JPS6115937A - Aluminum alloy plate for blind - Google Patents

Abstract

PURPOSE:To obtain a high strength Al alloy for a blind undergoing little reduction in the strength by coating and baking when the blind is made of the alloy, by adding specified amounts of Mg, Zn, Cu, etc. to Al. CONSTITUTION:When a blind is made of a lightweight Al alloy plate, an Al alloy contg., by weight, 3.0-5.5% Mg, 0.5-2.0% Zn, 0.6-1.5% Cu and 0.01- 0.2% Ti and 0.002-0.04% B or further contg. 0.05-0.5% one or more among Mn, Cr, V and Zr is used as the material of the plate for the blind. The Al alloy plate is a lightweight plate undergoing no reduction in the strength by coating and baking and having superior strength even after coating and baking.

Description

【発明の詳細な説明】 ［産業上の利用分野］ 本発明はブラインド用アルミニウム合金板に関し、さら
に詳しくは、塗装焼付後における強度の優れたブライン
ド用アルミニウム合金板に関する。DETAILED DESCRIPTION OF THE INVENTION [Industrial Application Field] The present invention relates to an aluminum alloy plate for blinds, and more particularly to an aluminum alloy plate for blinds that has excellent strength after baking the paint.

［従来技術１ いままでは、ブラインド用アルミニウム合金板としては
、Ａｌ−４〜５ｗｔ％Ｍｇ基合金の５０８３−Ｈ２Ｓの
板厚１５０〜３００μｍのものが用いられているが、ブ
ラインド製造工程中の塗装焼付は工程において強度が低
下する。そして、この対策としては、材料強度低下をカ
バーする手段として板厚を厚くしていた。[Prior Art 1 Up until now, aluminum alloy plates for blinds have been made of 5083-H2S, an Al-4 to 5 wt% Mg-based alloy, with a thickness of 150 to 300 μm. Seizure reduces strength during the process. As a countermeasure to this problem, the thickness of the plate was increased to compensate for the decrease in material strength.

しかして、ブラインドのアルミニウム合金板が厚くなる
と重くなるので、軽量化を図ることと、コスト低減のた
めに、できる限り薄い材料を使用する必要があることか
ら、薄く、かつ、強度の高いブラインド゛用アルミニウ
ム合金板が要望されており、例えば、２００〜２３０℃
の温度で０．５〜３分の加熱による塗装焼付けによる強
度低下率が５０８３−Ｈ２Ｓより小さく、がっ、強度の
高いブラインド用アルミニウム合金板かの出現が望まれ
ていた。However, the thicker the aluminum alloy plate of the blind, the heavier it becomes, so in order to reduce weight and cost, it is necessary to use as thin a material as possible. There is a demand for aluminum alloy plates for
It has been desired to develop an aluminum alloy plate for blinds which has a lower strength reduction rate than 5083-H2S due to paint baking when heated for 0.5 to 3 minutes at a temperature of

［発明が解決しようとする問題点１ 本発明者は上記に説明したように、従来使用されていた
５０８３−Ｈ２Ｓより塗装焼付けによる強度低下率がよ
り小さく、かつ、塗装焼付は後の強度が高いブラインド
用Ａｌ−１１／ｆＺｎ系アルミニウム合金板を開発した
が、その後さらに、研究を進めた結果、より塗装焼付は
後の強度が高く、かつ、より強度低下率の小さいＡｌ−
Ｚｎ−Ｍｇ−Ｃｕ系合金からなるブラインド用アルミニ
ウム合金板を開発した。[Problem to be Solved by the Invention 1] As explained above, the present inventor has found that the strength reduction rate due to paint baking is smaller than the conventionally used 5083-H2S, and the strength after paint baking is high. We developed an Al-11/fZn-based aluminum alloy plate for blinds, but as a result of further research, we found that Al-11/fZn-based aluminum alloy plate has higher strength after paint baking and has a lower rate of strength decline.
We have developed an aluminum alloy plate for blinds made of Zn-Mg-Cu alloy.

［問題点を解決するための手段１ 本発明に係るブラインド用ＡｌＭｇ−Ｚｎ系アルミニウ
ム合金板は、 （１）　　Ｍｇ　３．０−５．５ｗｔ％、Ｚ　ｎ　０．
５〜２．’　０ｗｔ％、Ｃｕ　０，６−１．！１ｏｕｔ
％ を含有し、かつ、 Ｔｉ　０．０１〜０．２＋ｕｔ％、Ｂ　０．００２〜０
．０４ｗｔ％の１種または２種 を含有し、残部Ａｌおよび不純物からなることを特徴の
するブラインド用アルミニウム合金板を第１の発明とし
、 （２）　　Ｍｇ３．０−５．５ｗｔ％、Ｚｎ　０．５〜
２．０ｗｔ％、Ｃｕ　０．６−１，５ｗｔ％ を含有し、かつ、 Ｔｉ　０．０１〜０．２ｗｔ％、Ｂ　０．００２＝０．
０４ｗｔ％の１種または２種 を含有し、さらに、 Ｍｎ　０．０５〜０．５ｗｔ％、Ｏｒ　０．０５〜０，
５＋ｕｔ％、Ｖ　０．０５〜０，５ｗｔ％、Ｚ　ｒ　０
．０５〜０．５ｗｔ％のうちから選んだ１種または２種
以上を 含有し、残部Ａｌおよび不純物からなることを特徴とす
るブラインド用アルミニウム合金板を第２の発明とする
２つの発明よりなるものである。[Means for Solving the Problems 1] The AlMg-Zn-based aluminum alloy plate for blinds according to the present invention contains: (1) Mg 3.0-5.5wt%, Zn 0.
5-2. ' 0 wt%, Cu 0.6-1. ! 1 out
%, and Ti 0.01-0.2+ut%, B 0.002-0
．． The first invention is an aluminum alloy plate for blinds, which is characterized by containing one or two of 0.04 wt% and the balance consisting of Al and impurities, (2) 3.0-5.5 wt% of Mg, 0.0-5.5 wt% of Zn. 5~
2.0 wt%, Cu 0.6-1.5 wt%, Ti 0.01-0.2 wt%, B 0.002=0.
Mn 0.05-0.5 wt%, Or 0.05-0,
5+ut%, V 0.05-0.5wt%, Z r 0
．． The second invention is an aluminum alloy plate for blinds containing one or more selected from 0.05 to 0.5 wt%, and the remainder being Al and impurities. It is.

本発明に係るブラインド用系アルミニウム合金板１こつ
いて以下詳細に説明する。The blind aluminum alloy plate 1 according to the present invention will be described in detail below.

先ず、本発明に係るブラインド用アルミニウム合金板の
含有成分および成分割合について説明する。First, the components and component ratios of the aluminum alloy plate for blinds according to the present invention will be explained.

Ｍｇは強度を向上させる元素であり、含有量が３、Ｏｗ
ｔ％未満ではブラインド用としての強度が低く、また、
５．５ＩＩｌｔ％を越えて含有されると強度は高くなる
が、熱間圧延性および冷間圧延性が悪くなる。よって、
Ｍｇ含有量は３．０−・５．５＋ｎｔ％とする。Mg is an element that improves strength, and the content is 3, Ow
If it is less than t%, the strength for blinds is low, and
If the content exceeds 5.5 IIlt%, the strength will increase, but hot rolling properties and cold rolling properties will deteriorate. Therefore,
The Mg content is 3.0-5.5+nt%.

ＺｎはＭ８３．０〜５．５１％含有するアルミニウム合
金に含有させると、２００〜２３０℃の温度において０
．５〜３分の塗装焼付は後の強度を向上させ、かつ、強
度低下率を小さくする元素であり、含有量が０．５ｗｔ
％未満ではこのような効果が小さく、また、　２．Ｏｗ
ｔ％を越えて含有されると強度向上の効果はあるが、熱
間圧延性および冷間圧延性が悪くなる。よって、Ｚｎ含
有量は０．５〜２．０ＩＩｌｔ％とする。When Zn is added to an aluminum alloy containing M83.0 to 5.51%, it becomes 0 at a temperature of 200 to 230°C.
．． Baking the paint for 5 to 3 minutes is an element that improves the strength afterward and reduces the rate of decrease in strength, and the content is 0.5wt.
If it is less than %, this effect will be small, and 2. Ow
If the content exceeds t%, there is an effect of improving strength, but hot rolling properties and cold rolling properties deteriorate. Therefore, the Zn content is set to 0.5 to 2.0 IIlt%.

ＣｕはＭｇ３．Ｌ５．５ｗｔ％、Ｚｎ　０．５〜２．Ｏ
ｗｔ％含有するアルミニウム合金に含有させると、塗装
焼付は後の強度向上および強度低下率を小さくさせる元
素であり、含有量が９．６ｗｔ％未満ではこのような効
果は小さく、また、１．５ｗｔ％を越えて含有されると
この効果は増大するが熱間圧延性および冷間圧延性が悪
くなる。よって、Ｃｕ含有量は０．６〜１．５１％とす
る。Cu is Mg3. L5.5wt%, Zn 0.5-2. O
When included in an aluminum alloy containing 1.5 wt%, paint baking is an element that improves the strength and reduces the rate of strength decrease afterward.If the content is less than 9.6 wt%, this effect is small; If the content exceeds %, this effect will increase, but hot rolling properties and cold rolling properties will deteriorate. Therefore, the Cu content is set to 0.6 to 1.51%.

Ｔｉ、Ｂは鋳塊の組織微細化に効果があり、Ｔｉ含有量
が０．０１ｗｔ％未満、Ｂ含有量が０．００２＋ｕｔ％
未満ではこの効果は小さく、また、Ｔｉ含有量が０．２
Ｉｌｌｔ％、Ｂ含有量か０．０４ｗｔ％を越えて含有さ
れるとこの効果は飽和してしまい無駄である。よって、
Ｔｉ含有量は０．０１四ｔ％〜０．２ｕｌｔ％、Ｂ含有
量は０．００２〜０．０４ｉｕｔ％とする。Ti and B are effective in refining the structure of the ingot, and the Ti content is less than 0.01wt% and the B content is 0.002+ut%.
This effect is small when the Ti content is less than 0.2
If the B content exceeds 0.04 wt%, this effect will be saturated and it will be useless. Therefore,
The Ti content is 0.014t% to 0.2ult%, and the B content is 0.002 to 0.04iut%.

Ｍｎ、Ｃｒ、■、Ｚｒは塗装焼付は後の強度を向上させ
る元素であり、含有量が夫々０，０５ｗｔ％未満ではこ
の効果は小さく、また、夫々０．５ｗｔ％を越えて含有
されるとこの効果は飽和してしまい無駄である。よって
、Ｍｎ、Ｃｒ、■、Ｚｒの含有量は夫１ｚ　０．０５〜
０，５ｗｔ％とする。なお、Ｍｎ、Ｃｒは上記の効果の
外に鋳塊の結晶粒微細化、熱間圧延性を向上させる効果
もある。Mn, Cr, ■, and Zr are elements that improve the strength after paint baking, and if the content is less than 0.05 wt% each, this effect is small, and if each content exceeds 0.5 wt%, This effect becomes saturated and is useless. Therefore, the content of Mn, Cr, ■, and Zr is 0.05~
It is set to 0.5 wt%. In addition to the above-mentioned effects, Mn and Cr also have the effect of refining the crystal grains of the ingot and improving hot rolling properties.

なお、上記の含有成分以外に不可避的な不純物が含まれ
ることがあるが、その不純物は１成分では０，２５ｗｔ
％以下、また、複数の場合にはその合計が（１，７５ｗ
ｔ％以下に規制する必要があり、この含有量は、本発明
に係るブラインド用アルミニウム合金板の目的を達成す
るのを阻害することなく許容される範囲である。In addition, unavoidable impurities may be included in addition to the above-mentioned components, but the impurities are 0.25wt in one component.
% or less, or in the case of multiple, the total is (1,75w
It is necessary to regulate the content to t% or less, and this content is within an allowable range without hindering the achievement of the purpose of the aluminum alloy plate for blinds according to the present invention.

［実施例１ 次に、本発明に係るブラインド用アルミニウム合金゛板
の実施例について説明する。[Example 1] Next, an example of an aluminum alloy plate for blinds according to the present invention will be described.

実施例 第１表に示す含有成分および成分割合のアルミニウム合
金を溶製後鋳造して得られた鋳塊を、面削→均質化処理
→熱間圧延→冷間圧延→中間熱処理→冷間圧延→熱処理
→冷間圧延の順で処理を行なって、１５０μＩＩＩ厚の
ブラインド用アルミニウムム合金板とした。Example An ingot obtained by melting and casting an aluminum alloy having the components and proportions shown in Table 1 is subjected to facing → homogenization → hot rolling → cold rolling → intermediate heat treatment → cold rolling. The aluminum alloy plate for blinds having a thickness of 150μIII was obtained by performing the following treatments: → heat treatment → cold rolling.

このアルミニウム合金板について、塗装焼付は条件２２
０°Ｃ×１分加熱前後における材料特性および圧延性に
ついて第２表に示す。Regarding this aluminum alloy plate, the paint baking condition is 22.
Table 2 shows the material properties and rollability before and after heating at 0°C for 1 minute.

この第２表から明らかなように、本発明に係るアルミニ
ウム合金板は比較合金２の５０８３−８１８および比較
合金１のＡｈ−Ｍｇ−Ｚｎ系アルミニウム合金に比して
塗装焼付は後の耐力が高く、また、耐力低下量が小さい
ことがわかる。As is clear from Table 2, the aluminum alloy plate according to the present invention has a higher yield strength after paint baking compared to Comparative Alloy 2 (5083-818) and Comparative Alloy 1 (Ah-Mg-Zn aluminum alloy). , It can also be seen that the amount of decrease in yield strength is small.

また、その外の比較合金に″おいても、特に、比較合金
３．４は塗装焼付けの耐力が高いが、圧延性が悪く、さ
らに、比較合金５は塗装焼付は後の耐力カ５極端に低い
ことがわかる。In addition, among the other comparative alloys, Comparative Alloy 3.4 has a high resistance to paint baking, but has poor rollability, and Comparative Alloy 5 has extremely high resistance to paint baking. You can see that it is low.

なお、第２表において、 ※１　：　強度低下率 ＝（加熱前のσ。、２−２２０℃×１分加熱後のσ。、
、）／加熱前のσ。、２Ｘ　１００ ×２　：　圧延性 熱間圧延時および冷開圧延時の耳割れにより判定 Ｇ　：　良好 ＮＧ　：　耳割れ発生大で歩留り低下 である。In Table 2, *1: Strength reduction rate = (σ before heating, σ after heating at 2-220°C x 1 minute.
, )/σ before heating. , 2X 100 ×2: Rollability Judgment based on edge cracking during hot rolling and cold open rolling G: Good NG: Severe edge cracking occurs and yield decreases.

［発明の効果１ 以上説明したように、本発明に係るブラインド用アルミ
ニウム合金板は上記に説明した構成であるから、現在使
用されている　５０８３−Ｈ２Ｏに比較して、２００〜
ｂ 塗装焼付けによる強度低下率が小さく、がっ、塗装焼付
は後の強度も高く、ブラインド用のアルミニウム合金板
として優れた効果を有するものである。[Effect of the Invention 1 As explained above, since the aluminum alloy plate for blinds according to the present invention has the above-described structure, compared to the currently used 5083-H2O,
(b) The rate of decrease in strength due to paint baking is small, and the strength after paint baking is also high, making it an excellent aluminum alloy plate for blinds.

Claims (2)

【特許請求の範囲】[Claims] （１）Ｍｇ　３．０〜５．５ｗｔ％、Ｚｎ　０．５〜２
．０ｗｔ％、Ｃｕ　０．６〜１．５ｗｔ％ を含有し、かつ、 Ｔｉ　０．０１〜０．２ｗｔ％、Ｂ　０．００２〜０．
０４ｗｔ％の１種または２種 を含有し、残部Ａｌおよび不純物からなることを特徴と
するブラインド用アルミニウム合金板。(1) Mg 3.0-5.5wt%, Zn 0.5-2
．． 0 wt%, Cu 0.6-1.5 wt%, and Ti 0.01-0.2 wt%, B 0.002-0.
1. An aluminum alloy plate for blinds, characterized in that the aluminum alloy plate contains 0.04 wt% of one or two types, and the remainder consists of Al and impurities. （２）Ｍｇ　３．０〜５．５ｗｔ％、Ｚｎ　０．５〜２
．０ｗｔ％、Ｃｕ　０．６〜１．５ｗｔ％ を含有し、かつ、 Ｔｉ　０．０１〜０．２ｗｔ％、Ｂ　０．００２〜０．
０４ｗｔ％の１種または２種 を含有し、さらに、 Ｍｎ　０．０５〜０．５ｗｔ％、Ｃｒ　０．０５〜０．
５ｗｔ％、Ｖ　０．０５〜０．５ｗｔ％、Ｚｒ　０．０
５〜０．５ｗｔ％のうちから選んだ１種または２種以上 を含有し、残部Ａｌおよび不純物からなることを特徴と
するブラインド用アルミニウム合金板。(2) Mg 3.0-5.5wt%, Zn 0.5-2
．． 0 wt%, Cu 0.6-1.5 wt%, and Ti 0.01-0.2 wt%, B 0.002-0.
04 wt% of one or two kinds, and further contains Mn 0.05 to 0.5 wt%, Cr 0.05 to 0.04 wt%.
5wt%, V 0.05-0.5wt%, Zr 0.0
An aluminum alloy plate for blinds, characterized in that it contains one or more selected from 5 to 0.5 wt%, with the balance being Al and impurities.