JPS6227990B2 - - Google Patents
Info
- Publication number
- JPS6227990B2 JPS6227990B2 JP54076016A JP7601679A JPS6227990B2 JP S6227990 B2 JPS6227990 B2 JP S6227990B2 JP 54076016 A JP54076016 A JP 54076016A JP 7601679 A JP7601679 A JP 7601679A JP S6227990 B2 JPS6227990 B2 JP S6227990B2
- Authority
- JP
- Japan
- Prior art keywords
- decorative layer
- film
- decorative
- pattern
- synthetic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明はエンボス化粧板、特にレンガ目地状或
いはタイル目地状その他の適宜凹模様を有し、し
かも表面が天然銘木の木質感を呈したエンボス化
粧板の製造方法に関するものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a method for manufacturing an embossed decorative board, particularly an embossed decorative board having a brick joint pattern, tile joint pattern, or other appropriate concave pattern, and whose surface has the wood texture of natural precious wood. It is.
従来からこの種の化粧板を製造する方法として
は、合板等の基板表面に天然銘木の突板を貼着し
たのち、ルーター等でタイル目地状或いはレンガ
目地状の凹溝を刻設して塗装仕上げを行う方法や
基板表面に木目柄等の適宜柄模様を有する樹脂含
浸紙を載置したのち該樹脂含浸紙表面にエンボス
平版を配して加熱圧締し、該エンボス平版により
導管溝やタイル目地状の凹模様を転刻して人工的
に木質感を現出させると共にタイル目地状の目地
外観を現わす方法がある。 Traditionally, the method for manufacturing this type of decorative board is to attach a veneer of natural wood to the surface of a substrate such as plywood, then use a router to carve grooves in the shape of tile or brick joints, and then finish with a coat of paint. After placing a resin-impregnated paper with an appropriate pattern such as a wood grain pattern on the surface of the substrate, an embossed planar plate is placed on the surface of the resin-impregnated paper and heated and pressed, and the embossed planar plate is used to form conduit grooves and tile joints. There is a method of reprinting a concave pattern to create an artificial wood texture and the appearance of tile joints.
しかしながら、前者の突板による場合には、天
然銘木の枯渇により高価になるという欠点があり
さらに天然銘木の突板そのもの使用するために色
違いや木目の柄違いが多く、均一な化粧性を有す
る化粧板を大量に生産するには不向きである。 However, the former method of using veneer has the disadvantage that it becomes expensive due to the depletion of natural wood.Furthermore, since the veneer of natural wood is used, there are many differences in color and grain pattern, and decorative board has uniform decorative properties. is not suitable for mass production.
又、後者の樹脂含浸紙を使用する方法によると
該表面の導管溝やタイル目地状の凹模様がエンボ
ス平版の熱圧により転刻したものであるから、凹
部が緩慢となつて自然感に劣ると共にエンボス平
版のエンボス模様を基板表面に配した樹脂含浸紙
の木目柄等の印刷模様に合わす際に、エンボス版
のエンボス模様を外部から直視しにくいために両
者の模様を正確に合致させて熱圧することが非常
に困難であり、エンボス平版の位置合せに細心の
注意を必要とする。又、量産する場合には多数枚
のエンボス平板を必要とし、さらに各エンボス平
版を樹脂含浸紙の模様面上の正確な位置に合わせ
て載置しなければならない関係上、手間がかゝり
作業能率が悪いため製品が高価になるという欠点
がある。 In addition, in the latter method of using resin-impregnated paper, the concave patterns on the surface, such as conduit grooves and tile joints, are engraved by the heat pressure of an embossing plate, so the concave portions are slow and less natural. At the same time, when matching the embossed pattern of the embossed flat plate to the printed pattern such as the wood grain pattern of resin-impregnated paper arranged on the surface of the substrate, it is difficult to see the embossed pattern of the embossed plate directly from the outside, so heat is applied to accurately match the two patterns. It is very difficult to press and requires great care in aligning the embossing plate. In addition, in the case of mass production, a large number of embossing flat plates are required, and each embossing flat plate must be placed in an accurate position on the pattern surface of the resin-impregnated paper, which is a time-consuming process. The disadvantage is that the product is expensive due to poor efficiency.
本発明はこのような欠点に鑑みてなされたもの
であり、豊富でかつ安価に入手できるカポール、
ラワン、アピトン等の木材薄板又は適宜の化粧紙
よりなる通気性材料を用いてチーク、ローズ、オ
ーク、マホガニー等の天然銘木に酷似した化粧面
を有し、しかもレンガ目地或いはタイル目地等の
立体感に富んだ凹模様を有するエンボス化粧板を
安価に且つ能率良く製造することができるエンボ
ス化粧板の製造方法を提供するものである。 The present invention was made in view of these drawbacks, and uses Kapol, which is abundant and inexpensively available.
Using breathable material made of wood thin boards such as lauan and apitone or appropriate decorative paper, it has a decorative surface that closely resembles natural precious woods such as teak, rose, oak, and mahogany, and has a three-dimensional effect such as brick joints or tile joints. To provide a method for manufacturing an embossed decorative board that can inexpensively and efficiently manufacture an embossed decorative board having a rich concave pattern.
本発明方法の実施例を図面について説明すると
第1図は本発明方法を工程順に示したものであり
1は合成、パーテイクルボード、繊維板その他の
適宜な板状物よりなる基板で、その表面にラワ
ン、カポール、アピトン等の雑木のロータリー木
材単板を貼着して表面化粧層2を形成する。 An embodiment of the method of the present invention will be explained with reference to the drawings. Fig. 1 shows the method of the present invention in the order of steps. 1 is a substrate made of synthetic material, particle board, fiberboard, or other suitable plate-like material, and its surface is A rotary wood veneer made of miscellaneous trees such as lauan, capor, and apitong is adhered to the surface to form a surface decorative layer 2.
尚、この表面化粧層2として使用した前記木材
単板は、あらかじめ漂白或いは着色されてその色
調を統一したものであつてもよい。 The wood veneer used as the surface decorative layer 2 may be bleached or colored in advance to have a uniform color tone.
次に、化粧層2の表面にエンボスロール3等に
よつてレンガ張りの目地模様状凹溝4を転刻す
る。 Next, concave grooves 4 in the form of a brick joint pattern are imprinted on the surface of the decorative layer 2 using an embossing roll 3 or the like.
この凹溝4はレンガ目地状の模様に限らず、求
める化粧板の用途に応じてタイル目地状或いは額
縁状もしくは平行な溝模様であつてもよく、その
柄模様については特に限定されない。 The grooves 4 are not limited to a brick joint pattern, but may be a tile joint pattern, a frame pattern, or a parallel groove pattern depending on the intended use of the decorative board, and the pattern is not particularly limited.
又、凹溝4を転刻する方法としてエンボス平版
を採用してもよい。 Furthermore, an embossing plate may be employed as a method for reprinting the grooves 4.
こうして基板1の化粧層2の表面に模様状凹溝
4を施したのち、該化粧層表面にチーク、マホガ
ニー、オークその他の適宜な天然銘木の木目模様
を印刷6aした透明な塩ビフイルム等の熱可塑性
合成樹脂フイルム6をその裏面に硬化後透明にな
るウレタン系接着剤等の接着剤を塗布して載置す
る。 After the patterned grooves 4 are formed on the surface of the decorative layer 2 of the substrate 1, a transparent PVC film or the like is printed with a grain pattern 6a of teak, mahogany, oak, or other suitable natural wood on the surface of the decorative layer. The plastic synthetic resin film 6 is placed on its back surface with an adhesive such as a urethane adhesive that becomes transparent after hardening.
この時、前記熱可塑性合成樹脂フイルム6にブ
ロツク調の木目模様の印刷を施しておき、該印刷
模様6aと基板表面の化粧層2に設けたレンガ目
地状の模様状凹溝4とが同調するように重ね合わ
してもよい。この場合には、熱可塑性合成樹脂フ
イルム6が透明であるので、両者の模様の位置合
わせが容易となるものである。 At this time, the thermoplastic synthetic resin film 6 is printed with a block-like wood grain pattern, and the printed pattern 6a and the patterned grooves 4 in the shape of brick joints provided in the decorative layer 2 on the surface of the substrate are aligned. They may be overlapped like this. In this case, since the thermoplastic synthetic resin film 6 is transparent, it is easy to align the patterns of both.
次いで、化粧層2上に重わ合わせた熱可塑性合
成樹脂フイルム6の表面に、下面を微細な凹凸粗
面7aに形成された金属板等よりなる当板7を載
置してホツトプレス8,9の熱板間で加熱圧締
し、熱可塑性合成樹脂フイルム6を軟化させると
共に化粧層2の表面に貼着する。 Next, on the surface of the thermoplastic synthetic resin film 6 superimposed on the decorative layer 2, a backing plate 7 made of a metal plate or the like whose lower surface is formed with a finely uneven rough surface 7a is placed and hot pressed 8, 9. The thermoplastic synthetic resin film 6 is softened and adhered to the surface of the decorative layer 2 by heating and pressing between hot plates.
この際、ホツトプレス8,9熱板間で加熱圧締
されると、熱可塑性合成樹脂フイルムは加熱によ
り軟化、膨脹して化粧層2の表面形状に沿つて、
該化粧層2の表面のうち導管溝2a及び模様状凹
溝4の部分でたるみを生じることになり、さらに
当板7の下面の微細な凹凸粗面7aと合成樹脂フ
イルム6との間に存在する空気が同時に加熱され
て膨脹し、両者間の空気圧が上昇して化粧層2の
導管溝による凹部及びエンボスロールによつて転
刻したレンガ目地状の凹溝4の内部に前記軟化し
た合成樹脂フイルム6が加熱空気の圧力によつて
押し込まれ、この押し込みによつて第2図及び第
3図に示すように、合成樹脂フイルム6がその裏
面に塗布した接着剤を介して化粧層2の導管溝2
a及びレンガ目地状凹溝4の内底面に密接して貼
着される。 At this time, when heated and pressed between the hot presses 8 and 9, the thermoplastic synthetic resin film softens and expands due to heating, and conforms to the surface shape of the decorative layer 2.
Sagging will occur at the conduit grooves 2a and the patterned grooves 4 on the surface of the decorative layer 2, and furthermore, sagging will occur between the finely uneven rough surface 7a on the lower surface of the backing plate 7 and the synthetic resin film 6. At the same time, the air is heated and expanded, and the air pressure between them rises, causing the softened synthetic resin to fill the concave portions of the decorative layer 2 formed by the conduit grooves and the concave grooves 4 in the shape of brick joints engraved by the embossing roll. The film 6 is pushed in by the pressure of the heated air, and as shown in FIGS. 2 and 3, the synthetic resin film 6 connects to the conduit of the decorative layer 2 through the adhesive applied to its back surface. Groove 2
a and the inner bottom surface of the brick joint-like groove 4 in close contact with each other.
なお、このように合成樹脂フイルム6の表面側
から空気の膨脹圧によつて該フイルム6を化粧層
2の凹部内底面にまで押し込ませるには、化粧層
2が通気性を有すること及び合成樹脂及び合成樹
脂フイルム6が熱可塑性であり且つ該合成樹脂フ
イルム表面を熱圧する当板7の下面が微細な凹凸
粗面7aであることが必要である。 Note that in order to push the synthetic resin film 6 from the surface side of the synthetic resin film 6 into the inner bottom surface of the recess of the decorative layer 2 by the expansion pressure of air, the decorative layer 2 must have air permeability and the synthetic resin must have air permeability. It is also necessary that the synthetic resin film 6 is thermoplastic, and that the lower surface of the plate 7 that heat-presses the surface of the synthetic resin film has a finely uneven rough surface 7a.
なんとなれば、基板表面の化粧層2が合成樹脂
層或いは金属シート等の非通気性材料で形成され
た場合には、合成樹脂フイルム凹溝部間に存在す
る空気が外部に逃げられなくなつて合成樹脂フイ
ルム表面側からの空気圧による押し込みにも拘ら
ず、凹溝部内底面に沿つて該フイルムを密着させ
ることができなくなつて接着不良を起すためであ
り、従つて、基板表面の化粧層2としては前述し
た木材単板或いは紙等の通気性を有する材料を使
用する必要がある。 This is because when the decorative layer 2 on the surface of the substrate is formed of a non-breathable material such as a synthetic resin layer or a metal sheet, the air existing between the grooves of the synthetic resin film cannot escape to the outside and This is because, despite being pushed by air pressure from the surface side of the resin film, the film cannot be brought into close contact along the inner bottom surface of the groove, resulting in poor adhesion. It is necessary to use an air-permeable material such as the aforementioned wood veneer or paper.
又、熱可塑性合成樹脂フイルム6の表面を熱圧
するのに用いられる当板7は、その下面が平滑で
ある場合には合成樹脂フイルム表面と当板下面と
が全面的に密着して両者間に所望の空気圧を発生
させることが困難であるが、本発明方法は前述し
たように下面を凹凸粗面7aに形成した当板7を
用いるので、該凹凸粗面7aと合成樹脂フイルム
表面との間に適量の空気を存在させることができ
この空気を加熱膨脹させてその空気圧により加熱
軟化した合成樹脂フイルム6をその下面側の化粧
層2の凹溝内底面に密着するまで押圧して貼着し
得るものである。 In addition, when the bottom surface of the backing plate 7 used for hot-pressing the surface of the thermoplastic synthetic resin film 6 is smooth, the surface of the synthetic resin film and the bottom surface of the backing plate are completely in close contact with each other, and there is no space between them. Although it is difficult to generate the desired air pressure, since the method of the present invention uses the contact plate 7 whose lower surface is formed with the uneven rough surface 7a as described above, the gap between the uneven rough surface 7a and the surface of the synthetic resin film is This air is heated and expanded, and the synthetic resin film 6 softened by the air pressure is pressed and adhered to the bottom surface of the concave groove of the decorative layer 2 on the lower surface side. It's something you get.
次に本発明の具体的な実施例を示す。 Next, specific examples of the present invention will be shown.
実施例
カポールの3プライ合板の表面に外周面を200
℃に加熱した金属製のエンボスロールによりレン
ガ目地模様状の凹模様を転刻したのち、裏面にチ
ークの木目模様を印刷した厚さ50μの透明な塩ビ
フイルムをその印刷面側にウレタン系接着剤を30
g/m2の割合で均一に塗布して前記カポール合板
表面に載置し、次いで該塩ビフイルム表面に、下
面を梨地調の凹凸粗面に形成しているジユラルミ
ン板を載せてこれらをホツトプレスの熱板間に挿
入し、120℃、10Kg/cm2、5分間の条件下で加熱
圧締した。Example: 200mm outer circumference on the surface of Capole's 3-ply plywood
After engraving a concave brick joint pattern using a metal embossing roll heated to ℃, a 50μ thick transparent PVC film with a teak wood grain pattern printed on the back side was attached to the printed side with urethane adhesive. 30
g/m 2 and placed on the surface of the Capol plywood. Next, a duralumin board whose lower surface had a rough textured surface was placed on the surface of the PVC film, and these were placed in a hot press. It was inserted between hot plates and heated and pressed under the conditions of 120°C, 10Kg/cm 2 , and 5 minutes.
その結果、加熱により軟化膨脹した塩ビフイル
ムがカポール合板の表単板表面の導管溝内部及び
レンガ目地状の凹模様内部に入り込み、ジユラル
ミン板下面とビフイルム表面間の加熱空気の空気
圧によつて該塩ビフイルムが導管溝と凹模様の内
底面に完全に密着して合板の表単板表面に貼着さ
れ、レンガ調の外観を呈したチーク柄で自然な導
管模様を有する化粧板を得た。 As a result, the PVC film, which had softened and expanded due to heating, entered the inside of the conduit groove and the brick joint-like concave pattern on the surface of the Kapor plywood, and the PVC The film was adhered to the surface of the front veneer of plywood by completely adhering to the conduit grooves and the inner bottom surface of the concave pattern, thereby obtaining a decorative board having a brick-like appearance and a natural conduit pattern with a teak pattern.
以上のように本発明は、基板表面に通気性を有
する適宜の化粧層を設けたのち、エンボスロール
又はエンボス平版等で化粧層表面にタイル目地状
その他の適宜凹模様を転刻し、次いで該化粧層表
面に適宜印刷模様を設けた透明な熱可塑性合成樹
脂フイルムをその裏面に硬化後透明になる接着剤
を塗布して載置し、しかるのち、前記熱可塑性合
成樹脂フイルム表面に、下面に微細な凹凸粗面を
設けた金属板等によりなる当板を配して熱圧する
ことにより、該フイルムを軟化させると共にこの
フイルムと当板下面間の加熱空気の空気圧により
該フイルムを前記化粧層表面の凹模様部内面に密
着するまで押し込んで貼着することを特徴とする
エンボス化粧板の製造方法に係るものであるから
基板表面の化粧層上に配した熱可塑性合成樹脂フ
イルムと化粧層の凹模様間に存在する空気が該フ
イルムの加熱硬化時にフイルム表面側の空気圧に
よつて通気性を有する化粧層から円滑に排除され
て該フイルムの下面を確実に化粧層の凹模様の内
底面にも密着させることができ、さらに、表面化
粧層として木材単板等を用いると、その導管溝等
の自然な凹模様とエンボスロール等で設けた人工
的な凹模様とをフイルム表面にそのまゝ再現でき
ると共にこれらの凹模様と熱可塑性合成樹脂フイ
ルムの印刷模様が調和した美麗な化粧面を得るこ
とができるものであり、又、合成樹脂フイルムが
透明であるために、その印刷模様と化粧層表面の
凹模様とを容易且つ正確にマツチさせて貼着する
ことができ、安価に且つ能率良くエンボス化粧板
を製造できるものである。 As described above, the present invention provides a suitable decorative layer having air permeability on the surface of a substrate, and then imprints a tile joint shape or other suitable concave pattern on the surface of the decorative layer using an embossing roll or an embossing plate, and then A transparent thermoplastic synthetic resin film with an appropriate printed pattern on the surface of the decorative layer is placed on the back side of the film by applying an adhesive that becomes transparent after curing, and then the thermoplastic synthetic resin film is coated with an adhesive that becomes transparent after curing. By placing a backing plate made of a metal plate or the like with a finely uneven rough surface and applying heat pressure, the film is softened, and the air pressure of the heated air between the film and the lower surface of the backing plate causes the film to be bonded to the surface of the decorative layer. The method for producing an embossed decorative board is characterized in that the thermoplastic synthetic resin film placed on the decorative layer on the surface of the substrate and the recesses in the decorative layer are bonded to the surface of the decorative layer. The air existing between the patterns is smoothly removed from the breathable decorative layer by the air pressure on the surface side of the film when the film is heated and cured, thereby ensuring that the lower surface of the film also covers the inner bottom surface of the concave pattern of the decorative layer. Furthermore, if a wood veneer or the like is used as the surface decorative layer, the natural concave patterns such as conduit grooves and the artificial concave patterns created with embossing rolls, etc. can be reproduced on the film surface. At the same time, it is possible to obtain a beautiful decorative surface in which these concave patterns and the printed pattern of the thermoplastic synthetic resin film harmonize, and since the synthetic resin film is transparent, the printed pattern and the surface of the decorative layer can be The embossed decorative board can be easily and accurately matched with the concave pattern of the embossed board, and an embossed decorative board can be manufactured at low cost and efficiently.
又、熱圧時に下面が微細な凹凸粗面に形成され
た当板を用いて該当板の下面とフイルム表面間の
加熱空気の空気圧を利用して前述したようにフイ
ルムを化粧層の凹模様内に押し込むものであるか
ら、フイルムが該凹模様の内底面に完全に密着し
て立体感に富んだ化粧面を現出でき、しかも上記
当板の凹凸粗面がフイルム表面の艶消しを兼ねて
照りの少ない重厚感のある化粧面を形成すること
ができるものである。 Also, during hot pressing, using a backing plate whose lower surface has a rough surface with minute irregularities, the film is pressed into the concave pattern of the decorative layer using the air pressure of the heated air between the lower surface of the plate and the surface of the film. Since the film is pressed into the inner bottom surface of the concave pattern, it can completely adhere to the inner bottom surface of the concave pattern, creating a decorative surface with a rich three-dimensional effect.Moreover, the uneven rough surface of the above-mentioned backing plate also serves as a matte surface of the film. It is possible to form a decorative surface with a heavy feeling and less shine.
図面は本発明方法の実施例を示すもので、第1
図はその製造工程図、第2図は当板で加熱した状
態の化粧板の断面図、第3図は化粧板の一部拡大
断面図、第4図は得られた化粧板の斜視図であ
る。
1……基板、2……化粧層、3……エンボスロ
ール、4……凹溝、6……熱可塑性合成樹脂フイ
ルム、6a……印刷模様、7……当板、7a……
凹凸粗面。
The drawings show an embodiment of the method of the present invention.
The figure is a diagram of the manufacturing process, Figure 2 is a sectional view of the decorative laminate heated by the plate, Figure 3 is a partially enlarged sectional view of the decorative laminate, and Figure 4 is a perspective view of the obtained decorative laminate. be. DESCRIPTION OF SYMBOLS 1... Substrate, 2... Decorative layer, 3... Emboss roll, 4... Concave groove, 6... Thermoplastic synthetic resin film, 6a... Print pattern, 7... Backing plate, 7a...
Uneven rough surface.
Claims (1)
けたのち、エンボスロール又はエンボス平版等で
化粧層表面にタイル目地状その他の適宜凹模様を
転刻し、次いで該化粧層表面に適宜印刷模様を設
けた透明な熱可塑性合成樹脂フイルムをその裏面
に硬化後透明になる接着剤を塗布して載置し、し
かるのち、前記熱可塑性合成樹脂フイルム表面
に、下面に微細な凹凸粗面を設けた当板を配して
熱圧することにより該フイルムを軟化させると共
にこのフイルムと当板下面間の加熱空気の空気圧
により該フイルムを前記化粧層表面の凹模様部内
面に密着するまで押し込んで貼着することを特徴
とするエンボス化粧板の製造方法。 2 前記化粧層が木材単板であることを特徴とす
る特許請求の範囲第1項記載のエンボス化粧板の
製造方法。 3 前記化粧層が化粧紙であることを特徴とする
特許請求の範囲第1項記載のエンボス化粧板の製
造方法。[Scope of Claims] 1. After providing a suitable decorative layer with air permeability on the surface of the substrate, a tile joint shape or other suitable concave pattern is imprinted on the surface of the decorative layer using an embossing roll or an embossing plate, and then the decorative layer is A transparent thermoplastic synthetic resin film with an appropriate printed pattern on the surface of the layer is coated with an adhesive that becomes transparent after curing on the back side, and then placed on the surface of the thermoplastic synthetic resin film. The film is softened by heat-pressing a backing plate having an uneven rough surface, and the film is brought into close contact with the inner surface of the concave pattern on the surface of the decorative layer by the air pressure of the heated air between the film and the lower surface of the backing plate. A method for manufacturing an embossed decorative board, which is characterized in that the embossed decorative board is pasted by being pressed until it is . 2. The method for manufacturing an embossed decorative board according to claim 1, wherein the decorative layer is a wood veneer. 3. The method for producing an embossed decorative board according to claim 1, wherein the decorative layer is a decorative paper.