JPS63141718A - Preventing oligomer from adherence on surface of roll in casting of polyphenylene sulfide - Google Patents
Preventing oligomer from adherence on surface of roll in casting of polyphenylene sulfideInfo
- Publication number
- JPS63141718A JPS63141718A JP61289536A JP28953686A JPS63141718A JP S63141718 A JPS63141718 A JP S63141718A JP 61289536 A JP61289536 A JP 61289536A JP 28953686 A JP28953686 A JP 28953686A JP S63141718 A JPS63141718 A JP S63141718A
- Authority
- JP
- Japan
- Prior art keywords
- cooling roll
- film
- roll
- wire
- pps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、ポリフェニレンスルフィドを二軸延伸してフ
ィルムを成形する製造工程の前段階などにおいてダイか
ら押出成形されたフィルムを冷却ロールによりキャステ
ィングする方法に係り、特にこのキャスティングの際に
オリゴマーによる白色化した油状の汚れが冷却ロールの
表面に付着するのを防止する方法に関する。[Detailed Description of the Invention] [Industrial Application Field] The present invention involves casting a film extruded from a die using a cooling roll in a pre-stage of a manufacturing process in which polyphenylene sulfide is biaxially stretched to form a film. The present invention relates to a method, and particularly to a method for preventing whitened oily stains caused by oligomers from adhering to the surface of a cooling roll during casting.
ポリフェニレンスルフィド(以下PPSと呼ぶ)は、ベ
ンゼン環とイオウとが交互結合されたものであり、例え
ば、パラフェニレンスルフィドポリマーとメタフェニレ
ンスルフィドポリマーとのプロ・ツクコーポリマー、あ
るいはパラフェニレンスルフィドのホモポリマーなとの
状態で加工される。PPS樹脂は添加剤が加えられない
状態で使用され、またはその用途に応じて無機または有
機添加剤や安定剤が添加されて加工される。Polyphenylene sulfide (hereinafter referred to as PPS) is a product in which benzene rings and sulfur are alternately bonded, and is, for example, a pro-tsukko polymer of para-phenylene sulfide polymer and meta-phenylene sulfide polymer, or a homopolymer of para-phenylene sulfide. It is processed in such a state. PPS resins are used without additives or processed with inorganic or organic additives or stabilizers added depending on the application.
この種のPPS[脂の用途としては、フィルムに加工し
て磁気ディスクや磁気テープあるいは他の電子部品材料
として使用することが考えられている。PPSをフィル
ムに加工するには、まずペレットを押出機とTダイとに
よってフィルム状に成形する1次にTダイからの押出し
速度よりも速い周速にて回転する冷却ロールの表面にフ
ィルムを密着させる。そして、冷却ロールから剥がされ
たキャストフィルムを縦延伸し横延伸して二軸延伸フィ
ルムを形成する。It is considered that this type of PPS [fat may be used by processing it into a film and using it as a magnetic disk, magnetic tape, or other electronic component material. To process PPS into a film, first, pellets are formed into a film using an extruder and a T-die.First, the film is tightly attached to the surface of a cooling roll that rotates at a peripheral speed faster than the extrusion speed from the T-die. let Then, the cast film peeled off from the cooling roll is longitudinally stretched and transversely stretched to form a biaxially stretched film.
上記の製造工程によってPPSのフィルムを成形する場
合、そのキャスティングの際に、冷却ロールの表面に白
色化した油状の汚れが付着する問題が生じている。この
汚れが冷却ロールの表面に付着すると、フィルムに対す
る冷却むらが生じ、冷却ロールによる冷却効率が低下す
る。また冷却ロールの表面に汚れが付着すると、実質的
に冷却ロールの表面の平滑性が損なわれることになり、
キャスティング後のフィルムの表面が荒れて、フィルム
に曇りが生じることにもなる。When a PPS film is formed by the above manufacturing process, a problem arises in that white oily dirt adheres to the surface of the cooling roll during casting. If this dirt adheres to the surface of the cooling roll, uneven cooling of the film will occur and the cooling efficiency of the cooling roll will decrease. Furthermore, if dirt adheres to the surface of the cooling roll, the smoothness of the surface of the cooling roll will be substantially impaired.
The surface of the film after casting becomes rough, and the film becomes cloudy.
このロール表面の汚れは、重合度の少ない重合体すなわ
ちオリゴマー(oligo■er)によるものである、
このオリゴマーが冷却ロールの表面に付着する理由につ
いては完全に解明しきれないが、フィルムと冷却ロール
との密着性の低下が原因のひとつであることが推測され
る。すなわちTダイから押出されたフィルムが冷却ロー
ルの表面に巻かれたときに急冷されるため、フィルムと
冷却ロール表面との間の粘着力が低下する。そのためフ
ィルムが冷却ロール2から剥がれる際に、フィルム表面
に現れているオリゴマーが冷却ロールの表面に白色化し
た油状の状態で付着しやすくなるものと思われる。This stain on the roll surface is caused by polymers with a low degree of polymerization, that is, oligomers.
Although it is not completely clear why this oligomer adheres to the surface of the cooling roll, it is assumed that one of the causes is a decrease in the adhesion between the film and the cooling roll. That is, since the film extruded from the T-die is rapidly cooled when wound on the surface of the cooling roll, the adhesive force between the film and the surface of the cooling roll is reduced. Therefore, when the film is peeled off from the cooling roll 2, the oligomers appearing on the film surface are likely to adhere to the surface of the cooling roll in the form of a white oil.
このオリゴマーの付着によってフィルムの表面の平滑性
が損なわれ曇りが生じたりすると、その後に二軸延伸し
た場合に、透明度が低下した品質の劣ったフィルムが成
形される結果となる。したがって、フィルムの品質を維
持するためには、フィルム成形作業を一定時間継続した
後に、冷却ロールの表面を清掃し、オリゴマーを除去す
ることが必要になる。ところが、PPSのキャスティン
グにおいては、前記オリゴマーがいかなる薬品を使用し
ても簡単に除去できるものではなく、その清掃作業がき
わめて煩雑なものとなっている。If this oligomer adhesion impairs the smoothness of the surface of the film and causes cloudiness, a film of inferior quality with reduced transparency will be formed when biaxially stretched thereafter. Therefore, in order to maintain the quality of the film, it is necessary to clean the surface of the cooling roll and remove the oligomer after continuing the film forming operation for a certain period of time. However, in PPS casting, the oligomers cannot be easily removed using any chemicals, making cleaning work extremely complicated.
本発明は上記の問題点を解決するものであり、Tダイか
ら押出されたPPSフィルムを冷却ロールによってキャ
スティングする際に、オリゴマーが冷却ロールの表面に
付着しにくい状態を実現して、冷却ロールの表面に白色
化した油状の汚れが付着しないようにした方法を提供す
るものである。The present invention solves the above-mentioned problems, and when the PPS film extruded from a T-die is cast by a cooling roll, oligomers are difficult to adhere to the surface of the cooling roll, and the cooling roll is To provide a method that prevents white oily stains from adhering to surfaces.
〔問題点を解決するための具体的な手段〕本発明による
方法は、ダイによって押出成形されたポリフェニレンス
ルフィドのフィルムを、回転する冷却ロールの表面に密
着させ且つロール表面から剥がすことによってキャスト
フィルムを成形するキャスティングにおいて、ダイによ
って押出成形されたフィルムを帯電させて冷却ロールの
表面に密着させることにより、オリゴマーが冷却ロール
の表面に付着するのを防止することを特徴としている。[Specific means for solving the problem] The method according to the present invention involves bringing a polyphenylene sulfide film extruded by a die into close contact with the surface of a rotating cooling roll and peeling it off from the roll surface to form a cast film. In the casting process, the film extruded by a die is charged and brought into close contact with the surface of the cooling roll, thereby preventing oligomers from adhering to the surface of the cooling roll.
以下、問題点を解決するための具体的な手段について詳
述する。Hereinafter, specific means for solving the problems will be explained in detail.
第1図は本発明による方法を採用したPPSのフィルム
成形作業を示す工程図、第2図は本発明の方法を実施す
るためのキャスティング装置を示す側面図である。FIG. 1 is a process diagram showing a PPS film forming operation employing the method according to the present invention, and FIG. 2 is a side view showing a casting apparatus for carrying out the method according to the present invention.
PPSのペレットは、スクリュ押出機などにより加熱さ
れて定量押出しされ、Tダイ1によってフィルム状に成
形される。このフィルムは、回転駆動されている冷却ロ
ール2の外周面に巻かれる。この冷却ロール2は金属ロ
ールの表面にハードクロームメッキが施されているもの
であり、その表面は鏡面に近い状態になっている。冷却
ロール2の表面の回転周速は、Tダイ1からのフィルム
の排出速度の10−15倍程度である。Tダイ1から排
出されたPPSフィルムは前記の速度差によって引延ば
され且つ冷却ロール2の表面によって冷却される。そし
てフィルムは引剥しロール4によって冷却ロール2の表
面から引剥される。PPS pellets are heated and quantitatively extruded using a screw extruder or the like, and then formed into a film using a T-die 1. This film is wound around the outer peripheral surface of the cooling roll 2 which is being driven to rotate. The cooling roll 2 is a metal roll whose surface is plated with hard chrome, and the surface is almost mirror-like. The peripheral speed of rotation of the surface of the cooling roll 2 is approximately 10-15 times the speed at which the film is discharged from the T-die 1. The PPS film discharged from the T-die 1 is stretched by the speed difference and cooled by the surface of the cooling roll 2. The film is then peeled off from the surface of the cooling roll 2 by a peeling roll 4.
第2図に示すように、冷却ロール2には帯電用のワイヤ
3が対向している。このワイヤ3は冷却ロール2の表面
に対して約5mm程度の間隔を開は且つ、冷却ロール2
に巻かれるフィルムの幅方向へほぼ全長にわたって張設
されている。このワイ。As shown in FIG. 2, a charging wire 3 faces the cooling roll 2. This wire 3 is spaced apart from the surface of the cooling roll 2 by about 5 mm, and
It is stretched across almost the entire length of the film wound in the width direction. This wai.
ャ3には6.5KV程度の直流高電圧が印加されている
。Tダイ1から排出されたフィルムはワイヤ3によって
帯電され、静電吸着によって冷却ロール2の表面に密着
させられる。帯電されたPPSが冷却ロール2の表面に
強く密着することにより、冷却ロール2からキャストフ
ィルム5が剥れた後に冷却ロール2の表面にオリゴマー
による白色化した油状の汚れがほとんど付着しなくなる
。その理由は、帯電されたフィルムが静電吸着により冷
却ロール2の表面に強<i着するために、フィルム表面
に現われているオリゴマーがフィルム側に強く引き付け
られる状態となり、キャストフィルム5が冷却ロール2
から剥がれるときにオリゴマーがロール表面にほどんど
付着しないためであると推測される。このように冷却ロ
ール2の表面にオリゴマーによる汚れが付着しなくなる
ことにより、冷却ロール2によるフィルムに対する冷却
効率が良くなる。また冷却ロール2の表面が常に平滑な
状態に維持されるので、キャストフィルム5に対して冷
却ロール2の表面の鏡面が転写され、フィルム表面が平
滑な状態に加工される。A DC high voltage of about 6.5 KV is applied to the carrier 3. The film discharged from the T-die 1 is charged by the wire 3 and brought into close contact with the surface of the cooling roll 2 by electrostatic adsorption. By strongly adhering the charged PPS to the surface of the cooling roll 2, almost no oily stains whitened by oligomers adhere to the surface of the cooling roll 2 after the cast film 5 is peeled off from the cooling roll 2. The reason for this is that the charged film adheres strongly to the surface of the cooling roll 2 due to electrostatic adsorption, so the oligomers appearing on the film surface are strongly attracted to the film side, and the cast film 5 is attached to the cooling roll 2. 2
It is presumed that this is because the oligomer hardly adheres to the roll surface when it is peeled off from the roll. In this way, by preventing stains caused by oligomers from adhering to the surface of the cooling roll 2, the cooling efficiency of the film by the cooling roll 2 is improved. In addition, since the surface of the cooling roll 2 is always maintained in a smooth state, the mirror surface of the surface of the cooling roll 2 is transferred to the cast film 5, and the film surface is processed into a smooth state.
冷却ロール2から剥がれた後のキャストフィルム5は、
周速差を有する延伸ロールなどによって縦方向へ延伸さ
れ、さらにテンタ方式などの横延伸装置により横延伸さ
れて、二軸延伸フィルムとして成形される(第1図参照
)。The cast film 5 after being peeled off from the cooling roll 2 is
The film is stretched in the longitudinal direction using stretching rolls having different circumferential speeds, and then laterally stretched using a transverse stretching device such as a tenter system to form a biaxially stretched film (see FIG. 1).
以下、本発明の詳細な説明する。 The present invention will be explained in detail below.
実」1例」2
PPSは、パラフェニレンスルフィドのホモポリマーで
あり、例えば特開昭81−7332号公報に開示されて
いるのと同種のものを使用した。使用したポリマーは3
10℃/剪断速度200(秒)−1の条件で測定した溶
融粘度が4,000ボイズであり、ガラス転移点の温度
は約88℃である。ガラス転移点の温度は、特開昭61
−14228号公報に開示されているのと同じ測定方法
によって測定された値、すなわち差動走査型熱量計(D
SC)を用い、窒素下でサンプルlong、昇温速度1
0℃/■inで測定した場合の吸熱開始を示す温度で表
される値である。押出工程では、PPSを約310℃の
温度に加熱し、リップクリアランスがlavのTダイに
よってフィルム状に成形した。冷却ロールは表面にハー
ドクロームメッキが施され且つ表面粗さが0.2S以下
の鏡面に近いものを使用した。冷却ロールの表面の回転
周速は約5.7m/ll1nであり、TダイからPPS
フィルムが排出される速度のlO〜15倍程度と程度、
また冷却ロール2の表面温度は約74℃に維持させた。Example 2 PPS is a homopolymer of paraphenylene sulfide, and for example, the same type as disclosed in JP-A-81-7332 was used. The polymers used were 3
The melt viscosity measured under the conditions of 10°C/shear rate of 200 (sec)-1 is 4,000 voids, and the glass transition temperature is about 88°C. The temperature of the glass transition point is disclosed in JP-A-61
The value measured by the same measurement method as disclosed in Publication No. 14228, that is, the differential scanning calorimeter (D
SC) under nitrogen, sample long, heating rate 1
It is a value expressed as a temperature indicating the start of endotherm when measured at 0° C./in. In the extrusion process, PPS was heated to a temperature of about 310° C. and formed into a film using a T-die with a lip clearance of lav. The cooling roll used had a hard chrome plated surface and a surface roughness of 0.2S or less, which was close to a mirror surface. The peripheral speed of rotation on the surface of the cooling roll is approximately 5.7 m/ll1n, and the PPS is
About 10 to 15 times the speed at which the film is ejected,
Further, the surface temperature of the cooling roll 2 was maintained at about 74°C.
ワイヤ3は冷却ロール2の表面に対して約51麿の間隔
にて対向させ、このワイヤ3には約8 、5KVの直流
電圧を印加した。以下の表は、ワイヤ3に直流電圧6.
5KVを印加したときと、電圧を印加しなかったときに
おけるフィルムの帯電量(静電気)を比較して記載した
ものである。測定箇所は第2図に示すA−Hの6箇所と
し、シムコ製の静電気測定器5S−2型を使用し、フィ
ルムから約5cm離れた位置にて測定した。またA−H
の各測定箇所において、フィルムの左端(第2図におけ
る紙面奥方向の端部)、この左端から100mm内側、
フィルムの中央、フィルムの右端(第2図における紙面
手前方向の端部)から100m■内側、およびフィルム
の右端の合計5つの位Mにて測定した。冷却ロール2の
表面に巻かれ且つ冷却ロール2から剥されたキャストフ
ィルム5の厚さは約95gmであり、フィルム幅は約4
50mmである。また測定環境は、気温21”0で湿度
45%である。The wire 3 was opposed to the surface of the cooling roll 2 at an interval of about 51 mm, and a DC voltage of about 8.5 KV was applied to the wire 3. The table below shows the DC voltage 6.
This is a comparison of the amount of charge (static electricity) of the film when 5 KV was applied and when no voltage was applied. The measurement points were six points A to H shown in FIG. 2, and measurements were made at positions approximately 5 cm away from the film using a static electricity meter 5S-2 manufactured by Shimco. Also A-H
At each measurement location, the left edge of the film (the edge toward the back of the paper in Figure 2), 100 mm inside from this left edge,
Measurements were made at a total of five positions M: the center of the film, 100 m inward from the right end of the film (the end toward the front of the paper in FIG. 2), and the right end of the film. The thickness of the cast film 5 wound on the surface of the cooling roll 2 and peeled off from the cooling roll 2 is approximately 95 gm, and the film width is approximately 4 gm.
It is 50mm. The measurement environment was a temperature of 21"0 and a humidity of 45%.
(以下余白)
表−1(ワイヤへの印加電圧8.5KV )表−2(ワ
イヤへ電圧を印加しない場合)上記表−1に示した電圧
印加条件の基で、合計約20時間のキャスティングを行
なったが、冷却ロール2の表面にはオリゴマーによる汚
れがほとんど付着せず、ロール表面の清掃が必要となる
状態には至らなかった。なお表−2に示したようにワイ
ヤ3に電圧を印加しない状態でキャスティングを行なう
と、冷却ロール2の表面にオリゴマーによる汚れが付着
し、清掃が必要な状態となった。(Left below) Table 1 (Voltage applied to the wire 8.5KV) Table 2 (When no voltage is applied to the wire) Casting was performed for a total of about 20 hours under the voltage application conditions shown in Table 1 above. However, almost no oligomer stains adhered to the surface of the cooling roll 2, and the roll surface did not require cleaning. As shown in Table 2, when casting was carried out without applying voltage to the wire 3, oligomer stains adhered to the surface of the cooling roll 2, requiring cleaning.
支直遣」
PPSは、実施例1と同じものを使用した。押出工程で
は、PPSを約310℃の温度に加熱し。The same PPS as in Example 1 was used. In the extrusion process, the PPS is heated to a temperature of approximately 310°C.
リップクリアランスが1■のTダイによってフィルム状
に成形した。冷却ロールは表面にハードクロームメッキ
が施され且つ表面粗さが0.2S以下の鏡面に近いもの
を使用した。冷却ロールの表面の回転周速は約3im/
winであり、TダイからPPSフィルムが排出される
速度の10〜15倍程度と程度、また冷却ロール2の表
面温度は約70℃に維持させた。ワイヤは冷却ロール2
の表面に対して約5mmの間隔にて対向させ、このワイ
ヤには約6.5KVの直流電圧を印加した。It was molded into a film using a T-die with a lip clearance of 1 square inch. The cooling roll used had a hard chrome plated surface and a surface roughness of 0.2S or less, which was close to a mirror surface. The peripheral speed of rotation on the surface of the cooling roll is approximately 3 im/
The speed was about 10 to 15 times the speed at which the PPS film was discharged from the T-die, and the surface temperature of the cooling roll 2 was maintained at about 70°C. The wire is on cooling roll 2
A DC voltage of about 6.5 KV was applied to the wire.
ト記条件の基で、合計約20時間のキャスティングを行
なったが、冷却ロール2の表面にはオリゴマーによる汚
れがほどんど付着せず、ロール表面の清掃が必要となる
状態には至らなかった。Casting was carried out for a total of about 20 hours under the conditions described above, but the surface of the cooling roll 2 was hardly contaminated with oligomers, and the roll surface did not reach a state where cleaning was required.
支ム皇」
P P S if、メタフェニレンスルフィドポリマー
とメタフェニレンスルフィドポリマーのモル比が85:
15程度であるブロックコーポリマーであり、例えば特
開昭61−14228号公報に開示されているのと同種
のものを使用した。使用したブロックコーポリマーは、
樹脂温度310℃/剪断速度200(秒)−1の条件で
測定した溶融粘度が4,000ボイズであり、ガラス転
移点の温度は約73℃である。If the molar ratio of metaphenylene sulfide polymer and metaphenylene sulfide polymer is 85:
A block copolymer having a molecular weight of about 15, for example, the same type as that disclosed in JP-A-61-14228 was used. The block copolymer used was
The melt viscosity measured under the conditions of resin temperature 310°C/shear rate 200 (sec)-1 is 4,000 voids, and the glass transition temperature is about 73°C.
ガラス転移点の温度は、特開昭81−14228号公報
に開示されているのと同じ測定方法によって測定された
値、すなわち差動走査型熱量計(DSC)を用い、窒素
下でサンプル10mg、昇温速度10℃/sinで測定
した場合の吸熱開始を示す温度で表される値である。押
出機では、PPSを約310℃の温度に加熱し、リップ
クリアランスが1mmのTダイによってフィルム状に成
形した。冷却ロールは表面にハードクロームメッキが施
され且つ表面粗さが0.2S以下の鏡面に近いものを使
用した。冷却ロールの表面の回転周速は約3m/win
であり、TダイからPPSフィルムが排出される速度の
lθ〜15倍程度と程度。また冷却ロール2の表面温度
は約60℃に維持させた。ワイヤは冷却ロール2の表面
に対して約5m厘の間隔にて対向させ、このワイヤには
約8.5KVの直流電圧を印加した。The temperature of the glass transition point is the value measured by the same measurement method as disclosed in JP-A-81-14228, that is, using a differential scanning calorimeter (DSC) and measuring 10 mg of the sample under nitrogen. This is a value expressed as a temperature indicating the start of endotherm when measured at a temperature increase rate of 10° C./sin. In the extruder, PPS was heated to a temperature of about 310° C. and formed into a film using a T-die with a lip clearance of 1 mm. The cooling roll used had a hard chrome plated surface and a surface roughness of 0.2S or less, which was close to a mirror surface. The rotation speed of the surface of the cooling roll is approximately 3 m/win
The speed is approximately lθ~15 times the speed at which the PPS film is discharged from the T-die. Further, the surface temperature of the cooling roll 2 was maintained at about 60°C. The wire was opposed to the surface of the cooling roll 2 at an interval of about 5 m, and a DC voltage of about 8.5 KV was applied to the wire.
上記条件の基で1合計約20時間のキャスティングを行
なったが、冷却ロール2の表面にはオリゴマーによる汚
れがほとんど付着せず、ロール表面の清掃が必要となる
状態には至らなかった。またキャストフィルムを二軸延
伸した後のフィルムには曇りなどが全く生じなかった。Casting was carried out for a total of about 20 hours under the above conditions, but there was almost no oligomer staining on the surface of the cooling roll 2, and the roll surface did not require cleaning. Further, after the cast film was biaxially stretched, no clouding occurred in the film.
以上のように本発明によれば、PPSのキャスティング
において、冷却ロールの表面にオリゴマーによる白色化
した油状の汚れが付着しなくなる。よって冷却ロールに
よる冷却効率の低下が防1Fでき、またキャストフィル
ムの表面も平滑になり、曇りのない良品質のフィルムを
成形できるようになる。また冷却ロールの表面からオリ
ゴマーを除去するための頻繁な清掃作業も不要になる。As described above, according to the present invention, whitened oily stains caused by oligomers do not adhere to the surface of the cooling roll during PPS casting. Therefore, a decrease in cooling efficiency due to the cooling roll can be prevented by 1F, and the surface of the cast film becomes smooth, making it possible to form a high-quality film without clouding. It also eliminates the need for frequent cleaning operations to remove oligomers from the surface of the cooling roll.
第1図は本発明による方法を使用したポリフェニレンス
ルフィドのフィルム成形工程を示す工程図、第2図はキ
ャスティングのための装置を示す側面図である。
1・・・Tグイ、2・・・冷却ロール、3・・・帯電用
ワイヤ、4・・・引剥しロール、5・・・PPSのキャ
ストフイ ル ム 。
出願人 呉羽化学工業株式会社
代理人 弁理士 野 崎 照 夫
”・5FIG. 1 is a process diagram showing a polyphenylene sulfide film forming process using the method according to the present invention, and FIG. 2 is a side view showing an apparatus for casting. 1... T guide, 2... Cooling roll, 3... Charging wire, 4... Peeling roll, 5... PPS cast film. Applicant Kureha Chemical Industry Co., Ltd. Agent Patent Attorney Teruo Nozaki”・5
Claims (1)
のフィルムを、回転する冷却ロールの表面に密着させ且
つロール表面から剥がすことによってキャストフィルム
を成形するキャスティングにおいて、ダイによって押出
成形されたフィルムを帯電させて冷却ロールの表面に密
着させることにより、オリゴマーが冷却ロールの表面に
付着するのを防止する方法。In casting, a polyphenylene sulfide film extruded by a die is brought into close contact with the surface of a rotating cooling roll and then peeled off from the roll surface to form a cast film. A method of preventing oligomers from adhering to the surface of a cooling roll by bringing them into close contact with the surface.