JPS6280095A - Treatment of base for planographic plate material - Google Patents

Treatment of base for planographic plate material

Info

Publication number
JPS6280095A
JPS6280095A JP22164685A JP22164685A JPS6280095A JP S6280095 A JPS6280095 A JP S6280095A JP 22164685 A JP22164685 A JP 22164685A JP 22164685 A JP22164685 A JP 22164685A JP S6280095 A JPS6280095 A JP S6280095A
Authority
JP
Japan
Prior art keywords
acid
aluminum plate
aluminum
aqueous solution
plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP22164685A
Other languages
Japanese (ja)
Other versions
JPH0336676B2 (en
Inventor
Hisao Maeda
前田　久雄
Yuzo Yokota
横田　雄三
Kiyotaka Kawase
川瀬　清隆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Foil Manufacturing Co Ltd
Original Assignee
Nippon Foil Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Foil Manufacturing Co Ltd filed Critical Nippon Foil Manufacturing Co Ltd
Priority to JP22164685A priority Critical patent/JPS6280095A/en
Publication of JPS6280095A publication Critical patent/JPS6280095A/en
Publication of JPH0336676B2 publication Critical patent/JPH0336676B2/ja
Granted legal-status Critical Current

Abstract

PURPOSE:To prevent aluminum hydroxide from being adhered to feeding rolls and prevent a surface of an aluminum plate from being damaged, by a method wherein an aluminum plate having a surface minutely roughened is immersed in an aqueous solution containing an anionic surfactant, an alkaline substance and a chelating agent. CONSTITUTION:The surface of an Al plate is minutely roughened to enhance adhesion of a photosensitive resin thereto. An alkylnaphthalenesulfonate or the like is used as an anionic surfactant, while sodium hydroxide or the like is used as an alkaline substance, and ethylenediaminetetraacetic acid or the like is used as a chelating agent. The three components are dissolved in water in such amounts that 2 to 20pts.wt. of the anionic surfactant, 1 to 10pts.wt. of the alkaline substance and 0.01 to 10pts.wt. of the chelating agent are present in 100pts.wt. of water. The Al plate having the minutely roughened surface is immersed in the aqueous solution thus prepared, whereby the surface is deprived of light gray parts and is whitened. Thereafter, the Al plate is subjected to anodic oxidation or a treatment for making the surface hydrophilic, thereby obtaining the intended base.

Description

【発明の詳細な説明】 （イ）産業上の利用分野 本発明は、平版印刷版を作成するのに用いる平版印刷版
材の支持体（以下単に「支持体」と言うこともある。）
の処理方法に関するものであり、支持体の表面を白色化
するための処理方法に関するものである。Detailed Description of the Invention (a) Industrial Field of Application The present invention relates to a support for a lithographic printing plate material (hereinafter sometimes simply referred to as a "support") used to create a lithographic printing plate.
The present invention relates to a treatment method for whitening the surface of a support.

（ロ）従来の技術 平版印刷版材の一つとして、支持体の表面に感光性樹脂
層を設けたものがある。このような平版印刷版材の支持
体として、従来よりアルミニウム板が広く用いられてい
るが、平版印刷版材の支持体としての要求性能を満足さ
せる目的で以下の如き処理がなされている。即ち、感光
性樹脂層と支持体との密着性を与えるためにアルミニウ
ム板表面を化学的１機械的に研磨して微細な凹凸を形成
（目立て処理）させ、次に表面を傷つきにくくするため
に陽極酸化処理を行い、更に親水性を高めるために珪酸
塩溶液等を用いて処理を行う等である。(b) Prior Art One of the lithographic printing plate materials is one in which a photosensitive resin layer is provided on the surface of a support. Aluminum plates have been widely used as supports for such lithographic printing plate materials, and the following treatments have been carried out in order to satisfy the required performance as a support for lithographic printing plate materials. That is, in order to provide adhesion between the photosensitive resin layer and the support, the surface of the aluminum plate is chemically and mechanically polished to form fine irregularities (sharpening treatment), and then to make the surface less likely to be scratched. Anodization treatment is performed, and further treatment is performed using a silicate solution or the like to increase hydrophilicity.

しかしながら、このような処理工程を経て製造されたア
ルミニウム板は感光性樹脂平版印刷版材の支持体として
要求される性能は殆ど満たしているが、アルミニウム板
表面が灰白色を呈しているため、平版印刷版の作成時に
おいて画像部と非画像部とのコントラストが不鮮明であ
るという欠点を有していた。そこで、この欠点を解決す
るために本発明者等は特願昭６０−４９５３２号に係る
発明を提案した。これは目立て処理されたアルミニウム
板を陰イオン界面活性剤及びアルカリ性物質を含有する
水溶液で浸漬処理し、その後アルミニウム板を陽極酸化
するというものである。However, although the aluminum plate manufactured through such a treatment process almost satisfies the performance required as a support for photosensitive resin lithographic printing plate material, the surface of the aluminum plate has a grayish-white color, making it difficult to use for lithographic printing. It has a drawback that the contrast between the image area and the non-image area is unclear when the plate is created. Therefore, in order to solve this drawback, the present inventors proposed the invention related to Japanese Patent Application No. 60-49532. This method involves immersing a polished aluminum plate in an aqueous solution containing an anionic surfactant and an alkaline substance, and then anodizing the aluminum plate.

（ハ）発明が解決しようとする問題点 この方法はアルミニウム板表面が白色化され好ましいも
のであるが、連続工程でアルミニウム板を処理するには
不適当な面があった。即ち、陰イオン界面活性剤及びア
ルカリ性物質廃含有する水溶液が満たされた水槽中をア
ルミニウム板が連続して通過してゆくうちに、水溶液中
に溶は出したアルミニウム金属が水酸化アルミニウムと
なって浮遊し、それがアルミニウム板表面に付着し更に
アルミニウム板の搬送ロール等に付着するということが
あった。この搬送ロール等への水酸化アルミニウムの付
着は、アルミニウム板の表面を傷つける原因となり好ま
しいものではない。(c) Problems to be Solved by the Invention Although this method is preferable because it whitens the surface of the aluminum plate, it is unsuitable for treating aluminum plates in a continuous process. That is, as the aluminum plate continues to pass through a water tank filled with an aqueous solution containing anionic surfactants and alkaline substances, the aluminum metal dissolved into the aqueous solution becomes aluminum hydroxide. There were cases where the particles floated, adhered to the surface of the aluminum plate, and further adhered to the conveyor roll of the aluminum plate. This adhesion of aluminum hydroxide to the conveyor roll etc. is not preferable because it causes damage to the surface of the aluminum plate.

そこで本発明は、水溶液中に熔は出したアルミニウム金
属を捕捉し、水溶液中に沈降させることにより、アルミ
ニウム板表面への水酸化アルミニウムの付着ひいてはア
ルミニウム板の搬送ロールへの水酸化アルミニウムの付
着を防止し、アルミニウム表面が傷つ（のを防止しよう
とするものである。Therefore, the present invention aims to prevent the adhesion of aluminum hydroxide to the surface of the aluminum plate and, ultimately, the adhesion of aluminum hydroxide to the conveyor roll of the aluminum plate, by capturing the aluminum metal released from the melt in an aqueous solution and allowing it to precipitate in the aqueous solution. The purpose is to prevent scratches on the aluminum surface.

（ニ）問題点を解決するための手段及び作用即ち本発明
は、表面に微細な凹凸が形成されているアルミニウム板
を、陰イオン界面活性剤とアルカリ性物質とアルミニウ
ム金属をキレート化するキレート剤とを含有する水溶液
で浸漬処理することを特徴とする平版印刷版材用支持体
の処理方法に係るものである。(d) Means and operation for solving the problem, that is, the present invention provides an aluminum plate having fine irregularities formed on its surface using an anionic surfactant, an alkaline substance, and a chelating agent that chelates aluminum metal. The present invention relates to a method for treating a support for a lithographic printing plate material, which comprises immersion treatment in an aqueous solution containing the following.

まず、本発明の方法において用いるアルミニウム板は、
その表面に微細な凹凸が形成されている。First, the aluminum plate used in the method of the present invention is
Fine irregularities are formed on its surface.

この凹凸はアルミニウム板表面に設けられる感光性樹脂
との密着性を向上させるためのものである。This unevenness is for improving the adhesion with the photosensitive resin provided on the surface of the aluminum plate.

ｙｋｍな凹凸は、従来公知のエアーホーニング法や液体
ホーニング法等の機械的手段で形成される。The ykm unevenness is formed by a conventionally known mechanical means such as an air honing method or a liquid honing method.

エアーホーニング法は研磨砂を空気によってアルミニウ
ム板表面に吹き付けて行うものであり、液体ホーニング
法は水によって吹き付けるものである。その他アルミニ
ウーム板表面に薬品を作用させて化学的手段で微細な凹
凸を形成することもできる。The air honing method uses air to spray abrasive sand onto the surface of the aluminum plate, and the liquid honing method uses water to spray the sand. In addition, fine irregularities can also be formed by chemical means by applying a chemical to the surface of the aluminum plate.

本発明で用いる陰イオン界面活性剤としては、脂肪酸、
アルキルベンゼンスルホン酸塩、アルキルスルホン酸塩
、アルキルナフタリンスルホン酸塩、α−オレフィンス
ルホン酸塩、ジアルキルスルホコハク酸塩、α−スルホ
ン化脂肪酸塩、Ｎ−メチル−Ｎ−オレイルタウリン、ポ
リオキシエチレンアルキルエーテル硫酸塩、アルキル硫
酸塩。The anionic surfactants used in the present invention include fatty acids,
Alkylbenzene sulfonate, alkyl sulfonate, alkylnaphthalene sulfonate, α-olefin sulfonate, dialkyl sulfosuccinate, α-sulfonated fatty acid salt, N-methyl-N-oleyl taurine, polyoxyethylene alkyl ether sulfate salts, alkyl sulfates.

アルキルリン酸塩、ポリオキシエチレンアルキルエーテ
ルリン酸塩、ポリオキシエチレンアルキルフェニルエー
テル硫酸塩、ポリオキシエチレンアルキルフェニルエー
テルリン酸塩、ナフタリンスルホン酸塩ホルムアルデヒ
ド縮合物、ナフタリンスルホン酸塩等が使用できる。こ
れらの中でも特にアルキルベンゼンスルホン酸塩、アル
キルナフタリンスルホン酸塩、ポリオキシエチレンアル
キルフェニルエーテル硫酸塩、とりわけアルキルナフタ
リンスルホン酸塩がアルカリ性物質を均一に分散しうる
能力に優れているので好ましい。Alkyl phosphates, polyoxyethylene alkyl ether phosphates, polyoxyethylene alkyl phenyl ether sulfates, polyoxyethylene alkyl phenyl ether phosphates, naphthalene sulfonate formaldehyde condensates, naphthalene sulfonates, and the like can be used. Among these, alkylbenzene sulfonates, alkylnaphthalene sulfonates, polyoxyethylene alkyl phenyl ether sulfates, and especially alkylnaphthalene sulfonates are particularly preferred because they have excellent ability to uniformly disperse alkaline substances.

陰イオン界面活性剤は、アルカリ性物質がアルミニウム
板表面に均一に作用するのを補助するためのものである
。The anionic surfactant is used to help the alkaline substance act uniformly on the surface of the aluminum plate.

本発明で用いるアルカリ性物質としては、水酸化カリウ
ム、水酸化ナトリウム、水酸化リチウム。The alkaline substances used in the present invention include potassium hydroxide, sodium hydroxide, and lithium hydroxide.

水酸化カリウム、水酸化ルビジウム、炭酸ソーダ。Potassium hydroxide, rubidium hydroxide, soda carbonate.

重炭酸ソーダ、セスキ炭酸ソーダ、ケイ酸カリウム、ケ
イ酸ナトリウム、メタケイ酸ナトリウム。Sodium bicarbonate, soda sesquicarbonate, potassium silicate, sodium silicate, sodium metasilicate.

第三リン酸ナトリウム、第ニリン酸ナトリウム。Sodium triphosphate, sodium diphosphate.

第三リン酸アンモニウム、第ニリン酸アンモニウム等を
使用することができる。これらの中でも特に水酸化ナト
リウムが少量の添加で、アルミニウム板表面を白色化し
うるので好ましい。Tertiary ammonium phosphate, diammonium diphosphate, etc. can be used. Among these, sodium hydroxide is particularly preferred since it can whiten the surface of the aluminum plate when added in a small amount.

アルカリ性物質はアルミニウム板表面に作用して、その
表面の灰白色化している部分を除去し、アルミニウム板
表面を白色化するためのものである。The alkaline substance is used to act on the surface of the aluminum plate, remove grayish white parts of the surface, and whiten the surface of the aluminum plate.

本発明で用いるキレ−１・剤としては、下記に挙げるも
のを使用することができる。As the Kill-1 agent used in the present invention, those listed below can be used.

（ｉ）ポリカルボン酸類及びその類似物。(i) Polycarboxylic acids and their analogs.

シュウ酸、コハク酸、マレイン酸、フタル酸。Oxalic acid, succinic acid, maleic acid, phthalic acid.

トリカルバリル酸、ブタン−１，２，３，４−テトラカ
ルボ７［、’＃’リコール酸、メルカプトコハク酸。Tricarballylic acid, butane-1,2,3,4-tetracarbo7[, '#' licolic acid, mercaptosuccinic acid.

２−カルボキシアニス酸等。2-carboxyanisic acid, etc.

（ＩＩ）オキシカルボン酸類及びその類似物。(II) Oxycarboxylic acids and their analogs.

グリコール酸、β−ヒドロキシプロピオン酸。Glycolic acid, β-hydroxypropionic acid.

酒石酸、イソクエン酸、ピルビン酸、マンデル酸。Tartaric acid, isocitric acid, pyruvic acid, mandelic acid.

サルチル酸等。salicylic acid etc.

（ｉｉｉ　）ポリアミン及びその類似物（例えば多窒素
含有複素環化合物）。(iii) Polyamines and their analogues (e.g. multi-nitrogen-containing heterocyclic compounds).

エチレンジアミン、プロピレンジアミン、Ｎ−イソプロ
ピルエチレンジアミン、　Ｎ、Ｎ−ジメチルエチレンジ
アミン、Ｎ、Ｎ′−ジメチルエチレンジアミン。Ethylenediamine, propylenediamine, N-isopropylethylenediamine, N,N-dimethylethylenediamine, N,N'-dimethylethylenediamine.

Ｎ、Ｎ−ジプロピルエチレンジアミン、トリメチレンジ
アミン、１．３−ジアミノ−２−アミノメチルプロパン
、ジエチレントリアミン、　２．２’、２’、−チルピ
リジル。N,N-dipropylethylenediamine, trimethylenediamine, 1,3-diamino-2-aminomethylpropane, diethylenetriamine, 2.2',2',-thylpyridyl.

１．２．３−　トリアミノプロパン、β、β′、β“−
トリアミノトリエチルアミン、イミダゾール、プリン。1.2.3- Triaminopropane, β, β′, β“-
Triaminotriethylamine, imidazole, purine.

２−アミノ−６−メルカプトプリン、５−メチル−〇−
フェナントロリン、５−７’ロム−〇−フェナントロリ
ン等。2-amino-6-mercaptopurine, 5-methyl-〇-
Phenanthroline, 5-7'rom-〇-phenanthroline, etc.

（ｉｖ　）アミノカルボン酸類及びその類似物（例えば
カルボキシル化複素環含窒素化合物）。(iv) Aminocarboxylic acids and analogs thereof (eg, carboxylated heterocyclic nitrogen-containing compounds).

ピリジン−２−カルボン酸、ピリジン−２，６−ジカル
ボン酸、イミノジ酢酸、　Ｎ−（３，３−ジメチルブチ
ル）イミノジ酢酸、メルカプトエチルイミノジ酢酸、２
−ヒドロキシシクロヘキシルイミノジ酢酸。Pyridine-2-carboxylic acid, pyridine-2,6-dicarboxylic acid, iminodiacetic acid, N-(3,3-dimethylbutyl)iminodiacetic acid, mercaptoethyliminodiacetic acid, 2
-Hydroxycyclohexyliminodiacetic acid.

２−ヒドロキシベンジルイミノジ酢酸、　Ｎ−（ｍ−カ
ルボキシフェニル）イミノジ酢酸、アミノエチルイミノ
ジ酢酸、ホスホノメチルイミノジ酢酸、０−スルホフェ
ニルイミノジ酢酸、　Ｎ、Ｎ−エチレンジアミンジ酢酸
、　Ｎ、Ｎ′−ジ（ヒドロキシエチル）エチレンジアミ
ンジ酢酸、　Ｎ−（ｏ−ヒドロキシシクロヘキシル）エ
チレンジアミントリ酢酸、エチレンジアミンテトラ酢酸
、プロピレンジアミンテトラ酢酸。2-Hydroxybenzyliminodiacetic acid, N-(m-carboxyphenyl)iminodiacetic acid, aminoethyliminodiacetic acid, phosphonomethyliminodiacetic acid, 0-sulfophenyliminodiacetic acid, N,N-ethylenediaminediacetic acid, N, N'-di(hydroxyethyl)ethylenediaminediacetic acid, N-(o-hydroxycyclohexyl)ethylenediaminetriacetic acid, ethylenediaminetetraacetic acid, propylenediaminetetraacetic acid.

ペンタメチレンジアミンテトラ酢酸、シクロベンクン−
１，２−ジアミンテトラ酢酸、シクロヘキサン−１，４
−ジアミンテトラ酢酸、２−ヒドロキシトリメチレンジ
アミンテトラ酢酸、アスパラギン酸、グリシルグリシン
、ジピコリン酸、ビス（イミノジ酢酸エステル）メチル
アミン、キノリン−２−カルボン酸、ジメチルジチオカ
ルバミン酸等。Pentamethylenediaminetetraacetic acid, cyclobencune-
1,2-diaminetetraacetic acid, cyclohexane-1,4
-Diaminetetraacetic acid, 2-hydroxytrimethylenediaminetetraacetic acid, aspartic acid, glycylglycine, dipicolinic acid, bis(iminodiacetate)methylamine, quinoline-2-carboxylic acid, dimethyldithiocarbamic acid, etc.

（ｖ）ヒドロキシルアミン及びその類似物（例えばヒド
ロキシル化複素環含窒素化合物）。(v) Hydroxylamine and its analogues (e.g. hydroxylated heterocyclic nitrogen-containing compounds).

ピリドキサミン、ヒポキサンチン、キサントシン、β、
β、β−トリヒドロキシトリエチルアミン、β−アミノ
−β′−ヒドロキシジエチルスルフィド、シチジン−３
′−リン酸、ウリジン−５′−リン酸。Pyridoxamine, hypoxanthine, xanthosine, β,
β, β-trihydroxytriethylamine, β-amino-β'-hydroxydiethyl sulfide, cytidine-3
'-phosphoric acid, uridine-5'-phosphoric acid.

アデノシン−５４リン酸、フラビンモノヌクレオチド、
４−メチルオキシン、７−メチルオキシン、４−ヒドロ
キシ−１，５−ナフチリジン、５−ヒドロキシキノキサ
リン、４１７−ジフェニル−０−フェナントロリン。adenosine-54 phosphate, flavin mononucleotide,
4-Methyloxine, 7-methyloxine, 4-hydroxy-1,5-naphthyridine, 5-hydroxyquinoxaline, 417-diphenyl-0-phenanthroline.

１−ニトロソ−β−ナフトール等。1-nitroso-β-naphthol, etc.

（ｖｉ　）ポリケトン、ポリオキシ等のその他のキレー
ト剤。(vi) Other chelating agents such as polyketone and polyoxy.

トロホリン、４−メチルトロポリン、クロモトロープ酸
、アセチルアセトン、ヘンジイルアセトン。Trophorin, 4-methyltropolin, chromotropic acid, acetylacetone, hendiylacetone.

フロイルアセトン、２−（α−チェニル）ピリジン。Furoylacetone, 2-(α-thenyl)pyridine.

５−ヒドロキシフラボン等。5-hydroxyflavone, etc.

以上のキレート剤のなかで好ましいのは（１ｖ）のアミ
ノカルボン酸類であって、特にエチレンジアミンテトラ
酢酸が最も好ましい。これは、キレート効果に優れ且つ
安価で入手が容易であるからである。Among the above chelating agents, aminocarboxylic acids (1v) are preferred, and ethylenediaminetetraacetic acid is particularly preferred. This is because it has an excellent chelating effect, is inexpensive, and is easily available.

キレ−ＢＰＩｔよアルミニウム板から熔は出したアルミ
ニウム金属に配位して、安定なキレート化合物を作り、
アルミニウム金属を水溶液中で速やかに沈降させるとい
う作用をするものである。The melt from the aluminum plate coordinates with the aluminum metal to create a stable chelate compound.
Its function is to quickly precipitate aluminum metal in an aqueous solution.

本発明に用いる水溶液は上記三成分を含有するものであ
り、その配合割合は陰イオン界面活性剤２〜２０重量部
程度、アルカリ性物質１〜１０重量部程度、キレート剤
０．０１〜１０重皇部程度が好ましく、これらを水１０
０重量部程度に溶解させることによって水溶液として調
整する。The aqueous solution used in the present invention contains the three components mentioned above, and the blending ratio is about 2 to 20 parts by weight of an anionic surfactant, about 1 to 10 parts by weight of an alkaline substance, and 0.01 to 10 parts by weight of a chelating agent. 10 parts of water is preferable.
It is prepared as an aqueous solution by dissolving it to about 0 parts by weight.

この水溶液中に表面に微細な凹凸が形成されているアル
ミニウム板を浸漬して処理するわけであるが、この処理
条件としては、水溶液温度４０〜８０℃程度、浸漬時間
１０〜６０秒程度が好ましい。この浸漬処理によりアル
ミニウム板表面の灰白色部分が除去され、表面が白色化
する。そしてこの後、所望により従来公知の陽極酸化処
理や親水化処理を行って、平版印刷版材用支持体を得る
ことができる。The aluminum plate with fine irregularities formed on its surface is immersed in this aqueous solution for treatment, and the preferred treatment conditions are an aqueous solution temperature of about 40 to 80°C and an immersion time of about 10 to 60 seconds. . This immersion treatment removes the grayish-white portion on the surface of the aluminum plate, making the surface white. Thereafter, if desired, a conventionally known anodizing treatment or hydrophilic treatment can be performed to obtain a support for a lithographic printing plate material.

（ホ）実施例 （実施例） 脱脂を完了した厚さ０．１５■■、巾５０値のアルミニ
ウム板（ＪＩＳ　Ａ−１，１００）の表面を平均粒径１
２０メツシユの研磨砂（宇治電■製、商品名エメリーエ
キストラ）で空気ホーニング方式によって研磨し、その
後水洗することにより、表面に微細な凹凸が形成された
アルミニウム板を得た。次いでこのアルミニウム板を、
下記組成の水溶液を水槽に貯留して、水溶液温度５５℃
で３０秒間浸漬処理した。(e) Example (Example) The surface of a degreased aluminum plate (JIS A-1,100) with a thickness of 0.15mm and a width of 50 was measured with an average particle size of 1.
An aluminum plate with fine irregularities formed on the surface was obtained by polishing with 20 mesh abrasive sand (manufactured by Ujiden ■, trade name Emery Extra) by an air honing method and then washing with water. Next, this aluminum plate
An aqueous solution with the following composition was stored in a water tank, and the aqueous solution temperature was 55°C.
The sample was immersed in water for 30 seconds.

水溶液組成 水　　　　　　　　　　　　　　　　　　　　１００正
量部水酸化ナトリウム　　　　　　　　　４　〃アルキ
ルナフタリンスルホン酸ソーダ（９菊花王アトラス製、
商品名ペレックスＮＢＬ　）４重量部 エチレンジアミンテトラ酢＠１ノ！ シリコーンエマルジョン（ユニチカ側製、商品名ユニバ
ブルＵＢ−１１）　　　　　０．０１重量部（比較例） 比較のため、上記水溶液組成からエチレンジアミンテト
ラ酢酸成分を除いた水溶液を用いて、上記実施例と同一
条件でアルミニウム板を浸漬処理した。Aqueous solution composition Water 100 parts Sodium hydroxide 4 Sodium alkylnaphthalene sulfonate (9 manufactured by Kikukao Atlas,
Product name Perex NBL ) 4 parts by weight ethylenediaminetetra vinegar @1 no! Silicone emulsion (manufactured by Unitika, trade name: Unibubble UB-11) 0.01 parts by weight (comparative example) For comparison, an aqueous solution with the ethylenediaminetetraacetic acid component removed from the above aqueous solution composition was used under the same conditions as the above example. An aluminum plate was immersed.

（実施例と比較例の結果） 実施例の場合、アルミニウム板を約１０００ｍ処理した
時点で、水溶液を貯留した水槽下部にキレート化された
アルミニウム金属が堆積し始めた。そしてその後約５０
０００　ｍ処理した時点でもアルミニウム板の表面やア
ルミニウム板搬送用ロールに異物が付着することはなか
った。これに対し比較例の場合、アルミニウム板を約５
００　ｍ処理した時点で水溶液中に異物が浮遊し始め、
約１０００ｍ処理した時点でアルミニウム板表面やアル
ミニウム板搬送用ロールに異物が付着し始めた。この結
果から明らかなように、実施例の場合アルミニウム板か
ら溶は出したアルミニウム金属は、エチレンジアミンテ
トラ酢酸によってキレート化され水槽下部に沈降、堆積
して、アルミニウム板表面を汚染しないのに対し、比較
例の場合はアルミニウム金属が水溶液中に浮遊しアルミ
ニウム板表面を汚染する。(Results of Examples and Comparative Examples) In the case of the Examples, chelated aluminum metal began to accumulate at the bottom of the water tank in which the aqueous solution was stored when the aluminum plate was processed for about 1000 m. and after that about 50
Even after 000 m of treatment, no foreign matter adhered to the surface of the aluminum plate or the roll for conveying the aluminum plate. On the other hand, in the case of the comparative example, the aluminum plate was
After 00 m of treatment, foreign matter began to float in the aqueous solution,
After approximately 1000 m of processing, foreign matter began to adhere to the aluminum plate surface and the aluminum plate conveying roll. As is clear from this result, in the case of the example, the aluminum metal leached from the aluminum plate was chelated by ethylenediaminetetraacetic acid and settled and deposited at the bottom of the water tank, and did not contaminate the aluminum plate surface, whereas in the comparison In this case, aluminum metal floats in the aqueous solution and contaminates the surface of the aluminum plate.

（へ）発明の効果 本発明に係る方法を採用すれば、アルミニウム板表面の
灰白色部が除去されて、その表面を白色化しうると共に
、水溶液中に熔は出したアルミニウム金属はキレート剤
によっキレート化され、アルミニウム板表面の汚染を防
止することができる。(f) Effects of the Invention If the method according to the present invention is adopted, the grayish white part on the surface of the aluminum plate can be removed and the surface can be whitened, and the aluminum metal released into the aqueous solution can be chelated by the chelating agent. This prevents contamination of the aluminum plate surface.

従って、異物によってアルミニウム板表面が傷つくのを
防止することができ、平版印刷版材用支持体として用い
るのに好適である。これに対し、キレート剤を配合して
いない水溶液でアルミニウム板を処理すると、水溶液中
に熔は出したアルミニウム金属によってアルミニウム板
表面が汚染され、更にアルミニウムＦｊ、ＩＩＩ送用ロ
ールにアルミニウム金属が付着し、アルミニウム板表面
を傷つけ、平版印刷版材用支持体として用いるのに悪影
響を与える。Therefore, it is possible to prevent the surface of the aluminum plate from being damaged by foreign matter, and it is suitable for use as a support for lithographic printing plate materials. On the other hand, if an aluminum plate is treated with an aqueous solution that does not contain a chelating agent, the surface of the aluminum plate will be contaminated by the aluminum metal that has melted into the aqueous solution, and the aluminum metal will also adhere to the aluminum Fj and III feed rolls. , it damages the surface of the aluminum plate and has an adverse effect on its use as a support for lithographic printing plate materials.

Claims (4)

【特許請求の範囲】[Claims] （１）表面に微細な凹凸が形成されているアルミニウム
板を、陰イオン界面活性剤とアルカリ性物質とアルミニ
ウム金属をキレート化するキレート剤とを含有する水溶
液で浸漬処理することを特徴とする平版印刷版材用支持
体の処理方法。(1) Lithographic printing characterized by immersing an aluminum plate with fine irregularities formed on its surface in an aqueous solution containing an anionic surfactant, an alkaline substance, and a chelating agent that chelates aluminum metal. A method of treating a plate support. （２）陰イオン界面活性剤がアルキルナフタリンスルホ
ン酸ソーダである特許請求の範囲第（１）項記載の平版
印刷版材用支持体の処理方法。(2) The method for treating a support for a lithographic printing plate material according to claim (1), wherein the anionic surfactant is sodium alkylnaphthalene sulfonate. （３）アルカリ性物質が水酸化ナトリウムである特許請
求の範囲第（１）項記載の平版印刷版材用支持体の処理
方法。(3) The method for treating a support for a lithographic printing plate material according to claim (1), wherein the alkaline substance is sodium hydroxide. （４）キレート剤がエチレンジアミンテトラ酢酸である
特許請求の範囲第（１）項記載の平版印刷版材用支持体
の処理方法。(4) The method for treating a support for a lithographic printing plate material according to claim (1), wherein the chelating agent is ethylenediaminetetraacetic acid.
JP22164685A 1985-10-03 1985-10-03 Treatment of base for planographic plate material Granted JPS6280095A (en)