JPS627489Y2 - - Google Patents
Info
- Publication number
- JPS627489Y2 JPS627489Y2 JP1981139763U JP13976381U JPS627489Y2 JP S627489 Y2 JPS627489 Y2 JP S627489Y2 JP 1981139763 U JP1981139763 U JP 1981139763U JP 13976381 U JP13976381 U JP 13976381U JP S627489 Y2 JPS627489 Y2 JP S627489Y2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- fibers
- resin
- pattern
- resin layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【考案の詳細な説明】
本考案は化粧材に関し、詳しくは偏光性、即
ち、観察角度によつて色調が変化し、立体的な繊
維質感に富むと共に、天然銘木にみられる照りの
移行感を備えた化粧材に関する。[Detailed explanation of the invention] This invention relates to decorative materials, and more specifically, it has polarization, that is, the color tone changes depending on the viewing angle, and it has a rich three-dimensional fiber texture, as well as a sense of transition of shine seen in natural precious woods. The present invention relates to decorative materials.
近年、種々の抽象模様や木目模様を有する化粧
材が室内装飾用板、家具や家電機器外装板等に広
く用いられているが、その色調は観察角度によら
ず一定、単調であるほか、図柄模様を有しても一
般に深みがなく、廉価品のイメージを与える。特
に、木目模様の場合、従来のような単なる印刷模
様のみによつては、天然銘木特有の繊維質感、立
体感、照りの移行感を与えることができない。 In recent years, decorative materials with various abstract patterns and wood grain patterns have been widely used for interior decoration boards, furniture and home appliance exterior boards, etc. However, the color tone is constant and monotonous regardless of the viewing angle, and the design Even if it has a pattern, it generally lacks depth and gives the impression of being a cheap product. In particular, in the case of wood grain patterns, it is not possible to provide the fiber texture, three-dimensional effect, and transitional feel of shine that are unique to natural precious wood by simply using a conventional printed pattern.
本考案は上記に鑑みてなされたものであつて、
偏光性を有すると共に、立体的な繊維質感と照り
の移行感を有し、図柄模様を有する場合、模様が
深みを有し、更に、木目模様の場合、天然銘木に
特有の繊維質感と照りの移行感を有する化粧材を
提供することを目的とする。 This invention was made in view of the above, and
In addition to having polarizing properties, it has a three-dimensional fiber texture and a sense of transition in shine, and if it has a design pattern, the pattern has depth, and if it has a wood grain pattern, it has a fiber texture and shine that are unique to natural precious woods. The purpose of the present invention is to provide a decorative material that has a transitional feel.
本考案による化粧材は、半透明乃至不透明な基
材の上に、(a)二酸化チタン被覆雲母と、(b)無機繊
維及び/又は有機繊維とが分散されている樹脂層
が積層されていることを特徴とする。 The decorative material according to the present invention has a resin layer in which (a) titanium dioxide-coated mica and (b) inorganic fibers and/or organic fibers are dispersed laminated on a translucent to opaque base material. It is characterized by
以下に実施例を示す図面に基づいて本考案を説
明する。 The present invention will be described below based on drawings showing embodiments.
第1図は本考案の一実施例を示し、半透明乃至
不透明な基材層1の上に、二酸化チタン被覆雲母
2と、無機繊維及び/又は有機繊維3(以下、単
に繊維と総称することがある。)とが分散されて
いる樹脂層4が積層されている。 FIG. 1 shows an embodiment of the present invention, in which titanium dioxide-coated mica 2 and inorganic fibers and/or organic fibers 3 (hereinafter simply referred to as fibers) are coated on a translucent to opaque base material layer 1. A resin layer 4 is laminated in which .
基材層1は紙、編織布、不織布、樹脂シート等
から形成される。樹脂シートは熱可塑性又は熱硬
化性樹脂のいずれから構成されていてもよく、例
えばポリ塩化ビニル、ポリエチレン、ポリプロピ
レン、エチレン−酢酸ビニル共重合体樹脂、ポリ
エステル、ポリウレタン等から構成される。しか
し、本考案においては、基材層は好ましくは後述
する樹脂層4と熱圧着するのが製造上有利であ
り、例えばポリ塩化ビニル、ポリエチレン、ポリ
プロピレン等の熱可塑性樹脂が好ましく用いられ
る。 The base material layer 1 is formed from paper, woven fabric, nonwoven fabric, resin sheet, or the like. The resin sheet may be made of either thermoplastic or thermosetting resin, such as polyvinyl chloride, polyethylene, polypropylene, ethylene-vinyl acetate copolymer resin, polyester, polyurethane, and the like. However, in the present invention, it is advantageous in production to bond the base material layer with a resin layer 4, which will be described later, by thermocompression, and thermoplastic resins such as polyvinyl chloride, polyethylene, and polypropylene are preferably used.
本考案において用いる二酸化チタン被覆雲母2
は、干渉色タイプと呼ばれている一種の着色剤で
あつて、その粒径、二酸化チタン被覆率及び雲母
の厚みによつて種々異なる反射色を与え、粒径5
〜130μ、二酸化チタン被覆率20〜55%、雲母厚
み0.2〜0.6μ程度の範囲のものが所望の色調に応
じて用いられる。二酸化チタン被覆雲母の樹脂へ
の配合量は、色相、樹脂層厚み、所望の干渉の程
度等によつて適宜に選ばれるが、通常、樹脂(樹
脂が可塑剤、充填剤その他の添加剤を含有する場
合には、その樹脂組成物)100重量部当り0.05〜
10重量部であり、作業性及び意匠効果からは0.1
〜5重量部が好ましい。 Titanium dioxide coated mica 2 used in the present invention
is a type of coloring agent called interference color type, and it gives various reflected colors depending on its particle size, titanium dioxide coverage, and mica thickness.
~130μ, titanium dioxide coverage 20~55%, mica thickness 0.2~0.6μ depending on the desired color tone. The amount of titanium dioxide-coated mica to be added to the resin is appropriately selected depending on the hue, resin layer thickness, desired degree of interference, etc. 0.05 to 100 parts by weight of the resin composition)
10 parts by weight, and 0.1 in terms of workability and design effect.
~5 parts by weight is preferred.
本考案において、二酸化チタン被覆雲母と共に
樹脂層に分散される繊維3の内、無機繊維として
はガラス繊維、金属繊維、セラミツク繊維等が用
いられるが、好ましくはガラス短繊維が用いられ
る。ガラス短繊維の径は特に制限されないが、繊
維質感を表現するためには5〜20mμ程度が好適
であり、また、長さは0.5〜20mm程度が好適であ
る。 In the present invention, among the fibers 3 dispersed in the resin layer together with the titanium dioxide-coated mica, glass fibers, metal fibers, ceramic fibers, etc. are used as the inorganic fibers, and short glass fibers are preferably used. The diameter of the short glass fibers is not particularly limited, but in order to express the texture of the fibers, it is preferably about 5 to 20 mμ, and the length is preferably about 0.5 to 20 mm.
有機繊維としては、例えば綿、絹等の天然繊
維、レーヨン、スフ、人絹、ポリエステル繊維、
ポリアミド繊維、アクリル繊維、ポリビニルアル
コール繊維等の半合成及び合成繊維が用いられる
が、これらに限定されるものではない。用いる有
機繊維の径及び長さは前記と同じ理由により、
0.5〜5デニール及び0.5〜20mm程度が適当であ
る。 Examples of organic fibers include natural fibers such as cotton and silk, rayon, cotton wool, human silk, polyester fibers,
Semi-synthetic and synthetic fibers such as polyamide fibers, acrylic fibers, polyvinyl alcohol fibers can be used, but are not limited thereto. For the same reason as above, the diameter and length of the organic fibers used are as follows:
Approximately 0.5 to 5 denier and 0.5 to 20 mm are appropriate.
この樹脂層2は好ましくはカレンダー法により
製造され、樹脂としては例えば、ポリ塩化ビニ
ル、ポリエチレン、ポリプロピレン等の熱可塑性
樹脂が好ましく用いられる。樹脂層の厚みは特に
制限されないが、通常、0.05〜1mmである。カレ
ンダー加工により樹脂層を形成することによつ
て、繊維を樹脂層の長手方向に配向させることが
できるので、本考案の化粧材によれば方向性を有
する繊維質感が効果的に表わされる。繊維の配合
割合は、樹脂(樹脂に可塑剤、充填剤その他の添
加剤を含有させる場合には樹脂組成物)100重量
部当り0.5〜50重量部、好ましくは1〜20重量部
である。尚、繊維は着色されていてもよい。 This resin layer 2 is preferably manufactured by a calendering method, and thermoplastic resins such as polyvinyl chloride, polyethylene, and polypropylene are preferably used as the resin. Although the thickness of the resin layer is not particularly limited, it is usually 0.05 to 1 mm. By forming the resin layer by calendering, the fibers can be oriented in the longitudinal direction of the resin layer, so the decorative material of the present invention effectively exhibits a directional fiber texture. The blending ratio of the fibers is 0.5 to 50 parts by weight, preferably 1 to 20 parts by weight, per 100 parts by weight of the resin (or the resin composition if the resin contains a plasticizer, filler, or other additives). Note that the fibers may be colored.
本考案の化粧材において、樹脂層が無機繊維、
特にガラス繊維を含有する場合、ガラス繊維はハ
ンマー・トーン調の模様を現出し、有機繊維を含
有するとき、シルク調の流れ模様が現出し、しか
も、偏光性を有する二酸化チタン被覆雲母による
照りの移行感と相俟つて、上記模様は立体感、深
みに富み、高級なイメージを与える。 In the decorative material of the present invention, the resin layer is made of inorganic fibers,
In particular, when glass fiber is contained, the glass fiber exhibits a hammer tone pattern, and when organic fiber is contained, a silk-like flowing pattern appears, and moreover, the polarizing titanium dioxide-coated mica produces a glare effect. Combined with the sense of transition, the above pattern gives a three-dimensional feel, rich depth, and a high-class image.
本考案においては、第2図に示すように、樹脂
層4を保護すると共に、樹脂層自体が表わす模様
に一層の深みと立体感を与えるために、樹脂層の
上に透明乃至半透明な表面層5を積層することが
できる。 In the present invention, as shown in Fig. 2, in order to protect the resin layer 4 and give deeper and three-dimensionality to the pattern expressed by the resin layer itself, a transparent or semi-transparent surface is provided on the resin layer. Layer 5 can be laminated.
表面層は熱可塑性又は熱硬化性樹脂のいずれか
ら形成されていてもよいが、好ましくは樹脂層4
に熱圧着されるため、例えばポリ塩化ビニルのよ
うな熱可塑性樹脂が好適である。表面層は必要に
応じて着色されていてもよく、この場合、着色剤
は基材層1を背景として、表面層を通して樹脂層
が透視されるように、透明乃至半透明性を阻害し
ない隠ぺい力を有するものから選ばれる。尚、表
面層の表面は化粧材に高級感を与えるために半艷
消し又は艷出しとすることができる。所望なら
ば、表面層としてメラミン樹脂、ジアリルフタレ
ート樹脂、ポリエステル樹脂等の熱硬化性樹脂も
用いられるが、必要に応じて紫外線硬化型樹脂も
用いられる。 The surface layer may be formed from either thermoplastic or thermosetting resin, but preferably the resin layer 4
For example, a thermoplastic resin such as polyvinyl chloride is suitable because it is thermocompression bonded to the material. The surface layer may be colored as necessary. In this case, the colorant has a hiding power that does not inhibit transparency or translucency so that the resin layer can be seen through the surface layer against the background of the base layer 1. selected from those with Incidentally, the surface of the surface layer can be semi-brushed or varnished to give a luxurious feel to the decorative material. If desired, a thermosetting resin such as a melamine resin, diallyl phthalate resin, or polyester resin may be used as the surface layer, and an ultraviolet curable resin may also be used if necessary.
本考案においては好ましくは、第3図に示すよ
うに、樹脂層4と表面層5との間に図柄模様層6
が設けられる。この図柄模様は抽象模様でも木目
模様でもよく、例えば樹脂層4の表面又は表面層
の裏面に印刷することにより図柄模様層が形成さ
れる。また、模様を予め印刷した透明フイルムを
表面層と樹脂層の間に積層することによつても、
図柄模様層を形成することができる。また、第4
図に示すように、図柄模様層6を基材層1と樹脂
層4の間に設け、表面層5を樹脂層の上に積層し
てもよい。 In the present invention, preferably, as shown in FIG. 3, a pattern layer 6 is provided between the resin layer 4 and the surface layer 5.
will be provided. This pattern may be an abstract pattern or a wood grain pattern, and the pattern layer is formed by printing on the surface of the resin layer 4 or the back surface of the surface layer, for example. In addition, by laminating a transparent film with a pre-printed pattern between the surface layer and the resin layer,
A patterned layer can be formed. Also, the fourth
As shown in the figure, the pattern layer 6 may be provided between the base layer 1 and the resin layer 4, and the surface layer 5 may be laminated on the resin layer.
本考案の化粧材は以上のように、二酸化チタン
被覆雲母と繊維とを均一に分散させた透明乃至半
透明の樹脂層を半透明乃至不透明の基材層の上に
積層して構成されているので、二酸化チタン被覆
雲母が偏光性を有し、化粧板はその観察角度によ
つてその色調が変化すると共に、立体感、深み、
照りの移行感が現出し、更に、ガラス繊維により
ハンマー・トーン調の模様が、また、有機繊維に
よつてシルク調の流れ模様が表わされるので、漸
新にして高級なイメージの化粧材を得ることがで
きる。図柄模様を施した場合には、二酸化チタン
被覆雲母による偏光性、照りの移行感と繊維によ
る繊維質感と相俟つて、模様が観察角度によつて
微妙にその色調を変えると共に、立体感、深みに
富み、化粧材の高級感が一層高まる。 As described above, the decorative material of the present invention is constructed by laminating a transparent or semitransparent resin layer in which titanium dioxide-coated mica and fibers are uniformly dispersed on a semitransparent to opaque base material layer. Therefore, titanium dioxide-coated mica has polarizing properties, and the color tone of the decorative board changes depending on the viewing angle, as well as giving it a three-dimensional effect, depth, and
A transitional sense of shine appears, and the glass fibers create a hammer tone pattern, and the organic fibers create a silk-like flow pattern, resulting in a decorative material with a progressively updated and luxurious image. be able to. When a pattern is applied, the color tone of the pattern changes subtly depending on the viewing angle due to the polarization of the titanium dioxide-coated mica, the sense of transition of light, and the texture of the fibers, and the pattern has a three-dimensional effect and depth. This makes the decorative material even more luxurious.
特に、図柄模様として木目模様を用いた場合に
は、二酸化チタン被覆雲母の偏光性によつて天然
銘木特有の照りの移行感と、繊維による繊維質
感、木肌感によつて天然銘木様の化粧材を得るこ
とができる。また、表面層を積層した場合には、
化粧材表面が保護されると共に、深み、立体感が
一層高められる。 In particular, when a wood grain pattern is used as a pattern, the polarization of titanium dioxide-coated mica creates a transitional shine unique to natural wood, and the fiber texture and wood texture create a decorative material similar to natural wood. can be obtained. In addition, when the surface layer is laminated,
The surface of the decorative material is protected, and the depth and three-dimensional effect are further enhanced.
第1図乃至第4図は本考案による化粧材の実施
例を示す断面図である。
1……基材層、2……二酸化チタン被覆雲母、
3……無機繊維及び/又は有機繊維、5……樹脂
層、6……図柄模様層。
1 to 4 are cross-sectional views showing examples of decorative materials according to the present invention. 1...Base material layer, 2...Titanium dioxide-coated mica,
3... Inorganic fiber and/or organic fiber, 5... Resin layer, 6... Design layer.
Claims (1)
チタン被覆雲母と、(b)無機繊維及び/又は有機
繊維とが分散されている樹脂層が積層されてい
ることを特徴とする化粧材。 (2) 基材層の上に、樹脂層、図柄模様層及び透明
乃至半透明な表面層がこの順序で積層されてい
ることを特徴とする実用新案登録請求の範囲第
1項記載の化粧材。 (3) 基材層の上に図柄模様層、樹脂層及び表面層
がこの順序で積層されていることを特徴とする
実用新案登録請求の範囲第1項記載の化粧材。 (4) 図柄模様層が木目模様層であることを特徴と
する実用新案登録請求の範囲第1項又は第2項
記載の化粧材。[Claims for Utility Model Registration] (1) A translucent to opaque base material layer and a resin layer on which (a) titanium dioxide-coated mica and (b) inorganic fibers and/or organic fibers are dispersed. A decorative material characterized by being laminated with. (2) The decorative material according to claim 1 of the utility model registration, characterized in that a resin layer, a design layer, and a transparent or semitransparent surface layer are laminated in this order on the base layer. . (3) The decorative material according to claim 1 of the utility model registration, characterized in that a pattern layer, a resin layer, and a surface layer are laminated in this order on the base layer. (4) The decorative material according to claim 1 or 2, wherein the pattern layer is a wood grain pattern layer.