JPS63111050A - Sheet for vacuum molding - Google Patents
Sheet for vacuum moldingInfo
- Publication number
- JPS63111050A JPS63111050A JP61257918A JP25791886A JPS63111050A JP S63111050 A JPS63111050 A JP S63111050A JP 61257918 A JP61257918 A JP 61257918A JP 25791886 A JP25791886 A JP 25791886A JP S63111050 A JPS63111050 A JP S63111050A
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- vacuum forming
- protective
- film
- vacuum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Abstract] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
産業上の利用分野
本発明は、真空成形相シートの改良ζ二関Tる。
従来の技術
アクリル樹脂シートは、表面光沢の良さから。
インテリア、看板等に多く便用されているが。
真空成形やトリハング等の堆扱いやスタッキングにより
傷がつくのを防止するために、保診紙や保接フィルムを
貼付けている。真空成形時にシー、前記保護紙や保護フ
ィルムを剥がして成形を行なっている。これは−保護紙
を貼付けたよま真空成形したときは、保護紙が真空成形
の伸び′二追従せず、rfc形できないためである。ま
た。
保護フィルムとして塩化ビニリデンフィルムを使用した
ときは、成形後にこのフィルムが成形品から容易に剥離
しないこと、ポリエチレンフヒ
イルムを使用したときは、成形Tるシートの密△
貴注に乏しく、真空成形時に保護フィルムとシートh間
にエアをかみ5!j、彫工具合を生じること等のために
、いずれも真空成形時に保護フィルムを剥がしている。
発明が解決しようとTる問題点
上記のように、従来は、保護紙や保握フィルムを真空成
形C二先立ち剥がしていつので、bν、:#1ユ
斐び成形品(二保護フィルムを貼らなけれはならない。
そして、成形品が凹凸C二重んだ三次元形状である場合
には、保護フィルムを成形品に。
看させるの11容易です<、隙間からほこりか入り汚れ
易い問題力INDUSTRIAL APPLICATION FIELD The present invention relates to improvements in vacuum-formed phase sheets. Conventional technology Acrylic resin sheets have a good surface gloss. It is often used for interior decoration, signboards, etc. In order to prevent damage from handling and stacking during vacuum forming, tri-hanging, etc., medical checkup paper and adhesive film are pasted. During vacuum forming, the protective paper and protective film are peeled off before forming. This is because - when vacuum forming is performed with the protective paper pasted, the protective paper does not follow the elongation of the vacuum forming, and RFC forming is not possible. Also. When a vinylidene chloride film is used as a protective film, the film should not be easily peeled off from the molded product after molding, and when polyethylene film is used, the density of the molded sheet may be poor, and the film may not be easily peeled off during vacuum forming. Create air between the protective film and the sheet h5! j. The protective film was removed during vacuum forming in all cases to prevent engraving from occurring. Problems to be Solved by the Invention As mentioned above, in the past, the protective paper or holding film was peeled off prior to vacuum forming. In addition, if the molded product has a three-dimensional shape with a double uneven surface, it is easy to apply a protective film to the molded product.
【ある。
本発明は、保護シートを貼付けたまま真空成形でさ、ま
た、成形後5二必要に応じてrfc影品から&表シート
を容易に剥がせる真空成形…シート1に提供することを
目的とする。
問題点を解決するための手段
上記目的′Ije運成Tるために、本発明は、真空成形
される熱可塑性樹脂シート流血C二、前記シー ) i
”−接電せず密看し真空成形時の抗張力が前記シートよ
り小さくかつ延伸性が前記シートより大さい保護シート
を貼付けたものである。
作中
上記禍成により、保護シートは、真空成形時に成形性に
悪影曽を及は丁ことなくhJt4彰品彰状に沿って延伸
される。そして成形品シー密着しているだけで接肴して
いないので、成形後に適宜成形品から容易に剥力τ丁こ
とができる。
実施例
次に、本発明の一実施例を説明よる。
実施例I
MMA/AB8 2mシート(m J!1.2.5 m
s ) ノyyh血に、低密度ポリエチレン/酢酸ビニ
ル−エチレンP、重合粥脂(以下rzvA」という)2
層フィルム(総厚20μ)を保護シートとして、そのE
VA向を貼付け、真空成形用シートとした。
このシートを、雄型突き上げ方式の真空成形に供し、成
形ン行なった結果VMt表に示す。
比較例
保護フィルムとして1紙/塩化ビニリデン(比較例1)
、塩化ビニリデン(比較例2)、低密度ポリエチレン(
比較例3)、EVA(比較例4)を、それぞれ保護フィ
ルム、として実施例】0) MMA/ABS 2 M
シートに貼付41.同様に真空成形を行なった。七の結
果をw11表に示す。
W&1 表
実施例1で、低密度ポリエチレンに、 EVAの強度を
補って、成形後の保W!IIフィルムの剥離を一層容易
にしている。
発明の効果
上述のようC二本発明は1保護フィルムを貼付(アたま
ま真空成形を良好に行なうことができる。
この保護フィルムはh!i、Y6品にV!!!右してお
り、適宜rfc形品から容易に剥が丁ことができる。【be. An object of the present invention is to provide a vacuum-formed sheet 1 that can be vacuum-formed with a protective sheet attached, and also allows the top sheet to be easily peeled off from the RFC image product after molding if necessary. . Means for Solving the Problems In order to achieve the above objectives, the present invention provides vacuum-formed thermoplastic resin sheet bloody C2) i
” - A protective sheet with a lower tensile strength than the above-mentioned sheet and a higher stretchability than the above-mentioned sheet during vacuum forming without being connected to electricity. At times, it is stretched along the hJt4 award certificate without affecting the moldability.And since the molded product sheet is only in close contact with the molded product and is not attached, it can be easily stretched from the molded product as appropriate after molding. The peeling force can be τ.Example Next, an example of the present invention will be explained.Example I MMA/AB8 2m sheet (m J!1.2.5 m
s) Noyyh blood, low density polyethylene/vinyl acetate-ethylene P, polymerized gruel (hereinafter referred to as rzvA) 2
Using a layer film (total thickness 20μ) as a protective sheet, the E
The VA direction was pasted to make a sheet for vacuum forming. This sheet was subjected to vacuum forming using a male push-up method, and the results of the forming are shown in the VMt table. Comparative Example: 1 paper/vinylidene chloride as a protective film (Comparative Example 1)
, vinylidene chloride (Comparative Example 2), low density polyethylene (
Comparative Example 3) and EVA (Comparative Example 4) were used as protective films respectively]0) MMA/ABS 2 M
Paste on the sheet 41. Vacuum forming was performed in the same manner. The results of 7 are shown in table w11. W & 1 In Table Example 1, low density polyethylene is supplemented with the strength of EVA to maintain W after molding! This makes it easier to peel off the II film. Effects of the Invention As mentioned above, the present invention applies a protective film to the product (vacuum forming can be performed well as it is). It can be easily peeled off from RFC shaped products as appropriate.
Claims (1)
ートに接着せず密着し真空成形時の抗張力が前記シート
より小さくかつ延伸性が前記シートより大きい保護シー
トを貼付けてなる真空成形用シート。 2、保護シートがポリエチレン/酢酸ビニル−エチレン
共重合樹脂の2層フィルムであり、酢酸ビニル−エチレ
ン共重合樹脂面を熱可塑性樹脂シート表面に貼付けた特
許請求の範囲第1項記載の真空成形用シート。[Scope of Claims] 1. A protective sheet is pasted on the surface of the thermoplastic resin sheet to be vacuum formed, which is in close contact with the sheet without adhesion, and has a tensile strength smaller than that of the sheet during vacuum forming and a greater stretchability than the sheet. Vacuum forming sheet. 2. For vacuum forming according to claim 1, wherein the protective sheet is a two-layer film of polyethylene/vinyl acetate-ethylene copolymer resin, and the vinyl acetate-ethylene copolymer resin side is attached to the surface of the thermoplastic resin sheet. sheet.