JPS6389574A - Extensible paint composition - Google Patents
Extensible paint compositionInfo
- Publication number
- JPS6389574A JPS6389574A JP23128686A JP23128686A JPS6389574A JP S6389574 A JPS6389574 A JP S6389574A JP 23128686 A JP23128686 A JP 23128686A JP 23128686 A JP23128686 A JP 23128686A JP S6389574 A JPS6389574 A JP S6389574A
- Authority
- JP
- Japan
- Prior art keywords
- diisocyanate
- polyisocyanate
- butanediol
- coating film
- coating composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
(産業上の利用分野)
本発明は、伸長性を有する2液型ポリウレタン塗料組成
物に関する。さらに詳しくは、建築外装材、ルーフイン
ク材、プラスチック等に使用される伸長性を有し耐候性
に優れた塗料組成物に関する。DETAILED DESCRIPTION OF THE INVENTION (Field of Industrial Application) The present invention relates to a two-component polyurethane coating composition having extensibility. More specifically, the present invention relates to a coating composition that has extensibility and excellent weather resistance and is used for architectural exterior materials, roof ink materials, plastics, and the like.
(従来の技術)
近年、建築外装に用いられる翅料に代表されるように、
伸長性と耐候性に優れた塗料の要求が高まって込る。こ
れらの*Xに対し、耐候性の後れた塗料に可塑剤を添加
したシ、アクリルやポリエステル系の樹脂(ポリオール
〕のガラス転移温度を下げ、無黄変ポリイソシアネート
で硬化したポリウレタン堕料が知られている。(Prior art) In recent years, as exemplified by wing materials used for architectural exteriors,
There is an increasing demand for paints with excellent elongation and weather resistance. In response to these * Are known.
しかしながら、伸長性と耐候性の両特性を同時に満足す
る塗料組成物を得ることは、極めて困難なことである。However, it is extremely difficult to obtain a coating composition that simultaneously satisfies both extensibility and weather resistance properties.
すなわち、011述の芋法で伸長性金高めると耐候性が
低下してゆく頑同に69、耐候性と伸長性は二律背反の
関係にあった。また、特願昭55−108189号や同
56−133269号にあるようなフッ素を含有するポ
リオールを主剤とし、多価イソシアネートで硬化させた
ボリウレメン塗料は、耐候性が非常に優れることは知ら
れているが、イノシアネートや可塑剤との相溶性が不十
分で、使用できるイソシアネートや′51塑剤に限界が
6フ、伸長性の高い塗膜は得られていない。In other words, when the extensibility of gold was increased using the potato method described in 011, the weather resistance was stubbornly reduced69, and there was an antinomic relationship between weather resistance and extensibility. In addition, it is known that polyurethane paints, which are made of fluorine-containing polyol as a main ingredient and cured with polyvalent isocyanate, as described in Japanese Patent Application No. 55-108189 and No. 56-133269, have excellent weather resistance. However, the compatibility with inocyanates and plasticizers is insufficient, and the usable isocyanates and '51 plasticizers are limited to 6 degrees, making it impossible to obtain coatings with high extensibility.
(本発明が解決しようとする問題点)
本発明の目的は、耐候性に優れるフッ素を含有するポリ
オールを用い、相容性が良好で、かつ伸長性を有する塗
料用組成物を得ることである。(Problems to be Solved by the Present Invention) An object of the present invention is to obtain a coating composition that uses a fluorine-containing polyol that has excellent weather resistance, has good compatibility, and has extensibility. .
(問題点を解決するための手段〕
本発明者らは、上記のii rtfJ題点を解決する/
こめ鋭意検討を重ねた結果、脂肪族ジイソシアネートま
たは脂環族ジイソシアネートを特定のジオールと反1i
Sせしめて得られる末端にイソシアネート基勿有するポ
リイソシアネートと含フツ素ポリオールと組み合わせる
ことによシ、十分な相溶性が得られ、塗膜駄伸長性を有
し、かつ、耐候性に優れる組成物が得られ、上記問題を
解決できることを見出し、本発明を完成するに到った。(Means for solving the problem) The present inventors solve the above ii rtfJ problem/
As a result of extensive research, we have found that aliphatic diisocyanates or alicyclic diisocyanates can be used in combination with specific diols.
By combining a polyisocyanate having an isocyanate group at the end obtained by adding S and a fluorine-containing polyol, a composition can be obtained that has sufficient compatibility, has coating film extensibility, and has excellent weather resistance. The present inventors have found that the above problem can be solved, and have completed the present invention.
すなわち、本発明は、脂肪族ジイソシアネートまたは脂
環族ジイソシアネートの単独もしくは混合物と、分岐を
有する炭素数5〜10のアルキレンジオールとの反16
生成物である末端にイソシアネート基を有するポリイソ
シアネートと、水酸基を2個以上Mする含フツ素ポリオ
ールとを、NCO/OH当量比0.5〜2.0の範囲で
混合してなることを特徴とする塗料用組成物に関し、フ
ッ素含有ポリオールとポリイソシアネートの相溶性が良
好で、かつ、得られる塗膜は伸長性と獣た耐候性を有し
ている。That is, the present invention provides an anti-16 combination of an aliphatic diisocyanate or an alicyclic diisocyanate alone or a mixture thereof and a branched alkylene diol having 5 to 10 carbon atoms.
It is characterized by mixing the product polyisocyanate having an isocyanate group at the end with a fluorine-containing polyol having two or more hydroxyl groups at an NCO/OH equivalent ratio in the range of 0.5 to 2.0. Regarding the coating composition, the compatibility between the fluorine-containing polyol and the polyisocyanate is good, and the resulting coating film has extensibility and excellent weather resistance.
本発明における脂肪族ジイソシアネートまたは脂環族ジ
イソシアネートとしては、例えば、テトラメチレンジイ
ソシアネート、ペンタメチレンジイソシアネート、ヘキ
サメチレンジイソシアネート、トリメチルへキサメチレ
ンジイソシアネート、リジンジイソシアネート、インホ
ロンジイソシアネート、水添キシリレンジイソシアネー
ト、114−ジイソシアネートシクロヘキサン等を挙げ
ることができるが、特に好ましいのはへキサメチレンジ
イソシアネートである。これらのジイソシアネート化合
物は、単独もしくは適宜組み合わせて用いることができ
る。Examples of the aliphatic diisocyanate or alicyclic diisocyanate in the present invention include tetramethylene diisocyanate, pentamethylene diisocyanate, hexamethylene diisocyanate, trimethylhexamethylene diisocyanate, lysine diisocyanate, inphorone diisocyanate, hydrogenated xylylene diisocyanate, and 114-diisocyanate. Examples include cyclohexane, but particularly preferred is hexamethylene diisocyanate. These diisocyanate compounds can be used alone or in appropriate combinations.
本発明に用いられる分岐を有する炭素数3〜1゜のフル
キレンジオールは、その骨格は飽和炭化水素であるか、
鎖中にエーテル結合、エステル結合等を含んでいてもよ
い。これらのジオールの例としては、例えば、1.2−
プロパンジオール、1.2−ブタンジオール、1.3−
ブタンジオール、2.3− ブタンジオール、2−メチ
ル−1,2−ニア’ロバンジオール、1.2−ベンタン
ジオール、2.3−ベンタンジオール、3−メチル−1
,2−ブタンジオール、2−メチル−1,2−ブタンジ
オール、2−メチル−2,3−ブタンジオール、2.5
−ジメチル−2゜3−ブタンジオール、2.4−ベンタ
ンジオール、2−メチル−2,4−ブタンジオール、2
,4−ジメチル−2,4−ベンタンジオール、ヘキサメ
チルトリメチレンクリコール、ネオペンチルグリコール
、2.2−ジメチル−1,3−ブタンジオール、2.2
−ジメチル−1,3−ベンタンジオール、2,2.4−
トリメチル−1,3−ベンタンジオール、1,4−ペン
タンジオール、2−メチル−2,5−ベンタンジオール
、3−メチル−2,5−ベンタンジオール、1.4−ヘ
キサンジオール、2.5−ジメチル−2゜5−ヘキサン
ジオール、ジプロピレングリコール、3−メトキシ−1
,2−プロパンジオール、3−ブトキシ−1,2−プロ
パンジオール、2−エチル−1,3−ヘキサンジオール
等が挙げられる。The branched fulkylene diol having 3 to 1 degrees of carbon atoms used in the present invention has a saturated hydrocarbon skeleton, or
The chain may contain an ether bond, an ester bond, etc. Examples of these diols include, for example, 1,2-
Propanediol, 1.2-butanediol, 1.3-
Butanediol, 2,3-butanediol, 2-methyl-1,2-nia'lovandiol, 1,2-bentanediol, 2,3-bentanediol, 3-methyl-1
, 2-butanediol, 2-methyl-1,2-butanediol, 2-methyl-2,3-butanediol, 2.5
-dimethyl-2゜3-butanediol, 2,4-bentanediol, 2-methyl-2,4-butanediol, 2
, 4-dimethyl-2,4-bentanediol, hexamethyltrimethylene glycol, neopentyl glycol, 2.2-dimethyl-1,3-butanediol, 2.2
-dimethyl-1,3-bentanediol, 2,2.4-
Trimethyl-1,3-bentanediol, 1,4-pentanediol, 2-methyl-2,5-bentanediol, 3-methyl-2,5-bentanediol, 1,4-hexanediol, 2.5-dimethyl -2゜5-hexanediol, dipropylene glycol, 3-methoxy-1
, 2-propanediol, 3-butoxy-1,2-propanediol, 2-ethyl-1,3-hexanediol, and the like.
これらは単独もしくは任意に混合して用いられる。これ
らジオールのうち特に好ましいのは、1゜3−ブタンジ
オール、2,3−ブタンジオール、ネオペンチルグリコ
ール、2−エチル−1,3−ヘキサンジオールである。These may be used alone or in any combination. Particularly preferred among these diols are 1°3-butanediol, 2,3-butanediol, neopentyl glycol, and 2-ethyl-1,3-hexanediol.
脂肪族ジイソシアネートまたは脂環族ジイソシアネート
と反応すべきアルキレンジオールは、上述の如く分岐を
有することが必要である。分岐のないジオール、例えば
、エチレングリコール、1゜5−プロパンジオール、1
.4−ブタンジオール、1.5−ベンタンジオール、1
.6−ヘキサンジオール、ジエチレングリコール等を用
いた場合は、反応生成物であるポリイソシアネートが固
体であつ7’(υ、有機溶剤に極めて難溶であったシ、
フッ素含有ポリオールとの相溶性が不十分であったシし
て、本発明の目的に反する。また、炭素数11以上のジ
オールを用いた場合も、得られたポリイソシアネートの
粘度が高すぎたシ、固体になったシ、フッ素ポリオール
との相溶性が不十分であったシして好ましくない。また
、一般のポリウレタン塗料で硬化剤として多用されてい
る、ビユレット構造やイソシアヌレート構造を有するポ
リイソシアネートは、含フツ素ポリオールと相溶性が劣
つ九シ、伸長性がなかったシして好ましくない。The alkylene diol to be reacted with the aliphatic diisocyanate or alicyclic diisocyanate needs to have a branch as described above. Unbranched diols, such as ethylene glycol, 1°5-propanediol, 1
.. 4-butanediol, 1,5-bentanediol, 1
.. When using 6-hexanediol, diethylene glycol, etc., the reaction product polyisocyanate is solid and 7'(υ, extremely poorly soluble in organic solvents).
The compatibility with the fluorine-containing polyol was insufficient, which is contrary to the purpose of the present invention. Furthermore, when a diol having 11 or more carbon atoms is used, it is not preferable because the viscosity of the obtained polyisocyanate is too high, the resulting polyisocyanate becomes solid, and the compatibility with the fluorine polyol is insufficient. . In addition, polyisocyanates having a billet structure or an isocyanurate structure, which are often used as curing agents in general polyurethane paints, are undesirable because they have poor compatibility with fluorine-containing polyols and lack extensibility. .
本発明で用いられる脂肪族ジイソシアネートまたは脂環
族ジイソシアネートと分岐を有するアルキレンジオール
とを反応させ、余剰のジイソシアネートを精製により除
去して得られる未満にイソシアネート基を有するポリイ
ソシアネートの製造は、一般に知られている方法でよく
、例えば、特願昭55−65406号記載の方法で行う
ことができる。The production of a polyisocyanate having fewer isocyanate groups, which is obtained by reacting the aliphatic diisocyanate or alicyclic diisocyanate used in the present invention with a branched alkylene diol and removing the excess diisocyanate by purification, is generally known. For example, the method described in Japanese Patent Application No. 55-65406 can be used.
本発明で用いられる水酸基を2個以上有する含フツ素ポ
リオールとは、フルオロオレフィンまたはフッ素含有ビ
ニル単量体と、水酸基含有ビニル単量体を必須成分とし
て、これらと共重合可能なビニル単量体とを共重合させ
て得られる有機溶剤に可溶なポリオールで、例えば、特
願昭55−108189号、同56−133269号に
よシ得られるものである。市販のものとしては、旭硝子
株式会社のルミ7F:1ンLF−100、I、F−20
0、LP−300,LF−60i等がある。The fluorine-containing polyol having two or more hydroxyl groups used in the present invention is a vinyl monomer copolymerizable with a fluoroolefin or a fluorine-containing vinyl monomer and a hydroxyl group-containing vinyl monomer as essential components. It is a polyol soluble in an organic solvent obtained by copolymerizing with and, for example, according to Japanese Patent Application No. 55-108189 and No. 56-133269. Commercially available products include Lumi 7F:1 LF-100, I, and F-20 from Asahi Glass Co., Ltd.
0, LP-300, LF-60i, etc.
末端にイソシアネート基を有するポリイソシアネートと
含フツ素ポリオールとの混合は、NCO/OH当量比で
0.5〜2.0が好ましい。この比が0.5未満では、
耐候性、耐溶剤性等に劣シ、ま九、2.0を超えると、
乾燥性が遅くなったシして好ましくない。The mixture of the polyisocyanate having an isocyanate group at the terminal and the fluorine-containing polyol preferably has an NCO/OH equivalent ratio of 0.5 to 2.0. If this ratio is less than 0.5,
Weather resistance, solvent resistance, etc. are poor, and if it exceeds 2.0,
It is not preferable because the drying property becomes slow.
また、これらの混合物に対して、ポリウレタン塗料で一
般に使用される硬化促進触媒、紫外線吸収剤、酸化防止
剤、レベリング剤などの添加剤を加えることもできる。Furthermore, additives commonly used in polyurethane paints, such as curing accelerating catalysts, ultraviolet absorbers, antioxidants, and leveling agents, can also be added to these mixtures.
(発明の効果)
不発明の館林組成物は、相容性が良好で、建築外装材、
床、屋根防水、プラスチック等に施工すると、一体や下
地の亀裂にもよく追随し、値膜の破断がない優れた伸長
性を有する塗膜を形成し。(Effect of the invention) The uninvented Tatebayashi composition has good compatibility and is suitable for building exterior materials,
When applied to floors, roof waterproofing, plastics, etc., it forms a coating film that has excellent elongation properties and follows cracks in the base and the base, and does not cause rupture of the film.
また、耐候性に優れた塗膜を形成する。It also forms a coating film with excellent weather resistance.
(実施例)
以下、実施例によりさらに詳しく本発明を説明するが、
これらの実施例によって本発明が限定されるものではな
い0例中、部は重量部、係はM量チである。なお、伸長
性は実施例中の引鑵シ試験において、150%以上の破
断伸度を示したものを@、100s以上のものを○、5
0憾以上のものをΔ、so1以下のものを×として表わ
した。(Example) Hereinafter, the present invention will be explained in more detail with reference to Examples.
In these examples, the present invention is not limited to these examples, parts are parts by weight, and m is m. In addition, in the extensibility test in the examples, those that showed a breaking elongation of 150% or more are @, those that are 100 seconds or more are ○, and 5.
A value of 0 or more is expressed as Δ, and a value of so1 or less is expressed as ×.
製造例1
2520部と104部のネオペンチルグリコールを、1
260部のリン酸トリメチルを溶媒とし、120Cで1
時間反応させた。反応液を#膜蒸発器を用い、0.22
闘Ig、160Cの条件下で未反応のHMDIおよび溶
媒を除去した1缶底液として、25Cにおける粘度が1
300Cp、NGO含有量18.13 %のポリイソシ
アネートを得た。Production Example 1 2520 parts and 104 parts of neopentyl glycol were mixed into 1
1 at 120C using 260 parts of trimethyl phosphate as a solvent.
Allowed time to react. Using a # membrane evaporator, the reaction solution was reduced to 0.22
The viscosity at 25C is 1 as the bottom liquid from which unreacted HMDI and solvent are removed under the conditions of 160C.
A polyisocyanate of 300 Cp and an NGO content of 18.13% was obtained.
製造例2〜4
製造例1のジイソシアネート、ジオールを表1に示すも
のに変え、製造例1と同様の反応、精製を行った。得ら
れたポリイソシアネートの特性値を同じく表1に示す。Production Examples 2 to 4 The same reactions and purification as in Production Example 1 were carried out except that the diisocyanate and diol in Production Example 1 were changed to those shown in Table 1. The characteristic values of the obtained polyisocyanate are also shown in Table 1.
実施例1
製造例1で得られ九ポリイソシアネート10.5部を轟
量の酢酸エチルで希釈し、ルミフロンLF−100(旭
硝子株式会社製〕100部と混合し、テフロン板上に乾
燥膜厚が100μになるようノ・ケf1!1シを行った
。20C,65RH係下で7日間乾燥した後、塗膜を剥
離し、透明性を肉眼で観察た、同じ塗膜を幅1o+u、
長さ701H11に切り、チャック間圧i 50 MM
で50t1M1分の速度で引つ張シ試験をしたところ、
破断伸度105僑を示し、Qのランクを示す伸長性を有
する塗膜が得られた。Example 1 10.5 parts of the 9-polyisocyanate obtained in Production Example 1 was diluted with a large amount of ethyl acetate, mixed with 100 parts of Lumiflon LF-100 (manufactured by Asahi Glass Co., Ltd.), and a dry film thickness was formed on a Teflon plate. After drying under 20C and 65RH for 7 days, the coating film was peeled off and the transparency was observed with the naked eye.The same coating film was coated with a width of 1o+u.
Cut to length 701H11, chuck pressure i 50 MM
When I did a tension test at a speed of 50t1M1 minute,
A coating film having elongation properties showing a breaking elongation of 105 and a rank of Q was obtained.
同じ塗料配合物をスレート板に乾燥膜厚が50μ、にな
るようハケm#)を行い、20C65RH%下で7日間
乾燥した後、JIS A 6910で規定の条件で
促進耐候性試験を1000時間行ったが、光沢の低下、
変色、ひび割れ、剥がれなどの変化は認められなかった
。The same paint formulation was brushed onto a slate board so that the dry film thickness was 50μ, and after drying for 7 days under 20C65RH%, an accelerated weathering test was conducted for 1000 hours under the conditions specified in JIS A 6910. However, the gloss decreases,
No changes such as discoloration, cracking, or peeling were observed.
実施例2〜5
実施例1と同様に、ポリイソシアネートおよびポリオー
ルを表2のように変えて試験した結果を、同じく表2に
示す。Examples 2 to 5 Similar to Example 1, the polyisocyanate and polyol were changed as shown in Table 2, and the test results are also shown in Table 2.
比較例1〜4
実施例1と同様に1ポリイソシアネートおよびポリオー
ルを表2のように変えて試験した結果を、同じく表2に
示す。Comparative Examples 1 to 4 Table 2 also shows the results of tests conducted in the same manner as in Example 1, with the polyisocyanate and polyol changed as shown in Table 2.
表 1 表1中の0内の数字は、仕込み量(部〕を示す。Table 1 The numbers within 0 in Table 1 indicate the amount (parts) to be prepared.
表1中の略号
IPI)I :インホロンジイソシアネート1.3−
BG : i 、 !−ブタンジオール2−Et−H
D:2−エチル−1,3−ヘキサンジオールNPG
:ネオペンチルグリコール表 2
*1:日本ポリウレタン工業株式会社製のHMDI系ポ
リイソシアネート
*2:住友バイエルウレタン株式会社製のHMDI系ポ
リイソシアネートAbbreviation in Table 1 IPI) I: Inphorone diisocyanate 1.3-
BG: i,! -butanediol 2-Et-H
D: 2-ethyl-1,3-hexanediol NPG
: Neopentyl glycol Table 2 *1: HMDI polyisocyanate manufactured by Nippon Polyurethane Industries Co., Ltd. *2: HMDI polyisocyanate manufactured by Sumitomo Bayer Urethane Co., Ltd.
Claims (3)
ネートの単独もしくは混合物と、分岐を有する炭素数3
〜10のアルキレンジオールとの反応生成物である末端
にイソシアネート基を有するポリイソシアネートと、水
酸基を2個以上有する含フツ素ポリオールとを、NCO
/OH当量比0.5〜2.0の範囲で混合してなること
を特徴とする塗料用組成物。(1) Aliphatic diisocyanate or alicyclic diisocyanate alone or as a mixture, and a branched carbon number 3
A polyisocyanate having an isocyanate group at the end, which is a reaction product with an alkylene diol of 1 to 10, and a fluorine-containing polyol having two or more hydroxyl groups are combined into NCO
1. A coating composition comprising a mixture of /OH equivalent ratio in the range of 0.5 to 2.0.
シアネートである特許請求の範囲第1項記載の塗料用組
成物。(2) The coating composition according to claim 1, wherein the aliphatic diisocyanate is hexamethylene diisocyanate.
ルが1,3−ブタンジオール、ネオペンチルグリコール
、2−エチル−1,3−ヘキサンジオールである特許請
求の範囲第1項記載の塗料用組成物。(3) The coating composition according to claim 1, wherein the branched alkylene diol having 3 to 10 carbon atoms is 1,3-butanediol, neopentyl glycol, or 2-ethyl-1,3-hexanediol. thing.