PURPOSE:To provide a cap label consisting of a film made of a resin composition composed of polypropylene, polyethylene and a filler, having excellent water-resistance and chemical-resistance, high tearability, and unable to be opened without damaging the film. CONSTITUTION:The objective cap label is produced from a film having a dart impact strength of <=2kg.cm and an Elmendorf tear strength of <=2kg/cm along at least one direction, and made of a composition obtained by compounding (A) 5-60(wt)% polypropylene such as random copolymer or block copolymer of propylene and ethylene, etc., (B) 30-90% polyethylene having a density of >=0.94g/cm<3>, such as copolymer of ethylene and butene-1 or hexene-1, etc., and (C) 5-30% filler having an average particle diameter of preferably 0.01-35mum, preferably mica, calcium carbonate or wollastonite.

Description

【発明の詳細な説明】 （技術分野） 本発明は、ポリオレフィン樹脂系組成物により成形され
た易引裂性フィルムを用いたキャップラベルに関する。DETAILED DESCRIPTION OF THE INVENTION (Technical Field) The present invention relates to a cap label using an easily tearable film formed from a polyolefin resin composition.

（従来技術） 近来、食品や薬品のビン、或いは小箱等の内容物に毒物
を混入する犯罪が発生し、大きな社会問題となっている
。その防止策としてビンの蓋部分、或いは容器全体を熱
収縮性フィルムで覆ってしまラキャップシールや、蓋と
本体とにわたって境界部にラベルを貼り、未開封を確認
するキャップラベルが用いられるようになってきた。(Prior Art) In recent years, crimes have occurred in which poisonous substances are mixed into the contents of food and medicine bottles, small boxes, etc., and this has become a major social problem. To prevent this, cap stickers, which cover the lid of the bottle or the entire container with heat-shrinkable film, and cap labels, which attach a label to the boundary between the lid and the main body to confirm that the bottle has not been opened, are being used. It has become.

（従来技術の問題点） ところで、上記キャップシール、或いはキャップラベル
は、いずれも未開封の確認には極めて有効であるが、前
者は熱収縮性フィルムを用いてキャッピングし、熱源に
よって所定の温度に加熱して熱収縮させて密着被覆する
ためコスト高となる。また、後者においてキャップラベ
ルは通常紙でつくられているので、水分、又は内容物よ
り発生する蒸気等により変色し、商品イメージぞ損う欠
点がある。(Problems with the prior art) By the way, both the cap seal and the cap label described above are extremely effective in confirming that the package has not been opened, but the former caps with a heat-shrinkable film and is heated to a predetermined temperature using a heat source. The cost is high because it is heated and heat-shrinked to cover tightly. Moreover, in the latter case, since the cap label is usually made of paper, it has the disadvantage that it discolors due to moisture or steam generated from the contents, which spoils the product image.

（発明の目的） 本発明は上記の事情に鑑み、耐水性、耐薬品性に優れ、
引裂性がよく、フィルムを損なわずには開封できないキ
ャップラベルを提供することを目的とする。(Object of the invention) In view of the above circumstances, the present invention has excellent water resistance and chemical resistance,
To provide a cap label that has good tearability and cannot be opened without damaging the film.

（発明の構成） 本発明は上記の目的を達成するためになされたものであ
り、その要旨は、ポリプロピレン５〜９０重量％、密度
０．Ｅ１４０ｇ／　ｃ　ｍ″以上ポリエチレン３０〜９
０重量％および充填剤５〜３０重量％からなる樹脂系組
成物により成形されたフィルムであり、タートインパク
トが２Ｋｇ／ｃｍ以下、エルメンドルフ引裂強度が少な
くとも一方向において２Ｋｇ／ｃ層以下であることを特
徴とするキャップラベル、にある。(Structure of the Invention) The present invention has been made to achieve the above object, and its gist is that polypropylene is 5 to 90% by weight, density is 0. E140g/cm″ or more Polyethylene 30~9
It is a film molded from a resin composition consisting of 0% by weight and 5 to 30% by weight of filler, and has a tart impact of 2Kg/cm or less and an Elmendorf tear strength of 2Kg/c layer or less in at least one direction. Features a cap label.

（構成の具体例） 本発明でのフィルムの成形に用いる樹脂系組成物におい
て、ポリプロピレンはプロピレンホモポリマー、プロピ
レンとエチレンのランダムコポリマー、フロピレンとエ
チレンのブロックコポリマー、これらを主体とするブレ
ンド物などであり、またポリエチレンはエチレンホモポ
リマー。(Specific example of composition) In the resin composition used for film molding in the present invention, polypropylene may be a propylene homopolymer, a random copolymer of propylene and ethylene, a block copolymer of fluoropylene and ethylene, or a blend mainly composed of these. Yes, polyethylene is an ethylene homopolymer.

エチレンとブテン−１、ヘキセン−１のような異種α−
オレフィンとのコポリマー、これらを主体とするブレン
ド物などであり、密度０．９４０ｇ／　ｃ　ｒｎ’未満
（ＪＩＳ　　Ｋ６７６０）ではキャップラベルの切味が
劣る６ さらに前記両樹脂の含有量が、ポリプロピレンで５〜６
０重量％を外れても、ポリエチレンが３０〜９０重量％
を外れても、キャップラベルの引裂が困難となり切味が
劣ってしまう、即ち両者の適度の併存により引裂のし易
さと切味の良さをもたらしている。Ethylene and heterogeneous α- such as butene-1 and hexene-1
Copolymers with olefins, blends mainly composed of these, etc., and if the density is less than 0.940g/crn' (JIS K6760), the sharpness of the cap label will be poor.6 Furthermore, if the content of both resins is 5. ~6
Even if it is less than 0% by weight, polyethylene is 30 to 90% by weight.
Even if the cap label is removed, it will be difficult to tear the cap label and the cutting quality will be poor.In other words, the moderate coexistence of both will result in ease of tearing and good cutting quality.

一方、充填剤は各樹脂は引裂し難い低流動性の場合でも
、引裂のし易さと切味を一層高めるものであり、無機系
としては、タルク、炭カル、ワラストナイト、ガラスピ
ーズ、ガラスファイバー、クレー、硫酸バリウム、ホワ
イトカーボン、マイカなどが挙げられ、なかでもマイカ
、炭カル、ワラストナイトが好ましく、また有機系とし
ては木粉、わらくず、ナイロンビーズなどが挙げられ。On the other hand, fillers are used to further improve tearability and sharpness even when the resin has low fluidity and is difficult to tear.Inorganic fillers include talc, charcoal, wollastonite, glass peas, and glass. Examples include fiber, clay, barium sulfate, white carbon, mica, etc., among which mica, charcoal, and wollastonite are preferred, and organic materials include wood flour, straw waste, nylon beads, etc.

５重量％未満では切味の向上効果が不足し、３０重竜％
を越えるとフィルムの成形が不安定になり勝ちである。If it is less than 5% by weight, the sharpness improvement effect will be insufficient, and if it is less than 30% by weight.
If it exceeds this value, the film will become unstable.

また充填剤の粒度は、平均粒度０．０１〜３５ＪＬｍが
好ましく、０．０ｉ　ｐ、　ｍ未満では組成物中での分
散が困難で凝集を招き、その凝集のためフィルム成形中
に孔がおいてしまい、また３５ＩＬｒｎを越えるとフィ
ルムの安定成形が困難となる。In addition, the particle size of the filler is preferably an average particle size of 0.01 to 35 JLm, and if it is less than 0.0 ip, m, it will be difficult to disperse in the composition and cause aggregation, and the aggregation will cause pores during film forming. Moreover, if it exceeds 35 ILrn, stable molding of the film becomes difficult.

また、成形したフィルムはダートインパクト（ＪＩＳ−
Ｚ−１７０２）が２．０Ｋｇ　＠ａｍ以下、エルメンド
ルフ引裂強度（ＡＳＴＭ−Ｄ−１７０９−７５）が、少
なくとも一方向において２．０Ｋｇ／Ｃ■以下であるこ
とが必要であり、使用時の引裂方向において２．０Ｋｇ
／ｃｍ以下とする。ダートインパクトが２．０Ｋｇ・ｃ
ａｔを越えると引裂が困難となり勝ちで、ダートインパ
クトは厚みにほぼ比例するので、単位厚み当りのエルメ
ンドルフ引裂強度が前記数値限定を満足しても厚手にな
ると引裂が困難となる。In addition, the formed film is a dirt impact (JIS-
Z-1702) must be 2.0 Kg @am or less, Elmendorf tear strength (ASTM-D-1709-75) must be 2.0 Kg/C or less in at least one direction, and the tear direction during use must be 2.0Kg in
/cm or less. Dirt impact is 2.0Kg・c
If the thickness exceeds at, tearing becomes difficult, and since the dart impact is approximately proportional to the thickness, even if the Elmendorf tear strength per unit thickness satisfies the above numerical limit, tearing becomes difficult as the thickness increases.

また、エルメンドルフ引裂強度はフィルム成形時の引取
速度にも影響されるが、使用時の引裂方向におけるエル
メンドルフ引裂強度が２．０Ｋｇ／ｃｍを越えると、蓋
を開く場合キャップラベルの切味が悪くなる。In addition, the Elmendorf tear strength is also affected by the take-off speed during film forming, but if the Elmendorf tear strength in the tear direction during use exceeds 2.0 kg/cm, the cap label will not cut well when opening the lid. .

すなわち、前記樹脂系組成物を用い、ダートインパクト
、エルメンドルフ引裂強度が上記範囲になるように成形
したフィルムによって作成したキャップラベルは、開封
時に引裂ができて切味もよく、さらにポリオレフィン樹
脂系組成物なので耐水性、耐薬品性に優れ、しかもラベ
ルを損傷せずに開封することができず、未開封確認に好
適なものとなる。In other words, a cap label made from a film formed using the resin composition so that the dart impact and Elmendorf tear strengths fall within the above ranges can be easily torn when opened, has a good sharpness, and has a polyolefin resin composition. Therefore, it has excellent water resistance and chemical resistance, and cannot be opened without damaging the label, making it suitable for checking whether the package has been opened.

夾羞」Ｌ」１忙１ スクリュー径：　４０ｍｍの下向きインフレーシ重ンフ
イルム成形機に、径：５０■φのダイスを取付け、膨張
比２．５、引取速度２０ＩＩ／ｗｉｎで第１表に示す“
樹脂系組成物を用いて厚み３０ｐｍ（比較例７のみ９０
ＪＬｍ）のフィルムをつくり、各フィルムのダートイン
パクトおよびエルメンドルフ引裂強度を測定した。但し
、ダートインパクトは低強度の測定となるため、落下距
離を下げて測定した。A die with a diameter of 50 φ was attached to a downward inflation film forming machine with a screw diameter of 40 mm, and the expansion ratio was 2.5 and the take-up speed was 20 II/win as shown in Table 1.
Using a resin composition, the thickness was 30 pm (only Comparative Example 7 was 90 pm).
JLm) films were made and the dart impact and Elmendorf tear strengths of each film were measured. However, since dirt impact is a measurement of low strength, the falling distance was lowered for measurement.

また、第１図に示すようにそれぞれのフィルムから、長
辺：　２０ｍｒａ　　短辺：　１０ｍｍの楕円形キャッ
プラベル１を長辺がＭＤとなるように打抜き、市販のプ
ラスチック用接着剤にて、内容積１００ｍ文のプラスチ
ック製ビン２の蓋３の縁部４とＭＤが平行となるように
して貼付し、蓋３をひねってキャップラベルの切味を比
較した。In addition, as shown in Figure 1, an oval cap label 1 with a long side of 20 mra and a short side of 10 mm was punched out from each film so that the long side was MD, and the internal volume was adjusted using a commercially available plastic adhesive. The cap label was attached to a 100 m long plastic bottle 2 so that the edge 4 of the cap 3 was parallel to the MD, and the cap label was twisted to compare the sharpness of the cap label.

実施例、比較例の結果を第１表に示す、なおＭＤはマシ
ンディレクシオンの略であって引取方向を意味し、ＴＤ
はトランスバースディレクションの略であって引取方向
と直角方向である。The results of Examples and Comparative Examples are shown in Table 1. MD is an abbreviation for Machine Direction and means the direction of take-off, and TD
is an abbreviation for transverse direction, which is a direction perpendicular to the take-up direction.

また樹脂系組成物の成分は次のとおりである。The components of the resin composition are as follows.

ポリプロピレン（以下、ＰＰと称する）プロピレンホモ
ポリマー ＭＦ’１　８ｇ／１０ｒａｒｎ　　（ＪＩＳ　　Ｋ６７
５８）ポリエチレン（以下、ＰＥと称する） 密度　０．９５０ｇ／　ｃｒｎ’　（Ｊ　Ｉ　Ｓ　　Ｋ
　６７６０）ＭＦＩ　　０．８ｇ／ｗｉｎ　　（ＪＩＳ
　　Ｋ６７６０）充填剤 マイカ、山口雲母（株）製、 商品名；Ａ−３１Ｃ以下、Ｍと称する）平均粒径　２０
ｐ、ｍ ワラストナイト、浅田製粉（株）製、 商品名；　ＪＥＴ−３０（以下、Ｗと称する）平均粒径
　６ルｍ アスペクト比　２０ （以下余白） （発明の効果） 以上述べたように１本発明に係るキャップラベルは耐水
性、＃薬品に優れ、長期にわたって変色、変質すること
なく、また開封時の切味がよく、さらにキャップラベル
を損傷せずに開封ができないので、未開封を確認するキ
ャップラベルとして極めて優れたものである。Polypropylene (hereinafter referred to as PP) propylene homopolymer MF'1 8g/10ran (JIS K67
58) Polyethylene (hereinafter referred to as PE) Density 0.950g/crn' (JISK
6760) MFI 0.8g/win (JIS
K6760) Filler mica, manufactured by Yamaguchi Mica Co., Ltd., Product name: A-31C (hereinafter referred to as M) Average particle size 20
p, m Wollastonite, manufactured by Asada Seifun Co., Ltd., trade name: JET-30 (hereinafter referred to as W) Average particle size: 6 lm Aspect ratio: 20 (hereinafter referred to as margin) (Effects of the invention) As stated above. 1. The cap label according to the present invention has excellent water resistance and chemical resistance, does not discolor or deteriorate over a long period of time, has good sharpness when opened, and can not be opened without damaging the cap label. This is an extremely excellent cap label for confirmation.

【図面の簡単な説明】[Brief explanation of drawings]

第１図は、キャップラベルを貼付したビンの側面図であ
る。FIG. 1 is a side view of a bottle with a cap label attached.

Claims (1)

【特許請求の範囲】[Claims] 　ポリプロピレン５〜６０重量％、密度０．９４０ｇ／
ｃｍ＾３以上のポリエチレン３０〜９０重量％および充
填剤５〜３０重量％からなる樹脂系組成物により成形さ
れたフィルムであり、ダートインパクトが２Ｋｇ・ｃｍ
以下、エルメンドルフ引裂強度が少なくとも一方向にお
いて２Ｋｇ／ｃｍ以下であることを特徴とするキャップ
ラベル。Polypropylene 5-60% by weight, density 0.940g/
It is a film molded from a resin composition consisting of 30 to 90% by weight of polyethylene of cm^3 or more and 5 to 30% by weight of filler, and has a dart impact of 2Kg/cm.
Hereinafter, a cap label characterized in that the Elmendorf tear strength is 2 Kg/cm or less in at least one direction.