除去できた。さらに、ＵＶ照射後のウェハのＲａ値は０．５ｎｍ未満であり、洗浄時にウェハは侵食されず、さらにＵＶ照射後に洗浄液Ｂの残渣は残らないことが確認できた。Example 4
The procedure was the same as Example 1 except that decyltrimethoxysilane [C 10 H 21 Si (OCH 3 ) 3 ] was used as the water repellent compound. As a result, the physical properties were as shown in Table 1, and the contact angle after the surface treatment was 70 °, which showed the effect of imparting water repellency. Moreover, the capillary force when water was held was 1.1 MN / m 2 , and the capillary force was small. Moreover, the contact angle after UV irradiation was less than 10 °, and the water-repellent surface state could be removed. Furthermore, the Ra value of the wafer after UV irradiation was less than 0.5 nm, and it was confirmed that the wafer was not eroded during cleaning, and that no residue of the cleaning liquid B remained after UV irradiation.
実施例５
撥水性化合物にオクタデシルトリメトキシシラン〔Ｃ18Ｈ37Ｓｉ（ＯＣＨ3）3〕を用いた以外はすべて実施例１と同じとした。評価結果は表１に示すとおり、表面処理後の接触角は７４°となり、撥水性付与効果を示した。また、水が保持されたときの毛細管力は０．９ＭＮ／ｍ2であり、毛細管力は小さかった。また、ＵＶ照射後の接触角は１０°未満であり撥水化された表面状態は除去できた。さらに、ＵＶ照射後のウェハのＲａ値は０．５ｎｍ未満であり、洗浄時にウェハは侵食されず、さらにＵＶ照射後に洗浄液Ｂの残渣は残らないことが確認できた。Example 5
All were the same as in Example 1 except that octadecyltrimethoxysilane [C 18 H 37 Si (OCH 3 ) 3 ] was used as the water repellent compound. As shown in Table 1, the evaluation result showed that the contact angle after the surface treatment was 74 °, indicating the effect of imparting water repellency. The capillary force when water was retained was 0.9 MN / m 2 , and the capillary force was small. Moreover, the contact angle after UV irradiation was less than 10 °, and the water-repellent surface state could be removed. Furthermore, the Ra value of the wafer after UV irradiation was less than 0.5 nm, and it was confirmed that the wafer was not eroded during cleaning, and that no residue of the cleaning liquid B remained after UV irradiation.
実施例６
撥水性化合物にオクタデシルトリメトキシシラン〔Ｃ18Ｈ37Ｓｉ（ＯＣＨ3）3〕を用い、且つ、酸性水溶液に１Ｎ酢酸水溶液（ｐＨ２．０）を用いた以外はすべて実施例１と同じとした。評価結果は表１に示すとおり、表面処理後の接触角は７０°となり、撥水性付与効果を示した。また、水が保持されたときの毛細管力は１．１ＭＮ／ｍ2であり、毛細管力は小さかった。また、ＵＶ照射後の接触角は１０°未満であり撥水化された表面状態は除去できた。さらに、ＵＶ照射後のウェハのＲａ値は０．５ｎｍ未満であり、洗浄時にウェハは侵食されず、さらにＵＶ照射後に洗浄液Ｂの残渣は残らないことが確認できた。Example 6
The same procedure as in Example 1 was conducted except that octadecyltrimethoxysilane [C 18 H 37 Si (OCH 3 ) 3 ] was used as the water repellent compound and 1N acetic acid aqueous solution (pH 2.0) was used as the acidic aqueous solution. As shown in Table 1, the evaluation results showed that the contact angle after the surface treatment was 70 °, indicating the effect of imparting water repellency. Moreover, the capillary force when water was held was 1.1 MN / m 2 , and the capillary force was small. Moreover, the contact angle after UV irradiation was less than 10 °, and the water-repellent surface state could be removed. Furthermore, the Ra value of the wafer after UV irradiation was less than 0.5 nm, and it was confirmed that the wafer was not eroded during cleaning, and that no residue of the cleaning liquid B remained after UV irradiation.
実施例７
撥水性化合物にトリフルオロプロピルトリメトキシシラン〔ＣＦ3ＣＨ2ＣＨ2Ｓｉ（ＯＣＨ3）3〕を用いた以外はすべて実施例１と同じとした。評価結果は表１に示すとおり、表面処理後の接触角は６８°となり、撥水性付与効果を示した。また、水が保持されたときの毛細管力は１．２ＭＮ／ｍ2であり、毛細管力は小さかった。また、ＵＶ照射後の接触角は１０°未満であり撥水化された表面状態は除去できた。さらに、ＵＶ照射後のウェハのＲａ値は０．５ｎｍ未満であり、洗浄時にウェハは侵食されず、さらにＵＶ照射後に洗浄液Ｂの残渣は残らないことが確認できた。Example 7
The same procedure as in Example 1 was conducted except that trifluoropropyltrimethoxysilane [CF 3 CH 2 CH 2 Si (OCH 3 ) 3 ] was used as the water repellent compound. As shown in Table 1, the evaluation result showed that the contact angle after the surface treatment was 68 °, indicating the effect of imparting water repellency. Moreover, the capillary force when water was held was 1.2 MN / m 2 , and the capillary force was small. Moreover, the contact angle after UV irradiation was less than 10 °, and the water-repellent surface state could be removed. Furthermore, the Ra value of the wafer after UV irradiation was less than 0.5 nm, and it was confirmed that the wafer was not eroded during cleaning, and that no residue of the cleaning liquid B remained after UV irradiation.
実施例８
撥水性化合物にトリデカフルオロオクチルトリメトキシシラン〔Ｃ6Ｆ13ＣＨ2ＣＨ2Ｓｉ（ＯＣＨ3）3〕を用いた以外はすべて実施例１と同じとした。評価結果は表１に示すとおり、表面処理後の接触角は７４°となり、撥水性付与効果を示した。また、水が保持されたときの毛細管力は０．９ＭＮ／ｍ2であり、毛細管力は小さかった。また、ＵＶ照射後の接触角は１０°未満であり撥水化された表面状態は除去できた。さらに、ＵＶ照射後のウェハのＲａ値は０．５ｎｍ未満であり、洗浄時にウェハは侵食されず、さらにＵＶ照射後に洗浄液Ｂの残渣は残らないことが確認できた。Example 8
The same procedure as in Example 1 was conducted except that tridecafluorooctyltrimethoxysilane [C 6 F 13 CH 2 CH 2 Si (OCH 3 ) 3 ] was used as the water repellent compound. As shown in Table 1, the evaluation result showed that the contact angle after the surface treatment was 74 °, indicating the effect of imparting water repellency. The capillary force when water was retained was 0.9 MN / m 2 , and the capillary force was small. Moreover, the contact angle after UV irradiation was less than 10 °, and the water-repellent surface state could be removed. Furthermore, the Ra value of the wafer after UV irradiation was less than 0.5 nm, and it was confirmed that the wafer was not eroded during cleaning, and that no residue of the cleaning liquid B remained after UV irradiation.
実施例９
撥水性化合物にヘキシルトリメトキシシラン〔Ｃ6Ｈ13Ｓｉ(ＯＣＨ3)3〕とトリデカフルオロオクチルトリメトキシシラン〔Ｃ6Ｆ13Ｃ2Ｈ4Ｓｉ（ＯＣＨ3）3〕を質量比で５０：５０とし、撥水性化合物濃度を３質量％とした以外はすべて実施例１と同じとした。評価結果は表１に示すとおり、表面処理後の接触角は７６°となり、撥水性付与効果を示した。また、水が保持されたときの毛細管力は０．８ＭＮ／ｍ2であり、毛細管力は小さかった。また、ＵＶ照射後の接触角は１０°未満であり撥水化された表面状態は除去できた。さらに、ＵＶ照射後のウェハのＲａ値は０．５ｎｍ未満であり、洗浄時にウェハは侵食されず、さらにＵＶ照射後に洗浄液Ｂの残渣は残らないことが確認できた。Example 9
Hexyltrimethoxysilane [C 6 H 13 Si (OCH 3 ) 3 ] and tridecafluorooctyltrimethoxysilane [C 6 F 13 C 2 H 4 Si (OCH 3 ) 3 ] in a weight ratio of 50: The same as Example 1 except that the water-repellent compound concentration was 3 mass%. As shown in Table 1, the evaluation result showed that the contact angle after the surface treatment was 76 °, indicating the effect of imparting water repellency. Moreover, the capillary force when water was held was 0.8 MN / m 2 , and the capillary force was small. Moreover, the contact angle after UV irradiation was less than 10 °, and the water-repellent surface state could be removed. Furthermore, the Ra value of the wafer after UV irradiation was less than 0.5 nm, and it was confirmed that the wafer was not eroded during cleaning, and that no residue of the cleaning liquid B remained after UV irradiation.
実施例１０
上記「（３）シリコンウェハ表面への洗浄液Ｂによる表面処理」でシリコンウェハを洗浄液Ｂに浸漬した後、シリコンウェハを２−プロパノールに１ｍｉｎ浸漬し、次いで、純水に１ｍｉｎ浸漬し、最後にシリコンウェハを純水から取出し、エアーを吹き付けて、表面の水分を除去して表面処理したウェハを得た以外はすべて実施例１と同じとした。評価結果は表１に示すとおり、表面処理後の接触角は６６°となり、撥水性付与効果を示した。また、水が保持されたときの毛細管力は１．３ＭＮ／ｍ2であり、毛細管力は小さかった。また、ＵＶ照射後の接触角は１０°未満であり撥水化された表面状態は除去できた。さらに、ＵＶ照射後のウェハのＲａ値は０．５ｎｍ未満であり、洗浄時にウェハは侵食されず、さらにＵＶ照射後に洗浄液Ｂの残渣は残らないことが確認できた。Example 10
After immersing the silicon wafer in cleaning liquid B in the above “(3) Surface treatment of silicon wafer surface with cleaning liquid B”, the silicon wafer is immersed in 2-propanol for 1 min, then immersed in pure water for 1 min, and finally silicon. The same procedure as in Example 1 was performed except that the wafer was taken out of pure water and air was blown to remove the surface moisture to obtain a surface-treated wafer. As shown in Table 1, the evaluation result showed that the contact angle after the surface treatment was 66 °, indicating the effect of imparting water repellency. Further, the capillary force when water was held was 1.3 MN / m 2 , and the capillary force was small. Moreover, the contact angle after UV irradiation was less than 10 °, and the water-repellent surface state could be removed. Furthermore, the Ra value of the wafer after UV irradiation was less than 0.5 nm, and it was confirmed that the wafer was not eroded during cleaning, and that no residue of the cleaning liquid B remained after UV irradiation.
実施例１１
上記「（３）シリコンウェハ表面への洗浄液Ｂによる表面処理」でシリコンウェハを洗浄液Ｂに浸漬した後、シリコンウェハを２−プロパノールに１ｍｉｎ浸漬し、最後にシリコンウェハを２−プロパノールから取出し、エアーを吹き付けて、表面の２−プロパノールを除去して表面処理したウェハを得た以外はすべて実施例１と同じとした。評価結果は表１に示すとおり、表面処理後の接触角は６６°となり、撥水性付与効果を示した。また、水が保持されたときの毛細管力は１．３ＭＮ／ｍ2であり、毛細管力は小さかった。また、ＵＶ照射後の接触角は１０°未満であり撥水化された表面状態は除去できた。さらに、ＵＶ照射後のウェハのＲａ値は０．５ｎｍ未満であり、洗浄時にウェハは侵食されず、さらにＵＶ照射後に洗浄液Ｂの残渣は残らないことが確認できた。Example 11
After immersing the silicon wafer in cleaning liquid B in “(3) Surface treatment with cleaning liquid B on the surface of silicon wafer” above, the silicon wafer is immersed in 2-propanol for 1 min, and finally the silicon wafer is taken out of 2-propanol and air. The same process as in Example 1 was performed except that 2-propanol on the surface was removed to obtain a surface-treated wafer. As shown in Table 1, the evaluation result showed that the contact angle after the surface treatment was 66 °, indicating the effect of imparting water repellency. Further, the capillary force when water was held was 1.3 MN / m 2 , and the capillary force was small. Moreover, the contact angle after UV irradiation was less than 10 °, and the water-repellent surface state could be removed. Furthermore, the Ra value of the wafer after UV irradiation was less than 0.5 nm, and it was confirmed that the wafer was not eroded during cleaning, and that no residue of the cleaning liquid B remained after UV irradiation.
実施例１２
上記「（３）シリコンウェハ表面への洗浄液Ｂによる表面処理」でシリコンウェハを洗浄液Ｂから取出した後、エアーを吹き付けて、表面の洗浄液Ｂを除去した。次に、シリコンウェハを２−プロパノールに１ｍｉｎ浸漬し、次いで、純水に１ｍｉｎ浸漬し、最後にシリコンウェハを純水から取出し、エアーを吹き付けて、表面の水分を除去して表面処理したウェハを得た以外はすべて実施例１と同じとした。評価結果は表１に示すとおり、表面処理後の接触角は６８°となり、撥水性付与効果を示した。また、水が保持されたときの毛細管力は１．２ＭＮ／ｍ2であり、毛細管力は小さかった。また、ＵＶ照射後の接触角は１０°未満であり撥水化された表面状態は除去できた。さらに、ＵＶ照射後のウェハのＲａ値は０．５ｎｍ未満であり、洗浄時にウェハは侵食されず、さらにＵＶ照射後に洗浄液Ｂの残渣は残らないことが確認できた。Example 12
After the silicon wafer was taken out from the cleaning liquid B in the above “(3) Surface treatment with the cleaning liquid B on the surface of the silicon wafer”, the surface cleaning liquid B was removed by blowing air. Next, the silicon wafer is dipped in 2-propanol for 1 min, then dipped in pure water for 1 min, and finally the silicon wafer is taken out from the pure water and blown with air to remove the surface moisture and surface-treat the wafer. All were the same as Example 1 except that they were obtained. As shown in Table 1, the evaluation result showed that the contact angle after the surface treatment was 68 °, indicating the effect of imparting water repellency. Moreover, the capillary force when water was held was 1.2 MN / m 2 , and the capillary force was small. Moreover, the contact angle after UV irradiation was less than 10 °, and the water-repellent surface state could be removed. Furthermore, the Ra value of the wafer after UV irradiation was less than 0.5 nm, and it was confirmed that the wafer was not eroded during cleaning, and that no residue of the cleaning liquid B remained after UV irradiation.
実施例１３
上記「（３）シリコンウェハ表面への洗浄液Ｂによる表面処理」でシリコンウェハを洗浄液Ｂから取出した後、エアーを吹き付けて、表面の洗浄液Ｂを除去した。次に、シリコンウェハを２−プロパノールに１ｍｉｎ浸漬し、最後にシリコンウェハを２−プロパノールから取出し、エアーを吹き付けて、表面の２−プロパノールを除去して表面処理したウェハを得た以外はすべて実施例１と同じとした。評価結果は表１に示すとおり、表面処理後の接触角は６８°となり、撥水性付与効果を示した。また、水が保持されたときの毛細管力は１．２ＭＮ／ｍ2であり、毛細管力は小さかった。また、ＵＶ照射後の接触角は１０°未満であり撥水化された表面状態は除去できた。さらに、ＵＶ照射後のウェハのＲａ値は０．５ｎｍ未満であり、洗浄時にウェハは侵食されず、さらにＵＶ照射後に洗浄液Ｂの残渣は残らないことが確認できた。Example 13
After the silicon wafer was taken out from the cleaning liquid B in the above “(3) Surface treatment with the cleaning liquid B on the surface of the silicon wafer”, the surface cleaning liquid B was removed by blowing air. Next, the silicon wafer was immersed in 2-propanol for 1 min. Finally, the silicon wafer was taken out of 2-propanol, and air was blown to remove the surface 2-propanol and obtain a surface-treated wafer. Same as Example 1. As shown in Table 1, the evaluation result showed that the contact angle after the surface treatment was 68 °, indicating the effect of imparting water repellency. Moreover, the capillary force when water was held was 1.2 MN / m 2 , and the capillary force was small. Moreover, the contact angle after UV irradiation was less than 10 °, and the water-repellent surface state could be removed. Furthermore, the Ra value of the wafer after UV irradiation was less than 0.5 nm, and it was confirmed that the wafer was not eroded during cleaning, and that no residue of the cleaning liquid B remained after UV irradiation.
実施例１４
上記「（３）シリコンウェハ表面への洗浄液Ｂによる表面処理」でシリコンウェハを洗浄液Ｂから取出した後、エアーを吹き付けて、表面の洗浄液Ｂを除去した。次に、シリコンウェハを純水に１ｍｉｎ浸漬し、最後にシリコンウェハを純水から取出し、エアーを吹き付けて、表面の水分を除去して表面処理したウェハを得た以外はすべて実施例１と同じとした。評価結果は表１に示すとおり、表面処理後の接触角は６８°となり、撥水性付与効果を示した。また、水が保持されたときの毛細管力は１．２ＭＮ／ｍ2であり、毛細管力は小さかった。また、ＵＶ照射後の接触角は１０°未満であり撥水化された表面状態は除去できた。さらに、ＵＶ照射後のウェハのＲａ値は０．５ｎｍ未満であり、洗浄時にウェハは侵食されず、さらにＵＶ照射後に洗浄液Ｂの残渣は残らないことが確認できた。Example 14
After the silicon wafer was taken out from the cleaning liquid B in the above “(3) Surface treatment with the cleaning liquid B on the surface of the silicon wafer”, the surface cleaning liquid B was removed by blowing air. Next, the silicon wafer was immersed in pure water for 1 min, and finally the silicon wafer was taken out from the pure water and air was blown to remove the surface moisture to obtain a surface-treated wafer. It was. As shown in Table 1, the evaluation result showed that the contact angle after the surface treatment was 68 °, indicating the effect of imparting water repellency. Moreover, the capillary force when water was held was 1.2 MN / m 2 , and the capillary force was small. Moreover, the contact angle after UV irradiation was less than 10 °, and the water-repellent surface state could be removed. Furthermore, the Ra value of the wafer after UV irradiation was less than 0.5 nm, and it was confirmed that the wafer was not eroded during cleaning, and that no residue of the cleaning liquid B remained after UV irradiation.
実施例１５
上記「（３）シリコンウェハ表面への洗浄液Ｂによる表面処理」でシリコンウェハを洗浄液Ｂから取出した後、エアーを吹き付けて、表面の洗浄液Ｂを除去して表面処理したウェハを得た以外はすべて実施例１と同じとした。評価結果は表１に示すとおり、表面処理後の接触角は６８°となり、撥水性付与効果を示した。また、水が保持されたときの毛細管力は１．２ＭＮ／ｍ2であり、毛細管力は小さかった。また、ＵＶ照射後の接触角は１０°未満であり撥水化された表面状態は除去できた。さらに、ＵＶ照射後のウェハのＲａ値は０．５ｎｍ未満であり、洗浄時にウェハは侵食されず、さらにＵＶ照射後に洗浄液Ｂの残渣は残らないことが確認できた。Example 15
All except that after the silicon wafer was taken out of the cleaning liquid B in “(3) Surface treatment of the silicon wafer surface with the cleaning liquid B”, air was blown to remove the surface cleaning liquid B to obtain a surface-treated wafer. Same as Example 1. As shown in Table 1, the evaluation result showed that the contact angle after the surface treatment was 68 °, indicating the effect of imparting water repellency. Moreover, the capillary force when water was held was 1.2 MN / m 2 , and the capillary force was small. Moreover, the contact angle after UV irradiation was less than 10 °, and the water-repellent surface state could be removed. Furthermore, the Ra value of the wafer after UV irradiation was less than 0.5 nm, and it was confirmed that the wafer was not eroded during cleaning, and that no residue of the cleaning liquid B remained after UV irradiation.
比較例１
シリコンウェハに洗浄液Ｂを供さなかった以外は、実施例１と同じとした。すなわち、本比較例では、撥水化された表面状態ではないシリコンウェハを評価した。評価結果は表１に示すとおり、ウェハの接触角は３°と低かった。また、水が保持されたときの毛細管力は３．２ＭＮ／ｍ2であり、毛細管力は大きかった。Comparative Example 1
Example 1 was the same as Example 1 except that the cleaning liquid B was not applied to the silicon wafer. That is, in this comparative example, a silicon wafer that was not in a water-repellent surface state was evaluated. As shown in Table 1, the evaluation results showed that the contact angle of the wafer was as low as 3 °. Moreover, the capillary force when water was held was 3.2 MN / m 2 , and the capillary force was large.
１ シリコンウェハ
２ シリコンウェハ表面の微細な凹凸パターン
３ パターンの凸部
４ パターンの凹部
５ 凹部の幅
６ 凸部の高さ
７ 凸部の幅
８ 凹部４に保持された洗浄液
９ 凹部４に保持された水系洗浄液
１０ 撥水性化合物により撥水化された表面状態DESCRIPTION OF
Claims (4)
前記洗浄液Ａは水系溶液からなり、
洗浄液Ｂは凹凸パターンの凹部を撥水化するものであり、
前記洗浄液ＢはシリコンウェハのＳｉと化学的に結合可能なユニットを生じせしめる加水分解性部位、疎水性基を含む撥水性化合物とアルコール溶媒を含むアルコール溶液、および、水または酸性水溶液が混合されてなるものであり、該撥水性化合物は、洗浄液Ｂの総量１００質量％中に０．２〜２０質量％となるように混合されてなる撥水性洗浄液とすることで、洗浄液Ｂにより撥水化されたシリコンウェハ表面の凹部に水が保持されたと仮定したときの毛細管力を２．１ＭＮ／ｍ2以下とせしめるものであることを特徴とするシリコンウェハの洗浄剤。It is a cleaning agent for silicon wafer having a fine uneven pattern on the surface, and the cleaning agent includes cleaning liquid A and cleaning liquid B,
The cleaning liquid A is an aqueous solution,
The cleaning liquid B is for repelling the concave portions of the concave / convex pattern,
The cleaning liquid B is a mixture of a hydrolyzable portion that generates a unit capable of chemically bonding to Si of a silicon wafer, an alcohol solution containing a hydrophobic group-containing water-repellent compound and an alcohol solvent, and water or an acidic aqueous solution. The water-repellent compound is made water-repellent by the cleaning liquid B by using a water-repellent cleaning liquid that is mixed in an amount of 0.2 to 20% by mass in 100% by mass of the total amount of the cleaning liquid B. A silicon wafer cleaning agent characterized by having a capillary force of 2.1 MN / m 2 or less assuming that water is retained in the recesses on the surface of the silicon wafer.
ＣmＨ2m+1ＳｉＲsＸ3-s （ｍ＝１〜１８）と
ＣnＦ2n+1ＣＨ2ＣＨ2ＳｉＲtＹ3-t （ｎ＝１〜８）と
からなる群から選ばれる少なくとも一つからなることを特徴とする請求項１に記載のシリコンウェハ用洗浄剤。
ここで、前記式中のｓとｔは、０〜２の整数であり、Ｒは、水素原子、または、１価の炭化水素基であり、ＸおよびＹは加水分解性部位である。In the cleaning liquid B, a water-repellent compound containing a hydrolyzable site and a hydrophobic group that gives rise to a unit capable of chemically bonding to Si of the silicon wafer,
C m H 2m + 1 SiR s X 3-s (m = 1-18) and C n F 2n + 1 CH 2 CH 2 SiR t Y 3-t (n = 1-8) It consists of at least one, The cleaning agent for silicon wafers of Claim 1 characterized by the above-mentioned.
Here, s and t in the above formula are integers of 0 to 2, R is a hydrogen atom or a monovalent hydrocarbon group, and X and Y are hydrolyzable sites.
洗浄液をシリコンウェハ表面から取り除いた後にシリコンウェハ表面を光照射又はシリコンウェハを加熱する工程
を有することを特徴とするシリコンウェハ表面の洗浄方法。A method for cleaning a silicon wafer surface using the cleaning agent according to claim 1, wherein the method comprises:
A method for cleaning a surface of a silicon wafer, comprising the step of irradiating the surface of the silicon wafer with light or heating the silicon wafer after removing the cleaning liquid from the surface of the silicon wafer.