JPS61270154A - Laminate - Google Patents
LaminateInfo
- Publication number
- JPS61270154A JPS61270154A JP11209985A JP11209985A JPS61270154A JP S61270154 A JPS61270154 A JP S61270154A JP 11209985 A JP11209985 A JP 11209985A JP 11209985 A JP11209985 A JP 11209985A JP S61270154 A JPS61270154 A JP S61270154A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- laminate
- cured
- composition
- hydroxyl group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
[産業上の利用分野1
本発明は積層体に関し、更に詳しくは、制振性、断熱性
および吸音性にすぐれ、各種の構造材料として有用な積
層体に関する。DETAILED DESCRIPTION OF THE INVENTION [Industrial Field of Application 1] The present invention relates to a laminate, and more particularly, to a laminate that has excellent vibration-damping, heat-insulating, and sound-absorbing properties and is useful as a variety of structural materials.
[従来技術]
従来、建築物、車両、船舶等の構造材料として、木板、
樹脂板あるいは金属板などと、水酸基含有液状ジエン系
重合体とポリイソシアネート化合物とからなる組成物の
硬化体よりなる層とを積層してなる積層体が知られてい
る。[Prior Art] Traditionally, wood boards,
A laminate is known in which a resin plate, a metal plate, or the like is laminated with a layer made of a cured product of a composition made of a hydroxyl group-containing liquid diene polymer and a polyisocyanate compound.
[発明が解決しようとする問題点1
かかる積層体は、軽量であり、しかも高い剛性とすぐれ
た耐水性を具備する材料であるが、しかし、とくに建築
材料として使用した場合に、制振性、断熱性および吸音
性が必ずしも満足すべきものではなく、改良の余地が残
されている。[Problem to be Solved by the Invention 1 This laminate is a material that is lightweight, has high rigidity, and excellent water resistance.However, especially when used as a building material, it has poor vibration damping properties, The heat insulation and sound absorption properties are not necessarily satisfactory, and there is still room for improvement.
[問題を解決するための手段]
本発明は、従来のかかる問題を解消し、制振性、断熱性
および吸音性にすぐれた積層体の提供を目的とする。[Means for Solving the Problems] The present invention aims to solve the conventional problems and provide a laminate having excellent vibration damping properties, heat insulation properties, and sound absorption properties.
本発明者らは、上記目的を達成するために鋭意研究を重
ねた結果、従来の水酸基含有液状ジエン系重合体とポリ
イソシアネートからなる組成物の硬化体層に代えて、該
2J&分に更に木質充填材を配合してなる新規な組成物
の硬化体層を積層体の構成層とすることにより良好な特
性が得られることを確認して本発明を完成するに到った
。As a result of extensive research in order to achieve the above object, the present inventors discovered that, in place of the conventional cured layer of a composition consisting of a hydroxyl group-containing liquid diene polymer and a polyisocyanate, the 2J&min. The present invention was completed after confirming that good properties can be obtained by using a cured layer of a novel composition containing a filler as a constituent layer of a laminate.
すなわち1本発明の積層体は、水酸基含有液状ジエン系
重合体、ポリイソシアネート化合物および木質充填材を
含有する組成物の硬化体よりなる層を少なくとも 1層
有することを特徴とする。That is, the laminate of the present invention is characterized by having at least one layer made of a cured product of a composition containing a hydroxyl group-containing liquid diene polymer, a polyisocyanate compound, and a wood filler.
[具体的説明]
本発明のa屠体は、上記したように、水酸基含有液状ジ
エン系重合体、ポリイソシアネート化合物および木質充
填材を含有する組成物の硬化体層を構成層として少なく
とも 1層含むものであり。[Specific Description] As described above, the carcass a of the present invention includes at least one layer of a cured product of a composition containing a hydroxyl group-containing liquid diene polymer, a polyisocyanate compound, and a wood filler as a constituent layer. It is a thing.
かかる硬化体層と組み合わされる層の構成材料はとくに
限定されるものではなく、例えば、木板、樹脂板、金属
板、セラミックス板1紙、布などをあげることができる
。このうち、構造材料としては、木板、樹脂板、金属板
などが好適である。また1本発明の積層体の構成層の数
は何ら制限されるものではない、なお、例えば、3層積
層体とする場合は、上記組成物の硬化体層を中間層とす
れば、該硬化体層が上下2層を接着せしめる機能を有す
るため有利である。The constituent material of the layer combined with such a cured body layer is not particularly limited, and examples thereof include a wooden board, a resin board, a metal board, a ceramic board, paper, and cloth. Among these, wood boards, resin boards, metal plates, etc. are suitable as structural materials. Furthermore, the number of constituent layers of the laminate of the present invention is not limited at all. For example, in the case of a three-layer laminate, if the cured product layer of the above composition is an intermediate layer, the cured This is advantageous because the body layer has the function of adhering the upper and lower layers together.
また、本発明の積層体において各構成層の層厚は、構成
層の素材あるいは積層体の用途に応じて適宜設定すれば
よいが、通常、硬化体層の層厚を 1〜10s層、その
他の構成層の層厚を 0.5〜5膳−程度にそれぞれ設
定することが好ましい。Further, in the laminate of the present invention, the layer thickness of each constituent layer may be appropriately set depending on the material of the constituent layer or the use of the laminate, but usually the thickness of the cured layer is 1 to 10s layer, etc. It is preferable to set the layer thickness of each of the constituent layers to about 0.5 to 5 layers.
本発明の積層体において、硬化体層を形成する組成物に
ついて以下に説明する。この組成物は。In the laminate of the present invention, the composition forming the cured body layer will be explained below. This composition is.
前述したように、水酸基含有液状ジエン系重合体、ポリ
イソシアネート化合物および木質充填材を必須成分とし
て含有する液状重合体組成物である。As mentioned above, this is a liquid polymer composition containing a hydroxyl group-containing liquid diene polymer, a polyisocyanate compound, and a wood filler as essential components.
まず、第1の必須成分である水酸基含有液状ジエン系重
合体は5分子内、好ましくは分子末端に水酸基(OH基
)を有する液状ジエン系重合体であり、その数平均分子
量が300〜25000、とくに 500〜10000
のものであることが好ましい。First, the hydroxyl group-containing liquid diene polymer, which is the first essential component, is a liquid diene polymer having hydroxyl groups (OH groups) within 5 molecules, preferably at the end of the molecule, and has a number average molecular weight of 300 to 25,000. Especially 500-10000
Preferably.
これらの液状ジエン系重合体とは炭素数4〜12のジエ
ン重合体、ジエン共重合体、さらにはこれらジエンモノ
マーと炭素数2〜22のα−オレフィン性付加重合性モ
ノマーとの共重合体などかある。具体的にはブタンジエ
ンホモポリマー、インプレンホモポリマー、ブタジェン
−スチレンコポリマー、フタジエン−イソプレンコポリ
マー、ブタジェン−アクリロニトリルコポリマー、ブタ
ジェン−2−エチルヘキシルアクリレートコポリマー、
ブタジェン−n−オクタデシルアクリレートコポリマー
などを例示することができる。これら液状ジエン系重合
体は、例えば液状反応媒体中で共役ジエンモノマーを過
酸化水素の存在下。These liquid diene polymers include diene polymers and diene copolymers having 4 to 12 carbon atoms, and copolymers of these diene monomers and α-olefinic addition polymerizable monomers having 2 to 22 carbon atoms. There is. Specifically, butane diene homopolymer, imprene homopolymer, butadiene-styrene copolymer, phtadiene-isoprene copolymer, butadiene-acrylonitrile copolymer, butadiene-2-ethylhexyl acrylate copolymer,
Examples include butadiene-n-octadecyl acrylate copolymer. These liquid diene polymers are produced by, for example, adding a conjugated diene monomer to a liquid reaction medium in the presence of hydrogen peroxide.
加熱反応させることにより製造することができる。It can be produced by heating reaction.
さらに、この水酸基含有液状ジエン系重合体のOH基含
有量は0.INIOmeq/Hさらには、0.3〜5、
Omeq/gであることが好ましい。Furthermore, the OH group content of this hydroxyl group-containing liquid diene polymer is 0. INIOmeq/H further, 0.3 to 5,
Preferably it is Omeq/g.
ついで、第2の必須成分であるポリイソシアネート化合
物は、 1分子中に2個若しくはそれ以上のインシアネ
ート基を有する有機化合物であって、前記活性水素基含
有液状ジエン系重合体およびポリオール化合物の活性水
素含有官能基に対する反応性イソシアネート基(NCO
基)゛を有するものである。ポリイソシアネート化合物
の例としては、通常の芳香族、脂肪族および脂環族のも
の・をあげることができ、たとえばトリレンジイソシア
ネート、ヘキサメチレンジイソシアネート、ジフェニル
メタンジイソシアネート(MDI) 、液状変性ジフェ
ニルメタンジイソシアネート、ポリメチレンポリフェニ
ルインシアネート、キシリレンジイソシアネート、シク
ロヘキシルジイソシアネート、シクロヘキサンフェニレ
ンジイソシアネート、ナフタリン−1,5−ジイソシア
ネート、イソプロピルベンゼン−2,4−ジイソシアネ
ート、ポリプロピレングリコールとトリレンジイソシア
ネート付加反応物などがあり、とりわけ[01、液状変
性ジフェニルメタンジイソシアネート、トリレンジイソ
シアネート等が好ましい。Next, the polyisocyanate compound, which is the second essential component, is an organic compound having two or more incyanate groups in one molecule, and is an organic compound that has two or more incyanate groups in one molecule, and has a high activity of the active hydrogen group-containing liquid diene polymer and the polyol compound. Reactive isocyanate groups toward hydrogen-containing functional groups (NCO
It has the group )゛. Examples of polyisocyanate compounds include the usual aromatic, aliphatic and cycloaliphatic ones, such as tolylene diisocyanate, hexamethylene diisocyanate, diphenylmethane diisocyanate (MDI), liquid modified diphenylmethane diisocyanate, polymethylene Polyphenylinocyanate, xylylene diisocyanate, cyclohexyl diisocyanate, cyclohexanephenylene diisocyanate, naphthalene-1,5-diisocyanate, isopropylbenzene-2,4-diisocyanate, polypropylene glycol and tolylene diisocyanate addition reaction product, etc., among others [01, Liquid modified diphenylmethane diisocyanate, tolylene diisocyanate and the like are preferred.
かかるポリイソシアネート化合物の配合量はとくに限定
されるものではないが、水酸基含有液状ジエン系重合体
の水酸基に対するポリイソシアネート化合物のポリイソ
シアネート基の比(NCO基10H基)が0.2〜!0
.0、さらには0.5〜6.0となるように設定される
ことが好ましい。The amount of the polyisocyanate compound to be blended is not particularly limited, but the ratio of the polyisocyanate groups of the polyisocyanate compound to the hydroxyl groups of the hydroxyl group-containing liquid diene polymer (NCO group 10H group) is 0.2~! 0
.. It is preferable to set it to 0, more preferably 0.5 to 6.0.
さらに、この組成物の第3の必須成分である木質充填材
としては、その種類、形状、寸法などはとくに限定され
るものではなく2例えば、木粉。Furthermore, the type, shape, size, etc. of the wood filler, which is the third essential component of this composition, are not particularly limited; for example, wood flour may be used.
木片、木毛などを好適なものとしてあげることができる
。Suitable materials include wood chips and wool.
この木質充填材の配合量はとくに制限されるものではな
いが、水酸基含有液状ジエン系重合体100重量部に対
して、5〜300重量部、更には50〜200重量部に
設定することが好ましい。The amount of this wood filler is not particularly limited, but it is preferably set at 5 to 300 parts by weight, more preferably 50 to 200 parts by weight, based on 100 parts by weight of the hydroxyl group-containing liquid diene polymer. .
また1本発明の液状重合体組成物にあっては、上記した
3つの必須成分のほかに、以下にあげる添加剤を必要に
応じて適宜添加使用することができる。Furthermore, in the liquid polymer composition of the present invention, in addition to the above-mentioned three essential components, the following additives may be added as appropriate.
すなわち、まず1強化剤としては、ポリオール化合物お
よびポリアミン化合物があげられる。That is, first, examples of reinforcing agents include polyol compounds and polyamine compounds.
ポリオール化合物としては特に制限はなく、1級ポリオ
ール、2級ポリオール、3級ポリオールのいずれを用い
てもよい、具体的には例えば1.2−プロピレングリコ
ール、ジプロピレングリコール、1.2−ブタンジオー
ル、1.3−ブタンジオール、2,3−ブタンジオール
、1.2−ベンタンジオール、2.3−ベンタンジオー
ル、2.5−ヘキサンジオール、2.4−ヘキサンジオ
ール、2−エチル−1,3−ヘキサンジオール、シクロ
ヘキサンジオール、グリセリン、N、N−ビス−2−ヒ
ドロキシプロピルアニリン、 N、N’−ビスヒドロ
キシイソプロビル−2−メチルピペラジン、ビスフェノ
ールAのプロピレンオキサイド付加物などの少なくとも
1個の二級炭素に結合した水酸基を含有する低分子量
ポリオールが挙げられる。The polyol compound is not particularly limited, and any of primary polyol, secondary polyol, and tertiary polyol may be used. Specifically, for example, 1,2-propylene glycol, dipropylene glycol, 1,2-butanediol. , 1.3-butanediol, 2,3-butanediol, 1.2-bentanediol, 2.3-bentanediol, 2.5-hexanediol, 2.4-hexanediol, 2-ethyl-1,3 - at least one dihydrogen such as hexanediol, cyclohexanediol, glycerin, N,N-bis-2-hydroxypropylaniline, N,N'-bishydroxyisopropyl-2-methylpiperazine, propylene oxide adduct of bisphenol A, etc. Examples include low molecular weight polyols containing hydroxyl groups bonded to carbon atoms.
さらに本発明にあっては、ポリオールとして二級炭素に
結合した水酸基を含有しないエチレングリコール、1.
3−プロピレングリコール、1.4−ブタンジオール、
1,5−ベンタンジオール、1.8−ヘキサンジオール
などを用いることもできる0本発明で用いるポリオール
としては通常ジオールが用いられるが、トリオール、テ
トラオールを用いてもよく、その分子量は50〜500
の範囲のものである。Furthermore, in the present invention, ethylene glycol which does not contain a hydroxyl group bonded to a secondary carbon as a polyol, 1.
3-propylene glycol, 1,4-butanediol,
1,5-bentanediol, 1,8-hexanediol, etc. can also be used. Diols are usually used as the polyols used in the present invention, but triols and tetraols may also be used, and their molecular weights are 50 to 500.
It is within the range of .
また、ポリアミン化合物としては特に制限はなく、ジア
ミン、トリアミン、テトラミンのいずれでもよい、さら
に、1級ポリアミン、2級ポリアミン、3級ポリアミン
のいずれを用いることもできる。ポリアミン化合物とし
ては例えば、ヘキサメチレンジアミン等、の脂肪族アミ
ン; 3,3’−ジメチルI、4′−ジアミノジシグ
ロヘキシルメタン等の脂肪族アミン;4,4−ジアミノ
ジフェニル等の芳香族アミン; 2,4.8−1リ (
ジメチルアミノメチル)フェノール等のテトラミンなど
をあげることができる。Further, the polyamine compound is not particularly limited and may be any of diamine, triamine, and tetramine, and furthermore, any of primary polyamine, secondary polyamine, and tertiary polyamine may be used. Examples of polyamine compounds include aliphatic amines such as hexamethylene diamine; aliphatic amines such as 3,3'-dimethyl I and 4'-diaminodicyclohexylmethane; aromatic amines such as 4,4-diaminodiphenyl; 2,4.8-1li (
Examples include tetramines such as (dimethylaminomethyl)phenol.
以上のような強化材、すなわち、ポリオール化合物、ポ
リアミン化合物の配合量は、前述の水酸基含有液状ジエ
ン系重合体100重量部に対し。The amount of the reinforcing material as described above, that is, the polyol compound and the polyamine compound, is based on 100 parts by weight of the above-mentioned hydroxyl group-containing liquid diene polymer.
1〜1000重量部、とくに、3〜200重量部に設定
することが好ましい。It is preferably set at 1 to 1000 parts by weight, particularly 3 to 200 parts by weight.
ついで、5411充填材として、マイカ、グラファイト
、ヒル石、炭酸カルシウム、スレート粉などがあげられ
、そのほか、粘度調整剤としてジオクチルフタレートな
どの可塑剤を加えたり、アロマ系、ナフテン系、パラフ
ィン系オイル等の軟化剤を加えたり、さらに粘着力、接
着力の調整のためにアルキルフェノール樹脂、テルペン
樹脂、テルペンフェノール樹脂、キシにンホルムアルデ
ヒド樹脂、ロジン、水添ロジン、クロマン樹脂、脂肪族
および芳香族石油樹脂等の粘着性付与樹脂を加えること
もできる。また、ジブチルスズジラウレート、第1スズ
オクトエート、ポリエチレンジアミン等の硬化促進剤を
加えることもできる。さらに耐候性向上のために老化防
止剤を加えたり、消泡剤としてシリコン化合物などを添
加することができる。Next, 5411 fillers include mica, graphite, vermiculite, calcium carbonate, slate powder, etc. In addition, plasticizers such as dioctyl phthalate are added as viscosity modifiers, aromatic, naphthenic, paraffinic oils, etc. To further adjust the adhesion and adhesion strength, add a softener or use alkylphenol resins, terpene resins, terpenephenol resins, xylene formaldehyde resins, rosins, hydrogenated rosins, chroman resins, aliphatic and aromatic petroleum resins. It is also possible to add tackifying resins such as. Further, curing accelerators such as dibutyltin dilaurate, stannous octoate, polyethylene diamine, etc. can also be added. Furthermore, an anti-aging agent can be added to improve weather resistance, and a silicon compound or the like can be added as an antifoaming agent.
また、上記添加剤に加えて、瀝青物質を添加することも
可能である。瀝青物質としては、ストレートアスファル
ト、ブローンアスファルト、セミプローンアスファルト
、プロパンを溶剤とする税源アスファルトなどの石油ア
スファルト;石油ピッチ;石油タール;石炭ピッチなど
があげられる。これらの瀝青物質の配合量は、水酸基含
有液状ジエン系重合体100重量部に対し、10〜10
0◎重量部程度に設定されることが好ましい。In addition to the above additives, it is also possible to add bituminous substances. Examples of bituminous materials include petroleum asphalts such as straight asphalt, blown asphalt, semi-prone asphalt, and base asphalt using propane as a solvent; petroleum pitch; petroleum tar; and coal pitch. The blending amount of these bituminous substances is 10 to 10 parts by weight per 100 parts by weight of the hydroxyl group-containing liquid diene polymer.
It is preferable to set the amount to about 0◎ parts by weight.
本発明で使用される液状重合体組成物は、以下のように
して容易に調製することができる。すなわち、まず、水
酸基含有液状ジエン系重合体およびその他の添加剤をそ
れぞれ所定量配合し攪拌混合を行なう、このときの温度
は10〜120℃、好ましくは、20〜100℃、Wl
拌時間は 1〜380分間、好ましくは5〜180分間
にそれぞれ設定される。The liquid polymer composition used in the present invention can be easily prepared as follows. That is, first, predetermined amounts of the hydroxyl group-containing liquid diene polymer and other additives are respectively blended and mixed by stirring, at a temperature of 10-120°C, preferably 20-100°C, Wl
The stirring time is set to 1 to 380 minutes, preferably 5 to 180 minutes.
ついで、得られた混合物にポリイソシアネート化合物お
よび木質充填材をそれぞれ所定量配合して再び攪拌混合
を行なうことにより目的とする組成物を得る。このとき
の温度は10〜100℃、好ましくは、20〜80℃、
攪拌時間は1秒間〜360分間。Next, predetermined amounts of a polyisocyanate compound and a wood filler are added to the resulting mixture, and the mixture is stirred and mixed again to obtain the desired composition. The temperature at this time is 10 to 100°C, preferably 20 to 80°C,
Stirring time is 1 second to 360 minutes.
好ましくは、 t−tso分間にそれぞれ設定される。Preferably, they are each set to t-tso minutes.
更に1本発明の積層体は次のようにして製造することが
できる。まず、積層体を構成する構成層のうち硬化体層
以外の層、例えば、木板上に、前述した液状重合体組成
物を塗布したのち、所定の条件下で硬化せしめることに
より、該組成物よりなる硬化体層を形成すると同時に木
板上に該硬化体層を接着させ積層体を完成する。このと
きの硬化条件は、温度θ〜200℃、好ましくは、50
〜150℃、時間0.5〜24時間、好ましくは、 1
〜15時間程時間上れぞれ設定することが好ましい。Furthermore, the laminate of the present invention can be manufactured as follows. First, the above-mentioned liquid polymer composition is applied to a layer other than the cured material layer among the constituent layers constituting the laminate, for example, a wooden board, and then cured under predetermined conditions. At the same time as forming a cured body layer, the cured body layer is adhered onto a wooden board to complete a laminate. The curing conditions at this time are a temperature of θ to 200°C, preferably 50°C.
~150°C, time 0.5~24 hours, preferably 1
It is preferable to set the time in increments of about 15 hours.
また、例えば、プレス成型機等を使用して、成形圧5〜
300kg/cmで硬化成形せしめることもできる。Also, for example, using a press molding machine etc., the molding pressure is 5 to 5.
It can also be hardened and molded at 300 kg/cm.
[実施例]
参考例(液状重合体組成物の調製)
以下に述べる各成分を使用して後述する実施例1〜3で
使用する各液状重合体組成物を調製した。[Example] Reference Example (Preparation of Liquid Polymer Composition) Using each component described below, each liquid polymer composition used in Examples 1 to 3 described later was prepared.
(1)水酸基含有液状ジエン系重合体二末端水酸基液状
ポリブタジェン(出光石油化学■製、R−45HT;数
平均分子量280G、 OR含有量0.79meq/g
)(2)ポリイソシアネート化合物ニジフェニルメタン
ジイソシアネート
(3)木質充填材:
A、木粉(のこくず、 10メツシユ)B、木薄片(か
んなくず、0.7X IOX 20■鳳)(4)ポリオ
ール化合物:
C0ビスフェノールAのプロピレンオキシド付加物
り、 N、N−ビス(2−ヒドロキシプロピル)アニ
リ ン
(5)可塑剤ニジオクチルフタレート
(6)老化防止剤:
E、 2.2°−メチレンビス(4−メチル−e−t
−ブチル)フェノール
F、 ヘンタエリスリチルーテトラキス−3,5−ジ
−t−ブチル−4−ヒドロキシフェノールプロピオネー
ト
0、 2−(3,5−ジ−t−ブチル−4−ヒドロキシ
フェニル)プロピオネート
(7)硬化促進剤ニジブチルスズラウレート以上の各成
分を第1表に示した配合量で使用し、まず、ポリイソシ
アネート化合物と木質充填材とを除いた他のすべての成
分をガラス製の容器内で混合した。ついで、この混合物
中に。(1) Hydroxyl group-containing liquid diene polymer Bi-terminal hydroxyl group liquid polybutadiene (manufactured by Idemitsu Petrochemical Co., Ltd., R-45HT; number average molecular weight 280G, OR content 0.79meq/g
) (2) Polyisocyanate compound Nidiphenylmethane diisocyanate (3) Wood filler: A. Wood flour (sawdust, 10 mesh) B. Wood flakes (sawdust, 0.7X IOX 20) (4) Polyol compound : C0 propylene oxide adduct of bisphenol A, N,N-bis(2-hydroxypropyl)aniline (5) Plasticizer nidioctyl phthalate (6) Antiaging agent: E, 2.2°-methylenebis(4- Methyl-et
-butyl)phenol F, hentaerythrityl-tetrakis-3,5-di-t-butyl-4-hydroxyphenolpropionate 0, 2-(3,5-di-t-butyl-4-hydroxyphenyl)propionate (7) Curing accelerator Nidibutyltin laurate Each of the above components is used in the amounts shown in Table 1, and all other components except the polyisocyanate compound and wood filler are placed in a glass container. mixed inside. Then into this mixture.
予め105℃において 1時間乾燥した木質充填材を加
えてステンレス製の棒を使用して室温で1分間攪拌した
。この攪拌のみで木質充填材は混合物中に均一に分散し
た。しかるのち、ポリイソシアネート化合物を加えて、
同じくステンレス製の棒により室温で1分間攪拌して本
発明の液状重合体組成物を得た。A wood filler previously dried at 105° C. for 1 hour was added and stirred for 1 minute at room temperature using a stainless steel rod. The wood filler was uniformly dispersed in the mixture only by this stirring. Then, by adding a polyisocyanate compound,
The liquid polymer composition of the present invention was obtained by stirring for 1 minute at room temperature using the same stainless steel rod.
実施例1
第1図に示したように厚さ2鳳■の合板1上に表示の組
成物を塗布し、プレス成形機を使用して、150℃にお
いて、200kg/cnlの成形圧で0.5時間硬化せ
しめて、厚さ3層層の硬化体層2を形成し、積層体を完
成した。この積層体に対し、制振性、断熱性および吸音
性の評価試験を行ない得られた結果を表に示した。なお
、これらの評価試験はそれぞれ以下に示す条件により実
施した。Example 1 As shown in FIG. 1, the indicated composition was coated on a plywood board 1 with a thickness of 2 mm, and a press molding machine was used to mold the composition at 150° C. with a molding pressure of 200 kg/cnl. It was cured for 5 hours to form a cured body layer 2 having a thickness of three layers, thereby completing a laminate. This laminate was subjected to evaluation tests for vibration damping, heat insulation, and sound absorption, and the results are shown in the table. Note that these evaluation tests were conducted under the conditions shown below.
制振性:共振法による損失係数
断熱性: JIS A1420に準拠した熱質流抵抗(
rr1′−h −’0 /kcal)吸音性: JIS
A1409に準拠した残響室法による 300〜10
00Hzにおける吸音率実施例2
硬化体層として表示した組成物を使用し、該硬化体層と
ポリプロピレンよりなる層とを組み合わせることにより
第2図に示した如き積層体を製造した。すなわち1図に
おいて、ポリプロピレン層3.3°を上下層とし1組成
物層4を中間層として、上記実施例1と同様の条件で該
組成物層4を硬化せしめて積層体を完成した。なお、ポ
リプロピレン層3.3゛はともに層厚2層厘とし、かつ
、硬化体層の層厚は3mmとした。Vibration damping property: Loss coefficient by resonance method Insulation property: Heat mass flow resistance (based on JIS A1420)
rr1'-h -'0 /kcal) Sound absorption: JIS
300-10 by reverberation room method in accordance with A1409
Sound Absorption Coefficient at 00 Hz Example 2 A laminate as shown in FIG. 2 was produced by using the composition indicated as a cured layer and combining the cured layer with a layer made of polypropylene. That is, in Figure 1, the polypropylene layer 3.3° was used as the upper and lower layers, and the composition layer 4 was used as the intermediate layer, and the composition layer 4 was cured under the same conditions as in Example 1 to complete a laminate. The polypropylene layers 3.3 and 3.3 were both 2-layer thick, and the cured material layer was 3 mm thick.
このようにして得られた積層体について、上記実施例と
同様の条件で各評価試験を行ない、その結果を表に示し
た。Regarding the thus obtained laminate, various evaluation tests were conducted under the same conditions as in the above examples, and the results are shown in the table.
実施例3
硬化体層として、表示した組成物を使用し、該硬化体層
とアルミニウム板とを組み合わせて、第2図に示したよ
うな硬化体層を中間層とする 3層積層体を製造した。Example 3 A three-layer laminate was produced by using the indicated composition as the cured layer and combining the cured layer with an aluminum plate to have the cured layer as an intermediate layer as shown in FIG. did.
なお、硬化体層の層厚は3mm 、アルミニウム板の厚
さは1■とじ、上記実施例1と同様の硬化条件により硬
化せしめた。このようにして得られた積層体について、
上記実施、例と同様の条件で各評価試験を行ない、その
結果を表に示した。The thickness of the cured material layer was 3 mm, the thickness of the aluminum plate was 1 mm, and the curing conditions were the same as in Example 1 above. Regarding the laminate thus obtained,
Each evaluation test was conducted under the same conditions as in the above implementation and examples, and the results are shown in the table.
比較例
硬化体層として、表示した如く、木質充填材を含まない
従来の組成物を使用し、該硬化体層と合板とを組み合わ
せることにより第1図と同様な2層積層体を製造した。Comparative Example As shown, a conventional composition containing no wood filler was used as the cured layer, and the cured layer and plywood were combined to produce a two-layer laminate similar to that shown in FIG.
なお、硬化条件は実施例1と同様に設定し、硬化体層の
層厚3腸■1合板の厚さ2履麿にそれぞれ設定した。こ
のようにして得られた積層体について、上記実施例と同
様の条件で各評価試験を行ない、その結果を表に示した
。The curing conditions were set in the same manner as in Example 1, and the thickness of the cured material layer was 3 mm, and the thickness of the plywood was 2 mm. Regarding the thus obtained laminate, various evaluation tests were conducted under the same conditions as in the above examples, and the results are shown in the table.
[発明の効果]
以上の説明から明らかなように、本発明の積層体は、新
規な組成物よりなる硬化体層を構成層として有するため
、従来の組成物の硬化体層を使用した積層体に比べ制振
性、断熱性および吸音性のすべての点においてすぐれて
おり、建築物、車両、船舶その他の構造材料として極め
て有用であり、その工業的価値は大である。[Effects of the Invention] As is clear from the above description, since the laminate of the present invention has a cured layer made of a novel composition as a constituent layer, it is different from a laminate using a cured layer made of a conventional composition. It has excellent vibration damping properties, heat insulation properties, and sound absorption properties compared to other materials, and is extremely useful as a structural material for buildings, vehicles, ships, and other objects, and its industrial value is great.
第1図および第2図はともに本発明の積層体の実施例を
示す断面図である。
l・・・・・・・・・合板、2.4・・・・・・・・・
硬化体層、3.39・・・・・・・・・アルミニウム板
。Both FIG. 1 and FIG. 2 are cross-sectional views showing embodiments of the laminate of the present invention. l・・・・・・Plywood, 2.4・・・・・・・・・
Hardened body layer, 3.39... Aluminum plate.
Claims (1)
ト化合物および木質充填材を含有する組成物の硬化体よ
りなる層を少なくとも1層有することを特徴とする積層
体。 2、該硬化体よりなる層以外の層が、木板、樹脂板また
は金属板である特許請求の範囲第1項記載の積層体。[Scope of Claims] 1. A laminate having at least one layer made of a cured product of a composition containing a hydroxyl group-containing liquid diene polymer, a polyisocyanate compound, and a wood filler. 2. The laminate according to claim 1, wherein the layer other than the layer made of the cured product is a wooden board, a resin board, or a metal board.