JPS63105043A - Processed film - Google Patents
Processed filmInfo
- Publication number
- JPS63105043A JPS63105043A JP61251106A JP25110686A JPS63105043A JP S63105043 A JPS63105043 A JP S63105043A JP 61251106 A JP61251106 A JP 61251106A JP 25110686 A JP25110686 A JP 25110686A JP S63105043 A JPS63105043 A JP S63105043A
- Authority
- JP
- Japan
- Prior art keywords
- polymer composition
- composition layer
- film
- silicone oil
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
産業上の利用分野
本発明は、磁気記録あるいは感熱転写記録分野に用いら
れる主に高分子フィルムからなる基材を加工した加工フ
ィルムに関する。DETAILED DESCRIPTION OF THE INVENTION Field of Industrial Application The present invention relates to a processed film obtained by processing a base material mainly consisting of a polymer film used in the field of magnetic recording or thermal transfer recording.
従来の技術
主に高分子フィルムからなる基材は磁気記録あるいは感
熱転写記録に多く用いられているが、それぞれの記録ヘ
ッド上を安定に走行するために、記録ヘッドに接する基
材面に高分子組成物層が設けられている。Conventional technology Substrates made mainly of polymeric films are often used for magnetic recording or thermal transfer recording, but in order to run stably on each recording head, a polymeric film is applied to the surface of the substrate in contact with the recording head. A composition layer is provided.
この高分子組成物層と記録ヘッドとの走行摩擦抵抗を小
さくするのに特に有効な物質として液状潤滑性物質が提
案されている。A liquid lubricating substance has been proposed as a particularly effective substance for reducing the running frictional resistance between the polymer composition layer and the recording head.
発明が解決しようとする問題点
液状潤滑性物質として特に潤滑性の優れたシリコーンオ
イルを含む高分子組成物層を基材の少なくとも片面に厚
さが6μm以下の薄膜状に形成した時、シリコーンオイ
ルが高分子組成物層から部分的に分離して水玉状の模様
を作り、均一な高分子組成物層を形成しにくい問題があ
る。Problems to be Solved by the Invention When a polymer composition layer containing silicone oil, which has particularly excellent lubricity as a liquid lubricant substance, is formed in the form of a thin film with a thickness of 6 μm or less on at least one side of a base material, silicone oil There is a problem in that it partially separates from the polymer composition layer, creating a polka dot-like pattern, making it difficult to form a uniform polymer composition layer.
本発明は、シリコーンオイルを含み水玉状の模様の少な
い均一な高分子組成物層を有する加工フィルムを得るこ
とを目的とする。An object of the present invention is to obtain a processed film containing silicone oil and having a uniform polymer composition layer with few polka dot patterns.
問題点を解決するための手段
基材の少なくとも片面に、25℃における粘度が200
センチストークス以下のシリコーンオイルと硬化樹脂と
微粒子と添加剤とからなる厚さが5μm以下の高分子組
成物層を設ける。Means for Solving the Problems At least one side of the base material has a viscosity of 200 at 25°C.
A polymer composition layer having a thickness of 5 μm or less is provided, which is composed of a silicone oil of centistoke or less, a cured resin, fine particles, and an additive.
作 用
シリコーンオイルは、粘度が高い程分子量が大きいため
、他物質との離形性、潤滑性が大きくなシ、記録ヘッド
に対する走行性がよくなる。一方、粘度が小さい程潤滑
性は劣るが、他物質との反撥性も低下して相溶性が大き
くなシ、高分子組成物層を基材上に薄膜状で設けてもシ
リコーンオイルが分離しにくくなるものと思われる。Function: The higher the viscosity of silicone oil, the larger the molecular weight, which improves mold releasability from other substances, lubricity, and runnability with respect to the recording head. On the other hand, the lower the viscosity, the worse the lubricity, but the lower the repulsion with other substances and the greater the compatibility, and even if the polymer composition layer is provided in the form of a thin film on the base material, the silicone oil will not separate. It seems that it will become difficult.
実施例
図に本発明の実施例である加工フィルムの断面模式図を
示す。基材1の片面にシリコーンオイル3、硬化樹脂4
.微粒子5.添加剤6とからなる高分子組成物層2が設
けられている。The example diagram shows a schematic cross-sectional view of a processed film that is an example of the present invention. Silicone oil 3 and hardened resin 4 on one side of base material 1
.. Fine particles 5. A polymer composition layer 2 comprising an additive 6 is provided.
基材は従来公知の各種基材を用いることができ、又、そ
の材質を特に限定するものでない。一般的にはポリエチ
レンテレフタレートフィルム(以下、PETフィルムと
略す)あるいはさらに耐熱性の優れた各種フィルムを用
いると良好である。又、基材自身に導電性を付与したも
の、あるいは基材の少なくとも片面に導電性を付与した
ものでもよい。又、基材が片面に磁性体層を有している
基材も用いることができる。Various conventionally known base materials can be used as the base material, and the material is not particularly limited. Generally, it is preferable to use polyethylene terephthalate film (hereinafter abbreviated as PET film) or various films with excellent heat resistance. Alternatively, the base material itself may be made conductive, or at least one side of the base material may be made conductive. Further, a base material having a magnetic layer on one side can also be used.
シリコーンオイルは、26℃における粘度が200セン
チストークス以下のジメチルシリコーンオイル(ジメチ
ルシロキサン)、メチルフェニルシリコーンオイル、メ
チルクロロフェニルシリコーンオイル、フロロシリコー
ンオイル、メチルハイドロジエンシリコーンオイルであ
り、単独あるいは混合して用いることができる。Silicone oils include dimethyl silicone oil (dimethylsiloxane), methylphenyl silicone oil, methylchlorophenyl silicone oil, fluorosilicone oil, and methylhydrogen silicone oil, each having a viscosity of 200 centistokes or less at 26°C, and used alone or in combination. be able to.
特にジメチルシリコーンオイルが少量で潤滑性を高分子
組成物層表面に付与するため良好である。In particular, a small amount of dimethyl silicone oil is good because it imparts lubricity to the surface of the polymer composition layer.
粘度が200センチストークス以下(200センチスト
ークスを含む)で粘度が小さい程、水玉状の模様を形成
する確率が小さくなシ良好である。The viscosity is 200 centistokes or less (including 200 centistokes), and the lower the viscosity, the lower the probability of forming a polka dot pattern.
特に100センチストークス以下が最適である。In particular, 100 centistokes or less is optimal.
添加量はバインダーである硬化樹脂に対し一般に10重
重量板下で用いられる。The amount added is generally 10% by weight or less based on the cured resin that is the binder.
硬化樹脂は、熱、波動エネルギーまたは粒子線で硬化す
る各種樹脂を用いることができる。例えばエポキシ樹脂
、ポリウレタン樹脂、ポリエステル樹脂、シコーン樹脂
、不飽和アルデヒド樹脂、アルキド樹脂、フラン樹脂、
オリゴアクリレート等がある。As the curable resin, various resins that are cured by heat, wave energy, or particle beams can be used. For example, epoxy resin, polyurethane resin, polyester resin, silicone resin, unsaturated aldehyde resin, alkyd resin, furan resin,
There are oligoacrylates, etc.
中でもオリゴアクリレートの硬化樹脂が耐熱性及び皮膜
硬さの大きい特性を示すため良好である。Among these, oligoacrylate cured resins are preferred because they exhibit high heat resistance and film hardness.
オリゴアクリレートとして、例えばポリオールアクリレ
ート、ポリエステルアクリレート、エポキシアクリレー
ト、ウレタンアクリレート、シリコーンアクリレート。Examples of oligoacrylates include polyol acrylate, polyester acrylate, epoxy acrylate, urethane acrylate, and silicone acrylate.
ポリアセタールアクリレート等がある。Examples include polyacetal acrylate.
又、硬化樹脂として芳香族ジアゾニウム塩、あるいは芳
香族ヨードニウム塩、あるいは芳香族スルホニウム塩触
媒等を用いてイオン反応によるエポキシ樹脂の光硬化樹
脂を周込ることができる。このエポキシ樹脂として例え
ば、脂環族エポキシ樹脂がある。Further, a photocurable resin of an epoxy resin can be incorporated by ionic reaction using an aromatic diazonium salt, an aromatic iodonium salt, or an aromatic sulfonium salt catalyst as the curing resin. Examples of this epoxy resin include alicyclic epoxy resins.
微粒子は、その粒径が小さいもの程良好である。The smaller the particle size of the fine particles, the better.
特に−次粒子径が0.2μ以下の粒子は、薄膜塗工の均
−性及びヘッドつまシの防止の点から優れている。In particular, particles having a primary particle size of 0.2 μm or less are excellent in terms of uniformity of thin film coating and prevention of head smudges.
微粒子として例えば合成非晶質シリカ、カーボンブラッ
ク、アルミナ、酸化チタン、珪酸カルシウム、珪酸アル
ミニウム等を用いることができる。As the fine particles, for example, synthetic amorphous silica, carbon black, alumina, titanium oxide, calcium silicate, aluminum silicate, etc. can be used.
添加剤は、高分子組成物層表面に滑性あるいは帯電防止
性あるいはその両特性を与える滑剤あるいは界面活性剤
である。The additive is a lubricant or a surfactant that imparts lubricity and/or antistatic properties to the surface of the polymer composition layer.
特に界面活性剤が良好であり、陰イオン界面活性剤、陽
イオン界面活性剤、非イオン界面活性剤。Particularly good are surfactants, including anionic surfactants, cationic surfactants, and nonionic surfactants.
両性界面活性、シリコーン系界面活性剤、フッ素系界面
活性剤等従来公知の界面活性剤を用いることができる。Conventionally known surfactants such as amphoteric surfactants, silicone surfactants, and fluorine surfactants can be used.
特にポリエーテル変性シリコーンオイル、脂肪酸エステ
ルが良好である。Particularly good are polyether-modified silicone oil and fatty acid ester.
又、滑剤としては、オレフィン変性シリコーンオイル等
の各種変性シリコーンオイル、多価アルコール等の除来
公知の物質を用いることができる。Further, as the lubricant, various modified silicone oils such as olefin-modified silicone oil, polyhydric alcohols, and other known substances can be used.
本発明の加工フィルムは、基材の片面に高分子組成物層
を有している場合、基材の他方の面に色材層を形成する
ことにより感熱転写記録に用いられるカラーシートを形
成することができる。色材層は、染料(例えば昇華性染
料)あるいは顔料等を含む。このカラーシートは、サー
マルヘッド上をヘッドつまりを発生しないで安定に走行
するためドロップアウトのない均一な記録画像を与える
。When the processed film of the present invention has a polymer composition layer on one side of the base material, a coloring material layer is formed on the other side of the base material to form a color sheet used for thermal transfer recording. be able to. The coloring material layer contains a dye (for example, a sublimable dye) or a pigment. This color sheet runs stably on the thermal head without causing head clogging, so it provides a uniform recorded image without dropouts.
又、基材が片面に磁性体層を有している場合、磁性体層
上に高分子組成物層を薄く設けることにより磁性体層を
保護する保護高分子組成物層を有する磁気テープを形成
することができる。この保護高分子組成物層は、磁気記
録ヘッドに対する走行摩擦係数が低く、又、ヘッドつま
シを発生しなりため走行安定性のよい磁気記録ができる
。In addition, when the base material has a magnetic layer on one side, a magnetic tape having a protective polymer composition layer that protects the magnetic layer can be formed by providing a thin polymer composition layer on the magnetic layer. can do. This protective polymer composition layer has a low running friction coefficient with respect to the magnetic recording head, and does not generate head bumps, so that magnetic recording with good running stability is possible.
実施例1 基材に厚さ6μmのPETフィルムを用いる。Example 1 A PET film with a thickness of 6 μm is used as the base material.
このフィルムの片面に以下の組成を有する塗布液をワイ
ヤーロンド方式により100 m連続塗工した。塗工は
90℃の熱風で溶媒を蒸発させた後e KWの高圧水銀
灯を照射して行ない、厚さ約1μmの硬化した高分子組
成物層を得た。A coating solution having the following composition was continuously coated on one side of this film for 100 m using a wire ironing method. Coating was carried out by evaporating the solvent with hot air at 90° C. and then irradiating it with an eKW high-pressure mercury lamp to obtain a cured polymer composition layer with a thickness of about 1 μm.
このようにして得た高分子組成物層は、シリコーンオイ
ルの分離による水玉状の模様が100mの長さにわたり
1つもなくたいへん均一であった。The polymer composition layer thus obtained was very uniform with no polka dot pattern over a length of 100 m due to separation of the silicone oil.
塗布液組成 実施例2 基材に厚さ10μmのPETフィルムを用いる。Coating liquid composition Example 2 A PET film with a thickness of 10 μm is used as the base material.
このフィルムの片面に以下の組成を有する塗布液を実施
例1と同様の方法で塗工し、長さ100m。A coating solution having the following composition was applied to one side of this film in the same manner as in Example 1, and the length was 100 m.
厚さ4μmの高分子組成物層を得た。A polymer composition layer with a thickness of 4 μm was obtained.
このようにして得た高分子組成物層は、実施例1と同様
に水玉状の模様がまったく発生しなかった。The polymer composition layer obtained in this manner did not have any polka dot pattern as in Example 1.
塗布液組成 比較例 基材に厚さ10μmのPETフィルムを用いる。Coating liquid composition Comparative example A PET film with a thickness of 10 μm is used as the base material.
このフィルムの片面に実施例1で用いた塗布液組成中の
ジメチルポリシロキサンのみを粘度が300センチスト
ークスのジメチルポリシロキサンに変えて100 m塗
工した結果、直径約1間以上の水玉状の模様が連続して
多数発生した。The dimethylpolysiloxane in the coating composition used in Example 1 was replaced with dimethylpolysiloxane having a viscosity of 300 centistokes, and the film was coated for 100 m on one side, resulting in a polka dot-like pattern with a diameter of about 1 cm or more. occurred many times in a row.
発明の効果
本発明によれば、水玉状の模様のない均一な高分子組成
物層を有する加工フィルムを得ることができる。Effects of the Invention According to the present invention, a processed film having a uniform polymer composition layer without polka dot patterns can be obtained.
図は本発明の一実施例として示した加工フィルムの断面
模式図である。
1・・・・・・基材、2・・・・・・高分子組成物層、
3・・・・・・シリコーンオイル、4・・・・・・硬化
樹脂、ε・・・・・・微粒子、6・・・・・・添加剤。The figure is a schematic cross-sectional view of a processed film shown as an example of the present invention. 1... Base material, 2... Polymer composition layer,
3... Silicone oil, 4... Cured resin, ε... Fine particles, 6... Additive.
Claims (6)
00センチストークス以下のシリコーンオイルと硬化樹
脂と微粒子と添加剤とからなる厚さが5μm以下の高分
子組成物層を有する加工フィルム。(1) At least one side of the base material has a viscosity of 2 at 25°C.
A processed film having a polymer composition layer having a thickness of 5 μm or less and consisting of a silicone oil of 0.00 centistoke or less, a cured resin, fine particles, and an additive.
る特許請求の範囲第1項記載の加工フィルム。(2) The processed film according to claim 1, wherein the silicone oil is dimethylpolysiloxane.
た樹脂である特許請求の範囲第1項記載の加工フィルム
。(3) The processed film according to claim 1, wherein the cured resin is a resin cured by wave energy or particle beams.
許請求の範囲第1項記載の加工フィルム。(4) The processed film according to claim 1, wherein the cured resin is a cured product of oligoacrylate.
特許請求の範囲第1項記載の加工フィルム。(5) The processed film according to claim 1, wherein the fine particles have a primary particle diameter of 0.2 μm or less.
の範囲第1項記載の加工フィルム。(6) The processed film according to claim 1, wherein the additive is a silicone surfactant.