JPS63213546A - Resin composition - Google Patents
Resin compositionInfo
- Publication number
- JPS63213546A JPS63213546A JP4597887A JP4597887A JPS63213546A JP S63213546 A JPS63213546 A JP S63213546A JP 4597887 A JP4597887 A JP 4597887A JP 4597887 A JP4597887 A JP 4597887A JP S63213546 A JPS63213546 A JP S63213546A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- resin composition
- polyacetal
- polyacetal resin
- tetrafluoroethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
（産業上の利用分野）
本発明は、ポリアセタール樹脂を基材とする樹脂組成物
に係り、特にその摩擦特性、摩耗特性および撥水性の向
上対策に関する。DETAILED DESCRIPTION OF THE INVENTION (Industrial Application Field) The present invention relates to a resin composition based on a polyacetal resin, and particularly to measures for improving its friction characteristics, wear characteristics, and water repellency.
（従来の技術）
従来より、ポリアセタール樹脂は、エンジニアリングプ
ラスチックの中でも、機械的特性、特に疲労強度が勝れ
ていること、耐薬品性が非常に優秀であること、および
ＩＩ！擦および摩耗特性が良好であること、寸法安定性
が良いことなどの長所を有しており、自動車、電気、電
子供各類等の部品に使用する構造用材料として、広範に
利用されている。(Prior Art) Polyacetal resin has traditionally been known to have excellent mechanical properties, especially fatigue strength, and excellent chemical resistance among engineering plastics, and II! It has advantages such as good friction and abrasion properties and good dimensional stability, and is widely used as a structural material for parts of automobiles, electrical appliances, electronic devices, etc. .
（発明が解決しようとする問題点）
しかし、ポリアセタール樹脂の摩耗特性には未だ改善の
余地が残されており、特に十分な自己潤滑性を有してい
ない。そのために、軸受などの摺動部品用材料としては
充分利用されるに至っていないという問題があり、また
撥水性が十分高くないために汚れが除去し難く、商品価
値を損ねるという問題がある。(Problems to be Solved by the Invention) However, there is still room for improvement in the wear characteristics of polyacetal resins, and in particular they do not have sufficient self-lubricating properties. For this reason, there is a problem that it has not been sufficiently used as a material for sliding parts such as bearings, and there is also a problem that dirt is difficult to remove because the water repellency is not high enough, which impairs commercial value.
本発明は斯かる点に鑑みてなされたものであり、その目
的は、ポリアセタール樹脂に他の適切な樹脂を適宜添加
することにより、ポリアセタール樹脂の持つ優秀な特性
を損なうことなくその１１！擦特性、摩耗特性および撥
水性を改善し、摺動部品の素材として優れた樹脂組成物
を提供することにある。The present invention has been made in view of these points, and its object is to add other appropriate resins to polyacetal resin as appropriate to achieve the 11! without impairing the excellent properties of polyacetal resin. The object of the present invention is to provide a resin composition that has improved friction properties, abrasion properties, and water repellency, and is excellent as a material for sliding parts.
（問題点を解決するための手段）
上記目的を達成するため本発明の解決手段は、ポリアセ
タールｌ［に４弗化エチレン樹脂を重發比で５０％以下
添加してなる樹脂組成物を偶成したものである。(Means for Solving the Problems) In order to achieve the above object, the solution of the present invention is to prepare a resin composition in which 50% or less of polyethylene tetrafluoride resin is added to polyacetal. It is something.
（作用）
以上の構成により、本発明の樹脂組成物では、低い表面
摩擦係数を有する４弗化エチレン樹脂がポリアセタール
樹脂に重量化で５０％以下添加されるので、ポリアセタ
ール樹脂の摩擦特性および摩耗特性が向上する。しかも
、４弗化エチレン樹脂樹脂は高い融点を有するので、ポ
リアセタール樹脂の耐熱性や疲労強度を低下させること
がなく、よって、優秀な機械的特性、摩擦特性および摩
耗特性を有するＩｎ部品材料を提供することができる。(Function) With the above configuration, in the resin composition of the present invention, 50% or less by weight of the tetrafluoroethylene resin having a low surface friction coefficient is added to the polyacetal resin, so that the friction and wear characteristics of the polyacetal resin are improved. will improve. Moreover, since the tetrafluoroethylene resin resin has a high melting point, it does not reduce the heat resistance and fatigue strength of the polyacetal resin, thus providing In component materials with excellent mechanical properties, friction properties, and wear properties. can do.
また、４弗化エチレン樹脂の撥水性は極めて高いので、
樹脂組成物全体の撥水性が向上し、付着した汚れを容易
に除去することができる。よって、商品の美観を長く保
持することができ、商品価値を向上覆ることができる。In addition, the water repellency of tetrafluoroethylene resin is extremely high, so
The water repellency of the entire resin composition is improved, and attached dirt can be easily removed. Therefore, the beauty of the product can be maintained for a long time, and the value of the product can be improved.
（実施例） 以下、本発明の実施例を第１図に基づき説明する。(Example) Embodiments of the present invention will be described below with reference to FIG.
第１図は本発明の樹脂組成物を適用した０ＡＩＩ器等に
使用される軸受部品を示し、（１）はアルミニウム系の
合金で形成された回転軸、（２）は該回転軸（１）を回
転自在に支承するための軸受であって、該軸受（２）は
、ポリアセタール樹脂に４弗化エチレン樹脂を添加して
構成された樹脂組成物で形成されている。FIG. 1 shows bearing parts used in 0AII equipment, etc. to which the resin composition of the present invention is applied, in which (1) shows a rotating shaft made of an aluminum alloy, and (2) shows the rotating shaft (1). The bearing (2) is made of a resin composition made by adding tetrafluoroethylene resin to polyacetal resin.
ここで、上記軸受（２）の構成要素をなすポリアセター
ル樹脂は、例えば第２図に示すような分子構造を有する
熱可塑性の高分子で、ホルムアルデヒドの重合反応によ
り侍られるホモポリマータイプのものの他、トリオキサ
ンを開環したものにエチレンオキサイド、１，３−ジオ
キソランなどの環状エーテルを適宜加えて共重合したコ
ポリマータイプのものがある。また、上記４弗化エチレ
ン樹脂は第３図に示すような分子構造を有する熱可塑性
の高分子である。そして、上記樹脂組成物は、ポリアセ
タール樹脂の粉末と、４弗化エチレン樹脂の粉末とをタ
ンブラ−等で混合後、射出成型、押出し成型などの成型
加工により得られるものである。Here, the polyacetal resin that constitutes the component of the bearing (2) is a thermoplastic polymer having a molecular structure as shown in FIG. There is a copolymer type obtained by copolymerizing ring-opened trioxane with appropriate addition of a cyclic ether such as ethylene oxide or 1,3-dioxolane. Further, the above-mentioned tetrafluoroethylene resin is a thermoplastic polymer having a molecular structure as shown in FIG. The resin composition is obtained by mixing polyacetal resin powder and tetrafluoroethylene resin powder in a tumbler or the like, and then performing a molding process such as injection molding or extrusion molding.
したがって、上記実施例では、ポリアセタール樹脂に４
弗化エチレン樹脂を添加した樹脂組成物を軸受（２）と
して使用することにより、その摩擦特性および摩耗特性
を改善することができる。Therefore, in the above example, the polyacetal resin has 4
By using a resin composition to which a fluorinated ethylene resin is added as the bearing (2), its frictional characteristics and wear characteristics can be improved.
すなわち、第３図に示されるように、４弗化エチレン樹
脂は、直鎖状の炭素原子鎖の骨格を大きなフッ素原子で
隙間無く取り囲んだ構造をとっており、分子の表面が滑
らかであって、その表面摩擦係数が非常に小さく、その
ため４弗化エチレン樹脂の添加によりポリアセタール樹
脂の摩擦係数が低下し、さらに、摩擦係数の低下によっ
て摩耗特性が向上するものである。In other words, as shown in Figure 3, tetrafluoroethylene resin has a structure in which a linear carbon atom chain skeleton is surrounded by large fluorine atoms without any gaps, and the surface of the molecule is smooth. The surface friction coefficient of the polyacetal resin is very small, and therefore, the addition of the tetrafluoroethylene resin lowers the friction coefficient of the polyacetal resin, and furthermore, the reduction in the friction coefficient improves the wear characteristics.
しかも、４弗化エチレン樹脂は高い融点を有するので、
ポリアセタール樹脂の耐熱性を低下させることがなく、
したがって、疲労強度や寸法安定性を損することがない
。Moreover, since tetrafluoroethylene resin has a high melting point,
Without reducing the heat resistance of polyacetal resin,
Therefore, fatigue strength and dimensional stability are not impaired.
また、４弗化エチレン樹脂の撥水性は極めて高いので、
ポリアセタール樹脂の撥水性が向上し、付着した汚れを
容易に除去することができる。よって、商品の美観を長
く保持することができ、商品価値を向上することができ
る。In addition, the water repellency of tetrafluoroethylene resin is extremely high, so
The water repellency of polyacetal resin is improved, and attached dirt can be easily removed. Therefore, the beauty of the product can be maintained for a long time, and the product value can be improved.
さらに、摩擦特性の改善により、上記のような樹脂組成
物の特性の改善のみでなく、ポリアセタール樹膓成型時
の成型特性をも改善することができる。すなわち、例え
ば射出成形時において、金型との摩擦係数が低下するの
で、金型の摩耗、損傷等が少なくなり、金型の寿命を向
上させることができる。Furthermore, by improving the frictional properties, it is possible not only to improve the properties of the resin composition as described above, but also to improve the molding properties when molding polyacetal resin. That is, during injection molding, for example, the coefficient of friction with the mold is reduced, so wear and damage to the mold are reduced, and the life of the mold can be improved.
本発明の樹脂組成物に使用されるポリアセタール樹脂は
、上記コポリマータイプとホモポリマータイプとがあり
、それらのうちいずれを用いてもよい。The polyacetal resin used in the resin composition of the present invention includes the above-mentioned copolymer type and homopolymer type, and any of them may be used.
また、本発明のｌｆｆ４脂組成物に使用される４弗化エ
チレン樹脂の粉末は４弗化エチレン樹脂を粉砕加工した
ものであって、その例として、商品名「サンフロンＳＧ
＃８００、＃１０００、＃３０００」で市販される各グ
レード別に粉砕された微粉末の４弗化工チレン＃ｉＡｍ
があり、使用される部品の大きさ、形状、作用する荷重
などの条件に応じて、各グレードを選択して用いること
ができる。Further, the powder of the tetrafluoroethylene resin used in the lff4 fat composition of the present invention is obtained by pulverizing the tetrafluoroethylene resin.
#800, #1000, #3000" pulverized fine powder of 4-fluorochemically modified tyrene #iAm for each grade
Each grade can be selected and used depending on conditions such as the size, shape, and load of the parts used.
そのとき、４弗化エチレン樹脂の添加量が重量圧で５０
％よりも多い場合にはポリアセタール樹脂の特性をかえ
って害する結果となるので、５０％（重量圧）以下の添
加量が好ましい。At that time, the amount of tetrafluoroethylene resin added was 50% by weight pressure.
If the amount is more than 50% (weight pressure), the properties of the polyacetal resin will be adversely affected, so the amount added is preferably 50% (weight pressure) or less.
なお、上記「サンフロン」は、樹脂の粉砕前に樹脂を３
８０℃前後の温度に一定時間保持したいわゆる焼成処理
を行っており、特に、そのような焼成処理を行った後に
粉砕した４弗化エチレン樹脂粉末ではポリアセタール樹
脂粉末との混合時に４弗化エチレン樹脂粉末の分散性が
良好であるので、樹脂組成物中に４弗化工チレン樹脂粒
子が均一に分布するという著効を有する。In addition, for the above "Sunflon", the resin is
A so-called firing process is performed in which the temperature is maintained at around 80°C for a certain period of time, and in particular, the tetrafluoroethylene resin powder that is crushed after such a firing process is mixed with the polyacetal resin powder. Since the powder has good dispersibility, it has the remarkable effect of uniformly distributing the tetrafluoroethylene resin particles in the resin composition.
尚、本発明の樹脂組成物には、グラスファイバーを添加
することができ、そのときには、４弗化エチレン樹脂の
みを添加したものに比べ機械的強度をさらに向上させる
ことができる。そのとき、グラスファイバーを添加した
場合、通常ポリアセタール樹脂の表面にグラスファイバ
ーが露出して、他の物体との活動部にグラスファイバー
の微粉末が脱落して相手部材を傷付ける危険性があるが
、４弗化エチレン樹脂により、グラスファイバーの表面
露出を抑制することができるので、その強度の強化効果
を有効に発揮するものである。また、グラスファイバー
の代わりにカーボンファイバー等の強化材を用いても同
様の効果が得られる。Incidentally, glass fiber can be added to the resin composition of the present invention, and in this case, the mechanical strength can be further improved compared to a composition in which only tetrafluoroethylene resin is added. At that time, if glass fiber is added, there is a risk that the glass fiber will be exposed on the surface of the polyacetal resin and the fine powder of glass fiber will fall into the active area with other objects and damage the other material. Since the tetrafluoroethylene resin can suppress the surface exposure of the glass fibers, its strength-enhancing effect can be effectively exhibited. Further, similar effects can be obtained by using a reinforcing material such as carbon fiber instead of glass fiber.
さらに、本発明の樹脂組成物には、二硫化モリブデン、
グラファイト粉末等の固体潤滑剤を添加して４弗化エチ
レン樹脂との相乗効果を得ることができる。Furthermore, the resin composition of the present invention includes molybdenum disulfide,
A solid lubricant such as graphite powder can be added to obtain a synergistic effect with the tetrafluoroethylene resin.
また、本発明の樹脂組成物は、上記実施例のようなＯＡ
機器の軸受部品のほか、自動車、電気機器、生産機械、
自動選別器、あるいはスポーツ用器具などの物体が摺Ｉ
Ｊする部分に使用される部品（軸受、歯車、案内溝、ロ
ンド等）、特に高精度を要求される部品の構成材料とし
て利用することができる。Further, the resin composition of the present invention can be applied to OA as in the above examples.
In addition to bearing parts for equipment, automobiles, electrical equipment, production machinery,
Objects such as automatic sorters or sports equipment may be
It can be used as a constituent material for parts used in J parts (bearings, gears, guide grooves, ronds, etc.), especially parts that require high precision.
さらに、本発明の樹脂組成物は、汚れの付着を容易に除
去でき美観を長く保持することができるので、水道の蛇
口、バルブ、筆記具のペン先等多くの方面に利用するこ
とができる。Further, the resin composition of the present invention can easily remove dirt and retain its beautiful appearance for a long time, so it can be used in many areas such as water faucets, valves, and pen nibs of writing instruments.
（具体例） 以下、具体例につき説明する。(Concrete example) A specific example will be explained below.
ポリアセタール樹脂粉末に、４弗化エチレン樹脂粉末を
体積比で１０％および２０％添加したものをそれぞれタ
ンブラ−で充分混合した後、射出成型により成型して上
記実施例の軸受（２）を形成した。下記表に、それらの
摩擦特性および摩耗特性のデータを従来のポリアセター
ル樹脂単体量のデータとともに示す。10% and 20% by volume of tetrafluoroethylene resin powder were added to polyacetal resin powder, respectively, which were thoroughly mixed in a tumbler and molded by injection molding to form the bearing (2) of the above example. . The table below shows data on their frictional and wear characteristics along with data on the amount of conventional polyacetal resin.
表
ここに、上記表において、摩耗係数には、ＣＩ”・ｓｅ
ｃ／Ｋｇ・ｍ −ｈｒのディメンジョンを有するもので
ある。また、表のデータは、回動によるＩＩＪ擦速変速
度０５ｍ／Ｓｅｃ 、加重２．８に９／Ｃ１一つまり、
ＰＶ値が０ 、７ ｈ−ｍ／ｃｎ−ｓｅｃの条件下で得
られた値である。In the above table, the wear coefficient includes CI"・se
It has a dimension of c/Kg·m-hr. In addition, the data in the table is IIJ friction change speed due to rotation 05 m/Sec, weight 2.8 and 9/C1 - that is,
This is a value obtained under conditions where the PV value is 0.7 hm/cn-sec.
上記表に示されるように、ポリアセタール樹脂単体で形
成される従来品に比べ、４弗化エチレン樹脂を１０％又
は２０％（体積比）添加した添加量では、摩耗係数にお
よび動摩擦係数が大巾に低下しており、その結果、無給
油の状態で使用することができる。したがって、本例の
ものは前記ポリアセタール樹脂の優れた機械的特性とあ
いまって、高精度を要求される部分の無給油軸受として
使用され得るものである。As shown in the table above, compared to conventional products made of polyacetal resin alone, when 10% or 20% (volume ratio) of tetrafluoroethylene resin is added, the coefficient of wear and coefficient of kinetic friction significantly increase. As a result, it can be used without lubrication. Therefore, this example, combined with the excellent mechanical properties of the polyacetal resin, can be used as an oil-free bearing for parts that require high precision.
（発明の効果）
以上説明したように、本発明の樹脂組成物によれば、ポ
リアセタール樹脂に４弗化エチレン樹脂を重量圧で５０
％以下添加したものであるので、ポリアセタール樹脂の
摩擦特性および摩耗特性を向上させることができ、優秀
な機械的特性、摩擦特性および摩耗特性を有する機構部
品材料、特に摺動部の部品材料として好適なものを提供
することができる。(Effects of the Invention) As explained above, according to the resin composition of the present invention, polyacetal resin is mixed with tetrafluoroethylene resin at a weight pressure of 50%.
% or less, it can improve the friction and wear characteristics of polyacetal resin, and it is suitable as a material for mechanical parts, especially for parts of sliding parts, which has excellent mechanical, friction and wear characteristics. can provide something.
また、撥水性を著しく向上させることができるので、美
観を長く保持することができ、商品価値を高めることが
できる。Furthermore, since the water repellency can be significantly improved, the aesthetic appearance can be maintained for a long time, and the commercial value can be increased.
第１図は本発明の実施例に係る軸受部品のｒＲＩ！ｇ構
成図である。第２図は実施例に係るポリアセタール樹脂
の分子構造図、第３図は４弗化エチレン樹脂の分子構造
図である。
二・、ｄ −１
第１図
第２図
第３図FIG. 1 shows the rRI! of a bearing component according to an embodiment of the present invention. g is a configuration diagram. FIG. 2 is a molecular structure diagram of a polyacetal resin according to an example, and FIG. 3 is a molecular structure diagram of a tetrafluoroethylene resin. 2., d-1 Figure 1 Figure 2 Figure 3
Claims (1)
比で５０％以下添加してなる樹脂組成物。(1) A resin composition obtained by adding 50% or less by weight of a tetrafluoroethylene resin to a polyacetal resin.