JPS61197511A - Cosmetic composition - Google Patents

Cosmetic composition

Info

Publication number
JPS61197511A
JPS61197511A JP3700785A JP3700785A JPS61197511A JP S61197511 A JPS61197511 A JP S61197511A JP 3700785 A JP3700785 A JP 3700785A JP 3700785 A JP3700785 A JP 3700785A JP S61197511 A JPS61197511 A JP S61197511A
Authority
JP
Japan
Prior art keywords
titanium oxide
kaolin
particles
component
coated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP3700785A
Other languages
Japanese (ja)
Other versions
JPH0655663B2 (en
Inventor
Shigeru Hashimoto
繁 橋本
Takashi Umeno
高 梅野
Midori Ugawa
鵜川　みどり
Norihiro Tanimoto
谷本　憲弘
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sunstar Inc
Teikoku Kako Co Ltd
Original Assignee
Sunstar Inc
Teikoku Kako Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sunstar Inc, Teikoku Kako Co Ltd filed Critical Sunstar Inc
Priority to JP3700785A priority Critical patent/JPH0655663B2/en
Publication of JPS61197511A publication Critical patent/JPS61197511A/en
Publication of JPH0655663B2 publication Critical patent/JPH0655663B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

PURPOSE:A cosmetic composition that contains kaolin particles coated with a specific amount of titanium oxide, thus enabling a large amount of titanium oxide to be included and being used as a homogeneous and stabilized sun- screening agent with high ultraviolet shielding. CONSTITUTION:Kaolin particles are coated with 1-50wt%, based on the total kaolin, of particles of titanium oxide and the resultant particles are added to give the objective composition. The kaolin particles coated with titanium oxide are prepared by adding a specific amount of kaolin particles of 0.5-30mum particle sizes to a titanium salt, hydrolyzing the titanium salt in the presence of the kaolin particles and filtering, rinsing, drying and roasting the resultant particles according to the usual manners. The resultant composition is used in the form of cake, milky foundation, white powder, lip sticks, lotion or cream. EFFECT:When it is used in sun-screening of skins, it gives good finish with good appearance and high sun shielding.

Description

【発明の詳細な説明】 発明の分野 本発明は、日焼は止めとして用いられる化粧料組成物に
関する。DETAILED DESCRIPTION OF THE INVENTION Field of the Invention The present invention relates to cosmetic compositions for use as sunscreens.

従来技術 酸化チタン粉末は、従来より、化粧品用顔料として広く
使用されている。特に、最大粒径０．１μ以下で、平均
粒径５〜５０都の微粒子酸化チタン粉末は、紫外線遮断
効果が著しいところから、最近、日焼は止めの化粧料用
として種々検討が加えられている。しかしながら、かか
る微粒子酸化チタンは、表面エネルギーが大きく、これ
を用いて化粧品を製造した場合、製造時における均一な
分散が困難であり、また、貯蔵中においては凝集物を形
成する傾向がある。さらに、例えば、水使用によるケー
キ状ファンデーソヨン中にかかる微粒子酸化チタンを配
合した場合には、使用時、化粧品が皮膚に均一に塗布さ
れず、仕上がりが非常に悪いなど化粧料として重大な欠
点かある。BACKGROUND OF THE INVENTION Titanium oxide powder has been widely used as a cosmetic pigment. In particular, fine-particle titanium oxide powder with a maximum particle size of 0.1μ or less and an average particle size of 5 to 50 mm has been recently investigated for use in sunscreen cosmetics because it has a remarkable effect of blocking ultraviolet rays. There is. However, such fine particle titanium oxide has a large surface energy, and when cosmetics are manufactured using it, it is difficult to uniformly disperse it during manufacture, and it also tends to form aggregates during storage. Furthermore, if such microparticle titanium oxide is blended into a cake-like foundation soybean made from water, the cosmetic may not be applied evenly to the skin during use, resulting in a very poor finish, resulting in serious drawbacks as a cosmetic. There is.

発明の概要 そこで本発明者らは、紫外線遮断効果に優れた酸化チタ
ンを均一かつ安定に配合した化粧料組成物を得るべく鋭
意検討を行なった結果、酸化チタンにより被覆されたカ
オリン粒子を用いることにより、前記問題点が解決しう
ろことを見出し本発明を完成するに至った。Summary of the Invention The present inventors have conducted intensive studies to obtain a cosmetic composition uniformly and stably blended with titanium oxide, which has excellent ultraviolet blocking effects.As a result, the present inventors have discovered the use of kaolin particles covered with titanium oxide. As a result, the inventors discovered that the above-mentioned problems could be solved and completed the present invention.

すなわち、本発明は、酸化チタン粒子により被覆された
カオリン粒子を配合したことを特徴とずろ化粧料組成物
を提供する乙のである。That is, the present invention provides a beige cosmetic composition characterized by containing kaolin particles coated with titanium oxide particles.

本発明化粧料組成物によれば、酸化チタンとカオリン粒
子とを単に別々に混合した場合に比し、多量の酸化チタ
ンを配合しえ、はるかに紫外線遮断効果が高く、しかも
均質で安定な化粧料組成物が得られ、皮膚に適用した場
合の仕上がりも良好で、化粧を行なった場合の外観なら
びに日焼は止め効果に優れる。According to the cosmetic composition of the present invention, compared to a case where titanium oxide and kaolin particles are simply mixed separately, a large amount of titanium oxide can be blended, and the cosmetic composition has a much higher ultraviolet blocking effect and is homogeneous and stable. A cosmetic composition is obtained which gives a good finish when applied to the skin, has an excellent appearance when makeup is applied, and has excellent sun protection effects.

発明の詳細 な説明化粧料組成物に配合される酸化チタン被覆カオリ
ンは、適宜のチタニウム塩に対し所定量のカオリン粒子
（粒径的０．５〜３０μｍ）を添加し、カオリンの存在
下に該チタニウム塩を加水分解し、ついで、常法により
ろ過、洗浄、乾燥した後、焼成を行なうことにより得ら
れる。かかる酸化チタン被覆カオリンの製造方法の一例
を具体的に挙げれば、１５　ｇ／　ｆｌ（Ｔ　ｉＯを換
算）の硫酸チタニル水溶液１／中に、平均粒径２μのカ
オリン１３５ｇを添加し、攪拌しながら加熱、沸騰させ
て２時間保持する。生成物をろ過、水洗し、得られたケ
ーキを分離して１１０℃にて乾燥する。さらに８００°
Ｃ程度にて３０分間焼成を行ない本発明にて用いる酸化
チタン被覆カオリンを得る。Detailed Description of the Invention Titanium oxide-coated kaolin to be blended into a cosmetic composition is prepared by adding a predetermined amount of kaolin particles (0.5 to 30 μm in particle size) to an appropriate titanium salt, and then adding the kaolin particles in the presence of kaolin. It is obtained by hydrolyzing a titanium salt, followed by filtration, washing, drying, and calcination in a conventional manner. To give a specific example of a method for producing such titanium oxide-coated kaolin, 135 g of kaolin with an average particle size of 2 μm is added to 1/2 of an aqueous solution of titanyl sulfate of 15 g/fl (calculated as TiO), and the mixture is stirred while stirring. Heat, bring to a boil and hold for 2 hours. The product is filtered and washed with water, and the resulting cake is separated and dried at 110°C. Another 800°
Firing is performed at about C for 30 minutes to obtain titanium oxide coated kaolin used in the present invention.

かかる方法にて得られた酸化チタン被覆カオリンは、母
体となるカオリン粒子表面に二酸化チタンの微粒子が被
覆されている。In the titanium oxide-coated kaolin obtained by such a method, the surface of the kaolin particles serving as the base material is coated with fine particles of titanium dioxide.

つぎに、該酸化チタン被覆カオリンを配合して製造した
試験クリームの紫外線遮断効果（Ｓ　Ｐ　Ｆ　：Ｓｕｎ
　　Ｐｒｏｔｅｃｔｉｏｎ　　Ｆａｃｔｏｒ）、透明性
、プルーミング、安定性につき、従来の微粒子酸化チタ
ン（平均粒径８ｍμ）とカオリンとの混合物を配合した
クリームの場合と比較して第１表に示す。Next, the ultraviolet blocking effect (S P F : Sun
Protection Factor), transparency, pluming, and stability are shown in Table 1 in comparison with a cream containing a conventional mixture of fine-particle titanium oxide (average particle size 8 mμ) and kaolin.

また、該酸化チタン被覆カオリンを用いて製造した試験
ケーキ状ファンデーションのＳＰＦ、製造時の分散性、
使用時の色味の差および使用時の仕上がりにつき評価し
た結果を同様にして第２表に示す。In addition, the SPF of the test cake-like foundation produced using the titanium oxide coated kaolin, the dispersibility during production,
The results of evaluating the difference in color tone during use and the finish during use are similarly shown in Table 2.

なお、以下において％とあるは、すべて重量％を意味す
る。In addition, in the following, all % means weight %.

各試験化粧料組成物は、つぎの組成および製造方法によ
り得た。Each test cosmetic composition was obtained using the following composition and manufacturing method.

（ａ）試験クリームの組成： 成　分　Ａ　　　　　　　　　　配合量（％）固形パラ
フィン　　　　　　　　　　５．０ミツロウ　　　　　
　　　　　　　　４．０マイクロクリスタリンワツクス
　　　４．０ワセリン　　　　　　　　　　　　　　７
．０スクワラン　　　　　　　　　　　３０．０ポリオ
キシエチレンモノ ラウリン酸ソルビタン（２０ＥＯ）　　　　　　１．０
セスキオレイン酸ソルビタン　　　　　４．０成　分　
Ｂ　　　　　　　　　　配合量（％）精製水　　　　　
　　　　　　　　　残部酸　分　Ｃ配合量（％） 酸化チタン被覆カオリン［１，！、　　第１表に記載ま
たは酸化チタンとカオリンとの 混合物［■］（酸化チタン／［■］ または［ＩＴ］の比は第１表に記載） タルク　　　　　　　　　　　　　　　５．０上記酸分
Ｃを均一に混合し、これに成分Ｂに加え、７０℃にてよ
く分散する。別に、成分Ａを７０℃で加熱、溶解し、こ
れに前記混合物を加え、ポモミキザーで均一に乳化する
。乳化後、３０℃まで冷却し製品とする。(a) Composition of test cream: Component A Amount (%) Solid paraffin 5.0 Beeswax
4.0 Microcrystalline wax 4.0 Vaseline 7
．． 0 Squalane 30.0 Sorbitan polyoxyethylene monolaurate (20EO) 1.0
Sorbitan sesquioleate 4.0 ingredients
B Blend amount (%) Purified water
Residual acid content C content (%) Titanium oxide coated kaolin [1,! , listed in Table 1 or mixture of titanium oxide and kaolin [■] (Ratio of titanium oxide/[■] or [IT] is listed in Table 1) Talc 5.0 The above acid content C is uniformly mixed. , is added to component B, and is well dispersed at 70°C. Separately, component A is heated and dissolved at 70° C., the above mixture is added thereto, and the mixture is uniformly emulsified using a pomo mixer. After emulsification, the product is cooled to 30°C.

（ｂ）ケーキ状ファンデーションの組成。(b) Composition of cake-like foundation.

成　分　Ａ　　　　　　　　　　配合量（％）酸化チタ
ン被覆カオリン［Ｉ］、　　第１表に記載または酸化チ
タンとカオリン［ＩＩ］ との混合物（酸化チタン／［Ｉ］ または［１］の比は第１表に記載） タルク　　　　　　　　　　　　　　　残部ベンガラ　
　　　　　　　　　　　　　　１．０黄酸化鉄　　　　
　　　　　　　　　　２．５黒酸化鉄　　　　　　　　
　　　　　　０．０５成　分　Ｂ　　　　　　　　　　
配合量（％）流動パラフィン　　　　　　　　　　　８
．５Ｉ　Ｉ）　Ｐ　　　　　　　　　　　　　　　　ｌ
　、　０セスキオレイン酸ソルビタン　　　　　３．０
プロピレングリコール　　　　　　　２．５パラベン　
　　　　　　　　　　　　　０．２成　分　Ｃ配合量（
％） 香料　　　　　　　　　　　　　　　　０．２５上記°
成分Ａをヘンシェルミキサーで５分間攪拌する。一方、
他の容器にて７０°Ｃに加温溶解した成分Ｂを前記成分
Ａに滴下しながら攪拌混合する。Component A Blend amount (%) Titanium oxide coated kaolin [I], listed in Table 1 or mixture of titanium oxide and kaolin [II] (ratio of titanium oxide/[I] or [1] listed in Table 1) Listed) Talc Remaining red iron
1.0 yellow iron oxide
2.5 black iron oxide
0.05 component B
Blend amount (%) Liquid paraffin 8
．． 5I I) P l
, 0 sorbitan sesquioleate 3.0
Propylene glycol 2.5 paraben
0.2 component C compounding amount (
%) Fragrance 0.25° above
Mix component A with a Henschel mixer for 5 minutes. on the other hand,
Component B, which was heated and dissolved at 70° C. in another container, was added dropwise to the component A while stirring and mixing.

ついで、該混合物に成分Ｃを加えて１分間攪拌混合し、
得られた混合物を一定量ずつ金皿に充填し、ケーキ状フ
ァンデーノヨンを製造する。Then, component C was added to the mixture and stirred and mixed for 1 minute,
A fixed amount of the obtained mixture is filled into a metal plate to produce a cake-like foundation noyon.

これら各化粧料組成物の評価は、つぎの方法により行な
った。Evaluation of each of these cosmetic compositions was performed by the following method.

（１）ＳＰＦ 光源：東芝ＦＬ２０Ｓ−Ｅ−３０３本 中心波長　３０６ｎｍ 被照射部位までの距離　６０ｃｍ 被照射部位二日本人、色白肌および普通肌の成人男女の
背部 試験化粧料塗布量：０．２ｇ／ｌ　００ｃｍ”上記の条
件によりＦＤＡに定められたＳＰＦ’の測定法に準じ、
光量一定とし照射時間を３〜６０分で変化させ、試験化
粧料未塗布部位と塗布部位との最小紅斑惹起紫外線ｆｉ
（ＭＥＤ）の比を次式により求めた。(1) SPF Light source: Toshiba FL20S-E-303 Center wavelength: 306 nm Distance to irradiated area: 60 cm Irradiated area: Back test of two Japanese, fair-skinned and normal-skinned adult men and women Cosmetic application amount: 0.2g/ According to the SPF' measurement method specified by the FDA under the above conditions,
The light intensity was kept constant and the irradiation time was varied from 3 to 60 minutes to determine the minimum erythema-inducing ultraviolet ray fi between the area where the test cosmetic was not applied and the area where it was applied.
The ratio of (MED) was determined using the following formula.

測定値の妥当性は、ＦＤＡ広の標孕ザンスクリーン（８
％ポモザレートａ−ノヨン）によって確認した（ｎ＝２
０以上）。The validity of the measured values is confirmed by the FDA standard xanscreen (8
% pomosarate a-noyon) (n=2
0 or more).

（２）透明性 前記試験クリームを肌に延ばしたとき、白味が認められ
ろか、否かを１０名のパネラ−により評価した。(2) Transparency When the test cream was spread on the skin, a panel of 10 people evaluated whether a white tinge was observed or not.

○：　１０名とも白味を認めない △：　１〜５名が白味を認めろ ×：　６名以上が白味を認める （３）ブルーミング 前記試験クリームを肌に延ばしたとき、ブルーミング（
青味）が認められるか、否かを１０名のパネラ−により
評価した。なお、このブルーミングは、従来の微粒子酸
化チタンを配合した化粧料で生じやすい。○: None of the 10 people recognized the white taste △: 1 to 5 people recognized the white taste ×: 6 or more people recognized the white taste (3) Blooming When the test cream was spread on the skin, blooming (
A panel of 10 people evaluated whether or not a blue tint was observed. Note that this blooming tends to occur with conventional cosmetics containing fine particle titanium oxide.

○：　１０名とも青味を認めない △：　１〜５名が青味を認める Ｘ二　６名以上が青味を認める （４）安定性 試験クリームを製造後、５０℃にて一週間放置し、凝集
（ツブ）の有無を観察し、つぎの基準で評価した。○: None of the 10 people noticed a blue taste. △: 1 to 5 people found a blue taste. The presence or absence of aggregation (stubble) was observed and evaluated according to the following criteria.

○：　異常なし △：　微かなツブが認められる ×：　明らかなツブが認められる （５）分散性 プレスして得られた試験ケーキ状ファンデーション中の
不均一な固まり（微粒子酸化チタン）の有無を観察し、
つぎの基準で評価した。○: No abnormality △: Slight lumps are observed ×: Clear lumps are observed (5) Observe the presence or absence of uneven lumps (fine particle titanium oxide) in the test cake-like foundation obtained by dispersion pressing. death,
Evaluation was made based on the following criteria.

○：　不均一な固まり、なし △：　不均一な固まりか、微かに認められる×：　不均
一な固まり、あり （６）色味の差 試験ケーキ状ファンデーションの製品そのものの色と、
肌に塗布した際の色味との差の有無を１０名のパネラ−
により評価した。なお、この色味の差は、従来の微粒子
酸化チタンを配合した化粧料で生じやすい。○: Non-uniform clumping, absent △: Non-uniform clumping, slightly observed ×: Non-uniform clumping, present (6) Color difference test The color of the cake-like foundation product itself and
A panel of 10 people evaluated whether there was a difference in color when applied to the skin.
Evaluated by. Note that this difference in color tends to occur in cosmetics containing conventional fine-particle titanium oxide.

○：　９名以上が同一と判断する △：　２〜５名が差有りと判断する Ｘ：　６名以上が差有りと判断する （６）仕上がり感 試験ケーキ状ファンデーションを水を用いて肌に塗布す
る。塗布した粉が凝集を起こして塗布部位周辺に白く粉
が集まる現象（白化）の有無、または、仕上がりムラの
有無をつぎの基準により評価　　　　。○: 9 or more people judge that it is the same △: 2 to 5 people judge that there is a difference X: 6 or more people judge that there is a difference (6) Finish feeling test Apply cake-like foundation to skin using water do. Evaluate the presence or absence of a phenomenon in which the applied powder causes aggregation and the white powder collects around the application area (whitening), or the presence or absence of uneven finish using the following criteria.

する。do.

Ｏ：　白化は生じない △：　わずかに白化が生じる（または、粉っぽい仕上が
り） ×：　白化が生じる（または、塗りムラが生じる）第１
表および第２表より明らかなごとく、酸化チタン被覆カ
オリンを配合した本発明のクリームおよびケーキ状ファ
ンデーションは、いずれも従来の微粒子酸化チタンをカ
オリンとともに単に混合して配合した化粧料組成物より
遥かに広範囲の配合量にて化粧料に配合することが可能
であり優れた紫外線遮断効果が得られるとともに化粧料
として好ましい性状を示す。O: No whitening occurs △: Slight whitening occurs (or powdery finish) ×: Whitening occurs (or uneven coating occurs) 1st
As is clear from Tables 1 and 2, the cream and cake-like foundation of the present invention containing titanium oxide-coated kaolin are far more effective than conventional cosmetic compositions containing simply mixing fine-particle titanium oxide with kaolin. It can be incorporated into cosmetics in a wide range of amounts, provides excellent ultraviolet blocking effects, and exhibits desirable properties as cosmetics.

また、酸化チタン被覆カオリンに対する酸化チタンの被
覆量は、１〜５０％が好ましい。被覆量が、１％未満の
場合は紫外線遮断効果が充分でなく、一方、５０％を越
えると、化粧料としての諸性質が低下する。　なお、か
かる酸化チタン被覆カオリンの組成物全体に対する配合
量は、化粧料の形態に応じて９０％以下の範囲にて適宜
変化させてよい。Further, the amount of titanium oxide coated on the titanium oxide-coated kaolin is preferably 1 to 50%. If the coating amount is less than 1%, the UV blocking effect will not be sufficient, while if it exceeds 50%, the properties as a cosmetic will deteriorate. The amount of the titanium oxide-coated kaolin in the entire composition may be varied within a range of 90% or less depending on the form of the cosmetic.

さらに、本発明の化粧料組成物には、従来の微粒子酸化
チタンを３％以下配合しても良い。Furthermore, the cosmetic composition of the present invention may contain 3% or less of conventional fine particle titanium oxide.

本発明の化粧料組成物としては、例えば、ケーキ状また
は乳液状のファンデーション、白粉、リップスティック
、乳液、クリームなどが挙げられる。Examples of the cosmetic composition of the present invention include cake-like or milky lotion foundations, white powders, lipsticks, milky lotions, and creams.

これらの化粧料組成物を製造するには、前記酸化チタン
被覆カオリンを配合し、それぞれ常法により処理を行な
う。In order to produce these cosmetic compositions, the titanium oxide-coated kaolin described above is blended and treated in a conventional manner.

実施例 以下に本発明を実施例にもとづき、さらに詳細に説明す
る。EXAMPLES The present invention will be explained in more detail below based on examples.

実施例１ つぎの組成により、ケーキ状ファンデーションを製造し
た。Example 1 A cake-like foundation was manufactured using the following composition.

成　分　Ａ　　　　　　　　　　配合量（％）酸化チタ
ン被覆カオリン （肢ｒｒ１’２１０　％）　　　　　　　　　　　５０
　、０微粒子酸化チタン （平均粒径８ｍ７ｚ）　　　　　　　　　　　３．０タ
ルク　　　　　　　　　　　　　　２９．３ベンガラ　
　　　　　　　　　　　　　　　０．６黄酸化鉄　　　
　　　　　　　　　　　１．５黒酸化鉄　　　　　　　
　　　　　　　０．１５成　分　Ｂ　　　　　　　　　
　配合量（％）流動パラフィン　　　　　　　　　　　
８５バルミチノ酸イソプロピル　　　　　　１０セスキ
オレイン酸ソルヒタン　　　　　３０プロピレングリコ
ール　　　　　　　２５パラベン　　　　　　　　　　
　　　　０．２成　分　Ｃ配合量（％） 香料　　　　　　　　　　　　　　　　０．２５成分Ａ
をヘンンエルミキサーで５分間攪拌する。Component A Amount (%) Titanium oxide coated kaolin (limb rr1'210%) 50
, 0 fine particle titanium oxide (average particle size 8m7z) 3.0 Talc 29.3 Red iron
0.6 yellow iron oxide
1.5 black iron oxide
0.15 ingredient B
Blend amount (%) Liquid paraffin
85 Isopropyl balmitinoate 10 Sorhitane sesquioleate 30 Propylene glycol 25 Paraben
0.2 component C blending amount (%) Fragrance 0.25 component A
Mix with a Hennel mixer for 5 minutes.

一方、他の容器にて７０°Ｃに加温溶解した成分Ｂを前
記成分へに滴下しながら攪拌混合し、ついで、成分Ｃを
加えて１分間攪拌混合し、得られた混合物を一定量ずつ
合冊に充填して、ケーキ状ファンデーソヨンを製造した
。Meanwhile, in another container, component B, which had been heated and dissolved at 70°C, was added dropwise to the above components while stirring and mixing. Next, component C was added and mixed with stirring for 1 minute. A cake-like foundation soyon was produced by filling the mixture into a bundle.

該ファンデーション製造において、酸化チタンは均一に
分散し、また、使用に際して、皮膚に均一な塗布を行う
ことができ、仕上がりか非常に良好であった。In the production of this foundation, titanium oxide was uniformly dispersed, and upon use, it could be applied uniformly to the skin and the finish was very good.

実施例２ つぎの組成により、乳液状ファンデーションを製造した
。Example 2 A milky lotion foundation was manufactured using the following composition.

；戊　分　Ａ　　　　　　　　　　配合ｍ（％）流動パ
ラフィン　　　　　　　　　　　４．０モノステアリン
酸グリセリン　　　　　２０ステアリン酸　　　　　　
　　　　　　３０ラノリン　　　　　　　　　　　　　
　２０固型バラフイノ　　　　　　　　　　　０・５モ
ノステアリン酸プロピレン グリコール　　　　　　　　　　　　　０５パラオキノ
安息香酸プロピル　　　　０１成　分　Ｂ　　　　　　
　　　　配合ｍ（％）精製水　　　　　　　　　　　　
　　５７．２トリエタノールアミン　　　　　　　　１
．０カルボキンメチルセルロース ナトリウム　　　　　　　　　　　　　０．２ベントナ
イト　　　　　　　　　　　　０５モノステアリン酸ポ
リオキシ エチレンソルビタン　　　　　　　　　１．５プロピレ
ングリコール　　　　　　　　７．５成　分　Ｃ配合量
（％） 酸化チタン被覆カオリン （被覆量３０％）　　　　　　　　　　　　Ｉ　Ｏ，０
微粒子酸化ヂクン （平均粒径８ｍμ）２．０ タルク　　　　　　　　　　　　　　　５．０ベンガラ
　　　　　　　　　　　　　　　０．７黄酸化鉄　　　
　　　　　　　　　　　２．０黒酸化鉄　　　　　　　
　　　　　　　０．３成分Ａおよび成分Ｂを各々別個の
容器で８０℃まで加温溶解後、成分Ｂを成分Ａに投入す
る。１０分間攪拌し、さらに成分Ｃを投入した後、１５
分間攪拌し、３０℃まで冷却して乳液状ファンデーショ
ンを製造した。；Broken A Mixture m (%) Liquid paraffin 4.0 Glycerin monostearate 20 Stearic acid
30 lanolin
20 Solid Balafino 0.5 Propylene glycol monostearate 05 Propyl para-oquinobenzoate 01 Component B
Blend m (%) Purified water
57.2 Triethanolamine 1
．． 0 Sodium carboxin methylcellulose 0.2 Bentonite 05 Polyoxyethylene sorbitan monostearate 1.5 Propylene glycol 7.5 Component C blending amount (%) Titanium oxide coated kaolin (coating amount 30%) I O,0
Fine particle oxide (average particle size 8mμ) 2.0 Talc 5.0 Red iron oxide 0.7 Yellow iron oxide
2.0 black iron oxide
0.3 After heating and dissolving component A and component B in separate containers to 80° C., component B is added to component A. After stirring for 10 minutes and adding component C,
The mixture was stirred for a minute and cooled to 30° C. to produce a milky foundation.

該ファンデーション製造において、酸化チタンは均一に
分散して貯蔵中も凝集を起こさず、また、使用に際して
、皮膚に均一な塗布を行うことができ、仕上がりが非常
に良好であった。In producing the foundation, the titanium oxide was uniformly dispersed and did not aggregate during storage, and when used, it could be applied uniformly to the skin and the finish was very good.

実施例３ つぎの組成により、白粉を製造した。Example 3 A white powder was produced with the following composition.

成　分　Ａ　　　　　　　　　　配合量（％）酸化チタ
ン被覆カオリン （披Ｗｉｌ１％）　　　　　　　　　　　　９０．０タ
ルク　　　　　　　　　　　　　　　　５．０黄酸化鉄
　　　　　　　　　　　　　　１．５ベンガラ　　　　
　　　　　　　　　　　１４黒酸化鉄　　　　　　　　
　　　　　　０．１成　分　Ｂ　　　　　　　　　　配
合量（％）スクワラン　　　　　　　　　　　　２．２
セスキオレイン酸ソルビタン　　　　　ｏ５５成Ｃ願Ｉ
Ｊ 香料　　　　　　　　　　　　　　　　ｏ３３成Ａをヘ
ンンエルミキサーで５分間攪拌ずろ。Component A Amount (%) Titanium oxide coated kaolin (1%) 90.0 Talc 5.0 Yellow iron oxide 1.5 Red iron oxide
14 black iron oxide
0.1 Ingredient B Blending amount (%) Squalane 2.2
Sorbitan sesquioleate o55 formulation C application I
J Fragrance O33 Mix A with a Hennel mixer for 5 minutes.

一方、成分Ｂを他の容器を用い７０’Ｃにて均一に溶融
し、前記成分Ａに滴下しながら攪拌混合を行なう。さら
に、成分Ｃを滴下後、１分間攪拌混合し、アトマイザ−
により粉砕し製品を得る。On the other hand, component B is uniformly melted at 70'C using another container, and is added dropwise to component A while stirring and mixing. Furthermore, after dropping component C, stir and mix for 1 minute, and
to obtain a product.

該白粉製造において、酸化チタンは均一に分散し、また
、使用ノこ際して、皮膚に均一な塗布を行うことがてき
、仕上がりが非常に良好であった。In the production of the white powder, titanium oxide was uniformly dispersed, and upon use, it was possible to uniformly apply it to the skin, resulting in a very good finish.

実施例４ つぎの組成により、リップスティックを製造し収−外−
Ａ　　　　　　　　　　配合量（％）酸化ヂタノ被覆カ
オリン　　　　′ （被覆１２０％）５０ 雲母末　　　　　　　　　　　　　　　５，０赤色２０
２号　　　　　　　　　　　　０５赤色２０４号　　　
　　　　　　　　　０．５成　分　Ｂ　　　　　　　　
　　配合量（％）キャンデリラロウ　　　　　　　　　
　７．０固形パラフイン　　　　　　　　　　　７０ミ
ツロウ　　　　　　　　　　　　　　　５０カルナウバ
ロウ　　　　　　　　　　　５，０ヒマノ油　　　　　
　　　　　　　　　４４８ミリスチン酸イソプロピル　
　　　　　１００成　分　Ｃ配合量（％） 香料　　　　　　　　　　　　　　　　０．２成分Ａお
よびヒマン浦の一部を乳鉢を用いて均一に混練し、顔料
部とする。成分Ｂの残部を加熱溶解し、これに面記顔料
部を加え、ホモミキサーで均一に分散し、さらに、成分
Ｃを添加、分散する。これを型に流し込みんでスティッ
ク状に急冷し、得られた固形物を容器に固定し、フレー
ミングを行ない製品とする。Example 4 A lipstick was manufactured with the following composition and then collected.
A Blending amount (%) Ditano oxide coated kaolin' (coating 120%) 50 Mica powder 5,0 Red 20
No. 2 05 Red No. 204
0.5 component B
Compounding amount (%) Candelilla wax
7.0 Solid paraffin 70 Beeswax 50 Carnauba wax 5.0 Himano oil
448 Isopropyl myristate
100 Component C Amount (%) Fragrance 0.2 Component A and a part of Himanura are uniformly kneaded using a mortar to form a pigment part. The remainder of component B is heated and dissolved, the surface pigment part is added thereto, and the mixture is uniformly dispersed using a homomixer, and then component C is added and dispersed. This is poured into a mold and rapidly cooled into a stick shape, and the resulting solid substance is fixed in a container and framed to produce a product.

該リップスティック製造において、酸化チタンは均一に
分散し、また、使用に際して、唇に均一な塗布を行うこ
とができ、仕上がりが非常に良好であった。In producing the lipstick, titanium oxide was uniformly dispersed, and upon use, it could be applied uniformly to the lips, giving a very good finish.

実施例５ つぎの組成により、乳液を製造した。Example 5 A milky lotion was produced with the following composition.

成　分　Ａ　　　　　　　　　　配合ｍ（％）ステアリ
ン酸　　　　　　　　　　　　　３．０セチルアルコー
ル　　　　　　　　　　１．５ワセリン　　　　　　　
　　　　　　　５．０流動パラフイン　　　　　　　　
　　１２．０パラオキンエチレンモノオレイン酸 エステル（Ｉ　０ＥＯ）　　　　　　　　　　２．５成
　分　Ｂ　　　　　　　　　　配合量（％）ポリエチレ
ングリコール １５００　　　　　　　　　　　　　　　２．０トリエ
タノールアミン　　　　　　　　　１０精製水　　　　
　　　　　　　　　　７１．５酸化チタン被覆カオリン （被覆量５０％）■、０ 成　分　Ｃ配合量（％） 香料　　　　　　　０．５ 成分Ｂを加熱し、７０°Ｃにて均一に分散する。Ingredients A Mixture m (%) Stearic acid 3.0 Cetyl alcohol 1.5 Vaseline
5.0 liquid paraffin
12.0 Paraoxene ethylene monooleate (I0EO) 2.5 Component B Blending amount (%) Polyethylene glycol 1500 2.0 Triethanolamine 10 Purified water
71.5 Titanium oxide coated kaolin (coating amount 50%) ■, 0 Component C blending amount (%) Fragrance 0.5 Component B is heated and uniformly dispersed at 70°C.

別個に成分Ａを７０°Ｃにて加熱、溶解し、前記成分Ｂ
に加え、ホモミキサーを用いて均一に乳化する。乳化後
、さらに攪拌しながら３０℃まで冷却し製品とする。Separately, heat and dissolve component A at 70°C, and then dissolve component B.
Add to this and homogeneously emulsify using a homomixer. After emulsification, the mixture is further cooled to 30°C while stirring to form a product.

該乳液製造において、酸化チタンは均一に分散して貯蔵
中ら凝集を起こさず、また、使用に際して、皮膚に均一
な塗布を行うことができ、仕上がりが非常に良好であっ
た。In the production of the emulsion, the titanium oxide was uniformly dispersed and did not aggregate during storage, and upon use, it could be applied uniformly to the skin and the finish was very good.

実施例６ つぎの組成によりクリームを製造した。Example 6 A cream was produced with the following composition.

成　分　Ａ　　　　　　　　　　配合量（％）固形パラ
フィン　　　　　　　　　　５．０ミツロウ　　　　　
　　　　　　　　４・０マイク〔７クリスタリンワツク
ス　　　４．０ワセリン　　　　　　　　　　　　　７
．０スクワラン　　　　　　　　　　　　３０．０ポリ
オキシエチレンモノ ラウリン酸ソルビタン（２０ＥＯ）　　　　　　１．０
セスキオレイン酸ソルビタン　　　　　４．０成　分　
Ｂ　　　　　　　　　　配合量（％）精製水　　　　　
　　　　　　　　　２０，０成　分　Ｃ配合量（％） 酸化チタン被覆カオリン （被覆量５％）　　　　　　　　　　　　　２０．０タ
ルク　　　　　　　　　　　　　　　５．０上記酸分Ｃ
を均一に混合し、成分口に加え、７０℃にてよく分散す
る。別に、成分Ａを７０℃で加熱、溶解し、これに前記
混合物を加え、ホモミキサーで均一に乳化する。乳化後
、３０°Ｃまて冷却し製品とする。Component A Amount (%) Solid paraffin 5.0 Beeswax
4.0 Microphone [7 Crystalline Wax 4.0 Vaseline 7
．． 0 Squalane 30.0 Sorbitan polyoxyethylene monolaurate (20EO) 1.0
Sorbitan sesquioleate 4.0 ingredients
B Blend amount (%) Purified water
20.0 Component C blending amount (%) Titanium oxide coated kaolin (coating amount 5%) 20.0 Talc 5.0 Above acid content C
Mix uniformly, add to the ingredient port, and disperse well at 70°C. Separately, component A is heated and dissolved at 70°C, the mixture is added thereto, and the mixture is uniformly emulsified using a homomixer. After emulsification, cool to 30°C to obtain a product.

該クリーム製造において、酸化チタンは均一に分散して
貯蔵中も凝集を起こさず、また、使用に際して、皮膚に
均一な塗布を行うことができ、仕上がりが非常に良好で
あった。In the production of the cream, the titanium oxide was uniformly dispersed and did not aggregate during storage, and when used, it could be applied uniformly to the skin and the finish was very good.

Claims (2)

【特許請求の範囲】[Claims] （１）酸化チタンにより被覆されたカオリン粒子を配合
したことを特徴とする化粧料組成物。(1) A cosmetic composition characterized by containing kaolin particles coated with titanium oxide. （２）酸化チタンにより被覆されたカオリン全体に対す
る酸化チタンの被覆量が、１〜５０重量％である前記第
１項の化粧料組成物。(2) The cosmetic composition according to item 1 above, wherein the amount of titanium oxide coated with respect to the entire kaolin coated with titanium oxide is 1 to 50% by weight.
JP3700785A 1985-02-25 1985-02-25 Cosmetic composition Expired - Fee Related JPH0655663B2 (en)