JPS61138567A - Production of heat resistant coated steel plate excellent in nonadhesive properties - Google Patents
Production of heat resistant coated steel plate excellent in nonadhesive propertiesInfo
- Publication number
- JPS61138567A JPS61138567A JP26001184A JP26001184A JPS61138567A JP S61138567 A JPS61138567 A JP S61138567A JP 26001184 A JP26001184 A JP 26001184A JP 26001184 A JP26001184 A JP 26001184A JP S61138567 A JPS61138567 A JP S61138567A
- Authority
- JP
- Japan
- Prior art keywords
- steel plate
- resin
- heat
- resistant
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
（産業上の利用分野〕
本発明は、所謂ベータウェア、オーブン天板、加熱プレ
ート等、食品加熱加工用具に好適な塗装鋼板、すなわち
常用の耐熱温度が２ｅｏ゛ａ＠度の耐熱性を有するとと
もに、優れた非粘着性、プレス成形性及び耐食性を有す
る耐熱塗装鋼板の製造方法に関する。Detailed Description of the Invention (Industrial Application Field) The present invention is a coated steel plate suitable for food heating processing tools such as so-called betaware, oven top plates, heating plates, etc. The present invention relates to a method for manufacturing a heat-resistant coated steel sheet that has high heat resistance, excellent non-adhesiveness, press formability, and corrosion resistance.
パンやケーキを焼くための所謂ベータウェア（部屋）や
オーブン天板等は、一般に２００℃前後の高温条件下で
使用され、しかも食品が直接触れるため耐食性及び耐熱
性が大きく要求される。加えて、コゲ付きが生ぜず、且
つ汚れ落しが簡単であるという所謂非粘着性＜ａｍ性）
があることが好ましい。So-called betaware (chambers), oven top plates, etc. for baking bread and cakes are generally used under high temperature conditions of around 200° C., and since they come into direct contact with food, corrosion resistance and heat resistance are highly required. In addition, it has a so-called non-adhesive property (am property) that does not cause scorching and is easy to remove stains.
It is preferable that there be.
耐食性１こ優れた鋼板として耐食性塗料による塗装鋼板
、例えば下塗りにエポキシ樹脂、上塗りにアクリル、ポ
リエステル、２フツ化ビニル系樹脂等が用いられた塗装
鋼板があるが、これらの塗膜の連続耐熱温度はせいぜい
高くても１２０〜１３０°０程度に過ぎず、高温域での
使用によって塗膜性能の劣化は避は難い。Steel sheets with superior corrosion resistance include coated steel sheets with corrosion-resistant paints, such as steel sheets coated with epoxy resin for the undercoat and acrylic, polyester, vinyl difluoride resin, etc. for the topcoat, but the continuous heat resistance temperature of these coatings is It is only about 120 to 130°0 at most, and deterioration of coating film performance is inevitable when used in a high temperature range.
また、このような従来の塗装鋼板は、その非粘着性が不
十分で、プレス成形性も十分で’ｘ ＜ 、絞り加工し
た場合、容易に割れを生じてしまうという難点がある。In addition, such conventional coated steel sheets have insufficient non-adhesive properties, insufficient press formability, and easily crack when drawn.
また、例えばフライパンや加熱プレート等については鋼
板にフッ素樹脂加工を施したものもあるが、その非粘着
性や耐食性が十分でなく、またプレス成形 −樹脂加工
で製造されるため、鋼板のプレス加工の際その成形性が
悪いという上述したと同様の問題がある。In addition, for example, frying pans and heating plates are made by applying fluororesin processing to steel plates, but the non-stick properties and corrosion resistance are insufficient, and since they are manufactured by press molding - resin processing, press processing of steel plates In this case, there is a problem similar to the above-mentioned problem of poor moldability.
本発明はこのような従来の問題に鑑み常用の耐熱温度が
２００ ’Ｏ以上の耐熱性を有し、しかも耐食性、非粘
着性及びプレス成形性に優れた塗装鋼板の製造法を提供
せんとするものであり、このため本発明は、ステンレス
鋼板またはメッキ鋼板面に、四フッ化エチレン樹脂と他
の耐熱樹脂との混合物を主成分とする塗料を塗布し、塗
膜焼付後、塗膜表面の平滑化と圧延とを目的としたロー
ル圧下を行うようにしたことをその基本的特徴とする。In view of these conventional problems, it is an object of the present invention to provide a method for producing a coated steel sheet that has a heat resistance of 200'O or more and has excellent corrosion resistance, non-adhesiveness, and press formability. Therefore, in the present invention, a paint mainly composed of a mixture of tetrafluoroethylene resin and other heat-resistant resin is applied to the surface of a stainless steel plate or a plated steel plate, and after the paint film is baked, the surface of the paint film is Its basic feature is that roll reduction is performed for the purpose of smoothing and rolling.
また、本発明は２コート２ベーク塗装鋼板として、ステ
ンレス鋼板またはメッキ鋼板面に、ポリフェニレンサル
ファイド樹脂またはポリエーテルサルフォン樹脂若しく
はポリフェニレンサルファイド樹脂とポリエーテルサル
フォン樹脂との混合物を耐熱樹脂とするプライマーを塗
布した後焼付け、その上に四フッ化エチレン樹脂と他の
耐熱樹脂との混合物を主成分とする塗料を塗付し、塗膜
焼付後、塗膜表面の平滑化と圧延とを目的としたロール
圧下を行うようにしたことを他の基本的特徴とする。In addition, the present invention provides a two-coat, two-bake painted steel sheet in which a primer containing a heat-resistant resin of polyphenylene sulfide resin, polyether sulfone resin, or a mixture of polyphenylene sulfide resin and polyether sulfone resin is applied to the surface of a stainless steel sheet or a plated steel sheet. After coating and baking, a paint mainly composed of a mixture of tetrafluoroethylene resin and other heat-resistant resins is applied on top of the coating, and after the coating is baked, the purpose is to smooth and roll the coating surface. Another basic feature is that roll reduction is performed.
以下本発明の詳細な説明する。The present invention will be explained in detail below.
本発明は所謂ベータウェア等の食品加熱加工用品に好適
な塗装鋼板の製造方法に関するもので、その素材鋼板と
してステンレス鋼板、各種メッキ鋼板を用いることがで
きる。上記メッキ鋼板としては、Ｚｎメッキ鋼板、Ａｔ
メッキ鋼板、Ｚｎ −Ａｔ系合金メッキ鋼板、Ｎｉ系メ
ッキ鋼板、Ｚｎ −Ｎｉ系合金メッキ鋼板、ステンレス
メッキ鋼板、 Ｃｒメッキ鋼板（所謂ティンフリー鋼板
）等がある。これら素材鋼板のうち塗装密着性及び高温
条件下における耐用性を重視する場合にはティンフリー
鋼板が好ましい。この鋼板は鋼板に電解クロメート処理
を施し、金属クロム及びクロム酸化物からなる被膜を形
成させたものであって、高温における耐酸化性が極めて
良好であり、４００°０前後の雰囲気ｔこ右いてもほと
んど酸化せず。The present invention relates to a method for manufacturing a coated steel plate suitable for food heating processing products such as so-called betaware, and stainless steel plates and various plated steel plates can be used as the raw steel plate. The above-mentioned plated steel plate includes Zn plated steel plate, At
There are plated steel plates, Zn-At alloy plated steel plates, Ni-plated steel plates, Zn-Ni alloy plated steel plates, stainless plated steel plates, Cr-plated steel plates (so-called tin-free steel plates), and the like. Among these steel plates, tin-free steel plates are preferred when painting adhesion and durability under high temperature conditions are important. This steel plate is made by applying electrolytic chromate treatment to the steel plate to form a coating consisting of metallic chromium and chromium oxide, and has extremely good oxidation resistance at high temperatures, even in an atmosphere of around 400°0. Almost no oxidation.
加えて、Ｚｎメッキ鋼板等に較べ優れた塗装密着性を有
している。また塗装密着性を重視する場合にはステンレ
ス系鋼板（ステンレス鋼板及びステンレスメッキ鋼板）
、Ｚｎ −Ａｔ系合金メッキ鋼板、Ｚｎ−Ｎｉ系合金メ
ッキ鋼板及びＮｉ系メッキ鋼板が好ましい。これらの鋼
板は通常の冷延鋼板、Ｚｎメッキ鋼板、Ｓｎメッキ鋼板
等に較べ耐食性に優れ、しかも塗装密着性にも優れてい
る。塗装密着性は、鋼板表面（メッキ鋼板の場合はメッ
キ面）に生じる酸化被膜の剥離性に大きく依存し、この
酸化被膜の剥離が塗装密着を阻害する主要な原因の１つ
となっている。この点、上記した各鋼板はＺｎメッキ鋼
板等の他の鋼板に較べ形成される酸化被膜が剥離しにく
い性質があり、このため優れた塗装密着性が得られる。In addition, it has superior paint adhesion compared to Zn-plated steel sheets and the like. In addition, if paint adhesion is important, use stainless steel plates (stainless steel plates and stainless steel plated steel plates).
, a Zn-At alloy plated steel sheet, a Zn-Ni alloy plated steel sheet, and a Ni-based plated steel sheet. These steel plates have better corrosion resistance than ordinary cold-rolled steel plates, Zn-plated steel plates, Sn-plated steel plates, etc., and also have excellent paint adhesion. Paint adhesion largely depends on the removability of the oxide film that forms on the surface of the steel plate (or the plated surface in the case of plated steel sheets), and peeling off of this oxide film is one of the main causes of inhibiting paint adhesion. In this respect, each of the steel plates described above has a property that the formed oxide film is less likely to peel off compared to other steel plates such as Zn-plated steel plates, and therefore excellent paint adhesion can be obtained.
なお、素材としてメッキ鋼板を用いる場合、リン酸塩処
理°またはクロメート処理による被膜を形成させること
により塗装密着性を向上させることができ、例えばＡｔ
−Ｚｎ合金メッキの場合でＡｔ係が低いような場合、特
に有効であるということができる。In addition, when using a plated steel plate as the material, coating adhesion can be improved by forming a film by phosphate treatment or chromate treatment, for example, At
- It can be said that this method is particularly effective when the At coefficient is low in the case of Zn alloy plating.
また、上記Ａｔ−Ｚｎ系メッキ％ Ｚｎ−Ｎ１系メッ
キ、及びＮ１系メブキに耐食性能等を考慮して他の元素
を添加することが可能である。Moreover, it is possible to add other elements to the above-mentioned At-Zn-based plating, Zn-N1-based plating, and N1-based plating in consideration of corrosion resistance and the like.
本発明はこのような素材鋼板面に高温（２００°０以上
）での常用耐熱性を有する耐熱塗料を塗布する。In the present invention, a heat-resistant paint having general heat resistance at high temperatures (200°0 or higher) is applied to the surface of such a raw steel plate.
塗装は１コートｌベーク又は２コート２べ−りで行われ
る。まず１コート１ベークの場合は、耐熱塗料として四
フッ化エチレン樹脂（ＰＴＦ’ｇ）と他の耐熱樹脂との
混合物を主成分とする塗料が用いられる。ＰＴＦ Ｅと
混合される他の耐熱樹脂としては、ポリフェニレンサル
ファイド（ｐｐｓ）、ポリエーテルサルフォン（ｐａｓ
）等があり、ＰＴＦＩ＋ＰＰＳ系塗料。Painting is done with one coat and one bake or two coats and two bakes. First, in the case of one coat and one bake, a paint whose main component is a mixture of polytetrafluoroethylene resin (PTF'g) and another heat-resistant resin is used as a heat-resistant paint. Other heat-resistant resins that can be mixed with PTF E include polyphenylene sulfide (pps), polyether sulfone (pas
) etc., PTFI + PPS paint.
ＰＴＦＩ ＋ ＰＥＳ系塗料の形で用いられる。Used in the form of PTFI + PES paint.
四フッ化エチレン樹脂は、耐熱性とともに加工潤滑性が
あるためプレス加工性に優れており、また、このため非
粘着性＜ｍｕ性）にも優れた特性を有している。Tetrafluoroethylene resin has heat resistance and processing lubricity, so it has excellent press workability, and therefore also has excellent properties in terms of non-adhesion (<mu property).
このような塗料は、連続式鋼帯塗装設備により通常のコ
ーティング条件で塗装し得るものである。Such coatings can be applied using continuous strip coating equipment under normal coating conditions.
鋼板は塗装後、一般に３５０ ’Ｏ以上の温度で焼付は
処理される。After painting, steel plates are generally baked at a temperature of 350'O or higher.
また２コート２ベークの場合には、まずプライマーとし
てポリフェニレンサルファイド樹脂（ｐｐｓ）またはポ
リエーテルサルフォン樹脂（ＰＥＳ）若しくはこれら両
樹脂の混合物（ｐｐｓ ＋ ｐｇｓ ）を耐熱樹脂とす
る塗料が塗布される。このプライマー塗料は高温（２０
０“０以上）での常用耐熱性を有している。このよ −
うなプライマーの例として次のような種類の塗料をあげ
ることができる。In the case of 2 coats and 2 bakes, first a paint containing polyphenylene sulfide resin (pps), polyether sulfone resin (PES), or a mixture of these resins (pps + pgs) as a heat-resistant resin is applied as a primer. This primer paint is applied at high temperatures (20
It has normal heat resistance at temperatures above 0 (0 or more).
Examples of primers include the following types of paints:
（ａ）溶 剤： ６０〜７０％（ＮＭＰ＋ツルペッツ
）耐熱樹脂： ２０〜３０％（ＰＥ３）
防錆顔料： Ｓｔ、 Ｃｒ、 ＠脂分の１％φ）溶
剤；６５％（ＮＭＰ＋ツルペッツ）耐熱樹脂： ２０〜
３０％（ｐａｓ）
防錆顔料；人を十無機顔料
このようなプライマーはその塗膜形成後、焼付処理され
る。この焼付温度は、上塗り後の焼付温度よりは低く、
一般ｌζは２００〜４００°０の温度範囲で行われる。(a) Solvent: 60-70% (NMP + Tsurupetz) Heat-resistant resin: 20-30% (PE3) Rust-preventing pigment: St, Cr, @1% of fat φ) solution
Agent; 65% (NMP + Tsurpets) Heat-resistant resin: 20~
30% (pas) Rust-preventing pigment; Inorganic pigment. After forming the coating film, such a primer is subjected to baking treatment. This baking temperature is lower than the baking temperature after topcoating.
Generally lζ is carried out in a temperature range of 200-400°0.
プライマー塗膜の上には上塗り（仕上げ）塗装がなされ
るが、この塗料は上述した１コート１ベーク鋼板の場合
と同様、耐熱樹脂として四フッ化エチレン樹脂（ＰＴＦ
Ｉ）を必須成分とするもので、四フッ化エチレン樹脂と
他の耐熱樹脂との混合物を主成分としている。A top coat (finishing) is applied on top of the primer coating, but this paint is made of polytetrafluoroethylene resin (PTF) as a heat-resistant resin, as in the case of the one-coat, one-bake steel sheet mentioned above.
I) is an essential component, and the main component is a mixture of tetrafluoroethylene resin and other heat-resistant resins.
塗装後、鋼板は加熱炉で２ベータ目の焼付処理がなされ
る。この焼付温度は３５０〜４００°０程度の温度で行
われる。After painting, the steel plate is subjected to a second beta baking treatment in a heating furnace. This baking temperature is about 350-400°0.
な詔、以上の２コートの塗膜のうち、プラ。Among the above two coats, plastic is the best.
イマー塗料には、耐食性能に重点をおく意味で防錆顔料
を含有せしめることが好ましく、この防錆顔料としては
、従来から用いられているストロンチウム系等の無機顔
料が使用される。一方、仕上げ塗料は、プレス加工番こ
おける潤滑性及び非粘着性が確保されるような観点から
、これらの特性を害する防錆顔料は含有−させていない
。但し、光沢用の顔料（例えば人ｔ）等は含有させるこ
とができる。It is preferable that the immersion paint contains a rust preventive pigment in order to place emphasis on corrosion resistance performance, and as the rust preventive pigment, conventionally used inorganic pigments such as strontium pigments are used. On the other hand, from the viewpoint of ensuring lubricity and non-adhesiveness during the press working process, the finishing paint does not contain anti-rust pigments that would impair these properties. However, pigments for luster (for example, human t) and the like may be included.
鋼板は以上のような塗装焼付後、塗膜表面の平滑化と圧
延とを目的としたロール圧下が施される。上述した耐熱
塗膜は、塗装焼付ままの状態では四フッ化エチレン樹脂
を含むとしても、その非粘着性、プレス成形性は十分で
はなく、また耐食性も十分とは言い難い。After the steel sheet is painted and baked as described above, it is rolled down with a roll for the purpose of smoothing and rolling the surface of the paint film. Even if the above-mentioned heat-resistant coating film contains tetrafluoroethylene resin in the as-baked state, its non-adhesiveness and press moldability are not sufficient, and its corrosion resistance is also not sufficient.
このような問題に対し、塗装焼付後の上記耐熱塗膜をロ
ール圧下することにより、塗膜面が圧延且つ平滑化され
、非粘着性、プレス成形性、さらには耐食性が大きく改
善できることが判った。第１図は、本発明で使用される
耐熱塗料の塗装焼付後、ロール圧下（圧下量ｏ、 ５
％ ）を行ったものと、ロール圧下を行わないものとの
プレス成形性（ＢＨＦ：ｇ絞り可能な最大しわ押え圧）
を比較して示すもので、プレス成形性をダイス： ４０
．９ｍ−３Ｒ、ポンチ： ４０ｊ１１−４Ｒ、Ｌ、わ押
え板：４０．５ダによる深絞り試験Ｊこおいて、しわ押
え圧を上げていき限界しわ押え王を測定したものである
。なお、非粘着性はプレス成形性と相関関係にあり、そ
の性能はプレス成形性で評価することができる。これに
よれば、塗装焼付後のロール圧下によりプレス成形性（
及び非粘着性）が好適に改善されていることが判る。To address these problems, it has been found that by rolling down the heat-resistant coating film after baking, the coating surface is rolled and smoothed, and non-adhesiveness, press formability, and corrosion resistance can be greatly improved. . Figure 1 shows the roll reduction (reduction amount o, 5
% ) and without roll reduction (BHF: Maximum wrinkle pressing pressure that can be squeezed in g)
This is a comparison of the press formability of the die: 40
．． 9m-3R, punch: 40j11-4R, L, wrinkle presser plate: deep drawing test J with 40.5 da, and the wrinkle presser limit was measured by increasing the wrinkle presser pressure. In addition, non-adhesiveness has a correlation with press formability, and its performance can be evaluated by press formability. According to this, press formability (
It can be seen that the properties (and non-adhesiveness) were suitably improved.
このようにロール圧下によりプレス成形性及び非粘着性
が改善されるのは、粗い塗膜面が平滑化されることがそ
の理由の１つとしてあげられるが、さらにもう１つの大
きな理由として、プレス成形性や非粘着性に極めて有効
な塗膜表面にセける四フッ化エチレン樹脂の均一化をあ
げることができる。すなわち、塗膜表面の四フッ化エチ
レン樹脂は、焼付ままではミクロ的にみて偏在した状態
にあるが、ロール圧下により偏在した表面の四フッ化エ
チレン樹脂が引き延ばされ、均一化されるものであり、
このように塗膜表面に均一に引き延ばされた四フッ化エ
チレン樹脂の作用によリプレス成形性及び非粘着性が向
上する。One of the reasons why roll reduction improves press formability and non-adhesive properties is that the rough coating surface is smoothed, but another major reason is that Uniformity of the tetrafluoroethylene resin applied to the surface of the coating film is extremely effective for moldability and non-adhesion. In other words, the polytetrafluoroethylene resin on the surface of the coating film is microscopically unevenly distributed as it is baked, but the unevenly distributed polytetrafluoroethylene resin on the surface is stretched and made uniform by rolling pressure. and
In this way, the action of the tetrafluoroethylene resin uniformly spread over the coating surface improves repress moldability and non-adhesiveness.
なお、第１図によれば、塗膜厚が大きくなるに従いプレ
ス成形性や非粘着性はむしろ低下する傾向ｉこあり、し
たがって耐食性能を確保するために塗膜厚を大きくする
ような場合、ロール臣下でプレス成形性及び非粘着性を
確保することが特に有効である。Furthermore, according to Fig. 1, as the coating thickness increases, the press formability and non-adhesiveness tend to decrease.Therefore, when increasing the coating thickness to ensure corrosion resistance, It is particularly effective to ensure press formability and non-adhesiveness using rolls.
また、ロール圧下によりＩＩ！膜のポーラスな組織が潰
されて塗膜組織が緻密化するものであり、これによって
耐食性が向上する効果が得られる。Also, II! due to roll reduction! The porous structure of the film is crushed and the coating film structure becomes denser, thereby improving corrosion resistance.
以上のようなロール圧下は、塗膜の表面粗さを平滑化し
且つ表面の樹脂を圧延する程度の圧下量で十分であり、
素材鋼板の圧延を伴うことを要しない。逆に一般的には
、素材鋼板の性質に影響を与えない程度の臣下にとどめ
るのが好ましい。The roll reduction as described above is sufficient to smooth the surface roughness of the coating film and roll the resin on the surface.
It is not necessary to involve rolling of the raw steel plate. On the other hand, it is generally preferable to keep it to a level that does not affect the properties of the steel sheet material.
このようにして得られる鋼板は２００ ’Ｏ以上の常用
耐熱性を有するとともに、プレス成形性及び非粘着性に
優れ、しかも耐食性にも優れた性能を有するものである
。The steel plate thus obtained has a general heat resistance of 200'O or more, excellent press formability and non-stick properties, and also excellent corrosion resistance.
なぢ、上記１コート１ベーク鋼板においては、塗装後、
鋼板を加熱炉で加熱して溶剤を蒸発させた後、インダク
ションヒーターで４００°０以上で焼付ける方法を採る
ことができる。In the above-mentioned one-coat, one-bake steel sheet, after painting,
A method can be adopted in which the steel plate is heated in a heating furnace to evaporate the solvent, and then baked at 400° or more with an induction heater.
インダクションヒーターを用いた加熱では、急速加熱が
可能であるとともに、塗膜がその内側、すなわち誘導加
熱された素材鋼側から加熱され、焼付けが行われるため
、残存した溶剤の蒸発を適切に行わしめ且つ均一な焼付
けを得ることができ、これによって優れた塗装密着性を
得ることができる。このようなインダクションヒーター
による加熱を、溶剤の蒸発加熱を行うことなく、塗料の
塗布後直ちに行った場合、急速加熱であるため溶剤が塗
膜内に閉じ込められ、その影響により塗膜の密着性が害
されるという問題があり、また急速に蒸発した溶剤がヒ
ーター内で結露し、再び板に付着してしまう問題がある
。したがってインダクションヒーターで加熱するに先立
ち溶剤を加熱炉で十分に蒸発させておくようにしたもの
である。Heating using an induction heater allows for rapid heating, and the coating is heated from the inside, that is, from the induction-heated material steel side, and baking is performed, so the remaining solvent can be properly evaporated. In addition, uniform baking can be obtained, and thereby excellent paint adhesion can be obtained. If such heating with an induction heater is performed immediately after coating the paint without evaporating the solvent, the solvent will be trapped within the paint film due to rapid heating, which will affect the adhesion of the paint film. There is also the problem that the rapidly evaporated solvent condenses inside the heater and adheres to the board again. Therefore, the solvent is sufficiently evaporated in a heating furnace before heating with an induction heater.
また、本発明法により得られる鋼板に対しては、そのロ
ール圧下前またはロール圧下後に綿実油等の食用植物油
を塗布して塗膜に古漬させることができ、これによりプ
レス成形性と非粘着性をさらに向上させ、この結果、食
品加熱加工用具に製品化された後、最初に使用する際に
非粘着性確保のため特に必要とされる食用油の塗油を全
く不要ならしめることができる。In addition, the steel sheet obtained by the method of the present invention can be coated with edible vegetable oil such as cottonseed oil before or after roll rolling to give the coating film an aged coating, thereby improving press formability and non-adhesiveness. As a result, it is possible to completely eliminate the need for applying edible oil, which is particularly required to ensure non-stick properties, when used for the first time after being manufactured into a food heating processing tool.
第１表に示す条件で塗装鋼板を製造し、それらについて
下記試験条件によりプレス成形性（非粘着性）及び耐熱
性を調べた。その結果を第２表に示す。Painted steel plates were manufactured under the conditions shown in Table 1, and their press formability (non-adhesiveness) and heat resistance were examined under the following test conditions. The results are shown in Table 2.
・プレス成形性試験（潤滑性）
ダイス： ４Ｇ、９１ＩＩ−３Ｒ、ポンチ：４０１！ｌ
−４Ｒ１しわ押え板：４Ｇ、５ｊｆによる深絞り試験に
おいて、しわ押え圧を上げていき限界しわ押え圧を測定
。・Press formability test (lubricity) Die: 4G, 91II-3R, punch: 401! l
-4R1 wrinkle presser plate: In a deep drawing test using 4G and 5jf, the wrinkle presser pressure was increased and the limit wrinkle presser pressure was measured.
・耐熱性試験
２６０°ワの炉中に１６時間保持し、空冷後のＯＴ Ｂ
ｅｎｄ＋テープ剥離による。・Heat resistance test OT B
By end+tape peeling.
◎：剥離なし
○：点状剥離
Δ：剥１１！１０％程度
Ｘ：剥離２０１＠度
また、供試材（１）（本発明材）及び供試材（４）（比
較材）について、湿度９８彊、５０゛Ｃの条件による湿
潤試験により耐食性を調べた。この結果、供試材（４）
では１７０時間で点状赤錆が発生したのｌこ対し、供試
材（１）ではＳＯＯ時間で点状赤錆が発生した。◎: No peeling ○: Point peeling Δ: Peeling 11! Approximately 10% Corrosion resistance was investigated by a wet test at 98 degrees Celsius and 50 degrees Celsius. As a result, sample material (4)
On the other hand, red spot spots were generated in sample material (1) after 170 hours, whereas red rust spots were generated in sample material (1) after 170 hours.
以上述べた本発明によれば、高温下における常用耐熱性
を有するととも１こ、優れたプレス成形性、非粘着性、
さらには耐食性を有する塗装鋼板を製造し得るものであ
り、ベータウェア、オーブン天板、加熱プレート等の食
品加熱加工用品用として特に好適な鋼板を安価に提供し
得るものである。According to the present invention described above, in addition to having general heat resistance at high temperatures, excellent press formability, non-adhesiveness,
Furthermore, it is possible to produce a coated steel plate having corrosion resistance, and it is possible to provide a steel plate particularly suitable for use in food heating processing products such as betaware, oven top plates, and heating plates at a low cost.
第１図は本発明で使用される耐熱塗料の塗装後、ロール
圧下を行った鋼板とロール圧下を行わない鋼板のプレス
成形性を塗膜厚との関係で示すものである。
特許出願人 日本鋼管株式会社
発明 者 下 村 １隆 良
同 蛇 目 達 志同
山 地 隆 文代理人弁
理士 吉 原 省 三手続補正書（自
発）
昭和６０年２月２１日
特許庁長官 志 賀 学 殿
（特許庁審査官 殿）
１、事件の表示
昭和号９ 年 待 許 願第２ｂｏｏ／／ 号２、
発明の名称
非迷占Ｍ／１ｔｌ＝不等虞４２耐ハイ計鳴タタ閾２よう
、の本ゐ妃本（４１２） 日本４管（−一式会社４
、代理人
５、補正命令の日付
袖 正 内 容
／本願明細書中第５頁５行目冒頭ｌこ「工用品」とある
次ｌこ「等」と加入する。
二回書第６頁１行目中「塗装密着性」と□あるを「耐食
性」と訂正する。
３、同書第８頁２０行目を以下のよう（こ訂正する。
「 防錆顔料：Ａｔ十無機顔料
（またはホウ酸塩系顔料） 」
ｌＡ同同書第１貞
ある次に「表面粗さが粗くなり、これに起因して」と加
入する。
よ同８第１３頁３行目中「塗装後、Ｊとあるを「塗装後
加熱炉でそのまま焼付けることもできるが、これ以外に
、」と訂正する。
ｋ同書第１４頁１１行目と１２行目の間に以下のように
加入する。
「以上のようにして得られる耐熱塗装鋼板は食品加熱加
工用具のほか，建築物のダクト等、適宜な用途に使用す
ることができる。
なお１本発明法は，素材板を鋼板以外の他の金属板、例
えばｋｔ板とする場合ｌこも応用できる。ｊ
７同書第１６頁第１表を別紙のように訂正する。FIG. 1 shows the press formability of a steel plate subjected to roll reduction and a steel plate not subjected to roll reduction after coating with the heat-resistant paint used in the present invention in relation to the coating film thickness. Patent applicant: Nippon Kokan Co., Ltd. Inventor: Kazutaka Shimomura Ryodo Tatsu Jaume Shido
Takashi Yamachi, Patent Attorney, Sho Yoshihara, Three procedural amendments (voluntary), February 21, 1985, Commissioner of the Patent Office, Manabu Shiga (Examiner of the Patent Office)
1. Indication of the incident Showa No. 9, Waiting Request No. 2boo // No. 2,
Name of the invention Non-transfer M / 1tl = Inequality 42 resistance high meter sound threshold 2 Yo, Nomoto Ihimoto (412) Japan 4 tube (-1 set company 4
, Agent 5, the date of the amendment order, correct contents/In the specification of the present application, page 5, line 5, at the beginning of the text, it says ``Work supplies,'' and then adds ``etc.'' In the first line of page 6 of the second edition, the word "paint adhesion" is corrected to "corrosion resistance." 3. Line 20 of page 8 of the same book reads as follows (this has been corrected. It becomes rough, and due to this," is added. In the 3rd line of page 13 of Yodo 8, replace "J" with "After painting, it is possible to bake it in a heating furnace as it is, but in addition to this," The following is added between lines 11 and 12 on page 14 of the same book: ``The heat-resistant coated steel sheets obtained in the above manner can be used not only for food heating processing tools but also for building ducts, etc. Note that the method of the present invention can also be applied when the material plate is a metal plate other than a steel plate, such as a KT plate. Correct as shown in the attached sheet.
Claims (2)
エチレン樹脂と他の耐熱樹脂と の混合物を主成分とする塗料を塗付し、 塗膜焼付後、重膜表面の平滑化と圧延と を目的としたロール圧下を行うことを特 徴とする非粘着性に優れた耐熱塗装鋼板 の製造方法。(1) Apply a paint mainly composed of a mixture of tetrafluoroethylene resin and other heat-resistant resin to the surface of a stainless steel plate or plated steel plate, and after baking the paint film, smooth the surface of the heavy film and roll it. A method for manufacturing a heat-resistant coated steel sheet with excellent non-stick properties, which is characterized by performing targeted roll reduction.
ニレンサルファイド樹脂または ポリエーテルサルフォン樹脂若しくはポ リフェニレンサルファイド樹脂とポリエ ーテルサルフォン樹脂との混合物を耐熱 樹脂とするプライマーを塗布した後焼付 け、その上に四フッ化エチレン樹脂と他 の耐熱樹脂との混合物を主成分とする塗 料を塗付し、塗膜焼付後、塗膜表面の平 滑化と圧延とを目的としたロール圧下を 行うことを特徴とする非粘着性に優れた 耐熱塗装鋼板の製造方法。(2) After applying a primer containing a heat-resistant resin of polyphenylene sulfide resin, polyether sulfone resin, or a mixture of polyphenylene sulfide resin and polyether sulfone resin to the surface of a stainless steel plate or plated steel plate, baking It is characterized by applying a paint whose main component is a mixture of ethylene chloride resin and other heat-resistant resins, and after baking the paint film, rolling it down with a roll for the purpose of smoothing and rolling the paint film surface. A method for manufacturing heat-resistant coated steel sheets with excellent adhesion.