JPS62176948A - Manufacture of product with metal shine - Google Patents
Manufacture of product with metal shineInfo
- Publication number
- JPS62176948A JPS62176948A JP1700686A JP1700686A JPS62176948A JP S62176948 A JPS62176948 A JP S62176948A JP 1700686 A JP1700686 A JP 1700686A JP 1700686 A JP1700686 A JP 1700686A JP S62176948 A JPS62176948 A JP S62176948A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- parts
- cement
- slurry
- mold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
（産業上の利用分野）
本発明は、金属光沢が得られる物品を製造するのに好適
な方法に関する。DETAILED DESCRIPTION OF THE INVENTION (Industrial Field of Application) The present invention relates to a method suitable for manufacturing an article that provides metallic luster.
（従来の技術）
従来、金属製表札、額縁、レリーフ等のような金属光沢
を有する物品を製造する方法としては、鋳造法で製造し
た鋳物の表面を研摩して製造する方法や、プラスチック
成形品の表面にメッキして製造する方法などがあるが、
前者は金属を溶解する必要があり、また後者は高価なプ
ラスチック成形機やメッキ装置が必要であるなどの問題
があった。しかも、鋳造品やプラスチック製品は一度成
形すると、その形状の修正が手作業では困難であった０
（発明の目的）
本発明は上記の事情に鑑みてなされたもので、鋳造法や
メッキを用いることなく金属光沢が得られる物品を容易
かつ安価に製造できる方法を提供することを目的とする
。(Prior Art) Conventionally, methods for manufacturing articles with metallic luster such as metal nameplates, picture frames, reliefs, etc. include methods for manufacturing by polishing the surface of castings manufactured by casting methods, and methods for manufacturing products with metallic luster such as metal nameplates, picture frames, reliefs, etc. There are methods of manufacturing by plating the surface of
The former requires the metal to be melted, and the latter requires expensive plastic molding machines and plating equipment. Furthermore, once a cast or plastic product is molded, it is difficult to manually modify its shape. It is an object of the present invention to provide a method for easily and inexpensively manufacturing an article that can obtain metallic luster without any problems.
（問題点を解決するための手段）
本発明における金属光沢が得られる物品の製造方法は、
金属粉末９７〜９０重量部とセメント３〜１０重量部と
を混合して得た混合粉１００重景装置、セメント硬化剤
液を１５〜２５重量部添加し、それらを混練してスラリ
ー状態にし、このスラリー状物を型に流し込んで平板状
態にし、その後、平板状物を彫刻刀で彫刻することを特
徴とする。(Means for solving the problem) The method for manufacturing an article that can obtain metallic luster according to the present invention is as follows:
100 parts by weight of mixed powder obtained by mixing 97 to 90 parts by weight of metal powder and 3 to 10 parts by weight of cement, 15 to 25 parts by weight of cement hardener liquid are added, and the mixture is kneaded to form a slurry. The method is characterized by pouring this slurry into a mold to form a flat plate, and then carving the flat plate with a chisel.
なお、所望の金属光沢を有する物品を得るに際し、金属
粉末とセメントとの混合割合およびセメント硬化剤液の
添加量並びに切削性について究明テストを行った結果を
、第１表および第２表に示す。すなわち、粒度３５０メ
、ソシュアンダーのブロンズ粉末とポルトランドセメン
トとを、各重量を種々変えて混合するとともに、これら
にセメント硬化剤液の重量を種々変えて添加した後、そ
れらを混練してスラリー状態にする。次いで、このスラ
リー状物を内径３０問・深さ５０羽の型に流し込み、３
分程経過してスラリー状物が硬化を完了した後、その硬
化物を型から取り出してテストピースを作る。次いで、
３０分経過後そのテストピースの表面をサンドペーパで
研摩して光沢の良否をチェックしかつ抗圧力を測定し、
その結果を第１表に示す。In addition, in order to obtain an article with the desired metallic luster, Tables 1 and 2 show the results of tests conducted on the mixing ratio of metal powder and cement, the amount of cement hardening agent added, and machinability. . That is, Sauceander bronze powder with a particle size of 350 mm and Portland cement are mixed at various weights, and after adding cement hardener liquid at various weights, they are kneaded to form a slurry. state. Next, pour this slurry into a mold with an inner diameter of 30 pieces and a depth of 50 pieces.
After about a minute has passed and the slurry has completely cured, the cured product is removed from the mold and a test piece is made. Then,
After 30 minutes had elapsed, the surface of the test piece was polished with sandpaper to check whether the gloss was good or not, and the resistance pressure was measured.
The results are shown in Table 1.
また、同様にしてテストピースを作り、スラリー状物を
型に注入後、所定時間経過毎に彫刻刀で切削してその切
削性についてテストした結果を第２表に示す。なお、セ
メント硬化剤液として東亜合成株式会社製のアロンクリ
ート（商品名）を使用した。そして、各表において、金
属粉、セメントおよび硬化剤液の単位は重量部であり、
さらに硬化剤液に係る数字は、金属粉とセメントの混合
粉に対する値である。In addition, a test piece was made in the same manner, and after pouring the slurry into the mold, the sample was cut with a chisel every predetermined time period to test its machinability. Table 2 shows the results. In addition, Aroncrete (trade name) manufactured by Toagosei Co., Ltd. was used as the cement hardening agent liquid. In each table, the units of metal powder, cement, and hardening agent liquid are parts by weight.
Furthermore, the numbers related to the hardening agent liquid are values for a mixed powder of metal powder and cement.
上記の第１表からは、次のことが判る。すなわち、金属
粉とポルトランドセメントの配合割合は、９７〜９０重
量部：３〜１０重量部が好ましく、この配合割合により
良好な金属光沢が得られる。また、金属粉・セメントの
混合粉とセメント硬化剤液の配合割合は、１００重量部
：１５〜２５重量部が好ましく、この配合割合により良
好な抗圧力が得られる。また、第２表からは次のことが
判る。第１表で示すところの良好な抗圧力を得た配合割
合で作ったテストピースは、型に注入後１時間以内では
良好な切削性が得られる。From Table 1 above, the following can be seen. That is, the mixing ratio of metal powder and Portland cement is preferably 97 to 90 parts by weight: 3 to 10 parts by weight, and good metallic luster can be obtained with this mixing ratio. Further, the mixing ratio of the mixed powder of metal powder/cement and the cement hardening agent liquid is preferably 100 parts by weight: 15 to 25 parts by weight, and good resistance pressure can be obtained by this mixing ratio. Furthermore, the following can be seen from Table 2. Test pieces made with the compounding ratios that gave good counter pressure as shown in Table 1 had good machinability within one hour after being poured into the mold.
（実施例）
金属光沢を有する表札を製造する場合について説明する
と、第１図の（イ）に示すように、縦１２０朋・横５Ｑ
ＭＩＲ・深さ２０１！ＩＭの凹み（１）を有する型（２
）内に、その（ロ）に図示するようにスラリー状物（３
）を流し込む。なお、該スラリー状物（３）とは金属粉
末９５重量部とセメント５重量部とを混合して得た混合
粉１００重量部に東亜合成株式会社製のセメント硬化剤
液（商品名アロンクリート）を添加し、それらを混練し
てスラリー状態にしたものである。型（２）に流し込ん
だスラリー状物（３）は３分程経過すると硬化するので
、型抜をするとその（ハ）に図示するように平板状物（
４）ができる。(Example) To explain the case of manufacturing a nameplate with metallic luster, as shown in Figure 1 (a), the height is 120 mm and the width is 5 Q.
MIR・Depth 201! Mold (2) with IM recess (1)
), as shown in (b), a slurry-like material (3
). The slurry (3) is 100 parts by weight of a mixed powder obtained by mixing 95 parts by weight of metal powder and 5 parts by weight of cement, and a cement hardening agent liquid (trade name: Aroncrete) manufactured by Toagosei Co., Ltd. are added and kneaded to form a slurry. The slurry (3) poured into the mold (2) will harden after about 3 minutes, so when the mold is removed, a flat plate (3) will be formed as shown in (c).
4) can be done.
この平板状物（４）に彫刻刀で氏名を凸状あるいは凹状
に彫刻すると、その（ニ）に図示するように表札原形体
（５）ができる、この表札原形体（５）の表面を目の細
かいサンドペーパ等で研摩すると、所望の金属光沢を有
する表札が得られる。When a name is engraved into a convex or concave shape with a chisel on this flat plate (4), a nameplate prototype (5) is created as shown in (d). By polishing with fine sandpaper or the like, a nameplate with the desired metallic luster can be obtained.
（発明の効果）
以上の説明からも明らかなように本発明は、金属粉末、
セメントおよびセメント硬化剤液を混練してスラリー状
態にした後、型に流し込んで平板状態にし、この平板状
物を彫刻刀で彫刻するようにしたから、溶融金属を用い
る鋳造法によることなく金属光沢が得られる物品を容易
に製造でき、しかも、従来方法のような高価なプ、ラス
チック成形機やメッキ装置は全く不要になり、その上、
型は鋳造法における鋳型はどの強度および耐熱性がいら
なくな°るなどの優れた効果を奏する。(Effect of the invention) As is clear from the above explanation, the present invention provides metal powder,
After kneading cement and cement hardener liquid to form a slurry, pouring it into a mold to form a flat plate, and carving this flat plate with a chisel, it is possible to achieve metallic luster without using a casting method using molten metal. It is possible to easily manufacture products that can obtain a
The mold has excellent effects such as eliminating the need for strength and heat resistance in the casting method.
第１図は本発明の詳細な説明するための工程図である。 FIG. 1 is a process diagram for explaining the present invention in detail.
Claims (1)
を混合して得た混合粉１００重量部に、セメント硬化剤
液を１５〜２５重量部添加し、それらを混練してスラリ
ー状態にし、このスラリー状物を型に流し込んで平板状
態にし、その後、平板状物を彫刻刀で彫刻することを特
徴とする金属光沢が得られる物品の製造方法。15 to 25 parts by weight of a cement hardener liquid is added to 100 parts by weight of a mixed powder obtained by mixing 97 to 90 parts by weight of metal powder and 3 to 10 parts by weight of cement, and the mixture is kneaded to form a slurry, A method for producing an article with metallic luster characterized by pouring this slurry into a mold to form a flat plate, and then carving the flat plate with a chisel.