JPS62169100A - Radiation image conversion panel - Google Patents
Radiation image conversion panelInfo
- Publication number
- JPS62169100A JPS62169100A JP1156186A JP1156186A JPS62169100A JP S62169100 A JPS62169100 A JP S62169100A JP 1156186 A JP1156186 A JP 1156186A JP 1156186 A JP1156186 A JP 1156186A JP S62169100 A JPS62169100 A JP S62169100A
- Authority
- JP
- Japan
- Prior art keywords
- radiation image
- image conversion
- phosphor
- conversion panel
- light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
［発ＩＪＩの分野］
本発明は、輝尽性蛍光体を利用する放射ｍ像変換力性に
用いられる放射線像変換パネルに関するものである。DETAILED DESCRIPTION OF THE INVENTION [Field of IJI] The present invention relates to a radiation image conversion panel used for radiation image conversion using a stimulable phosphor.
［発明の技術的背景］
放射線像を画像として得る方法として、従来より銀ｌｉ
！感光材料からなる乳剤層を有する放射線写真フィルム
と増感紙との組合わせを用いる、いわゆる放射線写真法
が利用されＣいる。最近、」−記数射線写真法に代る方
法の一つとして、たとえば特開昭５５−１２１４５号公
報などに記載されているような、輝尽性蛍光体を用いる
放射線像変換方法が注目されるようになった。放射線像
変換方法は、輝尽性蛍光体を含有する放射！！、像変換
パネル（蓄積性蛍光体シート）を利用するもので、被写
体を透過した放射線、あるいは被検体から発せられた放
射線を該パネルの輝尽性蛍光体に吸収させ、そののちに
輝尽性蛍光体を可視光線、赤外線などの電磁波（励起光
）で時系列的に励起することにより１．′、！！、輝尽
性蛍光体中に蓄積されている放射線エネルギーを蛍光（
輝尽発光）として放出させ、この蛍光を光電的に読み取
って電気信号を得、得られた°ＩＲ気信号を画像化する
ものである。[Technical Background of the Invention] As a method of obtaining radiation images as images, silver li
! A so-called radiographic method is used which uses a combination of a radiographic film having an emulsion layer made of a light-sensitive material and an intensifying screen. Recently, a radiation image conversion method using a stimulable phosphor, as described in JP-A No. 55-12145, has attracted attention as an alternative method to the radiography method. It became so. The radiation image conversion method uses radiation containing a stimulable phosphor! ! , which utilizes an image conversion panel (stimulable phosphor sheet), in which the radiation transmitted through the subject or the radiation emitted from the subject is absorbed by the stimulable phosphor of the panel, and then the stimulable phosphor sheet is used. By exciting the phosphor in a time-series manner with electromagnetic waves (excitation light) such as visible light and infrared light, 1. ',! ! , the radiation energy accumulated in the stimulable phosphor is converted into fluorescence (
The fluorescent light is emitted as stimulated luminescence (stimulated luminescence), this fluorescence is read photoelectrically to obtain an electrical signal, and the obtained IR signal is converted into an image.
この放射線像変換方法によれば、従来の放射線写真法に
よる場合に比較して、はるかに少ない被曝線Ｚ？、で情
報Ｘｌ′Ｌの豊富な放射線画像を得ることができるとい
う利点がある。従って、この方法は、特に医療診断を目
的とするＸ線撮影等の直接医療用放射線撮影において利
用価値の非常に高いものである。According to this radiation image conversion method, the exposure line Z? , it is possible to obtain a radiation image rich in information Xl'L. Therefore, this method has very high utility value especially in direct medical radiography such as X-ray photography for the purpose of medical diagnosis.
放射線像変換方法に用いられる放射線像変換パネルは、
ノ、（本構造として、支持体とその片面に設けられた蛍
光体層とからなるものである。なお。The radiation image conversion panel used in the radiation image conversion method is
(This structure consists of a support and a phosphor layer provided on one side of the support.)
蛍光体層の支持体とは反対側の表面（支持体に面らなる
透明な保護膜が設けられていて、蛍光体層を化学的な変
質あるいは物理的な衝撃から保護している。A transparent protective film is provided on the surface of the phosphor layer opposite to the support (the surface facing the support) to protect the phosphor layer from chemical alteration or physical impact.
蛍光体層は、輝尽性蛍光体とこれを分散状態で含有支持
する結合剤とからなるものであり、輝尽性蛍光体は、Ｘ
線などの放射線を吸収したのち、ｉ＋ｆ視光線および赤
外線などの電磁波（励起光）の照射を受けると発光（Ｎ
原発光）を示す性質を有するものである。従って、被写
体を透過した、あるいは被検体から発せられた放射線は
、その放射線ｊ、、′Ｌに比例して放射線像変換パネル
の蛍光体層に吸収され、放射線像変換パネル−にには被
写体あるいは被検体の放射線像が放！）１線エネルキ゛
−の蓄積像として形成される。この蓄積像は、Ｌ配電磁
波で時系列的に励起することにより輝尽発光として放射
させることができ、この輝ｊ又発光を光電的に読み取っ
て電気信号に変換することにより放射線エネルギーの、
η積置企画像化することがｒ’Ｔ ７近となる。The phosphor layer is composed of a stimulable phosphor and a binder containing and supporting the stimulable phosphor in a dispersed state.
After absorbing radiation such as radiation, it emits light (N
It has the property of exhibiting (original luminescence). Therefore, the radiation transmitted through the object or emitted from the object is absorbed by the phosphor layer of the radiation image conversion panel in proportion to the radiation j,,'L, and the radiation image conversion panel The radiation image of the subject is released! ) is formed as an accumulated image of one-line energy key. This accumulated image can be emitted as stimulated luminescence by time-series excitation with L-distribution electromagnetic waves, and by reading this luminescence photoelectrically and converting it into an electrical signal, the radiation energy can be extracted.
η accumulation plan imaging will be close to r'T 7.
切射襲像合撞Ｂノへｉｆ ｉ述のように、１［常に右利
な画像形成方法であるが、この方法に用いられる放射線
像変換パネルも従来の放射線写真法に用いられる増感紙
と同様に、高感Ｉｍであって、かつ画質（！Ｔ鋭度、粒
状性なとりの優れた画像をり−えるものであることが望
まれる。特に、放射線像変換方法を医療用放射線撮影に
適用するに際しては、人体の被曝６７．Ｈ，を軒減させ
、かつより多くの情報を得る必要から、該方法に用いら
れる放射線像変換パネルは感度ができるだけ高いことが
望ましい。As mentioned above, 1 [Although this is always a right-handed image forming method, the radiation image conversion panel used in this method is also similar to the intensifying screen used in conventional radiography. Similarly, it is desired that the image conversion method is highly sensitive and can produce images with excellent image quality (!T sharpness, graininess, etc.). When applying this method, it is desirable that the sensitivity of the radiation image conversion panel used in this method be as high as possible, since it is necessary to reduce the radiation exposure of the human body and to obtain more information.
放射線像変換パネルの感度は、基本的にはパネルに含有
される輝尽性蛍光体の輝尽定見￥によって決まり、この
発光量は蛍光体自体の発光特性に依存するのみならず、
１Ｉｌｉ尽発光を生じさせるための励起光が充分な強Ｉ
ｆを右１７ない場合にはその強＋ｉによ−）でも異なる
ものである。The sensitivity of a radiation image storage panel is basically determined by the photostimulability of the stimulable phosphor contained in the panel, and the amount of light emitted not only depends on the luminescent properties of the phosphor itself;
The excitation light is strong enough to cause 1Ili exhaustion emission.
If there is no f on the right, the strength +i -) is also different.
放射線像変換方法において放Ｑ４線像変換・くネルの読
出しは、たとえば励起光としζ；／−ザー光笠を用いて
パネル表面を走査することにより行なわれているが、励
起光の一部はパネル中、特に蛍光体層中で散乱されたの
ち輝尽性蛍光体を励起することなく１すび、該パネル表
面から放出されるために、蛍光体が１−分に励起されず
、従って励起光の利用効−タが必ずしも高いとはｔえな
かった。特に、励起光の光源として出力の小さなレーザ
ーを用いる場合には、励起光の利用効率を高めてパネル
の感度を向ｌニさせることが望まれる。In the radiation image conversion method, radiation Q4 radiation image conversion and reading of the tunnel is performed by scanning the panel surface using a laser light shade, for example, using excitation light. After scattering in the panel, especially in the phosphor layer, the stimulable phosphor is emitted from the panel surface without excitation, so the phosphor is not excited for 1 minute, and therefore the stimulable phosphor is not excited. The efficiency of light utilization was not necessarily high. In particular, when a laser with a small output is used as a light source for excitation light, it is desirable to improve the efficiency of use of excitation light to improve the sensitivity of the panel.
なお１本出願人は、パネル表面に無機物質などからなる
反射防０二膜が設けられた放射ｍ像変換バンルに゛つい
て既に出願しているが（特願昭６０−５５０９号）、こ
の出願において反射防止１模は、パネルに照射された励
起光がパネル表面で反射、されるのを防止するために設
けられており、巾に、励起光に対する光反射率が低いと
の特性を右−４る薄膜にすぎない。Note that the present applicant has already filed an application for a radiation m-image conversion bundle in which the panel surface is provided with an anti-reflection film made of an inorganic material, etc. (Japanese Patent Application No. 5509/1983); The anti-reflection type 1 is provided to prevent the excitation light irradiated onto the panel from being reflected on the panel surface. It is just a thin film.
［発ＩＪ１の霊旨］
本発明は、感度の向トした放射線像変換パネルを提供す
ることをそのＩＩ的とするものである。[Principle of IJ1] The second object of the present invention is to provide a radiation image conversion panel with improved sensitivity.
また、未発ＩＪＪは、高感度であっＣかつ鮮鋭度の高い
画像をり−える放射線像変換パネルを提供することも・
イの目的とするものである。In addition, for undeveloped IJJ, we can also provide radiation image conversion panels that have high sensitivity and can produce images with high C and sharpness.
This is the purpose of
Ｆ−記の［１的は、支持体と、この支持体上に１ｌｓｌ
１１性蛍光体を含む蛍光体層とを有する放射線像変換
パネルであって、１偵パネルの少なくとも一部が着色剤
により着色されている放射線像変換パネルにおいて、該
蛍光体層の支持体に接する側とは反対側の表面に、該輝
尽性蛍光体の励起波長における光透過率がＯ〜５°の範
囲の光の入射角度に対して７０％以りであり、かつ該励
起波長における光反射率が３０’以Ｅの光の入射角度に
対して６０％以にである多層膜フィルタが設けられてい
ることを特徴とする本発明の放射線像変換パネルにより
達成することができる。F-[1] A support and 1lsl on this support.
A radiation image conversion panel having a phosphor layer containing an 11-character phosphor, in which at least a part of the 1st panel is colored with a colorant, in which the radiation image conversion panel is in contact with the support of the phosphor layer. The light transmittance of the stimulable phosphor at the excitation wavelength is 70% or more with respect to the incident angle of light in the range of 0 to 5 degrees, and the light at the excitation wavelength is This can be achieved by the radiation image conversion panel of the present invention, which is provided with a multilayer filter having a reflectance of 60% or more with respect to the incident angle of light of 30' or more.
なお、本ＩＪＩ細占において入射角度とは、入射面のｌ
ｊ線からの角度を意味する。従って、入射角度はＯ〜９
０°の範囲をとりうる。In addition, in this IJI detailed analysis, the incident angle refers to the l of the incident surface.
It means the angle from the j line. Therefore, the angle of incidence is O~9
It can range from 0°.
本発明は、放射線像変換パネルの蛍光体層−Ｌに励起波
長について入射角度依存性のある光透過率および光反Ｉ
）１−＋を右する多層ＩＴＰ２フィルタを、没けること
により、励起光の利用効率を高めてパネルの感１８”の
顕亥な向ｔ−ｆｒ ’ｉ＜ Ｊυ十スものであスー通常
、放射線像変換パネルの読出しはパネル表面（蛍光体層
の支持体に接する側とは反対側の表面、あるいは該蛍光
体層ヒに保護膜が１没けられている場合には保護膜表面
）から行なわれており、読出しの際にレーザー光等の励
起光はパネル表面にほぼ東直に照射される。それに対し
、パネル中で散乱された励起光は大部分が角度をもって
入射方向とは逆方向のパネル表面に向かう。The present invention provides a phosphor layer-L of a radiation image conversion panel with a light transmittance and a light reflection I that are dependent on the angle of incidence with respect to the excitation wavelength.
) By submerging the multi-layer ITP2 filter, which is located at 1-+, the utilization efficiency of excitation light is increased and the panel sensitivity is 18". Readout of the radiation image conversion panel is performed from the panel surface (the surface of the phosphor layer opposite to the side that contacts the support, or the surface of the protective film if the phosphor layer is covered with a protective film). During readout, excitation light such as a laser beam is irradiated onto the panel surface almost directly east.On the other hand, most of the excitation light scattered within the panel is directed at an angle in the opposite direction to the direction of incidence. toward the panel surface.
未発ＩＪ１の放射！ａ像変換パネルにおいては、励起光
の入射角度が小さい（入射面に屯直に近い）場合には励
起光を′ｒｆｊｔ硝１５、逆に入射角度が大きい（斜め
入射）場合には励起光を透過しないで反射するような入
射角度に依存した透過および反射特性を有する多層膜フ
ィルタが、蛍光体層の支持体に接する側とは反対側の表
面に設けられている。Unexploded IJ1 radiation! In the a-image conversion panel, when the angle of incidence of the excitation light is small (nearly perpendicular to the plane of incidence), the excitation light is used as the ``rfjt 15'', and conversely, when the angle of incidence is large (oblique incidence), the excitation light is A multilayer filter having transmission and reflection characteristics dependent on the angle of incidence such that the phosphor layer is not transmitted but is reflected is provided on the surface of the phosphor layer opposite to the side in contact with the support.
この多層膜フィルタにより、パネル表面に照射された励
起光は透過されるが、パネル中で散乱されて角度をもっ
た励起光は透過されることなくフィルタ表面で反射され
て、＋Ｉｆびｊケ光体層に向かうことになる。このため
に、パネル中で散乱された励起光が輝尽性蛍光体の励起
に寄グーすることなく外部に逸脱するような励起光の損
失を防ぐことができ、励起される輝尽性蛍光体に蓄積さ
れた情報（トラップされた’ｉｔｊ Ｔ−）の比率を亮
めることができる。換汀すれば、励起光をパネル内に閉
じ込めることにより、蛍光体の輝尽発光量を大幅に増大
してパネルの感度を従来よりもＷｊＩ：Ｊ著に高めるこ
とができるものである。This multilayer filter allows the excitation light irradiated on the panel surface to be transmitted, but the excitation light that is scattered within the panel and has an angle is not transmitted and is reflected on the filter surface, resulting in +If It will go to the body layer. For this reason, the excitation light scattered in the panel does not contribute to the excitation of the stimulable phosphor, and loss of excitation light such as deviating to the outside can be prevented. The ratio of information stored in (trapped 'itj T-) can be increased. In other words, by confining the excitation light within the panel, the amount of stimulated luminescence of the phosphor can be greatly increased, and the sensitivity of the panel can be significantly increased by WjI:J compared to the conventional method.
また、本発明の放射！ａ像変換パネルはその少なくとも
一部が励起光を選択的に吸収するような着色剤によって
着色されているから、パネル内で散乱して広がりをもっ
た励起光は、多層膜フィルタにより反射された散乱励起
光も含めてその一部はこの着色剤によって吸収される。Also, the radiation of the present invention! Since at least a portion of the a-image conversion panel is colored with a coloring agent that selectively absorbs excitation light, the excitation light scattered and spread within the panel is reflected by the multilayer filter. A portion of the light, including the scattered excitation light, is absorbed by this colorant.
これにより、輝尽性蛍光体が散乱励起光によって励起さ
れることによる鮮鋭度等の画像の画質の低Ｆを防ぐこと
ができる。Thereby, it is possible to prevent the image quality such as sharpness from becoming low due to the excitation of the stimulable phosphor by the scattered excitation light.
従って、強度の弱い励起光の照射であってもパネル中の
蛍光体の輝尽発光量を多く保つことができ、得られる画
像の鮮鋭度等の画質を殆ど低下させることなくパネルを
高感度に維持することができる。特に、励起光の光源が
出力の小さなものである場合、あるいは読出しの設定条
件等から励起光の強度を高めることができない場合にお
いて、放射線像変換パネルの励起光に対する利用効率が
増大することは大きな利点といえる。Therefore, even when irradiated with weak-intensity excitation light, the amount of stimulated luminescence of the phosphor in the panel can be maintained at a high level, and the panel can be made to have high sensitivity without almost deteriorating the image quality such as the sharpness of the obtained image. can be maintained. In particular, when the light source of the excitation light has a small output, or when the intensity of the excitation light cannot be increased due to the readout setting conditions, the increase in the utilization efficiency of the excitation light of the radiation image conversion panel is significant. This can be said to be an advantage.
そして、末完ＩＪ１のパネルを使用することによって励
起光源および読出し系についての制約を緩和することが
できるから、パネルの読出しに用いられる放射線像変換
装置について小型化、高速化などの改良が容易となり、
ひいては放射線像変換方法の適用範囲を広げることが可
撤となる。In addition, by using the final IJ1 panel, restrictions on the excitation light source and readout system can be relaxed, making it easier to improve the radiation image conversion device used for panel readout, such as making it smaller and faster. ,
As a result, it becomes possible to expand the scope of application of the radiation image conversion method.
［発明の構成〕
以−１−ａべたような好ましい特性を持った本発明の放
射線像変換パネルの態様を第１図に示す。[Structure of the Invention] FIG. 1 shows an embodiment of the radiation image conversion panel of the present invention having the preferable characteristics as described below-1-a.
第１図は１本発明に係る放射線像変換パネルの層構成を
示す断面図である。第１図において、パネルは、支持体
ｌおよび蛍光体層２からなり、多層膜フィルタ３は蛍光
体層の支持体に面しない側（パネル表面側）に設けられ
ている。そして、支持体および／または蛍光体層が着色
剤によって着色されている。FIG. 1 is a sectional view showing the layer structure of a radiation image conversion panel according to the present invention. In FIG. 1, the panel is made up of a support 1 and a phosphor layer 2, and a multilayer filter 3 is provided on the side of the phosphor layer that does not face the support (panel surface side). The support and/or the phosphor layer are colored with a colorant.
ただし、本発明の放射線像変換パネルは第１図に示した
態様に限定されるものではなく、多層膜フィルタが蛍光
体層の支持体に面しない側の表面に設けられていればよ
く、各層の間には、下塗層、接着剤層、光反射層など種
々の中間層が設けられていてもよい、たとえば第２図に
示すように、支持体ｌと蛍光体層２の間に光反射層４が
設けられていてもよく、これらのうちの少なくとも一層
が着色剤によって着色されていればよい。However, the radiation image conversion panel of the present invention is not limited to the embodiment shown in FIG. Various intermediate layers such as an undercoat layer, an adhesive layer, and a light reflection layer may be provided between the support l and the phosphor layer 2. For example, as shown in FIG. A reflective layer 4 may be provided, and at least one layer of these may be colored with a coloring agent.
本発明の放射線像変換パネルは、例えば次に述へるよう
な方法により製造することができる。The radiation image storage panel of the present invention can be manufactured, for example, by the method described below.
放射線像変換パネルの少なくとも一部を着色するのに使
用される着色剤は、該パネルの蛍光体層に含まれる輝尽
性蛍光体を輝尽発光させるだめの励起光の一部を吸収す
るような着色剤である。この着色剤は、輝尽性蛍光体の
励起波長領域における平均吸収率が該輝尽性蛍光体の輝
尽発光波長領Ｖ Ｉｓ ｙ ＋＋ １ Ｊ７
Ｗｌｔｕｔ ＩＩＩＩ −１７１−ＬＩ ４．
４− ４ ＋ ＼ｌ−： Ａ＋ ’Ｍ−ｎＩＬ
ＩＩＩＩ特性を有するものであるのが好ましい。The coloring agent used to color at least a portion of the radiation image storage panel absorbs a portion of the excitation light that causes the stimulable phosphor contained in the phosphor layer of the panel to stimulably emit light. It is a coloring agent. This colorant has an average absorption rate in the excitation wavelength region of the stimulable phosphor in the stimulated emission wavelength region V Is y ++ 1 J7
Wltut III-171-LI 4.
4- 4 + \l-: A+ 'M-nIL
Preferably, it has III characteristics.
画像の鮮鋭度の向りの点から、上記着色剤の輝尽性蛍光
体の励起光波長領域における平均吸収率はできるだけ大
きい方がよい。一方、感度の点から、着色剤の輝尽性蛍
光体の輝尽発光波長領域における平均吸収率はできるだ
け小さい方がよい。From the viewpoint of image sharpness, it is preferable that the average absorption rate of the colorant in the excitation light wavelength region of the stimulable phosphor is as large as possible. On the other hand, from the viewpoint of sensitivity, the average absorption rate in the stimulated emission wavelength region of the stimulable phosphor of the colorant is preferably as small as possible.
従って、好ましい着色剤は放射線像変換パネルに使用さ
れる輝尽性蛍光体の種類によって変動するものである０
本発明の放射線像変換パネルに使用される蛍光体として
は、後述するように４００〜９００ｎｍの波長範囲にあ
る励起光によって３００〜５００ｎｍの波長範囲の輝尽
発光を示す１′ハ光体であることが望ましいことから、
このような輝尽性蛍光体に対しては、励起光波長領域に
おける平均吸収率が輝尽発光波長領域における平均吸収
率よりも大きくなり、かつ、両者の差ができるだけ大き
くなるように、青色乃至緑色の着色剤が使用される。Therefore, preferred colorants vary depending on the type of stimulable phosphor used in the radiation image storage panel.
The phosphor used in the radiation image conversion panel of the present invention is a 1' phosphor that exhibits stimulated luminescence in the wavelength range of 300 to 500 nm when excited by excitation light in the wavelength range of 400 to 900 nm, as described later. Since it is desirable that
For such a stimulable phosphor, blue to A green colorant is used.
末完］Ｊ＋におい′て好ましく使用される８色乃至緑色
の着色剤（！ｔ！！料および顔料）の例としては、前述
の特開昭５５−１６３５００号公報に開示されているよ
うな着色剤、すなわち、ザポンファストブルー３Ｇ（ヘ
キスト社製）、ニストロールプリルブルーＮ−３ＲＬ
（住友化学株製）、スミアクリルブルーＦ−ＧＳＬ （
住人化学■製）、Ｄ＆ＣブルーＮｏ、１（ナショナルア
ニリン社製）、スピリットブルー（保土谷化学■製）、
オイルブルーＮｏ、６０３（オリエント社製）、キトン
ブルーＡ（チバガイギー社製）、アイゼン力チロンブル
ーＧＬ）Ｉ （保七谷化学■製）、レイクブルーＡ。Examples of the eight to green coloring agents (!t!! materials and pigments) preferably used in J+' are the coloring agents disclosed in the above-mentioned Japanese Patent Application Laid-Open No. 163500/1983. agents, namely Zapon Fast Blue 3G (manufactured by Hoechst), Nistrol Prill Blue N-3RL
(manufactured by Sumitomo Chemical Co., Ltd.), Sumia Acrylic Blue F-GSL (
D&C Blue No. 1 (manufactured by National Aniline), Spirit Blue (manufactured by Hodogaya Chemical),
Oil Blue No. 603 (manufactured by Orient Co., Ltd.), Kitten Blue A (manufactured by Ciba Geigy), Eisenriki Chiron Blue GL) I (manufactured by Honanaya Kagaku ■), Lake Blue A.
Ｆ、Ｈ（協和産業■製）、ローダリンブルー６ＧＸ（協
和産業■製）、ブリモジアニン６ＧＸ（楡畑産ズ■製）
、プリルアシッドグリーン６８Ｈ（保北谷化学ｎ製）、
シアニンブルーＢＮＲ５（東洋インク■製）、ライオノ
ルブルーＳＬ（東洋インク■製）等の有機系着色剤：お
よび群青、コバルトブルー、セルリアンブルー、酸化ク
ロム、Ｔｉ０２−ＺｎＯ−Ｃｏｏ−Ｎ１Ｏ系顔料等の無
機系着色剤を挙げることができる。F, H (manufactured by Kyowa Sangyo ■), Rhodalin Blue 6GX (manufactured by Kyowa Sangyo ■), Brimodianin 6GX (manufactured by Yubata Sangyo ■)
, Prill Acid Green 68H (manufactured by Hochatani Kagaku n),
Organic colorants such as Cyanine Blue BNR5 (manufactured by Toyo Ink ■) and Lionol Blue SL (manufactured by Toyo Ink ■); and ultramarine blue, cobalt blue, cerulean blue, chromium oxide, Ti02-ZnO-Coo-N1O pigments, etc. Inorganic colorants can be mentioned.
また、特開昭５７−９６３００号公報に開示されている
ようなカラーインデックスＮｏ、２４４１１．２３１６
０．７４１８０．７４２００．２２８００．２３１５０
．２３１５５．２４４０１．１、４８８０．１５０５０
．１５７０６．１５７０７．１７９４１．７４２２０．
１３４２５．１３３６１．１３４２０．１１８３６．７
４１４０゜７４３８０．７４３５０、および７４４６０
などの有機系金属ｔｔ１１１着色剤も挙げることができ
る。Also, color index No. 24411.2316 as disclosed in Japanese Patent Application Laid-open No. 57-96300,
0.74180.74200.22800.23150
．． 23155.24401.1, 4880.15050
．． 15706.15707.17941.74220.
13425.13361.13420.11836.7
4140°74380.74350, and 74460
Organic metal TT111 colorants may also be mentioned.
これらの−ン色乃至緑色の着色剤のうちで、得られる画
像の粒状性およびコントラストなどの点から、後者の特
開昭５７−９６３００号公報に開示されているような、
励起光よりも長波長領域に発光を示さない有機基金Ｆｌ
ｓ ’ｊａ塩着包着色剤に好ましい。Among these dark to green colorants, the latter, as disclosed in Japanese Patent Application Laid-Open No. 57-96300, is preferred from the viewpoint of graininess and contrast of images obtained.
Organic foundation Fl that does not emit light in a wavelength region longer than the excitation light
Preferred for s'ja salt encapsulated colorants.
なお、本発明の放射線像変換パネルにおいてはパネルを
構成する複数の層のうちの少なくとも一層が着色剤によ
り着色されていればよい、好ましくは、蛍光体層が着色
されている場合である。In the radiation image conversion panel of the present invention, at least one layer out of the plurality of layers constituting the panel may be colored with a coloring agent, and preferably the phosphor layer is colored.
本発明において使用する支持体は、従来の放射線写真法
における増感紙の支持体として用いられている各種の材
料あるいは放射線像変換パネルの支持体として公知の各
種の材料から任意に選ぶことができる。そのような材料
の例としては、ガラス板、セルロースアセテート、ポリ
エステル、ポリエチレンテレフタレート、ポリアミド、
ポリイミド、トリアセテート、ポリカーボネートなどの
プラスチック物質のフィルム、アルミニウム箔、アルミ
ニウム合金箔などの金属シート、通常の紙、バライタ紙
、レジンコート紙、二酸化チタンなどの顔料を含有する
ピグメント紙、ポリビニルアルコールなどをサイジング
しだ紙などを挙げることができる。ただし、放射線像変
換パネルの情報記録材料としての特性および取扱いなど
を考慮Ｉ７た場合、本発明において特に好ましい支持体
の材料はプラスチックフィルムである。このプラスチッ
クフィルムには、カーボンブラックなどの光吸収性物質
が練り込まれていてもよく、あるいは二酸化チタンなど
の光反射性物質が練り込まれていてもよい。前者は高鮮
鋭度タイプの放射線写真法 、ぐ 今 １１．＋−糸
＋ ４ −、ｈ ）月１ト づ 起 Ｌｌ
仔、−ヒ １↓ 〒’ｒ： ｔ、？ ＋午 カィブ
の放射線像変換パネルに適した支持体である。The support used in the present invention can be arbitrarily selected from various materials used as supports for intensifying screens in conventional radiography methods or materials known as supports for radiation image conversion panels. . Examples of such materials include glass plates, cellulose acetate, polyester, polyethylene terephthalate, polyamide,
Sizing films of plastic materials such as polyimide, triacetate, polycarbonate, metal sheets such as aluminum foil, aluminum alloy foil, regular paper, baryta paper, resin coated paper, pigment paper containing pigments such as titanium dioxide, polyvinyl alcohol, etc. Examples include shida paper. However, in consideration of the characteristics and handling of the radiation image storage panel as an information recording material, a particularly preferred material for the support in the present invention is a plastic film. This plastic film may be kneaded with a light-absorbing substance such as carbon black, or may be kneaded with a light-reflecting substance such as titanium dioxide. The former is a high sharpness type radiography method.11. +-thread
＋ ４－、h）Once a month Ll
Child, -hi 1↓ 〒'r: t,? It is a support suitable for Kaibu's radiation image conversion panel.
上記支持体が着色剤により着色される場合には、該支持
体のいずれか一方の面が着色されてもよいし、両方の面
が着色されてもよい、あるいは支持体全体が着色されて
もよい。ただし、支持体として例えば、紙等の励起光不
透過性材料を用いた場合には、該支持体の蛍光体層側の
面を着色する必要がある。支持体の片面あるいは両面を
着色する方法としては、例えば、結合剤を適当な結合剤
に分散してなる塗布液を調製して、これを支持体表面に
塗布する方法が挙げられる。また、支持体全体を着色す
る方法としては、一般に支持体製作時に支持体中に着色
剤を分散して含有させる方法が採られる。When the support is colored with a colorant, either one side of the support may be colored, both sides may be colored, or the entire support may be colored. good. However, when a material that does not transmit excitation light, such as paper, is used as the support, it is necessary to color the surface of the support on the phosphor layer side. A method for coloring one or both sides of the support includes, for example, a method of preparing a coating solution by dispersing a binder in a suitable binder and coating the solution on the surface of the support. Further, as a method for coloring the entire support, a method is generally adopted in which a coloring agent is dispersed and contained in the support at the time of manufacturing the support.
支持体と蛍光体層の結合を強化するために、蛍光体層が
設けられる側の支持体表面にゼラチンなどの高分子物質
からなる接着性賦′ｊ層を設けることもできる。この接
着性賦！ｊ層が着色剤で着色されていてもよく、この場
合には着色剤は接着性賦１１層中に含有される。In order to strengthen the bond between the support and the phosphor layer, an adhesive layer made of a polymeric substance such as gelatin may be provided on the surface of the support on the side where the phosphor layer is provided. This adhesive property! The layer j may be colored with a colorant, and in this case, the colorant is contained in the adhesive layer 11.
次に、支持体［−には光反射層が設けられてもよい（第
２図参照）。Next, a light reflective layer may be provided on the support (see FIG. 2).
支持体と蛍光体層との間に光反射層を設けることにより
、輝尽性）゛ケ光体を励起せずそのまま支持体の方向に
向かった励起光はこの光反射層によつＣ反射ぎれて１■
１び蛍光体層中を進むことになるために、これによって
も蛍光体の輝尽発光六：を増大させてパネルの感度を一
層向にさせることができる。By providing a light-reflecting layer between the support and the phosphor layer, the excitation light that does not excite the stimulable phosphor and goes directly toward the support is reflected by the light-reflecting layer. 1■
Since the light passes through the phosphor layer, this also increases the stimulated luminescence of the phosphor and further improves the sensitivity of the panel.
光反射層は、光反射性物質を含む層である。光反射性物
質としては特開昭５６−１２６００時公報並びに特願昭
５８−３７８３８号の明細書等に記・浅きれいるような
材料から適宜選択して用いることができる。光反射性物
質としては、例えば。The light-reflecting layer is a layer containing a light-reflecting substance. The light-reflecting material can be appropriately selected from the materials described and described in Japanese Patent Application Laid-Open No. 12600/1982 and Japanese Patent Application No. 37838/1983. Examples of light reflective substances include:
アルミニウム、アルミニウム合金等の金属；二酸化チタ
ン、鉛白、硫化亜鉛、酸化アルミニウム、酸化マグネシ
ウムなどの白色顔料：弗化見比バリウム、弗化塩化／ヘ
リウム、弗化塩化ストロンチウム、弗化鳴止ストロンチ
ウム、弗化臭化カルシウム、弗化塩化力ルシウノ、など
のアルカリ土類金属弗化ハロゲン化物などを挙げること
ができる。Metals such as aluminum and aluminum alloys; White pigments such as titanium dioxide, white lead, zinc sulfide, aluminum oxide, and magnesium oxide; barium fluoride, fluorochloride/helium, strontium fluoride, strontium fluoride, Examples include alkaline earth metal fluorohalides such as calcium fluoride bromide, fluoride chloride, and the like.
また、光反射性物質として中空構造を有するスチレン系
および／またはアクリル系ポリマーからなるポリマー粒
−ｒを用いることもできる（特願昭６０−２７８６６５
号ｊＪＪ ｍ書参照）。Furthermore, polymer particles-r made of styrene and/or acrylic polymers having a hollow structure can also be used as the light-reflecting substance (Japanese Patent Application No. 60-278665
(Refer to No. jJJ m).
光反射層は、上記の光反射性物質を用いて、例えば、金
属においては真空蒸着法、あるいは金属箔をラミネート
する方法、また、白色顔料等の粉末粒子状の物質におい
ては、これを適当な結合剤に分散含有させた塗布液を塗
布し、加熱乾燥ｊる方法など番こより支持体−にに形成
することができる。The light-reflecting layer is formed by using the above-mentioned light-reflecting substance, for example, in the case of metals, by vacuum evaporation, or by laminating metal foil, or in the case of powder-like substances such as white pigments, by an appropriate method. It can be formed on a support by applying a coating liquid containing a binder dispersed therein and drying it by heating.
に記塗４ｉ液を調製する場合の結合剤としては、アクリ
ル酸エステル共重合体などの水性の高分子物質以外に、
後述する蛍光体層を形成するために用いられる結合剤の
中から適宜選択して用いることができる。In addition to water-based polymeric substances such as acrylic acid ester copolymers, binders for preparing Coating 4i liquid may include:
An appropriate binder can be selected from among the binders used for forming the phosphor layer described later.
塗布液における結合剤と光反射性物質との混合比は、−
殻に１＝１乃至１：５０（玉縫比）の範囲から選ばれ、
支持体との接着性などの点から好まＩ〜〈はｌ：２乃至
１：２０（屯驕比）の範囲から選ばれる。なお、上記光
反射性物質は単独で用いてもよいし、適当な−１，１合
で併用してもよい。The mixing ratio of the binder and the light-reflecting substance in the coating solution is -
The shell is selected from the range of 1=1 to 1:50 (tamauri ratio),
From the point of view of adhesion to the support, etc., I is preferably selected from the range of 1:2 to 1:20 (Tunko ratio). The above-mentioned light-reflecting substances may be used alone or in combination in an appropriate -1,1 ratio.
光反射層の層厚は５１’ｙ’Ｎ Ｉ ＯＯルｍとするの
が好ましい。The thickness of the light reflecting layer is preferably 51'y'NIOOlm.
なお、光反射層がＬ２着色剤により着色されＣもよく、
その場合には上記塗布液を調製する段階で着色剤は白色
顔料等の粉末粒子状の物質とともに結合剤中に添加され
る。In addition, the light reflection layer is colored with L2 colorant and C is also good,
In that case, the coloring agent is added to the binder together with a powdery particulate substance such as a white pigment at the stage of preparing the coating liquid.
さらに、特開昭５８−２００２００号公報に記載されて
いるように、得られる画像の鮮鋭度を向卜させる［１的
で、支持体の蛍光体層側の表面（支持体の蛍光体層側の
表面に接ｒｉ性賦与層、光反射層が設けられている場合
には、その表面を意味する）には、微細な凹凸が均質に
形成されていてもよい。Furthermore, as described in JP-A No. 58-200200, the sharpness of the obtained image is improved [1, the surface of the support on the phosphor layer side (the phosphor layer side of the support When an adhesion imparting layer and a light reflecting layer are provided on the surface of the substrate, fine irregularities may be uniformly formed on the surface (meaning the surface thereof).
次に、支持体１：（支持体−にに光反射層が設けられて
いる場合には光反射層−Ｉ−）には蛍光体層が形を分散
状態で含有支持する結合剤からなる層である。Next, support 1: (light reflective layer-I- if the light-reflecting layer is provided on the support) is a layer made of a binder containing and supporting a phosphor layer in a dispersed state. It is.
輝Ｊへ性蛍光体は、先に述べたように放射線を照射した
後、励起光を照射するど輝尽発光を示す蛍光体であるが
、実用的な面からは波長が４００〜９００ｎｍの範囲に
ある励起光によって３００〜５００ｎｍの波長範囲の輝
１４＜発光を示す蛍光体であることが望ましい。本発明
の放射線像変換パネルに用いられる輝尽性蛍光体の例と
しては、米国特許第３，８５９，５２７号−Ｅ！Ｊ細書
に記載されているＳｒＳ：Ｃｅ、Ｓｍ、ＳｒＳ：Ｅｕ。As mentioned above, a phosphorescent phosphor is a phosphor that exhibits stimulated luminescence when irradiated with radiation and then with excitation light, but from a practical standpoint it is a phosphor with a wavelength in the range of 400 to 900 nm. The phosphor is preferably a phosphor that emits light in the wavelength range of 300 to 500 nm when excited by excitation light. Examples of stimulable phosphors used in the radiation image storage panel of the present invention include U.S. Pat. No. 3,859,527-E! SrS:Ce, Sm, SrS:Eu described in J specification.
Ｓｍ、Ｔｈｅ２：Ｅｒ、およびＬａ２Ｏ２Ｓ：Ｅｕ、Ｓ
ｍ、
特開＋１／（５５−１２１４２号公報に記載されている
ＺｎＳ：Ｃｕ、Ｐｂ、Ｂａ０ｓｘＡｆｌ、、０３：Ｅｕ
（ただし、０．８≦Ｘ≦１０）、および、Ｍ’０ａｘＳ
ｉ０２ ：Ａ （ただし、ＭｌｌはＭｇ、Ｃａ、Ｓｒ、
Ｚｎ、Ｃｄ、またはＢａであり、ＡはＣｅ、Ｔｂ、Ｅｕ
、Ｔｍ、Ｐｂ、ＴＪＩ、Ｂｉ、すたＬ＋ Ｍ ｎ −１
４ｉｈ ｉｆ ｙ Ｌ十 〇 Ｒ＜ｖ＜９ Ｆｓ
−ｒ＆ある）、
特開昭５５、、−１２１４３号公報に記載されてい’？
ｙ （Ｂ ａ ｌ−ｘ −ｙ ＋ Ｍ ｇ ｘ 、 Ｃ
ａ ｙ ） Ｆ Ｘ ：ａＥｕ”（ただし、ＸはＣ見お
よびＢｒのうちの少なくとも一つであり、Ｘおよびｙは
、０くＸ＋Ｖ≦０．６、かつｘｙ≠０であ゛す、ａは、
１０’６≦ａ≦５Ｘ１０−２である）、
特開昭５５−１２１４４号公報に記載されているＬ ｎ
（’） Ｘ ： ｘ Ａ （ただし、ＬｎはＬａ、Ｙ
、Ｇｃ−１、およびＬ ｕのうちの少なくとも−っ、Ｘ
はＣＭおよびＢｒのうちの少なくとも−っ、ＡはＣｅお
よびＴｂのうちの少なくとも一つ、そして、Ｘは、０＜
ｘ＜０ 、Ｌである）、４′＋開閉５５−１２１４５号
−公報に記載されている（ Ｂ ａ、 Ｉ−Ｘ 、 Ｍ
’″″ｘ）ＦＸ：ｙＡ（ただし、Ｍ２冒ｆＭｇ、Ｃａ
、Ｓ ｒ、Ｚｎ、およびＣｄ（７）うちの少なく１１も
−・つ、ＸはＣ父、Ｂｒ、およびＩのｆ、：ｓ １．；
の少なくとも つ、ＡはＥ＋ｘ、Ｔｈ、Ｃｅ、Ｔｍ、Ｉ
）ｙ、Ｐｒ、Ｈｏ、Ｎｄ、Ｙｌ：＝、およびｌＥｉ□ｒ
の一°ｐ亡・の小なくとも−）、子し“ｒ： ｘ ＩＪ
、０・≦Ｘ≦０．６、ｙは、ｏ−＝ｙ−＝ｏ、ｚである
）、特開昭５５−１６００７８号公報１、二記載、乍Ｆ
１．．．−７ｙいるＭ” ＦＸ拳ｘＡ ： ｙＬｎ ｌ
ただ［２、Ｍ ” ！、ｋＢａ、Ｃａ、Ｓ ｒ、Ｍｇ、
Ｚｎ、およびＣｄの−〉ちの少なくとも一種、ＡはＢｅ
Ｏ，ＭｇＯ１Ｃ、、。Sm, The2:Er, and La2O2S:Eu, S
ZnS:Cu,Pb,Ba0sxAfl, 03:Eu described in JP-A No. 55-12142
(However, 0.8≦X≦10) and M'0axS
i02 :A (However, Mll is Mg, Ca, Sr,
Zn, Cd, or Ba, and A is Ce, Tb, Eu
, Tm, Pb, TJI, Bi, Sta L+ M n −1
4ih if y L10 R<v<9 Fs
-r&a), is described in Japanese Patent Application Laid-Open No. 12143/1983.
y (B a l−x −y + M g x , C
a y ) F ,
10'6≦a≦5X10-2), L n described in JP-A-55-12144
(') X : x A (However, Ln is La, Y
, Gc-1, and Lu, at least -, X
is at least one of CM and Br, A is at least one of Ce and Tb, and X is 0<
x < 0, L), 4'+opening/closing No. 55-12145-described in the publication (Ba, I-X, M
'''''x) FX: yA (However, M2 attack Mg, Ca
, S r, Zn, and Cd (7), at least 11 of which, X is C, Br, and I f, :s 1. ;
At least one of, A is E+x, Th, Ce, Tm, I
)y, Pr, Ho, Nd, Yl:=, and lEi□r
1 °p death, at least -), child "r: x IJ
,0.
1. ．． ．． -7y M” FX fist xA: yLn l
Just [2, M”!, kBa, Ca, S r, Mg,
At least one of Zn and Cd, A is Be
O, MgO1C,.
０、ＳｒＯ，ＢａＯ１ＺｎＯ，Ａｕ２０３．Ｙ２Ｏ１、
Ｌａ２０．、、Ｉｎ２Ｏ３，５ｉ０２．ＴｉＯ２、Ｚｒ
Ｏ２，Ｇｅｍ２．５ｎ０２．Ｎｂ２Ｏ６、Ｔａ２０５．
および−ｒ ｈ Ｏ２（７）うちの少なくとも一種、Ｌ
ｎはＥｕ、Ｔｂ、Ｃｅ、Ｔｍ、Ｄｙ、Ｐｒ、Ｈｏ、Ｎｄ
、Ｙｂ、Ｅｒ、Ｓｍ、、ｊ３よびＧｄのうちの少なくと
も一種、ＸはＯｆｆ、Ｂｒ、および工のうちの少なくと
も一種であり、Ｘおよびｙはそれぞれｓ ｘ ｉ ｏ−
’≦Ｘ≦０．５、および０＜ｙ≦０．２である］の組成
式で表わされる蛍光体、
特開昭５６−１１６７７７号公報に記載されている（Ｂ
ａｔ−ｘ 、Ｍ” 、）Ｆ２拳ａＢａＸ２：ｙＥｕ、ｚ
Ａ［ただし、Ｍｌはベリリウム、マグネシラノ・、カル
シウム、ストロンチウム、亜鉛、およびカドミウムのう
ちの少なくとも一種、Ｘは塩素、臭素、および沃素のう
ちの少ｔｒ： くとも・種、Ａはジルコニウムおよびス
カンジ・：：ｒ １．ｓ、のっちの′、（＞なくとも一
種であり、ａ、ｘ、ｙ、お〕、びＺ１マ・ヲれぞれ０．
５≦ａ≦１２５、ＯＧ ｘ ＜、、、、 ｌ、１０ ＝
≦ｙ嘱２ＸｌＯ−’、および０＜ｚダ１０−２である］
の組成式で表わされる蛍光体、特開昭５７〜２３６７３
壮公報に記載されている（ Ｂ ａ ＋−ｙ 、 Ｍ
” Ｈ） Ｆ ２＊ ａ１３ ａ、 Ｘ ２二ｙｌＥｕ
、ｚＢ［ただし、Ｍｌはベリリウム、マグ；ン、シラ１
１、カルシウ１１．ストロンチウム、１ｌｊｆｆｉ、お
よびカドミウムのうちの少なくとも・種、Ｘは４１４
、ド、鳴（素、および沃素のうちの少なくとも一挿亡あ
り、ａ、ｘ、ｙ、および２はそれぞれ０．５≦ａ≦１．
２５．０≦Ｘ≦１．１０−６≦ｙ≦２×１０゛′、およ
び０＜ｚ≦２ＸｌＯ−’Ｔある］の組成式で表わされる
蛍光体、
特開昭５７−２３６７５号−公報に記、成されている（
ｆｌａｔ−ｙ 、Ｍ” ｘ）Ｆ２ ・ａＢａＸ２ ：ｙ
Ｅｕ、ｚＡ［ただｌ、、、 Ｍ ” １．ｉ＜リリウＬ
・、マグネシウム、カルシウム、ストロンチウム、亜鉛
、およびカドミウムのうちの少なくとも一種、Ｘは塩素
、臭素、および沃素のうちの少なくとも一種、Ａは砒素
および硅素のうちの少なくとも一種であり、ａ、ｘ、ｙ
、および２はそれぞれ０．５≦ａＧ１．２５．０≦Ｘ≦
１．１０−６≦ｙ≦２×ｔｏ−’、およびＯくｚ≦５Ｘ
ｌＯ−’である］の組成式で表わされる蛍光体、
特開昭５８．−６９２８１号公報に記載されているＭ”
ＯＸ：ｘＣｅ［ただり、、Ｍ”はＰｒ、Ｎｄ、Ｐｍ、Ｓ
ｍ、、Ｅｕ、Ｔｂ、Ｄｙ、ｌ−１ｏ、Ｅｒ、Ｔｍ、Ｙｂ
、およびＢｉからなる群より選ばれる少なくとも一種の
三価金属であり、ＸはＣ９，８よびＢｒのうちのいずれ
か一方あるいはその両方であり、ｘｌ：ｉｏ＜ｘ＜０．
１である］の２組成式で表わされる蛍光体、
特開昭５８−２０６６７８号−公報に記載されているＢ
ａ Ｉ−ｘ Ｍ Ｘ ／２ Ｌ Ｘ ／２ Ｆ Ｘ
： ｙ Ｅ ＩＪ ２°［ただし、ＭはＬｉ、Ｎａ、Ｋ
、Ｒｈ、およびＣｓかうなる群より選ばねる少なくとも
・種のアルカリ・）属を表わし；Ｌは、ＳＣ，Ｙ、Ｌ
ａ１Ｃｅ、Ｐｒ、 Ｎｄ、 Ｐｍ、 Ｓｍ、 Ｇ
ｄ、 Ｔｂ、 Ｄｙ、 Ｈｏ 、Ｅｒ、 Ｔｍ、
Ｙｂ、Ｌｕ、 Ａ文、Ｇａ、Ｉｎ、およびＴＭからな
る群より選ばれる少なくとも一種の三価金属を表わし；
Ｘは、０文、Ｂｒ、および工からなる群より選ばれる少
なくとも−・種のハロゲンを表わし；そして、Ｘは１０
−２≦Ｘ≦０．５、ｙはｏ＜ｙ≦０．１である］の組成
式で表わされる蛍光体、
特開昭５９−２７９８０号公報に記載されているＢａＦ
ＸａｘＡ： ｙＥｕ２°［ただし、Ｘは、Ｃ１，Ｂｒ、
および工からなる群より選ばれる少なくとも一種のハロ
ゲンであり；Ａは、テトラフルオロホウ酸化合物の焼成
物であり；そして、Ｘは１０−６≦Ｘ≦ｏ、ｘ、ｙはｏ
＜ｙ≦０．１である］の組成式で表わされる蛍光体、
特開昭５９−４７２８９号公報に記載されているＢ ａ
ＦＸｓ ｘＡ ： ｙＥ ｕ２°［ただし、Ｘは、Ｃ１
、Ｂｒ、および工からなる群より選ばれる少なくとも一
種のハロゲンであり１Ａは、ヘキサフルオロケイ酸、ヘ
キサフルオロチタン酸およびヘキサフルオロジルコニウ
ム酸の一価もしくは二価金属の鳩からなるヘキサフルオ
ロ化合物群より選ばれる少なくとも一種の化合物の焼成
物であり；そして、Ｘは１０−６≦Ｘ≦ｏ、ｉ、ｙはｏ
＜ｙ≦０．１であるコの１！１成式で表わされる蛍光体
、特開１眉５９−５６４７９号公報に記・戒されている
ＢａＦＸ＊ ｘＮａＸ’：ａＥｕ” ［ただし、Ｘおよ
びＸ′は、それぞれＣ１、Ｂｒ、および■のうちの少な
くとも一種であり、Ｘおよびａはそれぞれ０＜ｘ≦２、
およびＯｖａ≦０．２である］の組成式で表わされる蛍
光体、
特開昭５９−５６４８０号公報に記載されているＭ ”
Ｆ Ｘ １１ｘ Ｎ ａ Ｘ ’ ： ｙ Ｅ ｕ
２°：ｚＡ［ただし、Ｍｌは、Ｂａ、Ｓｒ、およびＣａ
からなる群より選ばれる少なくとも一種のアルカリ土類
金属であり；ＸおよびＸ′は、それぞれＣ１，Ｂｒ、お
よびＩからなる群より選ばれる少なくとも一種のハロゲ
ンであり；Ａは、Ｖ、Ｃｒ、Ｍｎ、Ｆｅ、Ｃｏ、および
Ｎｉより選ばれる少なくとも一掃の遷移金属であり；そ
して、Ｘは０＜ｘ≦２、ｙはｏ＜ｙ≦ｏ、２、オヨびＺ
はＯ＜ｚ≦１０−２である］の組成式で表わされる蛍光
体、
特開ＩＩ／（５９−７５２００号公報ニ記載さｈ−ｃい
るＭ ” Ｆ Ｘ ａ ａ Ｍ ’ Ｘ ’ ＊ ｂ
Ｍ ’ ” Ｘ″２・ｃＭ”Ｘ”、＊ ｘＡ ： ｙＥ
ｕ” ［ただし、ＭｌはＢａ、Ｓｒ、およびＣａからな
る群より選ばれる少なくとも一種のアルカリ土類金属で
あり、 Ｍ ＋はＬｉ、Ｎａ、に、Ｒｈ、およびＣｓか
らなる群より選ばれる少なくとも一種のアルカリ金属で
あり；Ｍ゛はＢｅおよびＭｇからなる群より選ばれる少
なくとも一種の三価金属であり；Ｍ ＩはＡ文、Ｇａ、
Ｉｎ、およびＴｆＬからなる群より選ばれる少なくとも
一種の二価金属であり；Ａは金属酸化物であり：ＸはＣ
１、Ｂｒ、および工からなるＩＴより選ばれる少なくと
も一種のハロゲンであり；Ｘ’、Ｘ”、およびｘ”は、
Ｆ、（１１、Ｂｒ、および■からなる群より選ばれる少
なくとも一種のハロゲンであり；そして、ａは０≦ａ≦
かつａ＋ ｂ＋ｃ≧１０−６であり；Ｘは０＜ｘ≦０．
５、ｙはｏ＜ｙ≦０，２である］の組成式で表わされる
蛍光体、
特開ＩＶ（６０−８４３８１号公報に記載されているＭ
”Ｘ２ ＊ ａＭ”Ｘ’ ２ ： ｘＥｕ” ［ただし
、ＭｌはＢａ、ＳｒおよびＣａからなる群より選ばれる
少なくとも一種のアルカリ土類金属であり；ＸおよびＸ
′は０文、ＢｒおよびＩからなる群より選ばれる少なく
とも一種のハロゲンであって、かつＸ≠Ｘ′であり：そ
してａは０．１≦ａ≦１０．０、Ｘは０＜ｘ≦０．２で
ある］の組成式で表わされる輝尽性蛍光体、
特開昭６０−１０１１７３号公報に記載されているＭ”
ＦＸａ ａＭ’Ｘ’ ： ｘＥｕ” ［ただし、Ｍｕ
はＢａ、ＳｒおよびＣａからなる群より選ばれる少なく
とも一種のアルカリ土類金属であり；ＭＩはＲｂおよび
Ｃｓからなる群より選ばれる少なくとも一種のアルカリ
金属であり；Ｘは０文、Ｂｒおよび■からなる群より選
ばれる少なくともよび■からなる群より選ばれる少なく
とも一種のハロゲンであり；そしてａおよびＸはそれぞ
れＯ≦ａ≦４．０およびＯ＜ｘ≦０．２である］の組成
式で表わぎれる輝尽性蛍光体、
本出願人による特願昭６０−７０４８４号明細書に記載
されているＭ’Ｘ：ｘＢｉ［ただし、ＭｌはＲｂおよび
Ｃｓからなる群より選ばれる少なくとも・種のアルカリ
金属であり；ＸはＣ１゜ＢｒおよびＩからなる群より選
ばれる少なくとも・種のハロゲンであり：そしてＸはＯ
＜Ｘ≦０．２の範囲の数値である］の組成式で表わされ
る輝尽性蛍光体、
などを挙げることができる。0, SrO, BaO1ZnO, Au203. Y2O1,
La20. ,,In2O3,5i02. TiO2, Zr
O2, Gem2.5n02. Nb2O6, Ta205.
and at least one of -r h O2 (7), L
n is Eu, Tb, Ce, Tm, Dy, Pr, Ho, Nd
, Yb, Er, Sm, , j3, and Gd, X is at least one of Off, Br, and Engineering, and X and y are each s x i o-
'≦X≦0.5, and 0<y≦0.2] A phosphor is described in JP-A-56-116777 (B
at-x, M”,)F2 fist aBaX2:yEu,z
A [where Ml is at least one of beryllium, magnesylano, calcium, strontium, zinc, and cadmium; ::r 1. s, Nocchi', (> at least one kind, a, x, y, 〕, biZ1ma, wo each 0.
5≦a≦125, OG x <, , l, 10 =
≦y嘱2XlO-', and 0<zda10-2]
Phosphor expressed by the composition formula, JP-A-57-23673
It is described in the official publication (B a +-y, M
"H) F 2 * a13 a, X 22ylEu
, zB [where Ml is beryllium, mag;
1. Calciu 11. At least one species of strontium, 1ljffi, and cadmium, X is 414
, Do, Ning (there is at least one of the following: element, and iodine, and a, x, y, and 2 are each 0.5≦a≦1.
25.0≦X≦1.10-6≦y≦2×10゛' and 0<z≦2XlO-'T] A phosphor is described in JP-A-57-23675. It has been written (
flat-y, M" x) F2 ・aBaX2:y
Eu, zA [just l,,, M” 1.i<Liliu L
・, at least one of magnesium, calcium, strontium, zinc, and cadmium, X is at least one of chlorine, bromine, and iodine, A is at least one of arsenic and silicon, a, x, y
, and 2 are respectively 0.5≦aG1.25.0≦X≦
1.10-6≦y≦2×to-′, and Oz≦5X
A phosphor represented by the composition formula: -M” described in Publication No. 69281
OX:xCe [M” is Pr, Nd, Pm, S
m,, Eu, Tb, Dy, l-1o, Er, Tm, Yb
, and Bi, X is one or both of C9,8 and Br, and xl:io<x<0.
A phosphor represented by the following two compositional formulas:
a I-x M X /2 L X /2 F X
: y E IJ 2° [However, M is Li, Na, K
, Rh, and Cs; L represents the genus SC, Y, L;
a1Ce, Pr, Nd, Pm, Sm, G
d, Tb, Dy, Ho, Er, Tm,
represents at least one trivalent metal selected from the group consisting of Yb, Lu, A, Ga, In, and TM;
X represents at least one kind of halogen selected from the group consisting of 0, Br, and
-2≦X≦0.5, y is o<y≦0.1] A phosphor represented by the composition formula: BaF described in JP-A No. 59-27980
XaxA: yEu2° [where X is C1, Br,
and at least one halogen selected from the group consisting of; A is a fired product of a tetrafluoroboric acid compound;
A phosphor represented by the composition formula <y≦0.1], B a described in JP-A No. 59-47289
FXs xA : yE u2° [However, X is C1
, Br, and 1A is at least one halogen selected from the group consisting of hexafluorosilicic acid, hexafluorotitanic acid, and hexafluorozirconic acid. is a fired product of at least one selected compound; and X is 10-6≦X≦o, i and y are o
A phosphor expressed by the 1:1 formula of <y≦0.1, BaFX* ′ is at least one of C1, Br, and ■, and X and a are respectively 0<x≦2,
and Ova≦0.2], a phosphor represented by the composition formula M'' described in JP-A-59-56480.
F X 11x N a X': y E u
2°: zA [where Ml is Ba, Sr, and Ca
X and X' are at least one halogen selected from the group consisting of C1, Br, and I, respectively; A is V, Cr, Mn; , Fe, Co, and Ni; and X is 0<x≦2, y is o<y≦o, 2, and Z
is O<z≦10-2] A phosphor represented by the composition formula of JP-A II/(59-75200)
M'"X"2・cM"X", *xA: yE
u'' [However, Ml is at least one kind of alkaline earth metal selected from the group consisting of Ba, Sr, and Ca, and M + is at least one kind selected from the group consisting of Li, Na, Rh, and Cs. M is an alkali metal; M is at least one trivalent metal selected from the group consisting of Be and Mg; M is A, Ga,
is at least one divalent metal selected from the group consisting of In and TfL; A is a metal oxide; X is C
1, Br, and IT; X', X'', and x'' are
F, (at least one kind of halogen selected from the group consisting of (11, Br, and ■); and a is 0≦a≦
and a+b+c≧10-6; X is 0<x≦0.
5, y is o<y≦0,2] A phosphor represented by the composition formula:
"X2 * aM"
' is at least one kind of halogen selected from the group consisting of 0, Br, and I, and X≠X': and a is 0.1≦a≦10.0, and X is 0<x≦0. A stimulable phosphor represented by the composition formula:
FXa aM'X': xEu" [However, Mu
is at least one kind of alkaline earth metal selected from the group consisting of Ba, Sr and Ca; MI is at least one kind of alkali metal selected from the group consisting of Rb and Cs; at least one kind of halogen selected from the group consisting of; and a and X are respectively O≦a≦4.0 and O<x≦0.2] A stimulable phosphor that splits, M'X: is a metal; X is at least one halogen selected from the group consisting of C1°Br and I; and X is O
Examples include a stimulable phosphor represented by the composition formula <a numerical value in the range of X≦0.2].
また、上記特開昭６０−８４３８１号公報に記載コれて
いるＭ”Ｘ２ｅ ａＭ’Ｘ’ ２： ｘＥｕ”輝尽性蛍
光体には、以ｆに示すような添加物がＭ ” Ｘ ２・
ａＭ”Ｘ’２１モル当り以ドの割合で含まれていてもよ
い。In addition, the M"X2e aM'X' 2:
It may be contained in a proportion of less than 21 moles of aM''X'.
特開昭６０−１６６３７９号公報に記載されているｂＭ
’Ｘ” （ただＬ、ＭＩはＲｂおよびＣ３からなる群
より選ばれる少なくとも一種のアルカリ金属であり、Ｘ
”はＦ、ＣＩ、ＢｒおよびＩからなる群より選ばれる少
なくとも一種のハロゲンであり、モしてｂはｏ＜ｂ≦１
０．０である）；特開昭６０−２２１４８３号公報に記
載されているｂＫＸ″ａ ｃＭｇＸ”２ｅ ｄＭ”Ｘ″
”、（ただし、Ｍ厘はＳｃ、Ｙ、Ｌａ、ＧｄおよびＬｕ
からなる群より選ばれる少なくとも一種の三価金属であ
り、Ｘ”、ｘｌおよびＸ“はいずれもＦ、Ｃ１、Ｂｒお
よび■からなる群より選ばれる少なくとも一種のハロゲ
ンであり、そしてす、ｃおよびｄはそれぞれ、０≦ｂ≦
２．０．０≦Ｃ≦２゜０・ ０≦ｄ≦２・０であって、
かつ２ Ｘ １０−’≦ｂ＋ｃ＋ｄである）；本出願人
による特願昭５９−８４３５６号ＩＪ］細ｉ９に記載さ
れているＶＢ（ただし、ｙは２ Ｘ １０−’≦ｙ≦２
Ｘ１０−’である）；特願昭５９−８４３５８号明細書
に記載されているｂＡ（ただし、Ａは５ｉ０２およびＰ
２Ｏ５からなる群より選ばれる少なくとも一種の酸化物
であり、そしてｂは１０−４≦ｂ≦２ Ｘ １０−’で
ある）；特願昭５９−２４０４５２号明細書に記載され
ているｂｓｉｏ（ただし、ｂはｏ＜ｂ≦３ Ｘ １０−
２である）；特願昭５９−２４０４５４号明細書に記・
成されているｂＳｎＸ″２（ただし、Ｘ′′はＦ、 Ｃ
ＪＪ、Ｂｒおよび■からなる群より選ばれる少なくとも
一種のハロゲンであり、そしてｂはｏ＜ｂ≦１Ｏ−３で
ある）；特願昭６０−７８０３３号明細−）に記載され
ているｂＣｓＸ″＊ｃＳｎＸ”２（ただし、Ｘ″および
ＸｌはそれぞれＦ、ＣＬｌ、Ｂｒおよび工からなる群よ
り選ばれる少なくとも一種のハロゲンであり、モしてｂ
およびＣはそれぞれ、ｏ＜ｂ≦１０．０および１０−６
≦Ｃ≦２ Ｘ １０−２である）：および特願昭６０−
７８０３５号明細、！）に記載されているｂｃ：ｓＸ″
ｅｙＬｎ”（ただし、ｘ”はＦ、Ｃ１，Ｂｒおよび■か
らなる群より選ばれる少なくとも一種のハロゲンであり
、ＬｎはＳｃ、Ｙ、Ｃｅ、Ｐｒ、Ｎｄ、Ｓｍ、Ｇｄ、Ｔ
ｂ、ａｙ。bM described in JP-A-60-166379
'X' (However, L and MI are at least one kind of alkali metal selected from the group consisting of Rb and C3,
” is at least one kind of halogen selected from the group consisting of F, CI, Br and I, and b is o<b≦1
0.0); bKX″a cMgX″2e dM″X″ described in JP-A No. 60-221483
”, (However, M is Sc, Y, La, Gd and Lu
X", xl and X" are all at least one halogen selected from the group consisting of F, C1, Br and ■, and d is 0≦b≦, respectively.
2.0.0≦C≦2゜0・0≦d≦2.0,
and 2 X 10-'≦b+c+d);
bA described in Japanese Patent Application No. 59-84358 (However, A is 5i02 and P
at least one oxide selected from the group consisting of 2O5, and b satisfies 10-4≦b≦2X10-'); , b is o<b≦3 X 10−
2); described in the specification of Japanese Patent Application No. 59-240454.
bSnX″2 (where X″ is F, C
bCsX''cSnX"2 (where X" and Xl are each at least one kind of halogen selected from the group consisting of F, CLl, Br, and
and C are o<b≦10.0 and 10-6, respectively
≦C≦2×10-2): and patent application 1986-
Details of No. 78035! ) written in bc:sX″
eyLn" (where x" is at least one kind of halogen selected from the group consisting of F, C1, Br and ■, and Ln is Sc, Y, Ce, Pr, Nd, Sm, Gd, T
b, ay.
Ｈｏ、Ｅｒ、Ｔｍ、ＹｂおよびＬｕからなる群より選ば
れる少なくとも一種の希に類元素であり、そしてｂおよ
びｙはそれぞれ、ｏ＜ｂ≦１０．０およびｌＯ″６≦ｙ
≦１．８Ｘ１０”’である）。At least one rare element selected from the group consisting of Ho, Er, Tm, Yb and Lu, and b and y are o<b≦10.0 and lO″6≦y, respectively.
≦1.8×10'').
Ｌ記の輝尽性蛍光体のうちで、二価ユーロピウム賦活ア
ルカリ土類金属ハロゲン化物系蛍光体および希土類元素
賦活希土類オキシハロゲン化物系蛍光体は高輝度の輝尽
発光を示すので特に好ましい。ただし、本発明に用いら
れる輝尽性蛍光体はト述の蛍光体に限られるものではな
く、放射線を照射したのちに励起光を照射した場合に輝
尽発光を示す蛍光体であればいかなるものであってもよ
い。Among the stimulable phosphors listed in L, divalent europium-activated alkaline earth metal halide phosphors and rare earth element-activated rare earth oxyhalide phosphors are particularly preferred because they exhibit high-intensity stimulated luminescence. However, the stimulable phosphor used in the present invention is not limited to the phosphors mentioned above, but any phosphor that exhibits stimulated luminescence when irradiated with radiation and then irradiated with excitation light. It may be.
蛍光体層の結合剤の例としては、ゼラチン等の蛋白質、
デキストラン等のポリサッカライド、またはアラビアゴ
ムのような天然高分子物質：および、ポリビニルブチラ
ール、ポリ酢酸ビニル、二］・ロセルロース、エチルセ
ルロース、塩化ビニリデン・塩化ビニルコポリマー、ポ
リアルキル（メタ）アクリレート、塩化ビニル・酢酸ビ
ニルコポリマー、ポリウレタン、セルロースアセテート
ブチレート、ポリビニルアルコール、線状ポリエスチル
など五２な合成高分子物質などにより代表きれる結合剤
を挙げることができる。このような結合剤のなかで特に
々ｆましいものは、ニトロセルロー ス、線状ポリエス
テル、ポリアルキル（メタ）７クリレート、二１・＋７
セル「ｌ−スと線状ポリエステルとの混合物および一ト
ロセルロースとポリアルキル（メタ）アクリレートとの
混合物である。Examples of binders for the phosphor layer include proteins such as gelatin,
Polysaccharides such as dextran, or natural polymeric substances such as gum arabic: and polyvinyl butyral, polyvinyl acetate, dicellulose, ethylcellulose, vinylidene chloride/vinyl chloride copolymer, polyalkyl (meth)acrylate, vinyl chloride Binding agents include a wide variety of synthetic polymeric substances such as vinyl acetate copolymer, polyurethane, cellulose acetate butyrate, polyvinyl alcohol, and linear polyester. Particularly desirable among such binders are nitrocellulose, linear polyesters, polyalkyl (meth)7 acrylates, 21.+7
These are a mixture of cellulose and linear polyester, and a mixture of cellulose and polyalkyl (meth)acrylate.
なお、こわらの結合剤は架橋剤１こよって架橋されたも
のであってもよい。In addition, the stiff binder may be crosslinked with crosslinking agent 1.
イ１？光体層は、たとλば、次のような方法Ｖより支持
体］二に形成することができる。I1? The light layer can be formed on the support by the following method V, for example.
まず１−記の輝尽性蛍光体、結合剤とを適当な溶剤に添
加！、２、これを充分に混合して、結合剤溶液中に消・
光体粒子が均一・に分散した塗布液を調製する。また、
蛍光体層を着色剤によって着色する場合には、上記の輝
尽性蛍光体、着色剤および結合剤どを適当な溶剤に添加
し、これを充分に混合しで、結合剤溶液中に蛍光体粒子
および着色剤が均一に分散した塗Ｉｌｉ液を：ＪＪ製す
る。First, add the stimulable phosphor and binder described in 1- to a suitable solvent! , 2. Mix this thoroughly and add it to the binder solution.
Prepare a coating solution in which the photon particles are uniformly dispersed. Also,
When coloring the phosphor layer with a colorant, add the above-mentioned stimulable phosphor, colorant, binder, etc. to a suitable solvent, mix thoroughly, and add the phosphor to the binder solution. A coating liquid in which particles and colorant are uniformly dispersed is manufactured by JJ.
〜ミ布液２１製用の溶剤の例としては、メタノール、エ
タノール、ｎ−ブコバノール、ｎ−ブタメールなどの低
級アルコール：メチレンクロライド、エチレンクロライ
ドなどの塩素原子含有炭化水素；アセトン、メチルエチ
ルケトン、メチルイソブチルケトンなどのケトン：酢酸
メチル、酢酸エチル、酢酸ブチルなどの低級脂肪酸と低
級アルコールとのエステル；ジオキサン、エチレングリ
」−ルモノｙｌ 、ｆ ）レエーテル、エチレングリコ
ールモンメチルエーデルなどのエーテル：そして、それ
らの混合物を挙げることができる。~ Examples of solvents for making Mifuzu 21 include lower alcohols such as methanol, ethanol, n-bucobanol, and n-butamel; chlorine-containing hydrocarbons such as methylene chloride and ethylene chloride; acetone, methyl ethyl ketone, and methyl isobutyl. Ketones such as ketones: esters of lower fatty acids and lower alcohols such as methyl acetate, ethyl acetate, butyl acetate; ethers such as dioxane, ethylene glycol monoyl, f) ether, ethylene glycol monomethyl ether: and their Mixtures may be mentioned.
塗布液における結合剤と輝尽性蛍光体との混合比は、［
１的とする放射線像変換パネルの特性、蛍光体の種類な
どによって異なるが、一般には結合剤と蛍光体との混合
比は、ｌ：１乃至１：１００（重量比）の範囲から選ば
れ、そして特に１：８乃至１．：４０（重量比）の範囲
から選ぶことが好ましい。The mixing ratio of the binder and the stimulable phosphor in the coating solution is [
Generally, the mixing ratio of the binder and the phosphor is selected from the range of 1:1 to 1:100 (weight ratio), although it varies depending on the characteristics of the radiation image conversion panel to be used, the type of phosphor, etc. And especially 1:8 to 1. :40 (weight ratio).
また、塗布液における結合剤と着色剤との混合比は、蛍
光体の種類、含有量などによって異なるが、−・般には
結合剤と着色剤との混合比は、１：１０乃’１ｊｉ０５
：１（重量比）の範囲から選ばれる。In addition, the mixing ratio of the binder and coloring agent in the coating solution varies depending on the type and content of the phosphor, but generally speaking, the mixing ratio of the binder and coloring agent is 1:10 to 1:10.
:1 (weight ratio).
なお、塗Ｉｊｉ液には、該塗布液中における蛍光体の分
散性を向ｊ二させるための分散剤、また、形成後の蛍光
体層中における結合剤と蛍光体との間の結合力を向１．
させるための可塑剤などの種々の添加剤が混合されてい
てもよい。そのような目的に用いられる分散剤の例とし
ては、フタル酸、ステアリン酸、カプロン酸、親油性界
面活性剤などを挙げることができる。そしてｉｉｆ ｆ
ｌｊ剤の例としては、燐酸トリク。ニル、燐酸トリクレ
ジル、燐酸ノフェニルなどの燐酸１スプル；フタル酸ジ
ェチｔし、フタル酸シス）・ギシＴトルなどの７タル酸
ニスｉル；グリコール酸エチルフタリルエチル、グリコ
ール酸ブチルクタリルブトルなどのグリコール酸１スプ
ル；そして、トリエチレングリコールとアジピン酸との
ポリエステル、ジエチレ〉′グリコールとコハク酸との
ポリエステルなどのボリエ升レンゲリコールと脂肪族二
塩ノ、（酸とのポリエステルなどを挙げることができる
。The coating liquid contains a dispersant to improve the dispersibility of the phosphor in the coating liquid, and a dispersant to improve the bonding force between the binder and the phosphor in the phosphor layer after formation. Direction 1.
Various additives, such as plasticizers, may be mixed to make the material more durable. Examples of dispersants used for such purposes include phthalic acid, stearic acid, caproic acid, lipophilic surfactants, and the like. and iif f
Examples of lj agents include tric phosphate. Phosphoric acids such as tricresyl phosphate, tricresyl phosphate, and nophenyl phosphate; 7-thalic acid salts such as phthalic acid, tricresyl phosphate, and phthalic acid; ethyl phthalyl ethyl glycolate, butyl butyl glycolate, etc. polyesters of triethylene glycol and adipic acid, polyesters of diethyl glycol and succinic acid; I can do it.
また、１−記塗布液には、該塗布液中における蛍光体お
よび着色剤の分散性を向トさせるための分散剤を添加し
てもよい、特に、上記着色剤のうち顔料に対しては、既
に分散剤として公知の非イオン系界面活性剤の中から適
二１ｒ選択して用いることができる。In addition, a dispersant may be added to the coating solution described in 1- above to improve the dispersibility of the phosphor and colorant in the coating solution. However, suitable nonionic surfactants can be selected and used as dispersants from nonionic surfactants known as dispersants.
１−記のようにして調製された蛍光体と結合剤とを含有
する塗布液、あるいは蛍光体、結合剤および着色剤を含
有する９ ４ｉ液を、次に支持体の表面に均一に塗布す
ることにより塗布液の塗膜を形成する。この塗ＩＨｊ操
作は、通常の塗布手段、たとえばドクターブレード、ロ
ールコータ−、ナイフコーターなどを用いることにより
行なうことができる。1- The coating solution containing the phosphor and binder prepared as described above or the 94i solution containing the phosphor, binder and colorant is then uniformly applied to the surface of the support. By doing so, a coating film of the coating liquid is formed. This coating IHj operation can be carried out using ordinary coating means such as a doctor blade, roll coater, knife coater, etc.
ついで、形成された塗膜を徐々に加熱することにより乾
燥して、支持体上への蛍光体層の形成を完ｒする。The formed coating film is then dried by gradually heating to complete the formation of the phosphor layer on the support.
なお、蛍光体層は、必ずしも１−記のように支持体−に
に塗１．ｊＭを直接塗布して形成する必要はなく、例え
ば、別にガラス板、金属板、プラスチフクシートなどの
シート上に塗布液を塗布し乾燥することにより蛍光体層
を形成した後、これを支持体上に押圧するか、あるいは
接着剤を用いるなどして支持体と蛍光体層とを接合して
もよい。Note that the phosphor layer is not necessarily coated on the support as described in 1. It is not necessary to directly apply JM to form the phosphor layer; for example, after forming a phosphor layer by separately applying a coating liquid onto a sheet such as a glass plate, metal plate, plastic sheet, etc. and drying it, apply this to a support. The support and the phosphor layer may be bonded together by pressing onto the support or by using an adhesive.
また、蛍光体層は、上記のように結合剤を用いて塗４１
形成する方法以外に輝尽゛性蛍光体を支持体の上に蒸着
することなどにより形成することもできる。具体的には
例えば、蛍光体層の形成をピー拳エフ・カルシアとエル
・エッチ・ブリックスナー（Ｐ、Ｆ、ＣＡＲＣ：ＩＡ
ＡＮＤ Ｌ、）１．ＢＲＩＸＮＥＲ）が行ナツタ真
空蒸着法（ＥＬＥＣ：ＴＲ０ＮＩＧＳ ＡＮＤ ０ＰＴ
ＩＣＳ、 Ｔｈ１ｎ ５ｏｌｉｄ Ｆｉｔ■、Ｌ亜−（
１９８４） ８９−９５ ）を用いることにより行なう
ことができる。Further, the phosphor layer is coated with a binder as described above.
In addition to the formation method, it can also be formed by vapor depositing a stimulable phosphor on a support. Specifically, for example, the formation of the phosphor layer was carried out by P.F. Calcia and L.H. Brixner (P, F, CARC: IA
AND L, )1. BRIXNER) Natsuta vacuum evaporation method (ELEC:TR0NIGS AND 0PT
ICS, Th1n 5olid Fit■, L-(
1984) 89-95).
この蒸若法により形成された蛍光体層の表面は優れた表
面平滑性を有するため、この上に多層膜フィルタを形成
するのに極めて有利である。Since the surface of the phosphor layer formed by this vaporization method has excellent surface smoothness, it is extremely advantageous for forming a multilayer film filter thereon.
蛍光体層の層厚は、目的とする放射線像変換パネルの特
性、蛍光体の種類、結合剤を用いて形成する場合には、
結合剤と蛍光体との混合比などによって異なるが、通常
は２０ルｍ乃至ｌｒｎｍとする。ただし、この層厚は５
０乃至５００ ｇｍとするのが好ましい。The thickness of the phosphor layer depends on the characteristics of the intended radiation image conversion panel, the type of phosphor, and when forming it using a binder.
Although it varies depending on the mixing ratio of the binder and the phosphor, it is usually 20 lrnm to lrnm. However, this layer thickness is 5
Preferably, it is between 0 and 500 gm.
次に、蛍光体層の支持体に接する側とは反対側の表面に
は、本発明の特徴的な要件である多層膜フィルタが設け
られる。Next, a multilayer filter, which is a characteristic feature of the present invention, is provided on the surface of the phosphor layer opposite to the side in contact with the support.
未発ＩＩにおいて多層膜フィルタは、蛍光体層に含まれ
る輝尽性蛍光体を励起するための励起光の入射角度が０
〜５°の範囲にある場合に７０％以上の光透過率を有し
、かつ励起光の入射角度が３０°以上である場合に６０
％以上の光反射率を有するものである。好ましくは、励
起光の入射角度がＯ〜５°の範囲にある場合に８０％以
上の光透過率を有し、かつ励起光の入射角度が３０°以
上である場合に７０％以上の光反射率を有するものであ
る。すなわち、多層膜フィルタは、少なくとも輝尽性蛍
光体の励起波長領域に含まれる一つの波長に対してこの
ような角度依存の透過および反射特性を有している必要
がある。好ましくは、蛍光体の励起スペクトルのピーク
付近の波長に対して上記透過および反射特性を満足する
ものである。In Unemission II, the multilayer filter has an angle of incidence of 0 for excitation light to excite the stimulable phosphor contained in the phosphor layer.
60% when the incident angle of the excitation light is 30° or more and has a light transmittance of 70% or more when the angle is in the range of ~5°
% or more. Preferably, it has a light transmittance of 80% or more when the angle of incidence of the excitation light is in the range of 0 to 5 degrees, and a light reflection of 70% or more when the angle of incidence of the excitation light is 30 degrees or more. It has a certain rate. That is, the multilayer filter needs to have such angle-dependent transmission and reflection characteristics for at least one wavelength included in the excitation wavelength region of the stimulable phosphor. Preferably, the above-mentioned transmission and reflection characteristics are satisfied for a wavelength near the peak of the excitation spectrum of the phosphor.
一例として、市販の放射線像変換パネルには通常・二価
ユーロピウム賦活弗化臭化／くリウム系蛍光体が使用さ
れており、励起光としてＨｅ−Ｎｅレーザー光（波長：
６３３ｎｍ）が用いられている。従って、蛍光体層がこ
の輝尽性蛍光体を含有する場合には、多層膜フィルタは
６３３ｎｍの励起波長に対する光透過率が上記のような
角度依存性を有するものであればよい。As an example, commercially available radiation image storage panels use normal divalent europium-activated fluorobromide/curium-based phosphors, and the excitation light is He-Ne laser light (wavelength:
633 nm) is used. Therefore, when the phosphor layer contains this stimulable phosphor, the multilayer filter may be one in which the light transmittance with respect to the excitation wavelength of 633 nm has the angle dependence as described above.
また通常、輝尽発光光の検出も蛍光体層側の表面から行
なわれるから、パネルの感度の点から、多層膜フィルタ
は蛍光体の輝尽発光波長における光透過率が角度に関係
なく高いのが好ましい。一般に、入射角度がＯ〜４０°
の範囲にある場合に発光のピーク波長における透過率が
６０％以上であるのが好ましく、より好ましくは８０％
以上である。従って、上記二価ユーロピウム賦活弗化臭
化バリウム系蛍光体については、約３９０ｎｍのピーク
波長に対して上記のような透過率を有することが望まし
い。Furthermore, normally, the detection of stimulated emission light is also performed from the surface on the phosphor layer side, so from the viewpoint of panel sensitivity, multilayer filters have a high light transmittance at the stimulated emission wavelength of the phosphor regardless of the angle. is preferred. Generally, the angle of incidence is O~40°
The transmittance at the peak wavelength of light emission is preferably 60% or more, more preferably 80%.
That's all. Therefore, it is desirable that the divalent europium-activated barium fluoride bromide phosphor has the above-mentioned transmittance for a peak wavelength of about 390 nm.
多層膜フィルタは、透過スペクトルにおける透過４：？
の幅が広いショートパスフィルタであってもよいし、あ
るいは透過帯の幅が極めて狭いバンドパスフィルタであ
ってもよい。The multilayer filter has a transmission spectrum of 4:?
It may be a short-pass filter with a wide width, or a band-pass filter with an extremely narrow transmission band.
本発明に用いられる多層膜フィルタの透過スペクトル、
反射スペクトルおよびその角度依存性の例を第３図〜第
６図にそれぞれ示す。Transmission spectrum of the multilayer filter used in the present invention,
Examples of reflection spectra and their angular dependence are shown in FIGS. 3 to 6, respectively.
第３図は、ショートパスフィルタの入射角度０Ｏ１３０
″および４５°それぞれにおける透過スペクトルである
。Figure 3 shows the incident angle of the short pass filter at 0O130.
'' and 45°, respectively.
第４図は、ショートハスフィルタについて入射角度と透
過率との関係および入射角度と反射率との関係をそれぞ
れ示すグラフである。第４図において、６３３ｎｍは上
記二価ユーロピウム賦活弗化臭化バリウム系蛍光体の励
起波長に相当し、３９０ｎｍは輝尽発光のピーク波長に
相当する。FIG. 4 is a graph showing the relationship between the incident angle and the transmittance and the relationship between the incident angle and the reflectance for the short lotus filter. In FIG. 4, 633 nm corresponds to the excitation wavelength of the divalent europium-activated barium fluoride bromide phosphor, and 390 nm corresponds to the peak wavelength of stimulated luminescence.
第５図は、バンドパスフィルタの入射角度０゜における
透過スペクトルである。FIG. 5 shows the transmission spectrum of the bandpass filter at an incident angle of 0°.
ｉ ６１．４ ｉ；ｔ、バントハスフィルタについて３
９０ｎｍおよび６３３ｎｍにおける入射角度と透過率と
の関係および入射角度と反射率との関係をそれぞれ示す
グラフである。i 61.4 i;t, 3 about the Bandhus filter
3 is a graph showing the relationship between the incident angle and the transmittance and the relationship between the incident angle and the reflectance at 90 nm and 633 nm, respectively.
多層膜フィルタは、屈折率の異なる二種以上の物質が光
の波長の１／４程度の厚さで逐次積層されたものである
。多層膜フィルタには公知の光学薄膜に使用されている
各種の物質を用いることができるが、具体的にはＳｉＯ
２、ＭｇＦ２などの低屈折率物質およびＴｉｅ□、Ｚｒ
Ｏ２，ＺｎＳなどの高屈折率物質を挙げることができる
。A multilayer film filter is made by sequentially laminating two or more types of materials with different refractive indexes to a thickness of about 1/4 of the wavelength of light. Various materials used in known optical thin films can be used for the multilayer filter, but specifically, SiO
2. Low refractive index materials such as MgF2 and Tie□, Zr
Examples include high refractive index substances such as O2 and ZnS.
多層膜フィルタは、たとえば上記物質からなる薄膜を真
空蒸着、スパッタリング、イオンブレーティングなどの
方法によって、直接蛍光体層の表面に、あるいは多層膜
フィルタの上に保護膜を打設する場合には保護膜形成用
のシート表面に数層から致ト層に積層して形成すること
により設けることができる。For multilayer filters, for example, when a thin film made of the above substances is deposited directly on the surface of the phosphor layer, or a protective film is deposited on top of the multilayer filter, it is necessary to protect it. It can be provided by laminating several to several layers on the surface of a sheet for film formation.
多層膜フィルタの製造に際して、使用する物質（Ｅ折半
）および各層の膜厚を制御することにより、使用される
輝尽性蛍光体に合わせて上記の特性を右する種々のフィ
ルタを得ることができる。When manufacturing multilayer filters, by controlling the substance used (E/50) and the film thickness of each layer, it is possible to obtain a variety of filters with the above characteristics depending on the stimulable phosphor used. .
一般に、多層膜フィルタ全体の膜厚は約０．１乃至１０
ルｍの範囲にある。Generally, the thickness of the entire multilayer filter is about 0.1 to 10
It is within the range of le m.
保護ｊ膜形成用の透明シートの例としては、ポリエチレ
ンテレフタレート、ポリエチレン、ポリ塩化ビニリデン
、ポリアミドなどからなるプラスチックシート；および
ガラス板を挙げることができる。この透明シートの表面
には予め、表面を清浄にするための各種の表面処理、ｆ
塗処理などが施されていてもよい。Examples of the transparent sheet for forming the protective film include plastic sheets made of polyethylene terephthalate, polyethylene, polyvinylidene chloride, polyamide, etc., and glass plates. The surface of this transparent sheet is preliminarily treated with various surface treatments to clean the surface.
A coating treatment or the like may be applied.
保護膜および多層膜フィルタは、たとえば、上記多層膜
フィルタを該透明シート上に形成したのち、これを蛍光
体層の表面に適当な接着剤を用いて接着することにより
、蛍光体層上にＪジけることができる。また、多層膜フ
ィルタを蛍光体層上に直接真空蒸着法などにより設けた
場合には、保護膜は、上記透ＩＪＪシートを多層膜フィ
ルタの表面に適当な接着剤を用いて接着することにより
形成すること以外に、例えば、酢酸セルロース、ニトロ
セルロースなどのセルロース誘導体；あるいはポリメチ
ルメタクリレート、ポリビニルブチラール、ポリビニル
ホルマール、ポリカーボネート、ポリ酢酸ビニル、塩化
ビニル・酢酸ビニルコポリマーなどの合成高分子物質の
ような透明な高分子物質を適当な溶媒に溶解して調製し
た溶液を多層膜フィルタの表面に塗布する方法によって
も形成することができる。The protective film and the multilayer filter can be prepared, for example, by forming the multilayer filter on the transparent sheet and then adhering it to the surface of the phosphor layer using a suitable adhesive. I can get away with it. In addition, when the multilayer filter is provided directly on the phosphor layer by vacuum evaporation, etc., the protective film is formed by adhering the transparent IJJ sheet to the surface of the multilayer filter using an appropriate adhesive. Transparent materials such as cellulose derivatives such as cellulose acetate and nitrocellulose; or synthetic polymeric materials such as polymethyl methacrylate, polyvinyl butyral, polyvinyl formal, polycarbonate, polyvinyl acetate, and vinyl chloride-vinyl acetate copolymers. It can also be formed by applying a solution prepared by dissolving a polymeric substance in an appropriate solvent onto the surface of a multilayer filter.
保護膜および／または接着剤層がＬ２着色剤によって着
色されていてもよい。保３［が着色される場合には、そ
のいずれか一方の面が着色されていてもよいし、両面が
着色されていてもよい。あるいは保護膜全体が着色され
ていてもよい。着色力法としては、ｉ：述したように着
色剤含有塗布液を別に調製して塗布する方法、あるいは
保護ｌ模形成用塗１■ｊ液に着色剤を混合させて塗布す
る方法などが採られる。The protective film and/or the adhesive layer may be colored with an L2 colorant. When the holder 3 is colored, either one side thereof or both sides thereof may be colored. Alternatively, the entire protective film may be colored. As the tinting power method, as described above, a method of preparing a coating solution containing a coloring agent separately and applying it, or a method of mixing a coloring agent with a coating solution for protection model formation 1.j. It will be done.
なお、本発明の放射線像変換パネルは、特開昭５５−１
４６４４７号公報に記・成されているように、画像の鮮
鋭度を向［−させる［Ｉ的でその蛍光体層中に白色粉体
が分散されていてもよｌ、Ｘ。Note that the radiation image conversion panel of the present invention is disclosed in Japanese Patent Application Laid-Open No. 55-1
As described in Japanese Patent No. 46447, white powder may be dispersed in the phosphor layer to improve the sharpness of the image.
次に本発明の実施例および比較例を記載する。Next, Examples and Comparative Examples of the present invention will be described.
ただし、これらの各個は未発［ｙ■を制限するものでは
ない。However, each of these does not limit the unreleased [y■.
［実施例１］
約３５０℃に加熱した透明なガラス板（保護膜用シート
、厚み：約１ｍｍ）を真空容器内に入れ、ＴｉＯ□およ
び５ｉ０２を用いて各層の膜厚を制御しながら交互に繰
り返し真空蒸着することにより、ガラス板上に、第４図
にそれぞれに示した透過および反射特性を有する多層膜
フィルタ（ショートハスフィルタ）を約２ ｕＬｍの総
膜厚（約２０層積層）で形成した。[Example 1] A transparent glass plate (protective film sheet, thickness: about 1 mm) heated to about 350°C was placed in a vacuum container, and TiO□ and 5i02 were used to alternately control the film thickness of each layer. By repeated vacuum deposition, a multilayer filter (short lotus filter) having the transmission and reflection characteristics shown in Fig. 4 is formed on the glass plate with a total film thickness of approximately 2 uLm (approximately 20 layers laminated). did.
次に、粉末状の二価ユーロピウム賦活弗化臭化バリウム
蛍光体（Ｂ ａ Ｆ Ｂ ｒ ：Ｏ，０ＯＩＥ ｕ ”
）と線状ポリエステル樹脂との混合物にメチルエチルケ
トンを添加し、硝化度１１．５％のニトロセルロースを
添加し、更に蛍光体１００ｇ当りｌ Ｏｍ ｇの群”ｔ
”； （顔料； Ｎｏ ８８００第−化成工業■製）を
添加して、蛍光体および着色剤を分散状態で含有する分
散液を調製した。この分散液に燐酸）・リクレジル、ｎ
−ブタノールそしてメチルエチルケトンを添加したのち
、プロペラミキサーを用いて充分に攪拌混合して、蛍光
体及び着色剤が均一に分散し、かつ結合剤と蛍光体との
混合比が１ ：１０、粘度が２５〜３５ＰＳ（２５℃）
の塗布液を調製した。Next, powdered divalent europium-activated barium fluoride bromide phosphor (B a F B r :O,0OIE u ”
) and linear polyester resin, methyl ethyl ketone was added, nitrocellulose with a degree of nitrification of 11.5% was added, and a group of l Om g per 100 g of phosphor was added.
(Pigment; No. 8800 manufactured by Dai-Kasei Kogyo ■) was added to prepare a dispersion containing a phosphor and a colorant in a dispersed state.To this dispersion, phosphoric acid), licresil, n
- After adding butanol and methyl ethyl ketone, stir and mix thoroughly using a propeller mixer to ensure that the phosphor and colorant are uniformly dispersed, and the mixing ratio of binder and phosphor is 1:10, and the viscosity is 25. ~35PS (25℃)
A coating solution was prepared.
次いで、水モにといた多層膜フィルタの設けられたガラ
ス板上に塗布液をドクターブレードを用いて均一に塗布
した。そして塗布後に、塗膜が形成されたガラス板を乾
燥器内に入れ、この乾燥器の内部の温度を２５℃から１
００℃に徐々に上昇させて、塗膜の乾燥を行なった。こ
のようにして、多層膜フィルタ上に層厚が２５０ｕＬｍ
の青色に着色された蛍光体層を形成した。Next, the coating liquid was uniformly applied using a doctor blade onto a glass plate provided with a multilayer film filter which had been soaked in water. After coating, the glass plate on which the coating film was formed was placed in a dryer, and the temperature inside the dryer was increased from 25°C to 1°C.
The coating film was dried by gradually increasing the temperature to 00°C. In this way, the layer thickness is 250 uLm on the multilayer filter.
A blue colored phosphor layer was formed.
次に、着色蛍光体層上に、カーボンブラック練り込みポ
リエチレンテレフタレートシート（支持体、厚み：２５
０ｇｍ）をポリエステル系接着剤を用いて接着した。Next, a carbon black kneaded polyethylene terephthalate sheet (support, thickness: 25 mm) is placed on the colored phosphor layer.
0gm) was adhered using a polyester adhesive.
このようにして支持体１着色蛍光体層、多層膜フィルタ
および透明保護膜（ガラス板）から構成された放射線像
変換パネルを製造した。In this way, a radiation image storage panel was produced, which consisted of the colored phosphor layer of the support 1, the multilayer filter, and the transparent protective film (glass plate).
［実施例２］
実施例１において、ガラス板上にＴ ｉ Ｏ２およびＳ
ｉ０２を真空蒸着することにより、第６図にそれぞれ
示した透過および反射特性を有する多層膜フィルタ（バ
ンドパスフィルタ）を約２ ｇ ｍの膜厚で設けること
以外は、実施例１の方法と同様の操作を行なうことによ
り、支持体、着色蛍光体層、多層膜フィルタおよび透明
保護膜から構成された放射線像変換パネルを製造した。[Example 2] In Example 1, T i O2 and S were deposited on a glass plate.
The method was the same as in Example 1, except that a multilayer filter (bandpass filter) having the transmission and reflection characteristics shown in FIG. 6 was provided with a film thickness of about 2 gm by vacuum evaporating i02. By performing the following operations, a radiation image storage panel consisting of a support, a colored phosphor layer, a multilayer filter, and a transparent protective film was manufactured.
Ｕ比較例１］
実施例１において、ガラス板上に多層膜フィルタを設け
ないこと以外は実施例の方法と同様の操作を行なうこと
により、支持体、着色蛍光体層および透明保護膜から構
成された放射線像変換パネルを製造した。U Comparative Example 1] In Example 1, by performing the same operation as in the method of Example except that the multilayer film filter was not provided on the glass plate, a material composed of a support, a colored phosphor layer, and a transparent protective film was obtained. A radiation image conversion panel was manufactured using the following methods.
次に、各放射線像変換パネルについて、以下の感度試験
を行なうことにより評価を行なった。Next, each radiation image conversion panel was evaluated by performing the following sensitivity test.
放射線像変換パネルに、管電圧８０ＫＶｐのＸ線を照射
したのち、Ｈｅ−Ｎｅレーザー光（波長＋６３３ｎｍ）
で励起して感度を測定した。After irradiating the radiation image conversion panel with X-rays with a tube voltage of 80 KVp, a He-Ne laser beam (wavelength + 633 nm) is applied.
The sensitivity was measured by excitation.
得られた結果を第１表にまとめて示す。The results obtained are summarized in Table 1.
第１表
相対感度
実施例１ ２２０
実施例２ ２００
比較例１ １００
第１表に示された結果から明らかなように、未発ＩＪＩ
に係る多層膜フィルタが設けられた放射線像変換パネル
（実施例１および２）は、公知の多層膜フィルタが設け
られていない放射！ａ像変換パネル（比較例１）と比較
して、感度が著しく向にした。Table 1 Relative Sensitivity Example 1 220 Example 2 200 Comparative Example 1 100 As is clear from the results shown in Table 1, undeveloped IJI
The radiation image conversion panels (Examples 1 and 2) equipped with multilayer filters according to Compared to the a-image conversion panel (Comparative Example 1), the sensitivity was significantly improved.
第１図は、未発１月に係る放射線像変換パネルの態；様
を示す断面図である。
第２図は、本発明に係る放射線像変換パネルの別の態様
を示す断面図である。
ｌ：支持体、２：蛍光体層、
３：多層膜フィルタ、４：光反射層
温３図は、本発明に用いられるショートパスフィルタの
例について入射角度０’、３０’および４５°それぞれ
における透過スペクトルを示す図である。
第４図は、上記ショートパスフィルタについて３９０ｎ
ｍおよび６３３ｎｍにおける透過率、並びに反射率の角
度依存性を示すグラフである。
第５図は、本発明に用いられるバンドパスフィルタの例
について入射角度Ｏ０における透過スペクトルを示す図
である。
第６図は、」二足バンドパスフィルタについて３９０ｎ
ｍおよび６３３ｎｍにおける透過率、並びに反射率の角
度依存性を示すグラフである。FIG. 1 is a cross-sectional view showing the state of the radiation image conversion panel related to unexploded January. FIG. 2 is a sectional view showing another embodiment of the radiation image conversion panel according to the present invention. 1: Support, 2: Phosphor layer, 3: Multilayer filter, 4: Light reflection layer temperature 3 Figure 3 shows the temperature at incident angles of 0', 30' and 45°, respectively, for an example of the short pass filter used in the present invention. It is a figure showing a transmission spectrum. Figure 4 shows the above short pass filter with 390n
3 is a graph showing the transmittance at m and 633 nm, and the angular dependence of the reflectance. FIG. 5 is a diagram showing a transmission spectrum at an incident angle O0 for an example of a bandpass filter used in the present invention. Figure 6 shows the 390n for a bipedal bandpass filter.
3 is a graph showing the transmittance at m and 633 nm, and the angular dependence of the reflectance.
Claims (1)
体層とを有する放射線像変換パネルであって、該パネル
の少なくとも一部が着色剤により着色されている放射線
像変換パネルにおいて、該蛍光体層の支持体に接する側
とは反対側の表面に、該輝尽性蛍光体の励起波長におけ
る光透過率が０〜５°の範囲の光の入射角度に対して７
０％以上であり、かつ該励起波長における光反射率が３
０°以上の光の入射角度に対して６０％以上である多層
膜フィルタが設けられていることを特徴とする放射線像
変換パネル。 ２、上記多層膜フィルタの輝尽性蛍光体の励起波長にお
ける光透過率が０〜５°の範囲の光の入射角度に対して
８０％以上であり、かつ該励起波長における光反射率が
３０°以上の光の入射角度に対して７０％以上であるこ
とを特徴とする特許請求の範囲第１項記載の放射線像変
換パネル。 ３、上記多層膜フィルタの輝尽性蛍光体の輝尽発光波長
における光透過率が０〜４０°の範囲の光の入射角度に
対して６０％以上であることを特徴とする特許請求の範
囲第１項記載の放射線像変換パネル。 ４、上記多層膜フィルタの輝尽性蛍光体の輝尽発光波長
における光透過率が０〜４０°の範囲の光の入射角度に
対して８０％以上であることを特徴とする特許請求の範
囲第３項記載の放射線像変換パネル。 ５、上記多層膜フィルタがショートパスフィルタもしく
はバンドパスフィルタであることを特徴とする特許請求
の範囲第１項記載の放射線像変換パネル。 ６、上記多層膜フィルタが、ＳｉＯ＿２およびＭｇＦ＿
２からなる群より選ばれる少なくとも一種の低屈折率物
質と、ＴｉＯ＿２、ＺｒＯ＿２およびＺｎＳからなる群
より選ばれる少なくとも一種の高屈折率物質からなるこ
とを特徴とする特許請求の範囲第１項記載の放射線像変
換パネル。 ７、上記多層膜フィルタが真空蒸着により形成されたも
のであることを特徴とする特許請求の範囲第１項記載の
放射線像変換パネル。 ８、上記放射線像変換パネルが蛍光体層の上に保護膜を
有する構成であって、該保護膜が高分子物質からなり、
かつ上記多層膜フィルタがイオンプレーティングによっ
て該保護膜の表面に形成されたものであることを特徴と
する特許請求の範囲第１項記載の放射線像変換パネル。 ９、上記蛍光体層が着色剤により着色されていることを
特徴とする特許請求の範囲第１項記載の放射線像変換パ
ネル。 １０、上記輝尽性蛍光体の励起波長が４００〜９００ｎ
ｍの範囲にあることを特徴とする特許請求の範囲第１項
記載の放射線像変換パネル。 １１、上記輝尽性蛍光体が二価ユーロピウム賦活ハロゲ
ン化物系蛍光体であることを特徴とする特許請求の範囲
第１０項記載の放射線像変換パネル。 １２、上記二価ユーロピウム賦活ハロゲン化物系蛍光体
が二価ユーロピウム賦活弗化ハロゲン化物系蛍光体であ
ることを特徴とする特許請求の範囲第１１項記載の放射
線像変換パネル。[Claims] 1. A radiation image conversion panel comprising a support and a phosphor layer containing a stimulable phosphor on the support, wherein at least a part of the panel is colored with a colorant. In the radiation image storage panel, light having a light transmittance of 0 to 5 degrees at the excitation wavelength of the stimulable phosphor is incident on the surface of the phosphor layer opposite to the side in contact with the support. 7 for the angle
0% or more, and the light reflectance at the excitation wavelength is 3
1. A radiation image conversion panel characterized in that a multilayer filter is provided that has a filter ratio of 60% or more with respect to an incident angle of light of 0° or more. 2. The light transmittance of the stimulable phosphor of the multilayer filter at the excitation wavelength is 80% or more with respect to the incident angle of light in the range of 0 to 5 degrees, and the light reflectance at the excitation wavelength is 30%. 2. The radiation image conversion panel according to claim 1, wherein the radiation image conversion panel is 70% or more with respect to a light incident angle of .degree. or more. 3. The scope of claims characterized in that the light transmittance of the stimulable phosphor of the multilayer filter at the stimulated emission wavelength is 60% or more with respect to the incident angle of light in the range of 0 to 40 degrees. 2. The radiation image conversion panel according to item 1. 4. A claim characterized in that the light transmittance of the stimulable phosphor of the multilayer filter at the stimulated emission wavelength is 80% or more with respect to the incident angle of light in the range of 0 to 40 degrees. The radiation image conversion panel according to item 3. 5. The radiation image conversion panel according to claim 1, wherein the multilayer filter is a short pass filter or a band pass filter. 6. The above multilayer filter contains SiO_2 and MgF_
2, and at least one high refractive index substance selected from the group consisting of TiO_2, ZrO_2, and ZnS. Radiographic image conversion panel. 7. The radiation image conversion panel according to claim 1, wherein the multilayer filter is formed by vacuum deposition. 8. The radiation image conversion panel has a protective film on the phosphor layer, and the protective film is made of a polymeric substance;
The radiation image conversion panel according to claim 1, wherein the multilayer filter is formed on the surface of the protective film by ion plating. 9. The radiation image conversion panel according to claim 1, wherein the phosphor layer is colored with a colorant. 10. The excitation wavelength of the stimulable phosphor is 400 to 900n
2. The radiation image conversion panel according to claim 1, wherein the radiation image conversion panel is in the range of m. 11. The radiation image conversion panel according to claim 10, wherein the stimulable phosphor is a divalent europium activated halide phosphor. 12. The radiation image conversion panel according to claim 11, wherein the divalent europium-activated halide phosphor is a divalent europium-activated fluoride halide phosphor.